JP7409853B2 - 布帛および防護製品 - Google Patents
布帛および防護製品 Download PDFInfo
- Publication number
- JP7409853B2 JP7409853B2 JP2019222965A JP2019222965A JP7409853B2 JP 7409853 B2 JP7409853 B2 JP 7409853B2 JP 2019222965 A JP2019222965 A JP 2019222965A JP 2019222965 A JP2019222965 A JP 2019222965A JP 7409853 B2 JP7409853 B2 JP 7409853B2
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- fiber
- weight
- aromatic polyamide
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このような電気的アークやフラッシュ火災に対する防護のために各種の難燃性繊維を用いた布帛が提案されている(例えば特許文献1~12参照)。
上を加えた付加価値の高い布帛も求められている。
また、例えば、特許文献12のように、快適性の向上のため通気性に主眼を置いた布帛が提案されているが、アーク防護性能が不十分であった。
本発明の布帛は、難燃性繊維を含む経糸と緯糸から構成される織物組織を有し、耐アーク性試験ASTM F1959-1999に規定されるATPV値が8.0cal/cm2以上であり、下記式にて定義されるカバーファクター(CF)が1700~3500(より好ましくは2000~3200)であり、JIS L 1096:2010 A法(フラジール法)に規定される通気度が10~100cc/cm2・sec(より好ましくは、10~50cc/cm2・sec)である。
CF=(DWp/1.1)1/2×MWp+(DWf/1.1)1/2×MWf
[DWpは経糸総繊度(dtex)、MWpは経糸織密度(本/2.54cm)、DWfは緯糸総繊度(dtex)、MWfは緯糸織密度(本/2.54cm)である。]
上記範囲にすることで、布帛を衣類として用いた際に、電気的アーク事故やフラッシュ火災に遭った際に、人体へ到達する熱エネルギーを効率的に抑制することができ、電気的アークに対する防護性能に優れ、かつ、通気性に優れた布帛を得ることができる。
ここで、Ar1はメタ配位または平行軸方向以外に結合基を有する2価の芳香族基である。
H2N-Ar2-Y-Ar2-NH2・・・式(3)
XOC-Ar3-COX・・・式(4)
XOC-Ar3-Y-Ar3-COX・・・式(5)
ここで、Ar2はAr1とは異なる2価の芳香族基、Ar3はAr1とは異なる2価の芳香族基、Yは酸素原子、硫黄原子、アルキレン基からなる群から選ばれる少なくとも1種の原子または官能基であり、Xはハロゲン原子を表す。
紡糸装置は、特に限定されるものではなく、従来公知の湿式紡糸装置を使用することができる。また、安定して湿式紡糸できるものであれば、紡糸口金の紡糸孔数、配列状態、孔形状などは特に制限する必要はなく、例えば、孔数が1000~30000個、紡糸孔径が0.05~0.2mmのスフ用の多ホール紡糸口金などを用いてもよい。
(1)ATPV値
耐アーク性試験ASTMF1959-1999によりATPV値を測定した。8.0cal/cm2以上を合格(レベル2クリア)とした。
(2)カバーファクター(CF)
CF=(DWp/1.1)1/2×MWp+(DWf/1.1)1/2×MWf
[DWpは経糸総繊度(dtex)、MWpは経糸織密度(本/2.54cm)、DWfは緯糸総繊度(dtex)、MWfは緯糸織密度(本/2.54cm)である。]
(3)通気度
JIS L 1096:2010 A法(フラジール法)により通気性を測定した。
(4)織物の厚み
JIS L 1096:2010に従って測定した。
(5)織物の目付
JIS L 1096:2010 A法に従って測定した。
