JP3575879B2 - 空気入りタイヤ - Google Patents
空気入りタイヤ Download PDFInfo
- Publication number
- JP3575879B2 JP3575879B2 JP20224995A JP20224995A JP3575879B2 JP 3575879 B2 JP3575879 B2 JP 3575879B2 JP 20224995 A JP20224995 A JP 20224995A JP 20224995 A JP20224995 A JP 20224995A JP 3575879 B2 JP3575879 B2 JP 3575879B2
- Authority
- JP
- Japan
- Prior art keywords
- tire
- air
- nylon
- thermoplastic resin
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の属する技術分野】
本発明は空気入りタイヤに関し、更に詳しくは空気透過防止層の少なくとも一方のサイドウォール部の部分複層化によってタイヤの軽量化及び耐エア漏れ性能の向上をはかった空気入りタイヤに関する。
【0002】
【従来の技術】
燃料消費率の低減は自動車における大きな技術的課題の一つであり、この対策の一環として空気入りタイヤの軽量化に対する要求も益々強いものになってきている。ところで、空気入りタイヤの内面には、タイヤ空気圧を一定に保持するためにハロゲン化ブチルゴムなどのような低気体透過性のゴムからなるインナーライナー層などの空気透過防止層が設けられている。しかしながら、タイヤのサイド部はトータルゲージが薄いためにそこから空気が漏れやすいという問題がある。
【0003】
空気入りタイヤのインナーライナー層としてブチルゴムなどの低気体透過性ゴムに代えて種々の材料を用いる技術が提案されている。例えば、特公昭47−31761号公報には加硫タイヤの内面に、空気透過係数[cm3(標準状態)/cm・sec ・mmHg] が30℃で10×10−13 以下、70℃で50×10−13 以下の、ポリ塩化ビニリデン、飽和ポリエステル樹脂、ポリアミド樹脂などの合成樹脂の溶液又は分散液を0.1mm以下で塗布することが開示されている。
【0004】
特開昭5−330307号公報にはタイヤ内面をハロゲン化処理(従来から知られている塩素化処理溶液、臭素溶液、ヨウ素溶液を使用)し、その上にメトキシメチル化ナイロン、共重合ナイロン、ポリウレタンとポリ塩化ビニリデンのブレンド、ポリウレタンとポリフッ化ビニリデンのブレンドのポリマー皮膜(膜厚10〜200μm)を形成することが開示されている。
【0005】
更に特開平5−318618号公報には、メトキシメチル化ナイロンの薄膜をインナーライナーとする空気入りタイヤが開示されており、この技術によれば、グリーンタイヤ内面にメトキシメチル化ナイロンの溶液又はエマルジョンを散布又は塗布し、次いでタイヤを加硫するか、或いは加硫後タイヤ内面にメトキシメチル化ナイロンの溶液又はエマルジョンを散布又は塗布することによって空気入りタイヤを製造している。
【0006】
更に、特開平6−40207号公報には、ポリ塩化ビニリデンフィルムまたはエチレンビニルアルコール共重合体フィルムから成る非空気透過層と、ポリオレフィン系フィルム、脂肪族ポリアミドフィルム、または、ポリウレタンフィルムから成る接着層を有した多層フィルムをタイヤの空気透過防止層として使用している例がある。
【0007】
【発明が解決しようとする課題】
前述の通り、ブチルゴムに代わる、空気入りタイヤのインナーライナー層用の種々の材料が提案されているが、未だ実用化されるには至っていない。かかる状況下において、我々は、先きに、新たな空気透過防止層用材料として、熱可塑性樹脂又は熱可塑性樹脂とエラストマーとのブレンドを含む空気透過係数が25×10−12 cc・cm/cm2 ・sec ・cmHg以下でヤング率が1〜500MPa のタイヤ用ポリマー組成物を提案した(例えば特願平7−150353号(特開平8−259741号公報)、同7−28318号(特開平8−217923号公報)、同7−28257号(特開平8−217922号公報)、同7−26844号(特開平8−216285号公報)、同7−28320号(特開平8−216286号公報)及び同7−11752号(特開平8−258504号公報)など参照)。
