GB1602590A - Sintered magnesium alumina silicate material - Google Patents

Sintered magnesium alumina silicate material Download PDF

Info

Publication number
GB1602590A
GB1602590A GB2412278A GB2412278A GB1602590A GB 1602590 A GB1602590 A GB 1602590A GB 2412278 A GB2412278 A GB 2412278A GB 2412278 A GB2412278 A GB 2412278A GB 1602590 A GB1602590 A GB 1602590A
Authority
GB
United Kingdom
Prior art keywords
glass
weight
particles
psi
ppm
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB2412278A
Other languages
English (en)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ford Motor Co Ltd
Ford Motor Co
Original Assignee
Ford Motor Co Ltd
Ford Motor Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ford Motor Co Ltd, Ford Motor Co filed Critical Ford Motor Co Ltd
Publication of GB1602590A publication Critical patent/GB1602590A/en
Expired legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C10/00—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition
    • C03C10/0036—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition containing SiO2, Al2O3 and a divalent metal oxide as main constituents
    • C03C10/0045—Devitrified glass ceramics, i.e. glass ceramics having a crystalline phase dispersed in a glassy phase and constituting at least 50% by weight of the total composition containing SiO2, Al2O3 and a divalent metal oxide as main constituents containing SiO2, Al2O3 and MgO as main constituents
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/16—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay
    • C04B35/18—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay rich in aluminium oxide
    • C04B35/195—Alkaline earth aluminosilicates, e.g. cordierite or anorthite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Structural Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Dispersion Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Glass Compositions (AREA)
  • Compositions Of Oxide Ceramics (AREA)
GB2412278A 1977-08-15 1978-05-30 Sintered magnesium alumina silicate material Expired GB1602590A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US82494277A 1977-08-15 1977-08-15

Publications (1)

Publication Number Publication Date
GB1602590A true GB1602590A (en) 1981-11-11

Family

ID=25242716

Family Applications (1)

Application Number Title Priority Date Filing Date
GB2412278A Expired GB1602590A (en) 1977-08-15 1978-05-30 Sintered magnesium alumina silicate material

Country Status (3)

Country Link
CA (1) CA1098548A (de)
DE (1) DE2834103C2 (de)
GB (1) GB1602590A (de)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5270270A (en) * 1989-02-25 1993-12-14 Schott Glaswerke Process for producing dense-sintered cordierite bodies

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3905895C1 (de) * 1989-02-25 1990-05-23 Schott Glaswerke, 6500 Mainz, De
DE102005049985A1 (de) * 2005-10-19 2007-04-26 Robert Bosch Gmbh Filterelement und Trägerstruktur für einen Katalysator mit verbesserter Beständigkeit gegen Alkali- und Erdalkaliionen

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3531307A (en) * 1967-02-23 1970-09-29 Intern Pipe & Ceramics Corp Ceramic article and method for producing same
US3940255A (en) * 1974-08-05 1976-02-24 Ferro Corporation Process for making cordierite glass-ceramic having nucleating agent and increased percent cordierite crystallinity

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5270270A (en) * 1989-02-25 1993-12-14 Schott Glaswerke Process for producing dense-sintered cordierite bodies

Also Published As

Publication number Publication date
CA1098548A (en) 1981-03-31
DE2834103C2 (de) 1986-10-09
DE2834103A1 (de) 1979-03-01

Similar Documents

Publication Publication Date Title
US4767731A (en) Aluminum titanate-mullite base ceramics
EP1805112B1 (de) Auf aluminiumtitanat basierender keramikkörper mit einer glasphase
US5607885A (en) Low thermal expansion cordierite aggregate and its bonded body
US4001028A (en) Method of preparing crack-free monolithic polycrystalline cordierite substrates
EP0172738B1 (de) Stabilisierte Zircondioxidkörper mit verbesserter Festikeit und ihre Herstellung
US4225354A (en) Crystalline additive for magnesium alumina silicate
US4528275A (en) Mullite-cordierite composite ceramic and method for preparation
JP2002145659A (ja) チタン酸アルミニウム系焼結体の製造方法
WO1999018047A1 (en) Method for firing ceramic honeycomb bodies
US5403787A (en) Extruded ceramic honeycomb and method
GB1602590A (en) Sintered magnesium alumina silicate material
US3929494A (en) Sealant for glass-ceramic surfaces
JP2619832B2 (ja) チタン酸アルミニウムセラミックス及びその製造方法
JPH02258670A (ja) 低熱膨張性セラミックス
JPH07101772A (ja) 低熱膨張コーディエライト質骨材及びその結合体
US4888312A (en) Zirconyl phosphate sintered bodies and production thereof
JP2002167267A (ja) 低熱膨張セラミックス及びその製造方法
JP3368960B2 (ja) ＳｉＣ質耐火物
US4526876A (en) Mullite-beta spodumene composite ceramic
JPS61286264A (ja) 加熱炉用管状部材及びその製造方法
JPH11292616A (ja) 複合ガラスセラミックスおよびその製造方法
JPH0637326B2 (ja) 熱交換器の伝熱用部材
JPH04104945A (ja) ムライト―Ｓｉｃ複合焼結体
JPH01183463A (ja) チタン酸アルミニウム／β−スポジューメン／ムライト系複合焼結体及びその製造方法
JPH02217356A (ja) 鋳ぐるみ用セラミック材料とその製造方法

Legal Events

Date Code Title Description
PS Patent sealed
746 Register noted 'licences of right' (sect. 46/1977)
PCNP Patent ceased through non-payment of renewal fee