JP5727691B2 - Optical glass, optical element and optical instrument - Google Patents
Optical glass, optical element and optical instrument Download PDFInfo
- Publication number
- JP5727691B2 JP5727691B2 JP2008119336A JP2008119336A JP5727691B2 JP 5727691 B2 JP5727691 B2 JP 5727691B2 JP 2008119336 A JP2008119336 A JP 2008119336A JP 2008119336 A JP2008119336 A JP 2008119336A JP 5727691 B2 JP5727691 B2 JP 5727691B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- glass
- content
- optical
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、光学ガラス、光学素子及び光学機器に関する。 The present invention relates to an optical glass, an optical element, and an optical instrument.
近年、光学系を使用する機器のデジタル化や高精細化が急速に進んでおり、デジタルカメラやビデオカメラ等の撮影機器をはじめ、各種光学機器に用いられるレンズ等の光学素子に対する高精度化、軽量、及び小型化の要求は、ますます強まっている。 In recent years, the digitization and high definition of devices that use optical systems have been rapidly progressing, and the precision of optical elements such as lenses used in various optical devices, including photography devices such as digital cameras and video cameras, The demand for light weight and downsizing is increasing.
光学素子を作製する光学ガラスの中でも特に、1.65以上1.77以下の屈折率(nd)を有し、45以上60以下のアッベ数(νd)を有する高屈折率低分散ガラスの需要が非常に高まっている。このような高屈折率低分散ガラスとしては、例えば屈折率(nd)が1.63以上1.76以下、アッベ数(νd)が48.0以上60.5以下の範囲内にある光学ガラスとして、特許文献1に代表されるようなガラス組成物が知られている。
こうした光学素子の製造方法としては、ガラス材料を加熱軟化して成形(リヒートプレス成形)して得られたガラス成形品を研削研磨する方法や、ゴブ又はガラスブロックを切断し研磨したプリフォーム材、若しくは公知の浮上成形等により成形されたプリフォーム材を加熱軟化して、高精度な成形面を持つ金型で加圧成形する方法(精密プレス成形)が用いられている。 As a method for producing such an optical element, a method of grinding and polishing a glass molded product obtained by heating and softening a glass material (reheat press molding), a preform material obtained by cutting and polishing a gob or a glass block, Alternatively, a method (precise press molding) is used in which a preform material molded by a known floating molding or the like is heated and softened and pressure-molded with a mold having a highly accurate molding surface.
しかしながら、ガラスの失透を抑制するにはガラス成分の結晶化を抑制する必要があり、ガラス成分の結晶化を抑制するにはプレス時の温度と結晶化し始める温度との差が大きいほうが好ましい。すなわち結晶化開始温度(Tx)とガラス転移点(Tg)との差ΔTが大きい必要があるところ、特許文献1で開示されたガラスは結晶化開始温度(Tx)との差ΔTが大きくなく、プレス時に失透しやすいものであった。そのため、これらの溶融ガラスから、リヒートプレス成形用のガラス材料や精密プレス成形用のゴブ又はガラスブロックを作製しようとしても、ガラスが失透してしまい、これらのガラスから光学素子を作製するのが困難であった。 However, it is necessary to suppress the crystallization of the glass component in order to suppress the devitrification of the glass, and in order to suppress the crystallization of the glass component, it is preferable that the difference between the temperature at the time of pressing and the temperature at which crystallization starts is large. That is, where the difference ΔT between the crystallization start temperature (Tx) and the glass transition point (Tg) needs to be large, the glass disclosed in Patent Document 1 does not have a large difference ΔT from the crystallization start temperature (Tx). It was easy to devitrify during pressing. Therefore, even if trying to produce a glass material for reheat press molding or a gob or glass block for precision press molding from these molten glasses, the glass is devitrified, and optical elements are produced from these glasses. It was difficult.
本発明は、上記問題点に鑑みてなされたものであって、その目的とするところは、屈折率(nd)及びアッベ数(νd)が所望の範囲内にありながら、溶融状態からガラスを形成したときの耐失透性が高い光学ガラスと、これを用いた光学素子及び光学機器を得ることにある。 The present invention has been made in view of the above-mentioned problems, and the object of the present invention is to make glass from a molten state while the refractive index (n d ) and Abbe number (ν d ) are within the desired ranges. It is to obtain an optical glass having high resistance to devitrification when forming and an optical element and an optical apparatus using the optical glass.
本発明者らは、上記課題を解決するために、鋭意試験研究を重ねた結果、La2O3成分をガラス中に含有することによってガラスの高屈折率低分散化が図られること、並びに、SiO2成分、B2O3成分、La2O3成分、及びZnO成分を併用し、B2O3成分、SiO2成分、B2O3成分、La2O3成分、及びZnO成分の含有率を上記範囲内に抑えることによってガラス転移点(Tg)と結晶化開始温度(Tx)との差ΔTが大きく、プレス時に失透が生じにくいことを見出し、本発明を完成するに至った。具体的には、本発明は以下のようなものを提供する。 In order to solve the above-mentioned problems, the present inventors have conducted extensive test studies, and as a result, the glass has a high refractive index and low dispersion by containing a La 2 O 3 component in the glass. Containing SiO 2 component, B 2 O 3 component, La 2 O 3 component, and ZnO component together, containing B 2 O 3 component, SiO 2 component, B 2 O 3 component, La 2 O 3 component, and ZnO component By controlling the rate within the above range, the difference ΔT between the glass transition point (Tg) and the crystallization start temperature (Tx) is large, and it has been found that devitrification hardly occurs during pressing, and the present invention has been completed. Specifically, the present invention provides the following.
(1) 酸化物換算組成のガラス全質量に対して、質量%でSiO2成分を0.5〜40.0%、B2O3成分を5.0〜50.0%、La2O3成分を5.0〜56.0%、及びZnO成分を0.5〜20.0%含有する光学ガラス。 (1) 0.5 to 40.0% of SiO 2 component, 5.0 to 50.0% of B 2 O 3 component, La 2 O 3 in terms of mass% with respect to the total glass mass of the oxide equivalent composition. Optical glass containing 5.0 to 56.0% of components and 0.5 to 20.0% of ZnO components.
(2) 酸化物換算組成のガラス全質量に対して、質量%で
MgO成分 0〜15.0%及び/又は
CaO成分 0〜20.0%及び/又は
SrO成分 0〜20.0%及び/又は
BaO成分 0〜35.0%
の各成分をさらに含有する(1)記載の光学ガラス。
(2) MgO component 0 to 15.0% and / or CaO component 0 to 20.0% and / or SrO component 0 to 20.0% and / Or BaO component 0-35.0%
The optical glass according to (1), further comprising:
(3) 酸化物換算組成のガラス全質量に対する質量和(MgO+CaO+SrO+BaO)が2.0%以上38.0%以下である(2)記載の光学ガラス。 (3) The optical glass according to (2), wherein the mass sum (MgO + CaO + SrO + BaO) of the oxide equivalent composition with respect to the total glass mass is 2.0% or more and 38.0% or less.
(4) 酸化物換算組成の質量比(MgO+CaO+SrO+BaO)/(SiO2)が0.60以上1.65以下である(2)又は(3)記載の光学ガラス。 (4) The optical glass according to (2) or (3), wherein the mass ratio (MgO + CaO + SrO + BaO) / (SiO 2 ) of the oxide equivalent composition is 0.60 or more and 1.65 or less.
(5) 酸化物換算組成のガラス全質量に対して、質量%で
TiO2成分 0〜10.0%及び/又は
Nb2O5成分 0〜15.0%及び/又は
ZrO2成分 0〜15.0%
の各成分をさらに含有する(1)から(4)のいずれか記載の光学ガラス。
(5) TiO 2 component 0 to 10.0% and / or Nb 2 O 5 component 0 to 15.0% and / or ZrO 2 component 0 to 15% by mass with respect to the total glass mass of the oxide equivalent composition. .0%
The optical glass according to any one of (1) to (4), further comprising:
(6) 酸化物換算組成のガラス全質量に対する質量和(TiO2+Nb2O5+ZrO2)が2.8%以上17.0%以下である(5)記載の光学ガラス。 (6) The optical glass according to (5), wherein the mass sum (TiO 2 + Nb 2 O 5 + ZrO 2 ) with respect to the total glass mass of the oxide equivalent composition is 2.8% or more and 17.0% or less.
(7) 酸化物換算組成のガラス全質量に対して、質量%で
Gd2O3成分 0〜10.0%及び/又は
Y2O3成分 0〜10.0%及び/又は
Yb2O3成分 0〜10.0%及び/又は
Lu2O3成分 0〜10.0%及び/又は
の各成分をさらに含有する(1)から(6)のいずれか記載の光学ガラス。
(7) Gd 2 O 3 component 0 to 10.0% and / or Y 2 O 3 component 0 to 10.0% and / or Yb 2 O 3 in mass% with respect to the total glass mass of the oxide equivalent composition. components from 0 to 10.0% and / or Lu 2 O 3 component from 0 to 10.0% and / or any description of the optical glass from further contains the components (1) (6).
(8) 酸化物換算組成のガラス全質量に対して、質量%でAl2O3成分を0〜5.0%さらに含有する(1)から(7)のいずれか記載の光学ガラス。 (8) The optical glass according to any one of (1) to (7), further containing 0 to 5.0% of an Al 2 O 3 component in mass% with respect to the total glass mass of the oxide equivalent composition.
