JP6412532B2 - 塗装金属板の製造方法 - Google Patents
塗装金属板の製造方法 Download PDFInfo
- Publication number
- JP6412532B2 JP6412532B2 JP2016193211A JP2016193211A JP6412532B2 JP 6412532 B2 JP6412532 B2 JP 6412532B2 JP 2016193211 A JP2016193211 A JP 2016193211A JP 2016193211 A JP2016193211 A JP 2016193211A JP 6412532 B2 JP6412532 B2 JP 6412532B2
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- condensate
- composition
- organosilicate
- metal plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]金属板の表面に、オルガノシリケートの縮合物であるオルガノシリケートの縮合物を含む組成物を塗布および硬化させて塗膜を形成する工程と、前記塗膜にフレーム処理を行う工程と、を有し、前記オルガノシリケートの縮合物中のアルコキシ基の総数に対するエトキシ基の数の割合が50%以上である、塗装金属板の製造方法。
[3]前記組成物が、ポリエステル樹脂またはアクリル樹脂をさらに含む、[1]または[2]に記載の塗装金属板の製造方法。
[4]前記オルガノシリケートの縮合物の重量平均分子量が700以上である、[1]〜[3]のいずれかに記載の塗装金属板の製造方法。
本工程では、金属板に、オルガノシリケートの縮合物を含む組成物を塗布し、これを硬化させて塗膜を得る。金属板の表面に組成物を塗布する方法は特に制限されず、公知の方法から適宜選択することが可能である。組成物の塗布方法の例には、ロールコート法や、カーテンフロー法、スピンコート法、エアースプレー法、エアーレススプレー法および浸漬引き上げ法が含まれる。これらの中でも、ロールコート法が効率よく、所望の厚みを有する塗膜を得やすいとの観点から好ましい。
Si−(OR)4 (1)
上記一般式(1)において、Rはそれぞれ独立に、炭素数1〜10の炭化水素基を表し、複数のRは同一であってもよく、異なっていてもよい。
本工程では、前述のオルガノシリケート縮合物を含む組成物の塗膜に、フレーム処理を行う。前述のオルガノシリケート縮合物を含む塗膜をフレーム処理することで、塗膜表面のオルガノシリケート縮合物を加水分解し、塗膜表面にシラノール基やシロキサン結合を生じさせることができる。また、フレーム処理によれば、塗膜表面全体をムラなく親水化できる。したがって、前述のように、塗膜表面の親水性を十分に高めることができる。
板厚0.27mm、A4サイズ、片面当りめっき付着量90g/m2の溶融Zn−55%Al合金めっき鋼板を金属板として準備し、表面をアルカリ脱脂した。その後、当該表面に、塗布型クロメート処理液(日本ペイント株式会社製 NRC300NS)を、Crの付着量が50mg/m2となるように塗布した。さらに、エポキシ樹脂系プライマー塗料(日本ファインコーティングス株式会社製 700P)を、乾燥膜厚が5μmとなるようにロールコーターで塗布した。続いて、基材の最高到達板温215℃となるように焼き付け、プライマー塗膜を形成しためっき鋼板(以下、単に「めっき鋼板」とも称する)を得た。
2−1.材料の準備
オルガノシリケート縮合物は、それぞれ以下の市販品、もしくはその変性物を使用した。
[メチルシリケート縮合物]
・メチルシリケート53A(コルコート株式会社製、テトラメトキシシランの縮合物) 重量平均分子量(Mw):840、数平均分子量(Mn):610
・メチルシリケートMS57(三菱化学株式会社製、テトラメトキシシランの縮合物) 重量平均分子量(Mw):1400、数平均分子量(Mn):810
