JP2017523112A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2017523112A5 JP2017523112A5 JP2017501325A JP2017501325A JP2017523112A5 JP 2017523112 A5 JP2017523112 A5 JP 2017523112A5 JP 2017501325 A JP2017501325 A JP 2017501325A JP 2017501325 A JP2017501325 A JP 2017501325A JP 2017523112 A5 JP2017523112 A5 JP 2017523112A5
- Authority
- JP
- Japan
- Prior art keywords
- roll
- particles
- sic
- coating
- sialon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000002245 particle Substances 0.000 claims 9
- 239000000203 mixture Substances 0.000 claims 6
- 239000011248 coating agent Substances 0.000 claims 5
- 238000000576 coating method Methods 0.000 claims 5
- 229910003465 moissanite Inorganic materials 0.000 claims 5
- 229910010271 silicon carbide Inorganic materials 0.000 claims 5
- 238000000034 method Methods 0.000 claims 4
- GEIAQOFPUVMAGM-UHFFFAOYSA-N oxozirconium Chemical compound [Zr]=O GEIAQOFPUVMAGM-UHFFFAOYSA-N 0.000 claims 4
- 229910003564 SiAlON Inorganic materials 0.000 claims 3
- 229910000831 Steel Inorganic materials 0.000 claims 3
- 239000010959 steel Substances 0.000 claims 3
- PNEYBMLMFCGWSK-UHFFFAOYSA-N AI2O3 Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 claims 2
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 2
- 229910020203 CeO Inorganic materials 0.000 claims 2
- 229910004298 SiO 2 Inorganic materials 0.000 claims 2
- 238000007598 dipping method Methods 0.000 claims 2
- 239000005350 fused silica glass Substances 0.000 claims 2
- 239000011159 matrix material Substances 0.000 claims 2
- 229910052751 metal Inorganic materials 0.000 claims 2
- 239000002184 metal Substances 0.000 claims 2
- 229910052863 mullite Inorganic materials 0.000 claims 2
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 2
- 229910052851 sillimanite Inorganic materials 0.000 claims 2
- 239000004593 Epoxy Substances 0.000 claims 1
- 239000004372 Polyvinyl alcohol Substances 0.000 claims 1
- OGIDPMRJRNCKJF-UHFFFAOYSA-N TiO Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 claims 1
- 229910052782 aluminium Inorganic materials 0.000 claims 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminum Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims 1
- 239000011230 binding agent Substances 0.000 claims 1
- 238000001035 drying Methods 0.000 claims 1
- 125000003700 epoxy group Chemical group 0.000 claims 1
- 238000010438 heat treatment Methods 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 150000002739 metals Chemical class 0.000 claims 1
- 238000007750 plasma spraying Methods 0.000 claims 1
- 229920000058 polyacrylate Polymers 0.000 claims 1
- 229920000642 polymer Polymers 0.000 claims 1
- 229920002451 polyvinyl alcohol Polymers 0.000 claims 1
- 238000005507 spraying Methods 0.000 claims 1
Claims (12)
- 800℃で3時間後に摩耗性である、少なくとも1つのコーティングの層を有するロールであって、前記コーティングは、
a)83〜98重量%のSi3N4、SiC又はSiAlONの粒子若しくはこれらの混合物からなる凝集体、
b)100nmを超えかつ1000nmより小さい平均粒径を有する、2〜17重量%のAl2O3、SiO2、ZrO2、CeO2、Y2O3のサブミクロン粒子又はこれらの混合物、を含む、ロール。 - 前記凝集体はAl2TiO5の粒子を更に含む、請求項1に記載のロール。
- 前記粒子の凝集体の比表面積(BET)は、8m2/g以下であり、好ましくは0.5〜5m2/gである、請求項1又は2に記載のロール。
- 前記粒子の凝集体は、異なる比表面積を有する粒子を含む、請求項1〜3のいずれか一項に記載のロール。
- 前記コーティングは、請求項1に記載される複数の層から作製される、請求項1〜4のいずれか一項に記載のロール。
- 前記コーティングの平均厚さは少なくとも150μmである、請求項1〜5のいずれか一項に記載のロール。
- 前記ロールは、溶融シリカ、ムライト、シリマナイト、アルミナ、SiCマトリクス又は耐火鋼などの金属から作製される、請求項1〜6のいずれか一項に記載のロール。
- 前記コーティングは、アクリルポリマー、エポキシポリマー又はポリビニルアルコールなどの一時的なバインダーを含む、請求項1〜7のいずれか一項に記載のロール。
- a)溶融シリカ、ムライト、シリマナイト、アルミナ、SiCマトリクス又はコア及び表面を有する耐火鋼などの金属から作製されるロールを提供する工程、
b)前記ロールの表面の少なくとも一部分に、
50〜75重量%のSi 3 N 4 、SiC又はSiAlONの粒子若しくはこれらの混合物を含む凝集体と、
1.5〜10重量%、好ましくは1.5〜5重量%のAl 2 O 3 又はSiO 2 、ZrO 2 、CeO 2 、Y 2 O 3 のサブミクロン粒子又はこれらの混合物と、
15〜48.5重量%のH 2 O、を含み、
前記Si 3 N 4 、SiC又はSiAlONの粒子は、8m 2 /g以下、好ましくは0.5〜5m 2 /gの比表面積(BET)を有する組成物を塗布する工程、
c)前記ロールを乾燥する工程、を含む、請求項1〜8のいずれか一項に記載のロールを製造する、プロセス。 - 前記組成物は、噴霧、浸漬、水浸又はプラズマ噴霧することによってコーティングされる、請求項9に記載のプロセス。
- 少なくとも800℃の温度で少なくとも3時間、前記ロールを加熱する工程を更に含む、請求項9に記載のプロセス。
- アルミニウムで処理された鋼シートを移送するための、請求項1〜8のいずれか一項に記載のロールの使用。