(9) 酸化物換算組成のガラス全質量に対する質量和(SiO2+B2O3+La2O3+ZnO+MgO+CaO+SrO+BaO+TiO2+Nb2O5+ZrO2+Al2O3)が90.0%以上である(8)記載の光学ガラス。 (9) The mass sum (SiO 2 + B 2 O 3 + La 2 O 3 + ZnO + MgO + CaO + SrO + BaO + TiO 2 + Nb 2 O 5 + ZrO 2 + Al 2 O 3 ) relative to the total glass mass of the oxide equivalent composition is 90.0% or more (8) Optical glass.
(10) 酸化物換算組成のガラス全質量に対する質量和(La2O3+Gd2O3+Y2O3+Yb2O3+Lu2O3)が5.0%以上56.0%以下である(7)から(9)のいずれか記載の光学ガラス。 (10) The mass sum (La 2 O 3 + Gd 2 O 3 + Y 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ) with respect to the total glass mass of the oxide equivalent composition is 5.0% or more and 56.0% or less ( The optical glass according to any one of 7) to (9).
(11) 酸化物換算組成の質量比(La2O3+Gd2O3+Y2O3+Yb2O3+Lu2O3)/(La2O3)が1.00以上1.20以下である(7)から(10)のいずれか記載の光学ガラス。 (11) The mass ratio (La 2 O 3 + Gd 2 O 3 + Y 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ) / (La 2 O 3 ) of the oxide equivalent composition is 1.00 or more and 1.20 or less. The optical glass according to any one of (7) to (10).
(12) 酸化物換算組成のガラス全質量に対して、質量%で
Li2O成分 0〜20.0%及び/又は
Na2O成分 0〜25.0%及び/又は
K2O成分 0〜25.0%及び/又は
Ta2O5成分 0〜10.0%及び/又は
WO3成分 0〜10.0%及び/又は
Sb2O3成分 0〜1.0%
の各成分をさらに含有する(1)から(11)のいずれか記載の光学ガラス。
(12) the entire mass of the glass in terms of oxide composition, 0 to 20.0% Li 2 O component in% by weight and / or Na 2 O component from 0 to 25.0% and / or K 2 O ingredient 0 25.0% and / or Ta 2 O 5 component 0 to 10.0% and / or WO 3 component 0 to 10.0% and / or Sb 2 O 3 component 0 to 1.0%
The optical glass according to any one of (1) to (11), further comprising:
(13) 実質的に鉛化合物及びヒ素化合物を含有しない(1)から(12)のいずれか記載の光学ガラス。 (13) The optical glass according to any one of (1) to (12), which contains substantially no lead compound and arsenic compound.
(14) 1.65以上1.77以下の屈折率(nd)を有し、45以上60以下のアッベ数(νd)を有する(1)から(13)のいずれか記載の光学ガラス。 (14) The optical glass according to any one of (1) to (13), which has a refractive index (n d ) of 1.65 or more and 1.77 or less and an Abbe number (ν d ) of 45 or more and 60 or less.
(15) (1)から(14)のいずれか記載の光学ガラスを母材とする光学素子。 (15) An optical element having the optical glass according to any one of (1) to (14) as a base material.
(16) (1)から(14)のいずれか記載の光学ガラスをリヒートプレス成形して作製する光学素子。 (16) An optical element produced by reheat press molding the optical glass according to any one of (1) to (14).
(17) (1)から(14)のいずれか記載の光学ガラスからなるプリフォームを精密プレス成形して作製する光学素子。 (17) An optical element produced by precision press-molding a preform made of the optical glass according to any one of (1) to (14).
(18) (1)から(14)のいずれか記載の光学ガラスで作製された光学素子を備える光学機器。 (18) An optical device comprising an optical element made of the optical glass according to any one of (1) to (14).
本発明によれば、SiO2成分、B2O3成分、La2O3成分、及びZnO成分を併用し、B2O3成分、SiO2成分、B2O3成分、La2O3成分、及びZnO成分の含有率を上記範囲内に抑えることによって、屈折率(nd)及びアッベ数(νd)が所望の範囲内にありながら、溶融状態からガラスを形成したときの耐失透性が高い光学ガラスと、これを用いた光学素子及び光学機器を得ることができる。 According to the present invention, the SiO 2 component, the B 2 O 3 component, the La 2 O 3 component, and the ZnO component are used in combination, and the B 2 O 3 component, the SiO 2 component, the B 2 O 3 component, and the La 2 O 3 component are combined. And the ZnO component content within the above range, the devitrification resistance when the glass is formed from the molten state while the refractive index (n d ) and Abbe number (ν d ) are within the desired ranges. Optical glass having high properties, and an optical element and an optical instrument using the optical glass can be obtained.
本発明の光学ガラスは、酸化物換算組成のガラス全質量に対して、質量%でSiO2成分を0.5〜40.0%、B2O3成分を5.0〜50.0%、La2O3成分を5.0〜56.0%、及びZnO成分を0.5〜20.0%含有する。La2O3成分を加えることによって、ガラスの屈折率が高められて分散が抑えられる。また、SiO2成分、B2O3成分、La2O3成分、及びZnO成分を併用し、B2O3成分、SiO2成分、B2O3成分、La2O3成分、及びZnO成分の含有率を上記範囲内に抑えることによって、ガラス転移点(Tg)と結晶化開始温度(Tx)との差ΔTが大きくなる。このため、屈折率(nd)が1.65以上1.77以下の範囲内にあり、アッベ数(νd)が45以上60以下の範囲内にありながら、溶融状態からガラスを形成したときの耐失透性が高い光学ガラスを得ることができる。 In the optical glass of the present invention, the SiO 2 component is 0.5 to 40.0% and the B 2 O 3 component is 5.0 to 50.0% by mass% based on the total mass of the oxide-converted glass. The La 2 O 3 component is contained in an amount of 5.0 to 56.0%, and the ZnO component is contained in an amount of 0.5 to 20.0%. By adding the La 2 O 3 component, the refractive index of the glass is increased and dispersion is suppressed. Further, the SiO 2 component, the B 2 O 3 component, the La 2 O 3 component, and the ZnO component are used in combination, and the B 2 O 3 component, the SiO 2 component, the B 2 O 3 component, the La 2 O 3 component, and the ZnO component are combined. By suppressing the content ratio of S within the above range, the difference ΔT between the glass transition point (Tg) and the crystallization start temperature (Tx) increases. Therefore, when the glass is formed from the molten state while the refractive index (n d ) is in the range of 1.65 or more and 1.77 or less and the Abbe number (ν d ) is in the range of 45 or more and 60 or less. An optical glass having high devitrification resistance can be obtained.
以下、本発明の光学ガラスの実施形態について詳細に説明するが、本発明は、以下の実施形態に何ら限定されるものではなく、本発明の目的の範囲内において、適宜変更を加えて実施することができる。なお、説明が重複する箇所については、適宜説明を省略する場合があるが、発明の趣旨を限定するものではない。 Hereinafter, embodiments of the optical glass of the present invention will be described in detail. However, the present invention is not limited to the following embodiments, and may be implemented with appropriate modifications within the scope of the object of the present invention. be able to. In addition, although description may be abbreviate | omitted suitably about the location where description overlaps, the meaning of invention is not limited.
[ガラス成分]
本発明の光学ガラスを構成する各成分の組成範囲を以下に述べる。本明細書中において、各成分の含有率は特に断りがない場合は、全て酸化物換算組成のガラス全質量に対する質量%で表示されるものとする。ここで、「酸化物換算組成」とは、本発明のガラス構成成分の原料として使用される酸化物、複合塩、金属弗化物等が溶融時に全て分解され酸化物へ変化すると仮定した場合に、当該生成酸化物の総質量を100質量%として、ガラス中に含有される各成分を表記した組成である。
[Glass component]
The composition range of each component constituting the optical glass of the present invention is described below. In the present specification, unless otherwise specified, the content of each component is expressed in mass% with respect to the total mass of the glass in terms of oxide. Here, the “oxide equivalent composition” means that the oxide, composite salt, metal fluoride, etc. used as the raw material of the glass component of the present invention are all decomposed and changed into oxides when melted. It is the composition which described each component contained in glass by making the total mass of the said production | generation oxide into 100 mass%.
<必須成分、任意成分について>
SiO2成分は、ガラス内部で網目構造を形成し、安定なガラス形成を促して、光学ガラスとして好ましくないガラスを作製する際の失透(結晶物の発生)や脈理(ガラス内部の不均一性)を抑制する成分である。特に、SiO2成分の含有率を0.5%以上にすることで、ガラスの耐失透性を高めることができる。一方、SiO2成分の含有率を40.0%以下にすることで、ガラスの屈折率を低下し難くすることができる。従って、酸化物換算組成のガラス全質量に対するSiO2成分の含有率は、好ましくは0.5%、より好ましくは1.0%、最も好ましくは1.5%を下限とし、好ましくは40.0%、より好ましくは38.0%、最も好ましくは35.0%を上限とする。SiO2成分は、原料として例えばSiO2、K2SiF6、Na2SiF6等を用いてガラス内に含有することができる。
<About essential and optional components>
The SiO 2 component forms a network structure inside the glass, promotes stable glass formation, and devitrification (generation of crystals) and striae (nonuniformity inside the glass) when producing an unfavorable glass as an optical glass. Property). In particular, the devitrification resistance of the glass can be enhanced by setting the content of the SiO 2 component to 0.5% or more. On the other hand, by setting the content of SiO 2 component below 40.0% it can be difficult to lower the refractive index of the glass. Therefore, the content of the SiO 2 component with respect to the total glass mass of the oxide conversion composition is preferably 0.5%, more preferably 1.0%, and most preferably 1.5% as the lower limit, preferably 40.0. %, More preferably 38.0%, and most preferably 35.0%. SiO 2 component may be contained in the glass by using as a raw material such as SiO 2, K 2 SiF 6, Na 2 SiF 6 or the like.
