JP2009029076A - 転写シート - Google Patents
転写シート Download PDFInfo
- Publication number
- JP2009029076A JP2009029076A JP2007197660A JP2007197660A JP2009029076A JP 2009029076 A JP2009029076 A JP 2009029076A JP 2007197660 A JP2007197660 A JP 2007197660A JP 2007197660 A JP2007197660 A JP 2007197660A JP 2009029076 A JP2009029076 A JP 2009029076A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin
- transfer
- transfer sheet
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】基材に、少なくとも剥離層、装飾層、オーバープリント層及び接着剤層を含む転写層を積層した転写シートであって、オーバープリント層は接着剤層と接触し、接着剤層はウレタン系樹脂とマレイン酸樹脂を含有し、かつ、接着剤層中のマレイン酸樹脂の含有量が20〜40質量%である転写シートである。
【選択図】図1
Description
そして、転写層で用いる接着剤については、転写する被転写体の種類に応じて適宜選択される。例えば、被転写体がポリエチレンなどの樹脂フィルムの場合には、ウレタン系樹脂を主成分とした接着剤が用いられ、MDF(中密度圧縮合板)、HDF(高密度圧縮合板)などの木質系材料には、ポリアミド系接着剤や塩化ビニル・酢酸ビニル共重合体などの接着剤が適当である。
(1)基材に少なくとも剥離層、装飾層、オーバープリント層及び接着剤層を含む転写層を積層した転写シートであって、オーバープリント層は接着剤層と接触し、接着剤層はウレタン系樹脂とマレイン酸樹脂を含有し、かつ、接着剤層中のマレイン酸樹脂の含有量が20〜40質量%である転写シート、
(2)前記各層のいずれにも芳香族系溶媒を含有しない上記(1)に記載の転写シート、
(3)前記ウレタン系樹脂の、JIS K7127に準拠した引張試験によって測定した破断伸度が900〜1400%である上記(1)又は(2)に記載の転写シート、
(4)前記ウレタン系樹脂がブロッキング防止剤を0.1〜5質量%含有する上記(1)〜(3)のいずれかに記載の転写シート、
(5)前記マレイン酸樹脂の軟化点が120〜185℃である上記(1)〜(4)のいずれかに記載の転写シート、
(6)剥離層と装飾層の間にプライマー層を有する上記(1)〜(5)のいずれかに記載の転写シート、及び
(7)被転写面が樹脂含浸紙と木質基材の両方を有する基板用である上記(1)〜(6)のいずれかに記載の転写シート、
を提供するものである。
以下、図1を用いて本発明の転写シートについて詳細に説明する。
基材2は、転写層8と離型性が有り、また被転写面に凹凸が有る場合は該凹凸への形状追従性があるものであれば、従来公知のものでよく特に制限はない。従って、被転写面が平面又は二次元的凹凸表面で転写シートが伸ばされない場合には、一般的な2軸延伸ポリエチレンテレフタレートフィルム(シート)、又は延伸性が無い紙等を用いることができる。
また、被転写面が三次元的凹凸表面で転写シートが伸ばされる場合には、少なくとも転写時には延伸性の有る基材を用いることが肝要である。延伸性のある基材としては、例えば熱可塑性樹脂を用いることができ、具体的には、ポリプロピレン、ポリエチレン、ポリメチルペンテン、エチレン−プロピレン−ブテン3元共重合体、オレフィン系熱可塑性エラストマー等のオレフィン樹脂;エチレンテレフタレートイソフタレート共重合体、ポリエチレンテレフタレート、ポリブチレンテレフタレート等の熱可塑性ポリエステル樹脂;塩化ビニル樹脂;ポリアミド樹脂;ウレタン系熱可塑性エラストマー等のエラストマー等が挙げられる。
基材2は上述の材料からなるフィルム又はシートを単層で用いてもよいし、又は異種材料からなる積層体として用いてもよい。
基材2の厚さとしては特に限定されないが、通常は20〜200μm程度である。
また、剥離性を調整するために、基材2の転写層側の面に、コーティング処理、コロナ放電処理、オゾン処理などの表面処理を行ってもよい。
