JP7447826B2 - 蓄電デバイス用外装材、その製造方法、及び蓄電デバイス - Google Patents
蓄電デバイス用外装材、その製造方法、及び蓄電デバイス Download PDFInfo
- Publication number
- JP7447826B2 JP7447826B2 JP2021002908A JP2021002908A JP7447826B2 JP 7447826 B2 JP7447826 B2 JP 7447826B2 JP 2021002908 A JP2021002908 A JP 2021002908A JP 2021002908 A JP2021002908 A JP 2021002908A JP 7447826 B2 JP7447826 B2 JP 7447826B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- scratch
- storage device
- base material
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
少なくとも、耐傷層と、基材保護層と、基材層と、バリア層と、熱融着性樹脂層とをこの順に備える積層体から構成されており、
前記耐傷層は、無機粒子と樹脂とを含んでおり、
前記耐傷層及び前記基材保護層を合わせた平均膜厚は、10μm以下である、蓄電デバイス用外装材。
本開示の蓄電デバイス用外装材10は、例えば図1から図3に示すように、少なくとも、耐傷層7、基材保護層6、基材層1、バリア層3、及び熱融着性樹脂層4を備える積層体から構成されている。蓄電デバイス用外装材10において、耐傷層7が最外層になり、熱融着性樹脂層4は最内層になる。蓄電デバイス用外装材10と蓄電デバイス素子を用いて蓄電デバイスを組み立てる際に、蓄電デバイス用外装材10の熱融着性樹脂層4同士を対向させた状態で、周縁部を熱融着させることによって形成された空間に、蓄電デバイス素子が収容される。
[耐傷層7]
本開示の蓄電デバイス用外装材10は、耐傷性を高めることなどを目的として、外側表面に耐傷層7を有している。耐傷層7は、蓄電デバイス用外装材10を用いて蓄電デバイスを組み立てた時に、蓄電デバイス用外装材10の最外層に位置する層である。
蓄電デバイス用外装材を構成する積層体の耐傷層7及び基材保護層6の平均膜厚は、それぞれ、次のようにして測定・算出する。蓄電デバイス用外装材を構成する積層体の厚み方向の断面について、走査型電子顕微鏡(SEM)を用いて断面画像を取得する。次に、当該断面画像について、耐傷層7及び基材保護層6の断面の面積を、それぞれ、画像解析により測定する。このとき、断面の面積の測定エリアの横の長さ(積層体の厚み方向とは垂直方向の長さ)は25.4μmとする。次に、得られた面積を、当該横の長さ(25.4μm)で除することで、耐傷層7及び基材保護層6の平均膜厚(μm)を、それぞれ、算出する。耐傷層7及び基材保護層6を合わせた合計平均膜厚を測定・算出する際には、同じ測定エリアの耐傷層7及び基材保護層6の断面の面積を同時に測定し、得られた面積を、測定エリアの横の長さ(25.4μm)で除することで、耐傷層7及び基材保護層6を合わせた平均膜厚(μm)を算出する。
装置として、ナノインデンター(例えば、HYSITRON(ハイジトロン)社製の「
TI950 TriboIndenter」)を用いて硬さを測定する。ナノインデンターの圧子としては、Berkovich圧子(例えばTI-0039)を用いる。まず、相対湿度50%、23℃環境において、当該圧子を、蓄電デバイス用外装材の測定対象表面(耐傷層又は基材保護層が露出している面であり、各層の厚み方向と平行な面)に厚み方向とは垂直な方向から当て、10秒間かけて当該表面から荷重50μNまで圧子を押し込み、その状態で5秒間保持し、次に10秒間かけて除荷する。測定箇所をずらして測定したN=5の平均値を硬さとする。なお、圧子を押し込む表面は、蓄電デバイス用外装材の中心部を通るように厚み方向に切断して得られた、測定対象である耐傷層又は基材保護層の断面が露出した部分である。また、耐傷層又は基材保護層の樹脂の硬さの測定において、それぞれ、圧子を押し込む箇所は、表面に粒子が存在していない部分(樹脂部分)である。耐傷層又は基材保護層の粒子の硬さの測定においては、表面に粒子が存在している部分である。切断は、市販品の回転式ミクロトームを用いて行う。
