JPH01115945A - 難燃性電気絶縁組成物 - Google Patents
難燃性電気絶縁組成物Info
- Publication number
- JPH01115945A JPH01115945A JP27276787A JP27276787A JPH01115945A JP H01115945 A JPH01115945 A JP H01115945A JP 27276787 A JP27276787 A JP 27276787A JP 27276787 A JP27276787 A JP 27276787A JP H01115945 A JPH01115945 A JP H01115945A
- Authority
- JP
- Japan
- Prior art keywords
- flame
- frit
- inorganic
- parts
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は電線・ケーブルの絶縁材料やシース材料への適
用に好適な、燃焼時に有毒なハロゲン系ガスを発生しな
い難燃性電気絶縁組成物に関するものである。
用に好適な、燃焼時に有毒なハロゲン系ガスを発生しな
い難燃性電気絶縁組成物に関するものである。
［従来の技術］
電線・ケーブルの絶縁材料やシース材料としては、電気
絶縁性に優れたポリオレフィンが多く用いられてきてい
る。そして最近の趨勢として、原子力発電所用電線・ケ
ーブル、船舶用ケーブル等に対し垂直トレイ燃焼試験に
合格する高度の難燃性が要望されるようになってきた。
絶縁性に優れたポリオレフィンが多く用いられてきてい
る。そして最近の趨勢として、原子力発電所用電線・ケ
ーブル、船舶用ケーブル等に対し垂直トレイ燃焼試験に
合格する高度の難燃性が要望されるようになってきた。
ところで、ポリオレフィンを難燃化する方法としては、
ハロゲン含有化合物（塩素系又は臭素系化合物）を混和
する方法が一般に採用されてきている。しかし、これら
は燃焼時に多量の煙を発生し、また人体に有害なガスを
発生することなどから問題視されている。
ハロゲン含有化合物（塩素系又は臭素系化合物）を混和
する方法が一般に採用されてきている。しかし、これら
は燃焼時に多量の煙を発生し、また人体に有害なガスを
発生することなどから問題視されている。
このような情勢を踏まえ、発煙性・有毒性の非常に少な
い水和アルミナや水酸化マグネシウムなどの無機系難燃
剤を混和する方法が採用されてきている。
い水和アルミナや水酸化マグネシウムなどの無機系難燃
剤を混和する方法が採用されてきている。
［発明が解決しようとする問題点コ
しかしながら、ＩＥＥＥ（米国電気電子技術者協会）規
格３８３に規定される垂直トレイ燃焼試験（ＶＴ Ｆ
Ｔ）に合格する高度の難燃性を付与するためには、これ
らの無機系難燃剤を多量に添加する必要がある。この結
果、分散や引張特性の低下を招くだけでなく、材料の難
燃性の尺度である酸素指数を高めても燃焼後の灰分が柔
らかく、形状を保持できないため、ＶＴＦＴに合格でき
ないという重大な問題がある。
格３８３に規定される垂直トレイ燃焼試験（ＶＴ Ｆ
Ｔ）に合格する高度の難燃性を付与するためには、これ
らの無機系難燃剤を多量に添加する必要がある。この結
果、分散や引張特性の低下を招くだけでなく、材料の難
燃性の尺度である酸素指数を高めても燃焼後の灰分が柔
らかく、形状を保持できないため、ＶＴＦＴに合格でき
ないという重大な問題がある。
本発明はかかる事情に鑑みてなされたものであって、そ
の目的とするところは前記した従来技術の欠点を解消し
、少ない難燃剤の添加量でもってＶＴＦＴに合格できる
新規な難燃性電気絶縁組成物を提供することにある。
の目的とするところは前記した従来技術の欠点を解消し
、少ない難燃剤の添加量でもってＶＴＦＴに合格できる
新規な難燃性電気絶縁組成物を提供することにある。
