JP2022121031A - インサート成形品及びその製造方法 - Google Patents

インサート成形品及びその製造方法 Download PDF

Info

Publication number
JP2022121031A
JP2022121031A JP2021018158A JP2021018158A JP2022121031A JP 2022121031 A JP2022121031 A JP 2022121031A JP 2021018158 A JP2021018158 A JP 2021018158A JP 2021018158 A JP2021018158 A JP 2021018158A JP 2022121031 A JP2022121031 A JP 2022121031A
Authority
JP
Japan
Prior art keywords
insert
molded product
gate
resin
flat plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2021018158A
Other languages
English (en)
Inventor
成嘉 中村
Shigeyoshi Nakamura
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nakanishi Metal Works Co Ltd
Original Assignee
Nakanishi Metal Works Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nakanishi Metal Works Co Ltd filed Critical Nakanishi Metal Works Co Ltd
Priority to JP2021018158A priority Critical patent/JP2022121031A/ja
Priority to CN202210104082.9A priority patent/CN114905691A/zh
Priority to US17/649,251 priority patent/US11759985B2/en
Priority to EP22154452.1A priority patent/EP4039439A1/en
Publication of JP2022121031A publication Critical patent/JP2022121031A/ja
Pending legal-status Critical Current

Abstract

【課題】金属部品の平板状部の表面を覆う樹脂部品の被覆部の肉厚を薄くした場合であっても成形不良の発生を抑制し、それによりインサート成形品の寸法精度及び強度を安定させる。前ショットのコールドスラグが射出成形用金型のキャビティに進入することを抑制し、それによりインサート成形品の外観不良及び強度不良を防止する。【解決手段】金属部品１は、平板状部３を含む形状であり、平板状部３には貫通穴７が設けられる。樹脂部品２は、平板状部３の表面Ｅを覆う被覆部５を含む形状であり、被覆部５の表面にはゲート跡部Ｂがある。ゲート跡部Ｂの反対側に、金属部品１の平板状部３に設けた貫通穴７が位置する。樹脂部品２は、貫通穴７に充填された充填部Ｈを有する。【選択図】図３

Description

本発明は、金属部品と樹脂部品とからなるインサート成形品に関する。
様々な産業分野において、軽量化を図る等の目的で、金属部品と樹脂部品とからなるインサート成形品が広く使用されている（例えば、特許文献１及び２参照）。
特許文献１は、流体軸受装置に使用されるディスクハブの発明である。前記ディスクハブ１０は、金属部品である芯金１３と、樹脂部品である樹脂成形部１４とからなる。
特許文献２は、軸流ファン用ロータユニットの発明である。前記ロータユニットは、金属部品であるロータホルダ２５及び回転軸２１と、樹脂部品であるインペラ４とからなる。