【0008】
ところで、前記の如く、タイヤのサイド部はトータルゲージが薄いため、この部分から空気が漏れやすいという問題があり、これを解決しようとしてライナーのサイド部を厚目になるように押出したり、サイド部全体のライナーを多層化すると、タイヤ質量が増加するという問題がある。
【0009】
更に、タイヤサイドウォール部に例えば部分的に2層又はそれ以上のブチルゴム空気透過防止層を設けた場合には、部分的に設けたブチルゴム層の端部にエアだまりが必然的に生じる結果となり、これが加硫故障の原因となる。従って、本発明は前述の従来技術の問題を排除してタイヤの軽量化及びサイドウォール部の耐エア漏れ性能を達成した空気入りタイヤを提供することを目的とする。
【0010】
【課題を解決するための手段】
本発明に従えば、空気透過係数が25×10-12 cc・cm/cm2 ・sec ・cmHg以下でヤング率が1〜500MPa の熱可塑性樹脂又は熱可塑性樹脂とエラストマーとのブレンドを含むポリマー組成物のフィルムからなる、タイヤ内面に配された空気透過防止層を有し、該空気透過防止層が、少なくとも一方のサイドウォール部のタイヤ最大幅点を含むタイヤ内面ペリフェリーの5〜40%の領域に、部分的に複数層配されている空気入りタイヤが提供される。
【0011】
【発明の実施の形態】
以下、本発明の構成及び作用効果について詳しく説明する。
本発明に従った空気入りタイヤの空気透過防止層を構成するフィルムは、空気透過率が25×10−12 cc・cm/cm2 ・sec ・cmHg以下、好ましくは5×10−12 cc・cm/cm2 ・sec ・cmHg以下でヤング率が1〜500MPa 、好ましくは10〜300MPa であり、またフィルムの厚さは好ましくは0.02〜0.2mm、更に好ましくは0.05〜0.2mmである。空気透過率が25×10−12 cc・cm/cm2 ・sec ・cmHgを超えると空気入りタイヤの軽量化上好ましくない。またヤング率は低過ぎるとタイヤ成型時にシワなどの発生によって成型加工性が低下し、逆に高過ぎると耐久性に問題が生じるので好ましくない。
【0012】
前記熱可塑性樹脂は空気透過防止作用を有する任意の材料とすることができる。そのような熱可塑性樹脂としては、例えば以下のような熱可塑性樹脂及びこれらの又はこれらとエラストマーなどとの任意のポリマー混合物を挙げることができる。
【0013】
ポリアミド系樹脂(例えばナイロン6(N6)、ナイロン66(N66)、ナイロン46(N46)、ナイロン11(N11)、ナイロン12(N12)、ナイロン610(N610)、ナイロン612(N612)、ナイロン6/66共重合体(N6/66)、ナイロン6/66/610共重合体(N6/66/610)、ナイロンMXD6(MXD6)、ナイロン6T、ナイロン6/6T共重合体、ナイロン66/PP共重合体、ナイロン66/PPS共重合体)及びそれらのN−アルコキシアルキル化物、例えば6−ナイロンのメトキシメチル化物、6−610−ナイロンのメトキシメチル化物、612−ナイロンのメトキシメチル化物、ポリエステル系樹脂(例えばポリブチレンテレフタレート(PBT)、ポリエチレンテレフタレート(PET)、ポリエチレンイソフタレート(PEI)、PET/PEI共重合体、ポリアリレート(PAR)、ポリブチレンナフタレート(PBN)、液晶ポリエステル、ポリオキシアルキレンジイミド酸/ポリブチレートテレフタレート共重合体などの芳香族ポリエステル)、ポリニトリル系樹脂(例えばポリアクリロニトリル(PAN)、ポリメタクリロニトリル、アクリロニトリル/スチレン共重合体(AS)、メタクリロニトリル/スチレン共重合体、メタクリロニトリル/スチレン/ブタジエン共重合体)、ポリメタクリレート系樹脂(例えばポリメタクリル酸メチル