さらには、基材2の転写層に接する面の反対側に、ごみの付着防止の目的で静電気防止層を設けることができる。静電気防止層としては、非イオン界面活性剤及び/又はカチオン界面活性剤を配合した水溶液などを用いることができる。
剥離層3は基材2又は基材2に設けられた離型層と装飾層5との間の剥離性を調整するため、また、転写後の装飾層5の表面保護のために設けられる層である。
剥離層3としては、アクリル樹脂、塩化ビニル樹脂、ウレタン樹脂、塩化ビニル−酢酸ビニル共重合体、ブチラール樹脂、セルロース系樹脂等を単独で或いは2種以上混合したもの、及び電子線硬化性樹脂や紫外線硬化性樹脂を架橋硬化したものを用いることが好ましい。この場合、摩耗性、透明性を考慮すると、アクリル樹脂が好ましい。
また、剥離層3は、グラビア印刷、ロールコート、スクリーン印刷、オフセット印刷等の公知の手法により積層される。なお、本発明では剥離層3を構成する樹脂を基材2に塗布するに際し、溶媒としてトルエン、キシレン等の芳香族系溶媒を使用しないことが好ましい。
なお、プライマー層4は、剥離層3と同様の方法で積層することができ、また、溶媒としては同様に芳香族系溶媒を用いないことが好ましい。
模様としては、木目模様、大理石模様(例えばトラバーチン大理石模様)等の岩石の表面を模した石目模様、布目や布状の模様を模した布地模様、タイル貼模様、煉瓦積模様等があり、これらを複合した寄木、パッチワーク等の模様もある。これらの模様は通常の黄色、赤色、青色、および黒色のプロセスカラーによる多色印刷によって形成される他、模様を構成する個々の色の版を用意して行う特色による多色印刷等によっても形成される。
また、印刷は部分印刷でもベタ印刷でもよく、部分印刷とベタ印刷の両方を行ってもよい。また、剥離層へのエンボス加工等による凹凸模様であってもよい。
着色剤としては、カーボンブラック(墨)、鉄黒、チタン白、アンチモン白、黄鉛、チタン黄、弁柄、群青、コバルトブルー等の無機顔料、キナクリドンレッド、イソインドリノンイエロー、フタロシアニンブルー等の有機顔料又は染料、アルミニウム、真鍮等の鱗片状箔片からなる金属顔料、二酸化チタン被覆雲母、塩基性炭酸鉛等の鱗片状箔片からなる真珠光沢(パール)顔料等が用いられる。
オーバープリント層6を構成する成分としては、目止め層としての効果を有するものであれば特に制限はなく、例えば、1液硬化型ウレタン樹脂、2液硬化型ウレタン樹脂、エポキシ樹脂、アクリル樹脂、酢酸ビニル樹脂等が例示される。1液硬化型ウレタン樹脂及び2液硬化型ウレタン樹脂としては、後に詳述する接着剤層7を構成する転写用接着剤として用いられるものと同様のものを用いることができる。
また、アクリル樹脂としては、前述のプライマー層4に用いられるアミノ基含有アクリル樹脂、シリコーン系化合物を硬化剤として用いる、2液型のシリコーン・アミノ基含有アクリル樹脂などが好適に用いられる。
なお、オーバープリント層6は、剥離層3と同様の方法で積層することができ、また、溶媒としては同様に芳香族系溶媒を用いないことが好ましい。
ウレタン系樹脂としては、2液硬化型ウレタン樹脂、又は1液硬化型ウレタン樹脂等が使用できる。
2液硬化型ウレタン樹脂は、ポリオールを主剤とし、イソシアネートを架橋剤(硬化剤)とするウレタン樹脂である。ポリオールとしては、分子中に2個以上の水酸基を有するもので、例えばポリエチレングリコール、ポリプロピレングリコール、アクリルポリオール、ポリエステルポリオール、ポリエーテルポリオール、ポリカーボネートポリオール、ポリウレタンポリオール等が用いられる。また、イソシアネートとしては、分子中に2個以上のイソシアネート基を有する多価イソシアネートが用いられる。例えば、2,4−トリレンジイソシアネート、キシレンジイソシアネート、4,4′−ジフェニルメタンジイソシアネート等の芳香族イソシアネート、あるいは、1,6−ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、水素添加トリレンジイソシアネート、水素添加ジフェニルメタンジイソシアネート等の脂肪族(乃至は脂環式)イソシアネート、さらには上記各種イソシアネートの付加体、又は多量体を用いることもできる。例えば、トリレンジイソシアネートの付加体、トリレンジイソシアネート3量体(trimer)等がある。
