JP2009235544A - 微粒子分散体の製造方法及びそれを使用して製造された金属又は金属化合物の微粒子分散体並びにそれを分散媒置換した微粒子分散液 - Google Patents
微粒子分散体の製造方法及びそれを使用して製造された金属又は金属化合物の微粒子分散体並びにそれを分散媒置換した微粒子分散液 Download PDFInfo
- Publication number
- JP2009235544A JP2009235544A JP2008085786A JP2008085786A JP2009235544A JP 2009235544 A JP2009235544 A JP 2009235544A JP 2008085786 A JP2008085786 A JP 2008085786A JP 2008085786 A JP2008085786 A JP 2008085786A JP 2009235544 A JP2009235544 A JP 2009235544A
- Authority
- JP
- Japan
- Prior art keywords
- metal
- dispersion
- vapor pressure
- particulate dispersion
- pressure liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】金属、合金又は金属化合物の気体を、低蒸気圧液体に接触させることによって、金属、合金又は金属化合物の微粒子が該低蒸気圧液体に体積分布メジアン径(D50)100nm以下で分散された分散体を製造する方法であって、該低蒸気圧液体中に脂肪酸を溶解させておくことを特徴とする微粒子分散体の製造方法。
【選択図】図4
Description
低蒸気圧液体としてライオン拡散ポンプ油(A)(ライオン社製)380gを用い、それに脂肪酸として10−ウンデセン酸(CH2=CH(CH2)8COOH)を20g添加し攪拌した。ライオン拡散ポンプ油(A)は、炭素数12〜16個のアルキル基を有するアルキルナフタレンである。また、10−ウンデセン酸は炭素数11の不飽和脂肪酸である。
実施例1において、脂肪酸として、10−ウンデセン酸に代えて、オレイン酸(C8H17CH=CH(CH2)7COOH(cis))を用いた以外は実施例1と同様の方法で行なった。オレイン酸は炭素数17の不飽和脂肪酸である。
実施例1において、脂肪酸として、10−ウンデセン酸に代えて、エルカ酸を用いた以外は実施例1と同様の方法で行なった。エルカ酸は炭素数22の不飽和脂肪酸である。
実施例1において、10−ウンデセン酸に代えて、コハク酸イミドポリアミンを用いた以外は、実施例1と同様の方法で行なった。
実施例1において、10−ウンデセン酸に代えて、Disperbyk−102(ビックケミー社製)を用いた以外は、実施例1と同様の方法で行なった。Disperbyk−102は、酸性基を有するコポリマーである。
2 固定軸
3 脂肪酸が溶解された低蒸気圧液体
4 脂肪酸が溶解された低蒸気圧液体の膜
5 金属、合金又は金属化合物(金属類)
6 容器
7 水流
8 回転方向
9 原子又は分子
10 「金属、合金又は金属化合物」の微粒子(金属類の微粒子)
Claims (5)
- 金属、合金又は金属化合物の気体を低蒸気圧液体に接触させることによって、金属、合金又は金属化合物の微粒子が該低蒸気圧液体に体積分布メジアン径(D50)100nm以下で分散された分散体を製造する方法であって、該低蒸気圧液体中に脂肪酸を溶解させておくことを特徴とする微粒子分散体の製造方法。
- 上記脂肪酸が炭素数11以上のものである請求項1記載の微粒子分散体の製造方法。
- 金属の気体又は金属化合物の気体の、該低蒸気圧液体への接触を、10−4Pa〜10−1Paの範囲の圧力下で行なう請求項1又は請求項2記載の微粒子分散体の製造方法。
- 請求項1ないし請求項3の何れかの請求項記載の微粒子分散体の製造方法を使用して製造されたものであることを特徴とする微粒子分散体。
- 請求項4記載の微粒子分散体中の低蒸気圧液体を、他の分散媒に置換したものであることを特徴とする、金属、合金又は金属化合物の微粒子分散液。