JP2020132901A - 塊成物の製造方法および塊成物 - Google Patents
塊成物の製造方法および塊成物 Download PDFInfo
- Publication number
- JP2020132901A JP2020132901A JP2019023680A JP2019023680A JP2020132901A JP 2020132901 A JP2020132901 A JP 2020132901A JP 2019023680 A JP2019023680 A JP 2019023680A JP 2019023680 A JP2019023680 A JP 2019023680A JP 2020132901 A JP2020132901 A JP 2020132901A
- Authority
- JP
- Japan
- Prior art keywords
- starch
- binder
- raw material
- group
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の一実施形態に係る塊成物の製造方法は、鉄含有物を原料として用い、前記原料(鉄含有原料)とバインダーとを混合する工程により混合物を調整した後、前記混合物をペレットまたはブリケットに加工して塊成物とする。なお、前記混合物にはさらに、水などを混合してもよい。当該塊成物は、製銑工程および製鋼工程等において用いられてよい。
本実施形態に係る澱粉としては、エーテル化澱粉または非エステル化澱粉であることが好ましく、エーテル化澱粉かつ非エステル化澱粉である澱粉(以下、「エーテル化/非エステル化澱粉」と称する)がより好ましい。言い換えれば、前記化工澱粉としては、エーテル化澱粉および非エステル化澱粉からなる群より選ばれる少なくとも一つである澱粉が好ましい。
原料として、製鉄プロセスで発生する鉄含有副産物である原料Xおよび原料Yを用いて、塊成物(以下、「サンプル」と称することがある)の製造を行った。以下の表1に、原料Xおよび原料Yの化学成分組成を示す。
α澱粉A、α澱粉B、およびα澱粉Cをバインダーとして使用した場合、α澱粉Cのみが原料が高pHである影響を顕著に受けたため、その原因を検討した。
ここで、α澱粉A、α澱粉B、およびα澱粉Cはα化される前の化学処理方法が異なることから、それぞれ付加されている官能基が異なると考えられる。それぞれのα澱粉に付加されている官能基の違いが、高pH条件下における粘度に影響していると仮定し、FT−IR(フーリエ変換赤外分光光度計)による各α澱粉の官能基分析を行った。当該分析の結果について、図5に示す。
次に、滴定法によって各α澱粉のアセチル基、カルボキシル基、およびヒドロキシプロピル基の含有量を測定した。
塊成物の製造において、高pH原料である原料Yが含まれる原料を用いた場合でも、バインダーとしてα澱粉Aおよびα澱粉Bを用いれば、α澱粉Cを用いた場合と比較して、得られたサンプルの圧潰強度は良好であった。これは、α澱粉Aおよびα澱粉Bが非エステル化澱粉であること、非酸化澱粉であること、またはエーテル化澱粉であることに起因していることが、前記のα澱粉A、α澱粉B、およびα澱粉Cの官能基含有量測定結果により示された。
本発明は上述した各実施形態に限定されるものではなく、請求項に示した範囲で種々の変更が可能であり、異なる実施形態にそれぞれ開示された技術的手段を適宜組み合わせて得られる実施形態についても本発明の技術的範囲に含まれる。
Claims (6)
- 鉄含有原料とバインダーとを混合する工程を含む、塊成物の製造方法であって、
前記鉄含有原料として、pHが10以上のものを用い、
エーテル化澱粉および非エステル化澱粉からなる群より選ばれる少なくとも一つを前記バインダーとして選択する、塊成物の製造方法。 - 炭素数1以上10以下のヒドロキシアルキル基を有する前記エーテル化澱粉を含んだ前記バインダーを選択する、請求項1に記載の塊成物の製造方法。
- 前記ヒドロキシアルキル基の含有量が乾燥物換算で1重量%以上である前記エーテル化澱粉を含んだ前記バインダーを選択する、請求項2に記載の塊成物の製造方法。
- アセチル基およびカルボキシル基の含有量がいずれも乾燥物換算で0.1重量%以下である前記非エステル化澱粉を含んだ前記バインダーを選択する、請求項1から3の何れか1項に記載の塊成物の製造方法。
- 前記非エステル化澱粉および前記エーテル化澱粉は、α化されている、請求項1から4の何れか1項に記載の塊成物の製造方法。
- 鉄含有原料とバインダーとを有する塊成物であって、
前記鉄含有原料は、pHが10以上のものであり、
前記バインダーは、非エステル化澱粉およびエーテル化澱粉からなる群より選ばれる少なくとも一つである、塊成物。