(PMMA)、ポリメタクリル酸エチル)、ポリビニル系樹脂(例えば酢酸ビニル、ポリビニルアルコール(PVA)、ビニルアルコール/エチレン共重合体(EVOH)、ポリ塩化ビニリデン(PDVC)、ポリ塩化ビニル(PVC)、塩化ビニル/塩化ビニリデン共重合体、塩化ビニリデン/メチルアクリレート共重合体、塩化ビニリデン/アクリロニトリル共重合体)、セルロース系樹脂(例えば酢酸セルロース、酢酸酪酸セルロース)、フッ素系樹脂(例えばポリフッ化ビニリデン(PVDF)、ポリフッ化ビニル(PVF)、ポリクロルフルオロエチレン(PCTFE)、テトラフロロエチレン/エチレン共重合体)、イミド系樹脂(例えば芳香族ポリイミド(PI))などを挙げることができる。
【0014】
前記熱可塑性樹脂とブレンドすることができるエラストマーとしては、ブレンドとして上記空気透過係数及びヤング率を有するものであれば、特に限定されないが、例えば以下のようなものを挙げることができる。
ジエン系ゴム及びその水添物(例えばNR、IR、エポキシ化天然ゴム、SBR、BR(高シスBR及び低シスBR)、NBR、水素化NBR、水素化SBR)、オレフィン系ゴム(例えばエチレンプロピレンゴム(EPDM、EPM)、マレイン酸変性エチレンプロピレンゴム(M−EPM)、IIR、イソブチレンと芳香族ビニル又はジエン系モノマー共重合体、アクリルゴム(ACM)、アイオノマー)、含ハロゲンゴム(例えばBr−IIR、Cl−IIR、イソブチレンパラメチルスチレン共重合体の臭素化物(Br−IPMS)、CR、ヒドリンゴム(CHR)、クロロスルホン化ポリエチレン(CSM)、塩素化ポリエチレン(CM)、マレイン酸変性塩素化ポリエチレン(M−CM))、シリコンゴム(例えばメチルビニルシリコンゴム、ジメチルシリコンゴム、メチルフェニルビニルシリコンゴム)、含イオウゴム(例えばポリスルフィドゴム)、フッ素ゴム(例えばビニリデンフルオライド系ゴム、含フッ素ビニルエーテル系ゴム、テトラフルオロエチレン−プロピレン系ゴム、含フッ素シリコン系ゴム、含フッ素ホスファゼン系ゴム)、熱可塑性エラストマー(例えばスチレン系エラストマー、オレフィン系エラストマー、エステル系エラストマー、ウレタン系エラストマー、ポリアミド系エラストマー)などを挙げることができる。
【0015】
前記した特定の熱可塑性樹脂とエラストマー成分との相溶性が異なる場合は、第3成分として適当な相溶化剤を用いて両者を相溶化させるのが好ましい。系に相溶化剤を混合することにより、熱可塑性樹脂とエラストマー成分との界面張力が低下し、その結果、分散層を形成しているゴム粒子径が微細になることから両成分の特性はより有効に発現されることになる。そのような相溶化剤としては一般的に熱可塑性樹脂及びエラストマー成分の両方又は片方の構造を有する共重合体、或いは熱可塑性樹脂又はエラストマー成分と反応可能なエポキシ基、カルボニル基、ハロゲン基、アミノ基、オキサゾリン基、水酸基等を有した共重合体の構造をとるものとすることができる。これらは混合される熱可塑性樹脂とエラストマー成分の種類によって選定すれば良いが、通常使用されるものにはスチレン/エチレン・ブチレンブロック共重合体(SEBS)及びそのマレイン酸変性物、EPDM、EPDM/スチレン又はEPDM/アクリロニトリルグラフト共重合体及びそのマレイン酸変性物、スチレン/マレイン酸共重合体、反応性フェノキシン等を挙げることができる。かかる相溶化剤の配合量には特に限定はないが、好ましくはポリマー成分(熱可塑性樹脂とエラストマー成分の総和)100重量部に対して、0.5〜10重量部が良い。
【0016】
熱可塑性樹脂とエラストマーとをブレンドする場合の特定の熱可塑性樹脂(A)とエラストマー成分(B)との組成比は、特に限定はなく、フィルムの厚さ、耐空気透過性、柔軟性のバランスで適宜決めればよいが、好ましい範囲は重量比(A)/(B)で10/90〜90/10、更に好ましくは20/80〜85/15である。
【0017】