［問題点を解決するための手段］
本発明の要旨は、難燃助剤としてフリットを用いたこと
にある。
にある。
本発明において、ポリオレフィンとしては、ポリエチレ
ン、エチレン舎プロピレンコポリマー、エチレン拳プロ
ピレン・ジェンターポリマー、エチレン争酢酸ビニルコ
ポリマー、エチレン・エチルアクリレートコポリマー、
エチレン・ブテンコポリマー、エチレン・ブテン・ジェ
ンターポリマーといったものが挙げられ、これらは単独
又は２種以上混合して使用することができる。
ン、エチレン舎プロピレンコポリマー、エチレン拳プロ
ピレン・ジェンターポリマー、エチレン争酢酸ビニルコ
ポリマー、エチレン・エチルアクリレートコポリマー、
エチレン・ブテンコポリマー、エチレン・ブテン・ジェ
ンターポリマーといったものが挙げられ、これらは単独
又は２種以上混合して使用することができる。
無機系難燃剤としては、水酸化アルミニウム、水酸化マ
グネシウム、塩基性炭酸マグネシウム、水酸化カルシウ
ム、ハイドロタルサイト化合物などがある。無機系難燃
剤は、ポリオレフィン１００重量部に対して５００重量
部以上含有せしめる必要があり、５００重量部未満では
難燃性（自消性）の付与が十分でない。一方、３００重
量部を越えると機械的特性が低下する傾向がある。
グネシウム、塩基性炭酸マグネシウム、水酸化カルシウ
ム、ハイドロタルサイト化合物などがある。無機系難燃
剤は、ポリオレフィン１００重量部に対して５００重量
部以上含有せしめる必要があり、５００重量部未満では
難燃性（自消性）の付与が十分でない。一方、３００重
量部を越えると機械的特性が低下する傾向がある。
フリットとしては、数百度の高温では液状に、常温では
固体となる無機質で、かつ均質なガラス質である鉛カリ
フリット、ホウケイ塩酸、ホウケイ酸鉛、ジルコンフリ
ット、チタンフリット、高鉛無アルカリ、高鉛含リチウ
ムストロンチウムフリット、ビスマスホウケイ塩、リン
酸塩フリットなどが挙げられる。フリットはポリオレフ
ィン１００重量部に対して５重量部以上含有せしめる必
要があり、５重量部未満では灰の殻の形成が十分でない
。一方、５０重量部を越えると機械的特性が低下する傾
向がある。
固体となる無機質で、かつ均質なガラス質である鉛カリ
フリット、ホウケイ塩酸、ホウケイ酸鉛、ジルコンフリ
ット、チタンフリット、高鉛無アルカリ、高鉛含リチウ
ムストロンチウムフリット、ビスマスホウケイ塩、リン
酸塩フリットなどが挙げられる。フリットはポリオレフ
ィン１００重量部に対して５重量部以上含有せしめる必
要があり、５重量部未満では灰の殻の形成が十分でない
。一方、５０重量部を越えると機械的特性が低下する傾
向がある。
本発明では、上記成分に加えてりん系化合物（赤りんを
含む）、はう酸亜鉛、フェロセン等の難燃助剤、酸化防
止剤、滑剤、軟化剤、分散剤等を適宜添加してもよい。
含む）、はう酸亜鉛、フェロセン等の難燃助剤、酸化防
止剤、滑剤、軟化剤、分散剤等を適宜添加してもよい。
酸化防止剤としては、フェニル−α−ナフチルアミン、
Ｎ、Ｎ−−ジ−β−ナフチル−ｐ−フェニレンジアミン
等のアミン系酸化防止剤、２，６−ジーｔ−ブチル−４
−メチルフェノール、ヒンダードフェノール、４゜４゛
−チオビス−（６−ｔ−ブチル−４メチルフエノール）
等のフェノール系酸化防止剤等が上げられる。
Ｎ、Ｎ−−ジ−β−ナフチル−ｐ−フェニレンジアミン
等のアミン系酸化防止剤、２，６−ジーｔ−ブチル−４
−メチルフェノール、ヒンダードフェノール、４゜４゛
−チオビス−（６−ｔ−ブチル−４メチルフエノール）
等のフェノール系酸化防止剤等が上げられる。
本発明においては、当該組成物は架橋されていてもよい
。なお、架橋方法としては、架橋剤の添加による加熱架
橋や電子線等の照射による照射架橋がある。また、架橋
剤としてはポリマーに応じたものを使用でき、パーオキ
