JP2010144065A - 固着防止シリコーンゴム - Google Patents
固着防止シリコーンゴム Download PDFInfo
- Publication number
- JP2010144065A JP2010144065A JP2008323258A JP2008323258A JP2010144065A JP 2010144065 A JP2010144065 A JP 2010144065A JP 2008323258 A JP2008323258 A JP 2008323258A JP 2008323258 A JP2008323258 A JP 2008323258A JP 2010144065 A JP2010144065 A JP 2010144065A
- Authority
- JP
- Japan
- Prior art keywords
- silicone rubber
- group
- mass
- parts
- adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)平均組成式(1):R1 aSiO(4-a)/2(R1は置換もしくは非置換の炭素数1〜8の一価炭化水素基、aは1.95〜2.05の正数)で表されるオルガノポリシロキサン:100質量部、
(B)一般式(2):R2 bR3 cSi(OR4)4-b-c(R2は炭素数6〜15のアルキル基、R3は置換もしくは非置換の炭素数1〜8の一価炭化水素基、R4は炭素数1〜6のアルキル基、bは1〜3、cは0〜2、b+cは1〜3の整数)
で表されるアルコキシシラン:0.1〜5質量部、
(C)硬化剤:硬化に必要な量
を含有する組成物を硬化してなる固着防止シリコーンゴム。
【選択図】なし
Description
いずれの方法も被着体がガラスの場合、密着あるいは固着防止の効果があるかは記載されていない。
このような効果が得られる理由は必ずしも明確ではなく、以下の理論に拘束されるものではないが、上記長鎖アルキル基を有するアルコキシシランが、シリコーンゴムよりブリードし、被着体表面の水分によりこの長鎖アルキル基を有するアルコキシシランのアルコキシ基が加水分解して被着体表面に層を形成し、この層はその表面(シリコーンゴム側に接する面)に長鎖アルキル基が存在することにより、シリコーンゴム層と被着体との固着が防止されて容易に剥離するためと思われる。
〔請求項1〕
(A)下記平均組成式(1)
R1 aSiO(4-a)/2 (1)
(式中、R1は置換もしくは非置換の炭素数1〜8の一価炭化水素基、aは1.95〜2.05の正数である。)
で表されるオルガノポリシロキサン: 100質量部、
(B)下記一般式(2)
R2 bR3 cSi(OR4)4-b-c (2)
(式中、R2は炭素数6〜15のアルキル基、R3は置換もしくは非置換の炭素数1〜8の一価炭化水素基、R4は炭素数1〜6のアルキル基、bは1〜3の整数、cは0〜2の整数、b+cは1〜3の整数である。)
で表されるアルコキシシラン: 0.1〜5質量部、
(C)硬化剤: 硬化に必要な量
を含有する組成物を硬化してなることを特徴とする固着防止シリコーンゴム。
〔請求項2〕
更に、成分(D)として、25℃における粘度が0.1〜2Pa・sであり、フェニル基を3〜50モル%含有するフェニル基含有シリコーンオイル: 0.1〜5質量部
を含有する組成物であることを特徴とする請求項1に記載の固着防止シリコーンゴム。
〔請求項3〕
厚さ2mmのシリコーンゴムの光透過率(波長800nm)が85%以上であることを特徴とする請求項1又は2に記載の固着防止シリコーンゴム。
〔請求項4〕
JIS K 6253規定のタイプEデュロメータにより測定されるシリコーンゴムの硬さが70以下であることを特徴とする請求項1〜3のいずれか1項に記載の固着防止シリコーンゴム。
〔請求項5〕