但し、この粘着性がウレタン系樹脂のハンドリングを悪くするので、これを防止することを目的にブロッキング防止剤を含有させることが好ましい。
ブロッキング防止剤の粒径としては、効果の点から通常0.1〜5μm程度が好ましく、さらには0.5〜3μmの範囲が好ましい。
ブロッキング防止剤の含有量としては、ウレタン系樹脂中に0.1〜5質量%の範囲で含有されることが好ましい。0.1質量%以上であると粘着性を十分に抑制することができ、好適なハンドリング性が得られる。一方、5質量%以下であると、ブロッキングを抑制することができる。
特に有用なモノマーとしてはスチレン、イソブチレン、(メタ)アクリル酸アルキルエステル、ベンジル(メタ)アクリレート等が挙げられる。
無水マレイン酸と、これに共重合させるモノマーの割合は、無水マレイン酸1molに対し、共重合させるモノマーの合計が1〜5molの範囲であることが好ましく、さらには1〜3molの範囲が好ましい。無水マレイン酸と、これに共重合させるモノマーは、酢酸エステル、ジオキサンなどの重合を阻害しない有機溶剤(非芳香族系溶媒が好ましい)に溶解させ、アゾビスイソブチロニトリル、ベンゾイルパーオキサイド、ラウロイルパーオキサイドなどのラジカル発生剤を、無水マレイン酸と、これに共重合させるモノマーの合計100質量部に対して、通常0.1〜5質量部、好ましくは0.5〜2質量部の範囲で加え、70℃〜150℃の温度範囲で、2〜10時間反応させることにより共重合体が得られる。
マレイン酸樹脂の平均分子量としては2000〜50000の範囲が好ましく、さらには5000〜30000の範囲が好ましい。
赤外線吸収剤としては、例えば、ジチオール系金属錯体、フタロシアニン系化合物、ジインモニウム化合物等が用いられる。
充填剤としては、例えば硫酸バリウム、タルク、クレー、炭酸カルシウム、水酸化アルミニウムなどが用いられる。
着色剤としては、例えばキナクリドンレッド、イソインドリノンイエロー、フタロシアニンブルー、フタロシアニングリーン、酸化チタン、カーボンブラックなどの公知の着色用顔料などが用いられる。
接着剤層7の塗工方法については特に制限はなく、通常用いられる、グラビア印刷、スプレーコート、フローコート等の方法を用いることができる。なお、本発明の接着剤層を構成する樹脂組成物は、塗工に際し、芳香族系溶媒を使用することなく塗工することができる点が特徴である。
ここで、樹脂含浸紙とは、繊維質基材に樹脂を含浸したものである。繊維質基材としては紙が代表的であるが、この他、不織布、或いはこれらの積層体等でもよい。紙としては、例えば、薄葉紙、クラフト紙、上質紙、リンター紙、バライタ紙、硫酸紙、和紙等が使用される。また、不織布としては、例えば、ポリエステル樹脂、アクリル樹脂、ナイロン、ビニロン、硝子等の繊維からなる不織布が使用される。紙や不織布の坪量は、通常20〜100g/m2程度である。そしてこれらの繊維質基材に対して、アクリル樹脂、スチレンブタジエンゴム、メラミン樹脂、ウレタン樹脂、フタル酸ジアリル樹脂(DAP樹脂)などを添加(抄造後樹脂含浸、又は抄造時に内填)することで樹脂含浸紙となる。これらのうち、密着性の点から、DAP樹脂が好ましい。樹脂の含浸率{=〔(含浸後の坪量−含浸前の坪量)/含浸前の坪量〕×100〔%〕}については、曲加工適性の面から、30〜100%程度が好ましい。
また、木質系材料としては、木質合板、木質単板、パーチクルボード、中密度繊維板(MDF)、高密度繊維板(HDF)等の木質系材料が挙げられる。
なお、被転写体の形状についても特に限定はなく、シート、フィルム、平板、曲面板、棒状板、立体物などいずれの形状にも適用できる。
なお、基材2を剥離するタイミングは、転写圧の解除以降、基材2が剥離時応力で切断や塑性変形をしない程度に冷却し、接着剤層7が冷却や一部進行した硬化反応で固化し転写シート1が被転写体に固着した時点以降に行えばよい。
(評価方法)
MDF基板(大建工業(株)製「テクノウッド」、厚さ2mm)の周囲にDAP含浸紙(富士高分子(株)製「FLX−230BK」)を貼付した材料を用意した。この材料に実施例及び比較例で得られた化粧シートを、転写温度200℃、転写速度7m/分の条件で転写し、化粧板を製造した。このようにして製造した化粧板に関して、以下の項目について評価した。
