JP4589032B2 - Exhaust gas purification catalyst and oxygen storage material for the catalyst - Google Patents
Exhaust gas purification catalyst and oxygen storage material for the catalyst Download PDFInfo
- Publication number
- JP4589032B2 JP4589032B2 JP2004158702A JP2004158702A JP4589032B2 JP 4589032 B2 JP4589032 B2 JP 4589032B2 JP 2004158702 A JP2004158702 A JP 2004158702A JP 2004158702 A JP2004158702 A JP 2004158702A JP 4589032 B2 JP4589032 B2 JP 4589032B2
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- exhaust gas
- composite oxide
- primary particles
- oxygen storage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は排気ガス浄化用触媒及び同触媒用酸素吸蔵材に関する。 The present invention relates to an exhaust gas purifying catalyst and an oxygen storage material for the catalyst.
自動車の排気ガスを浄化するための三元触媒は、一般にはサポート材としてのアルミナ及びセリアを担体にコーティングした後、Pt、Pd、Rh等の触媒金属を当該コート層に含浸させて焼成することによって形成されている。また、排気ガス浄化用触媒に関し、排気ガスをその低温時から高温時まで安定して浄化できるようにするとともに、触媒の耐熱を向上させるべく、中空状酸化物粉末と中実状酸化物粉末とを含むサポート材に触媒金属を担持させるという提案が知られている(特許文献1参照)。 A three-way catalyst for purifying automobile exhaust gas is generally obtained by coating a support with alumina and ceria as support materials, and then impregnating the coating layer with a catalyst metal such as Pt, Pd, Rh, and firing. Is formed by. Further, regarding exhaust gas purification catalyst, in order to be able to stably purify exhaust gas from the low temperature to the high temperature, in order to improve the heat resistance of the catalyst, hollow oxide powder and solid oxide powder, There has been known a proposal of supporting a catalyst metal on a support material (see Patent Document 1).
すなわち、この提案の中空状酸化物粉末は、Laを含有するAl2O3からなり、これにRhが含浸法によって担持されている。また、特許文献1には、中空状酸化物粉末の殻壁の厚さは100nm以下であることが望ましく、50nm以下、さらには20nm以下であることがより望ましいこと、中空状酸化物粉末は外径が20〜2000nmであり、10〜2000nmの細孔をもつこと、中空状酸化物粉末の粒子はAl,Ti及びZrから選ばれる少なくとも一種の元素の酸化物又は複合酸化物から形成すること、比表面積は20m2/g以上であることが望ましい、と記載されている。 That is, the proposed hollow oxide powder is made of Al 2 O 3 containing La, and Rh is supported by the impregnation method. Patent Document 1 discloses that the thickness of the shell wall of the hollow oxide powder is desirably 100 nm or less, more desirably 50 nm or less, and further desirably 20 nm or less. Having a diameter of 20 to 2000 nm and having pores of 10 to 2000 nm, the hollow oxide powder particles being formed from an oxide or composite oxide of at least one element selected from Al, Ti and Zr; It is described that the specific surface area is desirably 20 m 2 / g or more.
ところで、上記セリアは、三元触媒においては酸素吸蔵材として働き、当該触媒が有効に働く空燃比領域を拡大するが、耐熱性が低いという問題がある。これに対して、触媒の耐熱性向上のために、セリアとジルコニアとを複合させた複合酸化物を触媒貴金属のサポート材として用いることは知られている。
本出願人は、先にCeとZrとを含有し結晶格子又は原子間に触媒金属を配置してなる複合酸化物を共沈法によって製造する方法を開発し、提案している(特願2003−379839号,出願人:マツダ株式会社)。この複合酸化物によれば、排気ガスの熱による触媒金属のシンタリングや表面に存在する触媒金属の埋没が抑えられ、すなわち、触媒の耐熱性が向上するとともに、酸素吸蔵能(吸蔵速度及び吸蔵量)が高まる。従って、触媒金属量を少なくしても、排気ガス浄化におけるライトオフ性能及び高温浄化性能を向上させることができた。 The present applicant has previously developed and proposed a method for producing a composite oxide containing Ce and Zr and having a catalyst metal arranged between crystal lattices or atoms by a coprecipitation method (Japanese Patent Application 2003). -379839, applicant: Mazda Motor Corporation). According to this composite oxide, sintering of the catalyst metal due to the heat of the exhaust gas and burying of the catalyst metal existing on the surface are suppressed, that is, the heat resistance of the catalyst is improved and the oxygen storage capacity (storage speed and storage speed) is increased. Amount). Therefore, even if the amount of catalyst metal is reduced, the light-off performance and the high-temperature purification performance in exhaust gas purification can be improved.
しかし、共沈法で得られる複合酸化物では、その結晶子(一次粒子)の微細化にも限界があり、触媒金属の添加量を少なくすると、結晶子表面に露出して排気ガスの酸化・還元に直接働く(触媒作用をする)触媒金属量が少なくなる。また、二次粒子も多数の一次粒子が凝集してなるものであるため、内部に埋もれている一次粒子は排気ガスと充分に接触しないという問題があった。これは、後出比較例に示すとおり、高温に晒した場合、比較的小さなBET比表面積がさらに低下することから、凝集した中実状複合酸化物同士がシンタリングを起こしやすいことに原因があると考えられる。 However, the complex oxide obtained by the coprecipitation method has a limit in the refinement of the crystallite (primary particles), and if the amount of the catalyst metal added is reduced, it is exposed on the crystallite surface and the exhaust gas is oxidized and oxidized. The amount of catalytic metal directly acting on the reduction (catalyzing) is reduced. Further, since the secondary particles are also formed by aggregating many primary particles, there is a problem that the primary particles buried inside do not sufficiently contact the exhaust gas. This is because the relatively small BET specific surface area is further reduced when exposed to a high temperature, as shown in the comparative example described later, and the cause is that the aggregated solid complex oxides are likely to cause sintering. Conceivable.
