Abstract

<P>PROBLEM TO BE SOLVED: To provide a double-color developing ink composition which is excellent in fixing properties of colorants, and finely forms profile lines. <P>SOLUTION: A water-base double-color developing ink composition comprises the double-color developing ink composition including at least one pigment (a) selected from a pearl pigment and a metal powder pigment, water (b), at least one water-soluble organic solvent (c) selected from an alcohol having a branched hydrophobic group, a glycol, and a glycol ether, a water-soluble dye (d), and a water-soluble fixative (e) composed of a processed starch. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

  The present invention, when written on a permeable porous substrate such as paper, has a double-colored handwriting consisting of a center line having a metallic luster and / or a pearl luster and a contour line surrounding the center line. The present invention relates to an aqueous dual color ink composition which gives a handwriting with a border. Furthermore, the present invention relates to an ink composition for a writing instrument comprising such an aqueous double color ink composition, particularly an ink composition for an aqueous ballpoint pen, and a writing instrument using such an aqueous double color ink composition, in particular, It relates to a water-based ballpoint pen.

  Conventionally, the aqueous double color ink composition includes, for example, a metal powder pigment such as aluminum powder, a water-soluble dye, water, and a permeable organic solvent (see Patent Documents 1 to 3). When writing with the ink composition on a porous substrate such as paper that can penetrate or absorb the solvent, the metal powder pigment is immediately captured in situ on the substrate with which they are in contact, A center line having a metallic luster is formed as written, and the dye penetrates and diffuses in the substrate together with the permeable organic solvent around the center line, so to speak, the center line exudes from the center line. A band-like outline is formed so as to enclose, thus giving a handwriting with double coloring, ie a handwriting with a border. Such a double color ink composition is used as an ink composition for marking pens, sign pens, water-based ballpoint pens and the like.

  However, as a first problem in the conventional aqueous double color ink composition, a water-soluble resin such as carboxymethyl cellulose sodium salt or polyvinyl alcohol is used as a fixing agent in order to improve the fixability of handwriting ( For example, in order to use an aqueous dual color ink composition as an ink composition for an aqueous ball-point pen, the ink composition is used with a relatively high viscosity. In this case, according to the ink composition, during the writing, the fixing agent tends to hinder the formation of the contour line of the handwriting, and the desired double color development effect cannot often be obtained. Sometimes.

  Although it is already known that a pearl pigment is used as a pigment and a water-soluble rosin or a styrene-acrylic acid copolymer is used as a fixing agent in a normal ink composition that is not double color developing (Patent Document) 4), these fixing agents also inhibit the formation of contour lines when used as fixing agents in water-soluble dual color ink compositions.

  The second problem is that, in the conventional double color ink composition, the center line of the handwriting is not affected by the coloring of the dye and is formed by the pigment, and the outline is clearly distinguished from the center line. As described above, a metal powder pigment having a strong hiding power is used as the pigment. Therefore, according to such a double color ink composition, the center line of the handwriting exhibits the color that the metal powder pigment originally has, regardless of the dye used, but it cannot be denied that the gloss is insufficient. . Therefore, recently, an aqueous double color ink composition using a pearl pigment as a pigment together with or in place of the metal powder pigment has been proposed (see Patent Document 5).

However, conventionally, in the double color ink composition using a pearl pigment, since the pearl pigment is less concealed than the metal powder pigment, the center line of the handwriting is affected by the color of the dye used, There is a problem that it is difficult to obtain a clear double coloring effect. Of course, even in the past, for example, when a light color dye is used and the outline is formed in a light color, the pearl pigment is inferior in concealment, but the center line of the handwriting is almost entirely the original pearl pigment. In this case, the contour line is lightly colored and formed temporarily. However, on the contrary, in order to form the outline of the handwriting in a dark color, when using a dark color as a dye, for example, black, amber, brown, dark green, etc., a double color using a conventional pearl pigment is used. In the color ink composition, the contour line is clearly formed in dark color by such a dye, but the center line is affected by the dark dye, so the pearl gloss of the center line and the dark contour line are Are difficult to distinguish visually and clearly, and there is a problem that it is difficult to obtain a clear double coloring effect. That is, the dark dye has a detrimental effect on the color development of the pearl pigment forming the center line, and the center line is not clearly formed by the pearl pigment.
JP 60-231777 A JP 61-123684 A JP 2000-129188 A Japanese Patent Laid-Open No. 10-245517 JP 2007-31558 A

  The present invention has been made in order to solve the above-mentioned problems in the conventional aqueous double color ink composition. First, the present invention has a clear outline even if it has a relatively high viscosity. An object of the present invention is to provide an aqueous double color ink composition that forms lines and has excellent fixability.

  Furthermore, in the present invention, secondly, in a double color ink composition using a pearl pigment as a pigment, a dark color is used as a dye to form a dark outline of a handwriting. The pearl pigment that forms the center line is not detrimentally affected by the dye, but rather is well-colored to form a center line with a strong pearl luster and is clearly distinguished from such a center line An object of the present invention is to provide an aqueous dual color ink composition capable of forming a contour line.

  Another object of the present invention is to provide an ink composition for a writing instrument comprising the aqueous double color ink composition as described above, in particular, an aqueous ballpoint ink composition. An object of the present invention is to provide a writing instrument using the color developing ink composition, particularly an aqueous ballpoint pen.

