JPH01264108A - 難燃性電気絶縁組成物 - Google Patents
難燃性電気絶縁組成物Info
- Publication number
- JPH01264108A JPH01264108A JP63091104A JP9110488A JPH01264108A JP H01264108 A JPH01264108 A JP H01264108A JP 63091104 A JP63091104 A JP 63091104A JP 9110488 A JP9110488 A JP 9110488A JP H01264108 A JPH01264108 A JP H01264108A
- Authority
- JP
- Japan
- Prior art keywords
- weight parts
- fire
- range
- barium
- inorganic flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
[産業上の利用分野]
本発明は、燃焼時に有毒なハロゲン系ガスを発生しない
難燃性電気絶縁組成物、特に電線・ケーブルの絶縁材料
やシース材料への適用に好適な難燃性電気絶縁組成物に
関するものである。
難燃性電気絶縁組成物、特に電線・ケーブルの絶縁材料
やシース材料への適用に好適な難燃性電気絶縁組成物に
関するものである。
[従来の技術]
電線・ケーブルの絶縁材料やシース材料としては電気絶
縁性に優れたポリオレフィンが多く用いられてきている
。最近のすう勢として原子力発電所用電線・ケーブル、
車両用電線・ケーブル、船舶用電線・ケーブルに垂直ト
レイ燃焼試験レベルの高度の難燃性が要望されるように
なってきた。
縁性に優れたポリオレフィンが多く用いられてきている
。最近のすう勢として原子力発電所用電線・ケーブル、
車両用電線・ケーブル、船舶用電線・ケーブルに垂直ト
レイ燃焼試験レベルの高度の難燃性が要望されるように
なってきた。
ポリオレフィンを難燃化する方法としてはハロゲン含有
化合物等を混和する方法が一般に採用されてきている。
化合物等を混和する方法が一般に採用されてきている。
しかし、これらは燃焼時多量の煙を発生し、機器への腐
食性、人体への有害性等が問題になってきている。特に
最近は、安全面からこのようなハロゲン系ガスを発生し
ないことが要望されるようになってきている。
食性、人体への有害性等が問題になってきている。特に
最近は、安全面からこのようなハロゲン系ガスを発生し
ないことが要望されるようになってきている。
このような情勢を踏まえ、発煙性、有毒性の非常に少な
い無機系難燃剤が注目されるようになってきた。
い無機系難燃剤が注目されるようになってきた。
[発明が解決しようとする課2F
しかしながら、無機系・難燃剤は難燃効果が小さいため
、単にポリマーに混和しただけでは燃焼時に溶融滴下す
るというドリップ現象がみられ、高度の難燃性を付与す
ることは難しい。
、単にポリマーに混和しただけでは燃焼時に溶融滴下す
るというドリップ現象がみられ、高度の難燃性を付与す
ることは難しい。
なお、高度の難燃性を付与するためには無機系難燃剤を
多量加えることも有効であるが、得られる絶縁体やシー
スの引張特性の低下を招いたり、押出加工性が低下する
という問題がある。
多量加えることも有効であるが、得られる絶縁体やシー
スの引張特性の低下を招いたり、押出加工性が低下する
という問題がある。
本発明は上記に基づいてなされたものであり、垂直トレ
イ燃焼試験レベルに合格する高度の難燃性を付与できる
と共に有毒なハロゲン系ガスを発生しない難燃性電気絶
縁組成物の提供を目的とするものである。
イ燃焼試験レベルに合格する高度の難燃性を付与できる
と共に有毒なハロゲン系ガスを発生しない難燃性電気絶
縁組成物の提供を目的とするものである。
[課題を解決するための手段]
本発明の難燃性電気絶縁組成物は、ポリオレフィン10
0mfa部に対して無機系難燃剤50〜300重量部、
およびバリウムあるいはバリウム化合物O15重計部以
」−を含Hするものである。
0mfa部に対して無機系難燃剤50〜300重量部、
およびバリウムあるいはバリウム化合物O15重計部以
」−を含Hするものである。
本発明において、ポリオレフィンとしては、エチレンプ
ロピレンコポリマー、エチレンプロピレンジェンターポ
リマー、ポリエチレン、エチレン酢酸ビニルコポリマー
、エチレンエチルアクレリレートコポリマー、エチレン
ブテンコポリマー、エチレンブテンジェンターポリマー
といったものが挙げられ、これらは単独使用又は2種以
上の併用が可能である。
ロピレンコポリマー、エチレンプロピレンジェンターポ
リマー、ポリエチレン、エチレン酢酸ビニルコポリマー
、エチレンエチルアクレリレートコポリマー、エチレン
ブテンコポリマー、エチレンブテンジェンターポリマー
といったものが挙げられ、これらは単独使用又は2種以
上の併用が可能である。
無機系難燃剤としては、水酸化アルミニウム、水酸化マ
グネシウム、塩基性炭酸マグネシウム、水酸化カルシウ
ム、ハイドロタルサイト類等が挙げられる。無機系難燃
剤の含有量は、ポリオレフィン100重量部に対して5
0〜300重量部の範囲とする必要があり、50重量部
未満では目的とする難燃性を付与できず、300重量部
を越えると加工性が著しく低下して押出成形が困難にな
る。
グネシウム、塩基性炭酸マグネシウム、水酸化カルシウ
ム、ハイドロタルサイト類等が挙げられる。無機系難燃
