JP6087644B2 - 発泡体成形品、および、発泡体成形品の製造方法 - Google Patents
発泡体成形品、および、発泡体成形品の製造方法 Download PDFInfo
- Publication number
- JP6087644B2 JP6087644B2 JP2013016440A JP2013016440A JP6087644B2 JP 6087644 B2 JP6087644 B2 JP 6087644B2 JP 2013016440 A JP2013016440 A JP 2013016440A JP 2013016440 A JP2013016440 A JP 2013016440A JP 6087644 B2 JP6087644 B2 JP 6087644B2
- Authority
- JP
- Japan
- Prior art keywords
- raw material
- urethane
- foam
- urethane gel
- polyol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
ルメタンジイソシアネート(MDI)、ポリメリックMDI(クルードMDI)、キシリレンジイ
ソシアネート、1,5−ナフタレンジイソシアネート等が挙げられる。脂肪族イソシアネートとしては、例えば、ヘキサメチレンジイソシアネート、イソプロピレンジイソシアネート、メチレンジイソシアネート等が挙げられる。脂環族イソシアネートとしては、例えば、シクロヘキサン−1,4−ジイソシアネート、イソホロンジイソシアネート、水添MDI等が挙げられる。それら種々のポリイソシアネートのうちの1種または2種以上を併用
したものを、ウレタン発泡体原料またはウレタンゲル原料として用いることが可能である。また、ウレタンフォーム原料のポリイソシアネートとウレタンゲル原料のポリイソシアネートとは、同じ種類のものであってもよく、異なる種類のものであってもよい。
イソシアネートを採用することができる。
図1および図2に示す配合の原料から、実施例1〜8および比較例1〜8の発泡体成形品を製造した。以下に、各原料の詳細を示す。
・ポリオール2;ポリエーテルポリオール、商品名:プレミノールS4011、旭硝子(株)製、重量平均分子量:10000、官能基数:2
・ポリオール3;ポリエーテルポリオール、商品名:サンニックスGP2000、三洋化成工業(株)製、重量平均分子量:2000、官能基数:3
・ポリオール4;ポリエーテルポリオール、商品名:サンニックスPP2000、三洋化成工業(株)製、重量平均分子量:2000、官能基数:2
・ポリオール5;ポリエーテルポリオール、商品名:サンニックスGP1000、三洋化成工業(株)製、重量平均分子量:1000、官能基数:3
・モノオール1;ポリエーテルモノオール、商品名:プレミノールS1004F、旭硝子(株)製、重量平均分子量:3300
・モノオール2;ブチルグリコール、商品名:ブチルグリコール、日本乳化剤(株)製、重量平均分子量:118・モノオール3;イソプロピルアルコール、重量平均分子量:60
・ポリイソシアネート;HDIプレポリマー、HDIの一部をエーテルポリオールと反応させたプレポリマー、イソシアネート基(NCO)含有量12.1質量%
・着色剤;青色顔料 銅化合物のフタル酸−ジ−ノルマルブチル分散液
・触媒;スズ系触媒、商品名;UL−28、モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製
・ポリイソシアネート;トリレンジイソシアネート、商品名:TDI−80、日本ポリウレタン工業(株)製
・発泡剤;水
・整泡剤;シリコーン整泡剤、商品名:TEGOSTAB BF2370、エボニック デグサ ジャパン(株)製
・触媒1;アミン触媒、商品名:カオライザーNo.25、花王(株)製
・触媒2;スズ系触媒、商品名;MRH−110、城北化学工業(株)製
上述のように製造された実施例1〜8および比較例1〜8の発泡体成形品に対して、以下の方法によって物性評価を行なった。
着色剤を含むことを特徴とする(1)項に記載の発泡体成形品。
モノオールを含むことを特徴とする(1)項または(2)項に記載の発泡体成形品。
65〜5000であることを特徴とする(3)項に記載の発泡体成形品。
1.8〜12.0であることを特徴とする(3)項または(4)項に記載の発泡体成形品。
1.7〜11.8であることを特徴とする(1)項ないし(5)項のいずれか1つに記載の発泡体成形品。
ポリオール、ポリイソシアネートを含むウレタンゲル原料を混合するウレタンゲル原料混合工程と、
混合された前記ウレタンフォーム原料と混合された前記ウレタンゲル原料とを不均一に混在させる混在工程と
を含み、ウレタンフォームとウレタンゲルとが不均一に混在してなる発泡体成形品の製造方法。
着色剤を含むことを特徴とする(7)項に記載の製造方法。
モノオールを含むことを特徴とする(7)項または(8)項に記載の製造方法。
65〜5000であることを特徴とする(9)項に記載の製造方法。
1.8〜12.0であることを特徴とする(9)項または(10)項に記載の製造方法。
1.7〜11.8であることを特徴とする(7)項ないし(11)項のいずれか1つに記載の
製造方法。
Claims (2)
- ポリオール、ポリイソシアネート、発泡剤を含むウレタンフォーム原料により成形されるウレタンフォームと、ポリオール、ポリイソシアネート、着色剤、モノオールを含むウレタンゲル原料により成形されるウレタンゲルとが不均一に混在してなり、
前記モノオールの重量平均分子量が、
65〜5000であり、
前記ウレタンゲル原料の前記ポリオールのモル数に対する前記モノオールのモル数の比率が、
1.8〜12.0であり、
前記ウレタンゲル原料の重量に対する前記ウレタンフォーム原料の重量が、
1.7〜11.8であり、
前記ウレタンゲル原料のポリオールの重量平均分子量が、1000より大きく、10000以下であることを特徴とする発泡体成形品。 - ポリオール、ポリイソシアネート、発泡剤を含むウレタンフォーム原料を混合するウレタンフォーム原料混合工程と、
ポリオール、ポリイソシアネート、着色剤、モノオールを含むウレタンゲル原料を混合するウレタンゲル原料混合工程と、
混合された前記ウレタンフォーム原料と混合された前記ウレタンゲル原料とを不均一に混在させる混在工程と
を含み、ウレタンフォームとウレタンゲルとが不均一に混在してなり、
前記モノオールの重量平均分子量が、
65〜5000であり、
前記ウレタンゲル原料の前記ポリオールのモル数に対する前記モノオールのモル数の比率が、
1.8〜12.0であり、
前記ウレタンゲル原料の重量に対する前記ウレタンフォーム原料の重量が、
1.7〜11.8であり、
前記ウレタンゲル原料のポリオールの重量平均分子量が、1000より大きく、10000以下である発泡体成形品の製造方法。