高温高湿85℃×85%RHの環境下で被着体に固着しないことを特徴とする請求項1〜4のいずれか1項に記載の固着防止シリコーンゴム。
本発明の固着防止シリコーンゴムは、
(A)下記平均組成式(1)で表されるオルガノポリシロキサン、
R1 aSiO(4-a)/2 (1)
(式中、R1は置換もしくは非置換の炭素数1〜8の一価炭化水素基、aは1.95〜2.05の正数である。)
(B)下記一般式(2)で表されるアルコキシシラン、
R2 bR3 cSi(OR4)4-b-c (2)
(式中、R2は炭素数6〜15のアルキル基、R3は置換もしくは非置換の炭素数1〜8の一価炭化水素基、R4は炭素数1〜6のアルキル基、bは1〜3の整数、cは0〜2の整数、b+cは1〜3の整数である。)
(C)硬化剤、
好ましくは更に
(D)25℃における粘度が0.1〜2Pa・sであり、フェニル基を3〜50モル%含有するフェニル基含有シリコーンオイル
を含有するシリコーンゴム組成物を硬化してなるものである。
R1 aSiO(4-a)/2 (1)
(式中、aは1.95〜2.05の正数である。)
R2 bR3 cSi(OR4)4-b-c (2)
C6H13Si(OCH3)3、C8H17Si(OC2H5)3、
C10H21Si(OCH3)3、C12H25Si(OCH3)3、
C10H21Si(CH3)(OCH3)2、C10H21Si(C6H5)(OCH3)2、
C10H21Si(CH3)(OC2H5)2、
C10H21Si(CH=CH2)(OCH3)2、
C10H21Si(CH2CH2CF3)(OCH3)2
上記硬化剤の具体例としては、ジ−t−ブチルパーオキサイド、2,5−ジメチル−2,5−ジ(t−ブチルパーオキシ)ヘキサン、ジクミルパーオキサイド等のラジカル反応に使用される有機過酸化物、また(A)成分のオルガノポリシロキサンがアルケニル基を有する場合は、ケイ素原子に結合した水素原子を1分子中に2個以上含有するオルガノハイドロジェンポリシロキサンと白金族系触媒からなる付加反応型硬化剤等が挙げられ、この添加量は通常のシリコーンゴム組成物と同様にすればよい。
シリコーンゴムの硬さが低くなると被着体に固着しやすくなるが、本発明においては、(B)成分の長鎖アルキル基を有するアルコキシシランの効果で固着を防ぐことができる。
(A)成分として25℃における粘度が30Pa・sのジメチルビニルシロキシ基で両末端を封止したジメチルポリシロキサン65質量部、25℃における粘度が0.7Pa・sのメチルビニルシロキサン単位1mol%、ジメチルシロキサン単位99mol%からなるメチルビニルポリシロキサン23質量部、25℃における粘度が1Pa・sのジメチルポリシロキサン12質量部からなる合計100質量部のオルガノポリシロキサンに、BET法による比表面積300m2/gの補強性シリカ充填剤であるエアロジル300(商品名、日本アエロジル株式会社製)25質量部、分散剤としてヘキサメチルジシラザン5質量部、水1.2質量部を添加し、プラネタリミキサーにて室温で30分間混合した後、温度150℃まで加熱してから3時間熱処理混合した(シリコーンゴムベースI)。
C10H21Si(OCH3)3 (4)
の長鎖アルキル基を有するアルコキシシラン1.2質量部を添加混合してから、(C)成分の硬化剤として触媒である塩化白金酸のビニルシロキサン錯体(白金含有量1質量%)0.1質量部と、反応制御剤であるエチニルシクロヘキサノール0.05質量部を添加混合し、更に下記構造式(5)
実施例1の長鎖アルキル基を有するアルコキシシランの添加量を3質量部に変更した以外は同様な方法で厚さ2mmのシートを作製し、各特性を評価した。