剤の含有量は、ポリオレフィン100重量部に対して5
0〜300重量部の範囲とする必要があり、50重量部
未満では目的とする難燃性を付与できず、300重量部
を越えると加工性が著しく低下して押出成形が困難にな
る。
本発明において無機系難燃剤に加えて併用されるバリウ
ム化合物としては、酸化バリウム、チタン酸バリウム、
炭酸バリウム、硫酸バリウム、ジメトキシバリウム、ジ
−n−ブトキシバリウム等が挙げられる。
ム化合物としては、酸化バリウム、チタン酸バリウム、
炭酸バリウム、硫酸バリウム、ジメトキシバリウム、ジ
−n−ブトキシバリウム等が挙げられる。
本発明において、バリウムあるいはバリウム化合物はポ
リオレフィン100重塁部に対して0.5重量部以上配
合する必要があり、0.5重量部未満では燃焼時のドリ
ップを防止できず、難燃性が不充分となる。
リオレフィン100重塁部に対して0.5重量部以上配
合する必要があり、0.5重量部未満では燃焼時のドリ
ップを防止できず、難燃性が不充分となる。
本発明においては、」二記成分に加えて架橋剤、酸化防
止剤、滑剤、軟化剤、分散剤等を適宜添加してもよい。
止剤、滑剤、軟化剤、分散剤等を適宜添加してもよい。
架橋剤としては、ジクミルパーオキサイド、3−ビス(
t−ブチルパーオキシイソプロピル)ベンゼンに代表さ
れる有機過酸化物が適切であり、これに架橋助剤として
、硫黄、エチレンジメタクリレート、ジアリルフタレー
ト、p−キノンジオキシム等を併用してもよい。また、
電子線等の電離性放射線による架橋の場合は、架橋助剤
としてトリメチロールプロパントリメリテート、トリア
リルイソシアヌレート等の反応性のモノマーを添加する
のが一般的である。酸化防止剤としては、フェニル−α
−ナフチルアミン、N。
t−ブチルパーオキシイソプロピル)ベンゼンに代表さ
れる有機過酸化物が適切であり、これに架橋助剤として
、硫黄、エチレンジメタクリレート、ジアリルフタレー
ト、p−キノンジオキシム等を併用してもよい。また、
電子線等の電離性放射線による架橋の場合は、架橋助剤
としてトリメチロールプロパントリメリテート、トリア
リルイソシアヌレート等の反応性のモノマーを添加する
のが一般的である。酸化防止剤としては、フェニル−α
−ナフチルアミン、N。
N゛−ジ−β−ナフチル−p−フェニレンジアミン等の
アミン系酸化防止剤、2.6−ジーt−ブチル−4−メ
チルフェノール、ヒンダードフェノール等のフェノール
系酸化防止剤が挙げられる。
アミン系酸化防止剤、2.6−ジーt−ブチル−4−メ
チルフェノール、ヒンダードフェノール等のフェノール
系酸化防止剤が挙げられる。
[実施例]
表に示すような配合に従って、各種成分を100℃に保
持された6インチロールに投入してロール混練を行い、
混線後120℃に保持された40m/m押出機(L/D
−25)を用い、外径5.3■の絶縁線心を3本撚合せ
た外周に2.0■の厚さで押出被覆した。なお、実施例
1,4゜5および比較例1については押出被覆に続いて
13 Kg/ cta”の水蒸気雰囲気中に3分間保持
して架橋した。
持された6インチロールに投入してロール混練を行い、
混線後120℃に保持された40m/m押出機(L/D
−25)を用い、外径5.3■の絶縁線心を3本撚合せ
た外周に2.0■の厚さで押出被覆した。なお、実施例
1,4゜5および比較例1については押出被覆に続いて
13 Kg/ cta”の水蒸気雰囲気中に3分間保持
して架橋した。
各側で作製した絶縁電線についての評価結果は表の下欄
に示した通りである。
に示した通りである。
なお、難燃性評価は次のようにして行った。長さ2mの
ケーブルを垂直に8本並べ、下から70.0OOBTU
の炎を20分間当て、自己消炎すれば合格であり、自−
己消炎せず全焼するものは不合格である。
ケーブルを垂直に8本並べ、下から70.0OOBTU
の炎を20分間当て、自己消炎すれば合格であり、自−
己消炎せず全焼するものは不合格である。
表からも明らかな通り、本発明に係る実施例1〜6はい
ずれも難燃性に合格し、押出加工性に優れている。これ
に対し、無機系難燃剤の含有量が規定値以下の比較例1
は難燃性が不合格であり、規定値以上の比較例2は押出
性が悪く成形不可能であった。また、バリウムあるいは
バリウム化合物の含有量が規定値以下の比較例3,4.
5はドリップが生じて難燃性が不合格となる。
ずれも難燃性に合格し、押出加工性に優れている。これ
に対し、無機系難燃剤の含有量が規定値以下の比較例1
は難燃性が不合格であり、規定値以上の比較例2は押出
性が悪く成形不可能であった。また、バリウムあるいは
バリウム化合物の含有量が規定値以下の比較例3,4.
5はドリップが生じて難燃性が不合格となる。
[発明の効果コ
以」二説明してきた通り、本発明は難燃剤として無機系
難燃剤とバリウムあるいはバリウム化合物とを併用した
ものであり、良好な押出加工性を維持しながら燃焼時の
ドリップを防止して高度の難燃性を付与でき、しかも燃
焼時に有毒なハロゲン系ガスを発生しない電気絶縁組成
物を提供できる。
難燃剤とバリウムあるいはバリウム化合物とを併用した
ものであり、良好な押出加工性を維持しながら燃焼時の
ドリップを防止して高度の難燃性を付与でき、しかも燃
焼時に有毒なハロゲン系ガスを発生しない電気絶縁組成
物を提供できる。
Claims (1)
- 1.ポリオレフィン100重量部に対して無機系難燃剤
50〜300重量部、およびバリウムあるいはバリウム
化合物0.5重量部以上を含有することを特徴とする難
燃性電気絶縁組成物。