According to the present invention,
(A) at least one pigment selected from pearl pigments and metal powder pigments;
(B) water,
(C) at least one water-soluble organic solvent selected from alcohols having branched hydrophobic groups, glycols and glycol ethers,
There is provided a water-soluble dual color ink composition comprising (d) a water-soluble dye, and (e) a water-soluble fixing agent comprising processed starch.

Further, according to the present invention, as a preferred embodiment, the color characteristics of the pearl pigment in which the color difference ΔE ^* between the white background and the black background is in the range of 30 to 80, and the L ^* in the white background is 80 or more. There is provided an aqueous dual color ink composition having the formula:

  Furthermore, according to the present invention, an ink composition for a writing instrument comprising the above-described aqueous double color ink composition, particularly an aqueous ball-point pen ink composition, and an aqueous double color ink composition as described above are used. Writing instruments, particularly aqueous ballpoint pens, are provided.

  Since the aqueous double color ink composition according to the present invention uses processed starch as a fixing agent, even if it has a relatively high viscosity as in the case of containing a thickener, In addition to excellent fixability of the handwriting on the dye, it is possible to provide a handwriting having a clear contour line with excellent penetration and diffusion of the dye into the substrate. Furthermore, the aqueous double color ink composition according to a preferred embodiment of the present invention is clearly distinguished from a centerline having a colored and strong pearly luster, even when a dark color dye is used. Handwriting consisting of contour lines can be given.

The aqueous double color ink composition according to the present invention comprises:
(A) at least one pigment selected from pearl pigments and metal powder pigments;
(B) water,
(C) at least one water-soluble organic solvent selected from alcohols having branched hydrophobic groups, glycols and glycol ethers,
(D) It contains a water-soluble dye, and (e) a water-soluble fixing agent made of processed starch.

  In the aqueous dual color ink composition according to the present invention, at least one selected from pearl pigments and metal powder pigments is used as the pigment. The pigment is fixed to the substrate by the fixing agent to form the center line of the handwriting.

  Of the pigments, pearl pigments are not particularly limited as long as they are excellent in radiance, and any conventionally known pearl pigment is used. For example, pearl pigments such as fish scale foil, basic carbonate, and bismuth oxychloride are also used. Preferably, the surface of natural mica or synthetic mica is coated with a metal oxide such as titanium oxide or iron oxide. Is used.

  Furthermore, the pearl pigment used in the aqueous dual color ink composition according to the present invention preferably has an average particle size in the range of 5 to 60 μm. When the average particle diameter of the pearl pigment is smaller than 5 μm, the pearl luster is weak. On the other hand, although the upper limit of the average particle diameter of the pearl pigment depends on the use of the dual color ink composition according to the present invention, for example, in the case of an ink composition for a ballpoint pen, it is usually 60 μm. When the average particle diameter of the pearl pigment exceeds 60 μm, the ink discharge becomes worse.

  According to the present invention, various commercial products are used as the pearl pigment as described above. Examples of such a pearl pigment include Iriodin 100 (particle size: 10 to 60 μm, silver), 103 (10 to 60 μm). , Silver), 201 (5-25 μm, pearl color), 221 (5-25 μm, pearl color), 231 (5-25 μm, pearl color), 300 (10-60 μm, gold color), 302 (same as above) 5-25 μm, gold), 323 (5-25 μm, gold), 504 (10-60 μm, red), 524 (5-25 μm, red), 502 (10-60 μm, bronze), 520 ( Iriodins (manufactured by Merck Japan) such as 5-25 μm, bronze), ULTIMICA SB-100 (5-30 μm, silver), SD-100 (10-60) m, silver), RYB-100 (same as 5-30 μm, gold), RYD-100 (10-60 μm, gold), ULTIMICAs (manufactured by Nihon Koken Kogyo Co., Ltd.), TAYCA PEARL TP-500 ( TAYCA PEARLs (manufactured by Teika Co., Ltd.) such as 10 to 70 [mu] m, silver) and TPX-720 (7 to 45 [mu] m, silver). These pearl pigments may be used alone or in combination of two or more.

  In the aqueous double color ink composition according to the present invention, as the metal powder pigment, any conventionally known metal powder pigment can be used without particular limitation as long as it has a metallic luster. For example, an aluminum powder pigment and a brass powder pigment can be mentioned. Examples of the aluminum powder pigment include al pastes such as Alpaste WJP-U75C, WE1200, WXM7675, and WXM0630 (manufactured by Toyo Aluminum Co., Ltd.), 1110W, 2172SW (manufactured by Showa Aluminum Co., Ltd.), AW-808C, and AW7000R. (Made by Asahi Kasei Co., Ltd.). Examples of the brass powder pigment include BS-605, BS-607 (manufactured by Toyo Aluminum Co., Ltd.), bronze powder P-555, P-777 (manufactured by Nakajima Metal Foil Powder Co., Ltd.), and the like. Can do.

  In addition to the above, colored aluminum powder pigments such as F500RG-W, F500BG-W, F701GR-W, and F701RE-W (manufactured by Showa Aluminum Co., Ltd.) are also used. These metal powder pigments may be used alone or in combination of two or more. The particle size of the metal powder pigment to be used can be appropriately selected according to the design of the handwriting.

  In the present invention, the pearl pigment and the metal powder pigment may be used alone or in combination. In any case, according to the present invention, the pigment content of the ink composition is appropriately determined according to the type of pigment to be used, etc., but is preferably in the range of 4 to 20% by weight as the solid content. More preferably, it is in the range of 5 to 15% by weight. When the content of the pigment in the ink composition exceeds 20% by weight, the solid content concentration in the ink composition becomes high, which may adversely affect the viscosity and fluidity of the ink composition. However, when the amount is less than 4% by weight, the concealing property by the pigment in the formed handwriting becomes very weak and there is a possibility that the desired double color development effect cannot be obtained.

