JP2006523761A - 懸濁重合により製造される溶融成形可能なテトラフルオロエチレン/フッ化ビニルエーテルコポリマー - Google Patents
懸濁重合により製造される溶融成形可能なテトラフルオロエチレン/フッ化ビニルエーテルコポリマー Download PDFInfo
- Publication number
- JP2006523761A JP2006523761A JP2006509784A JP2006509784A JP2006523761A JP 2006523761 A JP2006523761 A JP 2006523761A JP 2006509784 A JP2006509784 A JP 2006509784A JP 2006509784 A JP2006509784 A JP 2006509784A JP 2006523761 A JP2006523761 A JP 2006523761A
- Authority
- JP
- Japan
- Prior art keywords
- ether
- tetrafluoroethylene
- melt
- vinyl ether
- reaction vessel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
毛細管を介しての押出により測定される溶融粘度(毛細管または押出粘度)は、米国特許公報(特許文献10)に記載された通り、変形されたASTM法D1238−52Tで372℃で測定する。
重合は、ジャケット内に包まれている37.9リットル−ステンレス製オートクレーブで実施し、ジャケットを介して熱伝逹液が加熱または冷却のために循環する。このオートクレーブには、2つの刃を有し45゜の角度をなしている平らなダウンドラフト攪拌器が垂直軸に装着されて具備されている。圧力は、絶対値として報告される。
実施例1の手順が実施例2〜13にも反復され、方法条件と生成されたコポリマーを表1に示した。生成された全てのコポリマーは、破損せずに、曲げ試験を通過できる。
Claims (23)
- テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーを懸濁重合法で製造する方法において、
フッ素含有の有機溶媒を本質的に含まない水性媒体、フリーラジカル開始剤およびテロゲンを含有する、加圧されかつ攪拌される反応容器内で、テトラフルオロエチレンとフッ化ビニルエーテルとを共重合させる工程と、
テトラフルオロエチレンとフッ化ビニルエーテルとのコポリマーを凝固させるために、前記反応容器の内容物を重合の間に十分に攪拌する工程と、
約1×106Pa・S未満の溶融粘度を有する、前記溶融成形可能で強靭なコポリマーを、前記反応容器から直接分離する工程とを含むことを特徴とする、方法。 - 前記方法は、約1〜約20重量%のフッ化ビニルエーテルを含有する、テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーを製造するために十分な量のフッ化ビニルエーテルを用いることを特徴とする、請求項1に記載の方法。
- 前記方法は、約3〜約20重量%のフッ化ビニルエーテルを含有する、テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーを製造するために十分な量のフッ化ビニルエーテルを用いることを特徴とする、請求項1に記載の方法。
- 前記方法は、約3〜約15重量%のフッ化ビニルエーテルを含有する、テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーを製造するために十分な量のフッ化ビニルエーテルを用いることを特徴とする、請求項1に記載の方法。
- 前記方法は、約3〜約10重量%のフッ化ビニルエーテルを含有する、テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーを製造するために十分な量のフッ化ビニルエーテルを用いることを特徴とする、請求項1に記載の方法。
- 前記方法は、5重量%までのフルオロオレフィンコモノマー単位を含有する、テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーを製造するために十分な量のフルオロオレフィンコモノマーを用いる工程をさらに含むことを特徴とする、請求項1に記載の方法。
- 前記フルオロオレフィンがヘキサフルオロプロピレンであることを特徴とする、請求項6に記載の方法。
- 前記反応容器の前記内容物は界面活性剤を本質的に含まないことを特徴とする、請求項1に記載の方法。
- 前記テロゲンはフッ素不含有の有機化合物を含むことを特徴とする、請求項1に記載の方法。
- 前記テロゲンが1〜6個の炭素原子を含有する脂肪族炭化水素であることを特徴とする、請求項1に記載の方法。
- 前記テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーの溶融粘度が、約1×102Pa・S〜約1×106Pa・Sの範囲内にあることを特徴とする、請求項1に記載の方法。
- 前記テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーの溶融粘度が、約5×102Pa・S〜約5×104Pa・Sの範囲内にあることを特徴とする、請求項1に記載の方法。
- 前記テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーの溶融粘度が、約1×103Pa・S〜約3.5×104Pa・Sの範囲内にあることを特徴とする、請求項1に記載の方法。
- 前記反応容器内の前記内容物の攪拌は、前記テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーの約90重量%より多くを凝固させるのに十分であることを特徴とする、請求項1に記載の方法。
- 前記反応容器内の前記内容物の攪拌は、前記テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーの約95重量%より多くを凝固させるのに十分であることを特徴とする、請求項1に記載の方法。
- 前記反応容器内の前記内容物の攪拌は、前記テトラフルオロエチレンとフッ化ビニルエーテルとの溶融成形可能で強靭なコポリマーの約98重量%より多くを凝固させるのに十分であることを特徴とする、請求項1に記載の方法。
- 前記重合は、前記反応容器にテトラフルオロエチレン、フッ化ビニルエーテルおよびテロゲンを含むプレチャージを供給し、前記重合の進行中に、追加のテトラフルオロエチレンを前記反応容器に注入することによって行われ、前記テロゲンが、前記プレチャージに存在するテトラフルオロエチレンおよびテロゲンを基準にして約0.1モル%〜約20モル%の濃度で存在することを特徴とする、請求項1に記載の方法。
- 追加のフッ化ビニルエーテルが、前記重合の進行中に、前記反応容器に添加されることを特徴とする請求項17に記載の方法。
- 前記フッ化ビニルエーテルは、ペルフルオロ(アルキルビニルエーテル)であり、前記アルキル基は、1〜6個の炭素原子を含有することを特徴とする、請求項1に記載の方法。
- 前記ペルフルオロ(アルキルビニルエーテル)が、ペルフルオロ(プロピルビニルエーテル)であることを特徴とする、請求項19に記載の方法。
- 前記ペルフルオロ(アルキルビニルエーテル)が、ペルフルオロ(エチルビニルエーテル)であることを特徴とする、請求項19に記載の方法。
- 前記ペルフルオロ(アルキルビニルエーテル)が、ペルフルオロ(メチルビニルエーテル)であることを特徴とする、請求項19に記載の方法。
- 前記ペルフルオロ(アルキルビニルエーテル)が、ペルフルオロ(メチルビニルエーテル)およびペルフルオロ(プロピルビニルエーテル)であることを特徴とする、請求項19に記載の方法。