本発明に係るポリマー組成物には、上記必須ポリマー成分に加えて、本発明のタイヤ用ポリマー組成物の必要特性を損なわない範囲で前記した相溶化剤ポリマーなどの他のポリマーを混合することができる。他ポリマーを混合する目的は、熱可塑性樹脂とエラストマー成分との相溶性を改良するため、材料のフィルム成型加工性を良くするため、耐熱性向上のため、コストダウンのため等があり、これに用いられる材料としては、例えばポリエチレン(PE)、ポリプロピレン(PP)、ポリスチレン(PS)、ABS、SBS、ポリカーボネート(PC)等が挙げられる。また、ポリエチレン、ポリプロピレン等のオレフィン共重合体、そのマレイン酸変性体、又はそのグリシジル基導入体なども挙げることができる。本発明に係るポリマー組成物には、更に一般的にポリマー配合物に配合される充填剤、カーボン、石英粉体、炭酸カルシウム、アルミナ、酸化チタンなどを上記空気透過係数及びヤング率の要件を損わない限り任意に配合することもできる。
【0018】
本発明に従えば、図1及び図2に示すように、空気透過係数が25×10−12 cc・cm/cm2 ・sec ・cmHg以下でヤング率が1〜500MPa の熱可塑性樹脂又は熱可塑性樹脂とエラストマーとのブレンドを含むポリマー組成物のフィルム1をタイヤサイドウォール部のタイヤ全内周面を実質的におおうように配置する、ポリマーフィルム2の配置の仕方には特に限定はなく数限りなく考えられるが、例えば図1−1〜図1−6に例示したように、タイヤ内周面の実質的全体に少なくとも一層のポリマーフィルム1が存在し、かつ部分的に2層又はそれ以上のポリマーフィルム2が存在する。なお、2又はそれ以上のポリマーフィルムの材料は同じであっても異なっていてもよい。更にポリマーフィルムは常法に従って成型後貼付又は接着してもよく、或いは常法に従って塗布してもよい。また、複数のフィルムはサイドウォールより内側であれば隣接している必要はなく、例えばそれらの間にカーカス層などが存在していても差支えない。
【0019】
次に、本発明に従えば、図2に示すように、タイヤの最大幅点3を含むタイヤ内面ペリフェリーの5%以上であって、40%以下の領域に部分的に空気透過防止層となるポリマーフィルムが複数層存在していることがサイド部の空気透過量を少なくするため必要である。
【0020】
更に本発明の好ましい態様においては図3(a)に示す、ステップ量のS(mm)とフィルムライナーの一層当たり厚さt(mm)との関係は、段差によるエアだまりを防ぐために25t≦Sとするのが望ましい。なお、Sの上限は1′が存在するためには、1″の幅以下でなければならないため、自然に定まる。図3(b)に示すように、ステップ量Sが小さいとポリマーフィルム1,1′,1″の一層当りの厚さはうすくても全体の段差が大きくなり、エアだまりによる加硫故障の原因となるおそれがある。しかし、図3(c)に示すように上側のポリマーフィルム1′が下側のポリマーフィルム1″をおおっているような場合にはステップ量Sは小さくてもエアだまりは起らない。
【0021】
【実施例】
以下、実施例及び比較例に従って本発明を更に詳しく説明するが、本発明の技術的範囲をこれらの実施例に限定するものでないことは言うまでもない。
実施例1〜6及び比較例1〜8
表Iに示すように、材料A〜Dからなるポリマーフィルムを用いて表Iに示す構成の空気透過防止層を有するタイヤ(サイズ:165SR13、リムサイズ:13×4 1/2−J)を作製した。これらのタイヤ及び従来の標準例について下記試験を行なった。
結果を表Iに示す。
【0022】
エアだまり試験法
加硫後のタイヤをカットし、エアだまり故障が認められた場合は不良(×)、認められない場合は良好(○)とした。
【0023】
成型加工性の試験法
タイヤ成型の際、材料が伸びてしまう場合は不良(×)、伸びない場合は良好(○)とした。
【0024】
空気漏れ試験法(圧力低下率)
初期圧力200kPa 、室温21℃、無負荷条件にて3ヵ月間放置する。内圧の測定間隔は4日毎とし、測定圧力Pt、初期圧力Po、経過日数tとして、次の式
Pt/Po=exp(−αt)
に回帰してα値を求める。得られたαを用い、t=30(日)を代入し、
β= [1−exp(−αt)] ×100
を得る。この値βを1ヵ月当たりの圧力低下率(%/月)とする。