  When the pearl pigment and the metal powder pigment are used in combination, the weight ratio is appropriately determined according to the design required for the handwriting, the type of the pigment used, etc., preferably, the metal is based on 100 parts by weight of the pearl pigment. It is the range of 1-50 weight part of powder pigments, More preferably, it is the range of 2-30 weight part. When 50 parts by weight or more of the metal powder pigment is used with respect to 100 parts by weight of the pearl pigment, the obtained ink composition does not give a handwriting having a high gloss feeling inherent to the pearl pigment. On the other hand, when the amount is less than 1 part by weight, the hiding effect based on the metal powder pigment in the handwriting is insufficient, and the center line is easily affected by the color of the contour line. Depending on the color of the line, there is a possibility that the center line looks completely different.

In particular, according to the present invention, as a pearl pigment, a dye having a color difference ΔE ^* between a white background and a black background in a range of 30 to 80 and L ^{* on} a white background of 80 or more is used as a dye. To obtain a dual color ink composition that gives a bordered handwriting consisting of a central line having a color and strong pearly luster and a contour line clearly distinguishable from this even when a dark color is used Can do. The pearl pigment having the color characteristics described above has a feature that the start on a white background is very small.

The L ^* a ^* b ^* color system is known as one of the color systems defined by the CIE (International Commission on Illumination). In this color system, L ^* indicates the lightness of the color. A larger value means white, and a smaller value indicates black. The perfect white L ^* is 100. a ^* and b ^* indicate chromaticity representing hue and saturation. That is, according to the L ^* a ^* b ^* color system, one color has one coordinate (L ^* , a ^* , b ^* ), where the first color (L ₁ ^* , a ₁ ^* , b ₁ ^* ) and the second color (L ₂ ^* , a ₂ ^* , b ₂ ^* ) is the distance between the two colors, ie, the following equation (1)
ΔE = ((L ₁ ^* −L ₂ ^* ) ² + (a ₁ ^* −a ₂ ^* ) ² + (b ₁ ^* −b ₂ ^* ) ² ) ^1/2 (1)
It is represented by

  As described above, when a dark dye is used as a dye, by using a pearl pigment having the above-mentioned color characteristics, a dye is used in the center line portion as in the conventionally known double color ink composition. Rather than concealing the color by pigment, rather than using the color developed by the dye at the center line, the pearl pigment gives the center line a strong chromatic color with good color developability, and the above dark dye It is possible to obtain an aqueous dual color ink composition that gives a handwriting with a clear, dark and visually distinct outline relative to the centerline.

  Examples of the pearl pigment having the color characteristics include 201, 221 and 231 described above.

  In the dual color ink composition according to the present invention, the water-soluble organic solvent has a function of diffusing and penetrating the dye in the ink composition into the base material to form a contour line around the center line. In the present invention, as such a water-soluble organic solvent, at least one selected from alcohols having a branched hydrophobic group, glycols and glycol ethers is used. Here, the structure having “branched hydrophobic group” means a structure in which a hydrophobic group is bonded to the main chain as a side chain in a chain compound. The hydrophobic group is an alkyl group having 1 to 4 carbon atoms, preferably a methyl group or an ethyl group. One or two or more hydrophobic groups may be present in the molecule, and when two or more hydrophobic groups are present, they may be the same as or different from each other.

  Among the above water-soluble organic solvents, aliphatic saturated alcohols having 4 to 6 carbon atoms are preferably used as alcohols having a branched hydrophobic group. Examples of such alcohols include isobutanol, s-butanol, t-butanol), isopentanol, s-pentanol, t-pentanol, 3-pentanol, 3-methyl-2-butanol, and 2-methyl. Examples thereof include -1-butanol, 2-ethylbutanol, 4-methyl-2-pentanol and the like.

  Examples of glycols and glycol ethers having a branched hydrophobic group include 1,3-octylene glycol (2-ethyl-1,3-hexanediol) and hexylene glycol (2-methyl-2,4- Pentanediol), dipropylene glycol, tripropylene glycol, polypropylene glycol, poly (oxyethylene-oxypropylene) derivatives, ethylene glycol monoisopropyl ether, propylene glycol monobutyl ether, propylene glycol monoethyl ether, dipropylene glycol monobutyl ether, dipropylene Examples include glycol monopropyl ether, dipropylene glycol monoethyl ether, and dipropylene glycol monomethyl ether.

  According to the present invention, among the various organic solvents described above, dipropylene glycol monopropyl ether, dipropylene glycol monomethyl ether or hexylene glycol is particularly preferably used.

  The double color ink composition according to the present invention contains the water-soluble organic solvent in an amount of usually 1 to 50% by weight, preferably 5 to 30% by weight. In the ink composition, when the content of the soluble organic solvent exceeds 50% by weight, the solubility of the water-soluble resin is lowered and may be precipitated in the ink composition. On the other hand, when the content of the water-soluble organic solvent is less than 1% by weight, the dye does not sufficiently permeate and diffuse through the base material when written, and it becomes difficult to obtain a handwriting having a clear border. . In addition, as the amount of the water-soluble organic solvent increases with respect to water, a wider outline is formed, but at the same time, the stability of the ink composition is deteriorated. Therefore, in the present invention, the water / water-soluble organic solvent weight ratio is preferably in the range of 1.5 to 4.

