JP2009263651A - 光触媒コーティング組成物 - Google Patents
光触媒コーティング組成物 Download PDFInfo
- Publication number
- JP2009263651A JP2009263651A JP2009081070A JP2009081070A JP2009263651A JP 2009263651 A JP2009263651 A JP 2009263651A JP 2009081070 A JP2009081070 A JP 2009081070A JP 2009081070 A JP2009081070 A JP 2009081070A JP 2009263651 A JP2009263651 A JP 2009263651A
- Authority
- JP
- Japan
- Prior art keywords
- photocatalyst
- coating composition
- mass
- oxide particles
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】この光触媒コーティング組成物は、溶媒中に、酸化チタン粒子と、無機酸化物粒子と、銅元素と、銀元素と、水酸化第四アンモニウムと、任意成分として加水分解性シリコーンとを含んでなる。また、光触媒コーティング組成物の原料である光触媒酸化チタンゾルに水酸化第四アンモニウムを含むことで銅および銀を安定に分散させることが可能となる。
【選択図】なし
Description
本発明の光触媒コーティング組成物は、酸化チタン粒子、無機酸化物粒子、銅元素、銀元素、水酸化第四アンモニウム、および溶媒を含んでなる。本発明によれば、酸化チタン粒子を含有するコーティング組成物に銅元素と銀元素とを安定的に含有させることが可能となった。
1質量部以上20質量部未満の前記酸化チタン粒子と、
70質量部を超え99質量部以下の前記無機酸化物粒子と、
シリカ換算で0質量部以上10質量部未満の前記加水分解性シリコーンと、
を、前記酸化チタン粒子、前記無機酸化物粒子および前記加水分解性シリコーンのシリカ換算量の合計量が100質量部となるように含んでなる。本発明によるコーティング組成物を用いて光触媒層を形成することにより、基材(特に有機基材)への浸食を抑制しながら、被膜の耐候性、有害ガス分解性、カビや藻の繁殖抑制、または所望の各種被膜特性(透明性、膜強度等)に優れた被膜を得ることが可能となる。
本発明による光触媒塗装体は、基材と、この基材上に設けられる光触媒層とを備えてなる。光触媒層は、酸化チタン粒子と、無機酸化物粒子と、任意成分としての加水分解性シリコーンとを被膜形成成分として含み、さらに、銀および銅と、水酸化第四アンモニウムと、任意成分としての界面活性剤とを含んでなる。
本発明に用いる基材は、その上に光触媒層を形成可能な材料であれば無機材料、有機材料を問わず種々の材料であってよく、その形状も限定されない。材料の観点からみた基材の好ましい例としては、金属、セラミック、ガラス、プラスチック、ゴム、石、セメント、コンクリ−ト、繊維、布帛、木、紙、それらの組合せ、それらの積層体、それらの表面に少なくとも一層の被膜を有するものが挙げられる。用途の観点からみた基材の好ましい例としては、建材、建物の内外装、窓枠、窓ガラス、構造部材、乗物の内外装及び塗装、機械装置や物品の外装、防塵カバー及び塗装、交通標識、各種表示装置、広告塔、道路用遮音壁、鉄道用遮音壁、橋梁、ガードレ−ルの外装及び塗装、トンネル内装及び塗装、碍子、太陽電池カバー、太陽熱温水器集熱カバー、ビニールハウス、車両用照明灯のカバー、屋外用照明器具、台及び上記物品表面に貼着させるためのフィルム、シート、シール等が挙げられ、より好適には外装材全般が挙げられる。
本発明の光触媒塗装体は、本発明の光触媒コーティング組成物を基材上に直接、または中間層を介して、塗布することにより簡単に製造することができる。光触媒層の塗装方法は、前記液剤を刷毛塗り、ローラー、スプレー、ロールコーター、フローコーター、ディップコート、流し塗り、スクリーン印刷、電着、蒸着等、一般に広く行われている方法を利用できる。コーティング組成物の基材への塗布後は、常温乾燥させればよく、あるいは必要に応じて加熱乾燥してもよい。
材料の用意
以下の材料を用意し、例に使用した。
酸化チタン粒子
・四塩化チタン水溶液にアンモニア水を攪拌下で添加し、チタンゲルを生成させ、ろ過水洗して得たチタンゲルからなるスラリーに所望量の酸化銀(Ag2O、和光純薬工業 社製)と水酸化銅(Cu(OH)2、関東化学 社製)を添加し、さらに水酸化テトラメチルアンモニウム水溶液(多摩化学工業 社製)を添加して攪拌した後、オートクレーブに入れ、130℃で水熱処理を行って得た、銅化合物および銀化合物をゾルとして共存させたチタニア水分散体(以下、銅/銀含有チタニア水分散体という)(平均粒径:48nm 塩基性)を得た。
無機酸化物粒子
・水分散型コロイダルシリカ(平均粒径:26nm 塩基性)
・水分散型コロイダルシリカ(平均粒径:14nm 塩基性)
・水分散型コロイダルシリカ(平均粒径:5nm 塩基性)
界面活性剤
・ポリエーテル変性シリコーン系界面活性剤
加水分解性シリコーン
・テトラメトキシシランの重縮合物(SiO2換算濃度:51質量%、溶媒:アルコール・水)
