JP2020050823A - ゴム組成物、及びそれを用いた空気入りタイヤ、並びにゴム組成物の製造方法 - Google Patents
ゴム組成物、及びそれを用いた空気入りタイヤ、並びにゴム組成物の製造方法 Download PDFInfo
- Publication number
- JP2020050823A JP2020050823A JP2018183902A JP2018183902A JP2020050823A JP 2020050823 A JP2020050823 A JP 2020050823A JP 2018183902 A JP2018183902 A JP 2018183902A JP 2018183902 A JP2018183902 A JP 2018183902A JP 2020050823 A JP2020050823 A JP 2020050823A
- Authority
- JP
- Japan
- Prior art keywords
- cyclodextrin
- mass
- rubber
- molecule
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
・SBR2:JSR(株)製「HPR350」
・カーボンブラック:東海カーボン(株)製「シースト9」
・シリカ:エボニック・ジャパン(株)製「Ultrasil VN3」
・シランカップリング剤:エボニック・ジャパン(株)製「Si75」
・オイル:JXTGエネルギー(株)製「プロセスP200」
・酸化亜鉛:三井金属鉱業(株)製「酸化亜鉛2種」
・ステアリン酸:花王(株)製「ルナックS−20」
・老化防止剤:大内新興化学工業(株)製「ノクラック6C」
・ワックス:日本精蝋(株)製「OZOACE0355」
・化合物1:アドバンスト・ソフトマテリアルズ(株)製「SH2400B−0501」(直鎖状分子:ポリエチレングリコール、環状分子:カプロラクトンによる修飾基を有するシクロデキストリン、封鎖基:アダマンタン基、表面がシリカで被覆されている)、平均粒子径=7.4μm、真比重(He置換法)=1.18g/cc、シリカ含有割合=2%
・化合物2:アドバンスト・ソフトマテリアルズ(株)製「SH2400B−2001」(直鎖状分子:ポリエチレングリコール、環状分子:カプロラクトンによる修飾基を有するシクロデキストリン、封鎖基:アダマンタン基、表面がシリカで被覆されている)、平均粒子径=20μm、真比重(He置換法)=1.16g/cc、シリカ含有割合=2%
・化合物3:アドバンスト・ソフトマテリアルズ(株)製「SH3400P」(直鎖状分子:ポリエチレングリコール、環状分子:カプロラクトンによる修飾基を有するシクロデキストリン、封鎖基:アダマンタン基、表面がシリカで被覆されていない)
・硫黄:鶴見化学工業(株)製「粉末硫黄」
・加硫促進剤:住友化学(株)製「ソクシノールCZ」
Claims (7)
- ジエン系ゴムと、
直鎖状分子と、前記直鎖状分子を包接する環状分子と、前記直鎖状分子から前記環状分子が脱離しないように、前記直鎖状分子の両末端に配置された封鎖基とを有するロタキサンを、シリカで被覆した微粒子とを含有し、
前記微粒子の含有量が、ジエン系ゴム100質量部に対して1〜50質量部である、ゴム組成物。 - ジエン系ゴムと、
直鎖状分子と、前記直鎖状分子を包接する環状分子と、前記直鎖状分子から前記環状分子が脱離しないように、前記直鎖状分子の両末端に配置された封鎖基とを有するロタキサンを、シリカで被覆した微粒子とを含有し、
前記ロタキサンの含有量が、前記ジエン系ゴム100質量部に対して、0.98〜49質量部である、ゴム組成物。 - 前記ロタキサンが、前記環状分子にカプロラクトンによる修飾基を有する、請求項1又は2に記載のゴム組成物。
- 前記微粒子の平均粒子径が1〜50μmである、請求項1〜3のいずれか1項に記載のゴム組成物。
- 前記微粒子と補強性充填剤として配合したシリカとの合計量100質量部に対して、シランカップリング剤0.5〜20質量部含有する、請求項1〜4のいずれか1項に記載のゴム組成物。
- 請求項1〜5のいずれか1項に記載のゴム組成物を、トレッドに用いた空気入りタイヤ。
- ジエン系ゴム100質量部に対して、
直鎖状分子と、前記直鎖状分子を包接する環状分子と、前記直鎖状分子から前記環状分子が脱離しないように、前記直鎖状分子の両末端に配置された封鎖基とを有するロタキサンを、シリカで被覆した微粒子を1〜50質量部配合する工程を有する、ゴム組成物の製造方法。