つまり、Rhは、その一部が後述のように一次粒子(結晶子)の結晶格子又は原子間に配置されることによって酸素吸蔵量の増大等、酸素吸蔵能の向上に寄与するとともに、残りの一部が一次粒子表面に露出していることによって排気ガスと接触して浄化性能の向上に寄与するが、シンタリングによって粗大化した粒子内部にRhが埋没する結果、粒子表面に露出して排気ガス浄化性能に寄与するRh量が少なくなるという問題があった。そのため、排気ガス浄化性能をさらに高めることが難しかった。 That is, Rh contributes to the improvement of the oxygen storage capacity, such as an increase in the amount of oxygen storage by being partially disposed between the crystal lattices or atoms of the primary particles (crystallites) as described later, and the rest Although part of the surface is exposed to the primary particle surface, it contributes to the improvement of the purification performance by contacting with the exhaust gas. However, as a result of Rh being buried inside the particle coarsened by sintering, it is exposed to the particle surface and exhausted. There has been a problem that the amount of Rh contributing to gas purification performance is reduced. Therefore, it was difficult to further improve the exhaust gas purification performance.
そこで、本発明の課題は、触媒金属量を少なくしても、触媒の耐熱性を損なうことなく、その排気ガス浄化性能をさらに高めることができるようにすることにある。 Accordingly, an object of the present invention is to make it possible to further improve the exhaust gas purification performance without impairing the heat resistance of the catalyst even if the amount of catalyst metal is reduced.
本発明は、このような課題に対して、上記CeとZrとを含有し且つ触媒金属が結晶格子又は原子間に存する複合酸化物を中空の殻及びその破片のいずれかの形態で触媒に用いるようにした。 In order to solve such a problem, the present invention uses a composite oxide containing Ce and Zr and having a catalytic metal between crystal lattices or atoms in the form of a hollow shell and its fragments. I did it.
すなわち、請求項1に係る発明は、触媒担体上に形成された触媒層に、Ce及びZrを含有する複合酸化物と、Al2O3と、少なくとも一種類の触媒金属とが含まれている排気ガス浄化用触媒であって、
上記一種類の触媒金属はRhであり、
上記複合酸化物の少なくとも一部は、中空の殻及びその破片の少なくとも一方の形態となって上記触媒層に存在し、
上記中空の殻又はその破片を構成する上記Ce及びZrを含有する一次粒子の結晶格子又は原子間に上記Rhの少なくとも一部が配置されており、
上記Al 2 O 3 は、上記複合酸化物と混合して上記触媒層に含まれていることを特徴とする。
That is, in the invention according to claim 1, the catalyst layer formed on the catalyst carrier includes a composite oxide containing Ce and Zr, Al 2 O 3 , and at least one kind of catalyst metal. An exhaust gas purifying catalyst,
The one type of catalytic metal is Rh,
At least a part of the composite oxide is present in the catalyst layer in the form of at least one of a hollow shell and fragments thereof,
At least a part of the Rh is arranged between crystal lattices or atoms of primary particles containing the Ce and Zr constituting the hollow shell or fragments thereof ;
The Al 2 O 3 is mixed with the complex oxide and contained in the catalyst layer .
従って、上記複合酸化物の結晶格子又は原子間に配置されたRhは、Rh同士の接触が抑制された状態にあるから、高熱に晒されてもシンタリングを生じ難くなる。また、Rhが結晶格子又は原子間に配置された当該複合酸化物は、その雰囲気が酸素過剰になると、速やかに酸素を吸蔵するとともに、酸素吸蔵量も多くなる。 Therefore, Rh arranged between the crystal lattices or atoms of the composite oxide is in a state in which the contact between the Rhs is suppressed, so that it is difficult for sintering to occur even when exposed to high heat. In addition, the complex oxide in which Rh is disposed between crystal lattices or between atoms quickly absorbs oxygen and increases the amount of oxygen stored when the atmosphere is excessive in oxygen.
なお、Rh以外の触媒金属としては、PtやPd等が含浸法等で触媒層に含有されることが好ましい。或いは更にRhが含浸法等で触媒層に含有されてもよい。 In addition, as a catalyst metal other than Rh, it is preferable that Pt, Pd, or the like is contained in the catalyst layer by an impregnation method or the like. Alternatively, Rh may be further contained in the catalyst layer by an impregnation method or the like.
そうして、上記中空の殻及びその破片のいずれかの形態になっている複合酸化物は、中実の塊状となっている場合に比べて、表面(殻の外面及び内面を含む)に露出する一次粒子が多くなるとともに、排気ガスが当該複合酸化物の殻壁を通り抜けやすくなる。よって、一次粒子の表面に露出しているRhが排気ガスと接触し易くなるから、排気ガスの浄化性能が高まる。 Thus, the composite oxide in the form of any one of the hollow shell and its fragments is exposed on the surface (including the outer surface and the inner surface of the shell) as compared to a solid lump. As the number of primary particles increases, the exhaust gas easily passes through the shell wall of the composite oxide. Therefore, Rh exposed on the surface of the primary particles can easily come into contact with the exhaust gas, so that the exhaust gas purification performance is enhanced.
