JP2000342963A - Absorbent composition, production thereof and absorptive article containing the same - Google Patents

Absorbent composition, production thereof and absorptive article containing the same

Info

Publication number
JP2000342963A
JP2000342963A JP2000106727A JP2000106727A JP2000342963A JP 2000342963 A JP2000342963 A JP 2000342963A JP 2000106727 A JP2000106727 A JP 2000106727A JP 2000106727 A JP2000106727 A JP 2000106727A JP 2000342963 A JP2000342963 A JP 2000342963A
Authority
JP
Japan
Prior art keywords
absorbent
water
absorption
weight
absorbent composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2000106727A
Other languages
Japanese (ja)
Inventor
Kinya Nagasuna
Katsuyuki Wada
克之 和田
欣也 長砂
Original Assignee
Nippon Shokubai Co Ltd
株式会社日本触媒
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to JP7-224928 priority Critical
Priority to JP22492895 priority
Application filed by Nippon Shokubai Co Ltd, 株式会社日本触媒 filed Critical Nippon Shokubai Co Ltd
Publication of JP2000342963A publication Critical patent/JP2000342963A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide an absorbent composition capable of quickly absorbing an aqueous liquid even if a large quantity of aqueous the liquid is added at once and maintaining extremely high liquid dispersibility at any time and having excellent absorption characteristics such as the property of keeping a high absorption capacity per unit weight. SOLUTION: This absorption composition contains a finely granular water- insoluble inorganic powder and/or a polyamine compound with 5,000 or higher weight average molecular weight and has at least 25 g/g of dispersion/absorption magnification to 0.9 wt.% sodium chloride aqueous solution after 60 minutes from starting absorption under a load of 20 g/cm2 (1.96 kPa). The dispersion/ absorption index can be measured using a measurement apparatus to be employed for measuring the dispersion/absorption magnification by measuring the weight of the physiological salt solution 12 being absorbed in the absorbent composition with the lapse of time for 60 minutes from the time when a supporting cylinder 9 is put on a sheet 8.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、例えば、紙オムツ(使い捨てオムツ)や生理用ナプキン、いわゆる失禁パット等の衛生材料等に好適に用いられる吸収剤組成物およびその製造方法、並びに、吸収剤組成物を含む吸収物品に関するものである。 BACKGROUND OF THE INVENTION The present invention is, for example, a paper diaper (disposable diaper), sanitary napkins, absorbent composition suitable for use in sanitary materials such as so-called incontinent pads, and the like, and a manufacturing method thereof, and, absorbent it relates absorbent article comprising the composition.

【0002】 [0002]

【従来の技術】近年、紙オムツや生理用ナプキン、いわゆる失禁パット等の衛生材料には、その構成材として、 In recent years, disposable diapers, sanitary napkins, the sanitary materials called incontinent pads and the like, as a constituent material,
体液を吸収させることを目的とする吸水性樹脂が幅広く利用されている。 Water-absorbent resin for the purpose of to absorb body fluids are widely used.

【0003】上記の吸水性樹脂としては、例えば、ポリアクリル酸部分中和物架橋体(特開昭55−84304 [0003] Examples of the water-absorbent resin, for example, partially neutralized polyacrylic acid cross-linked (JP 55-84304
号公報、特開昭55−108407号公報、特開昭55 JP, Sho 55-108407, JP-Sho 55
−133413号公報)、澱粉−アクリロニトリルグラフト重合体の加水分解物(特開昭46−43995号公報)、澱粉−アクリル酸グラフト重合体の中和物(特開昭51−125468号公報)、酢酸ビニル−アクリル酸エステル共重合体のケン化物(特開昭52−1468 -133413 discloses), starch - acrylonitrile graft polymer hydrolyzate (JP 46-43995 JP), starch - neutralized product of acrylic acid graft polymer (JP 51-125468 JP), acetic acid vinyl - acrylic acid ester copolymer saponified (JP 52-1468
9号公報)、アクリロニトリル共重合体若しくはアクリルアミド共重合体の加水分解物(特開昭53−1595 9 JP), acrylonitrile copolymer or acrylamide copolymer hydrolyzate (JP 53-1595
9号公報)またはこれらの架橋体、カチオン性モノマーの架橋体(特開昭58−154709号公報、特開昭5 9 No.) or a cross-linked product thereof, cross-linked cationic monomer (Japanese 58-154709, JP-Sho 5
8−154710号公報)等が知られている。 8-154710 JP), and the like.

【0004】上記の吸水性樹脂が備えるべき特性としては、体液等の水性液体に接した際の優れた吸収量や吸収速度、ゲル強度、水性液体を含んだ基材から水を吸い上げる吸引力等が挙げられる。 [0004] The properties to be provided the above water-absorbent resin, excellent absorption amount and absorption speed when in contact with aqueous liquids such as body fluids, gel strength, suction force or the like to suck water from a substrate containing aqueous liquid and the like. そして、従来より、これら吸収特性の中から種々の特定範囲の物性を複数併せ持ち、紙オムツや生理用ナプキン等の衛生材料に用いられた場合に、優れた性能(吸収特性)を示す吸水性樹脂、 Then, conventionally, it combines a plurality of physical properties of various specific range from these absorption characteristics, when used for sanitary materials such as paper diapers and sanitary napkins, excellent performance water-absorbent resin exhibiting a (absorption properties) ,
または、該吸水性樹脂を用いた吸収体や吸収物品が種々提案されている。 Or, absorbent or absorbent article using the water absorbent resin have been proposed.

【0005】上記の吸水性樹脂、吸収体、または吸収物品としては、例えば、特定のゲル容量や剪断弾性率、抽出性重合体含量を組み合わせた吸水性樹脂(米国特許第4,654,039号)、吸収量や吸収速度、ゲル強度を特定した吸水性樹脂、および、該吸水性樹脂を用いた紙オムツや生理用ナプキン(特開昭60−185550 [0005] The above water-absorbent resin, as the absorbent or absorbent article, for example, a specific gel capacity and shear modulus, extractable polymer content of the combined water-absorbent resin (U.S. Pat. No. 4,654,039 ), absorption amount and absorption speed, water-absorbing resin identified gel strength, and paper diapers and sanitary napkins using the water absorbent resin (JP 60-185550
号公報、特開昭60−185551号公報、特開昭60 JP, Sho 60-185551, JP-Sho 60
−185804号公報)、特定の吸収量や吸収速度、ゲル安定性を有する吸水性樹脂を用いた紙オムツ(特開昭60−185805号公報)、吸収量や吸引力、水可溶成分量を特定した吸水性樹脂を配した吸水性物品(特開昭63−21902号公報)、吸収量や加圧下の吸収量、ゲル破壊強度を特定した吸水性樹脂を含有する吸水性衛生用品(特開昭63−99861号公報)、吸収量や加圧下の吸収速度を特定した吸水性樹脂を含有する紙オムツ(特開平2−34167号公報)、加圧下の吸収量や、その粒子径を特定した吸水性樹脂を含有する吸収剤(欧州特許第339,461号)、吸収速度や短時間での加圧下の吸収量を特定した吸水性樹脂を特定量以上含有する吸収剤(欧州特許第443,627号)、負荷時の変形や吸い上げ -185804 discloses), specific absorption amount and absorption speed, paper diapers using water-absorbent resin having a gel stability (JP 60-185805 JP), absorption or suction force, the water soluble content absorbent article which arranged the identified water-absorbent resin (JP-63-21902 JP), the absorption amount and absorption under pressure, water-absorbing hygiene articles containing a specific water-absorbent resin a gel breaking strength (JP Akira 63-99861 JP), paper diapers containing absorption and pressure specified water-absorbent resin absorption rate (JP-a-2-34167), the absorption amount and under pressure, and identifying the particle size absorbing agent containing a water-absorbent resin (European Patent No. 339,461), absorption rate and a short time under pressure absorber containing more than a specific amount of a specific water-absorbent resin absorption of (EP 443, 627 No.), deformation or wicking under load 数を特定した吸水性樹脂を特定量以上含有する吸水性複合材料(欧州特許第532,00 Absorbent composite containing a water-absorbent resin identified several specific amount or more (EP 532,00
2号)等が知られている。 No. 2) and the like are known.

【0006】一方、近年、紙オムツや生理用ナプキン等の衛生材料は、高機能化かつ薄型化が進み、衛生材料一枚当たりの吸水性樹脂の使用量、または、主に吸水性樹脂と親水性繊維とからなる吸収体における吸水性樹脂の重量%(以下、樹脂濃度と称する)が増える傾向にある。 [0006] In recent years, sanitary materials such as paper diapers and sanitary napkins, advances high functionality and thinner, the amount of the water-absorbent resin per sheet sanitary material, or predominantly water-absorbent resin and hydrophilic wt% of the water-absorbent resin in the absorbent body consisting of a sex fibers (hereinafter referred to as resin concentration) in increase trend. つまり、かさ比重の小さい親水性繊維を少なくし、 In other words, to reduce the small hydrophilic fiber bulk density,
吸収性に優れ、かつ、かさ比重の大きい吸水性樹脂を多くすることにより、吸収体における吸水性樹脂の比率を高め、これにより吸収量を低下させることなく衛生材料の薄型化を図っている。 Excellent absorption properties, and by increasing the high water-absorbent resin bulk density, increasing the ratio of the water-absorbent resin in the absorbent body, thereby working to thinning of the sanitary materials without lowering the absorption.

【0007】 [0007]

【発明が解決しようとする課題】しかしながら、本願発明者等が、衛生材料の吸収量を増加させるために、例えば吸収体における樹脂濃度を増加させるべく種々検討した結果、従来よりも樹脂濃度を高くした吸収体を用い、 [SUMMARY OF THE INVENTION However, the present inventors have found to increase the absorption amount of sanitary materials, such as the results of various studies in order to increase the resin concentration in the absorbent body, higher resin concentration than conventional using the absorber,
かつ、衛生材料からの水性液体の漏れ等の不都合を防止するには、上述した吸収量や吸収速度、ゲル強度、吸引力等の特性を制御するだけでは不充分であることが見い出された。 And, to prevent a disadvantage such as leakage of the aqueous liquid from the sanitary materials, the above-mentioned absorption amount and absorption speed, gel strength, it is only by controlling the characteristic of the suction force and the like insufficient was found. 例えば、近年、特に注目されている、加圧下の吸収量のみが非常に大きい吸水性樹脂においては、樹脂濃度を高くすると、吸収体での液拡散性が極端に低下する現象、また、吸収体が水性液体を吸収するのに長時間を要する等の問題点を有している。 For example, in recent years, especially in being noticed, under pressure absorption only very large water-absorbent resin, the higher the resin concentration, a phenomenon the liquid diffusibility in the absorber extremely lowered also, the absorber There has been a problem such as a long time is required to absorb aqueous liquids.

【0008】また、本願発明者等は、従来よりも樹脂濃度を高くした吸収体の吸収特性に着目して種々検討した結果、公知の吸水性樹脂と親水性繊維とを混合した混合物を吸収体として用いると、樹脂濃度が低い場合には一定レベルの吸収特性を示すものの、樹脂濃度が40重量%を越えると液拡散性が急激に低下し、吸収体の単位重量当たりの吸収量が低下することを見い出した。 Further, the present inventors as a result of various studies by focusing on the absorption characteristics than conventional high resin concentration absorber, the absorber a mixture prepared by mixing a known water-absorbent resin and hydrophilic fibers when used as, but when the resin concentration is low shows the absorption properties of a certain level, when the resin concentration exceeds 40 wt% liquid diffusibility decreases rapidly, absorption amount per unit weight of the absorber is reduced It was found to be. 即ち、 In other words,
公知の吸水性樹脂と親水性繊維とを混合した混合物を吸収体として用いると、上記の問題点が生じることとなる。 When using a mixture obtained by mixing a known water-absorbent resin and hydrophilic fibers as an absorber, so that the above problem arises.

【0009】従って、本発明の目的は、上述した問題点を解決し、例えば、吸収体や吸収物品における吸水性樹脂の重量%を高くしても、常時、非常に高い液拡散性を維持すると共に、吸収体や吸収物品の単位重量当たりの吸収量を保持する等の優れた性能(吸収特性)を示すことができる吸収剤組成物およびその製造方法、並びに、 It is therefore an object of the present invention is to solve the problems described above, for example, even by increasing the weight percent of the water-absorbent resin in the absorbent or absorbent article, at all times, to maintain a very high liquid-diffusivity with excellent performance absorbent composition which can exhibit (absorption properties) and methods for their preparation, such as to hold the absorption amount per unit weight of absorbent or absorbent article, and,
吸収剤組成物を含む吸収物品を提供することにある。 It is to provide an absorbent article comprising an absorbent composition.

【0010】 [0010]

【課題を解決するための手段】本願発明者等は、上記目的を達成すべく、吸収剤組成物およびその製造方法、並びに、吸収剤組成物を含む吸収物品について鋭意検討した。 Means for Solving the Problems The present inventors have found that in order to achieve the above object, absorbent compositions and methods for their preparation, and were intensively studied absorbent article comprising the absorbent composition. その結果、特定の条件下において吸収剤組成物が水性液体を吸収する際の液拡散速度を評価するのに好適な物性値である拡散吸収指数を見い出した。 As a result, the absorbent composition under specific conditions found diffusion absorption index is a preferred physical property values ​​to evaluate the liquid distribution speed in absorbing aqueous liquids. 上記拡散吸収指数に優れた吸収剤組成物は、拡散吸収倍率が特定値以上の吸水性樹脂に特定化合物を混合したり、特定条件下で吸水性樹脂表面近傍を架橋処理することにより、得ることができる。 Absorbent composition excellent in the diffusion absorption index, diffusion absorption capacity or a mixture of specific compound to a particular value or more of the water-absorbent resin, by crosslinking the surface vicinity of the water-absorbent resin under specific conditions, to obtain can.

【0011】そして、上記拡散吸収指数に優れた吸収剤組成物が、吸収体や吸収物品における吸水性樹脂の重量%が高い場合においても、一度に添加された多量の水性液体を素早く吸収することができ、かつ、常時、非常に高い液拡散性を維持すると共に、吸収体や吸収物品の単位重量当たりの吸収量を保持する等の優れた性能(吸収特性)を示すことを見い出した。 [0011] Then, the absorbent composition excellent in the diffusion absorption index, in the case wt% of the water-absorbent resin in the absorbent or absorbent article is higher, to quickly absorb large quantities of aqueous liquid is added in one portion can be, and, at all times, while maintaining a very high liquid-diffusivity, it was found to exhibit excellent performance such that holds the absorption amount per unit weight of absorbent or absorbent article (absorbent properties). また、これにより、吸収特性に優れた吸収体および吸収物品が得られることを見い出して、本発明を完成するに至った。 This also, absorber and absorbent article having excellent absorption properties is found that the resulting, and completed the present invention.

【0012】即ち、本発明にかかる吸収剤組成物の製造方法は、上記の課題を解決するために、20g/cm 2 Namely, the production method of the absorbent composition according to the present invention, in order to solve the above problems, 20 g / cm 2
(1.96kPa)の荷重下における、吸収開始から6 In under a load of (1.96kPa), from the absorption after 6
0分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、微粒子状の水不溶性無機粉体を添加することを特徴としている。 0.9 wt% aqueous sodium chloride solution diffusing absorbency of after 0 minutes is 25 g / g or more water absorbent resin is characterized by adding a particulate water-insoluble inorganic powder.

【0013】本発明にかかる吸収剤組成物の製造方法は、上記の課題を解決するために、20g/cm [0013] manufacturing process of the absorbent composition of the present invention, in order to solve the above problems, 20 g / cm
2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、重量平均分子量5,000以上のポリアミン化合物を添加することを特徴としている。 2 in under a load of (1.96 kPa), the diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation is 25 g / g or more water-absorbing resin, the weight average molecular weight of 5,000 or more It is characterized by the addition of the polyamine compound.

【0014】本発明にかかる吸収剤組成物の製造方法は、上記の課題を解決するために、20g/cm [0014] manufacturing process of the absorbent composition of the present invention, in order to solve the above problems, 20 g / cm
2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、微粒子状の水不溶性無機粉体と、重量平均分子量5,000 2 in under a load of (1.96 kPa), the water-absorbent resin diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation is 25 g / g or more, particulate water-insoluble inorganic powder and body weight-average molecular weight of 5,000
以上のポリアミン化合物とを添加することを特徴としている。 It is characterized by the addition of the above polyamine compound.

【0015】本発明にかかる吸収剤組成物の製造方法は、上記の課題を解決するために、吸水性樹脂の上記拡散吸収倍率が30.1g/g以上であることが好ましいが、さらに、33.9g/g以上であることがより好ましい。 [0015] manufacturing method of the absorbent composition of the present invention, in order to solve the above problem, but the diffusion absorbency of the water absorbing resin is preferably 30.1 g / g or more, further 33 more preferably .9g / g or more.

【0016】上記の方法によれば、一度に多量の水性液体が添加されても、該水性液体を素早く吸収することができ、かつ、常時、非常に高い液拡散性を維持すると共に、単位重量当たりの吸収量を保持する等の優れた性能(吸収特性)を示すことができる吸収剤組成物の製造方法を提供することができる。 [0016] According to the above method, be added a large amount of an aqueous liquid at a time, it can quickly absorb aqueous liquids, and, at all times, while maintaining a very high liquid-diffusivity, unit weight it is possible to provide a superior performance manufacturing method of absorbent composition which can exhibit (absorption properties) such as to hold the absorbed amount per.

【0017】本発明にかかる吸収剤組成物は、上記の課題を解決するために、微粒子状の水不溶性無機粉体を含み、20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上であることを特徴としている。 The absorbent composition according to the present invention, in order to solve the above problems, comprises a particulate water-insoluble inorganic powder, under a load of 20g / cm 2 (1.96kPa), the absorption initiation it is characterized in that 0.9 wt% aqueous sodium chloride solution diffusing absorbency of after 60 minutes is 25 g / g or more.

【0018】本発明にかかる吸収剤組成物は、上記の課題を解決するために、重量平均分子量5,000以上のポリアミン化合物を含み、20g/cm 2 (1.96k The absorbent composition according to the present invention, in order to solve the above problems, includes a weight average molecular weight of 5,000 or more polyamine compounds, 20g / cm 2 (1.96k
Pa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が2 In under a load of Pa), diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation 2
5g/g以上であることを特徴としている。 It is characterized in that it is 5 g / g or more.

【0019】本発明にかかる吸収剤組成物は、上記の課題を解決するために、微粒子状の水不溶性無機粉体と、 The absorbent composition according to the present invention, in order to solve the above problems, and particulate water-insoluble inorganic powder,
重量平均分子量5,000以上のポリアミン化合物とを含み、20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上であることを特徴としている。 And a weight average molecular weight of 5,000 or more polyamine compounds, in under load of 20g / cm 2 (1.96kPa), diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation 25g / it is characterized by g or more.

【0020】本発明にかかる吸収剤組成物は、上記の課題を解決するために、上記拡散吸収倍率が26.9g/ The absorbent composition according to the present invention, in order to solve the above problems, the diffusion absorbency 26.9 g /
g以上であることが好ましい。 It is preferable that the g or more.