  In the present invention, the water-soluble dye is mainly a colorant that forms a contour of a handwriting, and is usually an anthraquinone dye, diphenylmethane dye, triphenylmethane dye, xanthene dye, acridine dye, 1: At least one selected from a type 1 metal complex dye, a 1: 2 type metal complex dye, and a copper phthalocyanine dye is used. Among these, in the present invention, at least one of diphenylmethane dyes, triphenylmethane dyes, xanthene dyes, acridine dyes and metal complex dyes is preferably used.

  Any anthraquinone dye may be used as long as it has an anthraquinone skeleton, and includes an anthraquinone derivative and an anthrone derivative. Accordingly, specific examples of anthraquinone dyes include C.I. I. Acid Blue 27, C.I. I. Acid Blue 43, C.I. I. Acid Green 25, C.I. I. Basic Violet 25, C.I. I. Basic Blue 60, C.I. I. Modern Red 11, C.I. I. Acid Red 83, C.I. I. Direct Green 28, C.I. I. For example, Modern Blue 48 may be used.

  Specific examples of the diphenylmethane dye include C.I. I. Basic Yellow 2, C.I. I. Basic Yellow 3, C.I. I. Basic Yellow 37 etc. can be mentioned. Specific examples of triphenylmethane dyes include C.I. I. Acid Blue 90, C.I. I. Acid Blue 104, C.I. I. Acid Gren 16, C.I. I. Acid Violet 49, C.I. I. Acid Red 9, C.I. I. Basic Blue 7, C.I. I. Acid Violet 1, C.I. I. Acid Red 289, C.I. I. Direct Blue 41, C.I. I. Modern Blue 1, C.I. I. For example, Modern Violet 1 may be mentioned.

  Specific examples of the xanthene dye include C.I. I. Acid Yellow 73, C.I. I. Acid Yellow 74, C.I. I. Acid Red 52, C.I. I. Acid Violet 30, C.I. I. Basic Red 1, C.I. I. Basic Violet 10, C.I. I. Modern Red 27, C.I. I. For example, Modern Violet 25. Specific examples of acridine dyes include C.I. I. Basic Yellow 6, C.I. I. Basic Yellow 7, C.I. I. Basic Orange 14, C.I. I. Basic Orange 15 and the like can be mentioned.

  The metal complex dye includes a normal metal complex dye, a dye containing a metal, and a dye capable of coordinating with the metal. Examples of the dye capable of coordinating with a metal include azo dyes having a hydroxyl group, a carboxyl group, an amino group, and the like. Examples of such azo dyes include C.I. I. Modern Red 30, C.I. I. Modern Yellow 3, C.I. I. Modern Green 15, C.I. I. For example, Modern Blue 13 may be used.

  According to the present invention, among these metal complex dyes, copper phthalocyanine dyes, 1: 1 type metal complex dyes or 1: 2 type metal complex dyes are particularly preferably used. Specific examples of copper phthalocyanine dyes include C.I. I. Direct Blue 86 or the like is a specific example of the 1: 1 type metal complex dye, for example, C.I. I. Acid Yellow 54, C.I. I. Acid Orange 74, C.I. I. Acid Red 186, C.I. I. Acid Violet 56 etc., as a specific example of 1: 2 type metal complex dye, for example, C.I. I. Acid Yellow 59, C.I. I. Acid Black 60, C.I. I. Acid Red 296, C.I. I. Acid Blue 167 and the like can be mentioned respectively.

  In the present invention, the content of the water-soluble dye in the ink composition is appropriately determined according to the type of the water-soluble dye and the like, but is usually in the range of 0.05 to 5% by weight, preferably 0. 0.1 to 3% by weight. When the content of the water-soluble dye in the ink composition is more than 5% by weight, the viscosity and fluidity of the resulting ink composition may be adversely affected. On the other hand, when the ratio of the water-soluble dye in the ink composition is less than 0.05% by weight, it is difficult for the resulting ink composition to give a handwriting having a desired contour line.

  In the aqueous dual color ink composition according to the present invention, processed starch is used as a water-soluble fixing agent. Processed starch refers to derivatives obtained by adding functional groups to raw starches such as potato starch, corn starch, tapioca starch, and wheat starch, as well as those obtained by subjecting raw starch decomposition products and raw starch to physical treatment with heat, etc. .

  Examples of starch derivatives having a functional group added to the anhydrous glucose residue of starch include hydroxypropyl starch (Penon JE-66, Piostarch K5, etc.), carboxymethyl starch (Cypro Gum F-500, Cypro Gum M-800A). Etc.), etherified starch represented by cationic starch (Exel DH, Petrosize J, etc.), starch acetate (ZP-2, Z-100, etc.), octenyl succinic acid starch (natural Nisque, octie etc.), phosphate starch ( Cross-linked starch, grafted starch (Petrosize L-2B) typified by esterified starch typified by bribaine), distarch phosphate (SELEX, GFM, etc.), glycerol distarch (Longam CE-3, LeoTac ML, etc.) , Petrocoat C-8 etc.) It can be mentioned.

  Starch degradation products include white dextrin (red ball dextrin MF-30, No. 4-C, etc.), yellow dextrin (red ball dextrin No. 102S, ND-S, etc.), British gum (red ball British gum No. 69, APA). And the like, enzyme-modified dextrins generically called maltodextrin (Amicol SQ, Penon PKW, etc.), acid-decomposed starch, oxidized starch and the like. All the modified starches exemplified above can be obtained from Nippon Star Chemical Co., Ltd. Other examples of starch derivatives include unmodified pregelatinized starch and modified pregelatinized starch. These starch derivatives may be used alone or in combination of two or more.

