JP2012172227A - 金属腐食防止又は抑制剤及びこれを用いた方法 - Google Patents
金属腐食防止又は抑制剤及びこれを用いた方法 Download PDFInfo
- Publication number
- JP2012172227A JP2012172227A JP2011037368A JP2011037368A JP2012172227A JP 2012172227 A JP2012172227 A JP 2012172227A JP 2011037368 A JP2011037368 A JP 2011037368A JP 2011037368 A JP2011037368 A JP 2011037368A JP 2012172227 A JP2012172227 A JP 2012172227A
- Authority
- JP
- Japan
- Prior art keywords
- metal
- inhibitor
- corrosion
- water
- metal corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明によれば、オクタデシルアミンとヘキシルアミンとからなる金属表面の水又は水蒸気による腐食を抑制又は防止する薬剤及び該薬剤を用いる金属表面の腐食を抑制又は防止する方法が提供される。
【選択図】なし
Description
しかし、アルコールは引火性の高い物質であり、皮膜性アミンとの混合物を引火性が無くなるまで水で希釈すると皮膜性アミンを安定溶解状態に維持できない。界面活性剤は起泡し易く、また分解によって低級酸を発生させ腐食性物質が生成する。酢酸はそれ自体が腐食性物質である。シクロヘキシルアミンは、揮発性アミンであるため腐食抑制効果を有するが、使用濃度にかかわらず毒物及び劇物取締法による規制対象物質に該当し、その取扱いは厳重な注意を要する。
よって、これらを腐食抑制剤に配合することは好ましくない。
本発明はまた、前記薬剤を保護対象の金属表面に接触させることを特徴とする水又は水蒸気による金属腐食の防止又は抑制方法を提供する。
本発明によれば、また、実施が簡便であり、安全でかつ環境に優しい金属腐食防止又は抑制方法が提供される。
理論によって本発明が制限されることは意図していないが、本発明の金属腐食防止又は抑制剤は、一成分として皮膜性アミンであるオクタデシルアミンを含有することで、該オクタデシルアミンが金属の表面にそのアミノ基により吸着して単分子層又は多分子層の非常に緻密な皮膜を作り、該皮膜が金属表面と水分との接触を防止することにより、該金属表面の水又は水蒸気による腐食を抑制又は防止できる。
したがって、本発明の金属腐食防止又は抑制剤はシクロヘキシルアミンを含まない。
更に、製剤時に他の腐食防止成分を追加しやすくなる。
但し、該金属腐食防止又は抑制剤中に含まれる皮膜性アミンに関して、少なくとも60重量%、好ましくは少なくとも80重量%、より好ましくは少なくとも95重量%はオクタデシルアミンである。
但し、該金属腐食防止又は抑制剤中に含まれる揮発性アミンに関して、少なくとも50重量%、好ましくは少なくとも80重量%、より好ましくは少なくとも99重量%はヘキシルアミンである。
本発明の金属腐食防止又は抑制剤中の揮発性アミンは、例えばボイラ蒸気復水系内に存在する酸性物質(とりわけ、炭酸)を中和することにより該復水と接触する金属の腐食を抑制し得る。
一般的なその他の腐食防止又は抑制成分としては、例えば、水酸化ナトリウム、水酸化カリウム、炭酸カリウム、リン酸ナトリウム、リン酸水素2カリウム、グルコン酸ナトリウム、酒石酸ナトリウム、クエン酸ナトリウム、モリブデン酸ナトリウム、ベンゾトリアゾール等を指す。
また、一般的なスケール分散成分としては、EDTAといったキレート剤、マレイン酸とその塩、ポリアクリル酸とその塩といった高分子化合物等を指す。
スケール分散成分の系内の濃度は、例えば、腐食防止又は抑制剤の系内の濃度に対して、1:200〜500:20の比率で存在し得る。
水の含有量の下限は、薬剤中のアミンの含有量を40重量%以下とすることで危険物法令から除外することが出来るため、好ましくは60重量%以上であり得る。
また、本発明の金属腐食防止又は抑制剤は、原液で使用してもよいし、倍率を問わず希釈して使用してもよい。