本開示の蓄電デバイス用外装材10は、耐傷層7を備える蓄電デバイス用外装材10の成形性を高めることなどを目的として、耐傷層7と基材層1との間に、基材保護層6を有している。基材保護層6は、耐傷層7及び基材層1と接していることが好ましい。
本開示において、基材層1は、蓄電デバイス用外装材の基材としての機能を発揮させることなどを目的として設けられる層である。基材層1は、蓄電デバイス用外装材10の基材保護層6とバリア層3との間に位置する。
本開示の蓄電デバイス用外装材において、接着剤層2は、基材層1とバリア層3との接着性を高めることを目的として、必要に応じて、これらの間に設けられる層である。
着色層は、基材層1とバリア層3との間に必要に応じて設けられる層である(図示を省略する)。接着剤層2を有する場合には、基材層1と接着剤層2との間、接着剤層2とバリア層3との間に着色層を設けてもよい。また、基材層1の外側に着色層を設けてもよい。着色層を設けることにより、蓄電デバイス用外装材を着色することができる。
蓄電デバイス用外装材において、バリア層3は、少なくとも水分の浸入を抑止する層である。
により、製造される。アミノ化フェノール重合体は、1種単独で又は2種以上混合して使用される。
.0~40mg程度、リン化合物がリン換算で例えば0.5~50mg程度、好ましくは1.0~40mg程度、及びアミノ化フェノール重合体が例えば1.0~200mg程度、好ましくは5.0~150mg程度の割合で含有されていることが望ましい。
ePO4 -などの少なくとも1種)や、例えば、CrとPとOからなる2次イオン(例えば、CrPO2 +、CrPO4 -などの少なくとも1種)に由来するピークが検出される。
本開示の蓄電デバイス用外装材において、熱融着性樹脂層4は、最内層に該当し、蓄電デバイスの組み立て時に熱融着性樹脂層同士が熱融着して蓄電デバイス素子を密封する機能を発揮する層(シーラント層)である。
本開示の蓄電デバイス用外装材において、接着層5は、バリア層3(又は耐酸性皮膜)と熱融着性樹脂層4を強固に接着させるために、これらの間に必要に応じて設けられる層である。
蓄電デバイス用外装材の製造方法については、本開示の蓄電デバイス用外装材が備える各層を積層させた積層体が得られる限り、特に制限されず、外側から順に、少なくとも、耐傷層7と、基材保護層6と、基材層1と、バリア層3と、熱融着性樹脂層4とが積層された積層体を得る工程を備える方法が挙げられる。具体的には、本開示の蓄電デバイス用外装材の製造方法は、少なくとも、耐傷層と、基材保護層と、基材層と、バリア層と、熱融着性樹脂層とがこの順となるように積層して積層体を得る工程を備えており、耐傷層は、無機粒子と樹脂とを含んでおり、耐傷層及び基材保護層を合わせた平均膜厚は、10μm以下である。
本開示の蓄電デバイス用外装材は、正極、負極、電解質等の蓄電デバイス素子を密封して収容するための包装体に使用される。すなわち、本開示の蓄電デバイス用外装材によって形成された包装体中に、少なくとも正極、負極、及び電解質を備えた蓄電デバイス素子を収容して、蓄電デバイスとすることができる。
実施例1
基材層として、延伸ナイロン(ONy)フィルム(厚さ15μm)を準備した。また、バリア層として、アルミニウム箔(JIS H4160:1994 A8021H-O(厚さ35μm))を用意した。次に、バリア層と基材層とを2液型ウレタン接着剤(ポリオール化合物と芳香族イソシアネート系化合物の混合物)を用いてドライラミネート法で積層した後、エージング処理を実施することにより、基材層/接着剤層/バリア層の積層体を作製した。アルミニウム箔の両面には、化成処理が施してある。アルミニウム箔の化成処理は、フェノール樹脂、フッ化クロム化合物、及びリン酸からなる処理液をクロムの塗布量が10mg/m2(乾燥質量)となるように、ロールコート法によりアルミニウム
箔の両面に塗布し、焼付けすることにより行った。
