JP2020152871A - 水性塗料組成物 - Google Patents
水性塗料組成物 Download PDFInfo
- Publication number
- JP2020152871A JP2020152871A JP2019055020A JP2019055020A JP2020152871A JP 2020152871 A JP2020152871 A JP 2020152871A JP 2019055020 A JP2019055020 A JP 2019055020A JP 2019055020 A JP2019055020 A JP 2019055020A JP 2020152871 A JP2020152871 A JP 2020152871A
- Authority
- JP
- Japan
- Prior art keywords
- activated carbon
- coating composition
- water
- based catalyst
- manganese oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
例えば、米国のカリフォルニア州等の一部の地域では、オゾンを分解する触媒が担持されたラジエータを車両に搭載し、その車両を走行させることにより、大気の改善を図る大気浄化システムが検討されており、直接オゾン還元技術(DOR;Direct Ozone Reduction)を使用した自動車、例えば、大気中のオゾンをオゾン分解触媒(オゾン浄化触媒)により分解することができる車両用大気浄化装置を備えた自動車が実用化されている。特に、米国のカリフォルニア州等では、このような直接オゾン還元技術(DOR)を導入した車両やその車両を販売しているメーカーに対して、光化学スモッグの原因物質である非メタン有機ガス(NMOG;Non-Methane Organic Gases)の排出量を削減したとみなす所定の特典(NMOGクレジット認定)を付与している。
また、特許文献3には、金属酸化物の触媒だけでなく、オゾンを浄化する機能を備える活性炭を使用した車両用大気浄化装置が提案されている。
ところが、上述したNMOGクレジットにおいては、所定期間または所定距離走行後のオゾン浄化性能に応じて付与されることから、上記の車両用大気浄化装置を搭載した車両においては、オゾンの分解除去性能を検出することが義務づけられ、浄化装置のオゾン分解浄化性能をモニターする車載診断装置(OBD)も搭載されることになる。このため、上記の車両用大気浄化装置を搭載した車両は、コスト高となってしまう問題があった。また、ラジエータの熱交換性能を維持する必要から、ラジエータのフィンにオゾン分解触媒層を設ける面積にも制約があり、大気中のオゾンの分解にも限度があった。
また、「中位径」とは、JIS Z 8901「試験用粉体及び試験用粒子」の本文及び解説の用語の定義によれば、粉体の粒径分布において、ある粒子径より大きい個数(または質量)が、全粉体のそれの50%を占めるときの粒子径(直径)、即ち、オーバサイズ50%の粒径であり、通常、メディアン径または50%粒子径といいD50と表わされる。定義的には、平均粒子径と中位径で粒子群のサイズを表現されるが、ここでは、商品説明の表示、レーザ回折・散乱法によって測定した値である。そして、この「レーザ回折・散乱法によって測定した中位径」とは、レーザ回折式粒度分布測定装置を用いてレーザ回折・散乱法によって得られた粒度分布において積算重量部が50%となる粒子径(D50)をいう。なお、上記数値は、厳格なものでなく、製品毎の誤差があり、測定等による誤差を含むと1割程度以下の誤差の混入を否定するものではない。この誤差の観点から見ると、正規分布を呈しており、粒径は正規分布を示すものであるから、中位径≒平均粒子径と見做しても両者の違いは数パーセント内であり、誤差と見做される程度である。
更に、上記pH調整剤とは、塗料調製において水素イオン指数を所定のpH、好ましくは、pH7〜pH12、より好ましくは、pH9.5〜pH11の範囲内に調整するためのもので、中和剤を含む概念である。