特開２００８－１３０２０８号公報 特開２０１０－０２５０８７号公報
特許文献１及び２のような金属部品と樹脂部品とからなるインサート成形品において、金属部品は、平板状部（例えば、特許文献１の略円盤状の芯金１３、及び特許文献２のロータホルダ２５の環状の上面２５２の部分参照）を有し、樹脂部品は、前記平板状部の表面を覆う被覆部（例えば、特許文献１の円板部１０ａ、及び特許文献２のインペラカップ４１の略円盤状の部分参照）を有する。
前記インサート成形品を製造する射出成形用金型（例えば、特許文献１の図６参照）において、ゲートはピンゲートであり、金属部品の平板状部の表面に対向するようにゲートを配置している（例えば、特許文献１の図６（ａ）のゲート２４、特許文献２の図５のゲート痕４４３参照）。
前記インサート成形品において、さらなる軽量化や省スペース化の要請のため、金属部品の平板状部の表面を覆う樹脂部品の被覆部の肉厚を薄くすると、例えば、ゲート直下の肉厚がゲート径よりも小さい場合、ゲートが固化する前にゲート直下の樹脂肉厚が薄い部位の樹脂が固化してしまい、十分な保圧を掛けることができない。それにより、ヒケやボイド等の成形不良が発生しやすく、寸法精度及び強度が安定しないという問題点がある。その上、前ショットのコールドスラグが射出成形用金型のキャビティに進入して成形品の外観不良及び強度不良に繋がるおそれがある。
本発明は、金属部品の平板状部の表面を覆う樹脂部品の被覆部の肉厚を薄くした場合であっても成形不良の発生を抑制し、それによりインサート成形品の寸法精度及び強度を安定させることを目的とする。また、本発明は、前ショットのコールドスラグが射出成形用金型のキャビティに進入することを抑制し、それによりインサート成形品の外観不良及び強度不良を防止することを目的とする。
本発明の要旨は以下のとおりである。
〔１〕
金属部品と樹脂部品とからなるインサート成形品であって、
前記金属部品は、
平板状部を含む形状であり、
前記平板状部には貫通穴又は止り穴が設けられ、
前記樹脂部品は、
前記平板状部の表面を覆う被覆部を含む形状であり、
前記被覆部の表面にはゲート跡部があり、
前記ゲート跡部の反対側に、前記金属部品の前記平板状部に設けた前記貫通穴又は前記止り穴が位置し、
前記樹脂部品は、
前記貫通穴又は前記止り穴に充填された充填部を有する、
インサート成形品。
〔２〕
前記ゲート跡部から前記金属部品の前記平板状部の表面までの距離は、
前記樹脂部品の前記ゲート跡部の径よりも小さい、
〔１〕に記載のインサート成形品。
〔３〕
前記ゲート跡部から前記金属部品の前記平板状部の裏面までの距離、又は前記ゲート跡部から前記止り穴の底面までの距離は、
前記樹脂部品の前記ゲート跡部の径よりも大きい、
〔２〕に記載のインサート成形品。
〔４〕
金属部品と樹脂部品とからなるインサート成形品の製造方法であって、
前記金属部品は、
平板状部を含む形状であり、
前記平板状部には貫通穴又は止り穴が設けられ、
前記樹脂部品は、
前記平板状部の表面を覆う被覆部を含む形状であり、
射出成形用金型のゲートは、ピンゲートであり、
前記金型を開いて、インサート品である前記金属部品を、前記ピンゲートに前記貫通穴又は前記止り穴が対向するように前記金型内にセットする工程と、
前記金型を閉じて、前記ピンゲートから前記樹脂部品の溶融した成形樹脂材料を射出して前記樹脂部品を射出成形する工程と、
を含むインサート成形品の製造方法。
〔５〕
前記ピンゲートから前記金属部品の前記平板状部の表面までの距離は、
前記ピンゲートの径よりも小さい、
〔４〕に記載のインサート成形品の製造方法。
〔６〕
前記ピンゲートから前記金属部品の前記平板状部の裏面までの距離、又は前記ピンゲートから前記止り穴の底面までの距離は、
前記ピンゲートの径よりも大きい、
〔５〕に記載のインサート成形品の製造方法。
