JP2009036558A - 応力腐食割れ監視方法及びプラントの管理方法 - Google Patents
応力腐食割れ監視方法及びプラントの管理方法 Download PDFInfo
- Publication number
- JP2009036558A JP2009036558A JP2007199248A JP2007199248A JP2009036558A JP 2009036558 A JP2009036558 A JP 2009036558A JP 2007199248 A JP2007199248 A JP 2007199248A JP 2007199248 A JP2007199248 A JP 2007199248A JP 2009036558 A JP2009036558 A JP 2009036558A
- Authority
- JP
- Japan
- Prior art keywords
- structural member
- scc
- water
- concentration
- plant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】原子力プラントに設けられた各ECPセンサによって測定された各測定対象箇所でのECPの測定値がそれぞれSCC監視装置に入力される(ステップ22)。その原子力プラントに設けられた各水質測定装置で測定された各測定対象箇所での冷却水の硫酸濃度の測定値がそれぞれSCC監視装置に入力される。測定対象箇所の構造部材の炭素量がSCC監視装置に入力される(ステップ24)。各測定対象箇所の構造部材の歪み速度がSCC監視装置に入力される(ステップ25)。SCC監視装置はECP及び硫酸濃度の各測定値、構造部材の炭素量及び歪み速度に基づいて各構造部材におけるSCC発生時間を算出する(ステップ26)。
【選択図】図5
Description
バルク炉水の水質を測定する水質測定装置16aがサンプリング配管14に接続される。水質測定装置16bはサンプリング配管15に接続されている。給水の水質を測定する水質測定装置16cがサンプリング配管16に接続される。蒸気中の酸素濃度、水素濃度及び導電率を測定する測定装置16dがサンプリング配管17に接続される。イオンクロマトグラフ装置40がサンプリング配管14,15にそれぞれ接続されている。
Claims (12)
- プラントを構成する水と接する構造部材の応力腐食割れを監視する方法において、
前記構造部材の腐食電位、及び前記水に含まれる不純物イオンの濃度を測定し、前記腐食電位及び前記イオン濃度の各測定情報、前記構造部材の歪み速度、及び前記構造部材の粒界の腐食速度に基づいて前記構造部材における応力腐食割れの発生時間を求めることを特徴とする応力腐食割れ監視方法。 - 前記不純物イオンの濃度が前記水に含まれる硫酸イオンの濃度である請求項1に記載の応力腐食割れ監視方法。
- 前記構造部材の粒界の腐食速度は、前記構造部材に含まれる炭素量に基づいて求められる請求項1または請求項2に記載の応力腐食割れ監視方法。
- 前記構造部材の粒界の腐食速度は、前記構造部材の電気化学再活性化率に基づいて求められる請求項1または請求項2に記載の応力腐食割れ監視方法。
- 前記構造部材の粒界の腐食速度は、前記構造部材の粒界組成を模擬した材料の分極曲線に基づいて求められる請求項1または請求項2に記載の応力腐食割れ監視方法。
- 前記構造部材が、オーステナイト系ステンレス鋼及びニッケル基合金のいずれかで構成されている請求項1ないし請求項5のいずれか1項に記載の応力腐食割れ監視方法。
- プラントを構成する水と接する構造部材の応力腐食割れの発生を管理するプラントの管理方法において、
前記構造部材の腐食電位、及び前記水に含まれる不純物イオンの濃度を測定し、
前記腐食電位及び前記不純物イオン濃度の各測定情報、前記構造部材の歪み速度、及び前記構造部材の粒界の腐食速度に基づいて前記構造部材における応力腐食割れの発生時間を求め、
前記発生時間が設定時間よりも短いとき、前記腐食電位及び前記不純物イオンの濃度のうち少なくとも1つを減少させることを特徴とするプラントの管理方法。 - 前記不純物イオンの濃度が前記水に含まれる硫酸イオンの濃度である請求項7に記載のプラントの管理方法。
- 前記構造部材の粒界の腐食速度は、前記構造部材に含まれる炭素量に基づいて求められる請求項7または請求項8に記載のプラントの管理方法。
- プラントの起動運転時における前記発生時間を求め、前記起動運転時において前記発生時間が設定時間よりも短いとき、前記腐食電位及び前記不純物イオンの濃度のうち少なくとも1つを減少させる請求項7ないし請求項9のいずれか1項に記載のプラントの管理方法。
- プラントを構成する水と接する構造部材の腐食電位、及び前記水に含まれる不純物のイオン濃度を測定し、前記腐食電位及び前記イオン濃度の各測定情報、前記構造部材の歪み速度、及び前記構造部材の粒界の腐食速度に基づいて前記構造部材における応力腐食割れの発生時間を求め、得られたこの発生時間を起点にして前記構造部材の予寿命を求めることを特徴とするプラント構造部材の予寿命推定方法。
- 前記不純物のイオン濃度が前記水に含まれる硫酸イオンの濃度である請求項11に記載のプラント構造部材の予寿命推定方法。