基材保護層の平均膜厚を0.53μm、耐傷層の平均膜厚を1.34μmとしたこと以外は、実施例1と同様にして、外側から順に、耐傷層(平均膜厚1.34μm)/基材保護層(平均膜厚0.53μm)/基材層(15μm)/接着剤層(3μm)/バリア層(35μm)/接着層(20μm)/熱融着性樹脂層(20μm)が積層された積層体を得た。
基材保護層を設けずに、耐傷層を形成する樹脂組成物をグラビア印刷法で2回塗工することによって、耐傷層の平均膜厚を2.53μmとしたこと以外は、実施例1と同様にして、外側から順に、耐傷層(平均膜厚2.53μm)/基材層(15μm)/接着剤層(3μm)/バリア層(35μm)/接着層(20μm)/熱融着性樹脂層(20μm)が積層された積層体を得た。
耐傷層を設けずに、基材保護層を形成する樹脂組成物をグラビア印刷法で2回塗工することによって、基材保護層の平均膜厚を1.54μmとしたこと以外は、実施例1と同様にして、外側から順に、基材保護層(平均膜厚1.54μm)/基材層(15μm)/接着剤層(3μm)/バリア層(35μm)/接着層(20μm)/熱融着性樹脂層(20μm)が積層された積層体を得た。
蓄電デバイス用外装材を構成する積層体の耐傷層及び基材保護層の平均膜厚は、それぞれ、次のようにして測定・算出した。蓄電デバイス用外装材を構成する積層体の厚み方向の断面について、走査型電子顕微鏡(SEM)を用いて下記に示す条件により断面画像を取得した。次に、当該断面画像について、耐傷層及び基材保護層の断面の面積を、それぞれ、画像解析により測定した。このとき、断面の面積の測定エリアの横の長さ(積層体の厚み方向とは垂直方向の長さ)は25.4μmとした。次に、得られた面積を、当該横の長さ(25.4μm)で除することで、耐傷層及び基材保護層の平均膜厚(μm)を、それぞれ、算出した。耐傷層及び基材保護層を合わせた合計平均膜厚を測定・算出する際には、同じ測定エリアの耐傷層及び基材保護層の断面の面積を同時に測定し、得られた面積を、測定エリアの横の長さ(25.4μm)で除することで、耐傷層及び基材保護層を合わせた平均膜厚(μm)を算出した。
(条件)
装置: 日立ハイテクノロジーズ製S-4800
加速電圧:30kV
エミッション電流: 10μA
検出器: 透過電子検出器
傾斜: 無し
観察倍率: 5000倍
断面加工方法:
サンプルを短冊状に切り出し樹脂にて包埋した。樹脂が硬化した後粗く断面作製をして面出しした。その後、ルテニウム酸にて2~3時間染色を行いミクロトームにて超薄切片(厚み:約100nm)を作製した。ナイフはダイヤモンドナイフを使用した。
(SEMの条件)
装置: 日立ハイテクノロジーズ製S-4800
加速電圧:5kV
エミッション電流: 20μA
検出器: 2次電子検出器
傾斜: 無し
観察倍率: 5000倍
観察枚数: 23枚
断面加工方法:サンプルを短冊状に切り出し、プラスチックの板に接着剤で貼り付けた。接着剤が乾燥した後ミクロトームにて断面を作製した。ナイフはダイヤモンドナイフを使用した。また、観察はスキャンを5回ほど行いサンプルにダメージを与えた(電子線によるダメージ)後に、画像を取得した。
装置として、ナノインデンター((HYSITRON(ハイジトロン)社製の「TI9
50 TriboIndenter」)を用いて硬さを測定した。ナノインデンターの圧子としては、Berkovich圧子(TI-0039)を用いた。まず、相対湿度50%、23℃環境において、当該圧子を、蓄電デバイス用外装材の測定対象表面(耐傷層又は基材保護層が露出している面であり、各層の厚み方向と平行な面)に厚み方向とは垂直な方向から当て、10秒間かけて当該表面から荷重50μNまで圧子を押し込み、その状態で5秒間保持し、次に10秒間かけて除荷した。測定箇所をずらして測定したN=5の平均値を硬さとした。結果を表1に示す。なお、圧子を押し込む表面は、蓄電デバイス用外装材の中心部を通るように厚み方向に切断して得られた、測定対象である耐傷層又は基材保護層の断面が露出した部分である。また、耐傷層又は基材保護層の硬さの測定において、それぞれ、圧子を押し込む箇所は、表面に粒子が存在していない部分(樹脂部分)である。耐傷層又は基材保護層の粒子の硬さの測定においては、表面に粒子が存在している部分である。切断は、市販品の回転式ミクロトームを用いて行った。