本発明における「インサート成形品」は、射出成形用金型内に挿入した金属部品の周りに樹脂を注入して金属部品と樹脂部品とを一体化するインサート成形を行って製造した成形品である。
本発明における「ゲート跡部」は、インサート成形品における、射出成形用金型のゲートの跡、又は前記ゲートの跡を機械加工等で切除した部分である。
本発明のインサート成形品、及びインサート成形品の製造方法によれば、金属部品の平板状部の表面に対向するピンゲートから溶融樹脂材料を射出して樹脂部品を射出成形してインサート成形品を製造する際に、金属部品の貫通穴又は止り穴が前記ピンゲートに対向している。そのため、金属部品の平板状部の表面を覆う樹脂部品の被覆部の肉厚を薄くしても、ゲート直下の樹脂の肉厚が厚くなる。それにより、ゲートが固化する前にゲート直下の樹脂が固化してしまうことがなくなるので、十分な保圧を掛けることができる。
したがって、ヒケやボイド等の成形不良が発生し難くなるので、インサート成形品の寸法精度及び強度が安定する。その上、前ショットのコールドスラグが射出成形用金型のキャビティに進入することを抑制できるので、インサート成形品の外観不良及び強度不良を防止できる。
本発明の実施の形態に係るインサート成形品の斜視図である。 （ａ）は図１のインサート成形品の正面図、（ｂ）は図１のインサート成形品の縦断面右側面図である。 （ａ）は図１のインサート成形品の要部拡大正面図、（ｂ）は図１のインサート成形品の要部拡大縦断面右側面図である。 図１のインサート成形品の金属部品の斜視図である。 図１のインサート成形品を成形する射出成形用金型の概略を示す縦断面図である。 図５の射出成形用金型の要部拡大縦断面図である。 第１変形例であるインサート成形品の斜視図である。 （ａ）は図７のインサート成形品の正面図、（ｂ）は図７のインサート成形品の縦断面右側面図である。 （ａ）は図７のインサート成形品の要部拡大正面図、（ｂ）は図７のインサート成形品の要部拡大縦断面右側面図である。 図７のインサート成形品の金属部品の斜視図である。 図７のインサート成形品を成形する射出成形用金型の概略を示す縦断面図である。 図１１の射出成形用金型の要部拡大縦断面図である。 第２変形例であるインサート成形品の斜視図である。 （ａ）は図１３のインサート成形品の正面図、（ｂ）は図１３のインサート成形品の縦断面右側面図である。 第３変形例であるインサート成形品の斜視図である。 （ａ）は図１５のインサート成形品の正面図、（ｂ）は図１５のインサート成形品の縦断面右側面図である。 図１５のインサート成形品の金属部品の斜視図である。 図１５のインサート成形品を成形する射出成形用金型の概略を示す縦断面図である。 第４変形例であるインサート成形品の斜視図である。 （ａ）は図１９のインサート成形品の正面図、（ｂ）は図１９のインサート成形品の縦断面右側面図である。 図１９のインサート成形品の金属部品の斜視図である。 図１９のインサート成形品を成形する射出成形用金型の概略を示す縦断面図である。
以下、本発明に係る実施の形態を図面に基づいて説明する。
本明細書において、金属部品の平板状部の表面に向かって見た図（例えば、図２（ａ）、図８（ａ）、図１４（ａ）、図１６（ａ）、及び図２０（ａ））を正面図とする。
＜インサート成形品＞
図１の斜視図、図２（ａ）の正面図及び図２（ｂ）の縦断面右側面図、図３（ａ）の要部拡大正面図及び図３（ｂ）の要部拡大縦断面右側面図、並びに図４の斜視図に示すように、本発明の実施の形態に係るインサート成形品Ａは、金属部品１とび樹脂部品２とからなる。樹脂部品２は、例えば、生産性に優れる熱可塑性樹脂を成形したものである。
金属部品１は、平板状部３である中空円板３Ａ、及び筒状部４である円筒４Ａからなり、中空円板３Ａには、例えば３個の貫通穴７が周方向等分に設けられる。
樹脂部品２は、中空円板３Ａの表面Ｅを覆う被覆部５、及び円筒４Ａの外周面を覆う被覆部６からなり、被覆部５の表面５Ａには、ゲート逃がしである凹部５Ｃ内にゲート跡部Ｂがある。
