ES2374134T3 - Ladrillo refractario no cocido conteniendo grafito para hornos de la industria del cemento y su utilización. - Google Patents

Ladrillo refractario no cocido conteniendo grafito para hornos de la industria del cemento y su utilización. Download PDF

Info

Publication number
ES2374134T3
ES2374134T3 ES02774789T ES02774789T ES2374134T3 ES 2374134 T3 ES2374134 T3 ES 2374134T3 ES 02774789 T ES02774789 T ES 02774789T ES 02774789 T ES02774789 T ES 02774789T ES 2374134 T3 ES2374134 T3 ES 2374134T3
Authority
ES
Spain
Prior art keywords
cement industry
percentage
graphite
weight
containing graphite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES02774789T
Other languages
English (en)
Inventor
Pedro Fajardo Sola
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Application granted granted Critical
Publication of ES2374134T3 publication Critical patent/ES2374134T3/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Ladrillo refractario no cocido conteniendo grafito para hornos de la industria del cemento y su utilización para una mayor resistencia frente a la deformación térmica y físico -química caracterizado porque su composición química comprende la combinación de un porcentaje en peso de Oxido de magnesio (MgO) entre el 75 - 62 %, un porcentaje en peso de Alúmina (Al2O3) entre un 12 - 20 %, y entre un 4 - 11 % de Grafito. Así como un porcentaje en peso de aditivos mejoradores del choque térmico y la resistencia térmica y la oxidación ( en una composición conjunta de aluminio en polvo, silicio metal, carburo de silicio y arcilla ) de entre un 9 - 7 %. Utilizándose como ligante sobre estos porcentajes totales resinas entre un 3 - 4 % de porcentaje en peso.

