GB979270A - Titanium pigments - Google Patents
Titanium pigmentsInfo
- Publication number
- GB979270A GB979270A GB665862A GB665862A GB979270A GB 979270 A GB979270 A GB 979270A GB 665862 A GB665862 A GB 665862A GB 665862 A GB665862 A GB 665862A GB 979270 A GB979270 A GB 979270A
- Authority
- GB
- United Kingdom
- Prior art keywords
- phosphoric acid
- titanium
- heated
- precipitate
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
Titanium phosphate, believed to be the pyrophosphate TiP2O7, is prepared by simultaneously introducing a titanium tetrahalide and phosphoric acid or soluble salt of phosphoric acid, e.g. NH4H2PO4, into an aqueous liquid; recovering the titanium phosphate precipitate thus formed and then heating the precipitate. The titanium tetrahalide is preferably the tetrachloride, the pH of the aqueous liquid is preferably below 7, the precipitation being performed in the presence of excess phosphoric acid or soluble salt thereof, e.g. 1-50 gm./litre estimated as H3PO4. The titanium tetrahalide, the phosphoric acid, and the salt of phosphoric acid may be introduced as aqueous solutions, and are preferably introduced into the aqueous liquid at a rate such that no local excess of titanium tetrahalide occurs in the solution. The aqueous solution may be heated preferably to its b.pt. during the addition of the reactants or the reactants may be added and the solution subsequently heated. The halide solution used has a concentration of preferably 25-220 gms./litre (estimated as TiO2) and the precipitate produced may before separation be mixed with phosphoric acid or an aqueous solution of a salt thereof and boiled. The ppt. is then separated, dried and ground and heated at a temperature in the range 750 DEG to 1100 DEG C. and subsequently milled to produce a mean crystal size of 0.1 to 2 microns. After recovery but before heating, a compound which reduces the temperature to which the titanium phosphate must be heated to form a pigment may be added to the titanium phosphate precipitate. The preferred compound is potassium phosphate and it is added in an amount sufficient to give a concentration before heating (estimated as potassium) of at least 0.05% by weight, preferably 0.1% to 2% by weight.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB665862A GB979270A (en) | 1962-02-21 | 1962-02-21 | Titanium pigments |
DE19631223349 DE1223349C2 (en) | 1962-02-21 | 1963-02-13 | PROCESS FOR THE PRODUCTION OF A TITANIUM PYROPHOSHATE SUITABLE AS A PIGMENT |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB665862A GB979270A (en) | 1962-02-21 | 1962-02-21 | Titanium pigments |
Publications (1)
Publication Number | Publication Date |
---|---|
GB979270A true GB979270A (en) | 1965-01-01 |
Family
ID=9818442
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB665862A Expired GB979270A (en) | 1962-02-21 | 1962-02-21 | Titanium pigments |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE1223349C2 (en) |
GB (1) | GB979270A (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS4889199A (en) * | 1972-03-01 | 1973-11-21 |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE2159342C2 (en) * | 1971-11-30 | 1984-12-20 | Mizusawa Kagaku Kogyo K.K., Osaka | New white pigment |
-
1962
- 1962-02-21 GB GB665862A patent/GB979270A/en not_active Expired
-
1963
- 1963-02-13 DE DE19631223349 patent/DE1223349C2/en not_active Expired
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS4889199A (en) * | 1972-03-01 | 1973-11-21 | ||
JPS516000B2 (en) * | 1972-03-01 | 1976-02-24 |
Also Published As
Publication number | Publication date |
---|---|
DE1223349B (en) | 1974-02-07 |
DE1223349C2 (en) | 1974-02-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ES481060A1 (en) | Process for the preparation of dustless, readily-dispersible pigment or dyestuff granules | |
DE3268713D1 (en) | Process for the preparation of copper (ii) hydroxide | |
GB979270A (en) | Titanium pigments | |
GB1414685A (en) | Production of soluble alkali metal silicates | |
GB1474164A (en) | Process for the hydrolysis of titanium sulphate solutions | |
Pugh | CXCIX.—Germanium. Part IV. The solubility of germanium dioxide in acids and alkalis | |
GB1157106A (en) | Production of Tio2-Al2O3 Pigments | |
Mikheev et al. | REDUCTION OF MENDELEVIUM TO MONOVALENT STATE | |
US1922328A (en) | Process of preparing synthetic rutile titanium dioxide | |
GB896660A (en) | Improvements in the preparation of phosphates of bivalent metals | |
US5968249A (en) | Process for preparing silica pigment | |
US3238015A (en) | Process for the production of potassium magnesium fluoride | |
US2337215A (en) | Process for hydrolyzing titanium compounds | |
ES269964A1 (en) | Improvements in the preparation of titanium dioxide pigments | |
GB1318224A (en) | Production of potassium dihydrogen phosphate | |
DE1805958C3 (en) | Process for the production of ascorbic acid 3-phosphate | |
GB1415895A (en) | Alpha-2,9-difluoroquinacridone and methods for its preparation | |
US3027228A (en) | Method for producing trivalent titanium orthophosphate | |
DE557725C (en) | Production of potassium salts by converting potassium chloride into a potassium borate and decomposing the borate using an acid | |
GB1074665A (en) | Method for the preparation of aluminium fluoride | |
GB653993A (en) | Process of producing silicic acid from alkali silicates | |
GB427220A (en) | Improvements in or relating to the production of barium sulphate and composite titanium pigments containing the same | |
GB423543A (en) | Process for the production of beryllium compounds from beryllium-bearing minerals | |
GB1071514A (en) | Preparation of starting materials for phosphate phosphors | |
DE524638C (en) | Process for the preparation of pyrazolones |