Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB2979459A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Atomic Energy of Canada Ltd AECL
Original Assignee
Atomic Energy of Canada Ltd AECL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Atomic Energy of Canada Ltd AECLfiledCriticalAtomic Energy of Canada Ltd AECL
Publication of GB898141ApublicationCriticalpatent/GB898141A/en
C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
C22C—ALLOYS
C22C1/00—Making non-ferrous alloys
C22C1/02—Making non-ferrous alloys by melting
Landscapes
Chemical & Material Sciences
(AREA)
Engineering & Computer Science
(AREA)
Materials Engineering
(AREA)
Mechanical Engineering
(AREA)
Metallurgy
(AREA)
Organic Chemistry
(AREA)
Manufacture Of Metal Powder And Suspensions Thereof
(AREA)
Carbon And Carbon Compounds
(AREA)
Abstract
Alloys of Th with U233 or U235 are prepared by mixing Th powder with UF4 and heating the mixture in a graphite crucible under inert gas or vacuum to initiate the reaction, followed by further heating to at least 1600 DEG C. The alloy and slag form two distinct layers which are readily separated on cooling. The reactant mixture may be initially pelleted.
GB2979459A1958-11-141959-09-01Production of thorium-uranium alloys
ExpiredGB898141A
(en)
Improvements in or relating to processes for the production of a p-doped region in bodies consisting of substantially monocrystalline semi-conductor material
A method for the preparation of a metal belonging to groups ivb and vb of the periodic system of the elements or of an alloy of such metals. (Machine-translation by Google Translate, not legally binding)
Tantalum-tungsten refractory alloy used in the thrust chamber of the agena vehicle because of its ability to go from cryogenic to high temperature without losing its ductility