JP6071797B2 - 片面サブマージアーク溶接用フラックス - Google Patents
片面サブマージアーク溶接用フラックス Download PDFInfo
- Publication number
- JP6071797B2 JP6071797B2 JP2013164192A JP2013164192A JP6071797B2 JP 6071797 B2 JP6071797 B2 JP 6071797B2 JP 2013164192 A JP2013164192 A JP 2013164192A JP 2013164192 A JP2013164192 A JP 2013164192A JP 6071797 B2 JP6071797 B2 JP 6071797B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- content
- flux
- tio
- cao
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
また、Mnを0.1〜0.9質量%の範囲で含有していてもよい。
Si及びFe−SiなどのSi合金は、脱酸作用を有し、溶接金属中の酸素と反応してSiO2を生成し、このSiO2は、粘結剤やスラグ造滓剤として作用する。また、Si酸化物も同様に、スラグ造滓剤として作用する。
CaOは、溶融スラグの粘度を低下させ、スラグの流動性を高めて、表ビード幅を広げる効果がある。しかしながら、CaO含有量が9質量%を超えると、溶融スラグの凝固温度が高くなり過ぎて、表ビード形状が損なわれる。一方、CaO含有量が3質量%未満の場合、溶融スラグの流動性を高める効果が得られず、表ビード幅が不足するため、アンダーカットが発生しやすくなる。よって、CaO含有量は3〜9質量%とする。
MgOは、前述したCaOと同様に、溶融スラグの粘度を低下させ、スラグの流動性を高めて、表ビード幅を広げる効果がある。ただし、MgOの含有量が15質量%未満の場合、溶融スラグの流動性を高める効果が得られず、表ビード幅が不足し、アンダーカットが発生しやすくなる。
TiO2は、片面溶接におけるスラグ剥離性の改善に、特に有効な成分である。しかしながら、その含有量が23質量%を超えると、表ビードの波目が粗くなる。また、TiO2含有量が5質量%未満の場合、前述したスラグ剥離性の改善効果が得られず、更には鉄粒が発生しやすくなる。よって、TiO2含有量は5〜23質量%とする。
Al2O3は中性成分であり、スラグの粘性及び凝固温度の調整に有効な成分である。しかしながら、Al2O3含有量が5質量%未満の場合、スラグの粘性及び凝固温度が低下し、ビード幅が不揃いになる。一方、23質量%を超えてAl2O3を添加すると、スラグの凝固温度が高くなり過ぎて、ビードが広がり難くなり、ビード形状が凸型となる。よって、Al2O3含有量は5〜23質量%とする。
CaF2は、フラックス全体の溶融性を良好にする成分であり、特に片面サブマージアーク溶接のように、短時間にフラックスを溶かし、スラグを生成しなければならない溶接方法においては、不可欠な成分である。しかしながら、CaF2含有量が10質量%を超えると、アーク安定性が劣化し、アーク切れを発生しやすくなる。一方、CaF2含有量が2質量%未満の場合、フラックスの溶融性改善効果が得られず、ビード蛇行が発生する。よって、CaF2含有量は2〜10質量%とする。
CO2は、溶接金属への窒素の侵入抑制と、拡散性水素量の低減に有効な成分であり、金属炭酸塩としてフラックス中に添加される。しかしながら、CO2含有量が2質量%未満の場合、溶接金属中の拡散性水素量が高くなり、耐低温割れ性が劣化する。一方、CO2含有量が9質量%を超えると、ガス発生量が過大となり、表ビードにポックマークが発生する。よって、CO2含有量は2〜9質量%とする。
Na2Oはアーク安定性の確保のために必要な成分である。具体的には、Na2O含有量が0.5質量%未満の場合、アークが極端に不安定となり、アーク切れが発生し、ビード形状及び溶込みが不均一となる。一方、Na2O含有量が3質量%を超えると、耐吸湿性が低下して、耐低温割れ性が劣化する。よって、Na2O含有量は0.5〜3質量%とする。
B2O3は、溶接中に還元され、溶接金属中にBとして存在して、靭性の確保に有効に作用する。しかしながら、B2O3含有量が0.1質量%未満の場合、その効果が十分に発揮されず、靭性が劣化する。一方、B2O3含有量が1質量%を超えると、強度が過大となり、高温割れが発生する。よって、B2O3含有量は0.1〜1質量%とする。