上記二酸化マンガン系触媒としては、好ましくは、中位径(平均粒子径)が1μm〜20μmの範囲内にあり、BET法による比表面積が100〜400m2/gの範囲内である二酸化マンガン系触媒を用いるのが好ましい。粒子径が小さすぎるものは、再凝集しやすいため分散安定性や分散性に欠け、一方、粒子径が大きすぎるものは、表面積が小さいことで高いオゾン分解性能が得られない。更に、塗膜の成膜性や付着性にも劣る。また、表面積が大きすぎるものも、再凝集しやすいため分散安定性及び分散性に欠け、一方で、表面積が小さすぎるものでは、高いオゾン分解性能を得ることできない。更に、塗膜の成膜性や付着性能にも劣る。中位径(平均粒子径)が1μm〜20μmの範囲内にあり、BET法による比表面積が100〜400m2/gの範囲内である二酸化マンガン系触媒を用いることで、分散性や分散安定性が良く、高いオゾン分解性能を得ることができる。より好ましくは、中位径(平均粒子径)が3μm〜18μm、更に好ましくは、5μm〜15μmの範囲内にあるものである。また、BET法による比表面積が、より好ましくは、150〜350m2/g、更に好ましくは、180〜300m2/gの範囲内にあるものである。
なお、上記水性塗料組成物中の前記酸化マンガン系触媒と前記活性炭の配合重量比は、各成分の固形分換算重量比である。即ち、水性塗料組成物から形成される塗膜成分中の酸化マンガン系触媒及び活性炭の重量比が、20:80≦酸化マンガン系触媒:活性炭≦80:20、より好ましくは、30:70≦酸化マンガン系触媒:活性炭≦70:30となるように混合されたものである。
なお、上記重量平均分子量(Mw)は、ゲル浸透クロマトグラフィー(GPC;GEL permeation chromatography)法により測定され、GPCで測定したクロマトグラムを標準ポリスチレンの分子量に換算したものである。
なお、上述した数値は、必ずしも厳格であることを要求されず、使用する材料や、塗料の用途、計側・計量等による誤差を含む概略値であり、当然、数割の誤差を否定するものではない。
この請求項1の発明に係る水性塗料組成物によれば、ポリアクリレート系分散剤によって、酸化マンガン系触媒と活性炭を細かく高分散でき、また、その分散安定性も高くできる。よって、貯蔵安定性が高い。更に、硬化した塗膜にブツが生じ難く、成膜性及び付着性の高い塗膜を形成でき、高分散された酸化マンガン系触媒と活性炭に多くのオゾン量を付着できることによって、高いオゾン分解性能を発揮させることができる。特に、酸化マンガン系触媒及び活性炭の併用により、それらを単独で用いた場合と比較して高いオゾン分解性能が得られる。
本発明者らは、鋭意実験研究の結果、前記ポリアクリレート系分散剤を用いることで前記酸化マンガン系触媒及び前記活性炭の分散度が、グラインドゲージによる線状法の測定で最大粒子径(Dmax)20μm以下になるまで分散させることができ、グラインドゲージによる線状法の測定で最大粒子径(Dmax)20μm以下になるまで分散された水性塗料組成物では、活性炭等の凝集体が少なくて成膜性及び付着性の高い塗膜を形成でき、そして、前記酸化マンガン系触媒及び前記活性炭によるオゾン吸着量を高くできることで、高いオゾン分解性が得られ、更に、分散安定性も高くて貯蔵安定性にも優れることを見出した。
よって、請求項1乃至請求項6の何れか1つに記載の効果に加えて、安定した塗膜性能及び塗料組成物の長期の保存性を得ることができる。
本発明者らの鋭意実験研究により、前記ポリアクリレート系分散剤を用いることで前記酸化マンガン系触媒及び前記活性炭の粒子径が、レーザー解析法による体積基準の90%の累積粒子径(D90)で10μm以下となり、このような粒子サイズに分散された水性塗料組成物によれば、粗粒が少ないことで、塗膜ブツやざらつきが少なく、塗膜の外観性や付着性に優れることが確認された。また、凝集体が少ないから、前記酸化マンガン系触媒及び前記活性炭によるオゾン吸着量を高くできることで、高いオゾン分解性が得られ、更に、分散安定性も高くて貯蔵安定性にも優れるものであった。
よって、請求項1乃至請求項7の何れか1つに記載の効果に加えて、塗膜の外観性に優れ、また、オゾン分解性及び貯蔵安定性が高いものとなる。
したがって、ポリアクリレート系分散剤によって、酸化マンガン系触媒と活性炭を細かく高分散でき、また、その分散安定性も高くできる。よって、貯蔵安定性が高い水性塗料組成物を得ることができる。更に、このようにして得られた水性塗料組成物を基材に塗布し乾燥することにより硬化した塗膜においては、ブツが生じ難い。よって、成膜性及び付着性の高い塗膜を形成できる。そして、その硬化塗膜では、高分散された酸化マンガン系触媒と活性炭が多くのオゾン量を付着できることによって、高いオゾン分解性能を発揮させることができる。特に、酸化マンガン系触媒及び活性炭の併用により、それらを単独で用いた場合と比較して高いオゾン分解性能が得られる。
ここで、本発明者らは、鋭意実験研究の結果、前記ポリアクリレート系分散剤を用いることで前記酸化マンガン系触媒及び前記活性炭の分散度が、グラインドゲージによる線状法の測定で最大粒子径(Dmax)20μm以下になるまで分散させることができ、グラインドゲージによる線状法の測定で最大粒子径(Dmax)20μm以下になるまで分散された水性塗料組成物では、活性炭等の凝集体が少なくて成膜性及び付着性の高い塗膜を形成でき、そして、前記酸化マンガン系触媒及び前記活性炭によるオゾン吸着量を高くできることで、高いオゾン分解性が得られ、更に、分散安定性も高くて貯蔵安定性にも優れることを見出した。