B2O3成分は、ガラス内部で網目構造を形成し、安定なガラス形成を促す成分である。特に、B2O3成分の含有率を5.0%以上にすることで、ガラスの溶融性を改善することにより安定なガラスを得易くすることができる。一方、B2O3成分の含有率を50.0%以下にすることで、ガラスの屈折率を低下し難くすることができる。従って、酸化物換算組成のガラス全質量に対するB2O3成分の含有率は、好ましくは5.0%、より好ましくは8.0%、最も好ましくは10.0%を下限とし、好ましくは50.0%、より好ましくは48.0%、最も好ましくは45.0%を上限とする。B2O3成分は、原料として例えばH3BO3、Na2B4O7、Na2B4O7・10H2O、BPO4等を用いてガラス内に含有することができる。 The B 2 O 3 component is a component that forms a network structure inside the glass and promotes stable glass formation. In particular, by setting the content of the B 2 O 3 component to 5.0% or more, it is possible to easily obtain a stable glass by improving the meltability of the glass. On the other hand, the content of B 2 O 3 component by the following 50.0%, can be difficult to lower the refractive index of the glass. Therefore, the content ratio of the B 2 O 3 component with respect to the total glass mass of the oxide conversion composition is preferably 5.0%, more preferably 8.0%, and most preferably 10.0%, and preferably 50%. The upper limit is 0.0%, more preferably 48.0%, and most preferably 45.0%. The B 2 O 3 component can be contained in the glass using, for example, H 3 BO 3 , Na 2 B 4 O 7 , Na 2 B 4 O 7 .10H 2 O, BPO 4 or the like as a raw material.
La2O3成分は、ガラスの屈折率を高めて分散を小さくする成分である。特に、La2O3成分の含有率を5.0%以上にすることで、所望の高屈折率及び低分散を得易くすることができる。一方、La2O3成分の含有率を56.0%以下にすることで、溶融状態からガラスを形成したときの耐失透性をより高めることができる。従って、酸化物換算組成のガラス全質量に対するLa2O3成分の含有率は、好ましくは5.0%、より好ましくは8.0%、最も好ましくは10.0%を下限とし、好ましくは56.0%、より好ましくは53.0%、最も好ましくは50.0%を上限とする。La2O3成分は、原料として例えばLa2O3、La(NO3)3・XH2O(Xは任意の整数)等を用いてガラス内に含有することができる。 The La 2 O 3 component is a component that increases the refractive index of the glass and decreases dispersion. In particular, the desired high refractive index and low dispersion can be easily obtained by setting the content of the La 2 O 3 component to 5.0% or more. On the other hand, by setting the content of the La 2 O 3 component to 56.0% or less, the devitrification resistance when the glass is formed from the molten state can be further increased. Therefore, the content of the La 2 O 3 component with respect to the total glass mass of the oxide conversion composition is preferably 5.0%, more preferably 8.0%, and most preferably 10.0%, and preferably 56%. 0.0%, more preferably 53.0%, and most preferably 50.0%. The La 2 O 3 component can be contained in the glass using, for example, La 2 O 3 , La (NO 3 ) 3 .XH 2 O (X is an arbitrary integer) or the like as a raw material.
ZnO成分は、ガラスの溶融性を改善して安定なガラスを形成し易くする成分である。特に、ZnO成分の含有率を0.5%以上にすることで、安定なガラス成形を容易にすることができる。一方、ZnO成分の含有率を20.0%以下にすることで、溶融時の失透発生を抑制することができる。従って、酸化物換算組成のガラス全質量に対するZnO成分の含有率は、好ましくは0.5%、より好ましくは0.8%、最も好ましくは1.0%を下限とし、好ましくは20.0%、より好ましくは18.0%、最も好ましくは15.0%を上限とする。ZnO成分は、原料として例えばZnO、ZnF2等を用いてガラス内に含有することができる。 A ZnO component is a component which improves the meltability of glass and makes it easy to form stable glass. In particular, stable glass molding can be facilitated by setting the content of the ZnO component to 0.5% or more. On the other hand, by setting the content of the ZnO component to 20.0% or less, the occurrence of devitrification at the time of melting can be suppressed. Therefore, the content of the ZnO component with respect to the total glass mass of the oxide conversion composition is preferably 0.5%, more preferably 0.8%, and most preferably 1.0% as the lower limit, preferably 20.0%. More preferably, the upper limit is 18.0%, and most preferably 15.0%. The ZnO component can be contained in the glass using, for example, ZnO, ZnF 2 or the like as a raw material.
MgO成分は、ガラスの屈折率を調整する成分であり、本発明の光学ガラス中の任意成分である。特に、MgO成分の含有率を15.0%以下にすることで、ガラスの溶融時の失透発生を抑制することができる。従って、酸化物換算組成のガラス全質量に対するMgO成分の含有率は、好ましくは15.0%、より好ましくは13.0%、最も好ましくは10.0%を上限とする。MgO成分は、原料として例えばMgCO3、MgF2等を用いてガラス内に含有することができる。 The MgO component is a component that adjusts the refractive index of the glass, and is an optional component in the optical glass of the present invention. In particular, by setting the content of the MgO component to 15.0% or less, it is possible to suppress the occurrence of devitrification when the glass is melted. Therefore, the upper limit of the content of the MgO component with respect to the total glass mass of the oxide conversion composition is preferably 15.0%, more preferably 13.0%, and most preferably 10.0%. The MgO component can be contained in the glass using, for example, MgCO 3 or MgF 2 as a raw material.
CaO成分は、ガラスの屈折率及び分散を調整する成分であり、本発明の光学ガラス中の任意成分である。特に、CaO成分の含有率を20.0%以下にすることで、ガラスの屈折率を低下し難くし、ガラスの化学的耐久性を高めることができる。従って、酸化物換算組成のガラス全質量に対するCaO成分の含有率は、好ましくは20.0%、より好ましくは18.0%、最も好ましくは15.0%を上限とする。CaO成分は、原料として例えばCaCO3、CaF2等を用いてガラス内に含有することができる。 A CaO component is a component which adjusts the refractive index and dispersion | distribution of glass, and is an arbitrary component in the optical glass of this invention. In particular, by making the content of the CaO component 20.0% or less, the refractive index of the glass is hardly lowered and the chemical durability of the glass can be enhanced. Therefore, the content of the CaO component with respect to the total glass mass of the oxide conversion composition is preferably 20.0%, more preferably 18.0%, and most preferably 15.0%. The CaO component can be contained in the glass using, for example, CaCO 3 , CaF 2 or the like as a raw material.
SrO成分は、ガラスの屈折率及び分散を調整する成分であり、本発明の光学ガラス中の任意成分である。特に、SrO成分の含有率を25.0%以下にすることで、失透発生を抑制することができる。従って、酸化物換算組成のガラス全質量に対するSrO成分の含有率は、好ましくは25.0%、より好ましくは23.0%、最も好ましくは21.0%を上限とする。SrO成分は、原料として例えばSr(NO3)2、SrF2等を用いてガラス内に含有することができる。 The SrO component is a component that adjusts the refractive index and dispersion of the glass, and is an optional component in the optical glass of the present invention. In particular, the occurrence of devitrification can be suppressed by setting the content of the SrO component to 25.0% or less. Therefore, the content of the SrO component with respect to the total glass mass of the oxide conversion composition is preferably 25.0%, more preferably 23.0%, and most preferably 21.0%. The SrO component can be contained in the glass using, for example, Sr (NO 3 ) 2 , SrF 2 or the like as a raw material.
BaO成分は、ガラスの屈折率を高めて分散を小さくする成分であり、本発明の光学ガラス中の任意成分である。特に、BaO成分の含有率を35.0%以下にすることで、ガラスの化学的耐久性を高めることができる。従って、酸化物換算組成のガラス全質量に対するBaO成分の含有率は、好ましくは35.0%、より好ましくは34.5%、最も好ましくは34.1%を上限とする。BaO成分は、原料として例えばBaCO3、Ba(NO3)2等を用いてガラス内に含有することができる。 A BaO component is a component which raises the refractive index of glass and makes dispersion | distribution small, and is an arbitrary component in the optical glass of this invention. In particular, the chemical durability of glass can be improved by setting the content of the BaO component to 35.0% or less. Therefore, the content of the BaO component with respect to the total glass mass of the oxide-converted composition is preferably 35.0%, more preferably 34.5%, and most preferably 34.1%. The BaO component can be contained in the glass using, for example, BaCO 3 , Ba (NO 3 ) 2 or the like as a raw material.
