IN2014MN01579A - - Google Patents

Info

Publication number
IN2014MN01579A
IN2014MN01579A IN1579MUN2014A IN2014MN01579A IN 2014MN01579 A IN2014MN01579 A IN 2014MN01579A IN 1579MUN2014 A IN1579MUN2014 A IN 1579MUN2014A IN 2014MN01579 A IN2014MN01579 A IN 2014MN01579A
Authority
IN
India
Prior art keywords
flat steel
steel product
hold
atmosphere
temperature
Prior art date
Application number
Other languages
English (en)
Inventor
Marc Blumenau
Christopher Gusek
Fred Jindra
Rudolf Schönenberg
Hans Joachim Krautschick
Original Assignee
Outokumpu Nirosta Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Outokumpu Nirosta Gmbh filed Critical Outokumpu Nirosta Gmbh
Publication of IN2014MN01579A publication Critical patent/IN2014MN01579A/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/02—Alloys based on aluminium with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/10—Alloys based on aluminium with zinc as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C30/00—Alloys containing less than 50% by weight of each constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/003—Apparatus
    • C23C2/0038—Apparatus characterised by the pre-treatment chambers located immediately upstream of the bath or occurring locally before the dipping process
    • C23C2/004—Snouts
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Metallurgy (AREA)
  • Materials Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
IN1579MUN2014 2012-02-08 2012-12-13 IN2014MN01579A (de)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102012101018A DE102012101018B3 (de) 2012-02-08 2012-02-08 Verfahren zum Schmelztauchbeschichten eines Stahlflachprodukts
PCT/EP2012/075402 WO2013117273A1 (de) 2012-02-08 2012-12-13 Verfahren zum schmelztauchbeschichten eines stahlflachprodukts

Publications (1)

Publication Number Publication Date
IN2014MN01579A true IN2014MN01579A (de) 2015-05-15

Family

ID=47504886

Family Applications (1)

Application Number Title Priority Date Filing Date
IN1579MUN2014 IN2014MN01579A (de) 2012-02-08 2012-12-13

Country Status (9)

Country Link
US (1) US9803270B2 (de)
EP (1) EP2812458B8 (de)
JP (1) JP5796142B2 (de)
KR (1) KR101994989B1 (de)
CN (1) CN104245995B (de)
DE (1) DE102012101018B3 (de)
ES (1) ES2593531T3 (de)
IN (1) IN2014MN01579A (de)
WO (1) WO2013117273A1 (de)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2821520B1 (de) * 2013-07-03 2020-11-11 ThyssenKrupp Steel Europe AG Verfahren zum beschichten von stahlflachprodukten mit einer metallischen schutzschicht
JP6131919B2 (ja) * 2014-07-07 2017-05-24 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
DE102014109943B3 (de) 2014-07-16 2015-11-05 Thyssenkrupp Ag Stahlprodukt mit einer Korrosionsschutzbeschichtung aus einer Aluminiumlegierung sowie Verfahren zu dessen Herstellung
US20180312955A1 (en) * 2015-09-30 2018-11-01 Thyssenkrupp Steel Europe Ag Flat Steel Product Having a Zn-Galvannealed Protective Coating, and Method for the Production Thereof
JP6237937B2 (ja) * 2016-03-11 2017-11-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
KR102231412B1 (ko) 2016-10-25 2021-03-23 제이에프이 스틸 가부시키가이샤 고강도 용융 아연 도금 강판의 제조 방법
DE102016222993A1 (de) * 2016-11-22 2018-05-24 Volkswagen Aktiengesellschaft Verfahren zur Herstellung eines beschichteten Stahlbauteils
DE102018100842B3 (de) * 2018-01-16 2019-05-09 Ebner Industrieofenbau Gmbh Durchlaufofen für Aluminiumbänder
CN112522591B (zh) * 2019-09-19 2022-03-18 宝山钢铁股份有限公司 一种薄带连铸生产高强高耐蚀钢的方法
CN113969336B (zh) * 2020-07-23 2023-03-28 宝山钢铁股份有限公司 一种热镀锌钢板的制造方法、钢板及车用构件
CN115351295B (zh) * 2022-08-26 2023-10-27 河北建筑工程学院 一种复合板制备工艺