(A)成分として25℃における粘度が30Pa・sのジメチルビニルシロキシ基で両末端を封止したジメチルポリシロキサン35質量部、25℃における粘度が0.7Pa・sのメチルビニルシロキサン単位1mol%、ジメチルシロキサン単位99mol%からなるメチルビニルポリシロキサン15質量部、25℃における粘度が1Pa・sのジメチルポリシロキサン50質量部からなる合計100質量部のオルガノポリシロキサンに、BET法による比表面積300m2/gの補強性シリカ充填剤であるエアロジル300(前出)15質量部、分散剤としてヘキサメチルジシラザン3質量部、水0.8質量部を添加し、プラネタリミキサーにて室温で30分間混合した後、温度150℃まで加熱してから3時間熱処理混合した(シリコーンゴムベースII)。
実施例3の固着防止シリコーンゴム組成物に、(D)成分の25℃における粘度が1Pa・sのジフェニルシロキサン単位5mol%、ジメチルシロキサン単位95mol%からなるフェニル基含有シリコーンオイル0.7質量部を添加した以外は同様な方法で厚さ2mmのシートを作製し、各特性を評価した(実施例4)。
(A)成分として25℃における粘度が5Pa・sのジメチルビニルシロキシ基で両末端を封止したジメチルポリシロキサン60質量部、25℃における粘度が1Pa・sのジメチルポリシロキサン40質量部からなる合計100質量部のオルガノポリシロキサンに、シリコーンゴムの強度を向上させる(CH3)3SiO1/2単位、(CH2=CH)(CH3)2SiO1/2単位及びSiO2単位からなるシリコーン樹脂共重合体([(CH3)3SiO1/2単位と(CH2=CH)(CH3)2SiO1/2単位の合計]/SiO2単位=0.8(モル比)、ビニル基含有量=0.0008モル/g)20質量部、シリコーンゴムに粘着性を付与する(CH3)3SiO1/2単位とSiO2単位からなるシリコーン樹脂共重合体((CH3)3SiO1/2単位/SiO2単位=0.75(モル比))40質量部を添加し、プラネタリミキサーにて室温で30分間混合した(シリコーンゴムベースIII)。
厚さ2mmで大きさ25mm×34mm角のシリコーンゴムシートを厚さ5mmの被着体2枚の間に挟み、締め付け力10Nのクリップ2ヶで固定した。これらのサンプルを85℃×85%RHの恒温恒湿機中に放置して、500時間及び1,000時間後に取り出してシリコーンゴムと被着体の固着状態を確認した。被着体及び評価基準を下記に示す。
ガラス:フロートガラス
ステンレススチール:SUS304
アルミニウム:A5052
◎:被着体との離型性良好。剥離が軽い。
○:被着体との離型性OK。剥離は◎より重い。
△:部分的な接着あり。
×:接着。
××:全面接着。シートが破壊。
Claims (5)
- (A)下記平均組成式(1)
R1 aSiO(4-a)/2 (1)
(式中、R1は置換もしくは非置換の炭素数1〜8の一価炭化水素基、aは1.95〜2.05の正数である。)
で表されるオルガノポリシロキサン: 100質量部、
(B)下記一般式(2)
R2 bR3 cSi(OR4)4-b-c (2)
(式中、R2は炭素数6〜15のアルキル基、R3は置換もしくは非置換の炭素数1〜8の一価炭化水素基、R4は炭素数1〜6のアルキル基、bは1〜3の整数、cは0〜2の整数、b+cは1〜3の整数である。)
で表されるアルコキシシラン: 0.1〜5質量部、
(C)硬化剤: 硬化に必要な量
を含有する組成物を硬化してなることを特徴とする固着防止シリコーンゴム。 - 更に、成分(D)として、25℃における粘度が0.1〜2Pa・sであり、フェニル基を3〜50モル%含有するフェニル基含有シリコーンオイル: 0.1〜5質量部
を含有する組成物であることを特徴とする請求項1に記載の固着防止シリコーンゴム。 - 厚さ2mmのシリコーンゴムの光透過率(波長800nm)が85%以上であることを特徴とする請求項1又は2に記載の固着防止シリコーンゴム。
- JIS K 6253規定のタイプEデュロメータにより測定されるシリコーンゴムの硬さが70以下であることを特徴とする請求項1〜3のいずれか1項に記載の固着防止シリコーンゴム。
- 高温高湿85℃×85%RHの環境下で被着体に固着しないことを特徴とする請求項1〜4のいずれか1項に記載の固着防止シリコーンゴム。