よって、請求項10に記載の効果に加えて、安定した塗膜性能及び塗料組成物の長期の保存性を得ることができる。
ここで、本発明者らの鋭意実験研究により、前記ポリアクリレート系分散剤を用いることで前記酸化マンガン系触媒及び前記活性炭の粒子径が、レーザー解析法による体積基準90%の累積粒子径(D90)で10μm以下となり、このような粒子サイズに分散された水性塗料組成物によれば、粗粒が少ないことで、塗膜ブツやざらつきが少なく、塗膜の外観性や付着性に優れることが確認された。また、凝集体が少ないから、前記酸化マンガン系触媒及び前記活性炭によるオゾン吸着量を高くできることで、高いオゾン分解性が得られ、更に、分散安定性も高くて貯蔵安定性にも優れるものであった。
よって、請求項10または請求項11に記載の効果に加えて、貯蔵安定性が高い水性塗料組成物を得ることができ、また、水性塗料組成物から得られる塗膜が、その外観性に優れ、更に、高いオゾン分解性を発揮できる。
本発明の実施の形態に係る水性塗料組成物は、酸化マンガン系触媒と、活性炭と、ポリアクリレート系分散剤と、水性樹脂と、pH調整剤と、溶媒としての水とを含有するものである。
二酸化マンガンは、天然のものであってもよいし、電解法や化学合成法により製造されたものであってもよく、更に、非晶質のものであってもよいし、結晶構造を含むものであってもよい。二酸化マンガンの結晶構造としては、例えば、アルファ型、ベータ型、ガンマ型、デルタ型があるが、より好ましくは、α−二酸化マンガン(クリプトメレン(cryptomelane)形態のもの)である。また、二酸化マンガンは、アモルファス構造を有するものであってもよい。
なお、二酸化マンガン系触媒としては、二酸化マンガン(MnO2)をベースにして助触媒としてNiO、CuO、AgOなどが添加されたものであってもよいが、好ましくは、二酸化マンガンの含有率が70%以上、より好ましくは、80%以上のものである。
一方、酸化マンガン系触媒は高価であり、酸化マンガン系触媒のみを単独で用いた場合には、塗料がコスト高となってしまうところ、活性炭は安価に入手できるから、酸化マンガン系触媒及び活性炭を併用することにより、水性塗料組成物のコストも抑えられる
即ち、本実施の形態においては、分散工程として、酸化マンガン系触媒と、活性炭と、溶媒としてのイオン交換水等の水と、更に、酸化マンガン系触媒及び活性炭の高分散性を確保するために分散剤としてポリアクリレート系分散剤を混合し、それらを混合分散機に入れて分散する。
これにより、酸化マンガン系触媒及び活性炭を十分に脱凝集させて安定化させることができる。即ち、酸化マンガン系触媒及び活性炭を細かく高分散でき、例えば、JISK 5600及びJISK 5400(1990)に準拠しグラインドゲージにより測定される分散度が、線状法で、最大粒子径(Dmax)20μm以下にすることができる。また、レーザー回折式粒度分布測定装置を用いたレーザー解析法では、体積基準の90%の累積粒子径(D90)で、10μm以下にすることができる。そして、このように細かい粒度に酸化マンガン系触媒及び活性炭が高分散された水性塗料組成物から形成された塗膜では、ブツやざらつきが抑制され、優れた成膜性及び基材対する付着性が確保され、更に、酸化マンガン系触媒及び活性炭によるオゾン吸着量が高くなることで高いオゾン分解性能が発揮される。また、塗膜の平滑性が良いことで、良好な塗膜外観性が得られる。加えて、このようにポリアクリレート系分散剤を用いた水性塗料組成物では、酸化マンガン系触媒及び活性炭の分散安定性も高くて再凝集しないことで、貯蔵安定性も高く長期の保存が可能となる。
このポリアクリレート系分散剤は、その重量平均分子量が5000〜30000の範囲内にあるものが好ましい。分子量が高いものほど、分子内に複数の吸着サイトを有するため低濃度からでも酸化マンガン系触媒や活性炭を多点に吸着して凝集を阻止できる。しかし、分子量が高すぎるものでは、塗料成分との相溶性、親和性が低下して馴染みが悪くなり塗料化が困難となる。一方で分子量が低すぎるものでは、吸着点が少ないことで、酸化マンガン系触媒や活性炭の分散性に劣るものとなる。分散性を高めるために配合量を多くすると、酸化マンガン系触媒や活性炭へのオゾンの吸着を阻害し、オゾン性能を損なうことになる。重量分子量が5000〜30000の範囲内であるポリアクリレート系分散剤であれば、他の材料との馴染みもよく、酸化マンガン系触媒や活性炭の高分散性を確保できる。より好ましくは、重量平均分子量が6000〜28000の範囲内にあるものであり、更に好ましくは、重量平均分子量が7000〜25000の範囲内にあるものである。
