JP2023511987A - 酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトー及びその製造方法 - Google Patents
酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトー及びその製造方法 Download PDFInfo
- Publication number
- JP2023511987A JP2023511987A JP2022545387A JP2022545387A JP2023511987A JP 2023511987 A JP2023511987 A JP 2023511987A JP 2022545387 A JP2022545387 A JP 2022545387A JP 2022545387 A JP2022545387 A JP 2022545387A JP 2023511987 A JP2023511987 A JP 2023511987A
- Authority
- JP
- Japan
- Prior art keywords
- trabecular
- tibial plateau
- zirconium
- niobium alloy
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
2)第2の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-80℃~-120℃に下げ、一定温度で5時間~10時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて16時間~36時間置き、温度を室温に調整して第3の中間生成物を得るステップ、
3)第3の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-80℃~-120℃に下げ、一定温度で5時間~10時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて16時間~36時間置き、温度を室温に調整して第4の中間生成物を得るステップ、
4)第4の中間生成物を機械加工トリミング、光沢仕上げ、洗浄及び乾燥させ、半脛骨プラトートレイ上面の表面粗さRa≦0.050μmとなる第5の中間生成物を得るステップ、及び、
5)第5の中間生成物を管状炉に入れ、酸素含有量5質量%~15質量%の常圧不活性ガスを導入し、5℃/分~20℃/分で500℃~700℃に加熱し、0.4℃/分~0.9℃/分で温度を400℃~495℃に下げ、200℃以下に自然冷却してから取り出し、酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーを得るステップ、
を有する酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの製造方法であって、
前記不活性ガスはヘリウムガス又はアルゴンガスであり;
前記酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの構造は、半脛骨プラトートレイ1を含み、前記半脛骨プラトートレイの直線縁の上面に側壁2が設けられ、前記半脛骨プラトートレイの下面の側壁近くに長丸孔付きの半楕円形キール3が設けられ、前記半脛骨プラトートレイの下面及び長丸孔付きの半楕円形キールの表面に骨梁が設けられ、半脛骨プラトートレイの下面において前記長丸孔付きの半楕円形キールを連結する部分以外の他の部分に設けられた骨梁は、前方骨梁8及び後方骨梁9に分けられ、前記前方骨梁8と後方骨梁9の領域分割線6は前記側壁2に対して垂直に配置され、又は側壁に対して45°~70°の角度4をなすように配置され;
前記長丸孔付きの半楕円形キールの表面に設けられた骨梁は、上部骨梁10及び下部骨梁11に分けられ、前記上部骨梁及び下部骨梁の領域分割線が第2の領域分割線12であり、第2の領域分割線が長丸孔の頂部の下面又は長丸孔の底部の上面に位置し;
上部骨梁10の気孔径及び気孔率は、順次に後方骨梁、前方骨梁及び下部骨梁より小さい。
酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの製造方法であって、以下の構成を有する。すなわち、
1)ジルコニウム・ニオブ合金粉末を原料として、3Dプリントで一体成形して酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの第1の中間生成物を得、第1の中間生成物を熱間静水圧加圧装置に入れ、ヘリウムガスの保護雰囲気下にて、温度を1250℃に上げ、180MPaにて一定温度で3時間放置しながら常圧まで下げ、200℃以下となるまで炉内で冷却して取り出し、第2の中間生成物を得るステップ、
2)第2の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-80℃に下げ、一定温度で10時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて16時間置き、温度を室温に調整して第3の中間生成物を得るステップ、
3)第3の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-80℃に下げ、一定温度で10時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて16時間置き、温度を室温に調整して第4の中間生成物を得るステップ、