請求項2に係る発明は、請求項1において、
Rhが結晶格子又は原子間に配置された上記一次粒子の平均結晶子径が10nm未満であることを特徴とする。
The invention according to claim 2 is the invention according to claim 1,
The average crystallite diameter of the primary particles in which Rh is arranged between crystal lattices or atoms is less than 10 nm.
このような小さい結晶子径であれば、その表面に露出するRhの量が多くなり、排気ガス浄化性能の向上に有利になる。 With such a small crystallite diameter, the amount of Rh exposed on the surface increases, which is advantageous for improving the exhaust gas purification performance.
請求項3に係る発明は、請求項1又は請求項2において、
上記中空の殻は、その直径が0.05μm以上3.0μm以下の略球状であり、その殻壁の厚みが50nm以下であることを特徴とする。
The invention according to claim 3 is the invention according to claim 1 or claim 2,
The hollow shell has a substantially spherical shape with a diameter of 0.05 μm or more and 3.0 μm or less, and a thickness of the shell wall is 50 nm or less.
従って、一次粒子同士の接触による粒成長が抑制されるとともに、当該中空殻状複合酸化物のシンタリングも少なくなる。また、上記一次粒子の平均結晶子径が10nm未満である場合、殻壁の厚みと該殻壁を構成する一次粒子の平均結晶子径との関係から、殻壁の厚み方向に存在する一次粒子の数が約10個程度に或いは10個以下に抑えられるので、排気ガスが殻壁を通り易くなり、排気ガスの浄化性能が高まる。 Therefore, grain growth due to contact between primary particles is suppressed, and sintering of the hollow shell complex oxide is also reduced. Further, when the average crystallite size of the primary particles is less than 10 nm, the primary particles existing in the thickness direction of the shell wall from the relationship between the thickness of the shell wall and the average crystallite size of the primary particles constituting the shell wall. Therefore, the exhaust gas can easily pass through the shell wall, and the exhaust gas purification performance is enhanced.
請求項4に係る発明は、請求項1乃至請求項3のいずれか一に記載されている排気ガス浄化用触媒に含有される酸素吸蔵材であって、
Ce及びZrを含有し且つ結晶格子又は原子間にRhが配置されている複合酸化物の一次粒子から構成されていて、
上記Ce及びZrを含有する一次粒子が凝集して中空の殻及びその破片の少なくとも一方の形態となっていることを特徴とする。
The invention according to claim 4 is an oxygen storage material contained in the exhaust gas purifying catalyst according to any one of claims 1 to 3 ,
It is composed of primary particles of a composite oxide containing Ce and Zr and having Rh arranged between crystal lattices or atoms,
The primary particles containing Ce and Zr are aggregated to form at least one of a hollow shell and fragments thereof.
従って、この酸素吸蔵材によれば、Rhのシンタリングを生じ難くなり且つ優れた酸素吸蔵特性を示すことに加えて、表面に露出する一次粒子が多くなるとともに、排気ガスが当該複合酸化物の殻壁を通り抜け易くなるから、一次粒子の表面に露出しているRhが排気ガスと接触し易くなり、排気ガスの浄化性能が高まる。 Therefore, according to this oxygen storage material, Rh sintering is less likely to occur and excellent oxygen storage characteristics are exhibited. In addition, the number of primary particles exposed on the surface increases, and the exhaust gas contains the composite oxide. Since it becomes easy to pass through the shell wall, the Rh exposed on the surface of the primary particles can easily come into contact with the exhaust gas, and the purification performance of the exhaust gas is enhanced.
請求項5に係る発明は、請求項4において、
上記複合酸化物の平均結晶子径が10nm未満であることを特徴とする。
The invention according to claim 5 is the invention according to claim 4,
An average crystallite size of the composite oxide is less than 10 nm.
従って、酸素吸蔵材表面に露出するRhの量が多くなり、排気ガス浄化性能の向上に有利になる。 Therefore, the amount of Rh exposed on the surface of the oxygen storage material increases, which is advantageous for improving the exhaust gas purification performance.
以上のように本発明に係る排気ガス浄化用触媒によれば、Ce及びZrを含有しRhが結晶格子又は原子間に配置された複合酸化物が中空の殻及びその破片の少なくとも一方の形態になっているから、触媒の耐熱性が向上し、また、表面に露出する一次粒子が多くなるとともに、排気ガスが当該複合酸化物の殻壁を通り抜けやすくなるから、一次粒子の表面に露出しているRhが排気ガスと接触し易くなり、排気ガスの浄化性能が高まる。 As described above, according to the exhaust gas purifying catalyst of the present invention, the composite oxide containing Ce and Zr and having Rh arranged between crystal lattices or atoms is in the form of at least one of a hollow shell and its fragments. Therefore, the heat resistance of the catalyst is improved, the primary particles exposed on the surface increase, and the exhaust gas easily passes through the shell wall of the composite oxide, so that it is exposed on the surface of the primary particles. Rh that is in contact with the exhaust gas is easily contacted, and the exhaust gas purification performance is enhanced.
また、上記一次粒子の平均結晶子径を10nm未満にすると、排気ガス浄化性能の向上に有利になり、また、上記中空の殻を直径が0.05μm以上3.0μm以下の略球状とし、その殻壁の厚みを50nm以下にすると、一次粒子同士の接触による粒成長の抑制、当該中空殻状複合酸化物のシンタリング防止に有利になるとともに、排気ガスが殻壁を通り易くなり、排気ガスの浄化性能が高まる。 Further, when the average crystallite diameter of the primary particles is less than 10 nm, it is advantageous for improving the exhaust gas purification performance, and the hollow shell is made into a substantially spherical shape having a diameter of 0.05 μm or more and 3.0 μm or less. When the thickness of the shell wall is 50 nm or less, it is advantageous for suppressing grain growth due to contact between primary particles and preventing sintering of the hollow shell complex oxide, and the exhaust gas easily passes through the shell wall. The purification performance of increases.