メタ型全芳香族ポリアミド繊維(帝人(株)製、「TeijinconexNEO」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)、パラ型全芳香族ポリアミド繊維(帝人アラミド社製、「トワロン」(登録商標)、単繊維繊度1.7dtex、繊維長50mm)、導電繊維として導電性アクリル繊維(単繊維繊度3.3dtex、繊維長38mm)を用い、メタ型全芳香族ポリアミド繊維:93重量%、パラ型全芳香族ポリアミド繊維:5重量%、導電性アクリル繊維:2重量%となるように、撚り数24.0回/2.54cm(撚り方向Z)で綿番手40/1の紡績糸を作り、次いで、撚り数24.0回/2.54cm(撚り方向S)で双糸合撚加工糸条を得た。
メタ型全芳香族ポリアミド繊維(帝人(株)製、「TeijinconexNEO」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)、パラ型全芳香族ポリアミド繊維(帝人アラミド社製、「トワロン」(登録商標)、単繊維繊度1.7dtex、繊維長50mm)、導電繊維として導電性アクリル繊維(単繊維繊度3.3dtex、繊維長38mm)を用い、メタ型全芳香族ポリアミド繊維:85重量%、パラ型全芳香族ポリアミド繊維:5重量%、導電性アクリル繊維:10重量%となるように、撚り数22.2回/2.54cm(撚り方向Z)で綿番手36/1の紡績糸を作り、次いで、撚り数22.2回/2.54cm(撚り方向S)で双糸合撚加工糸条を得た。
メタ型全芳香族ポリアミド繊維(帝人(株)製、「TeijinconexNEO」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)、パラ型全芳香族ポリアミド繊維(帝人アラミド社製、「トワロン」(登録商標)、単繊維繊度1.7dtex、繊維長50mm)、導電繊維として導電性アクリル繊維(単繊維繊度3.3dtex、繊維長38mm)を用い、メタ型全芳香族ポリアミド繊維:85重量%、パラ型全芳香族ポリアミド繊維:5重量%、導電性アクリル繊維:10重量%となるように、撚り数20.3回/2.54cm(撚り方向Z)で綿番手30/1の紡績糸を作り、次いで、撚り数20.3回/2.54cm(撚り方向S)で双糸合撚加工糸条を得た。
経糸用として、メタ型全芳香族ポリアミド繊維(帝人(株)製、「TeijinconexNEO」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)、パラ型全芳香族ポリアミド繊維(帝人アラミド社製、「トワロン」(登録商標)、単繊維繊度1.7dtex、繊維長50mm)、赤外線吸収剤および導電剤を含む繊維として導電性アクリル繊維、単繊維繊度3.3dtex、繊維38mm、鞘部:アクリル/芯部:金属化合物の偏心芯鞘型導電性アクリル繊維)を用い、メタ型全芳香族ポリアミド繊維:80重量%、パラ型全芳香族ポリアミド繊維:5重量%、導電性アクリル繊維:15重量%となるように、撚り数23.4回/2.54cm(撚り方向Z)で綿番手40/1の紡績糸を作り、次いで、撚り数23.4回/2.54cm(撚り方向S)で双糸合撚加工糸条(A)を得た。
経糸用として、実施例4と同様にして、双糸合撚加工糸条(A)を得た。また、緯糸用として、カーボン粒子を5.0%練り込んだパラ型全芳香族ポリアミド繊維(帝人(株)製、「テクノーラ」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)を用い、撚り数23.4回/2.54cm(撚り方向Z)で綿番手40/1の紡績糸を作り、次いで、撚り数23.4回/2.54cm(撚り方向S)で双糸合撚加工糸条(B)を得た。
経糸用として、実施例4と同様にして、双糸合撚加工糸条(A)を得た。また、緯糸用として、炭素繊維(東邦テナックス(株)製、「パイロメックスCPX」(登録商標)、単繊維繊度2.2dtex、繊維長51mm)、メタ型全芳香族ポリアミド繊維(帝人(株)製、「TeijinconexNEO」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)、パラ型全芳香族ポリアミド繊維(帝人アラミド社製、「トワロン」(登録商標)、単繊維繊度1.7dtex、繊維長50mm)を用い、炭素繊維:50%、メタ型全芳香族ポリアミド繊維:45重量%、パラ型全芳香族ポリアミド繊維:5重量%となるように、撚り数23.4回/2.54cm(撚り方向Z)で綿番手40/1の紡績糸を作り、次いで、撚り数23.4回/2.54cm(撚り方向S)で双糸合撚加工糸条(B)を得た。