例えば、本発明の金属腐食防止又は抑制剤は、給水又は復水中の皮膜性アミンの濃度が0.5mg/L〜5mg/Lとなるように注入され得る。
保護対象の金属表面は、例えば、ボイラシステムの金属表面(例えば、ボイラ本体及び/又は配管の内面)であり得る。
金属腐食抑制又は防止剤は、ボイラシステムの復水中に混入することができる。
皮膜性アミンとしてオクタデシルアミン、揮発性アミンとしてヘキシルアミンを1:7.5で混合して実施例1の金属腐食防止又は抑制剤を製造した。
(実施例2)
前記皮膜性アミンと揮発性アミンの混合比を1:10としたこと以外は、実施例1と同様に混合して実施例2の金属腐食防止又は抑制剤を製造した。
前記皮膜性アミンと揮発性アミンの混合比を1:30としたこと以外は、実施例1と同様に混合して実施例3の金属腐食防止又は抑制剤を製造した。
(実施例4)
前記皮膜性アミンと揮発性アミンの混合比を1:50としたこと以外は、実施例1と同様に混合して実施例4の金属腐食防止又は抑制剤を製造した。
前記揮発性アミンをシクロヘキシルアミンとしたこと以外は、実施例1と同様に混合して比較例1の金属腐食防止又は抑制剤を製造した。
(比較例2)
前記揮発性アミンをシクロヘキシルアミンとし、皮膜性アミンと揮発性アミンの混合比を1:10としたこと以外は、実施例1と同様に混合して比較例2の金属腐食防止又は抑制剤を製造した。
前記揮発性アミンをシクロヘキシルアミンとし、皮膜性アミンと揮発性アミンの混合比を1:30としたこと以外は、実施例1と同様に混合して比較例3の金属腐食防止又は抑制剤を製造した。
(比較例4)
前記揮発性アミンをシクロヘキシルアミンとし、皮膜性アミンと揮発性アミンの混合比を1:50としたこと以外は、実施例1と同様に混合して比較例4の金属腐食防止又は抑制剤を製造した。
前記揮発性アミンをブチルアミンとしたこと以外は、実施例1と同様に混合して比較例5の金属腐食防止又は抑制剤を製造した。
(比較例6)
前記揮発性アミンをブチルアミンとし、皮膜性アミンと揮発性アミンの混合比を1:10としたこと以外は、実施例1と同様に混合して比較例6の金属腐食防止又は抑制剤を製造した。
前記揮発性アミンをブチルアミンとし、皮膜性アミンと揮発性アミンの混合比を1:30としたこと以外は、実施例1と同様に混合して比較例7の金属腐食防止又は抑制剤を製造した。
(比較例8)
前記揮発性アミンをブチルアミンとし、皮膜性アミンと揮発性アミンの混合比を1:50としたこと以外は、実施例1と同様に混合して比較例8の金属腐食防止又は抑制剤を製造した。
(比較例9)
前記揮発性アミンをオクチルアミンとし、皮膜性アミンと揮発性アミンの混合比を1:30としたこと以外は、実施例1と同様に混合して比較例9の金属腐食防止又は抑制剤を製造した。
腐食試験の試験液は、実施例4及び比較例4の腐食防止又は抑制剤を、皮膜性アミンとして1mg/L、揮発性アミンとして50mg/Lとなるよう純水中に添加したもの、又は腐食防止又は抑制剤を添加せず純水のみとしたものを用いた。
前記試験液を前記ジャーテスター試験器内に入れ、60℃に加温し、前記試験片を浸漬させ、撹拌回転数150rpmで撹拌し、7日間経過した後に試験片を取り出し、試験後の腐食度を計測した。
更に、本発明の溶解剤として選択した揮発性アミンであるヘキシルアミンは腐食防止又は抑制剤に配合することが好ましくない性質を有していないため、溶解剤としてシクロヘキシルアミンを用いる従来のものより安全性が高く取扱いが容易である。
Claims (8)
- オクタデシルアミンとヘキシルアミンとからなることを特徴とする水又は水蒸気による金属腐食の抑制又は防止剤。
- 前記オクタデシルアミンと前記ヘキシルアミンとの配合比(重量比)が1:7〜1:1000である請求項1に記載の金属腐食抑制又は防止剤。
- 前記配合比が1:10〜1:200である請求項2に記載の金属腐食抑制又は防止剤。
- 水を更に含み、かつ溶液の形態である請求項1〜3のいずれかに記載の金属腐食抑制又は防止剤。
- 前記金属の表面がボイラ及びその配管の内面である請求項1〜4のいずれか1項に記載の金属腐食抑制又は防止剤。
- 請求項1〜5に記載の金属腐食抑制又は防止剤を保護対象の金属表面に接触させることを特徴とする水又は水蒸気による金属腐食の防止又は抑制方法。
- 前記保護対象の金属表面がボイラシステムの金属表面である請求項6に記載の方法。
- 前記金属腐食抑制又は防止剤を給水又は復水中に注入する請求項7に記載の方法。