  In the present invention, among these processed starches, those having a low viscosity of the aqueous solution are preferable, and etherified starch or enzyme-modified dextrin is particularly preferably used. As a commercial item, Penon JE-66 mentioned above, Penon PKW, Amicol SQ (all are the Nissho Chemical Co., Ltd. product) etc. can be mentioned, for example.

  In particular, according to the present invention, among the above-described processed starches, those having an amylopectin skeleton content of 90% or more are preferably used. Such a processed starch has a low amylose content, so that aging hardly occurs, and in particular, the obtained ink composition has excellent low-temperature storage stability. Furthermore, according to the present invention, among such processed starches, etherified starch having a degree of etherification in the range of 3 to 10% is preferably used. The degree of etherification in the etherified starch represents the ratio of the total molecular weight of the functional group substituting the hydroxyl group of the glucose residue to the molecular weight per molecular chain of starch. Such an etherified starch has high dissolution stability in a system in which water and a large amount of a water-soluble organic solvent are mixed. Of these, hydroxypropylated starch is preferably used. Hydroxypropylated starch having a hydroxypropylation degree exceeding 10% provides an ink composition having excellent low-temperature stability, however, such an ink composition is stable at high temperatures exceeding 50 ° C. Getting worse. Hydroxypropylated starch having a hydroxypropylation degree of less than 3% hardly obtains the above effects.

  In the water-based dual color ink composition according to the present invention, the content of the water-soluble fixing agent is appropriately determined according to the content of the pigment used in addition to the type thereof, and is usually 0.5 to 15 wt. %, Preferably 1 to 10% by weight. When the content of the water-soluble fixing agent in the ink composition exceeds 15% by weight, the viscosity of the resulting ink composition becomes too high, and writing may be difficult. However, when the content of the water-soluble fixing agent in the ink composition is less than 0.5% by weight, the effect of fixing the pigment may not be obtained.

  Processed starch is excellent in solubility in water, but its solubility in water-soluble organic solvents is not so good or hardly soluble in water-soluble organic solvents. Therefore, when writing on a base material with an ink composition containing such processed starch as a fixing property, the processed starch penetrates and diffuses into the base material a water-soluble organic solvent containing a dye, and surrounds the center line. In most cases, it remains together with the pigment on the base material with little effect on the action of the water-soluble organic solvent that forms the contour line, and exhibits a good effect as a fixing agent. On the other hand, as described above, the processed starch hardly affects the action of the water-soluble organic solvent containing the dye to permeate and diffuse into the substrate, so that the water-soluble organic solvent forms a clear outline with the dye.

  On the other hand, when a water-soluble fixing agent having excellent solubility in a water-soluble organic solvent is used, the viscosity increases due to the dissolution of a large amount of the water-soluble fixing agent in the water-soluble organic solvent. As a result of suppressing the diffusion and penetration of the dye into the base material, it seems that the formation of the contour line is inhibited.

  The aqueous dual color ink composition according to the present invention may contain a water-soluble thickener in order to appropriately adjust the viscosity according to the application. For example, when the aqueous double color ink composition according to the present invention is used as an aqueous ballpoint ink composition, it is preferable to add a thickener and adjust the viscosity to a range described later. In the present invention, a polysaccharide gum is preferably used as such a water-soluble thickener. According to the present invention, among such polysaccharide gums, at least one selected from rhamzan gum, xanthan gum, welan gum, gellan gum, pullulan, xanthan gum, guar gum, locust bean gum and pectin is preferably used. In the present invention, the polysaccharide gum includes not only natural products but also processed products or derivatives thereof. However, in addition to the above-mentioned polysaccharide gum, according to the present invention, colloidal polysaccharides such as pectin, proteins such as casein and gelatin, and synthetic water-soluble resins such as sodium polyacrylate are also included. It can be used as a water-soluble thickener.

  The content of the thickener in the ink composition is appropriately determined according to the intended use and required characteristics of the ink composition to be obtained.For example, when the ink composition is used as a water-based ballpoint pen, the viscosity is: Usually, it is in the range of 0.05 to 0.5% by weight, and preferably in the range of 0.1 to 0.3% by weight. When there is too much content of a thickener, the viscosity of the ink composition obtained will be too high, the outflow of the ink composition from a nib will worsen, and it will be inferior to writing property. However, when the content of the thickener is too small, the viscosity of the resulting ink composition is too low, and the pigment in the ink composition is inferior in dispersion stability, and is easily clogged with the pen tip. Become.

  The aqueous dual color ink composition according to the present invention may contain urea or a derivative thereof so as to have a long-term storage stability at a low temperature. Examples of urea derivatives include methylurea, dimethylurea, tetramethylurea, ethylurea, tetraethylurea, hydroxyethylurea, dihydroxyethylurea, ethyleneurea, dimethylolurea, sulfonylurea, thiourea, monomethylthiourea, dimethylthiourea, and urea. An ethylene oxide adduct etc. can be mentioned. Of these, urea or dimethylurea is preferably used according to the present invention.

  According to the present invention, such urea or urea derivative is appropriately determined according to the type of the water-soluble fixing agent, the amount of the water-soluble organic solvent used, and the like. It is in the range of wt%, and preferably in the range of 5-15 wt% wt%. When the content of urea or urea derivative in the ink composition exceeds 20% by weight, the resulting ink composition has a relatively insufficient water content, so the viscosity of the ink composition may be too high. In addition, when used as an ink composition for a ballpoint pen, the handwriting may be extremely difficult to dry. On the other hand, when the content of urea or urea derivative in the ink composition is less than 2% by weight, the resulting ink composition has insufficient long-term storage stability at low temperatures or no long-term storage stability, and the ink composition Components, particularly processed starch, which is a fixing agent, may be separated.