・メチルシリケート51(コルコート株式会社製、テトラメトキシシランの縮合物)重量平均分子量(Mw):590、数平均分子量(Mn):470
[エチルシリケート縮合物]
・エチルシリケート40(コルコート株式会社製、テトラエトキシシランの縮合物)重量平均分子量(Mw):650、数平均分子量(Mn):430
・シリケート40(多摩化学工業株式会社製、テトラエトキシシランの縮合物) 重量平均分子量(Mw):930、数平均分子量(Mn):500
・エチルシリケート48(コルコート株式会社製、テトラエトキシシランの縮合物) 重量平均分子量(Mw):1300、数平均分子量(Mn):850
・エトキシ部分置換メチルシリケート縮合物は、以下に示す方法で、メチルシリケートとエタノールとを反応させることにより、合成した。当該エトキシ部分置換メチルシリケート縮合物中のアルコキシ基の総数に対する、エトキシ基の数の割合は、1H−NMRおよび13C−NMRのシグナル値(積分値)から算出した。1H−NMR測定には、日本電子株式会社製のEX400型を用い、13C−NMR測定には、日本電子株式会社製のAL400型を用いた。
メチルシリケートMS56(三菱化学株式会社製 重量平均分子量1,100、テトラメトキシシランの縮合物)100g(80mmol)に、エタノールに14.72g(320mmol)およびトリエチルアミン0.211g(2mmol)を加えた。系中でメタノールの生成状況を観察しながら、80℃で0.5〜1時間、100℃で1〜2時間、120℃で1〜3時間窒素気流中で加熱攪拌した。メタノールは100℃昇温後に流出しはじめた。エトキシ基の置換率は流出するメタノールの量から予測した。反応終了後に放冷し、一夜放置後、約670Pa、50〜55℃で3時間濃縮し、さらに、133Pa以下で5時間濃縮した。これにより、エトキシ部分置換メチルシリケート縮合物中のアルコキシ基の総数に対するエトキシ基の数の割合がそれぞれ表1および表2に示す値(20%、21%、46%、47%、53%、54%、73%、74%)である、エトキシ部分置換メチルシリケート縮合物を得た。
数平均分子量5,000、ガラス転移温度30℃、水酸基価28mgKOH/gの高分子ポリエステル樹脂(DIC株式会社製)と、メトキシ基90モル%のメチル化メラミン樹脂(三井サイテック製 サイメル303)とを混合し、ベースとなるポリエステル樹脂/メラミン塗料を得た。ポリエステル樹脂とメチル化メラミン樹脂との配合比は70/30とした。
得られた組成物中の水分量を、カールフィシャー法により測定したところ、0.46wt%であった。
アクリル樹脂(株式会社日本触媒製 アロセット5534−SB60)37.85質量部(固形分量)、平均粒径0.28μmの酸化チタン顔料(テイカ株式会社製 JR−603)37.85質量部、シクロヘキサノン10質量部、およびブタノール25質量部を混合し、ビーズミルで混練した。その後、硬化剤として、メラミン樹脂(DIC株式会社製 スーパーベッカミンL−155−70)15.06質量部(固形分量)を加え、ベースとなるアクリル樹脂塗料を調製した。
さらに、表1および表2に示すオルガノシリケート縮合物を、組成物の総固形分量に対して5質量%となるように添加した。また、表1および表2に示す脱水剤(オルト酢酸トリメチルまたはオルトギ酸トリエチル)を、組成物の総固形分量に対して5質量%添加した。得られた組成物中の水分量を、カールフィシャー法により測定したところ、0.41wt%であった。
3−1.フレーム処理(実施例1〜15、および比較例7〜11、18、19、23、24、28、および29)
上述の塗膜を形成しためっき鋼板を、株式会社東上熱学製 自動排出型乾燥器(型式 ATO−101)を用いて、設定温度80℃、風速2.0m/sの条件で、5分間熱処理した。
上述の塗膜を形成しためっき鋼板の塗膜表面をコロナ放電処理した。コロナ放電処理には、春日電機株式会社製の下記の仕様のコロナ放電処理装置を使用した。