経糸用として、実施例4と同様にして、双糸合撚加工糸条(A)を得た。また、緯糸用として、カーボン粒子を14%練り込んだパラ型全芳香族ポリアミド繊維(帝人(株)製、「テクノーラ」(登録商標)、単繊維繊度2.8dtex、繊維長51mm)100重量%を、撚り数20.3回/inch(撚り方向Z)で綿番手30/1の紡績糸を作り、次いで、撚り数20.3回/inch(撚り方向S)で双糸合撚加工糸条(B)を得た。
緯糸用として、実施例4と同様にして、双糸合撚加工糸条(A)を得た。経糸用として、カーボン粒子を5.0%練り込んだパラ型全芳香族ポリアミド繊維(帝人(株)製、「テクノーラ」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)100重量%を用い、撚り数20.3回/2.54cm(撚り方向Z)で綿番手30/1の紡績糸を作り、次いで、撚り数20.3回/2.54cm(撚り方向S)で双糸合撚加工糸条(B)を得た。
メタ型全芳香族ポリアミド繊維(帝人(株)製、「TeijinconexNEO」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)、パラ型全芳香族ポリアミド繊維(帝人アラミド社製、「トワロン」(登録商標)、単繊維繊度1.7dtex、繊維長50mm)、導電繊維として導電性アクリル繊維(単繊維繊度3.3dtex、繊維長38mm)を用い、メタ型全芳香族ポリアミド繊維:85重量%、パラ型全芳香族ポリアミド繊維:5重量%、導電性アクリル繊維:10重量%となるように、撚り数20.3回/2.54cm(撚り方向Z)で綿番手30/1の紡績糸を作り、次いで、撚り数20.3回/2.54cm(撚り方向S)で双糸合撚加工糸条を得た。
経糸用として、メタ型全芳香族ポリアミド繊維(帝人(株)製、「TeijinconexNEO」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)、パラ型全芳香族ポリアミド繊維(帝人アラミド社製、「トワロン」(登録商標)、単繊維繊度1.7dtex、繊維長50mm)を用い、メタ型全芳香族ポリアミド繊維:95重量%、パラ型全芳香族ポリアミド繊維:5重量%となるように、撚り数23.4回/inch(撚り方向Z)で綿番手40/1の紡績糸を作り、次いで、撚り数23.4回/inch(撚り方向S)で双糸合撚加工糸条(A)を得た。
双糸合撚加工糸条(A)を経糸、双糸合撚加工糸条(B)を緯糸に用いて、綾織(2/1綾組織)にて、経密度72本/2.54cm、緯密度50本/2.54cmの織物を製織した。
経糸用として、実施例4と同様にして、双糸合撚加工糸条(A)を得た。また、緯糸用として、経糸用の双糸合撚加工糸条(A)と同じ構成にて、双糸合撚加工糸条(B)を得た。
経糸用として、実施例4と同様にして、双糸合撚加工糸条(A)を得た。緯糸用として、カーボン粒子を4.0%練り込んだパラ型全芳香族ポリアミド繊維(帝人(株)製、「テクノーラ」(登録商標)、単繊維繊度1.7dtex、繊維長51mm)100重量%を、撚り数20.3回/inch(撚り方向Z)で綿番手30/1の紡績糸を作り、次いで、撚り数20.3回/inch(撚り方向S)で双糸合撚加工糸条(B)を得た。
Claims (5)
- 綿番手30/1~36/1でありメタ型全芳香族ポリアミド繊維60~87重量%およびパラ型全芳香族ポリアミド繊維3~10重量%を含む紡績糸を含み、経糸と緯糸から構成される織物組織を有し、耐アーク性試験ASTM F1959-1999に規定されるATPV値が8.0cal/cm2以上であり、下記式に定義するカバーファクター(CF)が1700~3500であり、JIS L 1096:2010 A法(フラジール法)に規定される通気度が66~100cc/cm2・secであることを特徴とする布帛。
CF=(DWp/1.1) 1/2 ×MWp+(DWf/1.1) 1/2 ×MWf
[DWpは経糸総繊度(dtex)、MWpは経糸織密度(本/2.54cm)、DW
fは緯糸総繊度(dtex)、MWfは緯糸織密度(本/2.54cm)である。] - 布帛のJIS L 1096:2010 A法に規定される目付けが120~260g/m2である、請求項1に記載の布帛。
- JIS L 1096:2010に規定される布帛の厚みが0.4~0.8mmである、請求項1または2に記載の布帛。
- 布帛が多層構造を有する、請求項1から3のいずれか1つに記載の布帛。
- 請求項1から4のいずれか1つに記載の布帛を用いてなる、アーク防護服、防炎防護服、作業服、活動服、手袋、防護用エプロン、および防護用部材からなる群より選択されるいずれかの防護製品。