  When the aqueous double color ink composition according to the present invention is used, for example, as an ink composition for a ballpoint pen, the pen tip does not dry even when the cap is removed and the ballpoint pen is left standing. A wetting agent comprising a polyhydric alcohol or a derivative thereof can be included as necessary so that the ink composition flows out smoothly from the nib and does not cause handwriting. As said polyhydric alcohol or its derivative (s), ethylene glycol, diethylene glycol, propylene glycol, glycerin, polyethylene glycol etc. can be mentioned, for example. Of these, ethylene glycol or glycerin is preferably used. Such a wetting agent is usually used in the range of 10% by weight or less, preferably in the range of 3 to 8% by weight, based on the ink composition.

  The aqueous double color ink composition according to the present invention can contain other additives as long as it does not interfere with the effects of the ink composition. Such additives include, for example, lubricants such as polyoxyethylene alkali metal salts, dicarboxylic amides, phosphate esters, N-oleyl sarcosine salts, benzotriazoles, tolyltriazoles, dicyclohexylammonium nitrates, and the like. Examples include rust preventives, benzoisothiazoline-based, pentachlorophenol-based, preservatives such as cresol, and antifungal agents. In addition to these, various dispersants, surfactants, thickeners and the like can be further exemplified.

  When the aqueous double color ink composition according to the present invention is used for an aqueous ballpoint pen, the viscosity measured at ELD viscometer 3 ° (R14) cone 0.5 rpm (20 ° C.) is in the range of 2000 to 10,000 mPa · s. It is preferable. By providing the viscosity in the above range, it is possible to obtain excellent temporal stability and writing property as an aqueous ball-point pen ink composition. In order to make the aqueous dual color ink composition according to the present invention have a viscosity within the above range, the above-mentioned water-soluble thickener is mainly added to the ink composition in an appropriate amount, and water in the ink composition is also added. Adjust the amount.

  The aqueous double color ink composition according to the present invention is not particularly limited in its production method. In the production of the ink composition, it can be produced by a conventionally known method such as dispersion, defoaming or filtration. As an example, after mixing and stirring water, a water-soluble dye and a pigment, a fixing agent and, if necessary, a thickening agent are blended therein, and then a water-soluble organic solvent and various kinds of water as necessary. It can be obtained by blending the additives and mixing them uniformly. In each step, mixing and stirring may be performed using a general stirring device known so far, such as a dissolver, a mixer, and a kneader.

  The aqueous double color ink composition according to the present invention can be used as an ink composition for various writing instruments such as markers and sign pens, and as described above, it is particularly preferably used as an ink composition for ballpoint pens. Can do. The writing instrument according to the present invention is the same as a conventionally known writing instrument such as a marker, a sign pen, and an aqueous ballpoint pen, except that the ink composition to be used is the above-described aqueous double color ink composition.

  Therefore, for example, in the water-based ballpoint pen according to the present invention, for example, the same ink storage tube as that in the past may be manufactured as it is using a conventionally known material. Therefore, the ink storage tube may be made of a synthetic resin pipe such as polyethylene or polypropylene, or may be made of a metal pipe.

  Also, the ballpoint pen tip is the same as that for water-based ballpoint pens known so far, but according to the present invention, the difference between the ball diameter and the inner diameter of the ball house is used. Is preferably 0.03 mm or more, and preferably a ballpoint pen tip in the range of 0.03 to 0.07 mm. The difference corresponds to the distance at the point where the distance between the ball and the inner surface of the ball house is closest. The difference between the ball diameter and the ball house inner diameter of a conventional ballpoint pen tip of a normal ballpoint pen is usually about 0.01 to 0.02 mm. However, in the ballpoint pen according to the present invention, as described above, 0.03 mm or more. By providing such a large difference, it is possible to more reliably obtain a desired double color forming effect by the aqueous double color ink composition according to the present invention. When assembling the ballpoint pen using various parts including the ink containing tube and the ballpoint pen tip, a conventionally known ordinary method may be used.

  Hereinafter, the present invention will be described more specifically by showing comparative examples together with examples. However, the present invention is not limited to these.

Examples 1-6 and Comparative Examples 1-6
Each of the components (% by weight) shown in Table 1 was stirred for 2 hours at room temperature using a desper to prepare aqueous double color ink compositions. Each component shown in Table 1 is as follows.

Pigment 1: Iriodin 323 (Merck's metal oxide-coated mica)
Pigment 2: Aluminum powder pigment (Alpaste WXM0630 manufactured by Toyo Aluminum Co., Ltd.)
Water-soluble organic solvent: Dipropylene glycol monomethyl ether Water-soluble dye 1: Acid Red 289
Water-soluble dye 2: Acid Green 16
Thickener: Ramzan gum (K7C233 manufactured by Sanki Co., Ltd.)
Fixing agent 1: Enzyme-modified dextrin (Penon PKW manufactured by Nissho Chemical Co., Ltd.)
Fixing agent 2: Hydroxypropyl starch (Penon JE-66 manufactured by Nissho Chemical Co., Ltd.)
Fixing agent 3: Polyvinyl alcohol (Kuraray PVA-204)
Fixing agent 4: Polyvinylpyrrolidone (Pitzkol K-15, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.)
Antiseptic: Proxel XL-2 manufactured by Arch Chemicals
Antifungal agent: Coatside H manufactured by Takeda Pharmaceutical Co., Ltd.