【0021】本発明にかかる吸収剤組成物は、上記の課題を解決するために、アクリル酸またはその塩を主成分とする親水性不飽和単量体を重合させて得られる架橋重合体を含むことを特徴としている。 The absorbent composition according to the present invention, in order to solve the above problems, including cross-linked polymer obtained by polymerizing a hydrophilic unsaturated monomer mainly composed of acrylic acid or a salt thereof it is characterized in that.

【0022】上記の構成によれば、一度に多量の水性液体が添加されても、該水性液体を素早く吸収することができ、かつ、常時、非常に高い液拡散性を維持すると共に、単位重量当たりの吸収量を保持する等の優れた性能(吸収特性)を示すことができる吸収剤組成物を提供することができる。 According to the arrangement, be added a large amount of an aqueous liquid at a time, it can quickly absorb aqueous liquids, and, at all times, while maintaining a very high liquid-diffusivity, unit weight it is possible to provide excellent performance absorbent composition which can exhibit (absorption properties) such as to hold the absorbed amount per.

【0023】本発明にかかる吸収物品は、上記の課題を解決するために、上記の吸収剤組成物を含む吸収層を、 The absorbent article according to the present invention, in order to solve the above problems, an absorbing layer containing the above-described absorbent composition,
透液性を有するシートと、不透液性を有するシートとで挟持してなることを特徴としている。 A sheet having a liquid-permeable, and characterized by being sandwiched between the sheet having a liquid-impervious.

【0024】上記の構成によれば、一度に多量の水性液体が添加されても、該水性液体を素早く吸収することができ、かつ、液拡散性や吸収量等の吸収特性に優れた衛生材料等の吸収物品を提供することができる。 According to the arrangement, a large amount of even an aqueous liquid is added, it is possible to quickly absorb the aqueous liquid, and excellent sanitary material on the absorption characteristics of such liquid diffusibility and absorption at a time it is possible to provide an absorbent article and the like.

【0025】以下に本発明を詳しく説明する。 [0025] the present invention will be described in detail below.

【0026】本発明における拡散吸収指数とは、吸水性樹脂または吸収剤組成物(以下、説明の便宜上、吸水性樹脂を例示して説明する)の坪量が高く、かつ、外力によって吸水性樹脂の粒子同士が密着している状態において、吸水性樹脂が水性液体を吸収する際の液拡散速度を評価するための新規な物性値である。 [0026] The diffusion absorption index in the present invention, the water-absorbing resin or absorbent composition (hereinafter, for convenience of explanation, will be exemplified a water-absorbent resin) high basis weight, and the water-absorbent resin by an external force in a state where each other particles are in close contact, it is a novel physical properties for water-absorbent resin to evaluate a liquid distribution velocity when absorbing aqueous liquids. 上記の拡散吸収指数は、所定条件下での測定における、吸水性樹脂が水性液体を吸水性樹脂層方向(以下、横方向と称する)に吸収する際の最大吸収速度の測定値から算出される。 Diffusion absorption index described above is calculated in the measurement of a predetermined condition, the water-absorbent resin is water-absorbent resin layer direction aqueous liquid from the maximum measured value of absorption rate at the time of absorption (hereinafter, referred to as lateral direction) . 尚、 still,
拡散吸収指数の測定方法については、後段の実施例にて詳述する。 Method of measuring the diffusion absorption index, is described in detail later in Examples.

【0027】上記の拡散吸収指数により、吸水性樹脂が水性液体をどの程度速やかに吸収し、かつ、吸水性樹脂が水性液体を横方向にどの程度均一に素早く拡散させることができるかを評価することができる。 [0027] The diffusion absorption index of the water-absorbent resin absorbs how quickly the aqueous liquid and the water-absorbing resin is to assess whether it is possible to how uniformly and quickly diffuse the aqueous liquid in the lateral direction be able to. 水性液体の横方向への液拡散性(液拡散能力および液伝達能力)は、 Liquid diffusibility in the lateral direction of the aqueous liquid (liquid distribution capacity and liquid transfer capacity) is
水性液体を多量に吸収する上において、特に重要な因子である。 In order to large amount of absorbed aqueous liquid, it is a particularly important factor. そして、上記評価の結果から、例えば、主に吸水性樹脂と親水性繊維とからなる吸収体、特に、吸水性樹脂の重量%(以下、樹脂濃度と称する)が高い吸収体における吸水性樹脂の吸収挙動をも容易に予測することができる。 Then, from the result of the evaluation, for example, mainly absorber comprising a water absorbent resin and a hydrophilic fiber, in particular, weight percent of the water-absorbing resin (hereinafter, referred to as resin concentration) of the water-absorbent resin in the high absorber the absorption behavior can also be easily predicted. 尚、吸収体の構成については後述する。 It will be described later configuration of the absorber.

【0028】本発明において、吸収剤組成物が有するより好ましい物性値として挙げられる拡散吸収倍率とは、 [0028] In the present invention, a diffusing absorbency mentioned as preferable physical properties than possessed by the absorbent composition,
吸水性樹脂の坪量が高く、かつ、外力によって吸水性樹脂の粒子同士が密着している状態における水性液体の拡散力を加味した、吸水性樹脂の吸収量を評価するための物性値である。 The basis weight of the water-absorbent resin is high and, in consideration of the diffusion force of the aqueous liquid in a state where particles of the water-absorbing resin is in close contact by an external force, is the physical property value for evaluating the absorption of the water-absorbent resin . 上記の拡散吸収倍率は、所定条件下での測定における、吸収開始から所定時間経過後、例えば6 Diffusing absorbency described above, in the measurement of a predetermined condition, after a predetermined time has elapsed from the absorption initiation, for example 6
0分経過後の測定値から算出される。 It is calculated from the measured values ​​after a lapse of 0 minutes. 尚、拡散吸収倍率の測定方法については、後段の実施例にて詳述する。 Note that the method of measuring the diffusing absorbency, later described in more detail in the examples.

【0029】尚、上述した先行出願には、吸収速度を評価している文献が見受けられるが、加圧状態下で、水性液体を横方向に拡散させながら吸収する際の最大吸収速度を評価している文献は無い。 [0029] Incidentally, in the prior application described above, although literature evaluating the absorption rate seen, under a pressurized state, and evaluates the maximum absorption rate at the time of absorption while diffusing the aqueous liquid in the lateral direction and that literature is not. 即ち、該加圧下の吸収速度の従来の評価は、水性液体が吸水性樹脂層方向と直交する方向(以下、縦方向と称する)に、短い距離を移動する場合についてのみ行われているだけである。 That is, the conventional evaluation of the absorption rate of the pressurized pressure, the direction in which the aqueous liquid is perpendicular to the water-absorbent resin layer direction (hereinafter, the longitudinal direction referred to as), just only have been made for the case of moving a short distance is there. 従って、上記従来の評価の結果のみからでは、例えば樹脂濃度が高い吸収体を用いた紙オムツ等における、該吸収体の吸収挙動を正確に予測することができない。 Therefore, the above only from the results of conventional evaluation, for example, in the paper diaper or the like which has a resin concentration with high absorber, it is impossible to accurately predict the absorption behavior of the absorbent body.

【0030】本発明にかかる吸収剤組成物は、20g/ The absorbent composition according to the present invention, 20 g /
cm 2 (1.96kPa)の荷重下における、0.9重量%塩化ナトリウム水溶液の拡散吸収指数が1.5g/ under a load of cm 2 (1.96kPa), diffusion absorption index of 0.9 wt% aqueous solution of sodium chloride 1.5 g /
g・min以上、より好ましくは3.0g/g・min g · min or more, more preferably 3.0g / g · min
以上である。 Or more. また、この吸収剤組成物は、20g/cm Further, the absorbent composition, 20 g / cm
2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上であることが好ましく、さらに、26.9g/g以上であることがより好ましい。 Under a load of 2 (1.96 kPa), preferably diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation is 25 g / g or more, further, 26.9 g / g or more more preferably.

【0031】具体的には、本発明にかかる吸収剤組成物は、例えば、20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量% [0031] More specifically, the absorbent composition of the present invention, for example, 20 g / cm 2 under a load of (1.96 kPa), 0.9 wt% after a lapse of 60 minutes from the absorption initiation
塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、微粒子状の水不溶性無機粉体(以下、単に水不溶性無機粉体と記す)を添加することにより得られる。 Diffusing absorbency sodium chloride aqueous solution to the water-absorbing resin is 25 g / g or more, particulate water-insoluble inorganic powder (hereinafter, simply referred to as water-insoluble inorganic powder) is obtained by adding. また、本発明にかかる吸収剤組成物は、例えば、20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、重量平均分子量(Mw)5,000以上のポリアミン化合物(以下、単にポリアミン化合物と記す)を添加することにより得られる。 Further, the absorbent composition of the present invention, for example, in a load of a 20g / cm 2 (1.96kPa), diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation 25g / g or more at which the water absorbent resin, the weight average molecular weight (Mw) 5,000 or higher polyamine compounds (hereinafter simply referred to as a polyamine compound) obtained by adding. さらに、本発明にかかる吸収剤組成物は、例えば、20g/cm 2 (1. Further, the absorbent composition of the present invention, for example, 20g / cm 2 (1.
96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、水不溶性無機粉体とポリアミン化合物とを添加することにより得られる。 In load under 96KPa), the diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation is 25 g / g or more water-absorbing resin, adding a water-insoluble inorganic powder and a polyamine compound It can be obtained by.

【0032】また、吸収剤組成物は、後述する特定の架橋剤を組み合わせて得られる表面架橋剤によって表面近傍が加熱処理されてなる吸水性樹脂表面を、さらに表面架橋剤と混合し、加熱処理する方法によっても得られる。 Further, the absorbent composition, the water-absorbent resin surface near the surface by surface cross-linking agent obtained by combining a specific crosslinking agent to be described later is formed by heat treatment, and further mixed with a surface crosslinking agent, heat treatment It can also be obtained by a method of.

【0033】上記の吸水性樹脂としては、例えば、カルボキシル基を含有する吸水性架橋重合体が好適である。 [0033] As the above water-absorbent resin, for example, water-absorbing cross-linked polymers containing carboxyl groups are preferred.
該吸水性架橋重合体は、例えば、アクリル酸またはその塩を主成分とする親水性不飽和単量体を(共)重合(以下、単に重合と記す)させることにより得られる。 Water-absorbent crosslinked polymer, for example, be obtained by a hydrophilic unsaturated monomer mainly composed of acrylic acid or a salt thereof (co) polymerization (hereinafter, simply referred to as polymerization). そして、該吸水性架橋重合体のうち、ポリアクリル酸塩の架橋重合体がさらに好ましい。 Of the water-absorbent crosslinked polymer, crosslinked polymer of polyacrylic acid salt is more preferred. また、ポリアクリル酸塩の架橋重合体は、該架橋重合体中の酸基のうち、50モル%〜90モル%が、例えば、アルカリ金属塩やアンモニウム塩、アミン塩等によって中和されていることがより好ましい。 Further, crosslinked polymers of polyacrylic acid salts, of the group of the crosslinking polymer, 50 mol% to 90 mol%, for example, alkali metal salts or ammonium salts, are neutralized by an amine salt, etc. it is more preferable.

【0034】尚、上記の吸水性樹脂として、例えば、ポリアクリル酸の部分中和物架橋体(米国特許第4,62 [0034] Incidentally, as the water-absorbing resin, for example, partially neutralized cross-linked polyacrylic acid (U.S. Pat. No. 4,62
5,001号、米国特許第4,654,039号、米国特許第5,250,640号、米国特許第5,275, No. 5,001, U.S. Patent No. 4,654,039, U.S. Pat. No. 5,250,640, U.S. Patent No. 5,275,
773号、欧州特許第456136号等)、澱粉−アクリロニトリルグラフト重合体の部分中和物架橋体(米国特許第4, 076, 663号)、イソブチレン−マレイン酸共重合体(米国特許第4, 389, 513号)、酢酸ビニル−アクリル酸共重合体のケン化物(米国特許第4, 124, 748号)、アクリルアミド(共)重合体の加水分解物(米国特許第3, 959, 569号)、アクリロニトリル重合体の加水分解物(米国特許第3, 9 773, EP 456136, etc.), starch - acrylonitrile graft copolymer partially neutralized crosslinked product of (US 4, 076, 663 issue), isobutylene - maleic acid copolymer (U.S. Patent No. 4, 389 , 513 JP), vinyl acetate - acrylic acid copolymer saponified (US 4, 124, 748 issue), acrylamide (co) polymer of the hydrolyzate (U.S. Patent No. 3, 959, 569), polyacrylonitrile hydrolyzate (U.S. Pat. No. 3, 9
35, 099号)等の、公知の吸水性樹脂を採用することもできる。 35, No. 099), etc., it may also be any conventional water-absorbing resin.

【0035】上記の親水性不飽和単量体は、必要に応じて、アクリル酸またはその塩以外の不飽和単量体(以下、他の単量体と記す)を含有していてもよい。 [0035] The above hydrophilic unsaturated monomer, optionally acrylic acid or an unsaturated monomer other than a salt thereof (hereinafter, referred to as other monomer) may contain. 他の単量体としては、具体的には、例えば、メタクリル酸、マレイン酸、ビニルスルホン酸、スチレンスルホン酸、2 Examples of the other monomer, specifically, for example, methacrylic acid, maleic acid, vinyl sulfonic acid, styrene sulfonic acid, 2
−(メタ)アクリルアミド−2−メチルプロパンスルホン酸、2−(メタ)アクリロイルエタンスルホン酸、2 - (meth) acrylamido-2-methylpropanesulfonic acid, 2- (meth) acryloyl ethanesulfonic acid, 2
−(メタ)アクリロイルプロパンスルホン酸等の、アニオン性不飽和単量体およびその塩;アクリルアミド、メタアクリルアミド、N−エチル(メタ)アクリルアミド、N−n−プロピル(メタ)アクリルアミド、N−イソプロピル(メタ)アクリルアミド、N,N−ジメチル(メタ)アクリルアミド、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、メトキシポリエチレングリコール(メタ) - (meth) acrylate such as acryloyl propane sulfonic acid, anionic unsaturated monomers and salts thereof; acrylamide, methacrylamide, N- (meth) acrylamide, N-n-propyl (meth) acrylamide, N- isopropyl (meth ) acrylamide, N, N-dimethyl (meth) acrylamide, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, methoxy polyethylene glycol (meth)
アクリレート、ポリエチレングリコールモノ(メタ)アクリレート、ビニルピリジン、N−ビニルピロリドン、 Acrylate, polyethylene glycol mono (meth) acrylate, vinyl pyridine, N- vinylpyrrolidone,
N−アクリロイルピペリジン、N−アクリロイルピロリジン等の、ノニオン性の親水基含有不飽和単量体;N, N- acryloylpiperidine, N- acrylate such as acryloyl pyrrolidine, and cationic unsaturated monomers; N,
N−ジメチルアミノエチル(メタ)アクリレート、N, N- dimethylaminoethyl (meth) acrylate, N,
N−ジエチルアミノエチル(メタ)アクリレート、N, N- diethylaminoethyl (meth) acrylate, N,
N−ジメチルアミノプロピル(メタ)アクリレート、 N- dimethylaminopropyl (meth) acrylate,
N,N−ジメチルアミノプロピル(メタ)アクリルアミド、および、これらの四級塩等の、カチオン性不飽和単量体;等が挙げられるが、特に限定されるものではない。 N, N-dimethylaminopropyl (meth) acrylamide, and the like these quaternary salts, cationic unsaturated monomer; but like, but is not particularly limited. これら他の単量体を併用する場合の使用量は、親水性不飽和単量体全体の30モル%以下が好ましく、10 The amount of the case of using these other monomers is preferably not more than 30 mole% of the total hydrophilic unsaturated monomer, 10
モル%以下がより好ましい。 The following is a more preferred molar%.

【0036】親水性不飽和単量体を重合させて得られる吸水性樹脂前駆体は、カルボキシル基を有している。 The hydrophilic unsaturated monomer is polymerized to obtain water-absorbent resin precursor has a carboxyl group. 該吸水性樹脂前駆体を得る際には、内部架橋剤を用いて架橋構造を内部に導入することが望ましい。 In obtaining the water absorbent resin precursor, it is desirable to introduce a crosslinked structure with an internal cross-linking agent therein. 上記の内部架橋剤は、重合性不飽和基および/または反応性基を一分子中に複数有する化合物であればよく、特に限定されるものではない。 The above internal cross-linking agent may be any polymerizable unsaturated groups and / or reactive group is a compound having a plurality in one molecule, it is not particularly limited. つまり、内部架橋剤は、親水性不飽和単量体と共重合および/または反応する置換基を一分子中に複数有する化合物であればよい。 That is, the internal crosslinking agent, the hydrophilic unsaturated monomer copolymerizable and / or reactive substituents may be any compound having a plurality in one molecule. 尚、親水性不飽和単量体は、内部架橋剤を用いなくとも架橋構造が形成される自己架橋型の化合物からなっていてもよい。 Incidentally, the hydrophilic unsaturated monomer may comprise a self-crosslinking compound which cross-linked structure without using the inner crosslinking agent is formed.

【0037】内部架橋剤としては、具体的には、例えば、N,N'−メチレンビス(メタ)アクリルアミド、 Examples of the internal crosslinking agent include, for example, N, N'-methylenebis (meth) acrylamide,
(ポリ)エチレングリコールジ(メタ)アクリレート、 (Poly) ethylene glycol di (meth) acrylate,
(ポリ)プロピレングリコールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、トリメチロールプロパンジ(メタ)アクリレート、 (Poly) propylene glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, trimethylolpropane di (meth) acrylate,
グリセリントリ(メタ)アクリレート、グリセリンアクリレートメタクリレート、エチレンオキシド変性トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、トリアリルシアヌレート、トリアリルイソシアヌレート、トリアリルホスフェート、トリアリルアミン、ポリ(メタ)アリロキシアルカン、(ポリ)エチレングリコールジグリシジルエーテル、グリセロールジグリシジルエーテル、エチレングリコール、ポリエチレングリコール、プロピレングリコール、グリセリン、ペンタエリスリトール、エチレンジアミン、ポリエチレンイミン、グリシジル(メタ)アクリレート等が挙げられるが、特に限定されるものではない。 Glycerin tri (meth) acrylate, glycerin acrylate methacrylate, ethylene oxide-modified trimethylolpropane tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol hexa (meth) acrylate, triallyl cyanurate, triallyl isocyanurate, tri triallyl phosphate, triallylamine, poly (meth) allyloxy alkane, (poly) ethylene glycol diglycidyl ether, glycerol diglycidyl ether, ethylene glycol, polyethylene glycol, propylene glycol, glycerol, pentaerythritol, ethylenediamine, polyethyleneimine, glycidyl (meth ) acrylate and the like, but is not particularly limited. これら内部架橋剤は、一種類のみを用いてもよく、また、二種類以上を併用してもよい。 These internal crosslinking agents may be used only one type, or may be used in combination of two or more. そして、 And,
上記例示の内部架橋剤のうち、重合性不飽和基を一分子中に複数有する内部架橋剤を用いることにより、得られる吸水性樹脂の吸収特性等をより一層向上させることができる。 Among the above-exemplified internal-crosslinking agent, by using an internal crosslinking agent having a plurality of polymerizable unsaturated groups in one molecule, it is possible to further improve the absorption properties of the resultant water-absorbing resin.