本発明の光学ガラスでは、RO成分(式中、RはMg、Ca、Sr、Baからなる群より選択される1種以上)の含有率の質量和が、1.5%以上38.0%以下であることが好ましい。この質量和を1.5%以上にすることで、ガラスの安定性を高めて溶融状態からガラスを形成したときの耐失透性を高めることができる。また、この質量和を38.0%以下にすることで、ガラスの屈折率を低下し難くすることができる。従って、酸化物換算組成のガラス全質量に対するRO成分の含有率の質量和は、好ましくは1.5%、より好ましくは1.8%、最も好ましくは2.0%を下限とし、好ましくは38.0%、より好ましくは37.0%、最も好ましくは36.0%を上限とする。 In the optical glass of the present invention, the mass sum of the content ratio of the RO component (wherein R is one or more selected from the group consisting of Mg, Ca, Sr, and Ba) is 1.5% or more and 38.0%. The following is preferable. By making this mass sum 1.5% or more, the stability of the glass can be increased and the devitrification resistance when the glass is formed from the molten state can be enhanced. Moreover, the refractive index of glass can be made hard to fall by making this mass sum into 38.0% or less. Therefore, the mass sum of the content of the RO component with respect to the total glass mass of the oxide conversion composition is preferably 1.5%, more preferably 1.8%, and most preferably 2.0% as the lower limit, preferably 38 The upper limit is 0.0%, more preferably 37.0%, and most preferably 36.0%.
また、本発明の光学ガラスでは、SiO2成分の含有量に対するRO成分の含有量の質量比が0.60以上1.68以下であることが好ましい。この質量比を0.60以上にすることで、ガラスの安定性を高めて溶融状態からガラスを形成したときの耐失透性を高めることができる。また、この質量比を1.68以下にすることで、ガラスの網目構造を形成し易くしてガラス化を容易にすることができる。従って、酸化物換算組成のSiO2の含有量に対するRO成分の含有量の質量比は、好ましくは0.60、より好ましくは0.61、最も好ましくは0.62を下限とし、好ましくは1.68、より好ましくは1.66、最も好ましくは1.65を上限とする。 In the optical glass of the present invention, the mass ratio of the RO component content to the SiO 2 component content is preferably 0.60 or more and 1.68 or less. By making this mass ratio 0.60 or more, the stability of the glass can be increased and the devitrification resistance when the glass is formed from the molten state can be increased. Moreover, by making this mass ratio 1.68 or less, it is easy to form a network structure of glass and facilitate vitrification. Therefore, the mass ratio of the content of the RO component to the content of SiO 2 having an oxide equivalent composition is preferably 0.60, more preferably 0.61, and most preferably 0.62, and preferably 1. 68, more preferably 1.66, and most preferably 1.65.
TiO2成分は、ガラスの屈折率を高め、ガラスの分散を大きくして、化学的耐久性を高める成分であり、本発明の光学ガラス中の任意成分である。特に、TiO2成分の含有率を10.0%以下にすることで、所望の低分散を得易くし、ガラスへの着色を低減し、特に可視短波長(500nm以下)における透過率を悪化し難くすることができる。従って、酸化物換算組成のガラス全質量に対するTiO2成分の含有率は、好ましくは10.0%、より好ましくは8.0%、最も好ましくは5.0%を上限とする。TiO2成分は、原料として例えばTiO2等を用いてガラス内に含有することができる。 TiO 2 component increases the refractive index of the glass, to increase the dispersion of the glass, or to enhance chemical durability, an optional component of the optical glass of the present invention. In particular, by making the content of TiO 2 component 10.0% or less, desired low dispersion can be easily obtained, coloring to glass is reduced, and in particular, the transmittance at a visible short wavelength (500 nm or less) is deteriorated. Can be difficult. Accordingly, the content of the TiO 2 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 8.0%, and most preferably 5.0%. TiO 2 component may be contained in the glass by using as the starting material for example TiO 2 or the like.
Nb2O5成分は、ガラスの屈折率を高め、ガラスの化学的耐久性を向上する成分であり、本発明の光学ガラス中の任意成分である。特に、Nb2O5成分の含有率を10.0%以下にすることで、所望の低分散を得易くし、ガラスの安定した成形を容易にすることができる。従って、酸化物換算組成のガラス全質量に対するNb2O5成分の含有率は、好ましくは10.0%、より好ましくは8.0%、最も好ましくは5.0%を上限とする。Nb2O5成分は、原料として例えばNb2O5等を用いてガラス内に含有することができる。 Nb 2 O 5 component increases the refractive index of the glass is a component for improving the chemical durability of the glass, an optional component of the optical glass of the present invention. In particular, by making the content of the Nb 2 O 5 component 10.0% or less, desired low dispersion can be easily obtained, and stable molding of the glass can be facilitated. Therefore, the content of the Nb 2 O 5 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 8.0%, and most preferably 5.0%. The Nb 2 O 5 component can be contained in the glass using, for example, Nb 2 O 5 as a raw material.
ZrO2成分は、ガラスの屈折率を高め、ガラスの化学的耐久性を高める成分であり、本発明の光学ガラス中の任意成分である。特に、ZrO2成分の含有率を10.0%以下にすることで、ガラスの製造時における高温での溶解を回避し、ガラス製造時のエネルギー損失を低減することができる。従って、酸化物換算組成のガラス全質量に対するZrO2成分の含有率は、好ましくは10.0%、より好ましくは9.0%、最も好ましくは8.5%を上限とする。ZrO2成分は、原料として例えばZrO2、ZrF4等を用いてガラス内に含有することができる。 The ZrO 2 component is a component that increases the refractive index of the glass and increases the chemical durability of the glass, and is an optional component in the optical glass of the present invention. In particular, by setting the content of the ZrO 2 component to 10.0% or less, melting at a high temperature during glass production can be avoided, and energy loss during glass production can be reduced. Therefore, the content of the ZrO 2 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 9.0%, and most preferably 8.5%. The ZrO 2 component can be contained in the glass using, for example, ZrO 2 , ZrF 4 or the like as a raw material.
本発明の光学ガラスでは、TiO2成分、Nb2O5成分、及びZrO2成分の含有率の質量和が、2.8%以上17.0%以下であることが好ましい。この質量和を2.8%以上にすることで、高屈折率を有し、溶融状態からガラスを形成したときの耐失透性が高いガラスを得易くすることができる。また、この質量和を17.0%以下にすることで、所望のガラスの低分散を得易くすることができる。従って、酸化物換算組成のガラス全質量に対するTiO2成分、Nb2O5成分、及びZrO2成分の含有率の質量和は、好ましくは2.8%、より好ましくは3.0%、最も好ましくは3.2%を下限とし、好ましくは17.0%、より好ましくは15.0%、最も好ましくは12.0%を上限とする。 In the optical glass of the present invention, TiO 2 component, Nb 2 O 5 component, and the mass sum of the content of the ZrO 2 component is not more than 17.0 percent 2.8% or more preferred. By setting the mass sum to 2.8% or more, it is possible to easily obtain a glass having a high refractive index and high devitrification resistance when the glass is formed from a molten state. Moreover, by making this mass sum 17.0% or less, desired low dispersion of glass can be easily obtained. Therefore, the mass sum of the contents of the TiO 2 component, the Nb 2 O 5 component, and the ZrO 2 component with respect to the total glass mass of the oxide conversion composition is preferably 2.8%, more preferably 3.0%, and most preferably Has a lower limit of 3.2%, preferably 17.0%, more preferably 15.0%, and most preferably 12.0%.
Gd2O3成分は、ガラスの屈折率を高めて分散を小さくする成分であり、本発明の光学ガラス中の任意成分である。特に、Gd2O3成分の含有率を10.0%以下にすることで、ガラスの材料コストを低減し、ガラスを作製する際にガラスを失透し難くすることができる。従って、酸化物換算組成のガラス全質量に対するGd2O3成分の含有率は、好ましくは10.0%、より好ましくは7.0%、最も好ましくは5.0%を上限とする。Gd2O3成分は、原料として例えばGd2O3、GdF3等を用いてガラス内に含有することができる。 The Gd 2 O 3 component is a component that increases the refractive index of the glass and decreases dispersion, and is an optional component in the optical glass of the present invention. In particular, by making the content of the Gd 2 O 3 component 10.0% or less, the material cost of the glass can be reduced, and the glass can be made hard to devitrify when it is produced. Therefore, the content of the Gd 2 O 3 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 7.0%, and most preferably 5.0%. The Gd 2 O 3 component can be contained in the glass using, for example, Gd 2 O 3 , GdF 3 or the like as a raw material.
Y2O3成分は、ガラスの屈折率を高めて分散を小さくする成分であり、本発明の光学ガラス中の任意成分である。特に、Y2O3成分の含有率を10.0%以下にすることで、ガラスの材料コストを低減し、ガラスを作製する際にガラスを失透し難くすることができる。従って、酸化物換算組成のガラス全質量に対するY2O3成分の含有率は、好ましくは10.0%、より好ましくは7.0%、最も好ましくは5.0%を上限とする。Y2O3成分は、原料として例えばY2O3、YF3等を用いてガラス内に含有することができる。 Y 2 O 3 component is a component to decrease the dispersion by increasing the refractive index of the glass, an optional component of the optical glass of the present invention. In particular, by making the content of the Y 2 O 3 component 10.0% or less, the material cost of the glass can be reduced, and the glass can be made less devitrified when the glass is produced. Therefore, the content of the Y 2 O 3 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 7.0%, and most preferably 5.0%. The Y 2 O 3 component can be contained in the glass using, for example, Y 2 O 3 , YF 3 or the like as a raw material.