このようなポリアクリレート系分散剤としては、市販の製品、例えば、BYK-Chemie(ビックケミー)社のDESPERBYK、Ciba Specialty Chemicals社やEFKA ADDITIVES B.V.(エフカアディティブズ)社のEFKA、楠本化成(株)社のDISPARLON、SANNOPKO(サンノプコ)社のSNシックナー等を使用することができる。
なお、このようなポリアクリレート系分散剤による酸化マンガン系触媒及び活性炭の高分散及び分散安定性の付与は、例えば、ポリアクリレートの酸化マンガン系触媒及び活性炭に対する電気的反発による吸着や、ポリアクリレートのアンカー基やポリマー鎖等による立体障害等によって、酸化マンガン系触媒及び活性炭の凝集を阻止(脱凝集)し、酸化マンガン系触媒及び活性炭を細かい粒子サイズで安定させていること等が考えられる。特に、ポリアクリレート系分散剤の高分子量体によって、複数の吸着サイトを有することで低濃度の使用量でも、酸化マンガン系触媒及び活性炭に吸着して、酸化マンガン系触媒及び活性炭の高分散を可能とし、高濃度の使用を必要としないことで、酸化マンガン系触媒及び活性炭へのオゾンの吸着を阻害し難い。
(メタ)アクリル酸エステルとしては、例えば(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸プロピル、(メタ)アクリル酸イソプロピル、(メタ)アクリル酸−n−ブチル、(メタ)アクリル酸イソブチル、(メタ)アクリル酸ペンチル、(メタ)アクリル酸ヘキシル、(メタ)アクリル酸エチルヘキシル、(メタ)アクリル酸−2−ヒドロキシエチル、(メタ)アクリル酸ヒドロキシプロピル、(メタ)アクリル酸−3−ヒドロキシブチル、(メタ)アクリル酸−2,2−ビス(ヒドロキシメチル)エチル、(メタ)アクリル酸−3−クロロ−2−ヒドロキシプロピル、(メタ)アクリル酸グリシジル、(メタ)アクリル酸アミノエチル、(メタ)アクリル酸アミノプロピル、(メタ)アクリル酸ジメチルアミノエチル、(メタ)アクリル酸ジエチルアミノエチル、(メタ)アクリル酸メトキシエチル、(メタ)アクリル酸メトキシプロピル、(メタ)アクリル酸メトキシブチル、(メタ)アクリル酸ステアリル等を挙げることができる。
このときの着色顔料としては、例えば、カーボンブラック、酸化チタン、酸化鉄、酸化亜鉛有機系のアゾキレート系顔料、不溶性アゾ系顔料、縮合アゾ系顔料、ジケトピロロピロール系顔料、ベンズイミダゾロン系顔料、フタロシアニン系顔料、インジゴ顔料、ペリノン系顔料、ペリレン系顔料、ジオキサン系顔料、キナクリドン系顔料、イソインドリノン系顔料、金属錯体顔料、黄鉛、黄色酸化鉄、ベンガラ、二酸化チタン等が使用できる。
消泡剤としては、例えば、シリコン系やアクリル系等の消泡剤が使用でき、このような消泡剤の添加により、塗料組成物を調製する混合時に細かい泡が発生して水性塗料組成物が不均一になるのを防止し、粘度や流動性を調整することができる。また、消泡により気泡からの水分の侵入による錆の発生を防止でき、防錆性の向上を図ることができる。
ドライヤ(乾燥剤)としては、例えば、ナフテン酸コバルト、ナフテン酸鉛等の金属ドライヤ(金属乾燥剤)を使用でき、このようなドライヤを添加することで、水性塗料組成物が塗布されて塗膜が形成される段階において、乾燥の促進を図り、水性樹脂が更に重合して緻密な塗膜となるのを促進できる。
安定剤としては、例えば、アルカノールアミン誘導体(ジイソプロパノールアミン、エタノールアミン、ジエタノールアミン、トリイソプロパノールアミン、トリエタノールアミン)等を使用でき、このような安定剤を添加した場合には、流動性、粘度、分散性等を調製して塗料の安定化を図ることができる。また、アルカノールアミン誘導体は、初期錆防止剤として機能することもある。
こうして作製された水性塗料組成物は、公知の塗装方法、例えば、エアスプレー法、シャワー法、スプレー法、ロールコート法、カーテンフローコート法、ダイコート法、刷毛塗り法、浸漬法、シボリ(シゴキ)法、ナイフコーター法、バーコート法、静電塗装法等の塗布手段により、基材の所定の塗装部位に任意の塗布量、厚さ及び塗布形態で塗布できる。
基材に塗布された水性塗料組成物は、自然乾燥によって、必要に応じて、所定温度での所定時間の加熱乾燥、乾燥機による強制乾燥によって水分、溶媒が蒸発、揮発されることで硬化し、塗布した基材の表面上で硬化塗膜となる。そして、本実施の形態の水性塗料組成物から形成された硬化塗膜においては、塗膜成分として酸化マンガン系触媒及び活性炭を含むことによりオゾン分解性を発揮する。