【0025】
【表1】
【0026】
【表2】
【0027】
表I脚注(部はすべて重量部を示す)
材料A:ナイロン6(N6)(東レ製 CM4061)28部、ナイロンMXD6(MXD6)(三菱ガス化学製レニー6002)42部、マレイン酸変性エチレンプロピレンゴム(M−EPM)30部及びメチレンジアニリン0.18部から成り、空気透過係数が2.13×10−12 cc・cm/cm2 ・s.cmHg)ヤング率が257MPa の材料。
材料B:N6 25.2部、MXD6 37.8部、マスターバッチA(ブチルゴム臭素化物:エクソンケミカル製エクソンブロモブチル2244 100部、東海カーボン製カーボンブラックGPF:シーストV 60部、ステアリン酸1部、石油系炭化水素樹脂エッソ製エスコレッツ1102 10部、パラフィン系プロセス油10部)48.9部、三井石油化学製ハイセックスミリオン240M(EEA)、酸化亜鉛1.5部、DM0.5部及びイオウ0.3部から成り、空気透過係数が0.84×10−12 cc・cm/cm2 ・sec .cmHgでヤング率が244MPa の材料
材料C:N6 25.2部、MXD6 37.8部、Br−(ポリイソブチレン−p−メチルスチレン)(エクソンケミカル製EXXPRO 89−4)27.0部並びにナイロン6/ナイロン66/ナイロン610(東レ製CM4001)から成り、空気透過係数が0.63×10−12 cc・cm/cm2 ・sec .cmHgでヤング率317MPa の材料
材料D:ブチルゴム(空気透過係数55×10−12 cc・cm/cm2 ・sec .cmHg、ヤング率15MPa )
【0028】
【発明の効果】
以上説明したように、本発明に従えば、空気透過係数が25×10−12 cc・cm/cm2 ・sec .cmHg以下でヤング率が1〜500MPa の熱可塑性樹脂又は熱可塑性樹脂とエラストマーとのブレンドを含むポリマー組成物の、好ましくは0.02〜0.2mm厚の、フィルムを空気透過防止層として用い、この空気透過防止層を特定領域に複数層設けることによって、1)ゲージが非常に薄くなるため、大幅な軽量化が可能となり、2)ゲージが非常に薄くなるため、従来のように段差でエアだまりがおきず、加硫故障の原因にならず、3)ゲージが薄くても、モジュラスが高いため、成型加工性が悪化しないという効果が達せられる。
【図面の簡単な説明】
【図1】本発明に従った空気透過防止層のポリマーフィルムのサイドウォール部断面における配置を示す図面でそのいくつかの態様を図(1−1)〜(1−6)に示す。
【図2】本発明に従った空気透過防止層のポリマーフィルムのサイドウォール部断面における複数層の配置の要件の一例を示す図面である。
【図3】本発明の好ましい態様におけるサイドウォール部のステップ量S(mm)と空気透過防止層一層当りの厚さ(mm)との関係を示す図面であり、図3(a)は部分的なポリマーフィルムが2層の場合の配置を示す図面であり、図3(b)はステップ量が小さくて一層当りの厚さはうすくても全体の段差が大きくなり、エアだまりによる加硫故障の原因となることを示す図面であり、更に図3(c)は上側のポリマーフィルム1′が下側のポリマーフィルム1″をおおっている場合にはステップ量Sは小さくてもエアだまりが起らないことを示す図面である。
【符号の説明】
1,1′,1″…ポリマー組成物フィルム
2…ポリマー組成物フィルム(部分多層化部)
3…タイヤ最大幅点
4…タイヤ
W…最大幅
P…内面ペリフェリー
d…段差
Claims (2)
- 空気透過係数が25×10-12 cc・cm/cm2 ・sec ・cmHg以下でヤング率が1〜500MPa の熱可塑性樹脂又は熱可塑性樹脂とエラストマーとのブレンドを含むポリマー組成物のフィルムからなる、タイヤ内面に配された空気透過防止層を有し、該空気透過防止層が、少なくとも一方のサイドウォール部のタイヤ最大幅点を含むタイヤ内面ペリフェリーの5〜40%の領域に、部分的に複数層配されている空気入りタイヤ。
- 空気透過防止層1層の厚さが、0.02〜0.2mmである請求項1に記載の空気入りタイヤ。