Yb2O3成分は、ガラスの屈折率を高める成分であり、本発明の光学ガラス中の任意成分である。特に、Yb2O3成分の含有率を10.0%以下にすることで、ガラスの材料コストを低減することができる。従って、酸化物換算組成のガラス全質量に対するYb2O3成分の含有率は、好ましくは10.0%、より好ましくは7.0%、最も好ましくは5.0%を上限とする。Yb2O3成分は、原料として例えばYb2O3等を用いてガラス内に含有することができる。 Yb 2 O 3 component is a component that raises the refractive index of the glass, an optional component of the optical glass of the present invention. In particular, by setting the content of Yb 2 O 3 component to 10.0% or less, it is possible to reduce the material cost of the glass. Therefore, the content of the Yb 2 O 3 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 7.0%, and most preferably 5.0%. The Yb 2 O 3 component can be contained in the glass using, for example, Yb 2 O 3 as a raw material.
Lu2O3成分は、ガラスの屈折率を高めて分散を小さくする成分であり、本発明の光学ガラス中の任意成分である。特に、Lu2O3成分の含有率を10.0%以下にすることで、ガラスの材料コストを低減することができる。従って、酸化物換算組成のガラス全質量に対するLu2O3成分の含有率は、好ましくは10.0%、より好ましくは7.0%、最も好ましくは5.0%を上限とする。Lu2O3成分は、原料として例えばLu2O3等を用いてガラス内に含有することができる。 Lu 2 O 3 component is a component to decrease the dispersion by increasing the refractive index of the glass, an optional component of the optical glass of the present invention. In particular, by setting the content of Lu 2 O 3 component to 10.0% or less, it is possible to reduce the material cost of the glass. Therefore, the upper limit of the content of the Lu 2 O 3 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 7.0%, and most preferably 5.0%. The Lu 2 O 3 component can be contained in the glass using, for example, Lu 2 O 3 as a raw material.
本発明の光学ガラスでは、La2O3成分、Gd2O3成分、Y2O3成分、Yb2O3成分、及びLu2O3成分の含有率の質量和が、5.0%以上56.0%以下であることが好ましい。この質量和を5.0%以上にすることで、所望の高屈折率及び低分散を得易くすることができる。また、この質量和を56.0%以下にすることで、溶融状態からガラスを形成したときの耐失透性をより高めることができる。従って、酸化物換算組成のガラス全質量に対するLa2O3成分、Gd2O3成分、Y2O3成分、Yb2O3成分、及びLu2O3成分の含有率の質量和は、好ましくは5.0%、より好ましくは8.0%、最も好ましくは10.0%を下限とし、好ましくは56.0%、より好ましくは54.0%、最も好ましくは53.0%を上限とする。 In the optical glass of the present invention, the mass sum of the contents of La 2 O 3 component, Gd 2 O 3 component, Y 2 O 3 component, Yb 2 O 3 component, and Lu 2 O 3 component is 5.0% or more. It is preferable that it is 56.0% or less. By making this mass sum 5.0% or more, desired high refractive index and low dispersion can be easily obtained. Moreover, by making this mass sum 56.0% or less, devitrification resistance when glass is formed from a molten state can be further improved. Therefore, the mass sum of the content ratios of La 2 O 3 component, Gd 2 O 3 component, Y 2 O 3 component, Yb 2 O 3 component, and Lu 2 O 3 component with respect to the total glass mass of the oxide conversion composition is preferable. Is 5.0%, more preferably 8.0%, most preferably 10.0% as the lower limit, preferably 56.0%, more preferably 54.0%, most preferably 53.0% as the upper limit. To do.
また、本発明の光学ガラスでは、La2O3成分の含有量に対する質量和(La2O3+Gd2O3+Y2O3+Yb2O3+Lu2O3)の質量比が、1.00以上1.20以下であることが好ましい。この質量比を1.20以下にすることで、溶融状態からガラスを形成したときの耐失透性をより高めることができる。従って、この質量比は、好ましくは1.20、より好ましくは1.17、最も好ましくは1.15を上限とする。 In the optical glass of the present invention, the mass ratio of the mass sum (La 2 O 3 + Gd 2 O 3 + Y 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ) to the content of the La 2 O 3 component is 1.00. It is preferable that it is 1.20 or more. By making this mass ratio 1.20 or less, devitrification resistance when glass is formed from a molten state can be further enhanced. Therefore, the upper limit of this mass ratio is preferably 1.20, more preferably 1.17, and most preferably 1.15.
Al2O3成分は、光学ガラスの化学的耐久性を高め、溶融ガラスからガラスを作製したときの耐失透性を向上する成分であり、本発明の光学ガラス中の任意成分である。特に、Al2O3成分の含有率を5.0%以下にすることで、ガラスの屈折率の低下を抑制することができる。従って、酸化物換算組成のガラス全質量に対するAl2O3成分の含有率は、好ましくは5.0%、より好ましくは4.0%、最も好ましくは3.5%を上限とする。Al2O3成分は、原料として例えばAl2O3、Al(OH)3、AlF3等を用いてガラス内に含有することができる。 The Al 2 O 3 component is a component that increases the chemical durability of the optical glass and improves the devitrification resistance when the glass is produced from molten glass, and is an optional component in the optical glass of the present invention. In particular, when the content ratio of the Al 2 O 3 component is 5.0% or less, a decrease in the refractive index of the glass can be suppressed. Therefore, the content of the Al 2 O 3 component with respect to the total glass mass of the oxide-converted composition is preferably 5.0%, more preferably 4.0%, and most preferably 3.5%. The Al 2 O 3 component can be contained in the glass using, for example, Al 2 O 3 , Al (OH) 3 , AlF 3 or the like as a raw material.
本発明の光学ガラスでは、SiO2成分、B2O3成分、La2O3成分、ZnO成分、MgO成分、CaO成分、SrO成分、BaO成分、TiO2成分、Nb2O5成分、ZrO2成分、Y2O3成分、及びAl2O3成分の含有率の質量和が90.0%以上であることが好ましい。この質量和を90.0%以上にすることで、ガラスの安定性を高め、成形時の耐失透性を高めることができる。従って、酸化物換算組成のガラス全質量に対するこの質量和は、好ましくは90.0%、より好ましくは95.0%、最も好ましくは98.0%を下限とする。 In the optical glass of the present invention, SiO 2 component, B 2 O 3 component, La 2 O 3 component, ZnO component, MgO component, CaO component, SrO component, BaO component, TiO 2 component, Nb 2 O 5 component, ZrO 2 component, it is preferred that Y 2 O 3 component, and Al 2 O 3 mass sum of the content of the component is 90.0% or more. By making this mass sum 90.0% or more, the stability of the glass can be increased, and the devitrification resistance during molding can be increased. Therefore, this mass sum with respect to the total glass mass of the oxide conversion composition is preferably 90.0%, more preferably 95.0%, and most preferably 98.0%.
Li2O成分は、ガラスの溶融性を改善する成分であり、本発明の光学ガラス中の任意成分である。特に、Li2O成分の含有率を20.0%以下にすることで、ガラスの屈折率を低下し難くして、ガラスの安定性を高めて失透等を生じ難くすることができる。従って、酸化物換算組成のガラス全質量に対するLi2O成分の含有率は、好ましくは20.0%、より好ましくは18.0%、最も好ましくは15.0%を上限とする。Li2O成分は、原料として例えばLi2CO3、LiNO3、LiF等を用いてガラス内に含有することができる。 Li 2 O component is a component for improving the meltability of the glass, an optional component of the optical glass of the present invention. In particular, by setting the content of the Li 2 O component to 20.0% or less, it is possible to make it difficult for the refractive index of the glass to decrease, to increase the stability of the glass, and to prevent devitrification and the like. Therefore, the content of the Li 2 O component with respect to the total glass mass of the oxide conversion composition is preferably 20.0%, more preferably 18.0%, and most preferably 15.0%. The Li 2 O component can be contained in the glass using, for example, Li 2 CO 3 , LiNO 3 , LiF or the like as a raw material.
Na2O成分は、ガラスの溶融性を改善する成分であり、本発明の光学ガラス中の任意成分である。特に、Na2O成分の含有率を25.0%以下にすることで、ガラスの屈折率を低下し難くして、ガラスの安定性を高めて失透等を生じ難くすることができる。従って、酸化物換算組成のガラス全質量に対するNa2O成分の含有率は、好ましくは25.0%、より好ましくは23.0%、最も好ましくは20.0%を上限とする。Na2O成分は、原料として例えばNa2CO3、NaNO3、NaF、Na2SiF6等を用いてガラス内に含有することができる。 Na 2 O component is a component for improving the meltability of the glass, an optional component of the optical glass of the present invention. In particular, by setting the content of the Na 2 O component to 25.0% or less, it is possible to make it difficult for the refractive index of the glass to decrease, to increase the stability of the glass, and to prevent devitrification and the like. Therefore, the content of the Na 2 O component with respect to the total glass mass of the oxide conversion composition is preferably 25.0%, more preferably 23.0%, and most preferably 20.0%. The Na 2 O component can be contained in the glass using, for example, Na 2 CO 3 , NaNO 3 , NaF, Na 2 SiF 6 or the like as a raw material.
K2O成分は、ガラスの溶融性を改善する成分であり、本発明の光学ガラス中の任意成分である。特に、K2O成分の含有率を25.0%以下にすることで、ガラスの屈折率を低下し難くして、ガラスの安定性を高めて失透等を生じ難くすることができる。従って、酸化物換算組成のガラス全質量に対するK2O成分の含有率は、好ましくは25.0%、より好ましくは23.0%、最も好ましくは20.0%を上限とする。K2O成分は、原料として例えばK2CO3、KNO3、KF、KHF2、K2SiF6等を用いてガラス内に含有することができる。 K 2 O component is a component for improving the meltability of the glass, an optional component of the optical glass of the present invention. In particular, by setting the content of the K 2 O component to 25.0% or less, it is possible to make it difficult for the refractive index of the glass to be lowered, to increase the stability of the glass, and to prevent devitrification and the like. Therefore, the content of the K 2 O component with respect to the total glass mass of the oxide conversion composition is preferably 25.0%, more preferably 23.0%, and most preferably 20.0%. The K 2 O component can be contained in the glass using, for example, K 2 CO 3 , KNO 3 , KF, KHF 2 , K 2 SiF 6 or the like as a raw material.