ステップ2)、ステップ3)の温度調整の具体的なステップは、温度を-120℃に上げ、一定温度で5時間保持し、次に温度を-40℃に上げ、一定温度で5時間保持し、さらに温度を4℃に上げ、一定温度で3時間保持した後、温度を上げ、
4)第4の中間生成物を機械加工トリミング、光沢仕上げ、洗浄及び乾燥させ、半脛骨プラトートレイ上面の表面粗さRa=0.012μmとなる第5の中間生成物を得るステップ、
5)第5の中間生成物を管状炉に入れ、酸素含有量5質量%の常圧ヘリウムガスを導入し、5℃/分で500℃に加熱し、0.4℃/分で温度を400℃に下げ、200℃以下に自然冷却してから取り出し、酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーを得るステップ、
酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの第1の中間生成物、第2の中間生成物、第3の中間生成物、第4の中間生成物、第5の中間生成物は、酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの構造と同じである。
前記長丸孔付きの半楕円形キールの表面に設けられた骨梁は、上部骨梁10及び下部骨梁11に分けられ、前記上部骨梁11及び下部骨梁の領域分割線が第2の領域分割線12であり、第2の領域分割線12が長丸孔の頂部の下面(図4)に位置し;
ジルコニウム・ニオブ合金粉末の化学組成は、質量%でZr:85.6%、Nb:12.5%を含有し、残部が不可避不純物であり;ジルコニウム・ニオブ合金粉末の粒子径は、45~150μmであり、西安賽隆金属材料有限責任会社から購入した。
後方骨梁9の気孔径は、500μmで、気孔率が68%であり;
前方骨梁8の気孔径は、600μmで、気孔率が73%であり;
下部骨梁11の気孔径は、700μmで、気孔率が78%である。
酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの製造方法であって、以下の構成を有する。すなわち、
1)ジルコニウム・ニオブ合金粉末を原料として、3Dプリントで一体成形して酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの第1の中間生成物を得、第1の中間生成物を熱間静水圧加圧装置に入れ、ヘリウムガスの保護雰囲気下にて、温度を1325℃に上げ、160MPaにて一定温度で2時間放置しながら常圧まで下げ、200℃以下となるまで炉内で冷却して取り出し、第2の中間生成物を得るステップ、
2)第2の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-100℃に下げ、一定温度で7時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて24時間置き、温度を室温に調整して第3の中間生成物を得るステップ、
3)第3の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-100℃に下げ、一定温度で7時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて24時間置き、温度を室温に調整して第4の中間生成物を得るステップ、
ステップ2)、ステップ3)の温度調整ステップは、温度を-100℃に上げ、一定温度で4時間保持し、次に温度を-30℃に上げ、一定温度で4時間保持し、さらに温度を6℃に上げ、一定温度で2時間保持した後、温度を上げ、
4)第4の中間生成物を機械加工トリミング、光沢仕上げ、洗浄及び乾燥させ、半脛骨プラトートレイ上面の表面粗さRa=0.035μmとなる第5の中間生成物を得るステップ、
5)第5の中間生成物を管状炉に入れ、酸素含有量10質量%の常圧ヘリウムガスを導入し、15℃/分で600℃に加熱し、0.7℃/分で温度を450℃に下げ、200℃以下に自然冷却してから取り出し、酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーを得るステップ、
酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの第1の中間生成物、第2の中間生成物、第3の中間生成物、第4の中間生成物、及び第5の中間生成物は、酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの構造と同じである。
前記長丸孔付きの半楕円形キールの表面に設けられた骨梁は、上部骨梁10及び下部骨梁11に分けられ、前記上部骨梁11及び下部骨梁の領域分割線が第2の領域分割線12であり、第2の領域分割線12が長丸孔の頂部の下面(図4)に位置し;
前記長丸孔付きの半楕円形キールの表面に設けられた骨梁は、上部骨梁10及び下部骨梁11に分けられ、前記上部骨梁10及び下部骨梁11の領域分割線が第2の領域分割線12であり、第2の領域分割線12が長丸孔の底部の上面(図3)に位置し;
ジルコニウム・ニオブ合金粉末の化学組成は、質量%でZr:93.4%、Nb:5.1%を含有し、残部が不可避不純物であり;ジルコニウム・ニオブ合金粉末の粒子径は、45~150μmであり、西安賽隆金属材料有限責任会社から購入し;
前記上部骨梁10の気孔径は、351μm、気孔率が60%;