Description

Ladrillo refractario no cocido conteniendo grafito para hornos de la industria del cemento y su utilización.
La invención que se protege en esta Patente, consiste en un ladrillo refractario no cocido y que contiene grafito para hornos de la industria del cemento y su utilización.
Se trata, por tanto, de un ladrillo aplicable a los recubrimientos interiores de los hornos de la industria del cemento compuesto por magnesia y alúmina conteniendo grafito en vez de cromo o hierro objeto de otras formulaciones, así como a su distribución localizada en determinadas zonas del mismo, en orden a su capacidad refractaria.
El uso de materiales refractarios, es ampliamente conocido en la industria del cemento para el recubrimiento interior de los hornos que elaboran dicho producto, con objeto de soportar las altas temperaturas de trabajo, que alcanza en algunas zonas en torno a los 1.500 grados centígrados, así como a los continuos cambios bruscos en las mismas de entre 800 -1.500º centígrados y sus consiguientes reacciones físico-químicas. Sin embargo, las diversas composiciones de los materiales refractarios conllevan también distintos grados de dureza y resistencia a su deformación. A tal efecto, con la presente invención se logra un material refractario de mayor dureza y resistencia a los ya empleados, y por tanto de mayor durabilidad.
En la actualidad, ya se conocen y son utilizados diversos materiales refractarios; pero todos ellos presentan limitaciones tanto operativas como funcionales, muy especialmente con respecto a su degradación progresiva por las altas y alternantes temperaturas de los hornos, y a las reacciones químicas; con lo cual el uso de los medios ya desarrollados presentan siempre ciertas limitaciones frente a la invención que se presenta, en base a sus ventajas técnicas y económicas. Así, son ya conocidos como materiales refractarios, la incorporación de crisoles para la fabricación de vidrio, la cal, la sílice, el cromo, la magnetita, el óxido de aluminio, y los vidrios silicoaluminosos ( F.H. Norton, REFRACTARIOS, primera edición española de la editorial Blume del año 1972 ), o también las patentes japonesas nº JP11230679 sobre el juego de la porosidad en los ladrillos refractarios, la nº JP11130485 como paneles prefabricados, o la nº JP11201649 como texturas de vidrio, o también en relación a la disposición de formas de los materiales destaca la patente europea nº EP0911594 y la alemana DE19729582 de ladrillos prefabricados o bien la patente de invención del propio solicitante la Patente PCT nº WO 02/059057, todas ellas como anterioridades próximas a la invención que se presenta, pero genéricas e imprecisas y como invenciones todas de las que resultan composiciones químicas o formas o bien no aplicadas a la especificidad de la industria del cemento, o dispuestas en zonas diferentes de los mismos hornos de cemento.
Estas limitaciones se superan con la composición química de la invención – oxido de magnesio ( MgO) , alúmina ( Al2O3 ), grafito - , aditivos mejoradores y resinas ligantes; que acrecientan su operatividad y rendimiento y cuya estructura presenta una baja porosidad y alta capacidad refractaria.
El ladrillo refractario puede ser realizado y dispuesto de la siguiente manera :
En relación a los componentes químicos, un porcentaje en peso de Oxido de magnesio ( MgO) entre el 75 – 62 %, preferentemente de una oxido de magnesio de agua de mar, un porcentaje en peso de Alúmina ( Al2O3 ) entre un 12
– 20 %, y un 4 – 11 % de Grafito. Siendo la pureza del Grafito preferentemente de un 94 % cristalino y en escamas. Así como un porcentaje en peso de aditivos mejoradores del choque térmico y la resistencia térmica y la oxidación ( en una composición conjunta de aluminio en polvo, silicio metal, carburo de silicio y arcilla ) de entre un 9 – 7 %. Utilizándose como ligante sobre estos porcentajes totales resinas de entre un 3 – 4 % de porcentaje en peso.
En suma, el resultado obtenido por la combinación de elementos, permite obtener una ventaja técnica con un producto de mayor dureza y de mayor resistencia al calor y a las reacciones físico-químicas, y de la que derivan notables ventajas económicas, puesto que con la nueva invención, se reduce el número de paradas de los hornos para su mantenimiento y su consiguiente restitución del material desgastado en cada periodo de trabajo, así como también conlleva, además de las mencionadas mejoras técnicas y económicas, a una ventaja en el proceso productivo para los hornos más frecuentes y extendidos - los de tipo rotatorio – y consigue una mayor resistencia y dureza.
Para una mejor comprensión de las características generales anteriormente mencionadas, y en relación a su utilización, se acompañan unos dibujos a la presente invención los cuales exponen como se especifica a continuación:
Figura 1: Proyección de perfil de un horno rotativo para la industria del cemento con enfriadores satélites, en un conjunto formado por un intercambiador de calor ( 1 ) , una zona de calcinación ( 2 ), zona de seguridad ( 3 ), zonas de transición – alta y baja - ( 4 ), zona de sinterización ( 5 ), zona de salida ( 6 ), enfriadores ( 7 ) cabeza de horno ( 8 ) , y lanza quemador de llama ( 9 ).
Figura 2: Proyección de perfil de un horno rotativo para la industria del cemento con enfriador de parrilla, en un conjunto formado por un intercambiador de calor ( 1 ) , una zona de calcinación ( 2 ), zona de seguridad ( 3 ), zonas de transición – alta y baja -( 4 ), zona de sinterización ( 5 ), zona de salida ( 6 ), enfriador ( 7 ), cabeza de horno ( 8 ) y lanza quemador de llama ( 9 ).
Y siendo su disposición en los hornos para las zonas de utilización de este ladrillo refractario: las zonas de transición – alta y baja -( 4 ) y la zona de sinterización ( 5 ).

Claims (1)

  1. REIVINDICACIONES
    1. -Ladrillo refractario no cocido conteniendo grafito para hornos de la industria del cemento y su utilización para una mayor resistencia frente a la deformación térmica y físico -química caracterizado porque su composición química comprende la combinación de un porcentaje en peso de Oxido de magnesio (MgO) entre el 75
    – 62 %, un porcentaje en peso de Alúmina (Al2O3) entre un 12 – 20 %, y entre un 4 – 11 % de Grafito. Así como un porcentaje en peso de aditivos mejoradores del choque térmico y la resistencia térmica y la oxidación ( en una composición conjunta de aluminio en polvo, silicio metal, carburo de silicio y arcilla ) de entre un 9 – 7 %. Utilizándose como ligante sobre estos porcentajes totales resinas entre un 3 – 4 % de porcentaje en peso.
ES02774789T 2002-10-03 2002-10-03 Ladrillo refractario no cocido conteniendo grafito para hornos de la industria del cemento y su utilización. Expired - Lifetime ES2374134T3 (es)