JP5079411B2 - 難燃性樹脂組成物、それが含まれた電線被膜材及びそれによって被覆された電線 - Google Patents
難燃性樹脂組成物、それが含まれた電線被膜材及びそれによって被覆された電線 Download PDFInfo
- Publication number
- JP5079411B2 JP5079411B2 JP2007183362A JP2007183362A JP5079411B2 JP 5079411 B2 JP5079411 B2 JP 5079411B2 JP 2007183362 A JP2007183362 A JP 2007183362A JP 2007183362 A JP2007183362 A JP 2007183362A JP 5079411 B2 JP5079411 B2 JP 5079411B2
- Authority
- JP
- Japan
- Prior art keywords
- flame retardant
- electric wire
- retardant resin
- resin composition
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(1)エチレン−酢酸ビニル共重合体(EVA−1という)
MFR 2g/10min,VA含量 21重量%(宇部丸善ポリエチレン社製)
(2)エチレン−酢酸ビニル共重合体(EVA−2という)
MFR 2g/10min,VA含量 15重量%(宇部丸善ポリエチレン社製)
(3)エチレン−酢酸ビニル共重合体(EVA−3という)
MFR 0.1g/10min,VA含量 26重量%(宇部丸善ポリエチレン社製)
(4)エチレン−酢酸ビニル共重合体(EVA−4という)
MFR 1g/10min,VA含量 20重量%(宇部丸善ポリエチレン社製)
(5)エチレン−酢酸ビニル共重合体(EVA−5という)
MFR 3g/10min,VA含量 22重量%(宇部丸善ポリエチレン社製)
(6)エチレン−アクリル酸エチル共重合体(EEAという)
MFR 2g/10min,VA含量 21重量%(三井デュポンポリケミカル社製)
(7)直鎖状低密度ポリエチレン(L−LDPEという)
MFR 4g/10min,密度 0.904g/cm3(宇部丸善ポリエチレン社製)
(8)無水マレイン酸変性直鎖状低密度ポリエチレン(MAH-LLという)
MFR 1.5g/10min,密度 0.920g/cm3,
無水マレイン酸含量 0.1重量%(宇部丸善ポリエチレン社製)
(9)炭酸カルシウム(炭酸カルシウム−1という)
SCP−E#2010 平均粒径 1.11μm(三共精粉社製)
(10)炭酸カルシウム(炭酸カルシウム−2という)
SCP−E#80 平均粒径 2.77μm(三共精粉社製)
(11)炭酸カルシウム(炭酸カルシウム−3という)
SCP−E#2300 平均粒径 0.96μm(三共精粉社製)
(12)天然水酸化マグネシウム
マグシーズW−H4(神島化学工業製)
(13)合成水酸化マグネシウム
キスマ5B(協和化学工業製)
(14)赤リン
(燐化学工業社製 ノーバレッド120UF)
(15)カーボンブラック
VULCAN9A32(キャボット社製)
(16)酸化防止剤
IRGANOX 1010(チバ・スペシャルティ・ケミカルズ社製)
(1)MFR
JIS K7210に準拠して行い、測定条件は荷重2.16kg 、測定温度190℃。
(2)引張強さおよび伸び
シートは厚さ1mmのものを使用し、JIS K6301指定の3号ダンベルにて打ち抜
き、試験速度200mm/minにて測定する。
(3)酸素指数
シートは厚さ3mmのものを使用し、JIS K7201に準拠して行う。結果は酸素指数で表されるが、この値は、大きい程、難燃性がより優れていることを意味する。
(4)脆化温度
シートは厚さ2mmのものを使用し、JIS K7216に準拠して行う。結果は脆化温度で表されるが、この値は、小さい程、耐低温衝撃性がより優れていることを意味する。
(5)判定
酸素指数、低温脆化、引長強さ及び引張伸びが全て下記の範囲に入った場合に○とした。
酸素指数:25%≦ (一般的な難燃性レベル)
低温脆化:−60℃≧ (寒冷地での耐低温衝撃性)
引張強さ:10MPa≦ (JCS 4418等の耐燃性ケーブル規格)
引張伸び:350%≦ (JCS 4418等の耐燃性ケーブル規格)
Claims (3)
- ポリオレフィン系樹脂35〜60wt%と、不飽和カルボン酸またはその誘導体、エポキシ基含有化合物、ヒドロキシル基含有化合物、アミノ基含有化合物、有機シラン化合物、及び有機チタネート化合物から選ばれる官能基含有化合物の少なくとも1種以上で変性された官能基含有化合物変性エチレン系樹脂1〜15wt%と、炭酸カルシウム30〜55wt%と、赤リン0.5〜5wt%と、を含むことを特徴とする難燃性樹脂組成物。
- 請求項1に係る難燃性樹脂組成分が含まれたことを特徴とする電線被膜材。
- 請求項2記載の電線被膜材によって被覆されたことを特徴とする電線。