(仕様)
・電極セラミック電極
・電極長さ 430mm
・出力 310W
また、塗膜のコロナ放電処理回数は、いずれも1回とした。コロナ放電処理量は、処理速度によって調整した。具体的には、4.8m/分または2.8m/分で処理することにより、コロナ放電処理量150W・分/m2または250W・分/m2とした。
各実施例および比較例で得られた塗装金属板について、以下の方法で、耐雨筋汚れ性の評価、および塗膜表面のSi原子濃度測定、およびオルガノシリケート縮合物の蒸発量の評価を行った。結果を表1および表2に示す。
耐雨筋汚れ性は、以下のように評価した。
まず、垂直暴露台に実施例、比較例、および参考例で作製した塗装金属板をそれぞれ取り付けた。さらに、当該塗装金属板の上部に、地面に対して角度20°となるように、波板を取り付けた。このとき、雨水が塗装金属板表面を筋状に流れるように、波板を設置した。この状態で、屋外暴露試験を2ヶ月間行い、汚れの付着状態を観察した。耐雨筋汚れ性の評価は、暴露前後の塗装金属板の明度差(ΔL)で、以下のように評価した。
×:ΔLが2以上の場合(汚れが目立つ)
△:ΔLが1以上2未満の場合(雨筋汚れは目立たないが視認できる)
〇:ΔLが1未満の場合(雨筋汚れがほとんど視認できない)
塗装金属板を10%塩酸水溶液に60秒浸漬して塗膜表面のシリケートを加水分解した後にSi原子濃度を測定した。塗膜表面のSi原子濃度は、X線電子分光法(以下、「XPS」とも称する)で測定した。
XPS分析装置 : KRATOS社製AXIS−NOVA
X線源 : 単色化AlKα(1486.6eV)
分析領域 : 300×700μm
分析室真空度 : 1.0×10−7Pa
厚さ0.5mmのアルミ板(JIS A5052)の表面に膜厚が18μmになるように、各実施例および比較例と同様に塗膜を形成した。そして、塗膜を形成した塗装アルミ板を10cm×10cm角に切り出し、フッ化水素酸、塩酸、硝酸の混合酸溶液に溶かし、さらにマイクロ波を照射して加熱分解した。その後、超純水で定容して検液を調製した。当該検液中のSiを、島津製作所製 ICPE−9820型ICP−AES分析装置を用いて、定量分析した。
一方、オルガノシリケート縮合物を添加しなかった以外は、実施例および比較例と同様に組成物を調製し、当該組成物を用いて各実施例および比較例と同様に塗膜を形成した。そして、上記と同様に検液中のSiを定量分析した。
これらを比較し、各実施例および比較例で作製した塗装金属板の塗膜中のオルガノシリケート縮合物由来のSi量を求めた。また、オルガノシリケート縮合物が全く蒸発しなかったと仮定した場合の塗膜中のSi量を計算で求めた。そして、オルガノシリケート縮合物が全く蒸発しなかった場合Si量と、実施例または比較例で作製した塗膜中のSi量との比から、塗膜形成時のオルガノシリケートまたはその縮合物の蒸発量を以下の基準で評価した。
×:オルガノシリケート縮合物の蒸発量が70%以上
△:オルガノシリケート縮合物の蒸発量が40%以上70%未満
〇:オルガノシリケート縮合物の蒸発量が30%以上40%未満
◎:オルガノシリケート縮合物の蒸発量が30%未満
なお、△、○、◎を合格とした。
22a 筐体
22b 炎口
22c 補助炎口
23 ガス供給管
Claims (2)
- 金属板の表面に、オルガノシリケートの縮合物およびポリエステル樹脂を含む組成物を塗布および硬化させて塗膜を形成する工程と、
前記塗膜にフレーム処理を行う工程と、
を有し、
前記オルガノシリケートの縮合物中のアルコキシ基の総数に対するエトキシ基の数の割合が50%以上であり、
前記ポリエステル樹脂のゲルパーミエーションクロマトグラフィーで測定される数平均分子量が2000〜8000である、
塗装金属板の製造方法。 - 前記オルガノシリケートの縮合物の重量平均分子量が700以上である、
請求項1に記載の塗装金属板の製造方法。