Ta2O5成分は、ガラスの屈折率を高め、ガラスを安定化する成分であり、本発明の光学ガラス中の任意成分である。特に、Ta2O5成分の含有率を10.0%以下にすることで、ガラスの材料コストを低減するとともに、高温での溶解を回避してガラス製造時のエネルギー損失を低減することができる。従って、酸化物換算組成のガラス全質量に対するTa2O5成分の含有率は、好ましくは10.0%、より好ましくは8.0%、最も好ましくは5.0%を上限とする。Ta2O5成分は、原料として例えばTa2O5等を用いてガラス内に含有することができる。 The Ta 2 O 5 component is a component that increases the refractive index of the glass and stabilizes the glass, and is an optional component in the optical glass of the present invention. In particular, by making the content of the Ta 2 O 5 component 10.0% or less, the material cost of the glass can be reduced, and melting at high temperatures can be avoided to reduce energy loss during glass production. . Therefore, the content of the Ta 2 O 5 component with respect to the total glass mass of the oxide conversion composition is preferably 10.0%, more preferably 8.0%, and most preferably 5.0%. The Ta 2 O 5 component can be contained in the glass using, for example, Ta 2 O 5 as a raw material.
WO3成分は、ガラスの屈折率を高め、ガラスの分散を大きくして、ガラスの化学的耐久性を向上する成分であり、本発明の光学ガラス中の任意成分である。特に、WO3成分の含有率を10.0%以下にすることで、特に可視短波長(500nm以下)における透過率を悪化し難くすることができる。従って、酸化物換算組成のガラス全質量に対するWO3成分の含有率は、好ましくは10.0%、より好ましくは8.0%、最も好ましくは5.0%を上限とする。WO3成分は、原料として例えばWO3等を用いてガラス内に含有することができる。 The WO 3 component is a component that increases the refractive index of the glass, increases the dispersion of the glass, and improves the chemical durability of the glass, and is an optional component in the optical glass of the present invention. In particular, by setting the content of the WO 3 component to 10.0% or less, it is possible to make it difficult to deteriorate the transmittance particularly in the visible short wavelength (500 nm or less). Accordingly, the content of the WO 3 component with respect to the total glass mass of the oxide-converted composition is preferably 10.0%, more preferably 8.0%, and most preferably 5.0%. The WO 3 component can be contained in the glass using, for example, WO 3 as a raw material.
Sb2O3成分は、溶融ガラスを脱泡する成分であり、本発明の光学ガラス中の任意成分である。特に、Sb2O3成分の含有率を1.0%以下にすることで、可視短波長における透過率を悪化し難くし、ガラス溶融時における過度の発泡を生じ難くし、Sb2O3成分が溶解設備(特にPt等の貴金属)と合金化し難くすることができる。従って、酸化物換算組成のガラス全質量に対するSb2O3成分の含有率は、好ましくは1.0%、より好ましくは0.8%、最も好ましくは0.5%を上限とする。Sb2O3成分は、原料として例えばSb2O3、Sb2O5、Na2H2Sb2O7・5H2O等を用いてガラス内に含有することができる。 The Sb 2 O 3 component is a component that defoams the molten glass and is an optional component in the optical glass of the present invention. In particular, by setting the content of Sb 2 O 3 ingredients below 1.0%, and less likely to deteriorate the transmittance in the visible short wavelength, and less likely to occur excessive foaming during glass melting, Sb 2 O 3 component Can be made difficult to alloy with melting equipment (especially noble metals such as Pt). Therefore, the content of the Sb 2 O 3 component with respect to the total glass mass of the oxide-converted composition is preferably 1.0%, more preferably 0.8%, and most preferably 0.5%. The Sb 2 O 3 component can be contained in the glass using, for example, Sb 2 O 3 , Sb 2 O 5 , Na 2 H 2 Sb 2 O 7 · 5H 2 O, or the like as a raw material.
<含有すべきでない成分について>
次に、本発明の光学ガラスに含有すべきでない成分、及び含有することが好ましくない成分について説明する。
<About ingredients that should not be included>
Next, components that should not be contained in the optical glass of the present invention and components that are not preferably contained will be described.
本発明の光学ガラスには、他の成分を本願発明のガラスの特性を損なわない範囲で必要に応じ、添加することができる。ただし、GeO2成分はガラスの分散を高めてしまうため、実質的に含まないことが好ましい。 If necessary, other components can be added to the optical glass of the present invention as long as the properties of the glass of the present invention are not impaired. However, it is preferable that the GeO 2 component is not substantially contained since it increases the dispersion of the glass.
また、Tiを除く、V、Cr、Mn、Fe、Co、Ni、Cu、Ag及びMo等の各遷移金属成分は、それぞれを単独又は複合して少量含有した場合でもガラスが着色し、可視域の特定の波長に吸収を生じる性質があるため、特に可視領域の波長を使用する光学ガラスにおいては、実質的に含まないことが好ましい。 Moreover, even if each transition metal component such as V, Cr, Mn, Fe, Co, Ni, Cu, Ag, and Mo, excluding Ti, is contained alone or in combination with a small amount, the glass is colored and visible region. In particular, in an optical glass using a wavelength in the visible region, it is preferably substantially not contained.
さらに、PbO等の鉛化合物及びAs2O3等のヒ素化合物、並びに、Th、Cd、Tl、Os、Be、Seの各成分は、近年有害な化学物資として使用を控える傾向にあり、ガラスの製造工程のみならず、加工工程、及び製品化後の処分に至るまで環境対策上の措置が必要とされる。従って、環境上の影響を重視する場合には、不可避な混入を除き、これらを実質的に含有しないことが好ましい。これにより、光学ガラスに環境を汚染する物質が実質的に含まれなくなる。そのため、特別な環境対策上の措置を講じなくとも、この光学ガラスを製造し、加工し、及び廃棄することができる。 Furthermore, lead compounds such as PbO, arsenic compounds such as As 2 O 3 , and components of Th, Cd, Tl, Os, Be, and Se have been refraining from being used as harmful chemical substances in recent years. Environmental measures are required not only in the manufacturing process but also in the processing process and disposal after commercialization. Therefore, when importance is placed on the environmental impact, it is preferable not to substantially contain them except for inevitable mixing. As a result, the optical glass is substantially free of substances that pollute the environment. Therefore, the optical glass can be manufactured, processed, and discarded without taking any special environmental measures.
本発明のガラス組成物は、その組成が酸化物換算組成のガラス全質量に対する質量%で表されているため直接的にモル%の記載に表せるものではないが、本発明において要求される諸特性を満たすガラス組成物中に存在する各成分のモル%表示による組成は、酸化物換算組成で概ね以下の値をとる。
SiO2成分 1.0〜60.0mol%及び
B2O3成分 7.0〜75.0mol%及び
La2O3成分 2.0〜20.0mol%及び
ZnO成分 1.0〜25.0mol%、
並びに
MgO成分 0〜45.0mol%及び/又は
CaO成分 0〜30.0mol%及び/又は
SrO成分 0〜30.0mol%及び/又は
BaO成分 0〜25.0mol%及び/又は
TiO2成分 0〜12.0mol%及び/又は
Nb2O5成分 0〜7.0mol%及び/又は
ZrO2成分 0〜12.0mol%及び/又は
Gd2O3成分 0〜5.0mol%及び/又は
Y2O3成分 0〜5.0mol%及び/又は
Yb2O3成分 0〜5.0mol%及び/又は
Lu2O3成分 0〜5.0mol%及び/又は
Al2O3成分 0〜5.0mol%及び/又は
Li2O成分 0〜60.0mol%及び/又は
Na2O成分 0〜45.0mol%及び/又は
K2O成分 0〜30.0mol%及び/又は
Ta2O5成分 0〜3.0mol%及び/又は
WO3成分 0〜5.0mol%及び/又は
Sb2O3成分 0〜0.3mol%
The glass composition of the present invention cannot be expressed directly in the description of mol% because the composition is expressed by mass% with respect to the total mass of the glass of oxide conversion composition, but various properties required in the present invention. The composition expressed by mol% of each component present in the glass composition satisfying the above conditions generally takes the following values in terms of oxide conversion.