また、本発明に係る酸素吸蔵材によれば、Ce及びZrを含有しRhが結晶格子又は原子間に配置された複合酸化物の一次粒子が凝集して中空の殻及びその破片の少なくとも一方の形態となったものであるから、耐熱性が高くなり且つ優れた酸素吸蔵特性を示すことに加えて、一次粒子の表面に露出しているRhが排気ガスと接触し易くなり、排気ガスの浄化性能を高める上で有利になる。また、上記一次粒子の平均結晶子径を10nm未満にすると、排気ガス浄化性能の向上にさらに有利になる。 In addition, according to the oxygen storage material of the present invention, primary particles of a composite oxide containing Ce and Zr and Rh arranged between crystal lattices or atoms aggregate to form at least one of a hollow shell and its fragments. Since it is in a form, in addition to high heat resistance and excellent oxygen storage characteristics, Rh exposed on the surface of the primary particles can easily come into contact with the exhaust gas, thereby purifying the exhaust gas. This is advantageous for improving performance. Further, when the average crystallite size of the primary particles is less than 10 nm, it is further advantageous for improving the exhaust gas purification performance.
以下、本発明の実施形態を図面に基づいて詳細に説明する。 Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
本発明の実施形態に係る排気ガス浄化用触媒は、自動車エンジンの排気ガス中のHC、CO及びNOxを浄化することに適したものであって、そのための触媒層がコージェライト等の無機多孔質によって形成されたハニカム形状等の担体上に形成されている。触媒層は次に説明する酸素吸蔵材として働く複合酸化物及びγ−アルミナをバインダと共に担体にウォッシュコートすることによって形成される。 The exhaust gas purifying catalyst according to the embodiment of the present invention is suitable for purifying HC, CO and NOx in the exhaust gas of an automobile engine, and the catalyst layer therefor is an inorganic porous material such as cordierite. Formed on a carrier having a honeycomb shape or the like. The catalyst layer is formed by wash-coating a composite oxide and γ-alumina serving as an oxygen storage material, which will be described next, together with a binder.
上記複合酸化物は、Ce及びZrを含有し且つ触媒金属としてのRhの少なくとも一部が結晶格子又は原子間に配置されたものであって、この複合酸化物の少なくとも一部は中空の略球状の殻及びその破片のいずれかの形態になっている。なお、上記複合酸化物は、以下の実施例に記載のNd等、Ce以外の希土類元素を含有してもよい。 The composite oxide contains Ce and Zr, and at least a part of Rh as a catalyst metal is arranged between crystal lattices or atoms, and at least a part of the composite oxide is a hollow, substantially spherical shape. In the form of a shell and its debris. The composite oxide may contain rare earth elements other than Ce, such as Nd described in the following examples.
<実施例>
上記複合酸化物を噴霧熱分解法によって製造した。すなわち、オキシ硝酸ジルコニウム、硝酸セリウム、硝酸ネオジム、硝酸ロジウム及び硫酸マグネシウムの各所定量を水に溶解させることにより、上記複合酸化物の原料溶液を調製した。ここで、硫酸マグネシウムは、中空状複合酸化物を製造する際の結晶子のシンタリングを抑制する、結晶子同士の接触点を減らしつつ中空構造に導く、という作用を有するものとして、各種添加化合物の中から選定されたものであり、その添加量、濃度等は適宜決定することができる。次いで、上記原料溶液を、空気をキャリアガスとして噴霧することにより、液滴化させて加熱炉に供給した。加熱炉の温度は1000℃に設定した。加熱炉を出た粒子はバグフィルターによって捕集し、これを水洗後、乾燥させることにより、当該複合酸化物を得た。この実施例においては、ZrO2:CeO2:Nd2O3=68:22:10、当該複合酸化物におけるRh量が0.125質量%となるようにした。
<Example>
The composite oxide was produced by a spray pyrolysis method. That is, a raw material solution of the composite oxide was prepared by dissolving predetermined amounts of zirconium oxynitrate, cerium nitrate, neodymium nitrate, rhodium nitrate, and magnesium sulfate in water. Here, magnesium sulfate is an additive compound that has the effect of suppressing sintering of crystallites when producing a hollow composite oxide and leading to a hollow structure while reducing the number of contact points between crystallites. The amount added, concentration, etc. can be determined as appropriate. Subsequently, the raw material solution was sprayed using air as a carrier gas to form droplets and supplied to the heating furnace. The temperature of the heating furnace was set to 1000 ° C. The particles exiting the heating furnace were collected by a bag filter, washed with water, and dried to obtain the composite oxide. In this example, ZrO 2 : CeO 2 : Nd 2 O 3 = 68: 22: 10, and the Rh amount in the composite oxide was 0.125% by mass.