耐摩耗性評価装置として、学振型摩擦堅牢度試験機AB-301(テスター産業製)を使用した。蓄電デバイス用外装材を摩擦試験機のテーブルに、乾燥した紙製のウェス(日本製紙クレシアのキムワイプ)を摩擦試験機上部のアーム先端(摩擦子:まさつし)にそれぞれ取り付けた。次に、蓄電デバイス用外装材の耐傷層の表面を、ウェスで200回往復摩擦を行った。このとき、往復摩擦の条件は、約500gfの荷重、1往復/秒の条件とし、ウェスには10滴のエタノールを含ませ、50往復毎にエタノール10滴をウェスに追加した。往復摩擦終了後、蓄電デバイス用外装材を耐摩耗性評価装置から取り外して、擦った箇所の状態を目視で確認し、一価の評価基準で評価した。結果を表1に示す。
(評価基準)
A:傷は確認されなかった。
B:傷は確認されたが、傷は10本以下であった。
C:10本を超える傷が確認された。
蓄電デバイス用外装材を裁断して、TDの方向120mm×MDの方向80mmの短冊片を作製し、これを試験サンプルとした。MDの方向31.6×TDの方向54.5mmの矩形状の雄型(表面は、JIS B 0659-1:2002附属書1(参考) 比較
用表面粗さ標準片の表2に規定される、最大高さ粗さ(Rzの呼び値)が1.6μmである。コーナーR2.0mm、稜線R1.0mm)とこの雄型とのクリアランスが0.3mmの雌型(表面は、JIS B 0659-1:2002附属書1(参考) 比較用表面
粗さ標準片の表2に規定される、最大高さ粗さ(Rzの呼び値)が3.2μmである。コーナーR2.0mm、稜線R1.0mm)からなるストレート金型を用い、雄型側にシーラント層側が位置するように雌型上に上記試験サンプルを載置し、試験サンプルを0.1MPaの押え圧(面圧)で押えて、冷間成形(引き込み1段成形)した。成形後の試験サンプルの凹部のコーナー部を走査型電子顕微鏡で最外層(実施例1,2及び比較例1は耐傷層であり、比較例2は基材保護層)を観察して、成形性を以下の規準で評価した。結果を表1に示す。
(評価基準)
A:割れは確認されなかった。
B:割れは確認されたが、基材層は露出していなかった。
C:割れが確認され、基材層が露出していた。
項1. 少なくとも、耐傷層と、基材保護層と、基材層と、バリア層と、熱融着性樹脂層とをこの順に備える積層体から構成されており、
前記耐傷層は、無機粒子と樹脂とを含んでおり、
前記耐傷層及び前記基材保護層を合わせた平均膜厚は、10μm以下である、蓄電デバイス用外装材。
項2. 前記耐傷層には、前記耐傷層の平均膜厚よりも粒子径の大きな粒子が含まれている、項1に記載の蓄電デバイス用外装材。
項3. 前記基材保護層には、前記基材保護層の平均膜厚よりも粒子径の大きな粒子が含まれている、項1又は2に記載の蓄電デバイス用外装材。
項4. 前記耐傷層及び前記基材保護層の厚み方向の断面について、走査型電子顕微鏡で観察される前記大きな粒子の粒子径が、1.0μm以上5.0μm以下である、項2又は3に記載の蓄電デバイス用外装材。
項5. 23℃環境において、それぞれ、前記耐傷層の厚み方向の断面の前記大きな粒子及び前記樹脂について、ナノインデンテーション法により硬さを測定した場合に、前記大きな粒子の硬さが前記樹脂の硬さよりも大きい、項2~4のいずれか1項に記載の蓄電デバイス用外装材。
項6. 前記大きな粒子の硬さと、前記樹脂の硬さとの差が、100MPa以上である、項2~5のいずれか1項に記載の蓄電デバイス用外装材。
項7. 23℃環境において、前記耐傷層の厚み方向の断面の前記大きな粒子について、ナノインデンテーション法により測定される硬さが、400MPa以上である、項2~6のいずれか1項に記載の蓄電デバイス用外装材。
項8. 前記大きな粒子は、有機粒子である、項2~7のいずれか1項に記載の蓄電デバイス用外装材。
項9. 前記耐傷層及び前記基材保護層には、それぞれ異なる樹脂が含まれている、項1~8のいずれか1項に記載の蓄電デバイス用外装材。
項10. 23℃環境において、それぞれ、前記耐傷層及び前記基材保護層の厚み方向の断面について、ナノインデンテーション法により硬さを測定した場合に、前記耐傷層の樹脂の硬さが、前記基材保護層の樹脂の硬さよりも大きい、項1~9のいずれか1項に記載の蓄電デバイス用外装材。
項11.
