JP5703770B2 - 難燃性粘着剤及び難燃性粘着テープ - Google Patents
難燃性粘着剤及び難燃性粘着テープ Download PDFInfo
- Publication number
- JP5703770B2 JP5703770B2 JP2011009357A JP2011009357A JP5703770B2 JP 5703770 B2 JP5703770 B2 JP 5703770B2 JP 2011009357 A JP2011009357 A JP 2011009357A JP 2011009357 A JP2011009357 A JP 2011009357A JP 5703770 B2 JP5703770 B2 JP 5703770B2
- Authority
- JP
- Japan
- Prior art keywords
- flame retardant
- parts
- acrylic polymer
- sensitive adhesive
- adhesive tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記ホスフィン酸塩(C)を、アクリル系ポリマー(A)100重量部に対して、30〜70重量部含有し、
さらに前記ホスフィン酸塩(C)の平均粒子径が0.1μm以上〜20μm以下であることを特徴とする難燃性粘着剤である。
一般式(1)
第二の発明は、基材と請求項1記載の難燃性粘着剤から形成されてなる粘着剤層を有することを特徴とする難燃性粘着テープである。
一般式(1)
上記ホスフィン酸塩(C)としては、たとえば、トリスジエチルホスフィン酸アルミニウム、トリスメチルエチルホスフィン酸アルミニウム、トリスジフェニルホスフィン酸アルミニウム、ビスジエチルホスフィン酸亜鉛、ビスメチルエチルホスフィン酸亜鉛、ビスジフェニルホスフィン酸亜鉛、ビスジエチルホスフィン酸チタニル、テトラキスジエチルホスフィン酸チタン、ビスメチルエチルホスフィン酸チタニル、テトラキスメチルエチルホスフィン酸チタン、ビスジフェニルホスフィン酸チタニル、テトラキスジフェニルホスフィン酸チタン等およびそれらの任意の混合物よりなる群から選択されるもの等が挙げられる。これらの中でもトリスジエチルホスフィン酸アルミニウムが特に好適に用いられる。
<アクリル系ポリマー(A)合成例1>
攪拌機、温度計、還流冷却器、滴下装置、窒素導入管を備えた反応容器に、n−ブチル
アクリレート99.85部、アクリル酸0.15部、酢酸エチル121.0部、ベンゾイルパーオキサイド0.2部を仕込み、攪拌しながら反応器中の空気を窒素置換し、還流するまで昇温して保持し、合計5 時間反応させた。反応終了後、酢酸エチル34.4部、トルエン28.3部、重合禁止剤として2、5−ジターシャリブチルハイドロキノン0.5部を添加して希釈し、室温まで冷却し、不揮発分34.0%のアクリル系ポリマー1の溶液を得た。アクリル系ポリマー1の重量平均分子量は50万であった。
n−ブチルアクリレート99.7部、アクリル酸0.3部とした以外は、合成例1と同様な手順で反応を行い、不揮発分34.0%のアクリル系ポリマー2の溶液を得た。アクリル系ポリマー2の重量平均分子量は55万であった。
n−ブチルアクリレート98.0部、アクリル酸2.0部とした以外は、合成例1と同様な手順で反応を行い、不揮発分34.0%のアクリル系ポリマー3の溶液を得た。アクリル系ポリマー3の重量平均分子量は60万であった。
n−ブチルアクリレート94.0部、アクリル酸6.0部とした以外は、合成例1と同様な手順で反応を行い、不揮発分34.0%のアクリル系ポリマー4の溶液を得た。アクリル系ポリマー4の重量平均分子量は61万であった。
n−ブチルアクリレート90.0部、アクリル酸10.0部とした以外は、合成例1と同様な手順で反応を行い、不揮発分34.0%のアクリル系ポリマー5の溶液を得た。アクリル系ポリマー5の重量平均分子量は70万であった。
n−ブチルアクリレート80.0部、アクリル酸20.0部とした以外は、合成例1と同様な手順で反応を行ったが、反応途中でゲル化してしまった。
n−ブチルアクリレート100.0部とした以外は、合成例1と同様な手順で反応を行い、不揮発分34.0%のアクリル系ポリマー7の溶液を得た。アクリル系ポリマー7の重量平均分子量は55万であった。
合成例1で得られたアクリル系ポリマー(A)溶液100部、ホスフィン酸塩(B)としてトリスジエチルホスフィン酸アルミニウム(クラリアントジャパン株式会社製:エクソリットOP−935 平均粒子径2〜3μm)68部、ついでこの溶液にメチルエチルケトンを加えて、不揮発分が30.0%になるように調製し、溶液を十分に攪拌した後に直径3.0mmのガラスビーズ(ポッターズ・バロティーニ社製)を用いてペイントコンデショナーで1時間分散し難燃剤分散液1を得た。
アクリル系ポリマー(A)として合成例2で得られたアクリル系ポリマー溶液を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液2を得た。
アクリル系ポリマー(A)として合成例2で得られたアクリル系ポリマー溶液、ホスフィン酸塩(B)としてトリスジエチルホスフィン酸アルミニウム(クラリアントジャパン株式会社製:エクソリットOP−935 平均粒子径2〜3μm)102部を用いた以外は、分散液調整例1と同様の配合、手順で難燃剤分散液3を得た。
