JP5503196B2 - 活性炭の製造方法および該製造方法により得られた活性炭を用いた電気二重層キャパシタ - Google Patents
活性炭の製造方法および該製造方法により得られた活性炭を用いた電気二重層キャパシタ Download PDFInfo
- Publication number
- JP5503196B2 JP5503196B2 JP2009146782A JP2009146782A JP5503196B2 JP 5503196 B2 JP5503196 B2 JP 5503196B2 JP 2009146782 A JP2009146782 A JP 2009146782A JP 2009146782 A JP2009146782 A JP 2009146782A JP 5503196 B2 JP5503196 B2 JP 5503196B2
- Authority
- JP
- Japan
- Prior art keywords
- activated carbon
- organic compound
- raw material
- carbon
- carbon raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
活性炭0.2gを200℃にて真空加熱した後、窒素吸着装置(Micromeritics社製、「ASAP−2400」)を用いてN2ガス吸着法による吸着等温線を求め、BET法により比表面積および全細孔容積を求めた。また、平均細孔径は、BET法により求められた比表面積および細孔径1.0nm〜30nmの範囲における細孔容積を用いて、下記式(1)に基づいて算出した。
炭素原料としての石炭ピッチコークス(三菱化学社製、石炭ピッチコークス、平均粒子径75μm未満)20.00g、有機化合物としてのN−メチル−2−ピロリドン10.28g(有機化合物/炭素原料(質量比)=0.5)、水酸化カリウム50g(水酸化カリウム/炭素原料(質量比)=2.5)を、ステンレス容器に入れ、室温(25℃)でスパチュラを用いて混合を行った。
有機化合物であるN−メチル−2−ピロリドン(NMP)の使用量を1.03g(有機化合物/炭素原料(質量比)=0.05)に変更したこと以外は、製造例1と同様にして活性炭を得た。得られた活性炭について評価し、結果を表1に示した。
有機化合物であるN−メチル−2−ピロリドン(NMP)の使用量を51.40g(有機化合物/炭素原料(質量比)=2.6)に変更したこと以外は、製造例1と同様にして活性炭を得た。得られた活性炭について評価し、結果を表1に示した。
有機化合物を、トルエン43.35g(有機溶媒/炭素原料(質量比)=2.2)に変更したこと以外は、製造例1と同様にして活性炭を得た。得られた活性炭について評価し、結果を表1に示した。
紙基材としてクラフト紙(坪量200g/m2)を用い、フェノール樹脂としてレゾール樹脂からなるフェノール樹脂ワニスを調製し、塗布樹脂量が紙基材70質量部に対し30質量部となるように紙基材に塗布し含浸させ、約160℃で乾燥してプリプレグを作製した。複数枚のプリプレグを積層し、両側をステンレス鋼製の鏡面板で挟み、さらにその両外側にクッション材を重ね、多段式油圧プレス機の熱盤間にセットした。この状態で、温度140℃、圧力6.9MPa(70kgf/cm2)、時間90分の条件で熱プレスした後、解板、耳切りを行って、寸法1020mm×1020mmで厚さ1.5mmの紙−フェノール樹脂積層板を得た。得られた紙−フェノール樹脂積層板を5mm以下に粉砕した。
上記製造例4で作製した紙−フェノール樹脂積層板(平均粒子径5mm未満)を、窒素雰囲気下、700℃で2時間加熱処理し、紙−フェノール樹脂積層板炭化物を得た。
有機化合物を使用しなかったこと以外は、製造例1、5、6と同様のアルカリ賦活剤使用量(水酸化カリウム/炭素原料(質量比)=2.5)および熱処理条件にて活性炭を得た。得られた活性炭について評価し、結果を表1に示した。
Claims (5)
- 石炭ピッチコークス、石炭、石油コークス、石炭コークス、石油ピッチコークス、合成樹脂、合成樹脂とセルロース系繊維との複合物およびこれらの炭化物よりなる群から選択される少なくとも1種の炭素原料と融点が40℃以下の有機化合物を混合した後、該混合物をアルカリ賦活し、その後、洗浄処理することを特徴とする活性炭の製造方法。
- 前記炭素原料と前記有機化合物との混合を、前記有機化合物の融点以上の温度で行う請求項1に記載の活性炭の製造方法。
- 前記有機化合物が、複素環式化合物または芳香族炭化水素である請求項1または2に記載の活性炭の製造方法。
- 前記有機化合物と前記炭素原料の質量比(有機化合物/炭素原料)が、0.05以上10以下である請求項1〜3のいずれか一項に記載の活性炭の製造方法。
- 請求項1〜4のいずれか一項に記載の製造方法により得られた活性炭を電極構成材料に用いたことを特徴とする電気二重層キャパシタ。