樹脂部品２の被覆部５の裏面５Ｂのゲート跡部Ｂの反対側に、金属部品１の中空円板３Ａに設けた貫通穴７が位置する。樹脂部品２は、貫通穴７に充填された充填部Ｈ（図３（ｂ）参照）を有する。充填部Ｈは金属部品１と樹脂部品２の回り止めとしても機能する。
図２（ｂ）に示すように、インサート成形品Ａは、中空円板３Ａの裏面及び円筒４Ａの内周面が露出している。したがって、後述するインサート成形品の製造方法におけるインサート品セット工程で金属部品１を射出成形用金型Ｉの可動型１０（図５）にセットする際に、中空円板３Ａの裏面及び円筒４Ａの内周面が可動型１０に当接するので、インサート品である金属部品１を可動型１０に対して軸方向及び径方向に位置決めできる。
図２（ａ）及び図２（ｂ）に示すように、中空円板３Ａの表面を覆う被覆部５の内径は、中空円板３Ａの内径よりも大きく、中空円板３Ａの表面の内周側部分が露出している。したがって、後述するインサート成形品の製造方法における射出成形工程で射出成形用金型Ｉを型締めした際に、中空円板３Ａの表面の内周側部分が固定型９（図５）に当接して安定する。
図３（ａ）及び図３（ｂ）に示すゲート跡部Ｂから金属部品１の平板状部３である中空円板３Ａの表面Ｅまでの距離Ｊは、樹脂部品２のゲート跡部Ｂの径Ｄよりも小さい（Ｊ＜Ｄ）。また、ゲート跡部Ｂから金属部品１の平板状部３である中空円板３Ａの裏面Ｆまでの距離Ｋは、樹脂部品２のゲート跡部Ｂの径Ｄよりも大きい（Ｋ＞Ｄ）。Ｋ＞Ｄとすることにより、ゲートが固化する前にゲート直下の樹脂が固化してしまうことがなくなるので、十分な保圧を掛けることができる。
＜インサート成形品の製造方法＞
図５の縦断面図、及び図６の要部拡大縦断面図に概略を示す射出成形用金型Ｉを参照して、インサート成形品Ａの製造方法について説明する。射出成形用金型ＩのゲートはピンゲートＧである。
（インサート品セット工程）
射出成形用金型Ｉの可動型１０を開き、インサート品である金属部品１を、固定型９のピンゲートＧに中空円板３Ａの貫通穴７が対向するように可動型１０にセットする。
（射出成形工程）
射出成形用金型Ｉの可動型１０を閉じて型締めし、固定型９のピンゲートＧからキャビティＣに樹脂部品２の溶融した成形樹脂材料Ｍを射出して樹脂部品２を射出成形する。
図６に示すピンゲートＧから金属部品１の中空円板３Ａの表面Ｅまでの距離Ｊは、ピンゲートＧの径Ｄよりも小さい（Ｊ＜Ｄ）。また、ピンゲートＧから金属部品１の中空円板３Ａの裏面Ｆまでの距離Ｋは、ピンゲートＧの径Ｄよりも大きい（Ｋ＞Ｄ）。
（成形品取出工程）
射出成形用金型Ｉを冷却して樹脂を固化させた後、可動型１０を開く。それにより、ピンゲートＧからインサート成形品Ａが自動的に分離され、インサート成形品Ａにはゲート跡部Ｂ（図２（ａ）、並びに図３（ａ）及び図３（ｂ）参照）が残る。次に、可動型１０に設けた図示しないエジェクターピンにより押し出すことによりインサート成形品Ａを取り出す。
＜第１変形例のインサート成形品＞
図７の斜視図、図８（ａ）の正面図及び図８（ｂ）の縦断面右側面図、並びに図９（ａ）の要部拡大正面図及び図９（ｂ）の要部拡大縦断面右側面図に示す第１変形例のインサート成形品Ａにおいて、図１、図２（ａ）及び図２（ｂ）、並びに図３（ａ）及び図３（ｂ）と同一符号は、同一又は相当する部品又は部分を示している。また、図１０の斜視図に示す金属部品１において、図４と同一符号は同一又は相当する部分を示している。
第１変形例のインサート成形品Ａにおける金属部品１の平板状部３である中空円板３Ａには、貫通穴７ではなく止り穴８が設けられる。
図９（ａ）及び図９（ｂ）に示すゲート跡部Ｂから金属部品１の平板状部３である中空円板３Ａの表面Ｅまでの距離Ｊは、樹脂部品２のゲート跡部Ｂの径Ｄよりも小さい（Ｊ＜Ｄ）。また、ゲート跡部Ｂから金属部品１の平板状部３である中空円板３Ａの止り穴８の底面までの距離Ｌは、樹脂部品２のゲート跡部Ｂの径Ｄよりも大きい（Ｌ＞Ｄ）。Ｌ＞Ｄとすることにより、ゲートが固化する前にゲート直下の樹脂が固化してしまうことがなくなるので、十分な保圧を掛けることができる。