【0038】内部架橋剤の使用量は、親水性不飽和単量体に対して、0.005モル%〜3モル%の範囲内がより好ましく、0.01モル%〜1.5モル%の範囲内がさらに好ましい。 The amount of the internal crosslinking agent with respect to the hydrophilic unsaturated monomer, more preferably in the range of 0.005 mol% to 3 mol%, 0.01 mol% to 1.5 mol% range is more preferred. 内部架橋剤の使用量が0.005モル%よりも少ない場合、並びに、3モル%よりも多い場合には、所望の吸収特性を備えた吸水性樹脂が得られないおそれがある。 When the amount of the internal crosslinking agent is less than 0.005 mol%, and, if more than 3 mol%, the water-absorbent resin may not be obtained with the desired absorption properties.

【0039】尚、親水性不飽和単量体を重合させて吸水性樹脂前駆体を得る際には、反応系に、澱粉、澱粉の誘導体、セルロース、セルロースの誘導体、ポリビニルアルコール、ポリアクリル酸(塩)、ポリアクリル酸(塩)架橋体等の親水性高分子;次亜リン酸(塩)等の連鎖移動剤;水溶性若しくは水分散性の界面活性剤等を添加してもよい。 [0039] Incidentally, when by polymerizing a hydrophilic unsaturated monomer to obtain the water-absorbent resin precursor, the reaction system, starch, derivatives of starch, cellulose, derivatives of cellulose, polyvinyl alcohol, polyacrylic acid ( may be added a water-soluble or water-dispersible surfactant or the like; a chain transfer agent such as hypophosphorous acid (salt); salt), polyacrylic acid (salt) crosslinked hydrophilic polymers or the like.

【0040】親水性不飽和単量体の重合方法は、特に限定されるものではなく、例えば、水溶液重合、逆相懸濁重合、バルク重合、沈澱重合等の公知の方法を採用することができる。 The polymerization process of the hydrophilic unsaturated monomer is not particularly limited, for example, aqueous solution polymerization, reversed phase suspension polymerization, it is possible to bulk polymerization, employing a known method of precipitation polymerization . このうち、重合反応の制御の容易さ、および、得られる吸水性樹脂の性能面から、親水性不飽和単量体を水溶液にして重合させる方法、即ち、水溶液重合および逆相懸濁重合が好ましい。 Among them, the ease of control of the polymerization reaction, and, from the performance side of the resultant water-absorbing resin, a method of polymerizing by an aqueous solution of a hydrophilic unsaturated monomer, i.e., aqueous solution polymerization and reversed phase suspension polymerization . 反応温度や反応時間等の反応条件は、親水性不飽和単量体の種類等に応じて適宜設定すればよく、特に限定されるものではない。 Reaction conditions such as reaction temperature and reaction time may be appropriately set according to the type of the hydrophilic unsaturated monomer is not particularly limited.

【0041】尚、親水性不飽和単量体の重合方法として、公知の重合方法(例えば、米国特許第4,625, [0041] As a polymerization method for the hydrophilic unsaturated monomer, known polymerization methods (e.g., U.S. Patent No. 4,625,
001号、米国特許第4,769,427号、米国特許第4,873,299号、米国特許第4,093,77 No. 001, U.S. Pat. No. 4,769,427, U.S. Pat. No. 4,873,299, U.S. Pat. No. 4,093,77
6号、米国特許第4, 367,323号、米国特許第4, 446, 261号、米国特許第4, 683, 274 6, U.S. Patent No. 4, No. 367,323, U.S. Patent No. 4, 446, 261, U.S. Patent No. 4, 683, 274
号、米国特許第4, 690, 996号、米国特許第4, , U.S. Patent No. 4, 690, 996, US 4,
721, 647号、米国特許第4, 738, 867号、 721, 647, U.S. Patent No. 4, 738, 867 Patent,
米国特許第4, 748, 076号等)を採用することもできる。 US 4, 748, 076 No. etc.) may be employed.

【0042】親水性不飽和単量体を重合させる際には、 [0042] When the polymerization of the hydrophilic unsaturated monomer,
例えば、過硫酸カリウム、過硫酸アンモニウム、過硫酸ナトリウム、t−ブチルハイドロパーオキサイド、過酸化水素、2,2'−アゾビス(2−アミジノプロパン) For example, potassium persulfate, ammonium persulfate, sodium persulfate, t- butyl hydroperoxide, hydrogen peroxide, 2,2'-azobis (2-amidinopropane)
二塩酸塩等のラジカル重合開始剤;紫外線や電子線等の活性エネルギー線;等を用いることができる。 Radical polymerization initiator such as dihydrochloride; UV and active energy rays such as electron beams; or the like can be used. また、酸化性ラジカル重合開始剤を用いる場合には、例えば、亜硫酸ナトリウム、亜硫酸水素ナトリウム、硫酸第一鉄、 In the case of using an oxidizing radical polymerization initiator, for example, sodium sulfite, sodium hydrogen sulfite, ferrous sulfate,
L−アスコルビン酸等の還元剤を併用してレドックス重合を行ってもよい。 In combination with a reducing agent such as L- ascorbic acid may be carried out redox polymerization. これら重合開始剤の使用量は、0. The amount of the polymerization initiator is 0.
001モル%〜2モル%の範囲内が好ましく、0.01 It is preferably in the range of 001 mol% to 2 mol%, 0.01
モル%〜0.5モル%の範囲内がより好ましい。 The range of mole% to 0.5 mole% is more preferable.

【0043】上記の重合方法によって得られる吸水性樹脂前駆体は、必要に応じて分級等の操作により、その粒子径が調整される。 The water-absorbent resin precursor obtained by the above polymerization method, by operating the classification, if necessary, the particle size is adjusted. 吸水性樹脂前駆体は、球状、鱗片状、不定形破砕状、繊維状、顆粒状、棒状、略球状、扁平状等の種々の形状であってもよい。 Water-absorbing resin precursor may be spherical, flake, irregular pulverized shape, fibrous, granular, rod-shaped, substantially spherical, or may be a different shape of the flat or the like.

【0044】本発明に用いられる、20g/cm [0044] used in the present invention, 20g / cm
2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂は、上記の吸水性樹脂前駆体を、特定の表面架橋剤の存在下に処理し、表面架橋することによって得ることができる。 Under a load of 2 (1.96 kPa), the water-absorbent resin diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation is 25 g / g or more, the above water-absorbent resin precursor was treated in the presence of a particular surface crosslinking agent may be obtained by surface crosslinking. 吸水性樹脂を得る方法としては、具体的には、例えば、吸水性樹脂前駆体の粒子径を、分級等の操作により、平均粒子径が200μm〜600μmの範囲内で、しかも、 As a method of obtaining a water absorbent resin, specifically, for example, the particle diameter of the water-absorbing resin precursor, by operating such as classification, mean particle diameter in the range of 200Myuemu~600myuemu, moreover,
粒子径が106μm未満の粒子の割合が10重量%以下となるように調整した後、該吸水性樹脂前駆体を、第一表面架橋剤および第二表面架橋剤を組み合わせてなる表面架橋剤(後述する)の存在下で加熱処理する方法(特願平7−145012号)等が挙げられる。 After the particle size was adjusted to the percentage of particles less than 106μm is 10 wt% or less, the water absorbent resin precursor, the first surface crosslinking agent and a second surface crosslinking agent comprising a combination of surface cross-linking agent (described later a method of heating in the presence of which) (Japanese Patent Application No. Hei 7-145012), and the like. 上記の方法により、吸水性樹脂の表面近傍の架橋密度を内部よりも高くすることができるので、拡散吸収倍率に優れた吸水性樹脂を得ることができる。 By the above method, since the crosslinking density in the vicinity of the surface of the water-absorbent resin may be higher than the internal, it is possible to obtain an excellent water-absorbent resin diffusing absorbency. 尚、吸水性樹脂前駆体の平均粒子径が200μm〜600μmの範囲外である場合や、粒子径が106μm未満の粒子の割合が10重量% Incidentally, and when the average particle diameter of the water-absorbing resin precursor is outside the range of 200Myuemu~600myuemu, the particle diameter ratio of particles less than 106 [mu] m 10 wt%
を越える場合には、拡散吸収倍率に優れた吸水性樹脂を得ることが困難となるおそれがある。 When exceeding, it may become difficult to obtain an excellent water-absorbent resin diffusing absorbency.

【0045】表面架橋剤は、吸水性樹脂前駆体が有するカルボキシル基と反応可能な化合物の混合物であり、溶解度パラメータ(SP値)が互いに異なる第一表面架橋剤および第二表面架橋剤を組み合わせてなる。 The surface crosslinking agent is a mixture of a compound capable of reacting with the carboxyl groups of the water-absorbent resin precursor, the solubility parameter (SP value) is a combination of different first surface crosslinking agent and a second surface-crosslinking agent together Become. 尚、上記の溶解度パラメータとは、化合物の極性を表すファクターとして一般に用いられる値である。 Note that the above-mentioned solubility parameter is a value which is generally used as a factor representing the polarity of the compound. 本発明においては、上記の溶解度パラメータに対して、ポリマーハンドブック第3版(WILEY INTERSCIENCE社発行)527頁〜 In the present invention, with respect to the solubility parameter, Polymer Handbook 3rd edition (WILEY INTERSCIENCE, published) page 527 -
539頁に記載されている溶媒の溶解度パラメータδ Solubility parameter of the solvent listed in 539 pages δ
(cal/cm 31/2 ((J/m 31/2 )の値を適用することとする。 (Cal / cm 3) 1/2 and applying the value of ((J / m 3) 1/2 ). また、上記の頁に記載されていない溶媒の溶解度パラメータに関しては、該ポリマーハンドブックの524頁に記載されているSmallの式に、 With respect to the solubility parameter of the solvent it is not described in pages described above, expression of Small listed in 524 pages of the Polymer Handbook,
同525頁に記載されているHoyの凝集エネルギー定数を代入して導かれる値を適用することとする。 And applying a value derived by substituting a cohesive energy constant of Hoy listed in the page 525.

【0046】上記の第一表面架橋剤は、吸水性樹脂前駆体が有するカルボキシル基と反応可能な、溶解度パラメータが12.5(cal/cm 31/2 (0.0256 The first surface cross-linking agents described above, capable of reacting with the carboxyl group of the water-absorbent resin precursor, the solubility parameter is 12.5 (cal / cm 3) 1/2 (0.0256
(J/m 31/2 )以上の化合物が好ましく、13.0 (J / m 3) 1/2) or more compounds are preferred, 13.0
(cal/cm 31/2 (0.0266(J/m 3 (Cal / cm 3) 1/2 ( 0.0266 (J / m 3)
1/2 )以上の化合物がより好ましい。 1/2) or more of compounds are more preferable. 上記の第一表面架橋剤としては、具体的には、例えば、エチレングリコール、プロピレングリコール、グリセリン、ペンタエリスリトール、ソルビトール、エチレンカーボネート(1, The first surface cross-linking agents described above, specifically, for example, ethylene glycol, propylene glycol, glycerol, pentaerythritol, sorbitol, ethylene carbonate (1,
3−ジオキソラン−2−オン)、プロピレンカーボネート(4−メチル−1,3−ジオキソラン−2−オン)等が挙げられるが、これら化合物に限定されるものではない。 3-dioxolan-2-one), although propylene carbonate (4-methyl-1,3-dioxolan-2-one), and the like, but is not limited to these compounds. これら第一表面架橋剤は、一種類のみを用いてもよく、また、二種類以上を併用してもよい。 These first surface-crosslinking agents may be used only one type, or may be used in combination of two or more.

【0047】上記の第二表面架橋剤は、吸水性樹脂前駆体が有するカルボキシル基と反応可能な、溶解度パラメータが12.5(cal/cm 31/2 (0.0256 The second surface cross-linking agents described above, capable of reacting with the carboxyl group of the water-absorbent resin precursor, the solubility parameter is 12.5 (cal / cm 3) 1/2 (0.0256
(J/m 31/2 )未満の化合物が好ましく、9.5 (J / m 3) 1/2) of less than compounds are preferable, 9.5
(cal/cm 31/2 〜12.0(cal/cm 3 (Cal / cm 3) 1/2 ~12.0 (cal / cm 3)
1/2 (0.0194(J/m 31/2 〜0.0246 1/2 (0.0194 (J / m 3 ) 1/2 ~0.0246
(J/m 31/2 )の範囲内の化合物がより好ましい。 Compounds within the scope of (J / m 3) 1/2) is more preferable.
上記の第二表面架橋剤としては、具体的には、例えば、 The second surface cross-linking agents described above, specifically, for example,
ジエチレングリコール、トリエチレングリコール、テトラエチレングリコール、ジプロピレングリコール、トリプロピレングリコール、1,3−ブタンジオール、1, Diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, 1,3-butanediol, 1,
4−ブタンジオール、1,5−ペンタンジオール、2, 4-butanediol, 1,5-pentanediol, 2,
4−ペンタンジオール、1,6−ヘキサンジオール、 4-pentanediol, 1,6-hexanediol,
2,5−ヘキサンジオール、トリメチロールプロパン、 2,5-hexanediol, trimethylolpropane,
ジエタノールアミン、トリエタノールアミン、エチレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、グリセロールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、 Diethanolamine, triethanolamine, ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerol polyglycidyl ether, diglycerol polyglycidyl ether,
ポリグリセロールポリグリシジルエーテル、プロピレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル、エチレンジアミン、ジエチレントリアミン、トリエチレンテトラミン、2,4− Polyglycerol polyglycidyl ether, propylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, ethylenediamine, diethylenetriamine, triethylenetetramine, 2,4
トリレンジイソシアネート、ヘキサメチレンジイソシアネート、4,5−ジメチル−1,3−ジオキソラン−2 Tolylene diisocyanate, hexamethylene diisocyanate, 4,5-dimethyl-1,3-dioxolane -2
−オン、エピクロロヒドリン、エピブロモヒドリン等が挙げられるが、これら化合物に限定されるものではない。 - one, epichlorohydrin, although epibromohydrin and the like, but is not limited to these compounds. これら第二表面架橋剤は、一種類のみを用いてもよく、また、二種類以上を併用してもよい。 These second surface-crosslinking agents may be used only one type, or may be used in combination of two or more.

【0048】表面架橋剤の使用量は、用いる化合物やそれらの組み合わせ等にもよるが、吸水性樹脂前駆体の固形分100重量部に対して、第一表面架橋剤の使用量が0.01重量部〜5重量部の範囲内、かつ、第二表面架橋剤の使用量が0.001重量部〜1重量部の範囲内が好ましく、第一表面架橋剤の使用量が0.1重量部〜2 The amount of the surface cross-linking agent varies depending on the compounds and combinations thereof, and the like to be used, 100 parts by weight of the solid content of the water-absorbent resin precursor, the amount of the first surface crosslinking agent is 0.01 in the range of 5 parts by weight, and, the amount of the second surface crosslinking agent is preferably in a range of 0.001 part by weight to 1 part by weight, the amount of the first surface crosslinking agent is 0.1 part by weight to 2
重量部の範囲内、かつ、第二表面架橋剤の使用量が0. In the range of parts by weight, and, the amount of the second surface crosslinking agent is 0.
005重量部〜0.5重量部の範囲内がより好ましい。 In the range of 005 parts to 0.5 parts by weight is more preferable.
表面架橋剤の使用量が上記範囲を越える場合には、不経済となるばかりか、吸水性樹脂における最適な架橋構造を形成する上で、表面架橋剤の量が過剰となるため、好ましくない。 If the amount of the surface crosslinking agent exceeds the above range, not only uneconomical, in order to form an optimal crosslinking structure in the water-absorbent resin, the amount of the surface crosslinking agent is excessive, undesirable. また、表面架橋剤の使用量が上記範囲よりも少ない場合には、吸水性樹脂における拡散吸収倍率等の性能を向上させる上で、その改良効果が得られ難いため、好ましくない。 Further, when the amount of the surface cross-linking agent is less than the above range, in order to improve the performance such as diffusion absorption capacity water-absorbing resin, since the improving effect is hardly obtained, which is not preferable.

【0049】吸水性樹脂前駆体と表面架橋剤とを混合する際には、溶媒として水を用いることが好ましい。 [0049] In mixing the water-absorbent resin precursor and the surface crosslinking agent, it is preferable to use water as a solvent. 水の使用量は、吸水性樹脂前駆体の種類や粒子径等にもよるが、吸水性樹脂前駆体の固形分100重量部に対して、 The amount of water depends on the type and particle diameter of the water-absorbing resin precursor, 100 parts by weight of the solid content of the water-absorbing resin precursor,
0を越え、20重量部以下が好ましく、0.5重量部〜 Greater than zero, preferably 20 parts by weight or less, 0.5 part by weight to
10重量部の範囲内がより好ましい。 In the range of 10 parts by weight is more preferable.

【0050】また、吸水性樹脂前駆体と表面架橋剤とを混合する際には、必要に応じて、溶媒として親水性有機溶媒を用いてもよい。 [0050] Furthermore, in mixing the water-absorbent resin precursor and the surface crosslinking agent, it may optionally be used a hydrophilic organic solvent as a solvent. 上記の親水性有機溶媒としては、 Examples of the hydrophilic organic solvent,
具体的には、例えば、メチルアルコール、エチルアルコール、n−プロピルアルコール、イソプロピルアルコール、n−ブチルアルコール、イソブチルアルコール、t Specifically, for example, methyl alcohol, ethyl alcohol, n- propyl alcohol, isopropyl alcohol, n- butyl alcohol, isobutyl alcohol, t
−ブチルアルコール等の低級アルコール類;アセトン等のケトン類;ジオキサン、テトラヒドロフラン、アルコキシポリエチレングリコール等のエーテル類;N,N− - lower alcohols such as butyl alcohol; ketones such as acetone; dioxane, tetrahydrofuran, ethers such as alkoxy polyethylene glycol; N, N-
ジメチルホルムアミド等のアミド類;ジメチルスルホキシド等のスルホキシド類等が挙げられる。 Amides such as dimethylformamide; sulfoxides such as dimethyl sulfoxide and the like. 親水性有機溶媒の使用量は、吸水性樹脂前駆体の種類や粒子径等にもよるが、吸水性樹脂前駆体の固形分100重量部に対して、20重量部以下が好ましく、0.1重量部〜10重量部の範囲内がより好ましい。 The amount of the hydrophilic organic solvent varies depending on the kind and particle diameter of the water-absorbing resin precursor, 100 parts by weight of the solid content of the water-absorbent resin precursor is preferably 20 parts by weight or less, 0.1 in the range of 10 parts by weight is more preferable.