後方骨梁9の気孔径は、451μmで、気孔率が66%であり;
前方骨梁8の気孔径は、551μmで、気孔率が70%であり;
下部骨梁11の気孔径は、651μmで、気孔率が76%である。
酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの製造方法であって、以下の構成を有する。すなわち、
1)ジルコニウム・ニオブ合金粉末を原料として、3Dプリントで一体成形して酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの第1の中間生成物を得、第1の中間生成物を熱間静水圧加圧装置に入れ、アルゴンガスの保護雰囲気下にて、温度を1400℃に上げ、140MPaにて一定温度で1時間放置しながら常圧まで下げ、200℃以下となるまで炉内で冷却して取り出し、第2の中間生成物を得るステップ、
2)第2の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-120℃に下げ、一定温度で5時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて36時間置き、温度を室温に調整して第3の中間生成物を得るステップ、
3)第3の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-120℃に下げ、一定温度で5時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて36時間置き、温度を室温に調整して第4の中間生成物を得るステップ、
ステップ2)、ステップ3)の温度調整の具体的なステップは、温度を-80℃に上げ、一定温度で3時間保持し、次に温度を-20℃に上げ、一定温度で3時間保持し、さらに温度を8℃に上げ、一定温度で1時間保持した後、温度を上げ、
4)第4の中間生成物を機械加工トリミング、光沢仕上げ、洗浄及び乾燥させ、半脛骨プラトートレイ上面の表面粗さRa=0.050μmとなる第5の中間生成物を得るステップ、
5)第5の中間生成物を管状炉に入れ、酸素含有量15質量%の常圧アルゴンガスを導入し、20℃/分で700℃に加熱し、0.9℃/分で温度を495℃に下げ、200℃以下に自然冷却してから取り出し、酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーを得るステップ、
前記酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの構造は、半脛骨プラトートレイ1を含み、前記半脛骨プラトートレイの直線縁の上面に側壁2が設けられ、前記半脛骨プラトートレイの下面の側壁近くに長丸孔付きの半楕円形キール3が設けられ、前記半脛骨プラトートレイの下面及び長丸孔付きの半楕円形キールの表面に骨梁が設けられ、半脛骨プラトートレイの下面において前記長丸孔付きの半楕円形キールを連結する部分以外の他の部分に設けられた骨梁は、前方骨梁8及び後方骨梁9に分けられ、前記前方骨梁8と後方骨梁9の領域分割線6は側壁に対して70°の角度4をなすように配置され;前記領域分割線6と側壁2との交点5が側壁の中心に位置し;
前記長丸孔付きの半楕円形キールの表面に設けられた骨梁は、上部骨梁10及び下部骨梁11に分けられ、前記上部骨梁10及び下部骨梁11の領域分割線が第2の領域分割線12であり、第2の領域分割線12が長丸孔の頂部の下面に位置し;
ジルコニウム・ニオブ合金粉末の化学組成は、質量%でZr:96.5%、Nb:1%を含有し、残部が不可避不純物であり;ジルコニウム・ニオブ合金粉末の粒子径は、45~150μmであり、西安賽隆金属材料有限責任会社から購入し;
前記上部骨梁10の気孔径は、450μm、気孔率が65%;
後方骨梁9の気孔径は、550μmで、気孔率が70%であり;
前方骨梁8の気孔径は、650μmで、気孔率が75%であり;
下部骨梁11の気孔径は、750μmで、気孔率が80%である。
均質な骨梁単一コンパートメント脛骨プラトーの製造方法及び構造と実施例1との相違点としては、
上部骨梁、下部骨梁、前方骨梁及び後方骨梁は、同種の骨梁であり、気孔径は500μm、気孔率は68%、骨梁の厚さは1.5mmである。
ジルコニウム・ニオブ合金粉末(実施例1と同じ)を原料として、3Dプリントによる一体成形及び機械加工トリミングを経て、実施例1と同じ構造の単一コンパートメント脛骨プラトーを得た。
プロテーゼと骨界面の信頼できる生物学的固定は、主にプロテーゼ固定の一次安定性に依存する。プロテーゼと骨界面の間の過度の相対的な運動は、オッセオインテグレーション過程を阻害する。研究によると、プロテーゼと骨界面の微動が50~150μmを超えると、骨界面に大量の線維性組織が形成され、プロテーゼの固定強度が低下し、最終的にはプロテーゼの緩みにつながる。実施例1と比較例1の有限要素モデル、及び脛骨プラトーの海綿骨領域分割の簡易モデルを有限要素解析にかけ、図7~図8に示す微動クラウドマップを得た。比較例1の均質な骨梁単一コンパートメント脛骨プラットフォームと比較して、実施例1の酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトー有限要素モデルと脛骨プラトー骨組織有限要素モデル界面との間の微動の最大値は4.50μmで、43%程度減少し、本発明の酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーは人体に植え込まれた後、優れた一次安定性を有することを示している。