アクリル系ポリマー(A)として合成例3で得られたアクリル系ポリマー溶液を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液4を得た。
アクリル系ポリマー(A)として合成例4で得られたアクリル系ポリマー溶液を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液5を得た。
アクリル系ポリマー(A)として合成例4で得られたアクリル系ポリマー溶液を用いた以外は、難燃剤分散液調整例3と同様の配合、手順で難燃剤分散液6を得た。
アクリル系ポリマー(A)として合成例5で得られたアクリル系ポリマー溶液を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液7を得た。
アクリル系ポリマー(A)として合成例7で得られたアクリル系ポリマー溶液を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液8を得た。
アクリル系ポリマー(A)として合成例3で得られたアクリル系ポリマー溶液とホスフィン酸塩(B)の代わりに水酸化アルミニウム(日本軽金属株式会社製:BF−013 平均粒子径1〜2μm)を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液9を得た。
アクリル系ポリマー(A)として合成例4で得られたアクリル系ポリマー溶液とホスフィン酸塩(B)の代わりに水酸化アルミニウム(日本軽金属株式会社製:BF−013平均粒子径1〜2μm)を用いた以外は、難燃剤分散液調整例3と同様の配合、手順で難燃剤分散液10を得た。
アクリル系ポリマー(A)として合成例3で得られたアクリル系ポリマー溶液とホスフィン酸塩( B )の代わりにメラミンシアヌレート(CBC株式会社:BUDIT315S 平均粒子径3μm)を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液11を得た。
アクリル系ポリマー(A)として合成例4で得られたアクリル系ポリマー溶液とホスフィン酸塩(B)の代わりにメラミンシアヌレート(CBC株式会社:BUDIT315S 平均粒子径3μm)を用いた以外は、難燃剤分散液調整例3と同様の配合、手順で難燃剤分散液12を得た。
アクリル系ポリマー(A)として合成例3で得られたアクリル系ポリマー溶液とホスフィン酸塩(B)の代わりにポリリン酸アンモニウム(CBC株式会社:C−60 平均粒子径7〜8μm)を用いた以外は、難燃剤分散液調整例1と同様の配合、手順で難燃剤分散液13を得た。
アクリル系ポリマー(A)として合成例4で得られたアクリル系ポリマー溶液とホスフィン酸塩(B)の代わりにポリリン酸アンモニウム(CBC株式会社:C−60 平均粒子径7〜8μm)を用いた以外は、難燃剤分散液調整例3と同様の配合、手順で難燃剤分散液14を得た。
得られた難燃剤分散液を23℃で放置し、経時での安定性を確認し、次の基準で評価した。結果は表1に示す。
◎・・・1週間放置後の分散液に変化がない
○・・・1週間放置後の分散液にほとんど変化がない
△・・・1週間放置後の分散液に凝集物が生じた
×・・・1週間以内に分散液がゲル化した。
難燃剤分散液例1で得られた難燃剤分散液100部に対して、合成例1で得られたアクリル系ポリマー(A)を88.2部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)0.7部を添加して良く攪拌し、粘着剤溶液を得た。得られた粘着剤溶液を、ドクターブレードで乾燥膜厚45μmとなるように、厚さ75μm の剥離シート上に塗布し、乾燥させ、粘着剤層を形成し、次いで厚さ25μmのPETフィルムの片面、及び坪量が6g/m2のレーヨン不織布の両面にラミネートして、PETフィルム/粘着剤層/剥離シートからなる片面粘着テープ1及び、剥離シート/粘着剤層/不織布/粘着剤層/剥離シートからなる両面粘着テープ1をそれぞれ得た。この粘着テープを23℃50%RHの雰囲気下で7日間熟成させた。
難燃剤分散液例2で得られた難燃剤分散液100部に対して、合成例2で得られたアクリル系ポリマー(A)88.2部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ2及び両面粘着テープ2を得た。
難燃剤分散液例4で得られた難燃剤分散液100部に対して、合成例3で得られたアクリル系ポリマー(A)88.2部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ3及び両面粘着テープ3を得た
難燃剤分散液例5で得られた難燃剤分散液100部に対して、合成例4で得られたアクリル系ポリマー(A)138.7部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)1.1部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ4及び両面粘着テープ4を得た。
難燃剤分散液例5で得られた難燃剤分散液100部に対して、合成例4で得られたアクリル系ポリマー(A)88.2部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ5及び両面粘着テープ5を得た。