【0051】そして、吸水性樹脂前駆体と表面架橋剤とを混合する際には、例えば、前記例示の親水性有機溶媒に吸水性樹脂前駆体を分散させた後、表面架橋剤を混合してもよいが、混合方法は、特に限定されるものではない。 [0051] Then, in mixing the water-absorbent resin precursor and the surface crosslinking agent, for example, after the water-absorbing resin precursor is dispersed in the above-exemplified hydrophilic organic solvent, a mixture of surface crosslinking agent it may also be, but the mixing method is not particularly limited. 種々の混合方法のうち、必要に応じて水および/または親水性有機溶媒に溶解させた表面架橋剤を、吸水性樹脂前駆体に直接、噴霧若しくは滴下して混合する方法が好ましい。 Among various mixing methods, the surface crosslinking agent dissolved in water and / or a hydrophilic organic solvent, if necessary, directly to the water-absorbing resin precursor, a method of mixing spraying or dropping to is preferred.

【0052】吸水性樹脂前駆体と表面架橋剤とを混合する際に用いられる混合装置(以下、混合装置aと記す) [0052] mixing apparatus used in mixing the water-absorbent resin precursor and the surface-crosslinking agent (hereinafter, referred to as the mixing device a)
は、両者を均一にかつ確実に混合するために、大きな混合力を備えていることが好ましい。 In order to mix uniformly and reliably both preferably provided with a large mixing force. 上記の混合装置aとしては、例えば、円筒型混合機、二重壁円錐型混合機、 The mixing apparatus a described above, for example, a cylindrical mixer, double-wall cone type mixers,
V字型混合機、リボン型混合機、スクリュー型混合機、 V-shaped mixer, a ribbon type mixer, screw type mixer,
流動型炉ロータリーデスク型混合機、気流型混合機、双腕型ニーダー、内部混合機、粉砕型ニーダー、回転式混合機、スクリュー型押出機等が好適である。 Fluidized-furnace rotary disk type mixers, gas current type mixers, twin-arm kneaders, internal mixers, pulverizing type kneaders, rotary mixers, and screw type extruders.

【0053】吸水性樹脂前駆体と表面架橋剤とを混合した後、加熱処理を行い、吸水性樹脂前駆体の表面近傍を架橋させる。 [0053] After mixing the water-absorbent resin precursor and the surface-crosslinking agent, heat treatment is performed to cross-link the neighborhood of the surface of the water-absorbing resin precursor. 上記加熱処理の処理温度は、用いる表面架橋剤にもよるが、160℃以上、250℃以下が好ましい。 Treatment temperature of the heat treatment depends on the surface cross-linking agent used, 160 ° C. or higher, preferably 250 ° C. or less. 処理温度が160℃未満の場合には、均一な架橋構造が形成されず、従って、拡散吸収倍率に優れた吸水性樹脂を得ることができないため、好ましくない。 Because if the processing temperature is lower than 160 ° C. is not uniform crosslinking structure is formed, therefore, it is not possible to obtain an excellent water-absorbent resin diffusing absorbency, which is not preferable. また、 Also,
加熱処理に時間がかかるので、生産性の低下を引き起こす。 Since the time for the heat treatment is applied, it causes a reduction in productivity. 処理温度が250℃を越える場合には、吸水性樹脂前駆体の劣化を引き起こし、従って、吸水性樹脂の性能が低下するため、好ましくない。 If the processing temperature exceeds 250 ° C. causes deterioration of the water-absorbent resin precursor, thus, because the performance of the water absorbent resin decreases, which is not preferable.

【0054】上記の加熱処理は、通常の乾燥機または加熱炉を用いて行うことができる。 [0054] The above heat treatment can be carried out using conventional dryers or heating furnaces. 上記の乾燥機としては、例えば、溝型混合乾燥機、ロータリー乾燥機、デスク乾燥機、流動層乾燥機、気流型乾燥機、赤外線乾燥機等が挙げられる。 As the dryer, for example, channel type mixing dryers, rotary dryers, desk dryers, fluidized-bed dryers, gas stream type dryers, and infrared dryers.

【0055】本発明にかかる吸収剤組成物に必要に応じて含まれる水不溶性無機粉体としては、具体的には、例えば、二酸化ケイ素、二酸化チタン、酸化アルミニウム、酸化マグネシウム、酸化亜鉛、タルク、リン酸カルシウム、リン酸バリウム、珪酸、珪酸塩、粘土、珪藻土、ゼオライト、ベントナイト、カオリン、ハイドロタルサイト、活性白土等が挙げられるが、特に限定されるものではない。 [0055] As the water-insoluble inorganic powder contained as required in such absorbent composition of the present invention, specifically, for example, silicon dioxide, titanium dioxide, aluminum oxide, magnesium oxide, zinc oxide, talc, calcium phosphate, barium phosphate, silicic acid, silicates, clay, diatomaceous earth, zeolite, bentonite, kaolin, hydrotalcite, although activated clay and the like, but is not particularly limited. これら水不溶性無機粉体は、一種類のみを用いてもよく、また、二種類以上を併用してもよい。 These water-insoluble inorganic powders may be used only one type, or may be used in combination of two or more.
上記例示の水不溶性無機粉体のうち、微細な非晶質二酸化ケイ素がより好ましい。 Among the above-exemplified water-insoluble inorganic powders, fine amorphous silicon dioxide are more preferable. また、該非晶質二酸化ケイ素の粒子径は、1,000μm以下が好ましく、100μ The particle diameter of the amorphous silicon dioxide is preferably at most 1,000 .mu.m, 100 microns
m以下がより好ましく、50μm以下がさらに好ましく、10μm以下が特に好ましい。 More preferably not more than m, more preferably less 50 [mu] m, and particularly preferably equal to or less than 10 [mu] m.

【0056】水不溶性無機粉体の使用量は、吸収剤組成物の用途等にもよるが、吸水性樹脂100重量部に対して、0.05重量部〜2重量部の範囲内が好ましく、 [0056] The amount of water-insoluble inorganic powders, depending on the application of the absorbent composition, based on 100 parts by weight of the water-absorbent resin is preferably in the range of 0.05 part by weight to 2 parts by weight,
0.1重量部〜1重量部の範囲内がより好ましい。 More preferably in the range of 0.1 parts to 1 parts by weight. 水不溶性無機粉体の使用量が0.05重量部よりも少ない場合には、所望の拡散吸収指数を備えた吸収剤組成物が得られないおそれがある。 When the amount of the water-insoluble inorganic powder is less than 0.05 part by weight, the absorbent composition may not be obtained with the desired diffusion absorption index. また、水不溶性無機粉体の使用量を2重量部よりも多くしても、該使用量に見合った効果が得られ難いので、経済的に不利となるおそれがある。 Further, even if the amount of the water-insoluble inorganic powder and more than 2 parts by weight, the effect is obtained hardly commensurate with the amount of use, it may become economically disadvantageous.

【0057】吸水性樹脂と水不溶性無機粉体とを混合する際に用いられる混合装置(以下、混合装置bと記す) [0057] mixing apparatus used in mixing the water absorbent resin and a water-insoluble inorganic powder (hereinafter, referred to as the mixing device b)
としては、例えば、円筒型混合機、スクリュー型混合機、スクリュー型押出機、タービュライザー、ナウター型混合機、V字型混合機、リボン型混合機、双腕型ニーダー、流動式混合機、気流型混合機、回転円盤型混合機、ロールミキサー、転動式混合機等が好適である。 The include cylinder type mixers, screw type mixers, screw type extruders, turbulizer, Nauta type mixers, V-shaped mixer, a ribbon type mixer, double-arm type kneaders, flow type mixers, stream type mixers, rotary disc type mixers, roll mixers, tumbling type mixers and the like. 混合速度は、高速であってもよく、また、低速であってもよい。 Mixing speed may be a high speed, or may be a low speed. 尚、水不溶性無機粉体は、溶媒を用いないで混合すること、つまり、ドライブレンドが好ましいが、上記溶媒を用いたエマルションの状態で吸水性樹脂と混合することもできる。 The water-insoluble inorganic powder, mixing without a solvent, i.e., a dry blend is preferred, can be mixed with the water-absorbing resin in the form of an emulsion with the solvent.

【0058】本発明にかかる吸収剤組成物に必要に応じて含まれるポリアミン化合物は、重量平均分子量が5, [0058] Polyamine compounds contained as required in the absorbent composition of the present invention has a weight average molecular weight of 5,
000以上であればよく、特に限定されるものではない。 Well as long as 000 or more, but the present invention is not particularly limited. ポリアミン化合物は、一級アミノ基、二級アミノ基、および三級アミノ基からなる群より選ばれる少なくとも一種のアミノ基を分子中に有していればよく、特に限定されるものではない。 Polyamine compounds, primary amino group, secondary amino group, and it is sufficient at least one amino group selected from the group consisting of tertiary amino groups having in the molecule, is not particularly limited.

【0059】上記のポリアミン化合物としては、例えば、(1) モノアリルアミン誘導体の単独重合体,ジアリルアミン誘導体の単独重合体;(2) 二種類以上のモノアリルアミン誘導体の共重合体,二種類以上のジアリルアミン誘導体の共重合体,モノアリルアミン誘導体とジアリルアミン誘導体との共重合体;(3) モノアリルアミン誘導体および/またはジアリルアミン誘導体と、ジアルキルジアリルアンモニウム塩との共重合体;(4) 三級アミノ基を有する不飽和カルボン酸誘導体(以下、不飽和カルボン酸誘導体aと記す)の単独重合体;(5) 二種類以上の不飽和カルボン酸誘導体aの共重合体;(6) 不飽和カルボン酸誘導体aと、三級アミノ基がプロトン化および/またはアルキル化されてなる四級アンモニウム塩、および/または、ジアルキ [0059] Examples of the polyamine compound, for example, (1) a homopolymer of monoallylamine derivative, a homopolymer of diallylamine derivatives; (2) a copolymer of two or more of monoallylamine derivative, two or more of diallylamine having (4) a tertiary amino group; copolymer derivatives, copolymers of monoallylamine derivative and a diallylamine derivative; (3) a monoallylamine derivative and / or diallylamine derivatives, copolymers of a dialkyl diallyl ammonium salt and (6) an unsaturated carboxylic acid derivative a; unsaturated carboxylic acid derivatives (hereinafter referred to as an unsaturated carboxylic acid derivative a) homopolymer of; (5) two or more copolymers of unsaturated carboxylic acid derivative a , quaternary ammonium salts tertiary amino groups are protonated and / or alkylated and / or dialkyl ジアリルアンモニウム塩を置換基として有する不飽和カルボン酸誘導体(以下、不飽和カルボン酸誘導体bと記す)との共重合体; Unsaturated carboxylic acid derivative having as a substituent a diallyl ammonium salt (hereinafter, referred to as an unsaturated carboxylic acid derivative b), a copolymer;
(7) 不飽和カルボン酸誘導体a、不飽和カルボン酸誘導体b、および、これら不飽和カルボン酸誘導体a・bと共重合可能なビニル単量体の三元共重合体;(8) 不飽和カルボン酸、および、該不飽和カルボン酸と共重合可能な不飽和単量体を共重合させて共重合体を得た後、該共重合体が有するカルボキシル基をアルキレンイミンと反応させてなる重合体;(9) ポリアルキレンイミン;(10) (7) unsaturated carboxylic acid derivative a, unsaturated carboxylic acid derivatives b, and, a terpolymer of an unsaturated carboxylic acid derivative a · b and copolymerizable vinyl monomer; (8) unsaturated carboxylic acid, and, after obtaining the copolymer by copolymerizing unsaturated carboxylic acid copolymerizable unsaturated monomer, formed by a carboxyl group which copolymer has reacted with an alkylene imine polymer ; (9) polyalkyleneimine; (10)
ポリアルキレンイミン・エピハロヒドリン樹脂;(11)ポリアルキレンポリアミン;(12)(2−メタクリロイルオキシエチル)エチレンイミンの重合体,(2−メタクリロイルオキシエチル)エチレンイミン、および、該(2 Polyalkyleneimine-epihalohydrin resin; (11) a polyalkylene polyamine; (12) (2-methacryloyloxyethyl) of ethylene imine, (2-methacryloyloxyethyl) ethyleneimine, and the (2
−メタクリロイルオキシエチル)エチレンイミンと共重合可能な不飽和単量体の共重合体;(13)ポリアミドポリアミン;(14)ポリアミドアミン・エピハロヒドリン樹脂;(15)ポリアクリルアミドのマンニッヒ反応変性物, - methacrylonitrile copolymer of acryloyloxyethyl) ethyleneimine and copolymerizable unsaturated monomer; (13) Polyamide polyamine; (14) polyamidoamine-epihalohydrin resin; (15) a Mannich reaction modified products of polyacrylamide,
ポリメタクリルアミドのマンニッヒ反応変性物;(16)ポリビニルアミン,ビニルアミン、および、該ビニルアミンと共重合可能な不飽和単量体の共重合体;(17)ジシアンジアミド・ジエチレントリアミン重縮合物;等が挙げられる。 Mannich reaction modified product of poly methacrylamide; (16) Polyvinyl amine, vinylamine, and a copolymer of the vinyl amine and copolymerizable unsaturated monomer; (17) dicyandiamide-diethylenetriamine polycondensate, and the like .

【0060】このようなポリアミン化合物としては、具体的には、例えば、ポリアリルアミン、ポリジアリルアミン、ポリ(N−アルキルアリルアミン)、ポリ(アルキルジアリルアミン)、モノアリルアミン−ジアリルアミン共重合体、N−アルキルアリルアミン−モノアリルアミン共重合体、モノアリルアミン−ジアルキルジアリルアンモニウム塩・共重合体、ジアリルアミン−ジアルキルジアリルアンモニウム塩・共重合体、ポリジメチルアミノエチルアクリレート、ポリジエチルアミノエチルアクリレート、ポリジメチルアミノエチルアクリルアミド、直鎖状ポリエチレンイミン、分岐鎖状ポリエチレンイミン、ポリエチレンポリアミン、ポリプロピレンポリアミン、ポリアミドポリアミン、ポリエーテルポリアミン、ポリビニルア [0060] As the polyamine compound, specifically, for example, polyallylamine, polydiallylamine, poly (N- alkyl allylamine), poly (alkyl diallyl amine), monoallylamine - diallylamine copolymer, N- alkylaryl amines - monoallylamine copolymers, monoallylamine - dialkyl diallyl ammonium salts, copolymers, diallylamine - dialkyl diallyl ammonium salts, copolymers, polydimethyl aminoethyl acrylate, poly diethylaminoethyl acrylate, poly dimethylaminoethyl acrylamide, linear polyethyleneimine, branched polyethyleneimine, polyethylene polyamine, polypropylene polyamine, polyamide polyamine, polyether polyamine, Poribinirua ン、ポリアミドポリアミン・エピクロロヒドリン樹脂、ポリアミジン等が挙げられる。 Emissions, polyamide polyamine epichlorohydrin resin, polyamidine, and the like. また、ポリアクリルアミドまたはポリメタクリルアミドに、ホルムアルデヒドとジエチルアミンとを反応させてなる、アミノ化された変性体等も挙げられる。 Moreover, polyacrylamide or poly methacrylamide, by reacting a formaldehyde and diethylamine, and also aminated modified products and the like.

【0061】また、ポリアミン化合物は、酸性化合物によって完全中和または部分中和されていてもよい。 [0061] Furthermore, polyamine compound, may be fully neutralized or partially neutralized with an acidic compound. 酸性化合物は、ポリアミン化合物を中和することができる化合物、即ち、無機酸および有機酸であればよく、特に限定されるものではない。 Acidic compounds, compounds that can neutralize the polyamine compound, i.e., may be any inorganic and organic acids, but is not particularly limited. 無機酸としては、具体的には、 Inorganic acids, specifically,
例えば、炭酸;塩酸、フッ化水素酸等の水素酸;硫酸、 For example, carbonate; hydrochloric, hydrochloric acid such as hydrofluoric acid, sulfuric acid,
亜硫酸、硝酸、次亜リン酸、亜リン酸、オルトリン酸、 Sulfurous acid, nitric acid, hypophosphorous acid, phosphorous acid, orthophosphoric acid,
メタリン酸、ピロリン酸等のポリリン酸、トリポリリン酸、ウルトラリン酸(酸性メタリン酸)、過塩素酸等の酸素酸;上記酸素酸の塩;等が挙げられる。 Salt of the oxygen acid; metaphosphoric acid, polyphosphoric acids such as pyrophosphoric acid, tripolyphosphate, Ultra phosphate (acidic metaphosphoric acid), oxygen acids such as perchloric acid and the like. 有機酸としては、例えば、カルボン酸、スルフィン酸、スルホン酸、フェノール酸、エノール(カルボニル化合物の互変異性体)、メルカプタン、イミド(酸イミド)、オキシム、スルホンアミド等の、酸性の官能基を有する化合物が挙げられ、具体的には、例えば、グリコール酸、乳酸、トリクロロ乳酸、グリセリン酸、リンゴ酸、酒石酸、クエン酸、タルトロン酸、没食子酸等のオキシ酸; The organic acid, e.g., carboxylic acid, sulfinic acid, sulfonic acid, phenol acid, enol (tautomer of the carbonyl compound), mercaptans, imides (acid imide), oximes, such as sulfonamides, an acidic functional group compounds having the like, specifically, for example, glycolic acid, lactic acid, trichloroacetic acid, glyceric acid, malic acid, tartaric acid, citric acid, tartronic acid, oxy acids such as gallic acid;
アスパラギン酸等のアミノ酸;等が挙げられる。 Amino acids such as aspartic acid, and the like. これら酸性化合物は、一種類のみを用いてもよく、また、二種類以上を併用してもよい。 These acidic compounds may be used only one type, or may be used in combination of two or more.

【0062】ポリアミン化合物の重量平均分子量は5, [0062] The weight average molecular weight of the polyamine compound 5,
000以上であり、10,000〜10,000,00 It is at 000 or more, 10,000~10,000,00
0の範囲内がより好ましい。 Within a range of 0 is more preferable. 重量平均分子量が5,00 Weight average molecular weight is 5,00
0未満のポリアミン化合物は、所望の拡散吸収指数を備えた吸収剤組成物が得られないことがあり、好ましくない。 0 less than the polyamine compound may absorbent composition having the desired diffusion absorption index can not be obtained, which is not preferable. ポリアミン化合物の使用量は、吸収剤組成物の用途等にもよるが、吸水性樹脂100重量部に対して、0. The amount of polyamine compound, depending on the application of the absorbent composition, based on 100 parts by weight of the water-absorbent resin, 0.
1重量部〜10重量部の範囲内が好ましい。 In the range of 1 to 10 parts by weight is preferred.