このように酸化マンガン系触媒及び活性炭が細かく高分散された水性塗料組成物から得られる硬化塗膜は、ブツの発生やざらつきが抑えられて優れた成膜性及び基材への付着性を有し、また、良好な平滑性、即ち、外観性を有する。例えば、乾燥膜厚5μm以下でも素地を十分に覆い隠すことができる薄膜の形成が可能である。また、この水性塗料組成物を基材に塗布し、乾燥させて得られる硬化塗膜では、ラジエータ等に対しバインダーで触媒を担持した従来のものと比較して、基材に対する付着性、密着性の向上が可能である。更に、従来は、ラジエータ等の基材表面に対しバインダーで触媒を担持するものであるから、基材表面に埃や垢等の異物が付着しやすく、それによって、触媒や活性炭のオゾン分解能の劣化が生じやすかった。しかし、本実施の形態の水性塗料組成物からなる塗膜においては、埃や垢等の異物が付着し難く、そして、腐食も生じ難いものとなる。よって、長期の使用による触媒及び活性炭の劣化や脱落が生じ難くて、耐久性が高く、長期に亘って持続的に高いオゾン分解性を発揮できる。
更に、このようにポリアクリレート系分散剤を配合した水性塗料組成物は、酸化マンガン系触媒及び活性炭の分散安定性も良く、例えば、1カ月間保管後も凝集による沈殿分離が生じ難く、保存安定性が高いものである。
こうして、本実施の形態の水性塗料組成物は、車両の走行により空気が接触して流れる車両部品に対してその表面を水性塗料組成物からなる塗膜で覆う表面処理(塗装)によりオゾン分解性能(大気浄化性能)を付与するものである。特に、本実施の形態の水性塗料組成物は、酸化マンガン系触媒及び活性炭を細かく分散させて塗料化したものであり、車両の部品に塗装する塗料であるから、車両の広範囲に亘って適用可能であり、車両全体として大気中の高いオゾン分解効果を期待できる。
本実施の形態に係る水性塗料組成物の実施例の配合組成を表1に示す。
なお、表1において、活性炭は固形分換算量であり、分散工程における水は、溶媒として添加したイオン交換水に加え、活性炭材料の商品に予め含まれていた溶媒としての水分量を含めた値である。
このときのビーズミルは、メディアとして1.5mmジルコン(ジルコニアビーズミル)を用い、回転数1500rpm×90分の条件で混合材料を分散した。
これにより、実施例1乃至実施例3では、分散後の混合材料中の粒子(活性炭及び二酸化マンガン系触媒)の粒度は、JISK 5600及びJISK 5400(1990)に準拠したグラインドケージによる線状法の測定で最大粒子径(Dmax)が20μm以下となった。また、レーザー回折式粒度分布測定装置を用いたレーザー解析法による測定で、体積基準の90%の累積粒子径(D90)が10μm以下となった。
次に、中和された混合物に対し、表1の配合にしたがって、水性樹脂としてのポリプロピレン樹脂(固形分30質量%)またはアクリル樹脂(固形分40質量%)を混合し、更に、添加剤(粘度調整剤、増粘助剤)を混合して、ディスパーで5分〜10分間攪拌することにより材料を混合分散させる塗料化工程を実施した。
以上の工程により、実施例1乃至実施例3に係る水性塗料組成物を得た。
比較例1は、分散剤を使用しない組成物の例である。
また、比較例2は、実施例で用いたポリアクリレート系分散剤に代えて、分散剤としてポリカルボン酸アンモニウム塩(アニオン)を使用した例である。
比較例3及び比較例6は、実施例で用いたポリアクリレート系分散剤に代えて、分散剤としてポリカルボン酸ナトリウム塩(アニオン)を使用した例である。
比較例4は、実施例で用いたポリアクリレート系分散剤に代えて、分散剤として燐酸エステルを使用した例である。
比較例5は、実施例で用いたポリアクリレート系分散剤に代えて、分散剤としてポリウレタンを使用した例である。なお、これら比較例に係る組成物においても、上記実施例と同じ手順で作製した。
貯蔵安定性については、作製した組成物を20℃の温度条件で1カ月間保管し、1カ月後の凝集の有無を確認した。20℃で1カ月間保管しても、凝集が生じなかったものは○とし、凝集によって沈降分離が生じたものは×とした。
そして、この試験体tを入れたパイプ10内にオゾンを含む空気(初期オゾン濃度;4.0ppm(体積基準)、温度;25℃)を風速1.0m/sで供給して流通させ、オゾンセンサー31で硬化塗膜1付きのPP材20、即ち、試験体tを通過する前のオゾン濃度を測定し、また、オゾンセンサー32で試験体t付近のオゾン濃度を測定した。なお、このときのオゾンセンサー32と硬化塗膜1との間隔距離xは2mmとした。また、このときの評価試験は、約25℃の室温(常温)下で行った。オゾンセンサー31で測定したオゾン濃度b1及びオゾンセンサー32で測定したオゾン濃度b2から硬化塗膜1によるオゾン分解率(=b2/b1×100)(%)を算出した。このときのオゾン分解除去率が24%以上であった場合を○とし、18%以上、24%未満であった場合を△とし、18%未満であった場合を×とした。