Family Cites Families (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60262950A (ja) 1984-06-08 1985-12-26 Nippon Steel Corp 耐熱性と耐食性にすぐれた溶融アルミニウムメツキ鋼板の製造法
JPS61147865A (ja) 1984-12-18 1986-07-05 Nisshin Steel Co Ltd 溶融アルミめつき鋼板およびその製造法
US4675214A (en) 1986-05-20 1987-06-23 Kilbane Farrell M Hot dip aluminum coated chromium alloy steel
US4883723A (en) 1986-05-20 1989-11-28 Armco Inc. Hot dip aluminum coated chromium alloy steel
US5066549A (en) 1986-05-20 1991-11-19 Armco Inc. Hot dip aluminum coated chromium alloy steel
US5023113A (en) * 1988-08-29 1991-06-11 Armco Steel Company, L.P. Hot dip aluminum coated chromium alloy steel
US5246563A (en) 1988-09-14 1993-09-21 Andritz-Patentverwaltungs-Gesellschaft M.B.H. Process for the electrolytic zinc coating of stainless steel
AT392089B (de) 1988-09-14 1991-01-25 Andritz Ag Maschf Verfahren zum ein- und beidseitigen elektrolytischen verzinken von edelstahl
JPH02285057A (ja) * 1989-04-27 1990-11-22 Sumitomo Metal Ind Ltd 溶融亜鉛めっき用鋼板の連続焼鈍方法
JP2727529B2 (ja) 1989-09-27 1998-03-11 新日本製鐵株式会社 メッキ密着性に優れた高耐蝕性アルミメッキＣｒ含有鋼板の製造方法
FR2664617B1 (fr) 1990-07-16 1993-08-06 Lorraine Laminage Procede de revetement d'aluminium par trempe a chaud d'une bande d'acier et bande d'acier obtenue par ce procede.
JP3111546B2 (ja) 1991-10-28 2000-11-27 株式会社ニコン アブソリュートエンコーダ
JP2743228B2 (ja) 1992-05-11 1998-04-22 新日本製鐵株式会社 加工性とめっき密着性に優れた溶融アルミめっきＣｒ含有鋼板の製造方法
US5447754A (en) 1994-04-19 1995-09-05 Armco Inc. Aluminized steel alloys containing chromium and method for producing same
WO2000050658A1 (fr) 1999-02-22 2000-08-31 Nippon Steel Corporation Plaque d'acier galvanise a haute resistance, d'excellent comportement pour l'adhesion des placages de metal et la mise en forme sous presse, et plaque d'acier allie galvanise a haute resistance, et procede de production correspondant
US6902829B2 (en) * 2001-11-15 2005-06-07 Isg Technologies Inc. Coated steel alloy product
JP2003253413A (ja) * 2002-03-06 2003-09-10 Nippon Steel Corp 高強度冷延鋼板とめっき鋼板の兼用製造設備および兼用製造方法
CN1985016B (zh) * 2003-01-15 2011-09-14 新日本制铁株式会社 高强度热浸镀锌钢板及其制备方法
CA2521710C (en) 2003-04-10 2009-09-29 Nippon Steel Corporation High strength molten zinc plated steel sheet and process of production of same
US8181331B2 (en) 2003-07-29 2012-05-22 Voestalpine Automotive Gmbh Method for producing hardened parts from sheet steel
JP4192051B2 (ja) * 2003-08-19 2008-12-03 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
JP2006051543A (ja) 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
DE102004059566B3 (de) 2004-12-09 2006-08-03 Thyssenkrupp Steel Ag Verfahren zum Schmelztauchbeschichten eines Bandes aus höherfestem Stahl
EP1693477A1 (de) 2005-02-22 2006-08-23 ThyssenKrupp Steel AG Beschichtetes Stahlblech oder -band
KR101011897B1 (ko) * 2005-10-14 2011-02-01 신닛뽄세이테쯔 카부시키카이샤 Ｓｉ를 함유하는 강판의 연속 어닐링 용융 도금 방법 및연속 어닐링 용융 도금 장치
EP1857566B1 (de) 2006-05-15 2017-05-03 ThyssenKrupp Steel Europe AG Mit einem Korrosionsschutzüberzug versehenes Stahlflachprodukt und Verfahren zu seiner Herstellung
EP2009128A1 (de) 2007-06-29 2008-12-31 ArcelorMittal France Verzinkter oder Galvanneal-Siliziumstahl
JP2009035756A (ja) 2007-07-31 2009-02-19 Nisshin Steel Co Ltd 高温強度に優れた二輪車排ガス経路部材用Ａｌ系めっき鋼板および部材
EP2055799A1 (de) 2007-11-05 2009-05-06 ThyssenKrupp Steel AG Stahlflachprodukt mit einem vor Korrosion schützenden metallischen Überzug und Verfahren zum Erzeugen eines vor Korrosion schützenden metallischen Zn-Mg Überzugs auf einem Stahlflachprodukt
JP5311380B2 (ja) 2008-09-22 2013-10-09 独立行政法人産業技術総合研究所 難燃性エポキシ樹脂及びその製造方法
DE102010037254B4 (de) * 2010-08-31 2012-05-24 Thyssenkrupp Steel Europe Ag Verfahren zum Schmelztauchbeschichten eines Stahlflachprodukts