  After filling each ink composition of Examples 1 to 6 and Comparative Examples 1 to 6 shown in Table 1 into a polypropylene ink containing tube having a stainless ball pen tip having a ball made of ceramics attached to one end, silicone oil A ballpoint pen refill was prepared by filling an ink backflow preventive body formed by gelation. Next, after attaching a ballpoint pen refill to the ballpoint pen body and attaching a cap, the air in the tube was removed by a centrifuge, and finally a tail plug was attached to obtain a ballpoint pen.

  A straight line was drawn as a handwriting on Kent paper at a speed of 7 cm / second using the ballpoint pens produced in the above Examples and Comparative Examples, and the double coloring property and fixing property of the handwriting were evaluated according to the following criteria. The results are shown in Table 1.

  Double color development was visually evaluated according to the following criteria. That is, when the contour line is clearly recognized, A, when the contour line is recognized but B is unclear, and when the contour line is hardly recognized, C.

  The fixability was evaluated by the following criteria for the degree of peeling of the handwriting by rubbing with a finger after the handwriting was sufficiently dried. That is, A when the film hardly peeled off, B when the handwriting remained, and C when completely handwritten.

  As is apparent from the results shown in Table 1, the ink compositions according to Comparative Examples 1 to 6 are incompatible with the dual color developability and the fixability, and the better the fixability, the lower the double color developability. In addition, the better the double color development, the poorer the fixability. On the other hand, in the ink compositions according to Examples 1 to 6, double color development and fixing properties are compatible.

Examples 7 to 10 and Reference Examples 1 to 5
Each of the components (% by weight) shown in Table 2 was stirred for 2 hours at room temperature using a desper, to prepare aqueous double color ink compositions. Each component shown in Table 2 is as follows. However, the components not described are the same as those described in Table 1.

Water-soluble dye: Acid Red 289
Water-soluble organic solvent 1: Dipropylene glycol monomethyl ether Water-soluble organic solvent 2: Ethylene glycol fixing agent 1: Enzyme-modified dextrin (Penon PKW manufactured by Nissho Chemical Co., Ltd.)
Fixing agent 2: Hydroxypropyl starch (Penon JE-66 manufactured by Nissho Chemical Co., Ltd.)

  Using each of the ink compositions of Examples 7 to 10 and Reference Examples 1 to 5 shown in Table 2, a ballpoint pen was obtained in the same manner as in the above example. The ink composition was evaluated for its low-temperature storage stability as well as its fixability and fixability. The results are shown in Table 2.

  The low temperature storage stability was evaluated according to the following criteria by observing the appearance of the ink composition after storing the ballpoint pen in a refrigerator at a temperature of 5 ° C. for 1 month. That is, A when the ink composition was not changed, B when the ink composition was slightly separated, and C when the ink composition was completely separated.

  Although all the ink compositions according to Reference Examples 1 to 5 were excellent in double color development and fixing properties, separation of components was observed when stored at a low temperature. Moreover, even if there is little addition amount of a dimethyl urea, it has shown that the effect is not enough. On the other hand, the ink compositions according to Examples 7 to 10 are excellent in all of double coloring property, fixing property and low temperature storage stability.

Examples 11-14 and Reference Examples 6-11
Each of the components (% by weight) shown in Table 3 was stirred for 2 hours at room temperature using a desper, to prepare aqueous double color ink compositions. Each component shown in Table 3 is as follows. However, the components not described are the same as those described in Table 1. The following hydroxypropyl starch was used as the water-soluble fixing agent.

Water-soluble dye: Acid Red 289
Fixing agent 1: 98% amylopectin skeleton content, 4.5% hydroxypropylation degree
Fixing agent 2: amylopectin skeleton content 98%, hydroxypropylation degree 6.3%
Fixing agent 3: amylopectin skeleton content 98%, hydroxypropylation degree 8.6%
Fixing agent 4: amylopectin skeleton content 79%, hydroxypropylation degree 2.0%
Fixing agent 5: amylopectin skeleton content 79%, hydroxypropylation degree 6.5%

  Using each of the ink compositions of Examples 11 to 14 and Reference Examples 6 to 11 shown in Table 3, a ballpoint pen was obtained in the same manner as in the above example. In addition to the properties and fixability, the low-temperature storage stability of the ink composition was examined in more detail. The results are shown in Table 3. The low temperature storage stability was evaluated based on the same criteria as described above by observing the appearance of the ink composition after storing the ballpoint pen in a refrigerator at 5 ° C. for one month in a freezer at 0 ° C. or −10 ° C.

  All of the ink compositions according to Reference Examples 6 to 11 are excellent in double color development and fixing properties, but are inferior in low-temperature storage stability. In particular, all inks when stored in a freezer at −10 ° C. Separation was seen in the composition. It is shown that even if the amount of dimethylurea added is large, the effect is not sufficient.

  On the other hand, the ink compositions according to Examples 11 to 14 are not only excellent in double colorability and fixing property, but also when stored in a freezer such as a temperature of 0 ° C. or −10 ° C. Excellent stability.

Examples 15-17
Each of the components (% by weight) shown in Table 4 was stirred for 2 hours at room temperature using a desper to prepare aqueous double color ink compositions. Each component shown in Table 4 is as follows. However, the components not described are the same as those described in Table 1.