【0063】吸水性樹脂とポリアミン化合物とを混合する際には、例えば、水および/または前記例示の親水性有機溶媒にポリアミン化合物を溶解若しくは分散させることにより溶液若しくは分散液を調製した後、該溶液若しくは分散液を吸水性樹脂に噴霧若しくは滴下して混合する方法が好適である。 [0063] In mixing the water-absorbent resin and polyamine compound, for example, after a solution or dispersion was prepared by the hydrophilic organic solvent of water and / or the illustrated dissolving or dispersing the polyamine compound, the the solution or dispersion method of mixing spraying or dropping to the water absorbent resin is preferable. そして、両者を混合する際には、前記例示の混合装置bを用いることができる。 Then, when mixing the two may be used mixing apparatus b of the illustrative. 混合速度は、高速であってもよく、また、低速であってもよい。 Mixing speed may be a high speed, or may be a low speed.

【0064】上記の水不溶性無機粉体およびポリアミン化合物は、単独で用いてもよく、必要に応じて併用してもよい。 [0064] The water-insoluble inorganic powders and polyamine compounds may be used alone or in combination as needed. また、吸水性樹脂と、これら水不溶性無機粉体およびポリアミン化合物とを混合する順序は、特に限定されるものではない。 The order of mixing the water-absorbent resin, and these water-insoluble inorganic powders and polyamine compound is not particularly limited.

【0065】また、前述したように、吸収剤組成物を得る他の方法としては、具体的には、例えば、次に示す方法等が挙げられる。 [0065] Further, as described above, other methods of obtaining an absorbent composition, specifically, for example, a method in which the following are mentioned. 即ち、先ず、カルボキシル基を有し、平均粒子径が200μm〜600μmの範囲内で、 That is, first, a carboxyl group, an average particle diameter in the range of 200Myuemu~600myuemu,
しかも、粒子径が106μm未満の粒子の割合が10重量%以下となるように調整された吸水性樹脂前駆体を、 Moreover, the water-absorbing resin precursor particle size ratio of particles less than 106μm was adjusted to be 10 wt% or less,
該カルボキシル基と反応可能な、溶解度パラメータが1 Capable of reacting with the carboxyl group, the solubility parameter 1
2.5(cal/cm 31/2 (0.0256(J/m 2.5 (cal / cm 3) 1/2 (0.0256 (J / m
31/2 )以上の第一表面架橋剤、および、溶解度パラメータが12.5(cal/cm 31/2 (0.025 3) 1/2) or more first surface crosslinking agent, and a solubility parameter 12.5 (cal / cm 3) 1/2 (0.025
6(J/m 31/2 )未満の第二表面架橋剤の存在下、 6 the presence of (J / m 3) 1/2) of less than the second surface-crosslinking agent,
160℃以上で加熱処理することにより、吸水性樹脂を得る;次に、この吸水性樹脂に、さらに、表面架橋剤、より好ましくは溶解度パラメータが12.5(ca By heating at 160 ° C. or higher to obtain a water-absorbent resin; Next, this water-absorbent resin, further, a surface cross-linking agent, more preferably a solubility parameter of 12.5 (ca
l/cm 31/2 (0.0256(J/m 31/2 )以上の第一表面架橋剤と、溶解度パラメータが12.5 l / cm 3) 1/2 and (0.0256 (J / m 3) 1/2) or more first surface crosslinking agent, a solubility parameter of 12.5
(cal/cm 31/2 (0.0256(J/m 3 (Cal / cm 3) 1/2 ( 0.0256 (J / m 3)
1/2 )未満の第二表面架橋剤とを添加・混合した後、1 After addition and mixing and 1/2) than the second surface-crosslinking agent, 1
60℃以上で加熱処理する;という方法により、吸収剤組成物を得ることもできる。 Heat treatment at 60 ° C. or higher; by the method of, can also be obtained absorbent composition.

【0066】上記の各種方法により得られる吸収剤組成物は、20g/cm 2 (1.96kPa)の荷重下における、0.9重量%塩化ナトリウム水溶液の拡散吸収指数が1.5g/g・min以上である。 [0066] The various absorbent composition obtained by the process is in under load of 20g / cm 2 (1.96kPa), diffusion absorption index of 0.9 wt% aqueous sodium chloride solution 1.5 g / g · min or more. このため、上記の吸収剤組成物は、上述したような優れた吸収特性を備えている。 Therefore, the above-described absorbent composition has excellent absorption properties as described above.

【0067】吸収体は、上記の吸収剤組成物を少なくとも一種類含み、かつ、該吸収剤組成物の含有量が40重量%以上、より好ましくは50重量%以上、さらに好ましくは60重量%以上、特に好ましくは70重量%以上である。 [0067] absorber comprises at least one of the above absorbent composition, and the content of the absorbent composition is 40 wt% or more, more preferably 50 wt% or more, more preferably 60 wt% or more , particularly preferably 70 wt% or more.

【0068】拡散吸収指数が1.5g/g・min未満である吸収剤組成物を含む吸収体は、一度に多量の水性液体が添加された場合には、該水性液体を素早く吸収することができない。 [0068] Absorber diffusion absorption index comprises an absorbent composition is less than 1.5 g / g · min is, when a large amount of aqueous liquid is added in one portion, to quickly absorb aqueous liquids Can not. つまり、このような吸収剤組成物を含む吸収体は、拡散吸収指数が低いので液拡散性が極端に劣っており、一度に多量の水性液体が添加された場合には、該水性液体を素早く吸収して吸収体中に拡散させることができない。 That is, the absorber containing such absorbent composition has a lower diffusion absorption index is poor liquid diffusibility extremely, if a large amount of aqueous liquid is added at once, quickly aqueous liquid it is not possible to diffuse absorption to in the absorbent body. その結果、吸収体は、水性液体を吸収するのに長時間を要し、吸収体全体の吸収容量が小さくなる。 As a result, the absorbent body, it takes a long time to absorb aqueous liquids, absorbent capacity of the entire absorbent body is reduced. また、吸収体を含む吸収物品は、一度に多量の水性液体が添加された場合には、上記原因等により、該水性液体の漏れ等の不都合を生じる。 Further, absorbent articles comprising absorbent body, when a large amount of aqueous liquid added all at once, by the reason such, results in disadvantages such as leakage of the aqueous liquid. 特に、吸収物品における同一箇所に多量の水性液体が繰り返し添加された場合には、上記漏れ等の不都合が顕著に生じることとなる。 In particular, when a large amount of the aqueous liquid is repeatedly added to the same location in the absorbent article, so that the disadvantage of the leakage or the like occurs markedly.

【0069】吸収体は、吸収剤組成物の他に、必要に応じて、親水性繊維を含んでいてもよい。 [0069] absorber, in addition to the absorbent composition, if desired, may contain a hydrophilic fiber. そして、吸収体が例えば吸収剤組成物と親水性繊維とからなる場合には、吸収体の構成としては、例えば、吸収剤組成物と親水性繊維とを均一に混合した構成;層状に形成した親水性繊維間に吸収剤組成物を挟持した構成;吸収剤組成物と親水性繊維とを均一に混合して層状に形成し、この上に、層状に形成した親水性繊維を積層した構成;吸収剤組成物と親水性繊維とを均一に混合して層状に形成し、 When the absorber is made of, for example, absorbent composition and hydrophilic fibers, the structure of the absorbent body, for example, configured to uniformly mix the absorbent composition and hydrophilic fibers; forming a layer configuration absorbent composition and a hydrophilic fiber are uniformly mixed to form a layer, thereon, by laminating the hydrophilic fibers formed into a layer; structure which sandwiches absorbent composition between the hydrophilic fibers; the absorbent composition and the hydrophilic fibers are uniformly mixed to form a layer,
これと、層状に形成した親水性繊維との間に吸収剤組成物を挟持した構成;等が挙げられる。 This results in configurations sandwiching the absorbent composition between the hydrophilic fibers formed into a layer; and the like. さらに、吸収体の構成としては、例えば、吸収剤組成物に特定量の水を配合することによって該吸収剤組成物をシート状に形成した構成であってもよい。 Further, as the structure of the absorbent body, for example, it may be a configuration in which the absorbent composition is formed into a sheet by incorporating a specific amount of water absorbent composition. 上記構成とすることにより、吸収体は、その吸収特性をより一層充分に発揮することができる。 By the above structure, the absorber can exhibit its absorption characteristics more sufficiently.

【0070】そして、上記例示の構成のうち、吸収体における吸収剤組成物の含有量(割合)が40重量%以上となるようにして、吸収剤組成物と親水性繊維とを均一に混合した構成がより好ましい。 [0070] Of the above-exemplified construction, as the content of the absorbent composition in the absorbent member (ratio) is 40 wt% or more, it was uniformly mixed and the hydrophilic fiber absorbent composition configuration is more preferable. また、上記例示の構成のうち、吸収剤組成物と親水性繊維との合計量に対する吸収剤組成物の割合が50重量%以上、より好ましくは60重量%以上、さらに好ましくは70重量%以上となるようにして、吸収剤組成物と親水性繊維とを均一に混合した構成がさらに好ましい。 Further, among the above-exemplified configuration, the ratio of the absorbent composition to the total amount of the absorbent composition and hydrophilic fibers 50% by weight or more, more preferably 60 wt% or more, more preferably 70 wt% or more and It becomes way, constituted by uniformly mixing the hydrophilic fibers absorbent composition is more preferable. 吸収体における樹脂濃度が高い程、吸収体の吸収特性は顕著に現れる。 The higher resin concentration in the absorbent body, the absorption characteristics of the absorber remarkable. 尚、吸収体の構成は、上記例示の構成に限定されるものではない。 The configuration of the absorbent body is not limited to the configuration exemplified above.

【0071】上記の親水性繊維としては、例えば、木材から得られるメカニカルパルプやケミカルパルプ、セミケミカルパルプ、溶解パルプ等のセルロース繊維;レーヨン、アセテート等の人工セルロース繊維;等が挙げられる。 [0071] Examples of the hydrophilic fibers, for example, mechanical pulp or chemical pulp obtained from wood, semi-chemical pulp, cellulose fibers such as dissolved pulp; rayon, artificial cellulose fibers such as acetate; and the like. 上記例示の繊維のうち、セルロース繊維がより好ましい。 Among the above-exemplified fibers, cellulose fibers are more preferable. また、親水性繊維は、ポリアミドやポリエステル、ポリオレフィン等の合成繊維を含有していてもよい。 Also, hydrophilic fibers, polyamide or polyester may contain synthetic fibers such as polyolefins. 尚、親水性繊維は、上記例示の繊維に限定されるものではない。 Incidentally, the hydrophilic fibers is not limited to the fibers of the examples.

【0072】また、吸収体における親水性繊維の割合が比較的少ない場合には、接着性バインダーを用いて吸収体、つまり、親水性繊維同士を接着させてもよい。 [0072] Also, when the ratio of the hydrophilic fibers in the absorbent body is relatively small, the absorbent body using an adhesive binder, i.e., may be bonded to the hydrophilic fibers. 親水性繊維同士を接着させることにより、吸収体の使用前や使用中における該吸収体の強度や保形性を高めることができる。 By adhering the hydrophilic fibers, it is possible to enhance the strength and shape retention of the absorber during use or before use of the absorbent body.

【0073】上記の接着性バインダーとしては、ポリエチレン、ポリプロピレン、エチレン−プロピレン共重合体、1−ブテン−エチレン共重合体等のポリオレフィン繊維等の熱融着繊維;接着性を有するエマルション;等が例示できる。 [0073] Examples of the above-mentioned adhesive binders include polyethylene, polypropylene, ethylene - thermally Chakusen'i polyolefin fibers such as ethylene copolymer - propylene copolymer, 1-butene; exemplary etc.; emulsion having adhesiveness it can. これら接着性バインダーは、単独で用いてもよく、また、二種類以上を適宜混合して用いてもよい。 These adhesive binders may be used alone or may be used in admixture of two or more as appropriate. 親水性繊維と接着性バインダーとの重量比は、50 The weight ratio of the hydrophilic fiber and the adhesive binder is 50
/50〜99/1の範囲内が好ましく、70/30〜9 / 50-99 / preferably within 1, and 70 / 30-9
5/5の範囲内がより好ましく、80/20〜95/5 More preferably in the range of 5/5, 80/20 to 95/5
の範囲内がさらに好ましい。 More preferably in the range of.

【0074】上記の方法により得られる吸収体は、上述したような優れた吸収特性を備えている。 [0074] absorber obtained by the method described above, has excellent absorption properties as described above.

【0075】吸収体は、例えば、紙オムツや生理用ナプキン、いわゆる失禁パット等の衛生材料等の吸収物品に用いた場合に、吸水性樹脂の使用量が多い場合、或いは、吸収体における樹脂濃度が高い場合においても、非常に高い液拡散性や吸収速度、長時間にわたって安定した吸収量を保持する等の優れた性能(吸収特性)を示すことができる。 [0075] absorber, for example, when used disposable diapers, sanitary napkins, the absorbent article of the sanitary materials such as so-called incontinent pads and the like, when the amount of the water absorbent resin is large, or, resin concentration in the absorbent body in the case is higher, it can exhibit very high liquid-diffusivity or rate of absorption, excellent performance, such as to retain a stable absorption over a long period of time (absorption properties).

【0076】本発明にかかる吸収物品は、上記の吸収体を含む吸収層を、透液性を有するシートと、不透液性を有するシートとで挟持してなる。 [0076] Absorbent articles according to the present invention, the absorbing layer comprising an absorber described above, formed by sandwiched a sheet having liquid permeability, a sheet having a liquid-impervious. 吸収層の構成や製造方法は、特に限定されるものではない。 Configuration and manufacturing method of the absorbing layer is not particularly limited. また、吸収物品の製造方法は、特に限定されるものではない。 The manufacturing method of an absorbent article is not particularly limited.

【0077】上記透液性を有するシート(以下、液透過性シートと称する)は、水性液体を透過する性質を備えた材料からなっている。 [0077] sheet having the liquid-permeable (hereinafter, referred to as liquid-permeable sheet) is made of a material having a property of transmitting an aqueous liquid. 液透過性シートの材料としては、例えば、不織布、織布;ポリエチレンやポリプロピレン、ポリエステル、ポリアミド等からなる多孔質の合成樹脂フィルム;等が挙げられる。 As the material of the liquid-permeable sheet, for example, a nonwoven fabric, woven fabric, polyethylene, polypropylene, polyester, synthetic resin porous film composed of a polyamide or the like; and the like. 上記不透液性を有するシート(以下、液不透過性シートと称する)は、水性液体を透過しない性質を備えた材料からなっている。 Sheet having the liquid-impermeable (hereinafter, referred to as liquid-impermeable sheet) is made of a material having a property of not transmitting an aqueous liquid. 液不透過性シートの材料としては、例えば、ポリエチレン、ポリプロピレン、エチレンビニルアセテート、ポリ塩化ビニル等からなる合成樹脂フィルム;これら合成樹脂と不織布との複合材からなるフィルム;上記合成樹脂と織布との複合材からなるフィルム;等が挙げられる。 As the material of the liquid-impermeable sheet, for example, polyethylene, polypropylene, ethylene vinyl acetate, synthetic resin films made of polyvinyl chloride or the like; a composite material of these synthetic resins with nonwoven film; the synthetic resin and the fabric of a composite material film; and the like.
尚、液不透過性シートは、蒸気を透過する性質を備えていてもよい。 The liquid impermeable sheet may have a property of transmitting steam.

【0078】上記構成の吸収物品は、上述したような優れた吸収特性を備えている。 [0078] The absorbent article of the above configuration is provided with excellent absorption properties as described above. 吸収物品としては、具体的には、例えば、紙オムツや生理用ナプキン、いわゆる失禁パット等の衛生材料等が挙げられるが、特に限定されるものではない。 The absorbent article, specifically, for example, paper diapers and sanitary napkins, but sanitary materials called incontinent pads and the like, but is not particularly limited. そして、吸収物品は優れた吸収特性を備えているので、例えば該吸収物品が紙オムツである場合には、尿の漏れを防止することができると共に、いわゆるドライ感を付与することができる。 Since absorbent article has excellent absorption properties, for example, when the absorbent article is a paper diaper, it is possible to prevent leakage of urine, it is possible to impart a so-called dry feeling.

【0079】尚、上記の吸収剤組成物、吸収体および吸収物品は、必要に応じて、消臭剤、抗菌剤、香料、発泡剤、顔料、染料、親水性短繊維、肥料、酸化剤、還元剤、水等をさらに含んでいてもよい。 [0079] The above-mentioned absorbent composition, absorbent and absorbent articles, if necessary, a deodorant, an antibacterial agent, perfume, foaming agent, pigment, dye, hydrophilic short fibers, fertilizers, oxidants, the reducing agent may further contain water, and the like. これにより、吸収剤組成物、吸収体および吸収物品に、種々の機能を付与させることができる。 Thus, the absorbent composition, the absorber and absorbent article, it is possible to impart various functions.

【0080】 [0080]

【実施例】以下、実施例および比較例により、本発明をさらに詳細に説明するが、本発明はこれらにより何ら限定されるものではない。 EXAMPLES The following examples and comparative examples, the present invention will be described in further detail, the present invention should not be construed as being limited thereto. 尚、吸収剤組成物、吸収体および吸収物品の諸性能(物性)は、以下の方法で測定した。 The absorption composition, various properties of the absorbent body and absorbent article (properties) were measured by the following method.

【0081】(a)吸収倍率 吸収剤組成物0.2gを不織布製の袋(60mm×60 [0081] (a) the absorption capacity absorbent composition 0.2g bag made of nonwoven fabric (60 mm × 60
mm)に均一に入れ、0.9重量%塩化ナトリウム水溶液(生理食塩水)中に室温で浸漬した。 Uniformly placed in mm), they were immersed at room temperature in a 0.9 wt% aqueous sodium chloride solution (saline). 60分後に袋を引き上げ、遠心分離機を用いて250Gで3分間水切りを行った後、袋の重量W 1 (g)を測定した。 The bag was pulled up after 60 minutes, after 3 minutes drained 250G using a centrifugal separator, and weighed W 1 (g) of the bag. また、同様の操作を吸収剤組成物を用いないで行い、そのときの重量W 0 (g)を測定した。 Also conducted without using the absorbent composition the same operation and weighed W 0 (g) at that time. そして、これら重量W 1 And, these weight W 1 ·
0から、次式、 吸収倍率(g/g)=(重量W 1 (g)−重量W From W 0, the following equation, the absorption capacity (g / g) = (Weight W 1 (g) - Weight W
0 (g))/吸収剤組成物の重量(g) に従って吸収倍率(g/g)を算出した。 0 (g)) / was calculated absorption capacity (g / g) according to the weight of the absorbent composition (g).

【0082】(b)拡散吸収倍率 先ず、拡散吸収倍率の測定に用いる測定装置について、 [0082] (b) diffusing absorbency First, the measurement device used for measuring the diffusing absorbency,
図1および図2を参照しながら、以下に簡単に説明する。 With reference to FIGS. 1 and 2, briefly described below.

