JP5563908B2 - ナノファイバシート - Google Patents
ナノファイバシート Download PDFInfo
- Publication number
- JP5563908B2 JP5563908B2 JP2010147371A JP2010147371A JP5563908B2 JP 5563908 B2 JP5563908 B2 JP 5563908B2 JP 2010147371 A JP2010147371 A JP 2010147371A JP 2010147371 A JP2010147371 A JP 2010147371A JP 5563908 B2 JP5563908 B2 JP 5563908B2
- Authority
- JP
- Japan
- Prior art keywords
- nanofiber
- layer
- base material
- material layer
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
基材層の初期帯電圧は、JIS L1094の帯電性試験方法に規定される半減期測定方法に従い、オネストメーター(シシド静電気社製、型番H−0110)を用いて、23℃、50%RHの環境下で測定する。初期帯電圧の測定は、基材層におけるナノファイバ層の積層面について実施する。測定条件は次の通り。印加電圧:10kV、印加電極と試料間の距離:15mm、受電圧部と試料間の距離:15mm。
サンプルを測定環境下で安定化させるため、23℃、50%RHの環境下でサンプルを4時間放置した後に、サンプルの表面低効率の測定を行う。JIS K6271の6項に規定される2重リング法による方法で500Vの電圧で測定する。表面低効率の測定にはADVANTEST社製の表面抵抗計R8340を用いることができる。
基材層における個々の開孔の面積は、好ましくは0.001mm2以上、更に好ましくは0.002〜5mm2である。
基材層の開孔率(1平方インチ当たりの空間面積/1平方インチ)は、好ましくは30%以上、更に好ましくは50〜90%である。
基材層における開孔の数は、1インチあたり5〜400個、好ましくは10〜200個である。個々の開孔の面積、開孔率、及び開孔の数は顕微鏡で観察し、画像から直接読み取ることで求めることができる。
開孔の平面視における形状は、特に限定されず、例えば円形、楕円形、四角形、菱形等とすることができる。
高分子化合物としてプルラン(水溶性高分子化合物、林原商事(株)製)を用い、これをイオン交換水に溶解し、濃度15%のエレクトロスピニング(ES)用溶液を得た。このES用溶液を用い、図1に示す装置によって、通気性を有する基材層となるべきメッシュシート(東京スクリーン株式会社製のポリエチレンテレフタレートメッシュ、商品名:ボルティングクロス テトロンT-No.120T)の表面にナノファイバ層を形成し、ナノファイバ層及び基材層の2層構造からなるナノファイバシートを得た。ナノファイバの製造条件は次のとおりである。印加電圧:27kV、キャピラリ−コレクタ間距離:185mm、水溶液吐出量:1ml/h、製造環境:28℃、36%RH。このようにして得られた実施例1のナノファイバシートにおけるナノファイバ層の厚みは30μm、ナノファイバの太さは300〜600nmであった。
実施例1において、基材層として下記表1に示すものを用いた以外は、実施例1と同様にしてナノファイバシートを得た。各実施例及び比較例で得られたナノファイバシートにおけるナノファイバ層の厚みは30μm、ナノファイバの太さは300〜600nmであった。
・実施例1(メッシュシート):東京スクリーン株式会社製のポリエチレンテレフタレートメッシュ(商品名:ボルティングクロス テトロンT-No.120T)であり、開孔(目開き)の平面視における形状は四角形であり、開孔率は52%、開孔の数は1インチあたり120個。
・実施例2(メッシュシート):東京スクリーン株式会社製のポリエチレンテレフタレートメッシュ(商品名:ボルティングクロス テトロンT-No.80T)であり、開孔(目開き)の平面視における形状は四角形であり、開孔率は47%、開孔の数は1インチあたり80個。
・比較例1(スパンボンド不織布):構成繊維はポリエチレンテレフタレート繊維、坪量16g/m2。
・比較例2(OA紙):構成繊維はパルプ、厚み100μm。
・比較例3(ポリエチレンテレフタレートフィルム):厚み25μm。
実施例及び比較例で得られたナノファイバシートについて、以下の方法で、ナノファイバ層におけるナノファイバの均一性について評価した。その結果を下記表1に示す。
ナノファイバシートにおけるナノファイバ層の表面を目視で観察し、下記評価基準に従って評価する。
○:ナノファイバの分布にムラがなく、ナノファイバが基材層におけるナノファイバ層の積層面上に均一に付着している。
×:基材層におけるナノファイバ層の積層面全体にナノファイバが付着しているが、ナノファイバの分布に細かいムラが見られる。
××:基材層におけるナノファイバ層の積層面において、ナノファイバが付着している部分と付着していない部分とが存在し、ナノファイバの分布に大きなムラが見られる。
31 シリンジ
32 高電圧源
33 導電性コレクタ
Claims (2)
- 基材層と、該基材層に積層され且つエレクトロスピニング法によって形成されたナノファイバを含むナノファイバ層とを備えたナノファイバシートであって、
前記基材層のJIS L1094に規定される半減期測定方法で測定される初期帯電圧が0.3kV以下であり、
前記基材層は、樹脂からなるメッシュシートであり、該基材層に多数の開孔が形成されているナノファイバシート。 - 前記樹脂は、ポリエチレン、ポリプロピレン、ポリアミド、ポリウレタン、ポリスチレン、エチレン−酢酸ビニル共重合体又はポリエチレンテレフタレートである請求項1記載のナノファイバシート。