GB869494A - Spalling resistant periclase brick - Google Patents

Spalling resistant periclase brick

Info

Publication number
GB869494A
GB869494A GB33562/59A GB3356259A GB869494A GB 869494 A GB869494 A GB 869494A GB 33562/59 A GB33562/59 A GB 33562/59A GB 3356259 A GB3356259 A GB 3356259A GB 869494 A GB869494 A GB 869494A
Authority
GB
United Kingdom
Prior art keywords
periclase
mgo
cr2o3
al2o3
inches
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB33562/59A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Canadian Refractories Ltd
Original Assignee
Canadian Refractories Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Canadian Refractories Ltd filed Critical Canadian Refractories Ltd
Publication of GB869494A publication Critical patent/GB869494A/en
Expired legal-status Critical Current

Abstract

A refractory brick of not more than 2% iron content comprises by weight 98% to 70% of dead burned periclase containing at least 90% MgO, and 2% to 30% of a refractory additive such as Al2O3, Cr2O3, MgO.Al2O3 or MgO.Cr2O3 which has a coefficient of linear thermal expansion less than that of periclase and a particle size range of 0.185 inches to 0.0232 inches (minus 4 plus 28 mesh Tyler). The periclase contains not more than 5% silica and not more than 2% lime and the composition may be fired before service or chemically bonded and fired during service. Specification 802,518 and U.S.A. Specifications 2,063,543 and 2,744,021 are referred to.ALSO:A refractory brick of not more than 2% iron content comprises by weight 98% to 70% of dead burned periclase containing a minimum of 90% MgO and 2% to 30% of a refractory addition which has a coefficient of linear thermal expansion less than that of periclase and has a particle size range of 0,185 inches to 0,0232 inches (minus 4 plus 28 mesh Tyler). The periclase contains not more than 5% silica and not more than 2% lime and the additive may be Al2O3, Cr2O3, MgO Al2O3 or MgO Cr2O3. The brick may be fired before service or chemically bonded. Specification 802,518 and U.S.A. Specifications 2,063,543 and 2,744,021 are referred to.
GB33562/59A 1958-10-16 1959-10-02 Spalling resistant periclase brick Expired GB869494A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
CA869494X 1958-10-16

Publications (1)

Publication Number Publication Date
GB869494A true GB869494A (en) 1961-05-31

Family

ID=4172739

Family Applications (1)

Application Number Title Priority Date Filing Date
GB33562/59A Expired GB869494A (en) 1958-10-16 1959-10-02 Spalling resistant periclase brick

Country Status (1)

Country Link
GB (1) GB869494A (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2163457A1 (en) * 1971-12-15 1973-07-27 Veitscher Magnesitwerke Ag

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2163457A1 (en) * 1971-12-15 1973-07-27 Veitscher Magnesitwerke Ag

Similar Documents

Publication Publication Date Title
GB1000080A (en) Volume stable refractory and method of making same
GB869494A (en) Spalling resistant periclase brick
GB977783A (en) Burned refractory product
GB1262328A (en) Refractory brick composition
SE7611161L (en) REFRACTORY LINING OF STATIONS OR MOVING CANLES FOR RECEIVING THE RAJERN
GB990949A (en) Oxygen converter lining
GB1115386A (en) Refractory magnesia
AU261956B2 (en) Composite refractory brick for furnace linings
GB955874A (en) Improvements in or relating to alumino-silicate refractories
GB872761A (en) A refractory batch composition and an article made therefrom
ES395853A1 (en) Refractory substance
GB1062891A (en) Improvements in or relating to methods of making basic refractories
GB1085977A (en) Refractory and method of making
GB869786A (en) Low-iron, spalling resistant periclase brick
GB1001430A (en) Improvements in or relating to a sprayable basic refractory composition for reparingthe hot basic refractory linings of high temperature furnaces and method
GB977782A (en) A batch for making refractories and brick made thereof
CA601872A (en) Refractory brick for suspension in furnace roofs
GB981528A (en) Improvements relating to refractories and refractory bricks containing calcined magnesia
GB955759A (en) Improvements relating to refractory compositions and method of applying the same
GB897357A (en) Improvements in or relating to furnace linings and products therefor
GB1071286A (en) Refractory composition
GB1014327A (en) Burned brick
GB713811A (en) Improvements in and relating to basic refractory bricks and other basic refractory products
GB571693A (en) An improved manufacture of magnesia-containing refractories
JPS5792145A (en) Tuyere part of refining furnace for metal