サイド系、硫黄系、アミン系等が考えられる。
。なお、架橋方法としては、架橋剤の添加による加熱架
橋や電子線等の照射による照射架橋がある。また、架橋
剤としてはポリマーに応じたものを使用でき、パーオキ
サイド系、硫黄系、アミン系等が考えられる。
なお、上記各種成分を含有する難燃性電気絶縁組成物は
シート状、管状、その他の形状に成形され、電気絶縁体
として使用される。
シート状、管状、その他の形状に成形され、電気絶縁体
として使用される。
［作 用］
添加されたフリットが燃焼時（ＶＴＦＴ試験時）の最高
８４θ℃程度の高温により溶融硬化し、ガラス質となっ
て強固な灰の殻が形成され、難燃剤の無機水和物が酸化
物に変化しても、これらのバインダーとして作用し、電
気絶縁体が直接灰にさらされるのを防ぐため、高度の難
燃性を有するものと考えられる。
８４θ℃程度の高温により溶融硬化し、ガラス質となっ
て強固な灰の殻が形成され、難燃剤の無機水和物が酸化
物に変化しても、これらのバインダーとして作用し、電
気絶縁体が直接灰にさらされるのを防ぐため、高度の難
燃性を有するものと考えられる。
［実施例］
表に示す配合割合（重量基準）に従って各種成分を配合
し、１３０℃に調整した１２インチロールで十分に混練
後、１５０°Ｃに保持された４０ｍ／ｍ押出機（Ｌ／Ｄ
−２０）を用い、外径３．０ｍｍの架橋ポリエチレン絶
縁線心を３本より合わせた外周に１．５■厚で押出被覆
して各種ケーブルを作製した。
し、１３０℃に調整した１２インチロールで十分に混練
後、１５０°Ｃに保持された４０ｍ／ｍ押出機（Ｌ／Ｄ
−２０）を用い、外径３．０ｍｍの架橋ポリエチレン絶
縁線心を３本より合わせた外周に１．５■厚で押出被覆
して各種ケーブルを作製した。
各側で得られたケーブルの評価結果は表の下欄に示すと
おりである。
おりである。
なお、評価は次のようにして行った。
引張特性＝２０℃の恒温室に１日放置後、ダンベル３号
で打ち抜き、ショツパー型 引張試験機で２００１ｍ／ｎ＋ｉｎの速度で測定した。
で打ち抜き、ショツパー型 引張試験機で２００１ｍ／ｎ＋ｉｎの速度で測定した。
難燃性：垂直のトレイに２．４ｍの長さのケーブルを外
径の１／２の間隔で８本 並べ、ケーブルの下端６０ｃｍの箇所 を熱ｆｆ１７０． ＯＯＯＢＴＵ／ｎ ｒの炎を２０
分間当てた後バーナを消炎 し、ケーブルが自己消炎すれば合格 とし、１．８ｍ以上の高さまで燃え るときは不合格とした。
径の１／２の間隔で８本 並べ、ケーブルの下端６０ｃｍの箇所 を熱ｆｆ１７０． ＯＯＯＢＴＵ／ｎ ｒの炎を２０
分間当てた後バーナを消炎 し、ケーブルが自己消炎すれば合格 とし、１．８ｍ以上の高さまで燃え るときは不合格とした。
表の評価結果からも明らかなとおり、実施例１〜５では
いずれの特性においても十分満足できる結果が得られた
。しかし、規定値以下のフリットを添加した比較例１で
はＶＴＦＴに不合格であり、難燃剤を３２０部、４００
部と多く添加した比較例２，４及びフリットを６０部と
多く添加した比較例３では押出性が悪く引張特性の低下
が著しかった。
いずれの特性においても十分満足できる結果が得られた
。しかし、規定値以下のフリットを添加した比較例１で
はＶＴＦＴに不合格であり、難燃剤を３２０部、４００
部と多く添加した比較例２，４及びフリットを６０部と
多く添加した比較例３では押出性が悪く引張特性の低下
が著しかった。
Ｃ発明の効果］
以上説明したように本発明によれば、無機系難燃剤を多
量に添加することなく、ＶＴＦＴに合格する高度の難燃
性を有する電気絶縁組成物を得ることができる。
量に添加することなく、ＶＴＦＴに合格する高度の難燃
性を有する電気絶縁組成物を得ることができる。
Claims (1)
- （１）ポリオレフィン１００重量部に対し、無機水和物
５０〜３００重量部及びフリット５〜５０重量部を含有
してなることを特徴とする難燃性電気絶縁組成物。