JP2015127417A - 樹脂組成物、樹脂ワニス、プリプレグ、金属張積層板、及びプリント配線板 - Google Patents
樹脂組成物、樹脂ワニス、プリプレグ、金属張積層板、及びプリント配線板 Download PDFInfo
- Publication number
- JP2015127417A JP2015127417A JP2015026057A JP2015026057A JP2015127417A JP 2015127417 A JP2015127417 A JP 2015127417A JP 2015026057 A JP2015026057 A JP 2015026057A JP 2015026057 A JP2015026057 A JP 2015026057A JP 2015127417 A JP2015127417 A JP 2015127417A
- Authority
- JP
- Japan
- Prior art keywords
- polyarylene ether
- resin composition
- ether copolymer
- compound
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】25℃の塩化メチレン中で測定した固有粘度が0.03〜0.12dl/gであって、分子末端にフェノール性水酸基を1分子当たり平均1.5〜3個有するポリアリーレンエーテル共重合体と、ベンゾオキサジン化合物を含む熱硬化性化合物とを含有し、前記ポリアリーレンエーテル共重合体及び前記ベンゾオキサジン化合物の合計含有量が、前記ポリアリーレンエーテル共重合体及び前記熱硬化性化合物の合計100質量部に対して、70〜100質量部であることを特徴とする樹脂組成物を用いる。
【選択図】なし
Description
[樹脂組成物の調製]
本実施例において、樹脂組成物を調製する際に用いる各成分について説明する。ここで、25℃の塩化メチレン中で測定した固有粘度を、固有粘度(IV)を示す。また、トルエンに対する、25℃における溶解度を、トルエン溶解度と示す。また、ポリアリーレンエーテル共重合体の、分子末端のフェノール性水酸基の1分子当たりの平均個数を、末端水酸基数と示す。
PAE 1:ポリアリーレンエーテル共重合体(SABICイノベーティブプラスチックス社製のMX−90、固有粘度(IV)0.085dl/g、末端水酸基数1.9個、数平均分子量Mn1050)
PAE 2:国際公開第2007/067669号に記載の方法で合成したポリアリーレンエーテル共重合体(固有粘度(IV)0.06dl/g、末端水酸基数1.8個、数平均分子量Mn800)
PAE 3:国際公開第2007/067669号に記載の方法で合成したポリアリーレンエーテル共重合体(固有粘度(IV)0.09dl/g、末端水酸基数2.8個、数平均分子量Mn1150)
PAE 4:ポリアリーレンエーテル共重合体(SABICイノベーティブプラスチックス社製のSA−120、固有粘度(IV)0.13dl/g、末端水酸基数0.9個、数平均分子量Mn3200)
PAE 5:国際公開第2007/067669号に記載の方法で合成したポリアリーレンエーテル共重合体(固有粘度(IV)0.15dl/g、末端水酸基数2.5個、数平均分子量Mn5000)
(ベンゾオキサジン化合物)
フェノールフタレイン型ベンゾオキサジン化合物:上記式(1)で表され、R1及びR2は、ともにフェニル基である化合物(ハンツマン社製)
ビスフェノールF型ベンゾオキサジン化合物:上記式(3)で表される化合物(ハンツマン社製)
DDM型ベンゾオキサジン化合物:上記式(4)で表される化合物(四国化成工業株式会社製)
(ベンゾオキサジン化合物以外の熱硬化性化合物)
エポキシ樹脂:クレゾールノボラック型エポキシ樹脂(DIC株式会社製のエピクロンN690、トルエン溶解度80質量%)
フェノール樹脂:DIC株式会社製のTD−2090
[調製方法]
まず、各成分を表1に記載の配合割合で、固形分濃度が60質量%となるように、トルエンに添加し、混合させた。その混合物を、80℃になるまで加熱し、80℃のままで30分間攪拌することによって、ワニス状の樹脂組成物(樹脂ワニス)が得られた。
1GHzにおける評価基板の誘電率及び誘電正接を、IPC−TM650−2.5.5.9に準拠の方法で測定した。具体的には、インピーダンスアナライザ(アジレント・テクノロジー株式会社製のRFインピーダンスアナライザ HP4291B)を用い、1GHzにおける評価基板の誘電率及び誘電正接を測定した。
セイコーインスツルメンツ株式会社製の粘弾性スペクトロメータ「DMS100」を用いて、プリプレグのTgを測定した。このとき、曲げモジュールで周波数を10Hzとして動的粘弾性測定(DMA)を行い、昇温速度5℃/分の条件で室温から280℃まで昇温した際のtanδが極大を示す温度をTgとした。
半田耐熱性は、JIS C 6481に準拠の方法で測定した。具体的には、評価基板を、121℃、2気圧(0.2MPa)、2時間のプレッシャークッカーテスト(PCT)を行い、各サンプルで行い、サンプル数5個で、260℃の半田槽中に20秒間浸漬し、ミーズリングや膨れ等の発生の有無を目視で観察した。ミーズリングや膨れ等の発生が確認できなければ、「○」と評価し、発生が確認できれば、「×」と評価した。また、別途、260℃の半田槽の代わりに、288℃の半田槽を用いて、同様の評価を行った。
JIS C 6481に準拠の方法で、評価基板の、Z軸方向における熱膨張係数を測定した。なお、測定条件は、昇温速度10℃/分、温度範囲は、Tg未満の温度範囲、具体的には、75〜125℃で測定した。
得られた評価基板を目視で評価した。
Claims (10)
- 25℃の塩化メチレン中で測定した固有粘度が0.03〜0.12dl/gであって、分子末端にフェノール性水酸基を1分子当たり平均1.5〜3個有するポリアリーレンエーテル共重合体と、
ベンゾオキサジン化合物を含む熱硬化性化合物とを含有し、
前記ポリアリーレンエーテル共重合体及び前記ベンゾオキサジン化合物の合計含有量が、前記ポリアリーレンエーテル共重合体及び前記熱硬化性化合物の合計100質量部に対して、80〜100質量部であり、
前記ベンゾオキサジン化合物の含有量が、前記樹脂組成物100質量部に対して、20〜60質量部であることを特徴とする樹脂組成物。 - 前記ポリアリーレンエーテル共重合体が、2,6−ジメチルフェノールと2官能フェノール及び3官能フェノールの少なくともいずれか一方とからなる請求項1に記載の樹脂組成物。
- 前記ポリアリーレンエーテル共重合体の含有量が、前記樹脂組成物100質量部に対して、40〜80質量部である請求項1又は請求項2に記載の樹脂組成物。
- 前記熱硬化性化合物が、前記ポリアリーレンエーテル共重合体及び前記ベンゾオキサジン化合物と反応可能なエポキシ化合物を含む請求項1〜3のいずれか1項に記載の樹脂組成物。
- 前記エポキシ化合物が、トルエンに対する溶解度が25℃において10質量%以上のエポキシ樹脂である請求項4に記載の樹脂組成物。
- 無機充填材、難燃剤、及び添加剤をさらに含有する請求項1〜5のいずれか1項に記載の樹脂組成物。
- 請求項1〜6のいずれか1項に記載の樹脂組成物と溶媒とを含有する樹脂ワニス。
- 請求項7に記載の樹脂ワニスを繊維質基材に含浸させて得られたことを特徴とするプリプレグ。
- 請求項8に記載のプリプレグに金属箔を積層して、加熱加圧成形して得られたことを特徴とする金属張積層板。
- 請求項8に記載のプリプレグを用いて製造されたことを特徴とするプリント配線板。