ES2361010T3 - LIP BAR CONTAINING A SEQUENCED POLYMER. - Google Patents

LIP BAR CONTAINING A SEQUENCED POLYMER. Download PDF

Info

Publication number
ES2361010T3
ES2361010T3 ES03798229T ES03798229T ES2361010T3 ES 2361010 T3 ES2361010 T3 ES 2361010T3 ES 03798229 T ES03798229 T ES 03798229T ES 03798229 T ES03798229 T ES 03798229T ES 2361010 T3 ES2361010 T3 ES 2361010T3
Authority
ES
Spain
Prior art keywords
sequence
equal
composition according
polymer
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES03798229T
Other languages
Spanish (es)
Inventor
Véronique Ferrari
Xavier Blin
Bertrand Lion
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LOreal SA
Original Assignee
LOreal SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LOreal SA filed Critical LOreal SA
Application granted granted Critical
Publication of ES2361010T3 publication Critical patent/ES2361010T3/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Composición de maquillaje de los labios que incluye al menos un medio líquido orgánico cosméticamente aceptable y al menos un polímero etilénico secuenciado lineal filmógeno libre de estireno, cuyo polímero secuenciado contiene primera y segunda secuencias unidas entre sí por un segmento intermedio, que es un polímero estadístico que incluye al menos un monómero constitutivo de la primera secuencia y al menos un monómero constitutivo de la segunda secuencia, siendo seleccionada la primera secuencia del polímero entre: - a) una secuencia que tiene una Tg superior o igual a 40°C, - b) una secuencia que tiene una Tg inferior o igual a 20°C y - c) una secuencia que tiene una Tg comprendida entre 20 y 40°C, y siendo seleccionada la segunda secuencia en una categoría a), b) o c) diferente de la primera secuencia; y cuyo polímero secuenciado tiene un índice de polidispersidad I superior o igual a 2,8, siendo dicho polímero tal que, cuando está presente en cantidad suficiente en la composición, esta última es apta para formar un depósito que tiene un índice de persistencia superior o igual al 80%, determinado según el protocolo de medición descrito en la descripción.Lip makeup composition that includes at least one cosmetically acceptable organic liquid medium and at least one styrene-free linear film-forming sequential ethylene polymer, whose sequenced polymer contains first and second sequences linked together by an intermediate segment, which is a statistical polymer which includes at least one constituent monomer of the first sequence and at least one constituent monomer of the second sequence, the first polymer sequence being selected from: - a) a sequence having a Tg greater than or equal to 40 ° C, - b ) a sequence that has a Tg less than or equal to 20 ° C and - c) a sequence that has a Tg between 20 and 40 ° C, and the second sequence being selected in a category a), b) or c) different from the first sequence; and whose sequenced polymer has a polydispersity index I greater than or equal to 2.8, said polymer being such that, when present in sufficient quantity in the composition, the latter is suitable for forming a deposit having a persistence index greater than or equal to 80%, determined according to the measurement protocol described in the description.

Description

La presente invención tiene por objeto una composición cosmética de maquillaje de los labios que contiene un polímero secuenciado particular. The present invention aims at a cosmetic lip makeup composition containing a particular sequenced polymer.

Las composiciones de barra de labios son habitualmente empleadas para aportar un color estético a los labios. Estos productos de maquillaje contienen generalmente fases grasas, tales como ceras y aceites, pigmentos y/o cargas y eventualmente aditivos, como principios activos cosméticos o dermatológicos. Lipstick compositions are usually used to provide an aesthetic color to the lips. These makeup products generally contain fatty phases, such as waxes and oils, pigments and / or fillers and possibly additives, as cosmetic or dermatological active ingredients.