【0083】図1に示すように、測定装置は、天秤1 [0083] As shown in FIG. 1, the measuring device, the balance 1
と、この天秤1上に載置された所定容量の容器2と、外気吸入パイプ3と、導管4と、ガラスフィルタ6と、このガラスフィルタ6上に載置された測定部5とからなっている。 When a container 2 of the placed a predetermined capacity on the balance 1, an air-inhaling pipe 3, a conduit 4, a glass filter 6, taken from the placed on the glass filter 6 has been measured portion 5 which there. 上記の容器2は、その頂部に開口部2aを、その側面部に開口部2bをそれぞれ有しており、開口部2 Container 2 above, an opening 2a at its top, has respectively an opening 2b at its side portions, the opening 2
aに外気吸入パイプ3が嵌入される一方、開口部2bに導管4が取り付けられている。 While external air intake pipe 3 is fitted to a, the conduit 4 is attached to the opening 2b. また、容器2には、所定量の生理食塩水12が入っている。 Further, the container 2, filled with a predetermined quantity of saline 12. 外気吸入パイプ3の下端部は、生理食塩水12中に没している。 The lower end of the air-inhaling pipe 3 is submerged in the saline 12. 上記のガラスフィルタ6は、直径70mmに形成されている。 Glass filter 6 mentioned above is formed with a diameter 70 mm. そして、容器2およびガラスフィルタ6は、導管4によって互いに連通している。 Then, the container 2 and the glass filter 6 communicate with each other by a conduit 4. また、ガラスフィルタ6は、その上面が、外気吸入パイプ3の下端に対してごく僅かに高い位置になるようにして固定されている。 The glass filter 6 has its upper surface is fixed so as to be only slightly higher position relative to the lower end of the air-inhaling pipe 3.

【0084】図2に示すように、上記の測定部5は、濾紙7と、シート8と、支持円筒9と、この支持円筒9の底部に貼着された金網10と、重り11とを有している。 [0084] As shown in FIG. 2, the measurement section 5 described above, the filter paper 7, a seat 8, chromatic and supporting cylinder 9, and attached to the wire mesh 10 at the bottom of the supporting cylinder 9, and a weight 11 doing. そして、測定部5は、ガラスフィルタ6上に、濾紙7、シート8、支持円筒9(つまり、金網10)がこの順に載置されると共に、支持円筒9内部、即ち、金網1 The measurement unit 5, on the glass filter 6, the filter paper 7, the sheet 8, the supporting cylinder 9 (i.e., metal gauze 10) with is placed in this order, the internal supporting cylinder 9, namely, wire mesh 1
0上に重り11が載置されてなっている。 0 weight 11 on top is made is placed. シート8は、 Sheet 8,
ポリエチレンテレフタレート(PET)からなり、中央部に直径18mmの開口部を有する厚さ0.1mmのドーナツ状に形成されている。 Made of polyethylene terephthalate (PET), and is formed in a donut shape having a thickness of 0.1mm with an opening diameter of 18mm in the central portion. 支持円筒9は、内径60m Supporting cylinder 9 has an inner diameter 60m
mに形成されている。 It is formed to m. 金網10は、ステンレスからなり、JIS規格で400メッシュ(目の大きさ38μ Wire gauze 10 is made of stainless steel, 400 mesh JIS standard (mesh size 38μ
m)に形成されている。 It is formed in m). そして、金網10上に所定量の吸収剤組成物が均一に撒布されるようになっている。 Then, so that the absorbent composition of the predetermined amount onto the wire mesh 10 is uniformly sprayed. 重り11は、金網10、即ち、吸収剤組成物に対して、2 Relative weights 11, a wire mesh 10, i.e., the absorbent composition, 2
0g/cm 2 (1.96kPa)の荷重を均一に加えることができるように、その重量が調整されている。 Load so that it can uniformly apply a of 0g / cm 2 (1.96kPa), its weight is adjusted.

【0085】上記構成の測定装置を用いて拡散吸収倍率を測定した。 [0085] was measured diffusing absorbency using the measurement device with the above structure. 測定方法について以下に説明する。 It will be described below measurement method.

【0086】先ず、容器2に所定量の生理食塩水12を入れる、容器2に外気吸入パイプ3を嵌入する、等の所定の準備動作を行った。 [0086] First, place the predetermined amount of saline 12 in the container 2, fitting the air-inhaling pipe 3 to the container 2, it performs a predetermined preparation operation and the like. 次に、ガラスフィルタ6上に濾紙7を載置し、この濾紙7上にシート8を、その開口部がガラスフィルタ6の中心部に位置するようにして載置した。 Next, placing a filter paper 7 on the glass filter 6, the sheet 8 on the filter paper 7, the opening portion is placed so as to be positioned in the center of the glass filter 6. 一方、これら載置動作に並行して、支持円筒9内部、即ち、金網10上に吸収剤組成物1.5gを均一に撒布し、この吸収剤組成物上に重り11を載置した。 On the other hand, in parallel with these mounting 置動 operation, the internal supporting cylinder 9, i.e., uniformly spraying the absorbent composition 1.5g on a wire mesh 10, placing the weight 11 on the absorbent composition.

【0087】次いで、シート8上に、金網10、つまり、吸収剤組成物および重り11を載置した上記支持円筒9を、その中心部がガラスフィルタ6の中心部に一致するようにして載置した。 [0087] Then, on the sheet 8, a wire mesh 10, i.e., the supporting cylinder 9 was placed on the absorbent composition and the weight 11, the center portion so as to coincide with the center of the glass filter 6 placed did.

【0088】そして、シート8上に支持円筒9を載置した時点から、60分間にわたって吸収剤組成物が吸収した生理食塩水12の重量W 2 (g)を、天秤1を用いて測定した。 [0088] Then, from the point of placing the supporting cylinder 9 on the sheet 8, the weight W 2 of the physiological saline 12 absorbent composition has absorbed (g) over 60 min, was measured using a balance 1. 尚、図2および図3に示すように、生理食塩水12は、シート8の開口部を通過した後、吸収剤組成物の横方向(図中、矢印で示す)にほぼ均一に拡散しながら、吸収剤組成物に吸収された。 As shown in FIGS. 2 and 3, the saline 12 is passed through the opening of the sheet 8, (shown by arrows) transverse direction of the absorbent composition with substantially uniformly diffused in It was absorbed into the absorbent composition.

【0089】そして、上記の重量W 2から、次式、 拡散吸収倍率(g/g)=重量W 2 (g)/吸収剤組成物の重量(g) に従って、吸収開始から60分後の拡散吸収倍率(g/ [0089] Then, the weight W 2 of the above, the following equation, diffusing absorbency (g / g) = according to the weight of the weight W 2 (g) / absorbent composition (g), the diffusion after 60 minutes from the absorption initiation absorption capacity (g /
g)を算出した。 g) was calculated.

【0090】(c)拡散吸収指数 拡散吸収指数は、上記拡散吸収倍率の測定に用いた測定装置を用い、シート8上に支持円筒9を載置した時点から、吸収剤組成物が60分間かけて吸収していく生理食塩水12の重量を、天秤1を用いて経時的に測定することによって求めた。 [0090] (c) diffusion absorption index diffusion absorption index, using a measuring apparatus used for measurement of the diffusing absorbency, from the point of placing the supporting cylinder 9 on the sheet 8, multiplied absorbent composition is 60 min the weight of saline 12 to continue to absorb Te was determined by measured over time using a balance 1. つまり、天秤1を用いて生理食塩水12の重量を分単位、より好ましくは秒単位で測定し、 That, in minutes on the weight of the physiological saline 12 using the balance 1, more preferably measured in seconds,
これら測定結果から、単位時間当たりの最大吸収量を求め、その値を拡散吸収指数(g/g・min)とした。 These measurement results, determine the maximum amount of absorption per unit time was the value as diffusion absorption index (g / g · min).

【0091】(d)吸収体の拡散吸収倍率 先ず、吸収体の拡散吸収倍率の測定に用いる測定装置について、図4および図5を参照しながら、以下に簡単に説明する。 [0091 (d) The diffusing absorbency of the absorbent body First, the measurement device used for measuring the diffusing absorbency of the absorbent body, with reference to FIGS. 4 and 5 will be briefly described below. 尚、説明の便宜上、前記拡散吸収倍率の測定に用いる測定装置と同一の機能を有する構成には、同一の符号を付記し、その説明を省略する。 For convenience of explanation, wherein the arrangement has a measuring device and the same functions used in the measurement of diffusion absorption capacity, the same reference numerals, and description thereof is omitted.

【0092】図4に示すように、測定装置は、天秤1 [0092] As shown in FIG. 4, the measuring device, the balance 1
と、容器2と、外気吸入パイプ3と、導管4と、直径1 When a container 2, an air-inhaling pipe 3, a conduit 4, a diameter of 1
20mmに形成されたガラスフィルタ6と、このガラスフィルタ6上に載置された測定部15とからなっている。 A glass filter 6 is formed in 20 mm, which is from the measurement unit 15 which is placed on the glass filter 6. 図5に示すように、上記の測定部15は、濾紙7 As shown in FIG. 5, the above-mentioned measurement unit 15, the filter paper 7
と、シート8と、支持角筒19と、重り11とを有している。 When a sheet 8, a supporting rectangular tube 19, and a weight 11. 尚、測定部15は、前記の金網は有していない。 The measurement unit 15, the wire mesh does not.

【0093】測定部15は、ガラスフィルタ6上に、濾紙7、シート8、支持角筒19がこの順に載置されると共に、支持角筒19内部に重り11が載置されてなっている。 [0093] Measurement unit 15, on the glass filter 6, the filter paper 7, the sheet 8, with the support rectangular tube 19 is placed in this order, supporting rectangular tube 19 inside the weight 11 is made is placed. シート8は、ポリエチレンテレフタレートからなり、中央部に12.5mm×100mmの長方形の開口部を有する厚さ0.1mmの矩形状に形成されている。 Sheet 8 is made of polyethylene terephthalate, and is formed in a rectangular shape having a thickness of 0.1mm having a rectangular opening of 12.5 mm × 100 mm in a central portion.
支持角筒19は、内寸法が100mm×100mmに形成されている。 Supporting rectangular tube 19, the inner dimensions are formed on 100 mm × 100 mm. そして、支持角筒19内部に所定の大きさの吸収体が載置されるようになっている。 The absorbent body having a predetermined size to the internal support angle cylinder 19 is adapted to be placed. 測定装置のその他の構成は、前記拡散吸収倍率の測定に用いる測定装置の構成と同一である。 Other configurations of the measuring device is the same as that of the measuring device used for measuring the diffusing absorbency.

【0094】上記構成の測定装置を用いて吸収体の拡散吸収倍率を測定した。 [0094] was measured diffusing absorbency of the absorbent body using a measurement device with the above structure. 測定方法について以下に説明する。 It will be described below measurement method. 尚、測定すべき吸収体は、下記の方法により作成した。 The absorption body to be measured was prepared as follows. 即ち、吸収剤組成物50重量部と、親水性繊維としての木材粉砕パルプ50重量部とを、ミキサーを用いて乾式混合した。 That is, the absorbent composition 50 parts by weight, and a crushed wood pulp 50 parts by weight of a hydrophilic fiber, were dry blended using a mixer. 得られた混合物を100mm×100m The resulting mixture was 100 mm × 100 m
mの大きさのウェブに成形した後、このウェブを圧力2 After forming to the size of the web of the m, the pressure the web 2
kg/cm 2 (196.14kPa)で1分間プレスすることにより、坪量が約0.047g/cm 2の吸収体を得た。 by pressing for 1 minute kg / cm 2 (196.14kPa), basis weight was obtained absorber about 0.047 g / cm 2.

【0095】先ず、測定装置については、所定の準備動作を行った。 [0095] First, the measuring apparatus performs a predetermined preparation operation. 次に、ガラスフィルタ6上に濾紙7を載置し、この濾紙7上にシート8を、その開口部がガラスフィルタ6の中心部に位置するようにして載置した。 Next, placing a filter paper 7 on the glass filter 6, the sheet 8 on the filter paper 7, the opening portion is placed so as to be positioned in the center of the glass filter 6. 次いで、シート8上に支持角筒19を、その中心部がガラスフィルタ6の中心部に一致するようにして載置した。 Then, the support angle cylinder 19 on the seat 8, the central portion is placed so as to coincide with the center of the glass filter 6.

【0096】その後、支持角筒19内部、即ち、シート8上に吸収体を載置し、この吸収体上に重り11を載置した。 [0096] Then, the internal supporting rectangular tube 19, i.e., placing the absorbent body on the sheet 8, placing the weight 11 on the absorber. 尚、吸収体および重り11の載置動作は、素早く行った。 It should be noted, 置動 work placement of the absorbent body and the weight 11 was carried out quickly.

【0097】そして、シート8上に吸収体を載置した時点から、60分間にわたって吸収体が吸収した生理食塩水12の重量W 3 (g)を、天秤1を用いて測定した。 [0097] Then, from the point of placing the absorbent body on the sheet 8, the weight W 3 of physiological saline 12 where the absorber has absorbed (g) over 60 min, was measured using a balance 1.
尚、図5および図6に示すように、生理食塩水12は、 As shown in FIGS. 5 and 6, saline 12,
シート8の開口部を通過した後、吸収体中を横方向(図中、矢印で示す)にほぼ均一に拡散しながら、吸収体に吸収された。 After passing through the opening of the sheet 8, through the absorbent body (shown by arrows) transverse direction while substantially uniformly diffused in, it has been absorbed into the absorbent body.

【0098】そして、上記の重量W 3から、次式、 吸収体の拡散吸収倍率(g/g)=重量W 3 (g)/吸収体の重量(g) に従って、吸収開始から60分後の、吸収体の拡散吸収倍率(g/g)を算出した。 [0098] Then, the weight W 3 of the following formula, according diffusing absorbency of the absorbent body weight (g / g) = Weight W 3 (g) / absorbent (g), the absorption begins after 60 minutes , it was calculated diffusing absorbency of the absorbent body (g / g).

【0099】(e)吸収体の吸収速度(コア・アクイジション) 測定すべき吸収体は、下記の方法により作成した。 [0099] (e) The rate of absorption of the absorber (core acquisition) to be measured absorber, were prepared by the following method. 即ち、吸収剤組成物8.8gと、木材粉砕パルプ8.8g That is, the absorbent composition 8.8g, crushed wood pulp 8.8g
とを、ミキサーを用いて乾式混合した。 Bets, were dry blended using a mixer. 得られた混合物を260mm×150mmの大きさのウェブに成形することにより、吸収体を得た。 The resulting mixture by forming a web of the size of 260 mm × 150 mm, to obtain an absorbent.

【0100】一方、尿素1.9重量%、NaCl0.8 [0100] On the other hand, urea 1.9 weight%, NaCl0.8
重量%、CaCl 2 0.1重量%、および、MgSO 4 Wt%, CaCl 2 0.1% by weight, and, MgSO 4
0.1重量%の組成(残りは水)を有する水溶液、即ち、人工尿を調製した。 Aqueous solution having a 0.1% by weight of the composition (remainder water), i.e., to prepare artificial urine.

【0101】そして、上記の吸収体全体に、18g/c [0101] Then, the entire absorber of the above, 18g / c
2 (1.77kPa)の荷重を均一に加えると共に、 m 2 uniformly with applying a load of (1.77kPa),
該吸収体の中心部分に、直径30mm、高さ120mm The central portion of the absorbent body, diameter 30 mm, height 120mm
の円筒を押し当て、該円筒を垂直に立てた。 Pressing a cylinder of, it made a cylindrical vertically. 次いで、該円筒内に25℃の人工尿50gを素早く(一気に)注ぎ、人工尿を注ぎ始めた時点から、該人工尿が吸収体に全て吸収されるまでの時間を測定し、1回目の吸収速度(秒)とした。 Then, quickly artificial urine 50g of 25 ° C. in the cylinder (once) was poured, from the time of starting to pour artificial urine, the artificial urine measures the time until all absorbed into the absorbent body, the first absorption It was the speed (in seconds). その後、上記測定に用いた吸収体を用いて、50分間隔で同様の測定を2回繰り返し、2回目の吸収速度(秒)、および3回目の吸収速度(秒)を測定した。 Then, using the absorber used in the above measurement, repeated twice same measurement at 50 minute intervals, to measure a second absorption rate (seconds), and the third absorption rate (seconds). 吸収体の液拡散性は、これら吸収速度が速い程、 Liquid diffusion of the absorber, as these absorption rate is fast,
高いと評価することができる。 It can be evaluated as high.

【0102】(f)吸収物品の性能評価(キューピー人形テスト) 測定すべき吸収物品は、下記の方法により作成した。 [0102] (f) an absorbent article performance evaluation (kewpie doll test) to be measured of the absorbent article, was prepared by the following method. 即ち、先ず、吸収剤組成物50重量部と、木材粉砕パルプ50重量部とを、ミキサーを用いて乾式混合した。 That is, first, the absorbent composition 50 parts by weight, and 50 parts by weight of crushed wood pulp were dry-mixed using a mixer. 次いで、得られた混合物を、400メッシュ(目の大きさ3 Then, the resulting mixture, 400 mesh (mesh size: 3
8μm)に形成されたワイヤースクリーン上にバッチ型空気抄造装置を用いて空気抄造することにより、120 By air papermaking using a batch-type air paper making device onto a wire screen formed to 8 [mu] m), 120
mm×400mmの大きさのウェブに成形した。 It was molded to the size of the web of mm × 400mm. さらに、このウェブを圧力2kg/cm 2 (196.14k Furthermore, the pressure this web 2kg / cm 2 (196.14k
Pa)で5秒間プレスすることにより、坪量が約0.0 By pressing 5 seconds Pa), a basis weight of about 0.0
47g/cm 2の吸収体を得た。 To obtain an absorber of 47g / cm 2.

【0103】続いて、不透液性のポリプロピレンからなり、いわゆるレッグギャザーを有するバックシート(液不透過性シート)、上記の吸収体、および、透液性のポリプロピレンからなるトップシート(液透過性シート) [0103] Subsequently, consists impermeable polypropylene, the back sheet having a so-called leg gather (liquid-impermeable sheet), the absorber above and the topsheet (liquid-permeable consisting liquid-permeable polypropylene sheet)
を、両面テープを用いてこの順に互いに貼着すると共に、この貼着物に2つのいわゆるテープファスナーを取り付けることにより、吸収物品(つまり、紙オムツ)を得た。 The, the stuck together in this order by using a double-sided tape, by attaching the two so-called tape fasteners to the stuck kimono, give an absorbent article (i.e., diapers) a.

【0104】上記の吸収物品を、いわゆるキューピー人形(体長55cm、重量5kg)に装着し、該人形をうつ伏せ状態にした後、吸収物品と人形との間にチューブを差込み、人体において排尿を行う位置に相当する位置に、1回当たり50mlの生理食塩水を、20分間隔で順次注入した。 [0104] The absorbent article described above, attached to a so-called Kewpie doll (body length 55cm, weight 5 kg), after the state prone position the doll, position for urination insert, in the human body the tube between the absorbent article and the dolls to the corresponding position, a saline 50ml per were sequentially injected at 20 minute intervals. そして、注入した生理食塩水が吸収物品に吸収されなくなって外部に漏れ出した時点で上記の注入動作を終了し、このときまでに注入した生理食塩水の量を測定した。 Then, injected saline ends the injection operation when leaked to the outside is no longer absorbed by the absorbent article, to determine the amount of saline was injected by this time.

