JP4521862B2 - 電気化学キャパシタ用電極及び電気化学キャパシタ - Google Patents
電気化学キャパシタ用電極及び電気化学キャパシタ Download PDFInfo
- Publication number
- JP4521862B2 JP4521862B2 JP2004244861A JP2004244861A JP4521862B2 JP 4521862 B2 JP4521862 B2 JP 4521862B2 JP 2004244861 A JP2004244861 A JP 2004244861A JP 2004244861 A JP2004244861 A JP 2004244861A JP 4521862 B2 JP4521862 B2 JP 4521862B2
- Authority
- JP
- Japan
- Prior art keywords
- electrode
- electrochemical capacitor
- active material
- ruthenium compound
- electrode active
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
ルテニウム化合物原料として三塩化ルテニウム・三水和物(小島化学薬品(株)製)0.383molとn−ブタノール100mLとを混合し、温度107℃で1時間、加熱還流した後、多重結合を有する疎水性溶媒であるベンゼン50mLを添加し、約80℃の温度で2時間、加熱還流して、電極活物質前駆体溶液を調製した。
実施例1で調製した電極活物質前駆体溶液100mLに、活性炭粉末(1200m2/g、大阪ガス製kタイプ)3gを浸漬させ、超音波を240分間印加させて含浸させた。該活性炭粉末を、空気中250℃で60分間熱処理して、電気化学キャパシタ用電極を得た。
ルテニウム化合物原料として塩化ルテニウム・三水和物0.383mol(Ru三価70%及び四価30%の混在品)と還元剤として蓚酸0.383molとをn−ブタノール100mL中で混合し、温度107℃で1時間、加熱還流した後、多重結合を有する疎水性溶媒であるベンゼン50mLを添加し、約80℃の温度で2時間、加熱還流して、電極活物質前駆体溶液を調製した。得られた溶液は、緑色透明な溶液であり、粒子状の懸濁物は観察されなかった。
硝酸ルテニウム溶液(田中貴金属工業(株)製、Ru含有量50g/L)50mLに、活性炭粉末(1200m2/g、大阪ガス製kタイプ)3gを浸漬させ、超音波を240分間印加させて、含浸させた。該活性炭粉末を、110℃で乾燥後、窒素雰囲気下600℃で60分間熱処理して、電気化学キャパシタ用電極を得た。
2 セパレータ
3 ガスケット
4 正極用集電体
5 負極用集電体
Claims (6)
- アルコール溶媒及び多重結合を有する疎水性溶媒からなる混合溶媒に、ルテニウム化合物を添加し、加熱還流させて得られる電極活物質前駆体溶液を導電性基材に塗布し、該導電性基材を空気中240〜260℃の温度で熱処理させることにより、導電性基材上に非晶質ルテニウム化合物を担持させることを特徴とする電気化学キャパシタ用電極の製造方法。
- アルコール溶媒及び多重結合を有する疎水性溶媒からなる混合溶媒に、ルテニウム化合物及び還元剤を添加し、加熱還流させて得られる電極活物質前駆体溶液を導電性基材に塗布し、該導電性基材を空気中240〜260℃の温度で熱処理させることにより、導電性基材上に非晶質ルテニウム化合物を担持させることを特徴とする電気化学キャパシタ用電極の製造方法。
- ルテニウム化合物が、三価のルテニウム化合物であることを特徴とする請求項1または請求項2に記載の電気化学キャパシタ用電極の製造方法。
- ルテニウム化合物が、三塩化ルテニウムであることを特徴とする請求項1または請求項2に記載の電気化学キャパシタ用電極の製造方法。
- 還元剤が、蓚酸及び/またはヒドラジンであることを特徴とする請求項2に記載の電気化学キャパシタ用電極の製造方法。
- 導電性基材が、チタン、タンタル、炭素及びシリコンからなる群から選ばれる少なくとも1種であることを特徴とする請求項1から請求項5のいずれか一項に記載の電気化学キャパシタ用電極の製造方法。