JP2015131543A - 空気入りタイヤ - Google Patents
空気入りタイヤ Download PDFInfo
- Publication number
- JP2015131543A JP2015131543A JP2014003485A JP2014003485A JP2015131543A JP 2015131543 A JP2015131543 A JP 2015131543A JP 2014003485 A JP2014003485 A JP 2014003485A JP 2014003485 A JP2014003485 A JP 2014003485A JP 2015131543 A JP2015131543 A JP 2015131543A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- mass
- tire
- pneumatic tire
- foamed rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
天然ゴム(NR):RSS#3 40質量部
ブタジエンゴム(BR):日本ゼオン(株)製のNipol BR1220
60質量部
カーボンブラック:三菱化学(株)製のシーストN550(窒素吸着比表面積:43m2/g) 60質量部
酸化亜鉛:三井金属鉱業(株)製の亜鉛華1号 5質量部
ステアリン酸:日本油脂(株)製のステアリン酸「椿」 5質量部
オイル:(株)ジャパンエナジー製のプロセスX−140 10質量部
老化防止剤:住友化学(株)製のアンチゲン6C(N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン) 3質量部
ワックス:大内新興化学工業(株)製のサンノックN 10質量部
硫黄:軽井沢硫黄(株)製の粉末硫黄 2質量部
加硫促進剤:大内新興化学工業(株)製のノクセラーCZ(N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミド) 1質量部
発泡剤:永和化成工業(株)製のネオセルボンN#1000SW(4,4’−オキソビスベンゼンスルホニルヒドラジド,平均粒径14μm) 可変
ゴム成分100質量部に対して表1に示す配合量の発泡剤を使用し、1.7Lバンバリーミキサーを用いて、硫黄及び加硫促進剤以外の材料を150℃の条件下で3分間混練りし、混練り物を得た。次に、得られた混練り物に硫黄及び加硫促進剤を添加し、オープンロールを用いて、50℃の条件下で5分間練り込み、未加硫ゴム組成物を得た。
供試タイヤを15x6JJのアルミホイールリムにリム組みし、かつ内圧210kPa(前後同一)を充填して、排気量2000ccの国産FF車の4輪に装着するとともに、テストコース内をドライバー1名乗車で、ロードノイズ計測路(アスファルト粗面路)を速度60km/Hで走行し、そのときの車内騒音を、ドライバーの官能評価により、比較例1を100とする指数で評価した。数値が大きいほど良好である。
供試タイヤを15x6JJのアルミホイールリムにリム組みし、かつ内圧210kPa(前後同一)を充填して、排気量2000ccの国産FF車の4輪に装着するとともに、テストコース内をドライバー1名乗車で走行して官能評価した。比較例1を100とする指数で評価した。数値が大きいほど良好である。
供試タイヤを15x6JJのアルミホイールリムにリム組みし、かつ内圧210kPa(前後同一)を充填して、排気量2000ccの国産FF車の4輪に装着するとともに、テストコース内をドライバー1名で、湿潤アスファルト路面にて、初速度100km/hからの制動距離を測定した。そして、比較例1のウェットグリップ性能指数を100とする指数で評価した。評価は、以下に示す計算式により、各配合のウェット制動性能(ウェットグリップ性能)を、比較例1を100として指数表示した。数値が大きいほどウェット制動性能に優れることを示す。
(ウェット制動性能指数)=(比較例1の制動距離)/(各配合の制動距離)×100
供試タイヤを15x6JJのアルミホイールリムにリム組みし、かつ内圧210kPa(前後同一)を充填して、排気量2000ccの国産FF車の4輪に装着するとともに、半径100mのアスファルト路面に、水深5mm、長さ20mの水たまりを設けたコース上を、速度を段階的に増加させながら進入させ、横加速度(横G)を計測し、50〜80km/hの速度における前輪の平均横Gを算出した(ラテラル・ハイドロプレーニングテスト)。結果は、比較例1を100とする指数で表示し、数値が大きい程良好である。
供試タイヤを15×6JJのアルミホイールリムにリム組みし、かつ内圧210kPa(前後同一)を充填して、排気量2000ccの国産FF車の4輪に装着するとともに、テストコース内をドライバー1名乗車で走行して官能評価した。比較例1を100とする指数で評価した。数値が大きいほど良好である。
Claims (4)