そうして、上記複合酸化物とγ−アルミナ粉末とを2:1の比率で混合してこれにバインダ及び水を加えてスラリーを得、このスラリーをコージェライト製ハニカム担体に担体1L当たりの担持量が167gとなるようにウォッシュコートして、乾燥、焼成工程を経て実施例に係る排気ガス浄化用触媒を得た。この触媒の担体に対するRh含有量は0.126g/Lである。 Then, the composite oxide and γ-alumina powder are mixed at a ratio of 2: 1, and a binder and water are added thereto to obtain a slurry. This slurry is supported on a cordierite honeycomb carrier per 1 L of carrier. Washing was performed so that the amount was 167 g, and the exhaust gas purifying catalyst according to the example was obtained through the drying and firing steps. The Rh content of this catalyst relative to the support is 0.126 g / L.
図1〜図4は上記複合酸化物のTEM(透過型電子顕微鏡)写真である。図1及び図2の写真に写っている中空球状の殻及び該殻が割れた破片(図2の写真に円弧状ないし直線状に黒く写っているもの)が上記複合酸化物である。球状殻の直径は0.05μm〜3μmである。図3は図1の写真の一部を拡大したものであり、複合酸化物の殻壁の厚みは50nm以下になっている。すなわち、TEMでは100nm程度の厚みのものを観察するとその背部が透過して見えるが、図3によれば大きな中空球状の複合酸化物の裏にやや小さめの中空球状の複合酸化物が見えているところから、殻壁の厚みは50nm以下であると特定した。 1 to 4 are TEM (transmission electron microscope) photographs of the composite oxide. The hollow spherical shells shown in the photographs of FIGS. 1 and 2 and the broken pieces of the shells (those that are black in the shape of an arc or a straight line in the photographs of FIG. 2) are the composite oxide. The diameter of the spherical shell is 0.05 μm to 3 μm. FIG. 3 is an enlarged view of a part of the photograph of FIG. 1, and the thickness of the shell wall of the composite oxide is 50 nm or less. That is, in TEM, when the thickness of about 100 nm is observed, the back portion appears to be transmitted, but according to FIG. 3, a slightly smaller hollow spherical composite oxide is seen behind the large hollow spherical composite oxide. Therefore, the thickness of the shell wall was specified to be 50 nm or less.
図4はさらに倍率を高めた写真であり、黒い粒状のものが見受けられるが、これらが一次粒子である。この写真によれば、該一次粒子の50%以上は直径が数nm以下になっていることが確認できる。 FIG. 4 is a photograph in which the magnification is further increased, and black particles can be seen, but these are primary particles. According to this photograph, it can be confirmed that 50% or more of the primary particles have a diameter of several nm or less.
したがって、実施例に係る複合酸化物は、中空球状の殻と該殻が割れた破片とが混合された形態となっている。また、図4の写真からわかるように、一次粒子である結晶子の一部は互いに接触した状態にあるが、一部の結晶子間には空隙が存在する。つまり、図2や図3に示される中空球状の殻やその破片は、一次粒子が部分的に結晶子間に空隙のある状態で凝集した二次粒子であると云える。そして、このように結晶子間に空隙が存在する、つまり多孔体であるが故に、複合酸化物は後述する比較的大きなBET比表面積が確保できているとともに、排気ガスが複合酸化物の殻壁を通り抜けやすく、その通り抜けの過程で一次粒子表面に露出しているRhと排気ガスとが接触するため、排気ガス性能が高まる。 Therefore, the composite oxide according to the example is in a form in which a hollow spherical shell and a broken piece of the shell are mixed. Further, as can be seen from the photograph in FIG. 4, some of the crystallites that are primary particles are in contact with each other, but there are voids between some of the crystallites. That is, it can be said that the hollow spherical shell and its fragments shown in FIG. 2 and FIG. 3 are secondary particles in which the primary particles are partially agglomerated with voids between the crystallites. Since the voids exist between the crystallites, that is, the porous body, the composite oxide can secure a relatively large BET specific surface area, which will be described later, and the exhaust gas is a shell wall of the composite oxide. Exhaust gas performance is enhanced because Rh exposed on the primary particle surface and the exhaust gas come into contact with each other in the process of passing through.
なお、図1及び図2の写真において、複合酸化物の背部に写っている線状のものは写真撮影のために複合酸化物を支持させたCu製ワイヤーメッシュである。 In the photographs of FIGS. 1 and 2, the linear shape that is reflected on the back of the complex oxide is a Cu wire mesh that supports the complex oxide for photography.
図5は上記複合酸化物の平均結晶子径を次に示すシェラーの式から導くために調べたXRD(X線回折)パターンである。 FIG. 5 is an XRD (X-ray diffraction) pattern examined in order to derive the average crystallite diameter of the composite oxide from the following Scherrer equation.
結晶子径D(hkl)=0.9λ/(β1/2・cosθ)
但し、hklはミラー指数、λは特性X線の波長(Å)、β1/2は(hkl)面の半価幅(ラジアン)、θはX線反射角度である。
Crystallite diameter D (hkl) = 0.9λ / (β1 / 2 · cosθ)
Where hkl is the Miller index, λ is the characteristic X-ray wavelength (Å), β 1/2 is the half width (radian) of the (hkl) plane, and θ is the X-ray reflection angle.
このシェラーの式によると、平均結晶子径は5.8nmとなる。 According to the Scherrer equation, the average crystallite diameter is 5.8 nm.
<排気ガス浄化性能について>
上記実施例の排気ガス浄化性能を比較例との比較において評価した。
<Exhaust gas purification performance>
The exhaust gas purification performance of the above example was evaluated in comparison with a comparative example.