得られた化粧板について、80℃で2時間加熱し、−20℃で2時間冷却するサイクルを3回繰り返し、デジタルマイクロスコープ(HIROX社製「SH−4500」)を用いて50倍で観察し、微小なクラック(マイクロクラック)の有無を確認した。以下の基準で評価した。
○;マイクロクラックなし
△;若干のマイクロクラックあり
×;マイクロクラックあり
(2)密着性
得られた化粧板の剥離層に18mm幅のセロファンテープ(ニチバン(株)製「セロテープ」)を密着させた後に、45度の方向に剥離を1回行い、以下の基準で評価した。
○;剥離なし
△;若干剥離あり
×;剥離あり
(3)ブロッキング性
得られた化粧板を2枚重ね、49kPa(0.5kg/cm2)の圧力をかけて、40℃で3日間保管した。その後のブロッキング性を以下の基準で評価した。
○;良好
△;PETフィルムに転写シートがわずかに密着するが実用上問題なし。
×;PETフィルムに転写シートが密着する。
基材2として、PET(三菱ポリエステルフィルム(株)製「E−130」、1000mm幅)を用い、その片面にアクリル樹脂をバインダーとし、添加剤としてポリエステルを含有する樹脂組成物を塗工して剥離層3を設けた。剥離層3の厚さは2μmであった。
次いで、剥離層3上に3級アミノ基含有アクリル樹脂及びシリコーン系硬化剤を配合してなる2液硬化型の湿気硬化型シリコーンアクリル樹脂((株)昭和インク工業所製「耐SOL AC剤」)からなるプライマー層4を設けた。プライマー層4の厚さは2μmであった。
その上に、アクリルセルロースをバインダーとし、フタロシアニン、イソインドリノン、及びキナクリドンを主成分とする着色剤を用いて、木目模様の装飾層5をグラビア印刷にて形成した。装飾層5の厚さは2μmであった。
次に、装飾層5上に剥離層3を形成するのに用いたのと同様の2液硬化型アミノ基含有アクリル樹脂を用いてオーバープリント層6を設けた。オーバープリント層6の厚さは2μmであった。
次に、フィルムとした際の破断伸度(明細書本文中に記載した測定条件)が1100%であるウレタン樹脂とマレイン酸樹脂(軟化点130℃)の混合物(ウレタン樹脂/マレイン酸樹脂、マレイン酸樹脂の含有量;33.3質量%、(株)昭和インク工業所製)に、マット剤としてシリカを5.0質量%含有させた樹脂組成物を、上記オーバープリント層6の上にグラビアコーティングし、乾燥後の厚さが13μmとなるように接着剤層7を形成した。このようにして製造した転写シートを上記方法により評価した。結果を第1表に示す。
実施例1において、接着剤層7を構成するウレタン樹脂として、フィルムとした際の破断伸度が1400%であるものを用いたこと以外は実施例1と同様にして転写シートを得、同様に評価した。結果を第1表に示す。
実施例2において、マット剤であるシリカの含有量を3.2質量%としたこと以外は実施例1と同様にして転写シートを得、同様に評価した。結果を第1表に示す。
実施例1において、オーバープリント層6を設けなかったこと以外は、実施例1と同様にして転写シートを得た。実施例1と同様に評価した結果を第1表に示す。
また、本発明の転写シートは、製造過程において、溶媒として芳香族系溶媒を用いることなく製造することができ、環境性能の高い転写シートである。
2.基材
3.剥離層
4.プライマー層
5.装飾層
6.オーバープリント層
7.接着剤層
8.転写層
Claims (7)
- 基材に、少なくとも剥離層、装飾層、オーバープリント層及び接着剤層を含む転写層を積層した転写シートであって、オーバープリント層は接着剤層と接触し、接着剤層はウレタン系樹脂とマレイン酸樹脂を含有し、かつ、接着剤層中のマレイン酸樹脂の含有量が20〜40質量%である転写シート。
- 前記各層のいずれにも芳香族系溶媒を含有しない請求項1に記載の転写シート。
- 前記ウレタン系樹脂の、JIS K7127に準拠した引張試験によって測定した破断伸度が900〜1400%である請求項1又は2に記載の転写シート。
- 前記ウレタン系樹脂がブロッキング防止剤を0.1〜5質量%含有する請求項1〜3のいずれかに記載の転写シート。
- 前記マレイン酸樹脂の軟化点が120〜185℃である請求項1〜4のいずれかに記載の転写シート。
- 剥離層と装飾層の間にプライマー層を有する請求項1〜5のいずれかに記載の転写シート。
- 被転写面が樹脂含浸紙と木質基材の両方を有する基板用である請求項1〜6のいずれかに記載の転写シート。