JP5040236B2 - 樹脂組成物およびそれを用いた成型体並びに床材 - Google Patents
樹脂組成物およびそれを用いた成型体並びに床材 Download PDFInfo
- Publication number
- JP5040236B2 JP5040236B2 JP2006262466A JP2006262466A JP5040236B2 JP 5040236 B2 JP5040236 B2 JP 5040236B2 JP 2006262466 A JP2006262466 A JP 2006262466A JP 2006262466 A JP2006262466 A JP 2006262466A JP 5040236 B2 JP5040236 B2 JP 5040236B2
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- nucleating agent
- weight
- polylactic acid
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
これまでも、それらの課題を解決する為に、各種添加剤の開発や、生分解性プラスチック自体の改質が行われてきた。
性をもつ構造となる。
実施例1から4の樹脂組成物と比較例1の樹脂組成物をそれぞれ約10mgずつ精秤し、DSC(示差走査熱量分析装置:セイコーインスツルメンツ製DSC6100)にて10℃/分で185℃まで昇温して10分間保持した後、130℃まで急冷、保持した時の結晶化時間を比較した。この結果を図1に示した。図で、横軸は時間(min.)、縦軸はDCS(ミクロンW)を示す。また、曲線1は、実施例2を、曲線2は、実施例1を、曲線3は、実施例4を、曲線4は、実施例3を、曲線5は、実施例5(比較例1)を、それぞれ示す。
実施例6において良好な木質樹脂発泡成形体を得ることができた。また、作成した木質樹脂発泡成形体の耐衝撃強度を測定,比較したところ,ほぼ同程度であり,本発明により環境負荷の小さく,かつ,必要物性を満たす床材を容易に成形できることが確認できた。
Claims (3)
- ポリ乳酸系または脂肪族ポリエステル系樹脂(a)と核剤(b)を含んでなる樹脂組成物であって、前記核剤は凍結粉砕した粒子径5μm以下のα‐キチンからなり、かつ、前記ポリ乳酸系または脂肪族ポリエステル系樹脂(a)100重量部に対し、前記核剤(b)が0.1から5重量部の範囲にあることを特徴とする樹脂組成物。
- 請求項1に記載の樹脂組成物を熱溶融して成形したことを特徴とする成型体。
- 請求項1に記載の樹脂組成物を熱溶融して成形したことを特徴とする床材。