＜第１変形例のインサート成形品の製造方法＞
図１１の縦断面図、及び図１２の要部拡大縦断面図に概略を示す射出成形用金型Ｉを参照して、第１変形例のインサート成形品Ａの製造方法について説明する。射出成形用金型ＩのゲートはピンゲートＧである。
（インサート品セット工程）
射出成形用金型Ｉの可動型１０を開き、インサート品である金属部品１を、固定型９のピンゲートＧに中空円板３Ａの止り穴８が対向するように可動型１０にセットする。
（射出成形工程）
射出成形用金型Ｉの可動型１０を閉じて型締めし、固定型９のピンゲートＧからキャビティＣに樹脂部品２の溶融した成形樹脂材料Ｍを射出して樹脂部品２を射出成形する。
図１２に示すピンゲートＧから金属部品１の中空円板３Ａの表面Ｅまでの距離Ｊは、ピンゲートＧの径Ｄよりも小さい（Ｊ＜Ｄ）。また、ピンゲートＧから金属部品１の中空円板３Ａの止り穴８の底面までの距離Ｌは、ピンゲートＧの径Ｄよりも大きい（Ｌ＞Ｄ）。
（成形品取出工程）
射出成形用金型Ｉを冷却して樹脂を固化させた後、可動型１０を開く。それにより、ピンゲートＧからインサート成形品Ａが自動的に分離され、インサート成形品Ａにはゲート跡部Ｂ（図８（ａ）、並びに図９（ａ）及び図９（ｂ）参照）が残る。次に、可動型１０に設けた図示しないエジェクターピンにより押し出すことによりインサート成形品Ａを取り出す。
＜第２変形例のインサート成形品＞
図１３の斜視図、図１４（ａ）の正面図及び図１４（ｂ）の縦断面右側面図に示す第２変形例のインサート成形品Ａにおいて、図１、図２（ａ）及び図２（ｂ）と同一符号は、同一又は相当する部品又は部分を示している。
第２変形例のインサート成形品Ａは、被覆部５の内周面Ｎの形状が図１、図２（ａ）及び図２（ｂ）のような円ではなく、ゲート跡部Ｂ及びゲート逃がしである凹部５Ｃの周囲を除いて内周面Ｎが径方向外方へ後退しており、それにより被覆部５の軽量化を図っている。
＜第３変形例のインサート成形品＞
図１５の斜視図、図１６（ａ）の正面図及び図１６（ｂ）の縦断面右側面図に示す第３変形例のインサート成形品Ａにおいて、図１、図２（ａ）及び図２（ｂ）と同一符号は、同一又は相当する部品又は部分を示している。また、図１７の斜視図に示す金属部品１において、図４と同一符号は同一又は相当する部分を示している。
第３変形例のインサート成形品Ａは、中空円板状である。したがって、図１７の斜視図に示す金属部品１には、図４のような筒状部４である円筒４Ａがなく、図１５の斜視図に示す樹脂部品２には、図１のような円筒４Ａの外周面を覆う被覆部６がない。
図１６（ｂ）に示すように、インサート成形品Ａは、中空円板３Ａの裏面が露出している。したがって、後述するインサート成形品の製造方法におけるインサート品セット工程で金属部品１を射出成形用金型Ｉの可動型１０（図１８）にセットする際に、中空円板３Ａの裏面が可動型１０に当接するので、インサート品である金属部品１を可動型１０に対して軸方向に位置決めできる。
図１６（ａ）及び図１６（ｂ）に示すように、中空円板３Ａの表面を覆う被覆部５の内径は、中空円板３Ａの内径よりも大きく、中空円板３Ａの表面の内周側部分が露出している。したがって、後述するインサート成形品の製造方法における射出成形工程で射出成形用金型Ｉを型締めした際に、中空円板３Ａの表面の内周側部分が固定型９（図１８）に当接して安定する。
＜第３変形例のインサート成形品の製造方法＞
図１８の縦断面図に概略を示す射出成形用金型Ｉを参照して、第３変形例のインサート成形品Ａの製造方法について説明する。射出成形用金型ＩのゲートはピンゲートＧである。
（インサート品セット工程）
射出成形用金型Ｉの可動型１０を開き、インサート品である金属部品１を、固定型９のピンゲートＧに中空円板３Ａの貫通穴７が対向するように可動型１０にセットする。
（射出成形工程）
射出成形用金型Ｉの可動型１０を閉じて型締めし、固定型９のピンゲートＧからキャビティＣに樹脂部品２の溶融した成形樹脂材料Ｍを射出して樹脂部品２を射出成形する。
（成形品取出工程）