SiO 2 component 1.0~60.0Mol% and B 2 O 3 component 7.0~75.0Mol% and La 2 O 3 component 2.0~20.0Mol% and ZnO ingredients 1.0~25.0Mol% ,
And MgO component 0~45.0Mol% and / or CaO component 0~30.0Mol% and / or SrO component 0~30.0Mol% and / or BaO component 0~25.0Mol% and / or TiO 2 component 0 12.0 mol% and / or Nb 2 O 5 component 0~7.0Mol% and / or ZrO 2 component 0~12.0Mol% and / or Gd 2 O 3 component 0~5.0Mol% and / or Y 2 O 3 components 0 to 5.0 mol% and / or Yb 2 O 3 components 0 to 5.0 mol% and / or Lu 2 O 3 components 0 to 5.0 mol% and / or Al 2 O 3 components 0 to 5.0 mol% and / or Li 2 O component 0~60.0Mol% and / or Na 2 O component 0~45.0Mol% and / or K 2 O ingredient 0~30.0Mol% and / or Ta 2 O 5 formed 0~3.0Mol% and / or WO 3 components 0~5.0Mol% and / or Sb 2 O 3 component 0~0.3Mol%
[製造方法]
本発明の光学ガラスは、例えば以下のように作製される。すなわち、上記原料を各成分が所定の含有率の範囲内になるように均一に混合し、作製した混合物を白金坩堝、石英坩堝又はアルミナ坩堝に投入して粗溶融した後、金坩堝、白金坩堝、白金合金坩堝又はイリジウム坩堝に入れて1300〜1400℃の温度範囲で3〜4時間溶融し、攪拌均質化して泡切れ等を行った後、1200℃以下の温度に下げてから仕上げ攪拌を行って脈理を除去し、金型に鋳込んで徐冷することにより作製される。
[Production method]
The optical glass of the present invention is produced, for example, as follows. That is, the above raw materials are uniformly mixed so that each component is within a predetermined content range, and the prepared mixture is put into a platinum crucible, a quartz crucible or an alumina crucible and roughly melted, then a gold crucible, a platinum crucible In a platinum alloy crucible or iridium crucible, melt in a temperature range of 1300 to 1400 ° C. for 3 to 4 hours, stir to homogenize, blow out bubbles, etc., then lower the temperature to 1200 ° C. or lower and perform final stirring It is manufactured by removing the striae, casting into a mold and slow cooling.
[物性]
本発明の光学ガラスは、所望の屈折率(nd)を有するとともに、低い分散(高いアッベ数)を有する必要がある。特に、本発明の光学ガラスの屈折率(nd)は、好ましくは1.65、より好ましくは1.66、最も好ましくは1.67を下限とし、好ましくは1.77、より好ましくは1.76、最も好ましくは1.75を上限とする。また、本発明の光学ガラスのアッベ数(νd)は、好ましくは45、より好ましくは48、最も好ましくは50を下限とし、好ましくは60、より好ましくは57、最も好ましくは55を上限とする。これらにより、光学設計の自由度が広がり、更に素子の薄型化を図っても大きな光の屈折量を得ることができる。
[Physical properties]
The optical glass of the present invention needs to have a desired refractive index (n d ) and low dispersion (high Abbe number). In particular, the refractive index (n d ) of the optical glass of the present invention is preferably 1.65, more preferably 1.66, most preferably 1.67, preferably 1.77, more preferably 1.77. 76, most preferably 1.75. The Abbe number (ν d ) of the optical glass of the present invention is preferably 45, more preferably 48, most preferably 50 as the lower limit, preferably 60, more preferably 57, and most preferably 55. . As a result, the degree of freedom in optical design is increased, and a large amount of light refraction can be obtained even if the device is made thinner.
また、本発明の光学ガラスは、ガラス材料を加熱軟化して成形(リヒートプレス成形)を行う際の耐失透性が高いことや、溶融状態からガラスを形成したときの耐失透性が高いことが好ましい。より具体的には、本発明の光学ガラスのガラス転移点(Tg)と結晶化開始温度(Tx)との差ΔTは、好ましくは100℃、より好ましくは110℃、最も好ましくは118℃を下限とする。また、本発明の光学ガラスに対して示差熱分析(DTA)を行った融液から降温する際の結晶化による発熱ピーク温度は、好ましくは750℃、より好ましくは730℃、最も好ましくは700℃を上限とする。これらにより、ガラスの熱的安定性が高められてガラス成分の結晶核の生成が低減されるとともに、より低い温度で溶融ガラスを流出してガラスを形成してもガラス成分の結晶の成長が低減されるため、失透によるガラスの光学特性への影響を低減することができる。 The optical glass of the present invention has high devitrification resistance when glass material is heated and softened to perform molding (reheat press molding), and high devitrification resistance when glass is formed from a molten state. It is preferable. More specifically, the difference ΔT between the glass transition point (Tg) and the crystallization start temperature (Tx) of the optical glass of the present invention is preferably 100 ° C., more preferably 110 ° C., and most preferably 118 ° C. And The exothermic peak temperature due to crystallization when the temperature is lowered from the melt obtained by performing differential thermal analysis (DTA) on the optical glass of the present invention is preferably 750 ° C., more preferably 730 ° C., most preferably 700 ° C. Is the upper limit. These increase the thermal stability of the glass and reduce the generation of crystal nuclei of the glass component, and also reduce the growth of crystal of the glass component even when the molten glass flows out at a lower temperature to form the glass. Therefore, the influence on the optical characteristics of the glass due to devitrification can be reduced.
[光学素子及び光学機器]
このように、本発明の光学ガラスは、様々な光学素子及び光学設計に有用であるが、その中でも特に、本発明の光学ガラスからリヒートプレス成形や精密プレス成形等の手段を用いて、レンズやプリズム等の光学素子を作製することが好ましい。これにより、カメラやプロジェクタ等の光学機器に用いたときに、高精細で高精度な結像特性及び投影特性を実現することができる。
[Optical elements and optical equipment]
As described above, the optical glass of the present invention is useful for various optical elements and optical designs. Among them, in particular, the optical glass of the present invention is used for a lens, a reheat press molding, a precision press molding, or the like. It is preferable to produce an optical element such as a prism. Thereby, when used in an optical apparatus such as a camera or a projector, it is possible to realize high-definition and high-precision imaging characteristics and projection characteristics.
本発明の実施例(No.1〜No.15)及び比較例(No.1)のガラスの組成、及び、これらのガラスの屈折率(nd)、アッベ数(νd)、ガラス転移点(Tg)、結晶化開始温度(Tx)、ガラス転移点及び結晶化開始温度の差(ΔT)、並びに、結晶化ピーク温度の結果を表1及び表2に示す。このうち、実施例(No.4〜No.11)と実施例(No.13〜No.15)は、本発明の参考例である。なお、以下の実施例はあくまで例示の目的であり、これらの実施例のみ限定されるものではない。
Composition of the glass of Examples (No. 1 to No. 15) and Comparative Example (No. 1) of the present invention, and the refractive index (nd), Abbe number (νd), and glass transition point (Tg) of these glasses. ), Crystallization start temperature (Tx), difference between glass transition point and crystallization start temperature (ΔT), and crystallization peak temperature results are shown in Tables 1 and 2. Among these, Examples ( No. 4 to No. 11 ) and Examples ( No. 13 to No. 15) are reference examples of the present invention. The following examples are merely for illustrative purposes, and are not limited to these examples.
本発明の実施例(No.1〜No.15)の光学ガラス及び比較例(No.1)のガラスは、いずれも各成分の原料として各々相当する酸化物、水酸化物、炭酸塩、硝酸塩、弗化物、水酸化物、メタ燐酸化合物等の通常の光学ガラスに使用される高純度原料を選定し、表1及び表2に示した各実施例及び比較例の組成の割合になるように秤量して均一に混合した後、白金坩堝に投入し、ガラス組成の熔融難易度に応じて電気炉で1300〜1350℃の温度範囲で3〜4時間溶解し、攪拌均質化して泡切れ等を行った後、1150℃以下に温度を下げて攪拌均質化してから金型に鋳込み、徐冷してガラスを作製した。 The optical glass of Examples (No. 1 to No. 15) of the present invention and the glass of Comparative Example (No. 1) are all oxides, hydroxides, carbonates and nitrates corresponding to the raw materials of the respective components. Select high-purity raw materials used in ordinary optical glass such as fluorides, hydroxides, metaphosphoric acid compounds, etc., so that the composition ratios of the examples and comparative examples shown in Tables 1 and 2 are obtained. After weighing and mixing uniformly, it is put into a platinum crucible and melted in a temperature range of 1300 to 1350 ° C. for 3 to 4 hours in accordance with the melting difficulty of the glass composition, and homogenized with stirring to remove bubbles. Then, the temperature was lowered to 1150 ° C. or lower, and the mixture was homogenized with stirring, cast into a mold, and slowly cooled to produce glass.
ここで、実施例(No.1〜No.15)の光学ガラス及び比較例(No.1)のガラスの屈折率(nd)、アッベ数(νd)は、徐冷降温速度を−25℃/hにして得られたガラスについて測定を行うことで求めた。 Here, the refractive index (n d ) and Abbe number (ν d ) of the optical glass of the example (No. 1 to No. 15) and the glass of the comparative example (No. 1) are set to -25. It calculated | required by measuring about the glass obtained by setting it at (degreeC / h).
また、実施例(No.1〜No.15)の光学ガラス及び比較例(No.1)のガラスのガラス転移点(Tg)及び結晶化開始温度(Tx)は、示差熱測定装置(ネッチゲレテバウ社製 STA 409 CD)を用いた測定を行うことで求めた。ここで、測定を行う際のサンプル粒度は425〜600μmとし、昇温速度は10℃/minとした。また、ΔTは、上記により求められたガラス転移点(Tg)と結晶化開始温度(Tx)との差から求めた。さらに、上記昇温を1200℃まで行って完全に融液の状態にした後に、降温速度を10℃/minとして300℃まで冷却することにより、融液からの結晶化ピーク温度を求めた。 Moreover, the glass transition point (Tg) and the crystallization start temperature (Tx) of the optical glass of Examples (No. 1 to No. 15) and the glass of Comparative Example (No. 1) were measured with a differential heat measuring apparatus (Netchgeretebau). It was determined by carrying out measurement using STA 409 CD manufactured by the company. Here, the sample particle size at the time of measurement was set to 425-600 micrometers, and the temperature increase rate was 10 degrees C / min. ΔT was determined from the difference between the glass transition point (Tg) determined above and the crystallization start temperature (Tx). Further, after the temperature was raised to 1200 ° C. to make it completely in a melt state, the temperature was lowered to 300 ° C. at a temperature lowering rate of 10 ° C./min to obtain the crystallization peak temperature from the melt.