前記耐傷層の樹脂の硬さと、前記基材保護層の樹脂の硬さとの差が、100MPa以上である、項10に記載の蓄電デバイス用外装材。
項12. 23℃環境において、前記耐傷層の厚み方向の断面について、ナノインデンテーション法により測定される樹脂の硬さが、150MPa以上である、項1~11のいずれか1項に記載の蓄電デバイス用外装材。
項13. 23℃環境において、前記基材保護層の厚み方向の断面について、ナノインデンテーション法により測定される樹脂の硬さが、150MPa以下である、項1~12のいずれか1項に記載の蓄電デバイス用外装材。
項14. 前記耐傷層の前記無機粒子が、シリカ粒子である、項1~13のいずれか1項に記載の蓄電デバイス用外装材。
項15. 前記基材保護層は、無機粒子と樹脂とを含んでいる、項1~14のいずれか1項に記載の蓄電デバイス用外装材。
項16. 前記基材保護層の前記無機粒子が、硫酸バリウムである、項15に記載の蓄電デバイス用外装材。
項17. 前記耐傷層の平均膜厚が、2.5μm以下である、項1~16のいずれか1項に記載の蓄電デバイス用外装材。
項18. 前記基材保護層の平均膜厚が、2.0μm以下である、項1~17のいずれか1項に記載の蓄電デバイス用外装材。
項19. 少なくとも、耐傷層と、基材保護層と、基材層と、バリア層と、熱融着性樹脂層とがこの順となるように積層して積層体を得る工程を備えており、
前記耐傷層は、無機粒子と樹脂とを含んでおり、
前記耐傷層及び前記基材保護層を合わせた平均膜厚は、10μm以下である、蓄電デバイス用外装材の製造方法。
項20. 少なくとも正極、負極、及び電解質を備えた蓄電デバイス素子が、項1~18のいずれか1項に記載の蓄電デバイス用外装材により形成された包装体中に収容されている、蓄電デバイス。
2 接着剤層
3 バリア層
4 熱融着性樹脂層
5 接着層
6 基材保護層
7 耐傷層
10 蓄電デバイス用外装材
61,71 無機粒子
62,72 有機粒子
Claims (28)
- 少なくとも、耐傷層と、基材保護層(但し、水溶性多糖類を含有するものを除く。)と、基材層と、バリア層と、熱融着性樹脂層とをこの順に備える積層体から構成されており、
前記耐傷層は、無機粒子と樹脂とを含んでおり、
前記耐傷層及び前記基材保護層を合わせた平均膜厚は、10μm以下であり、
前記耐傷層には、前記耐傷層の平均膜厚よりも粒子径の大きな粒子が含まれている、蓄電デバイス用外装材。 - 少なくとも、耐傷層と、基材保護層(但し、水溶性多糖類を含有するものを除く。)と、基材層と、バリア層と、熱融着性樹脂層とをこの順に備える積層体から構成されており、
前記耐傷層は、無機粒子と樹脂とを含んでおり、
前記耐傷層及び前記基材保護層を合わせた平均膜厚は、10μm以下であり、
前記基材保護層には、前記基材保護層の平均膜厚よりも粒子径の大きな粒子が含まれている、蓄電デバイス用外装材。 - 前記耐傷層には、前記耐傷層の平均膜厚よりも粒子径の大きな粒子が含まれている、請求項2に記載の蓄電デバイス用外装材。
- 23℃環境において、それぞれ、前記耐傷層の厚み方向の断面の前記大きな粒子及び前記樹脂について、ナノインデンテーション法により硬さを測定した場合に、前記大きな粒子の硬さが前記樹脂の硬さよりも大きい、請求項1又は3に記載の蓄電デバイス用外装材。
- 前記耐傷層の前記大きな粒子の硬さと、前記耐傷層の前記樹脂の硬さとの差が、100MPa以上である、請求項1,3,4のいずれか1項に記載の蓄電デバイス用外装材。
- 23℃環境において、前記耐傷層の厚み方向の断面の前記大きな粒子について、ナノインデンテーション法により測定される硬さが、400MPa以上である、請求項1,3~5のいずれか1項に記載の蓄電デバイス用外装材。
- 前記耐傷層及び前記基材保護層の厚み方向の断面について、走査型電子顕微鏡で観察される前記大きな粒子の粒子径が、1.0μm以上5.0μm以下である、請求項1~6のいずれか1項に記載の蓄電デバイス用外装材。
- 前記大きな粒子は、有機粒子である、請求項1~7のいずれか1項に記載の蓄電デバイス用外装材。
- 前記耐傷層及び前記基材保護層には、それぞれ異なる樹脂が含まれている、請求項1~8のいずれか1項に記載の蓄電デバイス用外装材。
