GB866372A - Improvements in or relating to the casting of metals - Google Patents
Improvements in or relating to the casting of metalsInfo
- Publication number
- GB866372A GB866372A GB3248258A GB3248258A GB866372A GB 866372 A GB866372 A GB 866372A GB 3248258 A GB3248258 A GB 3248258A GB 3248258 A GB3248258 A GB 3248258A GB 866372 A GB866372 A GB 866372A
- Authority
- GB
- United Kingdom
- Prior art keywords
- parts
- sodium silicate
- silicate solution
- hardened
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
A mix for making a moulding die comprises 95 parts of Swedish iron sponge powder and 5 parts of electrolytic copper powder mixed with 10 parts of aqueous sodium silicate solution of S.G. 1.56 and molar ratio Na2O : SiO2 of 1 : 2.05 2 parts by weight of molybdenum disulphide may be added, and the copper powder may be omitted. The mixture is hardened by CO2 gas and may then be dried by heating and if desired fired to sinter the metal particles. Specification 866,373 is referred to.ALSO:A foundry mould or moulding die has at least a self-sustaining p portion thereof made from a moulding material comprising a mixture of metal powder or powders and aqueous sodium silicate solution, said self-sustaining portion forming the moulding surface and having been hardened by the removal of water from the sodium silicate solution or by chemical action on the sodium silicate solution. The metal powder may be a mixture of Swedish sponge iron and copper, and some molybdenum disulphide may be included. The binder may be hardened by heating or CO2 gas, and the mould may be fired to sinter the metal particles Specification 866,373 is referred to.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3248258A GB866372A (en) | 1958-10-10 | 1958-10-10 | Improvements in or relating to the casting of metals |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3248258A GB866372A (en) | 1958-10-10 | 1958-10-10 | Improvements in or relating to the casting of metals |
Publications (1)
Publication Number | Publication Date |
---|---|
GB866372A true GB866372A (en) | 1961-04-26 |
Family
ID=10339253
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB3248258A Expired GB866372A (en) | 1958-10-10 | 1958-10-10 | Improvements in or relating to the casting of metals |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB866372A (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1991004118A1 (en) * | 1989-09-15 | 1991-04-04 | Mclaughlin Timothy M | Mold element construction and related method |
WO2015081923A1 (en) * | 2013-12-06 | 2015-06-11 | Hanseatische Waren Handelsgesellschaft Mbh & Co. Kg | Device and method for the production of near net-shape tial components |
-
1958
- 1958-10-10 GB GB3248258A patent/GB866372A/en not_active Expired
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1991004118A1 (en) * | 1989-09-15 | 1991-04-04 | Mclaughlin Timothy M | Mold element construction and related method |
WO2015081923A1 (en) * | 2013-12-06 | 2015-06-11 | Hanseatische Waren Handelsgesellschaft Mbh & Co. Kg | Device and method for the production of near net-shape tial components |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ES464063A1 (en) | Alkali metal silicate binder compositions | |
GB847478A (en) | Improvements in or relating to metal casting moulds | |
GB866372A (en) | Improvements in or relating to the casting of metals | |
GB1079200A (en) | Improvements in or relating to metal casting moulds | |
GB1362138A (en) | Apparatus and method for forming a channel when casting a metal block | |
ES385885A1 (en) | Heat-insulating antipiping compositions | |
GB738981A (en) | Improved process of manufacturing precision casting moulds for metals | |
GB1093726A (en) | Improvements in and relating to permanent moulds for the casting of metals | |
GB919884A (en) | Sintered silicon carbide compositions and method for their preparation | |
SU339090A1 (en) | Mixture for moulds and cores | |
GB722459A (en) | Improvements in or relating to coating compositions, permanent metal dies having an insulating coating of said composition and a method of making centrifugal castings employing said dies | |
SU141993A1 (en) | Method of making casting molds | |
GB1266606A (en) | ||
GB769719A (en) | Improvements in or relating to exothermic mixtures | |
GB729339A (en) | Cellular metal product and method of making the same | |
GB765747A (en) | Improvements in or relating to method of precision casting | |
GB895426A (en) | Improvements in and relating to shell moulds and cores | |
Reddy et al. | Effect Of Hardener Size And Content In Self Setting Sand Systems–A Nishiyama Approach | |
GB1016473A (en) | Fabrication of exothermic,self-hardening mould | |
SU128576A1 (en) | Binder for ceramic molds for casting on melted models | |
GB824124A (en) | Metal-ceramic materials | |
SU416145A1 (en) | ||
GB805823A (en) | Improvements in or relating to the manufacture of metal ingots and castings | |
Hiromoto et al. | Development of fired mold fluxes for continuous casting | |
GB1037878A (en) | Production of refractory silica articles |