【0105】上記の測定を4回繰り返し、得られた4つの測定値の平均を求め、この値を吸収量(g)とした。 [0105] repeated 4 times the measurement of the, an average of four measurements obtained was the value as absorption (g).
そして、吸収量が多い程、吸収物品の性能が良好であると評価した。 The larger the absorption, performance of the absorbent article is evaluated as good.

【0106】〔実施例1〕中和率75モル%のアクリル酸ナトリウム(親水性不飽和単量体)39重量%水溶液5,500gに、内部架橋剤としてのトリメチロールプロパントリアクリレート3.59gを溶解させて反応液とした。 [0106] in Example 1 neutralization ratio 75 mol% of sodium acrylate (hydrophilic unsaturated monomer) 39 wt% aqueous solution of 5,500 g, trimethylol propane triacrylate 3.59g as an internal crosslinking agent and a reaction solution. 次に、この反応液を、窒素ガス雰囲気下で30 Then, the reaction solution under a nitrogen gas atmosphere 30
分間脱気した。 It was degassed minutes. 次いで、シグマ型羽根を2本有する内容積10Lのジャケット付きステンレス製双腕型ニーダーに蓋を取り付けて形成した反応器に、上記の反応液を供給し、反応液を30℃に保ちながら系を窒素ガス置換した。 Then, the reactor formed by attaching a lid to a jacketed stainless double-arm kneader having an inner volume of 10L for 2 inborn sigma type blades, and supplying the reaction solution, and the system while maintaining the reaction solution at 30 ° C. nitrogen gas was replaced.

【0107】続いて、反応液を撹拌しながら、重合開始剤としての過硫酸アンモニウム2.4gおよびL−アスコルビン酸0.12gを添加したところ、およそ1分後に重合が開始した。 [0107] Subsequently, while stirring the reaction solution, was added ammonium persulfate 2.4g and L- ascorbic acid 0.12g as a polymerization initiator, polymerization started after about 1 minute. そして、30℃〜80℃で重合を行い、重合を開始してから60分後に反応を終了して含水ゲル状重合体を取り出した。 The polymerization is proceeded at 30 ° C. to 80 ° C., it was removed hydrogel polymer to complete the reaction from the start of the polymerization after 60 minutes.

【0108】得られた含水ゲル状重合体は、その径が約5mmに細分化されていた。 [0108] obtained water-containing gel-like polymer particle has a diameter subdivided into approximately 5 mm. この細分化された含水ゲル状重合体を50メッシュ(目開き300μm)の金網上に広げ、150℃で90分間熱風乾燥した。 Spread The finely divided hydrous gel-like polymer on a wire mesh of 50 mesh (mesh opening 300 [mu] m), and dried with hot air for 90 minutes at 0.99 ° C.. 次いで、乾燥物を振動ミルを用いて粉砕し、さらに20メッシュ(目開き850μm)の金網で分級することにより、平均粒子径が400μmで、しかも、粒子径が106μm Then, by the dry product was pulverized with a vibration mill and further classified with a 20 mesh wire gauze (mesh opening 850 .mu.m), the average particle diameter of 400 [mu] m, moreover, the particle diameter 106μm
未満の粒子の割合が5重量%の不定形破砕状の吸水性樹脂前駆体を得た。 Percentage of particles less than was obtained 5 wt% of the irregularly pulverized shaped water absorbent resin precursor.

【0109】得られた吸水性樹脂前駆体100重量部に、第一表面架橋剤としてのエチレングリコール〔SP [0109] the water-absorbing resin precursor 100 parts by weight of the obtained ethylene glycol as a first surface-crosslinking agent [SP
値:δ=14.6(cal/cm 31/2 (0.029 Value: δ = 14.6 (cal / cm 3) 1/2 (0.029
9(J/m 31/2 )〕0.5重量部と、第二表面架橋剤としてのグリセロールポリグリシジルエーテル〔SP 9 (J / m 3) 1/2 ) ] and 0.5 part by weight of glycerol polyglycidyl ether as a second surface-crosslinking agent [SP
値:δ=10.8(cal/cm 31/2 (0.022 Value: δ = 10.8 (cal / cm 3) 1/2 (0.022
1(J/m 31/2 )〕0.1重量部と、水3重量部と、エチルアルコール1重量部とからなる表面架橋剤溶液を混合した。 1 and (J / m 3) 1/2)] 0.1 parts by weight, and 3 parts by weight of water, was mixed with a surface cross-linking agent solution consisting of ethyl alcohol 1 part by weight. 上記の混合物を195℃で40分間加熱処理することにより、吸水性樹脂を得た。 By heating for 40 minutes the mixture at 195 ° C., to obtain a water-absorbent resin. 得られた吸水性樹脂の平均粒子径は400μmであり、粒子径が10 The average particle diameter of the resulting water-absorbent resin was 400 [mu] m, particle diameter of 10
6μm未満の粒子の割合は3重量%であった。 Proportion of 6μm less of the particles was 3 wt%.

【0110】吸水性樹脂の諸性能を上記の方法によって測定した結果、吸収倍率は30g/g、拡散吸収倍率は30.1g/g、拡散吸収指数は1.20g/g・mi [0110] The various properties of the water absorbent resin results measured by the above method, absorption capacity 30 g / g, diffusion absorption capacity 30.1 g / g, diffusion absorption index 1.20 g / g · mi
nであった。 It was n.

【0111】次に、上記の吸水性樹脂100gに、水不溶性無機粉体としての微粒子状の親水性二酸化ケイ素(商品名・アエロジル200;日本アエロジル株式会社製)0.5gを添加・混合することにより、本発明にかかる吸収剤組成物を得た。 [0111] Then, the above water absorbent resin 100 g, particulate hydrophilic silicon dioxide as the water-insoluble inorganic powder (trade name Aerosil 200; manufactured by Nippon Aerosil Co., Ltd.) added and mixed to a 0.5g gave a absorbent composition according to the present invention.

【0112】そして、上記吸収剤組成物の諸性能、並びに、該吸収剤組成物を用いた吸収体および吸収物品の諸性能を上記の方法によって測定した。 [0112] Then, various performances of the absorbent composition, as well as various properties of the absorber and absorbent article using the absorbent composition was determined by the above methods. その結果、吸収剤組成物の吸収倍率は30g/g、拡散吸収倍率は26. As a result, the absorption capacity of the absorbent composition is 30 g / g, diffusion absorption capacity 26.
9g/g、拡散吸収指数は2.87g/g・minであった。 9g / g, diffusion absorption index was 2.87g / g · min. 吸収体の拡散吸収倍率は18.9g/g、1回目の吸収速度は34秒、2回目の吸収速度は69秒、3回目の吸収速度は77秒であった。 Diffusing absorbency of the absorbent body 18.9 g / g, 1 round of the absorption rate 34 seconds, the absorption rate of the second time 69 seconds, the absorption rate of the third was 77 seconds. 吸収物品の吸収量は2 Absorption amount of the absorbent article 2
75gであり、性能は良好であった。 Is 75g, the performance was good. 結果を表1に示す。 The results are shown in Table 1.

【0113】〔実施例2〕上記の実施例1で得られた吸水性樹脂100gに、ポリアミン化合物としての重量平均分子量70,000のポリエチレンイミン30重量% [0113] Example 2 the resulting water-absorbent resin 100g in Example 1 above, polyethyleneimine having a weight-average molecular weight of 70,000 as a polyamine compound 30 wt%
水溶液(商品名・エポミンP−1000;株式会社日本触媒製)5gを添加・混合した。 Aqueous solution (trade name, Epomin P-1000; manufactured by Nippon Shokubai Co., Ltd.) was added to and mixed with 5g. 次いで、該混合物を熱風乾燥機に入れて90℃で20分間保持して硬化させた。 Then cured and the mixture was held for 20 minutes at placed in 90 ° C. in a hot air dryer. 得られた硬化物を、目の大きさが840μmの金網で分級し、通過物に水不溶性無機粉体としての微粒子状の親水性二酸化ケイ素(商品名・カープレックス22 The cured product obtained, the size of the eye was classified by wire mesh 840Myuemu, particulate hydrophilic silicon dioxide to pass product as water-insoluble inorganic powder (trade name, Carplex 22
S;塩野義製薬株式会社製)0.3gを添加・混合することにより、本発明にかかる吸収剤組成物を得た。 S; Shionogi by adding and mixing the Ltd.) 0.3 g, was obtained absorbent composition according to the present invention.

【0114】そして、上記吸収剤組成物の諸性能、並びに、該吸収剤組成物を用いた吸収体および吸収物品の諸性能を上記の方法によって測定した。 [0114] Then, various performances of the absorbent composition, as well as various properties of the absorber and absorbent article using the absorbent composition was determined by the above methods. 結果をまとめて表1に示す。 The results are summarized in Table 1.

【0115】〔実施例3〕アクリル酸20重量%水溶液5,500gに、内部架橋剤としてのN,N'−メチレンビスアクリルアミド2.35gを溶解させて反応液とした。 [0115] In Example 3 Acrylic acid 20 wt% aqueous solution of 5,500 g, of N as an internal crosslinking agent, by dissolving N'- methylenebisacrylamide 2.35g prepare a reaction solution. 次に、この反応液を、窒素ガス雰囲気下で30分間脱気した。 Then, the reaction solution was deaerated for 30 minutes under nitrogen gas atmosphere. 次いで、実施例1の反応器と同様の反応器に、上記の反応液を供給し、反応液を30℃に保ちながら系を窒素ガス置換した。 Then, the reactor similar to the reactor of Example 1, and supplying the reaction solution, the system was substituted nitrogen gas while maintaining the reaction solution at 30 ° C..

【0116】続いて、反応液を撹拌しながら、過硫酸アンモニウム1.5gおよびL−アスコルビン酸0.07 [0116] Subsequently, while stirring the reaction solution, ammonium persulfate 1.5g and L- ascorbic acid 0.07
gを添加したところ、およそ1分後に重合が開始した。 Was added g, polymerization started after about 1 minute.
そして、30℃〜80℃で重合を行い、重合を開始してから60分後に、中和剤である炭酸ナトリウム606. The polymerization is proceeded at 30 ° C. to 80 ° C., after 60 minutes from the initiation of polymerization, sodium carbonate 606 is a neutralizing agent.
7gを加えて撹拌し、中和した。 Stirred with 7 g, and neutralized. その後、反応を終了して含水ゲル状重合体を取り出した。 Then removed the hydrogel polymer to complete the reaction.

【0117】得られた含水ゲル状重合体は、中和率が7 [0117] The obtained hydrogel polymer, neutralization rate 7
5モル%であり、その径が約5mmに細分化されていた。 5 is the mole%, its diameter has been subdivided into approximately 5 mm. この細分化された含水ゲル状重合体を50メッシュ(目開き300μm)の金網上に広げ、150℃で90 Spread The finely divided hydrous gel-like polymer on a wire mesh of 50 mesh (mesh opening 300 [mu] m), 90 at 0.99 ° C.
分間熱風乾燥した。 Minutes and dried with hot air. 次いで、乾燥物を振動ミルを用いて粉砕し、さらに20メッシュ(目開き850μm)の金網で分級することにより、平均粒子径が390μmで、 Then, by the dry product was pulverized with a vibration mill and further classified with a wire net of 20 mesh (mesh opening 850 .mu.m), the average particle diameter is at 390 [mu] m,
しかも、粒子径が106μm未満の粒子の割合が4重量%の不定形破砕状の吸水性樹脂前駆体を得た。 Moreover, the particle diameter ratio of particles less than 106μm was obtained 4% by weight of irregularly pulverized water-absorbent resin precursor.

【0118】得られた吸水性樹脂前駆体100重量部に、第一表面架橋剤としてのプロピレングリコール〔S [0118] the water-absorbing resin precursor 100 parts by weight of the obtained propylene glycol as a first surface-crosslinking agent [S
P値:δ=12.6(cal/cm 31/2 (0.02 P-value: δ = 12.6 (cal / cm 3) 1/2 (0.02
58(J/m 31/2 )〕0.75重量部と、第二表面架橋剤としてのプロピレングリコールジグリシジルエーテル〔SP値:δ=10.1(cal/cm 3 58 (J / m 3) 1/2 ) ] and 0.75 parts by weight, propylene glycol diglycidyl ether as a second surface-crosslinking agent [SP value: δ = 10.1 (cal / cm 3)
1/2 (0.0207(J/m 31/2 )〕0.05重量部と、水3重量部と、エチルアルコール0.75重量部とからなる表面架橋剤溶液を混合した。 And 1/2 (0.0207 (J / m 3 ) 1/2) ] 0.05 parts by weight, and 3 parts by weight of water, was mixed with a surface cross-linking agent solution consisting of ethyl alcohol 0.75 parts by weight. 上記の混合物を195℃で40分間加熱処理することにより、吸水性樹脂を得た。 By heating for 40 minutes the mixture at 195 ° C., to obtain a water-absorbent resin. 得られた吸水性樹脂の平均粒子径は390μ The average particle diameter of the resulting water-absorbent resin 390μ
mであり、粒子径が106μm未満の粒子の割合は3重量%であった。 M, and a particle diameter ratio of particles less than 106μm was 3 wt%.

【0119】吸水性樹脂の諸性能を上記の方法によって測定した結果、吸収倍率は38g/g、拡散吸収倍率は33.9g/g、拡散吸収指数は0.90g/g・mi [0119] The various properties of the water absorbent resin results measured by the above method, absorption capacity 38 g / g, diffusion absorption capacity 33.9 g / g, diffusion absorption index 0.90 g / g · mi
nであった。 It was n.

【0120】次に、上記の吸水性樹脂100gに、水不溶性無機粉体としての微粒子状の親水性二酸化ケイ素(商品名・レオロシールQS−20;徳山曹達株式会社(現・株式会社トクヤマ)製)0.3gを添加・混合することにより、本発明にかかる吸収剤組成物を得た。 [0120] Then, the above water absorbent resin 100 g, particulate hydrophilic silicon dioxide as the water-insoluble inorganic powder (trade name, Reolosil QS-20; manufactured by Tokuyama Soda Co., Ltd. (currently Tokuyama Corporation)) by adding and mixing 0.3 g, to obtain a absorbent composition according to the present invention.

【0121】そして、上記吸収剤組成物の諸性能、並びに、該吸収剤組成物を用いた吸収体および吸収物品の諸性能を上記の方法によって測定した。 [0121] Then, various performances of the absorbent composition, as well as various properties of the absorber and absorbent article using the absorbent composition was determined by the above methods. 結果をまとめて表1に示す。 The results are summarized in Table 1.

【0122】〔比較例1〕中和率75モル%のアクリル酸ナトリウム39重量%水溶液5,500gに、トリメチロールプロパントリアクリレート7.18gを溶解させて反応液とした。 [0122] In Comparative Example 1 neutralization ratio 75 mol% of sodium acrylate 39 wt% aqueous solution of 5,500 g, and a reaction solution trimethylolpropane triacrylate 7.18 g. 次に、この反応液を、窒素ガス雰囲気下で30分間脱気した。 Then, the reaction solution was deaerated for 30 minutes under nitrogen gas atmosphere. 次いで、実施例1の反応器と同様の反応器に、上記の反応液を供給し、反応液を30 Then, the reactor similar to the reactor of Example 1, and supplying the reaction solution, the reaction solution 30
℃に保ちながら系を窒素ガス置換した。 ℃ in the system while keeping was replaced nitrogen gas.

【0123】続いて、反応液を撹拌しながら、過硫酸ナトリウム5.0gおよびL−アスコルビン酸0.25g [0123] Subsequently, while stirring the reaction solution, sodium persulfate 5.0g and L- ascorbic acid 0.25g
を添加したところ、およそ1分後に重合が開始した。 It was added and the polymerization started after about 1 minute. そして、30℃〜80℃で重合を行い、重合を開始してから60分後に反応を終了して含水ゲル状重合体を取り出した。 The polymerization is proceeded at 30 ° C. to 80 ° C., it was removed hydrogel polymer to complete the reaction from the start of the polymerization after 60 minutes.

【0124】得られた含水ゲル状重合体は、その径が約5mmに細分化されていた。 [0124] obtained water-containing gel-like polymer particle has a diameter subdivided into approximately 5 mm. この細分化された含水ゲル状重合体を50メッシュ(目開き300μm)の金網上に広げ、150℃で90分間熱風乾燥した。 Spread The finely divided hydrous gel-like polymer on a wire mesh of 50 mesh (mesh opening 300 [mu] m), and dried with hot air for 90 minutes at 0.99 ° C.. 次いで、乾燥物を振動ミルを用いて粉砕し、さらに20メッシュ(目開き850μm)の金網で分級することにより、平均粒子径が360μmで、しかも、粒子径が106μm Then, by the dry product was pulverized with a vibration mill and further classified with a 20 mesh wire gauze (mesh opening 850 .mu.m), the average particle diameter at 360 .mu.m, moreover, the particle diameter 106μm
未満の粒子の割合が5重量%の不定形破砕状の吸水性樹脂を得た。 Percentage of particles less than was obtained 5 wt% of the irregularly pulverized shaped water absorbent resin.

【0125】上記の吸水性樹脂を、そのまま比較用の吸収剤組成物とした。 [0125] The above water-absorbent resin, was as absorbent composition for comparison. 上記比較用吸収剤組成物の諸性能、 Various properties of the comparative absorbent composition,
並びに、該比較用吸収剤組成物を用いた比較用吸収体および比較用吸収物品の諸性能を上記の方法によって測定した。 And were the various performances of the comparative absorber and the comparative absorbent article using the comparative absorbent composition was determined by the above methods. 結果をまとめて表1に示す。 The results are summarized in Table 1.

【0126】〔比較例2〕中和率75モル%のアクリル酸ナトリウム39重量%水溶液5,500gに、トリメチロールプロパントリアクリレート3.59gを溶解させて反応液とした。 [0126] In Comparative Example 2 neutralization ratio 75 mol% of sodium acrylate 39 wt% aqueous solution of 5,500 g, and a reaction solution trimethylolpropane triacrylate 3.59 g. 次に、この反応液を、窒素ガス雰囲気下で30分間脱気した。 Then, the reaction solution was deaerated for 30 minutes under nitrogen gas atmosphere. 次いで、実施例1の反応器と同様の反応器に、上記の反応液を供給し、反応液を30 Then, the reactor similar to the reactor of Example 1, and supplying the reaction solution, the reaction solution 30
℃に保ちながら系を窒素ガス置換した。 ℃ in the system while keeping was replaced nitrogen gas.

【0127】続いて、反応液を撹拌しながら、過硫酸アンモニウム2.4gおよびL−アスコルビン酸0.12 [0127] Subsequently, while stirring the reaction solution, ammonium persulfate 2.4g and L- ascorbic acid 0.12
gを添加したところ、およそ1分後に重合が開始した。 Was added g, polymerization started after about 1 minute.
そして、30℃〜80℃で重合を行い、重合を開始してから60分後に反応を終了して含水ゲル状重合体を取り出した。 The polymerization is proceeded at 30 ° C. to 80 ° C., it was removed hydrogel polymer to complete the reaction from the start of the polymerization after 60 minutes.