射出成形用金型Ｉを冷却して樹脂を固化させた後、可動型１０を開く。それにより、ピンゲートＧからインサート成形品Ａが自動的に分離され、インサート成形品Ａにはゲート跡部Ｂ（図１６（ａ）参照）が残る。次に、可動型１０に設けた図示しないエジェクターピンにより押し出すことによりインサート成形品Ａを取り出す。
＜第４変形例のインサート成形品＞
図１９の斜視図、図２０（ａ）の正面図及び図２０（ｂ）の縦断面右側面図に示す第４変形例のインサート成形品Ａにおいて、図１、図２（ａ）及び図２（ｂ）と同一符号は、同一又は相当する部品又は部分を示している。また、図２１の斜視図に示す金属部品１において、図４と同一符号は同一又は相当する部分を示している。
第４変形例のインサート成形品Ａの金属部品１の板状部３は、図４のような中空円板３Ａではなく、例えば六角形である中空多角形板３Ｂである。金属部品１の筒状部４は、図４のような円筒４Ａではなく、例えば六角筒である角筒４Ｂである。
図２０（ｂ）に示すように、インサート成形品Ａは、中空多角形板３Ｂの裏面及び角筒４Ｂの内面が露出している。したがって、後述するインサート成形品の製造方法におけるインサート品セット工程で金属部品１を射出成形用金型Ｉの可動型１０（図２２）にセットする際に、中空多角形板３Ｂの裏面及び角筒４Ｂの内面が可動型１０に当接するので、インサート品である金属部品１を可動型１０に対して軸方向及び径方向に位置決めできる。
図２０（ａ）及び図２０（ｂ）に示すように、中空多角形板３Ｂの表面を覆う被覆部５の内径は、中空多角形板３Ｂの内径よりも大きく、中空多角形板３Ｂの表面の内周側部分が露出している。したがって、後述するインサート成形品の製造方法における射出成形工程で射出成形用金型Ｉを型締めした際に、中空多角形板３Ｂの表面の内周側部分が固定型９（図２２）に当接して安定する。
＜第４変形例のインサート成形品の製造方法＞
図２２の縦断面図に概略を示す射出成形用金型Ｉを参照して、第４変形例のインサート成形品Ａの製造方法について説明する。射出成形用金型ＩのゲートはピンゲートＧである。
（インサート品セット工程）
射出成形用金型Ｉの可動型１０を開き、インサート品である金属部品１を、固定型９のピンゲートＧに中空多角形板３Ｂの貫通穴７が対向するように可動型１０にセットする。
（射出成形工程）
射出成形用金型Ｉの可動型１０を閉じて型締めし、固定型９のピンゲートＧからキャビティＣに樹脂部品２の溶融した成形樹脂材料Ｍを射出して樹脂部品２を射出成形する。
（成形品取出工程）
射出成形用金型Ｉを冷却して樹脂を固化させた後、可動型１０を開く。それにより、ピンゲートＧからインサート成形品Ａが自動的に分離され、インサート成形品Ａにはゲート跡部Ｂ（図２０（ａ）参照）が残る。次に、可動型１０に設けた図示しないエジェクターピンにより押し出すことによりインサート成形品Ａを取り出す。
＜本発明の実施の形態に係るインサート成形品の構造＞
以上のとおり、本発明の実施の形態に係る金属部品１と樹脂部品２とからなるインサート成形品Ａにおいて、金属部品１は平板状部３を含む形状であり、平板状部３には貫通穴７又は止り穴８が設けられる。前記インサート成形品Ａにおいて、樹脂部品２は、平板状部３の表面Ｅを覆う被覆部５を含む形状であり、被覆部５の表面５Ａにはゲート跡部Ｂがある。そして、樹脂部品２の被覆部５の裏面５Ｂのゲート跡部Ｂの反対側に、金属部品１の平板状部３に設けた貫通穴７又は止り穴８が位置し、樹脂部品２は、貫通穴７又は止り穴８に充填された充填部Ｈを有する。
＜作用効果＞
本発明の実施の形態に係るインサート成形品Ａ、及びインサート成形品Ａの製造方法によれば、金属部品１の平板状部３の表面Ｅに対向するピンゲートＧから溶融樹脂材料Ｍを射出して樹脂部品２を射出成形してインサート成形品Ａを製造する際に、金属部品１の貫通穴７又は止り穴８がピンゲートＧに対向している。そのため、金属部品１の平板状部３の表面Ｅを覆う樹脂部品２の被覆部５の肉厚を薄くしても、ゲート直下の樹脂の肉厚が厚くなる。それにより、ゲートが固化する前にゲート直下の樹脂が固化してしまうことがなくなるので、十分な保圧を掛けることができる。