−比較例−
共沈法によって比較例に係る複合酸化物を調製した。すなわち、オキシ硝酸ジルコニウム、硝酸セリウム、硝酸ネオジム及び硝酸ロジウム溶液各々の所定量と水とを混合し、この混合溶液を室温で約1時間撹拌した後、80℃まで加熱昇温させ、これと28%アンモニア水50mLとを素早く混合した。このアンモニア水との混合により白濁した溶液を一昼夜放置し、生成したケーキを遠心分離器にかけ、十分に水洗した。この水洗したケーキを約150℃の温度で乾燥させた後、400℃の温度に5時間保持し、次いで1000℃の温度に1時間保持するという条件で焼成した。
-Comparative example-
A composite oxide according to a comparative example was prepared by a coprecipitation method. That is, a predetermined amount of each of zirconium oxynitrate, cerium nitrate, neodymium nitrate, and rhodium nitrate solution was mixed with water, and this mixed solution was stirred at room temperature for about 1 hour, and then heated to 80 ° C. to increase the temperature. % Aqueous ammonia (50 mL) was quickly mixed. The solution which became cloudy by mixing with the ammonia water was left for a whole day and night, and the resulting cake was centrifuged and washed thoroughly with water. The cake washed with water was dried at a temperature of about 150 ° C. and then calcined under the condition that it was kept at a temperature of 400 ° C. for 5 hours and then kept at a temperature of 1000 ° C. for 1 hour.
得られた複合酸化物は、Ce及びZrを含有しRhの少なくとも一部が結晶格子又は原子間に配置された中実の粉末であり、組成は実施例と同じく、ZrO2:CeO2:Nd2O3=68:22:10、当該複合酸化物におけるRh量は0.125質量%である。また、結晶子径は10〜20nmであった。 The obtained composite oxide is a solid powder containing Ce and Zr and having at least a part of Rh arranged between crystal lattices or atoms, and the composition is the same as in the example, ZrO 2 : CeO 2 : Nd. 2 O 3 = 68: 22: 10, and the Rh content in the composite oxide is 0.125% by mass. The crystallite diameter was 10 to 20 nm.
そうして、上記複合酸化物とγ−アルミナ粉末とを2:1の比率で混合してこれにバインダ及び水を加えてスラリーを得、このスラリーをコージェライト製ハニカム担体に担体1L当たりの担持量が167gとなるようにウォッシュコートして、乾燥、焼成工程を経て比較例に係る排気ガス浄化用触媒を得た。従って、比較例触媒の担体に対するRh含有量は実施例と同じく0.126g/Lである。 Then, the composite oxide and γ-alumina powder are mixed at a ratio of 2: 1, and a binder and water are added thereto to obtain a slurry. This slurry is supported on a cordierite honeycomb carrier per 1 L of carrier. Wash coating was performed so that the amount was 167 g, and an exhaust gas purifying catalyst according to a comparative example was obtained through drying and firing processes. Therefore, the Rh content with respect to the carrier of the comparative example catalyst is 0.126 g / L as in the examples.
−排気ガス浄化性能の評価試験−
上記実施例及び比較例の各触媒について、O2を2質量%、H2Oを10質量%含有するN2ガス雰囲気で1000℃の温度に24時間加熱するエージング処理を行なった後、モデルガス流通反応装置及び排気ガス分析装置を用いて、空燃比リッチのモデルガス(温度600℃)を20分間流した後のHC、CO及びNOxの浄化に関するライトオフ温度T50及び高温浄化率C400を測定した。T50は、触媒に流入するモデルガス温度を常温から漸次上昇させていき、浄化率が50%に達したときの触媒入口のガス温度である。C400は触媒入口ガス温度が400℃のときの浄化率である。モデルガスは、A/F=14.7±0.9とした。すなわち、A/F=14.7のメインストリームガスを定常的に流しつつ、所定量の変動用ガスを1Hzでパルス状に添加することにより、A/Fを±0.9の振幅で強制的に振動させた。空間速度SVは60000h−1、昇温速度は30℃/分である。
−Evaluation test of exhaust gas purification performance−
The catalysts of the above Examples and Comparative Examples, the O 2 2 wt%, after performing the aging treatment of heating for 24 hours of H 2 O to a temperature of 1000 ° C. in N 2 gas atmosphere containing 10% by weight, model gas Using a flow reactor and an exhaust gas analyzer, the light-off temperature T50 and the high temperature purification rate C400 related to the purification of HC, CO, and NOx after flowing an air-fuel ratio rich model gas (temperature 600 ° C.) for 20 minutes were measured. . T50 is the gas temperature at the catalyst inlet when the temperature of the model gas flowing into the catalyst is gradually increased from room temperature and the purification rate reaches 50%. C400 is the purification rate when the catalyst inlet gas temperature is 400 ° C. The model gas was A / F = 14.7 ± 0.9. That is, the A / F is forced at an amplitude of ± 0.9 by adding a predetermined amount of fluctuation gas in a pulse form at 1 Hz while constantly flowing the main stream gas of A / F = 14.7. Vibrated. The space velocity SV is 60000 h −1 , and the heating rate is 30 ° C./min.
T50の結果を図6に示す。HC、CO及びNOxいずれの浄化に関しても実施例触媒の方が比較例触媒よりも50℃前後低いT50になっている。C400の結果を図7に示す。HC、CO及びNOxいずれの浄化率に関しても、実施例触媒は比較例触媒よりも5%前後高くなっている。 The result of T50 is shown in FIG. Regarding purification of HC, CO, and NOx, the catalyst of the example has a T50 lower by about 50 ° C. than the catalyst of the comparative example. The result of C400 is shown in FIG. With respect to the purification rates of HC, CO, and NOx, the example catalyst is about 5% higher than the comparative example catalyst.
