JP2020066680A - ポリシロキサン粒子、体質顔料、充填材、および、ポリシロキサン粒子の製造方法 - Google Patents
ポリシロキサン粒子、体質顔料、充填材、および、ポリシロキサン粒子の製造方法 Download PDFInfo
- Publication number
- JP2020066680A JP2020066680A JP2018200435A JP2018200435A JP2020066680A JP 2020066680 A JP2020066680 A JP 2020066680A JP 2018200435 A JP2018200435 A JP 2018200435A JP 2018200435 A JP2018200435 A JP 2018200435A JP 2020066680 A JP2020066680 A JP 2020066680A
- Authority
- JP
- Japan
- Prior art keywords
- polysiloxane particles
- oil
- polysiloxane
- basic compound
- soluble basic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
エマルゲンA−500:ポリオキシエチレンジスチレン化フェニルエーテル、花王社製
KF−6204:エーテル変性シリコーンオイル、信越化学
TEOS:テトラエトキシシラン、富士フィルム和光純薬工業社製
MTMS:メチルトリメトキシシラン、TCI−GR、TCI製
1.ポリシロキサン粒子の製造
実施例1
(第1工程)
脱イオン水14.9gに、エマルゲンA−500 1.7gおよびKF−6204 1.4gを配合し、その後、撹拌し、界面活性剤水溶液を調製した。
脱イオン水75.00gおよび酢酸0.3gを、撹拌混合して、酸性水溶液を調製した。
DMLA内包ポリシロキサン粒子を含む水分散液を、回転数15000rpm、30分の条件で遠心分離し、その後、上澄み液を取り除いて固液分離した。
その後、沈殿物を、40℃で24時間乾燥し、これにより、乾燥物(DMLA内包ポリシロキサン粒子)を得た。
配合処方を、表1の記載に従って変更した以外は、実施例1と同様に処理して、ポリシロキサン粒子を得た。
2.評価
以下の項目を評価した。
各実施例のポリシロキサン粒子を含む水分散液について、粒粒度分布計(LA−920、堀場製作所株式会社)を用いるレーザー回折法により、体積基準のメジアン径として、平均一次粒子径を測定した。その結果を表1に示す。
各実施例のポリシロキサン粒子について、BELLSORP−miniII(マイクロトラック・ベル株式会社)を用いるBET法により、比表面積を測定した。その結果を表1に示す。
各実施例のポリシロキサン粒子について、BET法によって、細孔容積を測定した。その結果を表1に示す。
各実施例のポリシロキサン粒子について、BET法によって、平均細孔径を測定した。その結果を表1に示す。
実施例2のDMLA内包ポリシロキサン粒子を、ビスフェノール型液状エポキシ樹脂に混合してアミン硬化させた。次いで、これをウルトラミクロトームで切断することにより超薄切片を調製し、透過型電子顕微鏡(JEM−1230、日本電子株式会社)で、粒子断面のTEM観察した。その結果を図3に示す。
実施例2のDMLA内包ポリシロキサン粒子、および、実施例2のポリシロキサン粒子を、走査型電子顕微鏡日立TM−3000(日立ハイテクノロジーズ社製)で、SEM観察した。その結果を、図4および図5に示す。
3.考察
化粧品原料における体質顔料や電子部品材料における液状ポリマー用充填材などに用いられる多孔質フィラーの一例として、サンスフェアH−31(シリカ、AGCエスアイテック株式会社社製)を、比較例1として、表1に併記した。
4 ポリシロキサン粒子
Claims (7)
- 平均一次粒子径が、0.1μm以上50μm以下であり、
BET比表面積が、300m2/g以上であり、
平均細孔径が、5nm以下であることを特徴とする、ポリシロキサン粒子。 - 請求項1に記載のポリシロキサン粒子からなることを特徴とする、体質顔料。
- 請求項1に記載のポリシロキサン粒子からなることを特徴とする、充填材。
- 水に、油溶性の塩基性化合物を配合し、前記油溶性の塩基性化合物の液滴を含む水分散液を調製する第1工程と、
前記水分散液およびシラン原料を配合し、前記シラン原料を脱水縮合反応させてポリシロキサン化合物を生成することにより、前記油溶性の塩基性化合物を前記ポリシロキサン化合物に分散させた油溶性の塩基性化合物内包ポリシロキサン粒子を得る第2工程と、
前記油溶性の塩基性化合物内包ポリシロキサン粒子から、前記油溶性の塩基性化合物を除去し、ポリシロキサン粒子を得る第3工程とを備えることを特徴とする、ポリシロキサン粒子の製造方法。 - 油溶性の塩基性化合物が、油溶性の3級アミン化合物であることを特徴とする、請求項4に記載のポリシロキサン粒子の製造方法。
- 前記第1工程において、水に、界面活性剤を配合することを特徴とする、請求項4または5に記載のポリシロキサン粒子の製造方法。
- 前記界面活性剤が、ノニオン性界面活性剤であることを特徴とする、請求項6に記載のポリシロキサン粒子の製造方法。