また、実施例1乃至実施例3に係る水性塗料組成物においては、二酸化マンガン系触媒及び活性炭が高分散されて粒度が細かいことで、実施例1乃至実施例3に係る水性塗料組成物から形成された硬化塗膜には、ブツやざらつきが少なく、その硬化塗膜は、PP製の基材にコーティングした乾燥膜厚が約5μmの薄膜で素地を十分に覆い隠すことができる優れた成膜性を有し、そして、オゾン分解性能にも優れるものであった。
また、分散剤としてポリカルボン酸アンモニウム塩を用いた比較例2においても、活性炭と二酸化マンガン系触媒が分散されずに凝集ゲル化し、塗料化することができなかった。
これに対し、本実施例においては、ポリアクリレート系分散剤の使用によって、活性炭と二酸化マンガン系触媒が細かく分散されたことで、形成された硬化塗膜にブツやざらつきが少なく、成膜性及び外観性も良好であり、水性樹脂としてポリプロピレン樹脂及びアクリル樹脂を用いた実施例1乃至実施例3では金属製の基材に対し、後述する付着性試験を行った際でも、剥離した枡目の個数が2個以下であり、金属製の基材に対し高い付着性、接着性を得ることができた。特に、水性樹脂としてポリプロピレン樹脂を用いた実施例2及び実施例3では、金属製の基材のみならず、樹脂製の基材に対しても、後述する付着性試験で、剥離した枡目の個数が2個以下であり、樹脂製の基材に対しても高い付着性、接着性を得ることができた。よって、水性樹脂としてポリプロピレン樹脂を用いた場合では、金属製及び樹脂製の基材に対して、塗膜の高い付着性を確保できる。そして、塗膜の付着に特別な処理設備を必要としないことで、低コスト化が可能である。一方、水性樹脂としてアクリル樹脂を用いたものでは、金属製の基材に対する接着性、付着性が良好であるが、樹脂製の基材に対して塗膜の高い付着性を確保するためには、基材に対し前処理を施したのち塗装を行うのが好ましい。
即ち、表1に示した実施例2の配合組成のうち、ポリアクリレート系分散剤の配合量(g)のみを変化させ、ポリアクリレート系分散剤以外の配合材料は全て実施例2と同じに統一し、ポリアクリレート系分散剤の濃度が異なる各種水性塗料組成物を作製した。
ここでも上記表1のときと同じ材料を使用し、同じ手順で作製した。
そして、ポリアクリレート系分散剤の濃度を変化させた水性塗料組成物についても、上記表1のときと同様、貯蔵安定性の試験評価及びオゾン分解性の試験評価(図1)を行った。
更に、本発明者らの鋭意実験研究により、二酸化マンガン系触媒と活性炭(固形分)の合計量100質量部に対し、ポリアクリレート系分散剤の配合量が、1.5質量部以上、より好ましくは、2質量部以上、更に好ましくは、2.5質量部以上であれば、貯蔵安定性を確保でき、75質量部以下、より好ましくは、60質量部以下、更に好ましくは、50質量部以下であれば、高いオゾン分解性が得られ、塗膜の成膜性、付着性及び外観性も良好であることを確認している。
まず、オゾン分解能を有する活性炭と二酸化マンガン系触媒の配合割合(比率)による水性塗料組成物及びそれから形成される塗膜性能への影響を調べるため、以下の表3に示すように、活性炭と二酸化マンガンの配合割合(比率)を変化させて各種塗料組成物を作製した。ここでも上記表1のときと同じ材料を使用し、同じ手順で作製した。また、作製した塗料組成物について、貯蔵安定性とオゾン分解性の試験を行った。
一方、オゾン分解性の試験については、図2に示したように行った。即ち、20Lのマイラーバック50内に評価用としてポリプロピレンTP基材20(PP材20)(5cm×7cm)に水性塗料組成物を塗付し乾燥(100℃×10分)させてなる試験体tを入れ、更に、バック50内にエアブローで空気を封入後、オゾン発生機で発生させたオゾンを注入して、バック50内のオゾン濃度を0.2ppm(体積基準)に調整してから、バックをヒートシールで密閉した。そして、30分経過後にオゾンセンサー33によってバック50内のオゾン濃度を測定することにより、初期のオゾン濃度との比較で、オゾン分解率を算出した。なお、このときの評価試験は、25℃の室温(常温)下で行い、また、各種塗料組成物は、PP材20に対し、その素地が覆い隠れるまでに塗布を行っている。
作製した各種塗料組成物の配合組成を表3の上段に示し、評価試験の結果を表3の下段に示す。なお、表3においても、活性炭は固形分換算量であり、分散工程における水は、溶媒として添加したイオン交換水に加え、活性炭材料の商品に予め含まれていた溶媒としての水分量を含めた値である。
