JP5121272B2 - 導電性エンドレスベルト - Google Patents
導電性エンドレスベルト Download PDFInfo
- Publication number
- JP5121272B2 JP5121272B2 JP2007088606A JP2007088606A JP5121272B2 JP 5121272 B2 JP5121272 B2 JP 5121272B2 JP 2007088606 A JP2007088606 A JP 2007088606A JP 2007088606 A JP2007088606 A JP 2007088606A JP 5121272 B2 JP5121272 B2 JP 5121272B2
- Authority
- JP
- Japan
- Prior art keywords
- belt
- endless belt
- intermediate transfer
- image
- conductive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
結晶融点210℃以上のポリエステル系エラストマーからなるか、または、該ポリエステル系エラストマーを主成分とし、熱可塑性ポリエステル系樹脂を49重量%以下にて含有する基材に対し、高分子イオン導電剤およびカーボンブラックが添加されてなることを特徴とするものである。
導電性エンドレスベルトには、一般に、ジョイントありのものとジョイントなしのもの(いわゆるシームレスベルト)とがあるが、本発明においてはいずれのものであってもよい。好ましくはシームレスベルトである。本発明の導電性エンドレスベルトは、前述したように、タンデム方式、中間転写方式およびタンデム中間転写方式の転写部材等として用いることができるものである。
下記の表1〜4中にそれぞれ示す配合にて、各実施例および比較例の導電性エンドレスベルトを作製した。具体的には、各配合成分を二軸混練機により溶融混練して、得られた混練物を所定の環状ダイスを用いて押出し成形することにより、内径220mm、厚み100μm、幅250mmの寸法を有する導電性エンドレスベルトを得た。混練・押出成形温度は、実施例7〜12は250℃、それ以外は240℃であった。得られた各実施例および比較例のベルトにつき、下記の手順に従い、評価を行った。これらの結果を下記の表1〜4中に併せて示す。
以下に示す条件にて、引張弾性率の測定を行った。
装置:(株)島津製作所製、引張試験機 EZ test(解析ソフト:Trappezium)サンプル:短冊形状(長さ100mm×幅10mm×標準厚み100μm)引張速度:5mm/secデータサンプリング間隔:100msec測定方法:0.5〜0.6%伸度での傾き(記載ある場合はJISに記載の接線法)測定環境:室温(23±3℃、55±10%RH)
各ベルトから長さ100mm、幅15mmの試験片を切り出し、東洋精機(株)製のMIT耐揉疲労試験機を用いて、折り曲げ速度175回/min、回転角度135度、引張荷重14.7N(1.5kgf)の条件で耐折り曲げ回数を測定した。結果は、比較例5を3000とする指数にて表示した。数値が大なるほど結果は良好である。
各ベルトから長さ150mm、幅10mmの試験片を切り出し、長さ方向に100mm間隔の標線を記入して、長さ方向に荷重200gを付与した状態で、温度60℃、相対湿度85%の環境下に4時間放置した。放置前の標線間距離をL0、放置後の標線間距離をL1としたときのクリープひずみを、下記式に従い求めた。評価結果は、クリープひずみが0.5%以下のものを○、0.5%を超えるものを×とした。なお、標線間距離の測定は、試験片を温度23℃、相対湿度50%の環境下に一時間以上放置した後、長さ方向に荷重200gを付与して行った。
クリープひずみ(%)={(L1−L0)/L0}×100
温度23℃、相対湿度50%にて、測定装置として、アドバンテスト(ADVANTEST)社製の、抵抗計R8340AにサンプルチャンバーR12704Aを接続したものを用いて、電圧500Vにて測定を行い、周方向に20mmピッチで20箇所抵抗値を測定して、その最大値Rmaxおよび最小値Rminから、下記式より求めた。桁数が1以下であれば良好である。
(桁数)=log(Rmax/Rmin)
低温低湿(LL)環境(12℃10%RH)と高温高湿(HH)環境(32.5℃85%RH)に各ベルトを24h放置し、それぞれ測定電圧500Vでの体積抵抗値RLL,RHHを求めて、下記式に従い評価した。桁数が2.5以下であれば良好である。
(桁数)=log(RLL/RHH)
*2)PBT:(株)東レ製 トレコン1401CH2
*3)PBN:帝人化成(株)製 TQB−OT
*4)ポリエーテルエステルアミド+LiCF3SO3:三光化学(株)製 サンコノールTBX65
*5)ポリエーテルエステルアミド:三洋化成工業(株)製 ペレスタットNC6321
*6)カーボンブラック:電気化学(株)製 デンカブラック粒状
2、7 帯電ロール
3 現像ロール
4 現像ブレード
5 トナー供給ロール
6 クリーニングブレード
8 除電ロール
9、30、55 駆動ローラ(駆動部材)
10 転写搬送ベルト
12 一次帯電器
13 画像露光
14、35 クリーニング装置
19 給紙カセット
20 中間転写部材
25 転写ローラ
26、53 記録媒体
29、61 電源
41、42、43、44 現像器
50 タンデム中間転写部材
54a〜54d 第1現像部〜第4現像部
56 記録媒体送りローラ
57 記録媒体送り装置
58 定着装置
59 電源装置(電圧印加手段)
Claims (6)
- 画像形成装置に用いられる無端ベルト状の導電性エンドレスベルトにおいて、
結晶融点210℃以上のポリエステル系エラストマーからなるか、または、該ポリエステル系エラストマーを主成分とし、熱可塑性ポリエステル系樹脂を49重量%以下にて含有する基材に対し、高分子イオン導電剤およびカーボンブラックが添加されてなることを特徴とする導電性エンドレスベルト。 - 前記高分子イオン導電剤がポリエーテルエステルアミドである請求項1記載の導電性エンドレスベルト。
- 前記熱可塑性ポリエステル系樹脂がポリブチレンテレフタレートまたはポリブチレンナフタレートである請求項1または2記載の導電性エンドレスベルト。
- 前記高分子イオン導電剤の配合量が、前記基材100重量部に対し0.5〜40重量部の範囲内である請求項1〜3のうちいずれか一項記載の導電性エンドレスベルト。
- 前記カーボンブラックの配合量が、前記基材100重量部に対し5〜30重量部の範囲内である請求項1〜4のうちいずれか一項記載の導電性エンドレスベルト。
- 請求項1〜5のうちいずれか一項記載の導電性エンドレスベルトを用いたことを特徴とする画像形成装置。