JP2005344122A - フレキシブルフォームの製造方法 - Google Patents
フレキシブルフォームの製造方法 Download PDFInfo
- Publication number
- JP2005344122A JP2005344122A JP2005211050A JP2005211050A JP2005344122A JP 2005344122 A JP2005344122 A JP 2005344122A JP 2005211050 A JP2005211050 A JP 2005211050A JP 2005211050 A JP2005211050 A JP 2005211050A JP 2005344122 A JP2005344122 A JP 2005344122A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- prepolymer
- polyol
- water
- polyisocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】 ポリウレタンフレキシブルフォームの製造方法において、プレポリマーが、少なくとも85重量%以上の4,4’−シフェニルメタンジイソシアネートあるいはその誘導体を含む過剰量のポリイソシアネートと、公称の平均ヒドロキシ基官能基数が、2.5〜3.5のポリオールを、反応させて作ったものであり、そして、該プレポリマーのNCO量が5〜10重量%であって、平均ヒドロキシ当量が、1000〜3000であり、オキシエチレン含有量が、50〜85重量%であるプレポリマーを100重量部と、少なくとも20重量部の水とを反応させて作ることを特徴とする、前記フレキシブルフォームの製造方法。
【選択図】なし
Description
これらのポリエーテルの一般的なイソシアネートと組み合わせての高い使用率は、不可能であるが、それは、開いた空孔を作るかわりに、閉じた空孔のフォームを作ることになるためである。
本発明の方法に使用されるポリイソシアネート組成物は、本質的に純粋な、4,4’−ジフェニルメタンジイソシアネートあるいはそのイソシアネートと一つまたはそれ以上の他の有機ポリイソシアネートとの混合物、特に、例えば2,4’−アイソマーあるいは2,2’−アイソマーとともに2,4’−アイソマーを、他のジフェニルメタンジイソシアネートアイソマーとした混合物が好適であり、かかるアイソマーとしては、例えば2,4’−アイソマーあるいは2,2’−アイソマーと2,4’−アイソマーとの混合物である。
2.5〜3.5の平均ヒドロキシ官能基数を得るためには、ヒドロキシ官能基が公称3のポリオールを使用するか、あるいは公称2〜6のヒドロキシ官能基数を有するポリオールの混合物を使用することにより、上述の2.5〜3.5ヒドロキシ有効官能基数の範囲が与えるのものである。
平均的な、ポリオール組成物のヒドロキシ官能基数は公称3であり、また好適な平均等量は、1000〜2000である。最適なポリオールとしては、ヒドロキシ官能基数は公称3であり、平均等量としては、1200〜1600である。
次の材料は、反応組成物を特定されるために含まれるが、含まれないものもある。
A2580は、アルコル2580であり、ポリエステルトリオールであって、ランダムのオキシエチレンとオキシプロピレン残渣を有し、77%のオキシエチレンを含み、分子量は約4000である。そして、商業的には、アルコ社から入手可能であり、ここで、アルコル(Arcol)は、アルコ社の登録商標である。
ポリイソシアネート2は、80重量%の4,4’−MDIを含み、NCO基数としては、2.01である。
実施例1〜3
プレポリマーは、A2580を70重量部と4,4−MDIを30重量部反応させることにより得られた。そして、このプレポリマーから、フレキシブルフォームが、表1に示される物質と反応させることにより得られた。
プレポリマーは、ポリイソシアネートとポリオールを混合し、反応させて得られた。そして、続いてフレキシブルフォームを得るために、プレポリマーと水とを反応させた(重量比 プレポリマー/水=100/60)。なお、詳細については、表2に示す。
プレポリマーは、実施例1と同様に得た。そして、続いてフレキシブルフォームを得るために、プレポリマーと水とを反応させた(重量比 プレポリマー/水=100/70)。得られたフォームは、白色のフレキシブルフォームであり、100kg/m3の密度を有し、圧縮セット(ASTM D3574−77、テストD、乾燥50%)は、12%であり、簡単に破壊することができた。
Claims (7)
- 少なくとも85重量%以上の4,4’−ジフェニルメタンジイソシアネートまたはその誘導体を含む過剰量のポリイソシアネートと、公称の平均ヒドロキシ基官能価が2.5〜3.5、平均ヒドロキシ当量が1000〜3000であり、そしてオキシエチレン含有量が50〜85重量%であるポリオールと、を反応させて得た反応生成物である、NCO量が5〜10重量%のプレポリマーを、水と反応させる、軟質ポリウレタンフォームの製造方法であって、
ここで、水の量が、プレポリマー100重量部当り、少なくとも20重量部であることを特徴とする、前記方法。 - 前記ポリオールが、ポリ(オキシエチレン−オキシプロピレン)ポリオールであることを特徴とする請求項1に記載の方法。
- 前記ポリオールが、公称のヒトロキシ基官能価が3、平均ヒドロキシ当量が1200〜1600であることを特徴とする請求項1または2に記載の方法。
- 前記ポリイソシアネートが、少なくとも90重量%以上の4,4’−ジフェニルメタンジイソシアネートを含むことを特徴とする請求項1〜3のいずれか1項に記載のフレキシブルフォームの製造方法。
- 前記ポリイソシアネートが、少なくとも95重量%以上の4,4’−ジフェニルメタンジイソシアネートを含むことを特徴とする請求項1〜4のいずれか1項に記載の方法。
- 前記ポリイソシアネートが、最大2.05の官能価を有することを特徴とする請求項1〜5のいずれか1項に記載の方法。
- 前記プレポリマーが、25℃において、最大10,000mPa・sの粘度を有することを特徴とする請求項1〜6のいずれか1項に記載の方法。