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−1〜T−6に示される配合比で混合して、光触媒コーティング組成物を得た。なお、この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−1、T−4、T−7およびT−8に示される配合比で混合して、光触媒コーティング組成物を得た。なお、例8および例9この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
NOx除去量=[NO(照射後)−NO(照射時)]−[NO2(照射時)−NO2(照射後)]
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として550nmの波長の透過率が94%のフロート板ガラスを用意した。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−1〜T−4に示される配合比で混合して、光触媒コーティング組成物を得た。
<直線透過率>
A:直線(550nm)透過率が97%以上
B:直線(550nm)透過率が95%以上97%未満
<紫外線遮蔽率>
a:紫外線(300nm)遮蔽率が80%以上
b:紫外線(300nm)遮蔽率が30%以上80%未満
c:紫外線(300nm)遮蔽率が30%未満
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として550nmの波長の透過率が94%のフロート板ガラスを用いた。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−1、T−9、T−10に示される配合比で混合して、光触媒コーティング組成物を得た。なお、この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上に白色顔料を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体およびチタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−1、T−11〜T−14およびT−22に示される配合比で混合して、光触媒コーティング組成物を得た。なお、この光触媒コーティング組成物は加水分解性シリコーンを含まない。なお、例25〜29においては、銀化合物と銅化合物の配合比を調整(例28は全て銅化合物、例29は全て銀化合物)した銅/銀含有チタニア水分散体を使用した。また、例30においては銀化合物および銅化合物を含まないチタニア水分散体を使用した。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、例29がわずかに黄変した以外は、いずれも沈殿や変色は見られず安定な組成物であった。
光触媒としての銅/銀含有チタニア水分散体およびチタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−15およびT−16に示される配合比で混合して、光触媒コーティング組成物を得た。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
得られた光触媒コーティング組成物を、例25〜例30と同様の方法で製膜し、例31および例32の光触媒塗装体を得た。
この光触媒塗装体について、例25〜例30と同様の方法にて抗カビ性の評価を行った。
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−3に示される配合比で混合して、光触媒コーティング組成物を得た。なお、この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、沈殿や変色は見られず安定な組成物であった。
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、シーラー処理した窯業系サイディング基材上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−9、T−17およびT−18に示される配合比で混合して、光触媒コーティング組成物を得た。なお、この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−17、T−19およびT−20に示される配合比で混合して、光触媒コーティング組成物を得た。したがって、この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
<親水性>
A:接触角が10°未満
B:接触角が10°以上、20°未満
C:接触角が20°以上
表9に示されるように、光触媒層中の光触媒粒子の含有量を2質量部以上とすることによって、高い親水性を確保することが分かった。
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、エポキシ樹脂で目止め処理したスレート板に、カーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−17およびT−21に示される配合比で混合して、光触媒コーティング組成物を得た。したがって、この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