For the pearl pigment used, the color difference ΔE ^* between the white background and the black background and L ^* on the white background are shown. Each pearl pigment is dispersed in nitrocellulose lacquer (Nihon Paint Co., Ltd. 2210 Clear) at a concentration of 10% by weight, applied to a white background and black with a 20 μm wire bar, and a color difference colorimeter CR manufactured by Minolta Co., Ltd. Using -30, the color difference ΔE ^* between the white background and the black background and the L ^* on the white background were measured. For the white and black backgrounds, concealment rate test papers manufactured by Nippon Test Panel Co., Ltd. were used. The pearl pigments used have a white to milky pearl color per se, and have a white to slightly yellow color when applied to a white background.

Pearl pigment 1: Iriodin 201 (ΔE ^* = 36.4, L ^* = 90.6)
Pearl pigment 2: Iriodin 221 (ΔE ^* = 56.8, L ^* = 90.6)
Pearl pigment 3: Iriodin 231 (ΔE ^* = 34.8, L ^* = 90.6)
Dye aqueous solution: Black dye (BONJET BLACK 256-L (manufactured by Orient Chemical Co., Ltd., 13% by weight aqueous solution)
Fixing agent: Modified dextrin (Penon PKW manufactured by Nissho Chemical Co., Ltd.)

  Table 4 shows the viscosities of the ink compositions of Examples 15 to 17 measured at an ELD viscometer 3 ° (R14) cone of 0.5 rpm (20 ° C). Moreover, the ball-point pen was obtained like the said Example using each ink composition of Examples 15-17. Using this ballpoint pen, a straight line was drawn on Kent paper at a speed of 7 cm / second, and the color development of the center line in the obtained handwriting was observed. For all ink compositions, the center line in the handwriting formed shows the clear color shown in Table 4 as the pearl pigment is affected by the color development of the dye and can be clearly distinguished from the black outline It was a thing.

  Pearl pigments are scaly particles in which the surface of mica is covered with a thin layer of a metal oxide such as titanium oxide or iron oxide. Therefore, if a coating film containing a pearl pigment is applied on the base to form a coating film, a part of the visible light incident on the surface of such pigment particles is reflected by the metal oxide layer on the surface, and The part is reflected by the internal mica layer, and part is reflected by the underlayer, and thus the reflected light is mixed in a complicated manner to give a pearl color. In this embodiment, since the background is dark, visible light that has entered the pigment from the surface of the pigment particles is absorbed by the background, and the color of reflected light on the background is affected. Furthermore, since the various reflected light colors are also affected by the thickness of the pearl pigment, the center line of the handwriting thus has the color shown in Table 4 depending on the thickness of the pearl pigment and the color of the base.

Claims (18)

(A) at least one pigment selected from pearl pigments and metal powder pigments;
(B) water,
(C) at least one water-soluble organic solvent selected from alcohols having branched hydrophobic groups, glycols and glycol ethers,
A dual color ink composition comprising (d) a water-soluble dye, and (e) a water-soluble fixing agent comprising processed starch.   The dual color ink composition according to claim 1, wherein the pearl pigment is a metal oxide-coated mica.   The double color ink composition according to claim 1, wherein the metal powder pigment is an aluminum powder pigment.   The dual color ink composition according to any one of claims 1 to 3, comprising both a pearl pigment and a metal powder pigment.   The metal powder pigment is contained in an amount of 1 to 50 parts by weight with respect to 100 parts by weight of the pearl pigment, and the ink composition contains the pearl pigment and the metal powder pigment in a total amount of 4 to 20% by weight. Item 5. The double color ink composition according to Item 4. 3. The aqueous two-dimensional composition according to claim 1, wherein the pearl pigment has a color characteristic in which the color difference ΔE ^* between the white background and the black background is in the range of 30 to 80, and L ^{* on} the white background is 80 or more. Heavy color ink composition.   2. The duplex according to claim 1, wherein the water-soluble fixing agent is contained in a ratio of 10 to 100 parts by weight with respect to 100 parts by weight of the pigment and in the ink composition in a range of 0.4 to 20% by weight. Colored ink composition.   The dual color ink composition according to claim 1, wherein the water-soluble organic solvent is at least one selected from dipropylene glycol monopropyl ether, dipropylene glycol monomethyl ether and hexylene glycol.   The aqueous double color ink composition according to claim 1, comprising a water-soluble thickener.   The aqueous double color ink composition according to claim 9, wherein the water-soluble thickener is a polysaccharide gum.   The aqueous double color ink composition according to claim 10, wherein the polysaccharide gum is at least one selected from ramzan gum, xanthan gum, welan gum, gellan gum, pullulan, xanthan gum, guar gum and locust bean gum.   The dual color ink composition according to any one of claims 9 to 11, comprising a water-soluble thickener in a range of 0.05 to 0.5% by weight.   The dual color ink composition according to any one of claims 1 to 12, comprising urea or a urea derivative.   The dual color ink composition according to claim 13, comprising urea or a urea derivative in the range of 2 to 20% by weight.   The dual color ink composition according to claim 13 or 14, wherein the urea derivative is at least one selected from ethylene urea, methylurea and dimethylurea.   An ink composition for water-based ballpoint pens comprising the double color ink composition according to any one of claims 1 to 15.   The ink composition for water-based ballpoint pens according to claim 16, wherein the ink viscosity is 2000 to 10000 mPa · s as measured at an ELD viscometer 3 ° (R14) cone of 0.5 rpm (20 ° C).   A water-based ballpoint pen using the ink composition according to claim 16 or 17.