即ち、実施例触媒は比較例触媒に比べて、より低温でも高い触媒活性を発揮するとともに、高温域においても高い触媒活性が維持されるものであって、耐熱性に優れ、排気ガス浄化性能が高い。従って、本発明の如く、Ce及びZrを含有しRhの少なくとも一部が結晶格子又は原子間に配置された複合酸化物が中空略球状の殻及びその破片のいずれかの形態になると、耐熱性の向上、排気ガス浄化性能の向上に有利であることがわかる。 That is, the example catalyst exhibits higher catalytic activity even at a lower temperature than the comparative example catalyst, and maintains a high catalytic activity even in a high temperature range, and has excellent heat resistance and exhaust gas purification performance. high. Therefore, as in the present invention, when a complex oxide containing Ce and Zr and at least a part of Rh is arranged between crystal lattices or atoms is in the form of a hollow substantially spherical shell and its fragments, It can be seen that this is advantageous for improving the exhaust gas purification performance.
これは、本発明の場合、複合酸化物が中空略球状の殻又はその破片の形態であるから、排気ガスが当該複合酸化物の殻壁を通り抜けやすくなるとともに、凝集によって内部に埋もれる一次粒子が可及的に少なくなるため、排気ガスとRhなどの触媒金属及び酸素吸蔵材との接触効率が向上したこと、しかも、高温に暴露した場合でも、複合酸化物の粒成長が抑制され粒子内部に埋没するRhが少ないため、Rhのほぼ全量、つまり一次粒子内部における結晶格子又は原子間に配置されたRhと、当該一次粒子内部から表面に露出したRhとが、それぞれの機能を発揮して排気ガスの浄化に寄与したことによるものであり、少量でも高い浄化性能を維持できるものである。 This is because, in the case of the present invention, since the composite oxide is in the form of a hollow substantially spherical shell or a fragment thereof, the exhaust gas can easily pass through the shell wall of the composite oxide, and the primary particles buried inside by aggregation are formed. Because it reduces as much as possible, the contact efficiency between exhaust gas and catalytic metals such as Rh and oxygen storage materials has been improved, and even when exposed to high temperatures, the growth of complex oxide particles is suppressed and the inside of the particles is reduced. Since the buried Rh is small, almost the entire amount of Rh, that is, Rh arranged between crystal lattices or atoms inside the primary particle and Rh exposed on the surface from the inside of the primary particle exert their respective functions and exhaust. This is because it contributed to the purification of gas and can maintain high purification performance even with a small amount.
複合酸化物の粒成長を抑制できたのは、一次粒子同士の接触面積を限りなく小さくしたことにより、接触面での相互拡散による焼結を抑制できたこと、並びにRhは結晶格子又は原子間に配置されているのでRh同士の接触が抑制されたことによるものと考えられる。更に、結晶子サイズが小さいことによって、一次粒子表面に露出するRhが多くなり、反応効率が向上したものと推定される。 The grain growth of the composite oxide was suppressed because the contact area between the primary particles was made extremely small, so that sintering due to mutual diffusion at the contact surface could be suppressed, and Rh was the crystal lattice or interatomic This is considered to be because the contact between Rh is suppressed. Furthermore, it is presumed that the reaction efficiency is improved because the Rh exposed on the surface of the primary particles is increased due to the small crystallite size.
すなわち、上記実施例及び比較例の複合酸化物について、そのフレッシュ時及びエージング後のBET比表面積を測定したところ、表1の結果が得られた。このエージングは複合酸化物を大気雰囲気で1000℃の温度に24時間加熱するというものである。 That is, for the composite oxides of the above Examples and Comparative Examples, the BET specific surface area at the time of freshness and after aging was measured, and the results shown in Table 1 were obtained. This aging is to heat the composite oxide to a temperature of 1000 ° C. for 24 hours in an air atmosphere.
この比表面積の測定結果によれば、実施例の複合酸化物は比較例に比べてフレッシュ時の比表面積が十数倍大きく、エージング後も5倍程度大きい。これは、実施例の複合酸化物が中空略球状の殻又はその破片の形態となっているからであり、このように比表面積が大きいということは、複合酸化物表面に露出しているRh量も多いということであり、触媒中のRhが排気ガス浄化に効率良く働いているということができる。 According to the measurement result of the specific surface area, the complex oxide of the example has a specific surface area of 10 times larger than that of the comparative example and about 5 times larger after aging. This is because the composite oxide of the example is in the form of a hollow, substantially spherical shell or a fragment thereof, and the large specific surface area means that the amount of Rh exposed on the surface of the composite oxide. It can be said that Rh in the catalyst works efficiently for exhaust gas purification.
−複合酸化物の酸素吸蔵能について−
上述のCe及びZrを含有し且つRhが結晶格子又は原子間に配置された複合酸化物は、雰囲気が酸素過剰になると、速やかに酸素を吸蔵するとともに、酸素吸蔵量も多くなるが、その酸素吸蔵のメカニズムは以下のように推定される。
-Oxygen storage capacity of complex oxides-
The composite oxide containing Ce and Zr and having Rh arranged between crystal lattices or atoms quickly absorbs oxygen and increases the amount of oxygen stored when the atmosphere is excessive in oxygen. The occlusion mechanism is estimated as follows.