<耐摺動磨耗性>
A:接触角が10°未満
B:接触角が10°以上、20°未満
表10に示されるように、例40の光触媒塗装体は、摺動に対して、より強固な膜を形成することが分かった。
光触媒層を備えた光触媒塗装体を以下の通り製造した。まず、基材として着色有機塗装体を用意した。この着色有機塗装体は、フロート板ガラス上にカーボンブラック粉末を添加した汎用アクリルシリコーンを塗布して、十分に乾燥および硬化させたものである。一方、光触媒としての銅/銀含有チタニア水分散体と、無機酸化物としての水分散型コロイダルシリカと、溶媒として水と、界面活性剤とを表1のT−9、T−17およびT−20に示される配合比で混合して、光触媒コーティング組成物を得た。したがって、この光触媒コーティング組成物は加水分解性シリコーンを含まない。光触媒コーティング組成物中の光触媒および無機酸化物の合計の固形分濃度は5.5質量%とした。また、得られた光触媒コーティング組成物を室温で1ヶ月間放置した後観測したが、いずれも沈殿や変色は見られず安定な組成物であった。
NOx除去量=[NO(照射後)−NO(照射時)]−[NO2(照射時)−NO2(照射後)]
四塩化チタン水溶液(TiO2=0.5質量%)にアンモニア水(NH3=3.0質量%)を攪拌下で添加し、チタンゲルを生成させた。これをろ液中の塩素イオンがチタンゲル(TiO2)に対して100ppm以下になるまでろ過水洗した。このゲルをオートクレーブに入れ120℃で水熱処理を行い、TiO2=6.2質量%のスラリーを得た。このスラリー200gに酸化銀0.1gと水酸化銅0.6gおよび水酸化テトラメチルアンモニウム25質量%水溶液1.7gを添加してよく攪拌した後、130℃で水熱処理し、ゾルを得た。
このゾルを100℃で乾燥させて得られる粉を粉末X線回折法により測定したところ、アナターゼ型の酸化チタンのピークが認められた。得られたゾルを室温で1ヶ月間放置した後観測したが、いずれも沈殿は見られず安定なゾルであった。また、得られたゾルの変色の程度を評価するため、色質指数ΔL値を求めたところ、1.29であった。
〈色質指数ΔLの測定方法〉
ゾルをAg2O=0.05%になるよう濃度調整した後、50mlのガラス製サンプル瓶に30g分注する。ブラックライト照射前のゾルの色質指数L1値を測定した後、サンプル瓶は震盪器に据え付け、20W型のブラックライト照射下で容器表面が1mW/cm2(365nm)になるようにセットし、30分間照射後のゾルの色質指数L2値を測定する。なお、色質指数L値の測定は日本電色工業(株)製Z−1001DPPを用い、照射面積30mmΦのセルに試料5gを入れて測定し、その差を色質指数ΔL値=|L1−L2|とした。
四塩化チタン水溶液(TiO2=0.5質量%)にアンモニア水(NH3=3.0質量%)を攪拌下で添加し、チタンゲルを生成させた。これをろ液中の塩素イオンがチタンゲル(TiO2)に対して100ppm以下になるまでろ過水洗し、TiO2=6.2質量%のスラリーを得た。このスラリー200gに酸化銀0.1gと水酸化銅0.6gおよび100質量%モノエタノールアミン溶液0.3gを添加してよく攪拌した後、これを130℃で水熱処理を行ない、ゾルを得た。このゾルを100℃で乾燥させて得られる粉を粉末X線回折法により測定したところ、アナターゼ型の酸化チタンのピークが認められた。さらに、得られたゾルの変色の程度を評価するために、色質指数ΔL値を求めたところ、4.82であった。また、得られたゾルは、室温で保存中7日後には粘度が上昇し、ゲル化した。
Claims (9)
- 酸化チタン粒子、無機酸化物粒子、銅元素、銀元素、水酸化第四アンモニウム、および溶媒を含んでなる、光触媒コーティング組成物
- 前記銀元素および前記銅元素の合計量が、Ag2OおよびCuOに換算した合計量で表したとき、酸化チタン粒子に対して0.1質量%を超え10質量%以下である、請求項1に記載の光触媒コーティング組成物。
- 前記銀元素および前記銅元素の量が、Ag2OおよびCuOに換算した量で表したとき、Ag2O/CuO(質量比)が、0/100<[Ag2O/CuO]≦65/35を満たすものである、請求項1または2に記載の光触媒コーティング組成物。
- 水酸化第四アンモニウムが水酸化テトラメチルアンモニウムである、請求項1〜3のいずれか一項に記載の光触媒コーティング組成物。
- 水酸化第四アンモニウムの量が、酸化チタン1モルに対して0.01〜0.1モルである、請求項1〜4のいずれか一項に記載の光触媒コーティング組成物。
- 加水分解性シリコーンをさらに含んでなる、請求項1〜5のいずれか一項に記載の光触媒コーティング組成物。
- 1質量部以上20質量部未満の前記酸化チタン粒子と、
70質量部を超え99質量部以下の前記無機酸化物粒子と、
シリカ換算で0質量部以上10質量部未満の前記加水分解性シリコーンと、
を、前記酸化チタン粒子、前記無機酸化物粒子および前記加水分解性シリコーンのシリカ換算量の合計量が100質量部となるように含んでなる、請求項1〜5のいずれか一項に記載の光触媒コーティング組成物。 - 前記無機酸化物粒子がシリカ粒子である、請求項1〜7のいずれか一項に記載の光触媒コーティング組成物。
- 外装材用コーティングのための、請求項1〜8のいずれか一項に記載の光触媒コーティング組成物。