本発明者らの鋭意実験研究によれば、実施例4乃至実施例8として表3に示したように、好ましくは、水性塗料組成物中における活性炭(固形分)と二酸化マンガン系触媒の比率を、20/80≦活性炭/二酸化マンガン系触媒≦80/20とすることで、良好なオゾン分解率を得ることができ、かつ、実用的な貯蔵安定性を確保できる。特に、実施例5乃至実施例7に示したように、より好ましくは、活性炭(固形分)と二酸化マンガン系触媒の比率を、30/70≦活性炭/二酸化マンガン系触媒≦70/30とすることで、優れたオゾン分解率と貯蔵安定性が得られ、長期間の極めて高いオゾン分解性と塗料安定性を確保することができる。なお、水性塗料組成物中における活性炭(固形分)と二酸化マンガン系触媒の比率は、その水性塗料組成物から形成される塗膜成分中の活性炭と二酸化マンガン系触媒の比率に一致する。即ち、水性塗料組成物中における活性炭(固形分)と二酸化マンガン系触媒の比率が、20/80≦活性炭/二酸化マンガン系触媒≦80/20であると、水性塗料組成物から得られる硬化塗膜中においても、活性炭と二酸化マンガン系触媒が、20/80≦活性炭/二酸化マンガン系触媒≦80/20の比率で含まれることになる。
そして、作製した塗料組成物について、オゾン分解性及び基材に対する付着性の試験を行った。
また、付着性試験については、PP基材に水性塗料組成物をエアースプレー塗装し、乾燥(100℃×10分)させることにより、PP材上に硬化塗膜が形成された供試体を用いた。そして、かかる供試体について、JIS−K5600−5−6:1999に準拠して、付着性(クロスカット法)の評価を行った。具体的には、供試体の塗装面にカッターナイフで縦横に1mm間隔で11本ずつの平行な切れ目を入れて、合計100個の1mm×1mmの桝目を形成し、これら100個の桝目形成部分に上から粘着テープ(マスキングテープ)を強く圧着させて貼り付け、そして一気に引き剥がし、100個の升目のうち何個剥がれたかを測定した。剥離した枡目の個数が2個以下であれば合格(○)とし、3個以上の剥がれが見られた場合には△と評価した。
作製した各種塗料組成物中の活性炭及び二酸化マンガン系触媒の濃度を表4の上段に示し、評価試験の結果を表4の下段に示す。
一方で、活性炭と二酸化マンガン系触媒の濃度が高くなり過ぎると、付着性能が低下した。基材への付着性能が低いと、塗膜剥がれや塗膜成分の脱落が生じやすくなり、持続的に高いオゾン分解性能を得ることができなくなる恐れがある。
よって、塗膜成分中の活性炭(固形分)及び二酸化マンガン系触媒濃度は、好ましくは、60%以上、90%以下であり、より好ましくは、70%以上、80%以下であれば、基材への付着性を確保して長時間の高いオゾン分解性能を維持できる。
なお、水性塗料組成物から形成された塗膜成分中における活性炭及び二酸化マンガンの濃度(質量%)は、活性炭及び二酸化マンガンの合計固形分量/塗膜成分となる水性塗料組成物中の全体の固形分量×100で算出したものである。
更に、活性炭としては、その中位径(平均粒子径)が1〜20μmの範囲内にあり、BET比表面積が500〜3000m2/gの範囲内にある活性炭を用いるのが好ましい。中位径(平均粒子径)が1〜20μmの範囲内にあり、BET比表面積が500〜3000m2/gの範囲内にある活性炭によれば、組成物の分散性及び分散安定性が高く、オゾン分解性が高い塗膜が得られる。
更に、このポリアクリレート系分散剤は、二酸化マンガン系触媒及び活性炭の合計量を100質量部に対し、1.5質量部〜70質量部の範囲内で配合されるのが好ましい。これにより、高いオゾン分解性と貯蔵安定性を両立できる。また、好ましくは、水性塗料組成物中に、ポリアクリレート系分散剤を0.3質量%〜5質量%の範囲内で含有されることにより、高いオゾン分解性と貯蔵安定性を両立できる。
これによって、活性炭等の凝集体が少なくて成膜性及び付着性の高い塗膜を形成でき、そして、二酸化マンガン系触媒及び活性炭によるオゾン吸着量を高くできることで、高いオゾン分解性が得られ、更に、分散安定性も高くて貯蔵安定性にも優れる。故に、安定した塗膜性能及び塗料組成物の長期の保存性を得ることができる。
即ち、分散工程では、ビーズミルまたはロールミルで、二酸化マンガン系触媒及び活性炭の粒子径が、レーザー解析法による体積基準の90%の累積粒子径(D90)で10μm以下になるまで分散される。
このような粒子サイズに分散された水性塗料組成物によれば、粗粒が少ないことで、塗膜ブツやざらつきが少なく、塗膜の外観性や付着性に優れる。また、凝集体が少ないから、二酸化マンガン系触媒及び活性炭によるオゾン吸着量を高くできることで、高いオゾン分解性が得られ、更に、分散安定性も高くて貯蔵安定性にも優れる。故に、塗膜の外観性に優れ、また、オゾン分解性及び貯蔵安定性が高いものである。