【0128】得られた含水ゲル状重合体は、その径が約5mmに細分化されていた。 [0128] obtained water-containing gel-like polymer particle has a diameter subdivided into approximately 5 mm. この細分化された含水ゲル状重合体を50メッシュ(目開き300μm)の金網上に広げ、150℃で90分間熱風乾燥した。 Spread The finely divided hydrous gel-like polymer on a wire mesh of 50 mesh (mesh opening 300 [mu] m), and dried with hot air for 90 minutes at 0.99 ° C.. 次いで、乾燥物を振動ミルを用いて粉砕し、さらに20メッシュ(目開き850μm)の金網で分級することにより、平均粒子径が400μmで、しかも、粒子径が106μm Then, by the dry product was pulverized with a vibration mill and further classified with a 20 mesh wire gauze (mesh opening 850 .mu.m), the average particle diameter of 400 [mu] m, moreover, the particle diameter 106μm
未満の粒子の割合が5重量%の不定形破砕状の吸水性樹脂前駆体を得た。 Percentage of particles less than was obtained 5 wt% of the irregularly pulverized shaped water absorbent resin precursor.

【0129】得られた吸水性樹脂前駆体100重量部に、エチレングリコール0.5重量部と、水3重量部と、エチルアルコール1重量部とからなる表面架橋剤溶液を混合した。 [0129] the water-absorbing resin precursor 100 parts by weight of the obtained, and ethylene glycol 0.5 parts by weight, and 3 parts by weight of water, was mixed with a surface cross-linking agent solution consisting of ethyl alcohol 1 part by weight. 上記の混合物を195℃で20分間加熱処理することにより、吸水性樹脂を得た。 By heating 20 minutes the mixture at 195 ° C., to obtain a water-absorbent resin. 得られた吸水性樹脂の平均粒子径は400μmであり、粒子径が10 The average particle diameter of the resulting water-absorbent resin was 400 [mu] m, particle diameter of 10
6μm未満の粒子の割合は3重量%であった。 Proportion of 6μm less of the particles was 3 wt%.

【0130】上記の吸水性樹脂を、そのまま比較用の吸収剤組成物とした。 [0130] The above water-absorbent resin, was as absorbent composition for comparison. 上記比較用吸収剤組成物の諸性能、 Various properties of the comparative absorbent composition,
並びに、該比較用吸収剤組成物を用いた比較用吸収体および比較用吸収物品の諸性能を上記の方法によって測定した。 And were the various performances of the comparative absorber and the comparative absorbent article using the comparative absorbent composition was determined by the above methods. 結果をまとめて表1に示す。 The results are summarized in Table 1.

【0131】〔比較例3〕上記の比較例1で得られた吸水性樹脂100gに、微粒子状の親水性二酸化ケイ素(商品名・アエロジル200;日本アエロジル株式会社製)0.3gを添加・混合することにより、比較用の吸収剤組成物を得た。 [0131] to [Comparative Example 3] The above Comparative Example 1 obtained water absorbent resin 100 g, particulate hydrophilic silicon dioxide; added and mixed (trade name, Aerosil 200 manufactured by Nippon Aerosil Co., Ltd.) 0.3 g by obtain an absorbent composition for comparison.

【0132】上記比較用吸収剤組成物の諸性能、並びに、該比較用吸収剤組成物を用いた比較用吸収体および比較用吸収物品の諸性能を上記の方法によって測定した。 [0132] Various performance of the comparative absorbent composition, as well, and the various performances of the comparative absorber and the comparative absorbent article using the comparative absorbent composition was determined by the above methods. 結果をまとめて表1に示す。 The results are summarized in Table 1.

【0133】〔比較例4〕上記の比較例2で得られた吸水性樹脂100gに、微粒子状の親水性二酸化ケイ素(商品名・レオロシールQS−20;徳山曹達株式会社製)0.5gを添加・混合することにより、比較用の吸収剤組成物を得た。 [0133] In Comparative Example 4 above Comparative Example 2 obtained water absorbent resin 100 g, particulate hydrophilic silicon dioxide; added (trade name, Reolosil QS-20 manufactured by Tokuyama Soda Co., Ltd.) 0.5 g · by mixing, to obtain an absorbent composition for comparison.

【0134】上記比較用吸収剤組成物の諸性能、並びに、該比較用吸収剤組成物を用いた比較用吸収体および比較用吸収物品の諸性能を上記の方法によって測定した。 [0134] Various performance of the comparative absorbent composition, as well, and the various performances of the comparative absorber and the comparative absorbent article using the comparative absorbent composition was determined by the above methods. 結果をまとめて表1に示す。 The results are summarized in Table 1.

【0135】 [0135]

【表1】 [Table 1]

【0136】表1に記載された結果から明らかなように、本発明にかかる吸収剤組成物は、比較用の吸収剤組成物と比較して、拡散吸収指数が高い。 [0136] As apparent from the results described in Table 1, the absorbent composition of the present invention, compared with the absorbent composition for comparison, a higher diffusing absorbency index. また、吸収体は、比較用の吸収体と比較して、吸収速度が速く、液拡散性に優れている。 Further, the absorber, as compared to absorbent for comparison, the absorption rate is high, has excellent liquid diffusibility. さらに、本発明にかかる吸収物品は、比較用の吸収物品と比較して、吸収量が多く、性能が良好である。 Further, absorbent articles according to the present invention, as compared to the absorbent article for comparison, often absorption performance is good. このため、吸収剤組成物、吸収体、および吸収物品は、一度に多量の水性液体が添加されても、 Therefore, absorbent composition, absorbent, and absorbent article, be added a large amount of an aqueous liquid at a time,
該水性液体を素早く吸収することができ、かつ、常時、 Can quickly absorb aqueous liquids, and, at all times,
非常に高い液拡散性を維持することができると共に、単位重量当たりの吸収量を保持することができる等の優れた性能(吸収特性)を示すことがわかる。 It is possible to maintain a very high liquid-diffusivity, excellent performance (absorption properties) such as can hold the absorption amount per unit weight it can be seen that.

【0137】 [0137]

【発明の効果】本発明にかかる吸収剤組成物の製造方法は、以上のように、20g/cm 2 (1.96kPa) Manufacturing method of the absorbent composition to the present invention, as described above, 20g / cm 2 (1.96kPa)
の荷重下における、吸収開始から60分経過後の0.9 In under a load of 0.9 after a lapse of 60 minutes from the absorption start
重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/ Diffusing absorbency of weight percent sodium chloride aqueous solution 25 g /
g以上である吸水性樹脂に、微粒子状の水不溶性無機粉体を添加する構成である。 The water-absorbent resin g or more, a configuration of adding the particulate water-insoluble inorganic powder.

【0138】本発明にかかる吸収剤組成物の製造方法は、以上のように、20g/cm 2 (1.96kPa) [0138] manufacturing method of the absorbent composition of the present invention, as described above, 20g / cm 2 (1.96kPa)
の荷重下における、吸収開始から60分経過後の0.9 In under a load of 0.9 after a lapse of 60 minutes from the absorption start
重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/ Diffusing absorbency of weight percent sodium chloride aqueous solution 25 g /
g以上である吸水性樹脂に、重量平均分子量5,000 The water-absorbent resin g or more, a weight average molecular weight of 5,000
以上のポリアミン化合物を添加する構成である。 It is a configuration of adding the above polyamine compounds.

【0139】本発明にかかる吸収剤組成物の製造方法は、以上のように、20g/cm 2 (1.96kPa) [0139] manufacturing method of the absorbent composition of the present invention, as described above, 20g / cm 2 (1.96kPa)
の荷重下における、吸収開始から60分経過後の0.9 In under a load of 0.9 after a lapse of 60 minutes from the absorption start
重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/ Diffusing absorbency of weight percent sodium chloride aqueous solution 25 g /
g以上である吸水性樹脂に、微粒子状の水不溶性無機粉体と、重量平均分子量5,000以上のポリアミン化合物とを添加する構成である。 The water-absorbent resin g or more, a configuration of adding the particulate water-insoluble inorganic powder, and a weight average molecular weight of 5,000 or higher polyamine compounds.

【0140】本発明にかかる吸収剤組成物の製造方法は、以上のように、吸水性樹脂の上記拡散吸収倍率が3 [0140] manufacturing method of the absorbent composition of the present invention, as described above, the diffusing absorbency of the water absorbing resin 3
0.1g/g以上である構成である。 A configuration is 0.1g / g or more.

【0141】上記の方法によれば、一度に多量の水性液体が添加されても、該水性液体を素早く吸収することができ、かつ、常時、非常に高い液拡散性を維持すると共に、単位重量当たりの吸収量を保持する等の優れた性能(吸収特性)を示すことができる吸収剤組成物の製造方法を提供することができるという効果を奏する。 [0141] According to the above method, be added a large amount of an aqueous liquid at a time, it can quickly absorb aqueous liquids, and, at all times, while maintaining a very high liquid-diffusivity, unit weight an effect that it is possible to provide a superior performance manufacturing method of absorbent composition which can exhibit (absorption properties) such as to hold the absorbed amount per.

【0142】本発明にかかる吸収剤組成物は、以上のように、微粒子状の水不溶性無機粉体を含み、20g/c [0142] absorbent composition according to the present invention, as described above, includes a particulate water-insoluble inorganic powder, 20 g / c
2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である構成である。 in under a load of m 2 (1.96kPa), diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation it is configured at 25 g / g or more.

【0143】本発明にかかる吸収剤組成物は、以上のように、重量平均分子量5,000以上のポリアミン化合物を含み、20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である構成である。 [0143] absorbent composition according to the present invention, as described above, include a weight average molecular weight of 5,000 or more polyamine compounds, in under load of 20g / cm 2 (1.96kPa), 60 minutes from the absorption initiation 0.9 diffusing absorbency weight% aqueous sodium chloride solution after it is configured at 25 g / g or more.

【0144】本発明にかかる吸収剤組成物は、以上のように、微粒子状の水不溶性無機粉体と、重量平均分子量5,000以上のポリアミン化合物とを含み、20g/ [0144] absorbent composition according to the present invention, as described above, includes a particulate water-insoluble inorganic powder, and a weight average molecular weight of 5,000 or more polyamine compounds, 20 g /
cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である構成である。 in under a load of cm 2 (1.96kPa), diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation it is configured at 25 g / g or more.

【0145】本発明にかかる吸収剤組成物は、以上のように、上記拡散吸収倍率が26.9g/g以上である構成である。 [0145] absorbent composition according to the present invention, as described above, the configuration described above diffusing absorbency is 26.9 g / g or more.

【0146】本発明にかかる吸収剤組成物は、以上のように、アクリル酸またはその塩を主成分とする親水性不飽和単量体を重合させて得られる架橋重合体を含む構成である。 [0146] absorbent composition according to the present invention, as described above, a configuration including a crosslinked polymer obtained by polymerizing a hydrophilic unsaturated monomer mainly composed of acrylic acid or a salt thereof.

【0147】上記の構成によれば、一度に多量の水性液体が添加されても、該水性液体を素早く吸収することができ、かつ、常時、非常に高い液拡散性を維持すると共に、単位重量当たりの吸収量を保持する等の優れた性能(吸収特性)を示すことができる吸収剤組成物を提供することができるという効果を奏する。 [0147] According to the arrangement, be added a large amount of an aqueous liquid at a time, it can quickly absorb aqueous liquids, and, at all times, while maintaining a very high liquid-diffusivity, unit weight an effect that it is possible to provide excellent performance absorbent composition which can exhibit (absorption properties) such as to hold the absorbed amount per.

【0148】本発明にかかる吸収物品は、以上のように、上記の吸収剤組成物を含む吸収層を、透液性を有するシートと、不透液性を有するシートとで挟持してなる構成である。 [0148] Absorbent articles according to the present invention, as described above, the absorbent layer including the above absorbent composition, formed by sandwiched a sheet having liquid permeability, a sheet having a liquid-impervious structure it is.

【0149】上記の構成によれば、一度に多量の水性液体が添加されても、該水性液体を素早く吸収することができ、かつ、液拡散性や吸収量等の吸収特性に優れた衛生材料等の吸収物品を提供することができるという効果を奏する。 [0149] According to the arrangement, a large amount of even an aqueous liquid is added, it is possible to quickly absorb the aqueous liquid, and excellent sanitary material on the absorption characteristics of such liquid diffusibility and absorption at a time an effect that it is possible to provide an absorbent article and the like.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明における吸収剤組成物が示す性能の一つである拡散吸収倍率の測定に用いる測定装置の概略の断面図である。 1 is a schematic sectional view of a measuring device used for measuring is one diffusing absorbency performance indicated absorbent composition of the present invention.

【図2】上記測定装置の要部の断面図である。 2 is a cross-sectional view of a main part of the measuring device.

【図3】上記測定装置において、生理食塩水の拡散方向を説明する説明図である。 [3] In the measuring apparatus, it is an explanatory diagram for explaining a diffusion direction of saline.

【図4】吸収体が示す性能の一つである拡散吸収倍率の測定に用いる測定装置の概略の断面図である。 4 is a schematic sectional view of a measuring device used for measuring the diffusing absorbency is one of the performance absorber shown.

【図5】図4の測定装置の要部の断面図である。 5 is a cross-sectional view of a main part of the measuring device of FIG.

【図6】図4の測定装置において、生理食塩水の拡散方向を説明する説明図である。 In the measurement apparatus of FIG. 6 FIG. 4 is an explanatory diagram for explaining a diffusion direction of saline.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 天秤 2 容器 3 外気吸入パイプ 4 導管 5 測定部 6 ガラスフィルタ 7 濾紙 8 シート 9 支持円筒 10 金網 11 重り 12 生理食塩水 15 測定部 19 支持角筒 1 balance 2 container 3 air-inhaling pipe 4 conduit 5 measuring unit 6 glass filter 7 filter paper 8 sheets 9 supporting cylinder 10 wire mesh 11 weight 12 saline 15 measuring unit 19 support rectangular tube

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl. 7識別記号 FI テーマコート゛(参考) C08K 3/00 C08L 79/02 C08L 33/02 101/14 79/02 A61F 13/18 307B 101/14 A41B 13/02 D // A61F 13/49 ────────────────────────────────────────────────── ─── of the front page continued (51) Int.Cl. 7 identification mark FI theme Court Bu (reference) C08K 3/00 C08L 79/02 C08L 33/02 101/14 79/02 A61F 13/18 307B 101/14 A41B 13/02 D // A61F 13/49

Claims (10)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量% 1. A 20 g / cm 2 under a load of (1.96 kPa), 0.9 wt% after a lapse of 60 minutes from the absorption initiation
    塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、微粒子状の水不溶性無機粉体を添加することを特徴とする吸収剤組成物の製造方法。 The water-absorbent resin diffusing absorbency of aqueous sodium chloride solution is 25 g / g or more, a manufacturing method of the absorbent composition, characterized in that the addition of fine-particle water-insoluble inorganic powder.
  2. 【請求項2】20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量% 2. A 20 g / cm 2 under a load of (1.96 kPa), 0.9 wt% after a lapse of 60 minutes from the absorption initiation
    塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、重量平均分子量5,000以上のポリアミン化合物を添加することを特徴とする吸収剤組成物の製造方法。 Manufacturing method of the absorbent composition diffusing absorbency sodium chloride aqueous solution to the water-absorbing resin is 25 g / g or more, and adding a weight average molecular weight of 5,000 or higher polyamine compounds.
  3. 【請求項3】20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量% 3. A 20 g / cm 2 under a load of (1.96 kPa), 0.9 wt% after a lapse of 60 minutes from the absorption initiation
    塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上である吸水性樹脂に、微粒子状の水不溶性無機粉体と、 The water-absorbent resin diffusing absorbency of aqueous sodium chloride solution is 25 g / g or more, and particulate water-insoluble inorganic powder,
    重量平均分子量5,000以上のポリアミン化合物とを添加することを特徴とする吸収剤組成物の製造方法。 Manufacturing method of the absorbent composition, characterized in that the addition of the weight average molecular weight of 5,000 or higher polyamine compounds.
  4. 【請求項4】吸水性樹脂の上記拡散吸収倍率が30.1 The diffusion absorbency wherein the water-absorbing resin is 30.1
    g/g以上であることを特徴とする請求項1ないし3の何れか1項に記載の吸収剤組成物の製造方法。 The process according to claim 1 to absorbent composition according to any one of 3, characterized in that the g / g or more.
  5. 【請求項5】微粒子状の水不溶性無機粉体を含み、20 5. A comprises particulate water-insoluble inorganic powder, 20
    g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上であることを特徴とする吸収剤組成物。 in under a load of g / cm 2 (1.96kPa), absorbent compositions diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation is characterized in that it is 25 g / g or more .
  6. 【請求項6】重量平均分子量5,000以上のポリアミン化合物を含み、20g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g Includes wherein the weight average molecular weight of 5,000 or more polyamine compounds, in under load of 20g / cm 2 (1.96kPa), diffusion of 0.9 wt% aqueous sodium chloride solution after 60 minutes from the absorption initiation absorption capacity is 25g / g
    以上であることを特徴とする吸収剤組成物。 Absorbent composition, characterized in that at least.
  7. 【請求項7】微粒子状の水不溶性無機粉体と、重量平均分子量5,000以上のポリアミン化合物とを含み、2 Wherein 7. A particulate water-insoluble inorganic powder, and a weight average molecular weight of 5,000 or more polyamine compound, 2
    0g/cm 2 (1.96kPa)の荷重下における、吸収開始から60分経過後の0.9重量%塩化ナトリウム水溶液の拡散吸収倍率が25g/g以上であることを特徴とする吸収剤組成物。 In under a load of 0g / cm 2 (1.96kPa), absorbent compositions diffusing absorbency of 0.9% by weight aqueous sodium chloride solution after 60 minutes from the absorption initiation is characterized in that it is 25 g / g or more .
  8. 【請求項8】上記拡散吸収倍率が26.9g/g以上であることを特徴とする請求項5ないし7の何れか1項に記載の吸収剤組成物。 8. The absorbent composition according to any one of the above items diffusing absorbency is 5 claims, characterized in that at 26.9 g / g or more and 7.
  9. 【請求項9】アクリル酸またはその塩を主成分とする親水性不飽和単量体を重合させて得られる架橋重合体を含むことを特徴とする請求項5ないし8の何れか1項に記載の吸収剤組成物。 9. claimed in any one of 5 to claim, characterized in that it comprises an acrylic acid or a hydrophilic unsaturated monomer is polymerized obtained crosslinked polymer comprising a salt 8 absorbent composition.
  10. 【請求項10】請求項5ないし9の何れか1項に記載の吸収剤組成物を含む吸収層を、透液性を有するシートと、不透液性を有するシートとで挟持してなることを特徴とする吸収物品。 10. The absorbent layer including an absorbent composition according to any one of claims 5 to 9, the sheet having a liquid-permeable, that is formed by sandwiched between the sheet having a liquid-impervious the absorbent article according to claim.
JP2000106727A 1995-09-01 2000-04-04 Absorbent composition, production thereof and absorptive article containing the same Pending JP2000342963A (en)