Claims (7)
- 1)ジルコニウム・ニオブ合金粉末を原料として、3Dプリントで一体成形して酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの第1の中間生成物を得、前記第1の中間生成物を熱間静水圧加圧装置に入れ、不活性ガスの保護雰囲気下にて、温度を1250℃~1400℃に上げ、140MPa~180MPaにて一定温度で1時間~3時間放置しながら常圧まで下げ、200℃以下となるまで炉内で冷却して取り出し、第2の中間生成物を得るステップ、
2)前記第2の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-80℃~-120℃に下げ、一定温度で5時間~10時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて16時間~36時間置き、温度を室温に調整して第3の中間生成物を得るステップ、
3)前記第3の中間生成物をプログラム冷却ボックスに入れ、1℃/分の速度で温度を-80℃~-120℃に下げ、一定温度で5時間~10時間放置し、プログラム冷却ボックスから取り出し、液体窒素内に入れて16時間~36時間置き、温度を室温に調整して第4の中間生成物を得るステップ、
4)前記第4の中間生成物を機械加工トリミング、光沢仕上げ、洗浄及び乾燥させ、半脛骨プラトートレイ上面の表面粗さRa≦0.050μmとなる第5の中間生成物を得るステップ、
5)前記第5の中間生成物を管状炉に入れ、酸素含有量5質量%~15質量%の常圧不活性ガスを導入し、5℃/分~20℃/分で500℃~700℃に加熱し、0.4℃/分~0.9℃/分で温度を400℃~495℃に下げ、200℃以下に自然冷却してから取り出し、酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーを得るステップ、
を有する酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの製造方法であって、
前記不活性ガスはヘリウムガス又はアルゴンガスであり;
前記酸化物層を含むジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトーの構造は、半脛骨プラトートレイ(1)を含み、前記半脛骨プラトートレイの直線縁の上面に側壁(2)が設けられ、前記半脛骨プラトートレイの下面の前記側壁近くに長丸孔付きの半楕円形キール(3)が設けられ、前記半脛骨プラトートレイの下面及び前記長丸孔付きの半楕円形キールの表面に骨梁が設けられ、前記半脛骨プラトートレイの下面において前記長丸孔付きの半楕円形キールを連結する部分以外の他の部分に設けられた骨梁は、前方骨梁(8)及び後方骨梁(9)に分けられ、前記前方骨梁(8)と前記後方骨梁(9)の領域分割線(6)は前記側壁(2)に対して垂直に配置され、又は前記側壁(2)に対して45°~70°の角度(4)をなすように配置され;前記長丸孔付きの半楕円形キールの表面に設けられた骨梁は、上部骨梁(10)及び下部骨梁(11)に分けられ、前記上部骨梁及び前記下部骨梁の領域分割線が第2の領域分割線(12)であり、前記第2の領域分割線が長丸孔の頂部の下面又は長丸孔の底部の上面に位置し;
上部骨梁(10)の気孔径及び気孔率は、順次に前記後方骨梁、前記前方骨梁及び前記下部骨梁より小さい、
ことを特徴とする製造方法。 - 前記ジルコニウム・ニオブ合金粉末の化学組成は、質量%でZr:85.6%~96.5%、Nb:1.0%~12.5%を含有し、残部が不可避不純物であり;前記ジルコニウム・ニオブ合金粉末の粒子径は、45μm~150μmである
請求項1に記載の方法。 - 前記ステップ2)、前記ステップ3)の温度調整は、温度を-120℃~-80℃に上げ、一定温度で3時間~5時間保持し、次に温度を-40℃~-20℃に上げ、一定温度で3時間~5時間保持し、さらに温度を4℃~8℃に上げ、一定温度で1時間~3時間保持した後、温度を上げる
請求項1に記載の方法。 - 前記領域分割線(6)は、前記側壁(2)に対して垂直に設置され、前記領域分割線(6)と前記側壁(2)との交点(5)が前記側壁を側壁前部(13)及び側壁後部(14)に分割し、前記側壁前部(13)と前記側壁後部(14)の比率が(2-3):1である
請求項1に記載の方法。 - 前記領域分割線(6)は、前記側壁に対して45°~70°の角度(4)をなすように配置され、領域分割線(6)と前記側壁(2)との前記交点(5)が前記側壁の中心に位置する
請求項1に記載の方法。 - 前記上部骨梁(10)の気孔径は、351μm~450μmで、気孔率が60%~65%であり;
前記後方骨梁(9)の気孔径は、451μm~550μmで、気孔率が66%~70%であり;
前記前方骨梁(8)の気孔径は、551μm~650μmで、気孔率が70%~75%であり;
前記下部骨梁(11)の気孔径は、651μm~750μmで、気孔率が76%~80%であり;
前記上部骨梁(10)、前記後方骨梁(9)、前記前方骨梁(8)及び前記下部骨梁(11)は、1mm~2mmの範囲の同じ厚さを有する
請求項1に記載の方法。 - 請求項1ないし6のいずれかに記載の方法で製造された酸化物層を含む
ことを特徴とするジルコニウム・ニオブ合金の領域分割骨梁単一コンパートメント脛骨プラトー。