また、酸化マンガン系触媒及び活性炭は、水性塗料組成物から形成される塗膜成分中に酸化マンガン系触媒及び活性炭の合計量が60質量%〜90質量%の範囲内となるように配合されるのが好ましい。これにより、基材に対する塗膜の付着性を損なうことなく、高いオゾン分解性能を得ることができる。
そして、この試験体tを入れたパイプ10内にオゾンを含む空気(初期オゾン濃度;4.0ppm(体積基準)、温度;25℃)を風速1.0m/sで供給して流通させ、オゾンセンサー31で硬化塗膜1付きのPP材20、即ち、試験体tを通過する前のオゾン濃度を測定し、また、オゾンセンサー32で試験体t付近のオゾン濃度を測定した。なお、このときのオゾンセンサー32と硬化塗膜1との間隔距離xは2mmとした。また、このときの評価試験は、約25℃の室温(常温)下で行った。オゾンセンサー31で測定したオゾン濃度b1及びオゾンセンサー32で測定したオゾン濃度b2から硬化塗膜1によるオゾン分解率(={(b1−b2)/b1}×100)(%)を算出した。このときのオゾン分解除去率が24%以上であった場合を○とし、18%以上、24%未満であった場合を△とし、18%未満であった場合を×とした。
更に、このポリアクリレート系分散剤は、二酸化マンガン系触媒及び活性炭の合計量を100質量部に対し、1.5質量部〜70質量部の範囲内で配合されるのが好ましい。これにより、高いオゾン分解性と貯蔵安定性を両立できる。また、好ましくは、水性塗料組成物中に、ポリアクリレート系分散剤を0.3質量%〜5質量%の範囲内で含有されることにより、高いオゾン分解性と貯蔵安定性を両立できる。
Claims (12)
- 水を溶媒の主成分とする水性塗料組成物であって、
酸化マンガン系触媒と、活性炭と、ポリアクリレート系分散剤と、水性樹脂と、pH調整剤とを含むことを特徴とする水性塗料組成物。 - 前記酸化マンガン系触媒は、二酸化マンガン系触媒であることを特徴とする請求項1に記載の水性塗料組成物。
- 前記酸化マンガン系触媒と前記活性炭の配合比率は、20/80≦酸化マンガン系触媒/活性炭≦80/20であることを特徴とする請求項1または請求項2に記載の水性塗料組成物。
- 前記酸化マンガン系触媒及び前記活性炭は、前記水性塗料組成物から形成される塗膜成分中に前記酸化マンガン系触媒及び前記活性炭の合計量が60質量%〜90質量%の範囲内となるように配合されたことを特徴とする請求項1乃至請求項3の何れか1つに記載の水性塗料組成物。
- 前記ポリアクリレート系分散剤は、重量平均分子量が500〜30000の範囲内であり、酸価が1〜50の範囲内であり、水素イオン指数がpH4〜pH9の範囲内であるものを用いたことを特徴とする請求項1乃至請求項4の何れか1つに記載の水性塗料組成物。
- 前記ポリアクリレート系分散剤は、前記酸化マンガン系触媒及び前記活性炭の合計量を100質量部に対し、1.5質量部〜75質量部の範囲内で配合されることを特徴とする請求項1乃至請求項5の何れか1つに記載の水性塗料組成物。
- 前記酸化マンガン系触媒及び前記活性炭は、グラインドゲージにより測定された分散性が、最大粒子径(Dmax)20μm以下であることを特徴とする請求項1乃至請求項6の何れか1つに記載の水性塗料組成物。
- 前記酸化マンガン系触媒及び前記活性炭は、レーザー解析法による体積基準の90%の累積粒子径(D90)が、10μm以下であることを特徴とする請求項1乃至請求項7の何れか1つに記載の水性塗料組成物。
- 前記水性樹脂は、アクリル樹脂またはポリプロピレン樹脂であることを特徴とする請求項1乃至請求項8の何れか1つに記載の水性塗料組成物。
- 水を主成分とする溶媒と、酸化マンガン系触媒と、活性炭と、ポリアクリレート系分散剤とを混合し、分散する分散工程と、
前記分散された混合物にpH調整剤を混合する中和工程と、
前記中和された混合物に水性樹脂を混合する塗料化工程と
を具備することを特徴とする水性塗料組成物の製造方法。 - 前記分散工程では、ビーズミルまたはロールミルで、前記酸化マンガン系触媒及び前記活性炭の粒子径が、グラインドゲージによる測定で最大粒子径(Dmax)20μm以下になるまで分散されることを特徴とする請求項10に記載の水性塗料組成物の製造方法。
- 前記分散工程では、ビーズミルまたはロールミルで、前記酸化マンガン系触媒及び前記活性炭の粒子径が、レーザー解析法による体積基準の90%の累積粒子径(D90)で10μm以下になるまで分散されることを特徴とする請求項10または請求項11に記載の水性塗料組成物の製造方法。