JP7396893B2 - タイヤトレッド用ゴム組成物、及びそれを用いた空気入りタイヤ - Google Patents
タイヤトレッド用ゴム組成物、及びそれを用いた空気入りタイヤ Download PDFInfo
- Publication number
- JP7396893B2 JP7396893B2 JP2019239128A JP2019239128A JP7396893B2 JP 7396893 B2 JP7396893 B2 JP 7396893B2 JP 2019239128 A JP2019239128 A JP 2019239128A JP 2019239128 A JP2019239128 A JP 2019239128A JP 7396893 B2 JP7396893 B2 JP 7396893B2
- Authority
- JP
- Japan
- Prior art keywords
- vulcanization accelerator
- rubber composition
- parts
- sulfur
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
窒素置換された耐熱反応容器に、シクロヘキサンを2.5L、テトラヒドロフラン(THF)を50g、n-ブチルリチウムを0.12g、スチレンを100g、1,3-ブタジエンを400g入れ、反応温度50℃で重合を行った。重合が完了した後にN,N-ビス(トリメチルシリル)アミノプロピルメチルジエトキシランを1.7g加えて、1時間反応させた後、水素ガスを0.4MPa-ゲージの圧力で供給し、20分間撹拌した。次いで、水素ガス供給圧力を0.7MPa-ゲージ、反応温度を90℃とし、チタノセンジクロリドを主とした触媒を用いて目的の水素添加率となるまで反応させ、溶媒を除去することにより、水添共重合体1を得た。
バンバリーミキサーを使用し、下記表1に示す配合(質量部)に従い、まず、第一混合段階(ノンプロ練り工程)で、加硫促進剤及び硫黄を除く成分を添加混合し(排出温度=160℃)、次いで、得られた混合物に、最終混合段階(プロ練り工程)で、加硫促進剤及び硫黄を添加混合して(排出温度=90℃)、ゴム組成物を調製した。
・水添SBR1:上記合成例1に従い作製した水添共重合体1
・シリカ:エボニックジャパン社製「UltrasilVN3」
・シランカップリング剤:エボニックジャパン社製「Si69」
・カーボンブラック:東海カーボン(株)製「シースト3」
・オイル:JXTGエネルギー(株)製「NC-140」
・酸化亜鉛:三井金属鉱業(株)製「酸化亜鉛2種」
・老化防止剤:住友化学(株)製「アンチゲン6C」
・ステアリン酸:花王(株)製「ルナックS-20」
・ワックス:日本精蝋(株)製「OZOACE0355」
・硫黄:鶴見化学工業(株)製「微粉末硫黄」
・加硫促進剤1:N-シクロヘキシル-2-ベンゾチアゾリルスルフェンアミド(CZ)、住友化学(株)製「ソクシノールCZ」、スルフェンアミド系加硫促進剤
・加硫促進剤2:大内新興化学工業(株)製「ノクセラ-D」、グアニジン系加硫促進剤
・加硫促進剤3:三新化学工業(株)製「サンセラーZBE」、ジチオカルバミン酸塩系加硫促進剤
Claims (3)
- 芳香族ビニル-共役ジエン共重合体が水素添加された水添共重合体であって、ゲル浸透クロマトグラフィーにより測定された重量平均分子量が30万以上であり、共役ジエン部の水素添加率が80モル%以上である水添共重合体を70~100質量部含むゴム成分100質量部に対して、
硫黄3~10質量部と、
スルフェンアミド系加硫促進剤とを含有し、
スルフェンアミド系加硫促進剤と硫黄との含有割合(スルフェンアミド系加硫促進剤/硫黄)が、質量比で0.05~0.3である、タイヤトレッド用ゴム組成物。 - 前記スルフェンアミド系加硫促進剤が、N-シクロヘキシル-2-ベンゾチアゾリルスルフェンアミドである、請求項1に記載のタイヤトレッド用ゴム組成物。
- 請求項1又は2に記載のタイヤトレッド用ゴム組成物を用いて作製した、空気入りタイヤ。