表1及び表2に表されるように、本発明の実施例の光学ガラスは、示差熱分析(DTA)を用いて測定したところ、ΔTは100℃以上、より詳細には110℃以上であった。一方で、比較例のガラスは、ΔTが100℃未満であった。また、いずれも融液からの結晶化ピーク温度が750℃以下、より詳細には700℃以下であった。このため、本発明の実施例の光学ガラスは、比較例のガラスに比べてガラス成分の結晶核が生成し難く、また結晶核から結晶が成長し難いため、ガラスの耐失透性が高いことが明らかになった。 As shown in Tables 1 and 2, the optical glasses of the examples of the present invention were measured using differential thermal analysis (DTA), and ΔT was 100 ° C. or higher, more specifically 110 ° C. or higher. It was. On the other hand, the glass of the comparative example had a ΔT of less than 100 ° C. In all cases, the crystallization peak temperature from the melt was 750 ° C. or lower, more specifically 700 ° C. or lower. For this reason, the optical glass of the example of the present invention is less likely to generate crystal nuclei of the glass component than the glass of the comparative example, and it is difficult for crystals to grow from the crystal nuclei. Became clear.
また、本発明の実施例の光学ガラスは、いずれも屈折率(nd)が1.65以上、より詳細には1.67以上であるとともに、この屈折率(nd)は1.77以下、より詳細には1.75以下であり、所望の範囲内であった。 The optical glasses of the examples of the present invention all have a refractive index (n d ) of 1.65 or more, more specifically 1.67 or more, and this refractive index (n d ) is 1.77 or less. More specifically, it was 1.75 or less, and was within a desired range.
また、本発明の実施例の光学ガラスは、いずれもアッベ数(νd)が45以上、より詳細には50以上であるとともに、このアッベ数(νd)は60以下、より詳細には55以下であり、所望の範囲内であった。一方で、比較例のガラスは、アッベ数(νd)が45未満であった。 The optical glasses of the examples of the present invention all have an Abbe number (ν d ) of 45 or more, more specifically 50 or more, and the Abbe number (ν d ) of 60 or less, more specifically 55. And within the desired range. On the other hand, the glass of the comparative example had an Abbe number (ν d ) of less than 45.
従って、本発明の実施例の光学ガラスは、屈折率(nd)、アッベ数(νd)が所望の範囲内にありながら、溶融状態からガラスを形成したときの耐失透性が高いことが明らかになった。 Therefore, the optical glass of the embodiment of the present invention has high devitrification resistance when the glass is formed from a molten state while the refractive index (n d ) and Abbe number (ν d ) are within the desired ranges. Became clear.
さらに、本発明の実施例の光学ガラスを用いて、リヒートプレス成形を行った後で研削及び研磨を行い、レンズ及びプリズムの形状に加工した。また、本発明の実施例の光学ガラスを用いて、精密プレス成形用プリフォームを形成し、精密プレス成形用プリフォームを精密プレス成形加工した。いずれの場合も、加熱軟化後のガラスに乳白化及び失透等の問題は生じず、安定に様々なレンズ及びプリズムの形状に加工することができた。 Furthermore, using the optical glass of the example of the present invention, after performing reheat press molding, grinding and polishing were performed to process into the shape of a lens and a prism. Further, a precision press-molding preform was formed using the optical glass of the example of the present invention, and the precision press-molding preform was precision press-molded. In any case, problems such as opacification and devitrification did not occur in the glass after heat softening, and it could be stably processed into various lens and prism shapes.
以上、本発明を例示の目的で詳細に説明したが、本実施例はあくまで例示の目的のみであって、本発明の思想及び範囲を逸脱することなく多くの改変を当業者により成し得ることが理解されよう。 Although the present invention has been described in detail for the purpose of illustration, this embodiment is only for the purpose of illustration, and many modifications can be made by those skilled in the art without departing from the spirit and scope of the present invention. Will be understood.
Claims (6)
SiO2成分を1.5〜36.5%、
B2O3成分を8.0〜43.0%、
La2O3成分を8.0〜50.0%、及び
ZnO成分を3.59〜20.0%(但し、ZnO成分の含有量が12%以上のものを除く)
を含有し、
任意成分である
CaO成分の含有量が0〜11.00%、
ZrO2成分の含有量が0〜3.90%、
Gd2O3成分の含有量が0〜10.0%、
Li2O成分の含有量が0〜0.50%、
MgO成分の含有量が0〜15.0%、
SrO成分の含有量が0〜25.0%、
BaO成分の含有量が0〜13.71%、
TiO2成分の含有量が0〜10.0%、
Nb2O5成分の含有量が0〜15.0%、
Y2O3成分の含有量が0〜10.0%、
Yb2O3成分の含有量が0〜10.0%、
Lu2O3成分の含有量が0〜10.0%、
Al2O3成分の含有量が0〜5.0%、
Ta2O5成分の含有量が0〜10.0%、
WO3成分の含有量が0〜10.0%及び
Sb2O3成分の含有量が0〜1.0%
であり(但し、SnO2成分の含有量が0.05%以上のものを除く)、
質量和(SiO 2 +B 2 O 3 )が44.5%以下であり、
質量和(MgO+CaO+SrO+BaO)が1.5%以上38.0%以下であり、
質量比(MgO+CaO+SrO+BaO)/(SiO2)が0.60以上1.68以下であり、
質量和(TiO2+Nb2O5+ZrO2)が2.8%以上17.0%以下であり、
質量和(SiO2+B2O3+La2O3+ZnO+MgO+CaO+SrO+BaO+TiO2+Nb2O5+ZrO2+Y2O3+Al2O3)が90.0%以上であり、
質量和(La2O3+Gd2O3+Y2O3+Yb2O3+Lu2O3)が8.0%以上56.0%以下であり、
質量比(La2O3+Gd2O3+Y2O3+Yb2O3+Lu2O3)/(La2O3)が1.00以上1.20以下であり、
実質的に鉛化合物及びヒ素化合物を含有しない、
1.65以上1.77以下の屈折率(nd)を有し、48以上60以下のアッベ数(νd)を有し、ガラス転移点(Tg)と結晶化開始温度(Tx)との差ΔTが100℃以上である光学ガラス。 With respect to the total mass of the glass with an oxide conversion composition, the SiO 2 component is 1.5 to 36.5% by mass % ,
B 2 O 3 component is 8.0 to 43.0% ,
La 2 O 3 component is 8.0 to 50.0% , and ZnO component is 3.59 to 20.0% (excluding ZnO component content of 12% or more)
Containing
The content of the optional component CaO is 0 to 11.00%,
The content of ZrO 2 component is 0 to 3.90%,
The content of Gd 2 O 3 component is 0 to 10.0%,
The content of the Li 2 O component is 0 to 0.50%,
The content of MgO component is 0 to 15.0%,
SrO component content is 0-25.0%,
The content of the BaO component is 0 to 13.71%,
The content of TiO 2 component is 0 to 10.0%,
The content of Nb 2 O 5 component is 0 to 15.0%,
The content of Y 2 O 3 component is 0 to 10.0%,
The content of Yb 2 O 3 component is 0 to 10.0%,
The content of the Lu 2 O 3 component is 0 to 10.0%,
The content of Al 2 O 3 component is 0 to 5.0%,
Content of Ta 2 O 5 component is 0 to 10.0%,
WO 3 component content is 0 to 10.0% and Sb 2 O 3 component content is 0 to 1.0%
(However, except for SnO 2 content of 0.05% or more),
The mass sum (SiO 2 + B 2 O 3 ) is 44.5% or less,
The mass sum (MgO + CaO + SrO + BaO) is 1.5% or more and 38.0% or less,
The mass ratio (MgO + CaO + SrO + BaO) / (SiO 2 ) is 0.60 or more and 1.68 or less,
The mass sum (TiO 2 + Nb 2 O 5 + ZrO 2 ) is 2.8% or more and 17.0% or less,
The mass sum (SiO 2 + B 2 O 3 + La 2 O 3 + ZnO + MgO + CaO + SrO + BaO + TiO 2 + Nb 2 O 5 + ZrO 2 + Y 2 O 3 + Al 2 O 3 ) is 90.0% or more,
The mass sum (La 2 O 3 + Gd 2 O 3 + Y 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ) is 8.0% or more and 56.0% or less,
The mass ratio (La 2 O 3 + Gd 2 O 3 + Y 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ) / (La 2 O 3 ) is 1.00 or more and 1.20 or less,
Substantially free of lead and arsenic compounds,
A 1.65 1.77 less refractive index (n d), have a 48 or more 60 or less Abbe number (ν d), the glass transition point (Tg) and the crystallization initiation temperature (Tx) An optical glass having a difference ΔT of 100 ° C. or more .
Na2O成分 0〜0.20%、
K2O成分 0〜0.20%
の各成分をさらに含有する請求項1記載の光学ガラス。 Na 2 O component 0 to 0.20% in mass% with respect to the total glass mass of oxide conversion composition,
K 2 O component 0 to 0.20%
The optical glass according to claim 1, further comprising: