JP2021138804A - ポリエステル樹脂組成物及びその成形品、並びにこれらの製造方法 - Google Patents
ポリエステル樹脂組成物及びその成形品、並びにこれらの製造方法 Download PDFInfo
- Publication number
- JP2021138804A JP2021138804A JP2020035743A JP2020035743A JP2021138804A JP 2021138804 A JP2021138804 A JP 2021138804A JP 2020035743 A JP2020035743 A JP 2020035743A JP 2020035743 A JP2020035743 A JP 2020035743A JP 2021138804 A JP2021138804 A JP 2021138804A
- Authority
- JP
- Japan
- Prior art keywords
- polyester resin
- resin composition
- component
- mol
- respect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
ステンレス製オートクレーブにTPA、EG、1,4−シクロヘキサンジメタノール(CHDM)を表1〜表3の樹脂組成(比較例9のみトリメチロールプロパン(TMP)を添加)で、グリコール成分のモル数/酸成分のモル数=1.16、250℃、200kPaの条件下でエステル化を行い、その後、リン酸、Ge触媒を仕込んで、275℃、100Paの減圧下で重縮合反応を行った。押出のカッター回転数を調整して、表1〜表3のIV、100チップの質量のチップを採取した。その後、ドラム乾燥機で120℃×15Hr(真空)(比較例2のみ、110℃×15Hr(真空))の条件で結晶化し、ドラム型の固相重合機で表1〜表3の条件(真空下で固相重合)で固相重合し、冷却後、固相重合品のチップを採取した。得られたチップを分析及び評価結果を表1〜表3に示した。表において用いた略語は以下の通りである。表1〜表3に示す評価項目の評価方法及び評価基準を以下に示す。
後、MI測定機を使用して、測定温度270℃、荷重2.16kg、オリフイス径2mm、滞留6分の条件でメルトフローレート(g/10分)を測定した。
○:連続成形可;
△:ドローダウンが大或いは小のため、成形が困難;
×:ドローダウンが非常に大或いは非常に小のため、成形不可。
○:透明性良好;
×:白濁或いはぶつあり。
○:無色;
×:黄味。
○:5本落下テストし、全部割れなかった;
△:5本落下テストし、1〜2本割れた;
×:5本落下テストし、3本以上割れた。
Claims (4)
- ジカルボン酸成分としてテレフタル酸成分、ジオール成分としてエチレングリコール成分を主成分とする共重合ポリエステル含むポリエステル樹脂組成物であって、
前記ジオール成分は、ジオール成分のモル数に対して、1,4−シクロヘキサンジメタノールを5.0〜10.0モル%、及びジエチレングリコール成分を1.0〜4.0モル%含み、
前記ジカルボン酸成分において、3個以上のカルボキシ基を有する多官能性酸成分はジカルボン酸成分のモル数に対して0.02モル%以下であり、
前記ジオール成分において、3個以上のヒドロキシ基を有する多官能性アルコール成分はジオール成分のモル数に対して0.02モル%以下であり、
極限粘度が1.12〜1.20dl/gであり、
前記ポリエステル樹脂組成物の質量に対してGe原子含有量が65〜100ppmであり、
前記ポリエステル樹脂組成物の質量に対してP原子含有量が1〜50ppmであり、
末端カルボキシ基が20当量/トン以下であり、
270℃におけるメルトフローレイトが0.5〜7.5g/10minである、
ことを特徴とするポリエステル樹脂組成物。 - 請求項1に記載のポリエステル樹脂組成物を成形したダイレクトブロー成形品。
- 重合触媒としてゲルマニウム化合物を用い、リン化合物を添加し、ジカルボン酸のモル数に対して95モル%以上のテレフタル酸を含むジカルボン酸と、ジオールのモル数に対して90モル%以上のエチレングリコール及び5〜10モル%の1,4−シクロヘキサンジメタノールを含むジオールとを溶融重合させて、チップ形態を有する中間物を作製する溶融重合工程と、
前記中間物を208℃以上の重合温度で固相重合する固相重合工程と、を含み、
前記ゲルマニウム化合物は、製造されるポリエステル樹脂組成物の質量に対してゲルマニウム原子の含有量が65〜100ppmとなるように添加し、
前記ジカルボン酸において、3個以上のカルボキシ基を有する多官能性酸化合物はジカルボン酸のモル数に対して0.02モル%以下であり、
前記ジオールにおいて、3個以上のヒドロキシ基を有する多官能性アルコール化合物はジオールのモル数に対して0.02モル%以下であり、
前記リン化合物は、製造されるポリエステル樹脂組成物の質量に対してリン原子の含有量が1〜50ppmとなるように添加し、
前記固相重合工程における前記チップは100個当たり1.0〜2.5gである、ポリエステル樹脂組成物の製造方法。 - 請求項3に記載の製造方法によってポリエステル樹脂組成物を得る工程と、
前記ポリエステル樹脂組成物をダイレクトブロー成形する工程と、を含む、
ダイレクトブロー成形品の製造方法。