La patente EE.UU. 6.153.206 describe composiciones cosméticas, y especialmente barras de labios, que contienen copolímeros etilénicos lineales preparados por GTP (Group Transfer Polymerisation). La solicitud de patente FR U.S. Patent 6,153,206 describes cosmetic compositions, and especially lipsticks, containing linear ethylene copolymers prepared by GTP (Group Transfer Polymerisation). FR patent application

2.809.306 se relaciona con la utilización en composiciones cosméticas de maquillaje de copolímeros etilénicos secuenciados preparados por polimerización por radicales controlada. Finalmente, la solicitud de patente FR 2,809,306 relates to the use in cosmetic makeup compositions of sequenced ethylene copolymers prepared by controlled radical polymerization. Finally, the FR patent application

2.832.719 no publicada a fecha de depósito de la solicitud se relaciona con copolímeros etilénicos secuenciados que pueden ser preparados por polimerización por vía aniónica, por polimerización por radicales controlada o por polimerización por radicales clásica, y con su utilización en cosmética para mejorar el poder fijador y la permanencia. 2,832,719 not published at the time of deposit of the application relates to sequenced ethylene copolymers that can be prepared by anionic polymerization, by controlled radical polymerization or by classical radical polymerization, and with its use in cosmetics to improve power fixative and permanence.

Estas composiciones, cuando se aplican sobre los labios, presentan el inconveniente de transferirse, es decir, de depositarse al menos en parte, dejando rastros, sobre ciertos soportes con los que pueden entrar en contacto, y especialmente un vaso, una taza, un cigarrillo, una prenda de ropa o la piel. Se produce como resultado una mala permanencia de la película aplicada, que necesita una renovación regular de la aplicación de la composición de barra de labios. Por otra parte, el maquillaje de los labios puede también alterarse por contacto con líquidos, especialmente agua o bebidas consumidas por ejemplo durante una comida, o también aceites, como los aceites alimentarios, o también el sebo, o también la saliva, en particular tras un contacto con agua o con un aceite alimentario. These compositions, when applied to the lips, have the disadvantage of transferring, that is, of depositing at least in part, leaving traces, on certain supports with which they can come into contact, and especially a glass, a cup, a cigarette. , a piece of clothing or skin. It results in a poor permanence of the applied film, which needs a regular renewal of the application of the lipstick composition. On the other hand, the makeup of the lips can also be altered by contact with liquids, especially water or drinks consumed for example during a meal, or also oils, such as food oils, or also tallow, or also saliva, particularly after a contact with water or a food oil.

De forma más precisa, la presente invención tiene, pues, por objeto una composición cosmética de maquillaje de los labios (o barra de labios) que contiene al menos un medio líquido orgánico cosméticamente aceptable y al menos un polímero etilénico secuenciado lineal filmógeno tal como se describe a continuación, siendo la composición especialmente tal como se define más adelante. More precisely, the present invention therefore has as its object a cosmetic composition of lip makeup (or lipstick) containing at least one cosmetically acceptable organic liquid medium and at least one film-forming linear sequenced ethylenic polymer as it is described below, the composition being especially as defined below.

Ventajosamente, según un primer modo de realización de la composición según la invención, el polímero etilénico secuenciado lineal filmógeno está libre de estireno, conteniendo dicho polímero secuenciado primera y segunda secuencias unidas entre sí por un segmento intermedio, que es un polímero estadístico que incluye al menos un monómero constitutivo de la primera secuencia y al menos un monómero constitutivo de la segunda secuencia, siendo seleccionada la primera secuencia del polímero entre: Advantageously, according to a first embodiment of the composition according to the invention, the film-forming linear sequenced ethylene polymer is free of styrene, said first and second sequenced polymer containing sequences linked together by an intermediate segment, which is a statistical polymer that includes the at least one constituent monomer of the first sequence and at least one constituent monomer of the second sequence, the first polymer sequence being selected from:

--
a) una secuencia que tiene una Tg superior o igual a 40°C,  a) a sequence that has a Tg greater than or equal to 40 ° C,

--
b) una secuencia que tiene una Tg inferior o igual a 20°C y  b) a sequence that has a Tg less than or equal to 20 ° C and

--
c) una secuencia que tiene una Tg comprendida entre 20 y 40°C, y  c) a sequence having a Tg between 20 and 40 ° C, and

siendo seleccionada la segunda secuencia en una categoría a), b) o c) diferente de la primera secuencia; y teniendo dicho polímero secuenciado un índice de polidispersidad I superior o igual a 2,8, siendo dicho polímero tal que, cuando está presente en una cantidad suficiente en la composición, esta última es apta para formar un depósito con un índice de permanencia superior o igual al 80%. the second sequence being selected in a category a), b) or c) different from the first sequence; and said sequenced polymer having a polydispersity index I greater than or equal to 2.8, said polymer being such that, when present in a sufficient amount in the composition, the latter is suitable to form a deposit with a permanence index greater than or equal to 80%.