- 23℃環境において、それぞれ、前記耐傷層及び前記基材保護層の厚み方向の断面について、ナノインデンテーション法により硬さを測定した場合に、前記耐傷層の樹脂の硬さが、前記基材保護層の樹脂の硬さよりも大きい、請求項1~9のいずれか1項に記載の蓄電デバイス用外装材。
- 前記耐傷層の樹脂の硬さと、前記基材保護層の樹脂の硬さとの差が、100MPa以上である、請求項10に記載の蓄電デバイス用外装材。
- 23℃環境において、前記耐傷層の厚み方向の断面について、ナノインデンテーション法により測定される樹脂の硬さが、150MPa以上である、請求項1~11のいずれか1項に記載の蓄電デバイス用外装材。
- 23℃環境において、前記基材保護層の厚み方向の断面について、ナノインデンテーション法により測定される樹脂の硬さが、150MPa以下である、請求項1~12のいずれか1項に記載の蓄電デバイス用外装材。
- 前記耐傷層の前記無機粒子が、シリカ粒子である、請求項1~13のいずれか1項に記載の蓄電デバイス用外装材。
- 前記基材保護層は、無機粒子と樹脂とを含んでいる、請求項1~14のいずれか1項に記載の蓄電デバイス用外装材。
- 前記基材保護層の前記無機粒子が、硫酸バリウムである、請求項15に記載の蓄電デバイス用外装材。
- 前記耐傷層の平均膜厚が、2.5μm以下である、請求項1~16のいずれか1項に記載の蓄電デバイス用外装材。
- 前記基材保護層の平均膜厚が、2.0μm以下である、請求項1~17のいずれか1項に記載の蓄電デバイス用外装材。
- 前記蓄電デバイス用外装材が、着色されている、請求項1~18のいずれか1項に記載の蓄電デバイス用外装材。
- 前記基材層と前記バリア層との間に接着剤層を備え、
前記接着剤層が、着色剤を含む、請求項1~19のいずれか1項に記載の蓄電デバイス用外装材。 - 前記基材層と前記バリア層との間に着色層を備える、請求項1~20のいずれか1項に記載の蓄電デバイス用外装材。
- 前記バリア層は、アルミニウム合金箔及びステンレス鋼箔の少なくとも一方を含む、請求項1~21のいずれか1項に記載の蓄電デバイス用外装材。
- 前記バリア層と前記熱融着性樹脂層との間に接着層を備えており、
前記接着層の厚さが、20μm以下であるか、
前記接着層の厚さが、20μm超50μm以下である、請求項1~22のいずれか1項に記載の蓄電デバイス用外装材。 - 前記バリア層と前記熱融着性樹脂層との間に接着層を備えており、
前記接着層は、酸変性ポリオレフィンと、イソシアネート基を有する化合物、オキサゾリン基を有する化合物、及びエポキシ基を有する化合物からなる群より選択される少なくとも1種と、を含む樹脂組成物の硬化物である、請求項1~23のいずれか1項に記載の蓄電デバイス用外装材。 - 前記バリア層と前記熱融着性樹脂層との間に接着層を備えており、
前記接着層は、ポリウレタン、ポリエステル、及びエポキシ樹脂からなる群より選択される少なくとも1種を含む、請求項1~24のいずれか1項に記載の蓄電デバイス用外装材。 - 少なくとも、耐傷層と、基材保護層(但し、水溶性多糖類を含有するものを除く。)と、基材層と、バリア層と、熱融着性樹脂層とがこの順となるように積層して積層体を得る工程を備えており、
前記耐傷層は、無機粒子と樹脂とを含んでおり、
前記耐傷層及び前記基材保護層を合わせた平均膜厚は、10μm以下であり、
前記耐傷層には、前記耐傷層の平均膜厚よりも粒子径の大きな粒子が含まれている、蓄電デバイス用外装材の製造方法。 - 前記バリア層と前記熱融着性樹脂層との間に接着層を備えており、
前記接着層と前記熱融着性樹脂層とは、共押出しラミネート法、タンデムラミネート法、サーマルラミネート法、サンドイッチラミネート法、又は、前記バリア層上に前記接着層を形成させるための接着剤を積層させ、前記接着層上に予めシート状に製膜した前記熱融着性樹脂層を積層する方法により積層する、請求項26に記載の蓄電デバイス用外装材の製造方法。 - 少なくとも正極、負極、及び電解質を備えた蓄電デバイス素子が、請求項1~25のいずれか1項に記載の蓄電デバイス用外装材により形成された包装体中に収容されている、蓄電デバイス。