Moは、焼入れ性向上に有効な成分であり、Mo単体の他、Fe−Moなどの合金の形態で、フラックスに添加される。ただし、Mo含有量が0.2質量%未満の場合、溶接金属の組織が粗大化し、靭性が劣化する。一方、1質量%を超えてMoを添加すると、溶接金属の強度が過大となり、高温割れが発生する。よって、Mo含有量は0.2〜1質量%とする。
鉄粉は、一度に多量の溶着金属が必要とされる片面サブマージアークにおいて必須の添加成分である。そして、鉄粉含有量が10質量%未満の場合、溶着金属量を補う効果が得られなくなると共に、フラックスの見掛密度が小さくなるため、耐吹き上げ性が劣化する。一方、30質量%を超えて鉄粉を含有させると、溶融・凝固中のフラックス内で鉄粉が凝集しやすくなり、凝集鉄粉が沈降する量が多くなって、ビード表面に鉄粒が付着しやすくなる。加えて、フラックスの見掛密度が高くなり、ビード幅が確保できなくなる。よって、鉄粉の含有量は10〜30質量%とする。
前述したように、CaO及びTiO2はスラグの流動性やスラグ剥離性の向上に有効な成分であるが、CaO含有量(質量%)とTiO2含有量(質量%)との比A(=[CaO]/[TiO2])が0.1未満の場合、アークが不安定となり、ビードに凹凸が生じやすくなる。一方、Aが1.7を超えるとビードが蛇行する。そこで、本実施形態のフラックスでは、CaO含有量及びTiO2含有量を前述した範囲にすると共に、大入熱において良好な溶接作業性を確保するため、CaO含有量とTiO2含有量との比Aを0.1〜1.7の範囲にする。
Tiは、前述したSiやSi合金と同様に、溶接金属中の酸素量低減に有効な成分であるが、この効果はSi及び/又はSi合金の添加などによって十分達成可能であるため、本実施形態のフラックスにおいて、Tiは必須の成分ではない。また、Ti含有量が1質量%を超えると、スラグがビード表面に焼付き、スラグ剥離性が劣化する。よって、Ti含有量は1質量%以下に規制する。
Mnは、前述したMoと同様に、焼入れ性を向上させる効果があり、強度及び靭性の向上に有効な成分であるが、Mn含有量が0.9質量%を超えると、スラグがビード表面に焼付き、スラグ剥離性が劣化する。また、本実施形態のフラックスでは、Moを添加しており、それにより焼入れ性の効果が得られるため、Mn含有量は0.9質量%以下に規制する。
Alは、溶接金属の組織を微細にして、靭性の向上に有効な成分である。しかしながら、この効果は他成分の添加により十分達成可能であるため、本実施形態のフラックスにおいて、Alは必須の成分ではない。また、Al含有量が3質量%を超えると、焼入れが過度となり、強度が上昇して低温割れが発生する。よって、Al含有量は3質量%以下に規制する。なお、Alは不可避的不純物であるが、前述したように溶接金属の組織を微細化する効果があることから、3質量%以下の含有は許容される。
本実施形態のフラックスでは、各成分の含有量を前述した範囲にすると共に、上記数式4又は数式5を満たすように、CaO含有量、TiO2含有量、Al2O3含有量、MgO含有量、並びにSi、Si合金及びSi酸化物の総含有量を調整する。これにより、スラグが凝固する過程においてスラグ内のCa・Ti系酸化物の生成を抑制すると共に、溶接ビードが固まる温度付近の温度においてスラグ内にMg・Al・Ti系酸化物を積極的に生成することが可能となる。
本実施形態のフラックスにおける上記以外の成分は、FeO、ZrO2及びK2Oなどである。
2 溶接金属
2a ビード表面
3 未溶融のフラックス
4 溶融・凝固中のフラックス(スラグ)
5 鉄粉
6 鉄粉の凝集
7 凝集鉄粉(鉄粒)
Claims (3)
- Si、Si合金及びSi酸化物からなる群から選択される少なくとも1種(SiO2換算値):合計で6〜12質量%、
CaO:3〜9質量%、
MgO:15〜35質量%、
TiO2:5〜23質量%、
CaF2:2〜10質量%、
Al2O3:5〜23質量%、
CO2:2〜9質量%、
Na2O:0.5〜3質量%、
B2O3:0.1〜1質量%、
Mo:0.2〜1質量%、
鉄粉:10〜30質量%
を含有すると共に、
Mn:0.9質量%以下、
Ti:1質量%以下、
Al:3質量%以下
に規制され、
CaOの含有量(質量%)を[CaO]、TiO2の含有量(質量%)を[TiO2]、Al2O3の含有量(質量%)を[Al2O3]、MgOの含有量(質量%)を[MgO]、Si、Si合金及びSi酸化物の総含有量のSiO2換算値(質量%)を[T.SiO2]としたとき、CaOの含有量とTiO2の含有量との比A(=[CaO]/[TiO2])が下記数式(I)〜(III)を満たす片面サブマージアーク溶接用フラックス。
- Tiを0.1〜1質量%含有することを特徴とする請求項1に記載の片面サブマージアーク溶接用フラックス。
- Mnを0.1〜0.9質量%含有することを特徴とする請求項1又は2に記載の片面サブマージアーク溶接用フラックス。