難燃剤分散液例5で得られた難燃剤分散液100部に対して、合成例4で得られたアクリル系ポリマー(A)61.1部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)0.6部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ6及び両面粘着テープ6を得た。
難燃剤分散液例7で得られた難燃剤分散液100部に対して、合成例5で得られたアクリル系ポリマー(A)88.2部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ7及び両面粘着テープ7を得た。
難燃剤分散液例5で得られた難燃剤分散液100部に対して、合成例4で得られたアクリル系ポリマー(A)166.7部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)1.3部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ8及び両面粘着テープ8を得た。
難燃剤分散液例5で得られた難燃剤分散液100部に対して、合成例4で得られたアクリル系ポリマー(A)29.4部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)0.4部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ9及び両面粘着テープ9を得た。
難燃剤分散液例8で得られた難燃剤分散液100部に対して、合成例7で得られたアクリル系ポリマー(A)88.2部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ10及び両面粘着テープ10を得た。
難燃剤分散液例9で得られた難燃剤分散液100部に対して、合成例3で得られたアクリル系ポリマー(A)29.4部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)0.4部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ11及び両面粘着テープ11を得た。
難燃剤分散液例11で得られた難燃剤分散液100部に対して、合成例3で得られたアクリル系ポリマー(A)88.2部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ12及び両面粘着テープ12を得た。
難燃剤分散液例11で得られた難燃剤分散液100部に対して、合成例3で得られたアクリル系ポリマー(A)29.4部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)0.4部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ13及び両面粘着テープ13を得た。
難燃剤分散液例14で得られた難燃剤分散液100部に対して、合成例4で得られたアクリル系ポリマー(A)88.2部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ14及び両面粘着テープ14を得た。
難燃剤分散液例14で得られた難燃剤分散液100部に対して、合成例4で得られたアクリル系ポリマー(A)29.4部、架橋剤としてTDI/TMP(トリレンジイソシネートのトリメチロールプロパンアダクト体)0.4部を用いた以外は、実施例1と同様な配合、手順で片面粘着テープ15及び両面粘着テープ15を得た。
合成例4で得られたアクリル系ポリマー(A)を100重量部に対して、難燃剤としてホスフィン酸塩(B)の代わりにホスファゼン(大塚化学株式会社:SPB−100)17部を17部のMEKで溶解させて添加して良く攪拌し、粘着剤溶液を得た以外は、実施例1と同様な配合、手順で片面粘着テープ16及び両面粘着テープ16を得た
上記片面粘着テープを23℃×50%RHの標準状態において、それぞれ25mm幅×100mm長さでカットし、ステンレス板に2kgのゴムローラーを1往復させて貼り付け、同標準状態で24時間放置後、85℃及び60℃×95%RH環境下で168時間放置後、引っ張り速度300mm/分、剥離角度180°の条件で引っ張り試験機にて粘着力を測定した。
上記片面粘着テープを23℃×50%RHの標準状態において、それぞれ25mm幅×100mm長さでカットし、そのうち25mm幅×25mm長さをステンレス板に2kgのゴムローラーを1往復させて貼り付け、貼付から20分後に80℃雰囲気下1kgfの荷重をかけ、1時間後のズレ距離または落下時間を測定した。
上記両面粘着テープを用いて、UL規格(UL94:薄手材料垂直燃焼試験)に準じて燃焼試験を行って判定した。
○:UL94規格VTM−0グレードを達成できる。
△:UL94規格VTM−1グレードを達成できる。
×:UL94規格VTM−0、VTM−1グレードを達成できない。
Claims (2)
- 少なくともカルボキシル基含有モノマー(a)を0.1〜15重量%用いてなるアクリル系ポリマー(A)と、イソシアネート系硬化剤(B)と、下記一般式(1)で示されるホスフィン酸塩(C)とを含む難燃性粘着剤であって、
前記ホスフィン酸塩(C)を、アクリル系ポリマー(A)100重量部に対して、30〜65重量部含有し、
さらに前記ホスフィン酸塩(C)の平均粒子径が0.1μm以上〜20μm以下であることを特徴とする難燃性粘着剤。
一般式(1)
- 基材と、請求項1記載の難燃性粘着剤から形成されてなる粘着剤層とを有することを特徴とする難燃性粘着テープ。