Ventajosamente, según un segundo modo de realización de la composición según la invención, el polímero etilénico secuenciado lineal filmógeno es no elastomérico, conteniendo dicho polímero secuenciado primera y segunda secuencias unidas entre sí por un segmento intermedio, que es un polímero estadístico que incluye al menos un monómero constitutivo de la primera secuencia y al menos un monómero constitutivo de la segunda secuencia, siendo seleccionada la primera secuencia del polímero entre: Advantageously, according to a second embodiment of the composition according to the invention, the ethylenic polymer film-forming linear sequencing is non-elastomeric, said first and second sequenced polymer containing sequences linked together by an intermediate segment, which is a statistical polymer that includes at least one constituent monomer of the first sequence and at least one constituent monomer of the second sequence, the first polymer sequence being selected from:

--
a) una secuencia que tiene una Tg superior o igual a 40°C,  a) a sequence that has a Tg greater than or equal to 40 ° C,

--
b) una secuencia que tiene una Tg inferior o igual a 20°C y  b) a sequence that has a Tg less than or equal to 20 ° C and

--
c) una secuencia que tiene una Tg comprendida entre 20 y 40°C, y  c) a sequence having a Tg between 20 and 40 ° C, and

siendo seleccionada la segunda secuencia en una categoría a), b) o c) diferente de la primera secuencia; y teniendo dicho polímero secuenciado un índice de polidispersidad I superior o igual a 2,8, siendo dicho polímero tal que, cuando está presente en una cantidad suficiente en la composición, esta última es apta para formar un depósito con un índice de permanencia superior o igual al 80%. the second sequence being selected in a category a), b) or c) different from the first sequence; and said sequenced polymer having a polydispersity index I greater than or equal to 2.8, said polymer being such that, when present in a sufficient amount in the composition, the latter is suitable to form a deposit with a permanence index greater than or equal to 80%.

La invención tiene igualmente por objeto un procedimiento cosmético de maquillaje de los labios, consistente en la A subject of the invention is also a cosmetic lip makeup procedure, consisting of the

aplicación sobre los labios de una composición tal como se ha definido anteriormente. application on the lips of a composition as defined above.

La invención tiene igualmente por objeto la utilización de una composición tal como se ha definido anteriormente para obtener un depósito de maquillaje sobre los labios que tiene una buena permanencia, especialmente una 5 buena permanencia tras un contacto con agua o con un aceite alimentario. The object of the invention is also the use of a composition as defined above to obtain a makeup deposit on the lips that has a good permanence, especially a good permanence after contact with water or a food oil.

La patente EE.UU. 6.153.206 describe una composición cosmética que incluye un polímero que contiene unidades repetitivas que tienen una Tg de -10 a 75°C y unidades repetitivas que tienen una Tg de 76 a 120°C. Describe igualmente polímeros de bloques que comprenden bloques de metacrilato de polimetilo y bloques de metacrilato de poliisobutilo, y también polímeros tribloque que comprenden bloques de metacrilato de polimetilo, bloques de metacrilato de poliisobutilo y bloques de metacrilato de etilo. U.S. Patent 6,153,206 describes a cosmetic composition that includes a polymer containing repetitive units having a Tg of -10 to 75 ° C and repetitive units having a Tg of 76 to 120 ° C. It also describes block polymers comprising polymethyl methacrylate blocks and polyisobutyl methacrylate blocks, and also triblock polymers comprising polymethyl methacrylate blocks, polyisobutyl methacrylate blocks and ethyl methacrylate blocks.