したがって、ヒケやボイド等の成形不良が発生し難くなるので、インサート成形品Ａの寸法精度及び強度が安定する。その上、前ショットのコールドスラグが射出成形用金型ＩのキャビティＣに進入することを抑制できるので、インサート成形品Ａの外観不良及び強度不良を防止できる。
以上の実施の形態において、平板状部３は中空円板３Ａ又は中空多角形板３Ｂであり、何れも、中空穴がある。本発明はこのような形状のものに限定されるものではなく、本発明の「平板状部」には中央穴がないものも含まれる。
以上の実施の形態の記載はすべて例示であり、これに制限されるものではない。本発明の範囲から逸脱することなく種々の改良及び変更を施すことができる。
１ 金属部品
２ 樹脂部品
３ 平板状部
３Ａ 中空円板
３Ｂ 中空多角形板
４ 筒状部
４Ａ 円筒
４Ｂ 角筒
５ 被覆部
５Ａ 表面
５Ｂ 裏面
５Ｃ 凹部（ゲート逃がし）
６ 被覆部
７ 貫通穴
８ 止り穴
９ 固定型
１０ 可動型
Ａ インサート成形品
Ｂ ゲート跡部
Ｃ キャビティ
Ｄ ゲート跡部の径（ピンゲートの径）
Ｅ 表面
Ｆ 裏面
Ｇ ピンゲート
Ｈ 充填部
Ｉ 射出成形用金型
Ｊ ゲート跡部から金属部品の平板部の表面までの距離
Ｋ ゲート跡部から金属部品の平板部の裏面までの距離
Ｌ ゲート跡部から止り穴の底面までの距離
Ｍ 樹脂部品の溶融した成形樹脂材料
Ｎ 内周面

Claims (6)

  1. 金属部品と樹脂部品とからなるインサート成形品であって、
    前記金属部品は、
    平板状部を含む形状であり、
    前記平板状部には貫通穴又は止り穴が設けられ、
    前記樹脂部品は、
    前記平板状部の表面を覆う被覆部を含む形状であり、
    前記被覆部の表面にはゲート跡部があり、
    前記ゲート跡部の反対側に、前記金属部品の前記平板状部に設けた前記貫通穴又は前記止り穴が位置し、
    前記樹脂部品は、
    前記貫通穴又は前記止り穴に充填された充填部を有する、
    インサート成形品。
  2. 前記ゲート跡部から前記金属部品の前記平板状部の表面までの距離は、
    前記樹脂部品の前記ゲート跡部の径よりも小さい、
    請求項１に記載のインサート成形品。
  3. 前記ゲート跡部から前記金属部品の前記平板状部の裏面までの距離、又は前記ゲート跡部から前記止り穴の底面までの距離は、
    前記樹脂部品の前記ゲート跡部の径よりも大きい、
    請求項２に記載のインサート成形品。
  4. 金属部品と樹脂部品とからなるインサート成形品の製造方法であって、
    前記金属部品は、
    平板状部を含む形状であり、
    前記平板状部には貫通穴又は止り穴が設けられ、
    前記樹脂部品は、
    前記平板状部の表面を覆う被覆部を含む形状であり、
    射出成形用金型のゲートは、ピンゲートであり、
    前記金型を開いて、インサート品である前記金属部品を、前記ピンゲートに前記貫通穴又は前記止り穴が対向するように前記金型内にセットする工程と、
    前記金型を閉じて、前記ピンゲートから前記樹脂部品の溶融した成形樹脂材料を射出して前記樹脂部品を射出成形する工程と、
    を含むインサート成形品の製造方法。
  5. 前記ピンゲートから前記金属部品の前記平板状部の表面までの距離は、
    前記ピンゲートの径よりも小さい、
    請求項４に記載のインサート成形品の製造方法。
  6. 前記ピンゲートから前記金属部品の前記平板状部の裏面までの距離、又は前記ピンゲートから前記止り穴の底面までの距離は、
    前記ピンゲートの径よりも大きい、
    請求項５に記載のインサート成形品の製造方法。
JP2021018158A 2021-02-08 2021-02-08 インサート成形品及びその製造方法 Pending JP2022121031A (ja)