Also Published As

Publication number Publication date
JP5796142B2 (ja) 2015-10-21
KR101994989B1 (ko) 2019-07-02
EP2812458B1 (de) 2016-06-29
EP2812458B8 (de) 2016-08-24
US20150345002A1 (en) 2015-12-03
DE102012101018B3 (de) 2013-03-14
CN104245995A (zh) 2014-12-24
JP2015509556A (ja) 2015-03-30
ES2593531T3 (es) 2016-12-09
US9803270B2 (en) 2017-10-31
CN104245995B (zh) 2016-08-03
WO2013117273A1 (de) 2013-08-15
KR20140128416A (ko) 2014-11-05
EP2812458A1 (de) 2014-12-17

Similar Documents

Publication Publication Date Title
IN2014MN01579A (de)
UA107340C2 (en) Flux and fluxing bath for hot dip galvanization, process for the hot dip galvanization of an iron or steel article
MX2018007649A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tenga ductilidad y conformabilidad mejorada, y lamina de acero recubierta obtenida.
MX2017006303A (es) Metodo para fabricar un producto de acero de alta resistencia y un producto de acero obtenido por el mismo.
MX369651B (es) Metodo para aplicar un recubrimiento protector a un producto plano de acero y un producto plano de acero que tiene un recubrimiento protector correspondiente.
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX2018007749A (es) Lamina de acero recubierta con aleacion de aluminio-hierro para formacion en prensa caliente, que tiene excelente resistencia de fractura retardada de hidrogeno, resistencia de desprendimiento y soldabilidad, y el miembro formado en caliente usando la misma.
MX2017005568A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para la fabricacion de las mismas.
ATE541061T1 (de) Glüh- und beizverfahren
MX2016006777A (es) Componente de lamina de acero formada en caliente y metodo para producir el mismo asi como la lamina de acero para formacion en caliente.
MX2017001529A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2020010051A (es) Articulo moldeado por estampado en caliente, lamina de acero enrollada en frio, y metodo para manufacturar el articulo moldeado por estampado en caliente.
BR112014005641A2 (pt) tira de aço galvanizada por imersão a quente de alta resistência
MX2013012422A (es) Lamina de acero para miembro de estampado en caliente y metodo para producir la misma.
MX2017005567A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para fabricacion de las mismas.
MX2018007185A (es) Cinta de acero galvanizada por inmersion en caliente de alta resistencia.
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
MX2018011888A (es) Lamina de acero y lamina de acero enchapada, metodo para producir una lamina de acero laminada en caliente, metodo para producir una lamina de acero laminada en frio de dureza completa, metodo para producir una lamina tratada termicamente, metodo para producir una lamina de acero, y metodo para producir una lamina de acero enchapada.
MX2015013538A (es) Placa de acero chapada de alta resistencia para elemento estructural soldado, metodo para producir la misma.
MX2016016705A (es) Metodo para la fabricacion de una lamina de acero galvanizada de alta resistencia.
MX354352B (es) Lámina de acero galvanizado de alta resistencia excelente en términos de adherencia de recubrimiento y método para la fabricación de la misma.
MX2014003159A (es) Cinta electrica de resistencia superior, de grano no orientado, con alta polarizacion y metodo para la produccion de la misma.
MX2021000661A (es) Articulos de cuero biofabricado y metodos de estos.
RU2016151793A (ru) Способ изготовления высокопрочной листовой стали, имеющей улучшенную формуемость, и полученный лист
MX2016011337A (es) Lamina de acero laminada en frio, metodo para la produccion de la misma, lamina de acero galvanizada por inmersion en caliente de alta resistencia, y lamina de acero galvano-recocida por inmersion en caliente de alta resistencia.