すなわち、図8(a)は実施例の複合酸化物(以下、Rhドープ複合酸化物という。)の、図8(b)はCe及びZrを含有する複合酸化物にRhを後から担持させた従来例のRh後担持複合酸化物の、各々推定される酸素吸蔵メカニズムを模式的に表したものである。なお、図8ではZr原子の図示は省略している。 That is, FIG. 8A shows a composite oxide of the example (hereinafter referred to as Rh-doped composite oxide), and FIG. 8B shows a composite oxide containing Ce and Zr, with Rh supported later. It is a schematic representation of the presumed oxygen storage mechanisms of the post-Rh-supported composite oxide of the conventional example. In FIG. 8, illustration of Zr atoms is omitted.
まず、図8(b)のRh後担持複合酸化物では、酸素(O2)は、複合酸化物内部の表面近傍に存する酸素欠損部(O空孔)には酸素イオンとなって吸蔵されるが、複合酸化物内部の比較的深い部位に存する酸素欠損部には到達することができず、この酸素欠損部は酸素吸蔵にはあまり利用されていないと考えられる。 First, in the post-Rh-supported composite oxide of FIG. 8B, oxygen (O 2 ) is occluded as oxygen ions in oxygen deficient portions (O vacancies) existing near the surface inside the composite oxide. However, it is considered that the oxygen deficient part existing in a relatively deep part inside the complex oxide cannot be reached, and this oxygen deficient part is not often used for oxygen storage.
これに対して、図8(a)のRhドープ複合酸化物では、酸素(O2)が酸素イオンとなって複合酸化物内部に存するRhに引き寄せられ、このRhを介して複合酸化物内部の酸素欠損部に瞬時に移動すると考えられる。また、複合酸化物内部にはRhが分散して存在するから、酸素イオンは複合酸化物表面から複数のRhを介してホッピング移動し、複合酸化物内部の深いところの酸素欠損部に入ると考えられる。このため、Rhドープ複合酸化物の場合は、酸素過剰雰囲気になったときの酸素吸蔵速度が速やかに高くなるとともに、この酸素吸蔵速度の最高値も高くなり、また、酸素吸蔵材内部の比較的深いところの酸素欠損部も酸素吸蔵に利用されるから、酸素吸蔵量が多くなると考えられる。 On the other hand, in the Rh-doped composite oxide of FIG. 8A, oxygen (O 2 ) becomes oxygen ions and is attracted to Rh existing inside the composite oxide, and the Rh-doped composite oxide in FIG. It is thought that it moves instantaneously to the oxygen deficient part. Further, since Rh is dispersed inside the complex oxide, oxygen ions are considered to hop through the complex oxide surface through a plurality of Rhs and enter oxygen deficient portions deep inside the complex oxide. It is done. For this reason, in the case of the Rh-doped composite oxide, the oxygen storage rate when an oxygen-excess atmosphere is rapidly increased, the maximum value of this oxygen storage rate is also increased, It is considered that the oxygen storage amount increases because the oxygen deficient portion in the deep part is also used for oxygen storage.
なし None
Claims (5)
上記一種類の触媒金属はRhであり、
上記複合酸化物の少なくとも一部は、中空の殻及びその破片の少なくとも一方の形態となって上記触媒層に存在し、
上記中空の殻又はその破片を構成する上記Ce及びZrを含有する一次粒子の結晶格子又は原子間に上記Rhの少なくとも一部が配置されており、
上記Al 2 O 3 は、上記複合酸化物と混合して上記触媒層に含まれていることを特徴とする排気ガス浄化用触媒。 An exhaust gas purifying catalyst, wherein a catalyst layer formed on a catalyst carrier contains a composite oxide containing Ce and Zr, Al 2 O 3 and at least one kind of catalyst metal,
The one type of catalytic metal is Rh,
At least a part of the composite oxide is present in the catalyst layer in the form of at least one of a hollow shell and fragments thereof,
At least a part of the Rh is arranged between crystal lattices or atoms of primary particles containing the Ce and Zr constituting the hollow shell or fragments thereof ;
The catalyst for purifying exhaust gas , wherein the Al 2 O 3 is mixed with the complex oxide and contained in the catalyst layer .
Rhが結晶格子又は原子間に配置された上記一次粒子の平均結晶子径が10nm未満であることを特徴とする排気ガス浄化用触媒。 In claim 1,
An exhaust gas purifying catalyst, wherein Rh is a crystal lattice or an average crystallite diameter of the primary particles arranged between atoms is less than 10 nm.
上記中空の殻は、その直径が0.05μm以上3.0μm以下の略球状であり、その殻壁の厚みが50nm以下であることを特徴とする排気ガス浄化用触媒。 In claim 1 or claim 2,
The exhaust gas purifying catalyst, wherein the hollow shell has a substantially spherical shape with a diameter of 0.05 μm or more and 3.0 μm or less, and a thickness of the shell wall is 50 nm or less.
Ce及びZrを含有し且つ結晶格子又は原子間にRhが配置されている複合酸化物の一次粒子から構成されていて、
上記Ce及びZrを含有する一次粒子が凝集して中空の殻及びその破片の少なくとも一方の形態となっていることを特徴とする酸素吸蔵材。 An oxygen storage material contained in the exhaust gas purifying catalyst according to any one of claims 1 to 3 ,
It is composed of primary particles of a composite oxide containing Ce and Zr and having Rh arranged between crystal lattices or atoms,
An oxygen storage material, wherein the primary particles containing Ce and Zr are aggregated to form at least one of a hollow shell and fragments thereof.
上記一次粒子の平均結晶子径が10nm未満であることを特徴とする酸素吸蔵材。 In claim 4,
An oxygen storage material, wherein an average crystallite diameter of the primary particles is less than 10 nm.