Los documentos FR-A-2.809.306 y WO 03/046032 describen composiciones cosméticas que contienen un polímero etilénico secuenciado. En los ejemplos, el único polímero ejemplificado tiene un índice de polidispersidad Documents FR-A-2,809,306 and WO 03/046032 describe cosmetic compositions containing a sequenced ethylene polymer. In the examples, the only exemplified polymer has a polydispersity index

15 respectivamente igual a 2,2 y 1,16. 15 respectively equal to 2.2 and 1.16.

Ventajosamente, el polímero etilénico secuenciado lineal filmógeno utilizado en la composición según la invención es tal que, cuando está presente en una cantidad suficiente en la composición, esta última es apta para formar un depósito con un índice de permanencia superior o igual al 80%, preferentemente superior o igual al 85%, preferentemente inferior o igual al 90% y preferentemente superior o igual al 95%. Advantageously, the film-forming linear ethylenic polymer used in the composition according to the invention is such that, when present in a sufficient amount in the composition, the latter is suitable for forming a deposit with a permanence index greater than or equal to 80%, preferably greater than or equal to 85%, preferably less than or equal to 90% and preferably greater than or equal to 95%.

El índice de permanencia del depósito obtenido con la composición según la invención es determinado según el protocolo de medición descrito a continuación. The permanence index of the deposit obtained with the composition according to the invention is determined according to the measurement protocol described below.

25 Se prepara un soporte (rectángulo de 40 mm X 70 mm) constituido por un revestimiento acrílico (adhesivo acrílico hipoalergénico sobre película de polietileno vendido bajo la denominación BLENDERME ref FH5000-55113 por la sociedad 3M Santé) pegado sobre una capa de espuma de polietileno adhesivo sobre la cara opuesta a aquélla sobre la cual se fija el esparadrapo (capa de espuma vendida bajo la denominación RE40X70EP3 de la sociedad JOINT TECHNIQUE LYONNAIS IND). 25 A support is prepared (rectangle of 40 mm X 70 mm) consisting of an acrylic coating (hypoallergenic acrylic adhesive on polyethylene film sold under the name BLENDERME ref FH5000-55113 by 3M Santé company) glued on a layer of polyethylene foam adhesive on the opposite side to that on which the tape is fixed (foam layer sold under the name RE40X70EP3 of the company JOINT TECHNIQUE LYONNAIS IND).

Se mide con un colorímetro MINOLTA CR 300 el color L*0a*0b*0 del soporte, por el lado de la cara de revestimiento acrílico. The color L * 0a * 0b * 0 of the support is measured with a MINOLTA CR 300 colorimeter, on the side of the acrylic coating face.

Se precalienta el soporte así preparado sobre una placa calefactora mantenida a una temperatura de 40°C para que 35 la superficie del soporte se mantenga a una temperatura de 33°C  1°C. The support thus prepared is preheated on a heating plate maintained at a temperature of 40 ° C so that the surface of the support is maintained at a temperature of 33 ° C  1 ° C.

Dejando el soporte sobre la placa calefactora, se aplica la composición a toda la superficie no adhesiva del soporte (es decir, a la superficie del revestimiento acrílico), extendiéndola con un pincel para obtener un depósito de la composición de aproximadamente 15 m, y luego se deja secar durante 10 minutos. Leaving the support on the heating plate, the composition is applied to the entire non-adhesive surface of the support (ie, to the surface of the acrylic coating), extending it with a brush to obtain a deposit of the composition of approximately 15 m, and then let it dry for 10 minutes.

Después de secar, se mide el color L*a*b* de la película así obtenida. After drying, the color L * a * b * of the film thus obtained is measured.

Se determina entonces la diferencia de color E1 entre el color de la película y el color del soporte desnudo por la relación siguiente. The color difference E1 is then determined between the color of the film and the color of the bare support by the following relationship.

45 Four. Five

imagen1image 1

Se pega entonces el soporte por su cara adhesiva (cara adhesiva de la capa de espuma) sobre un yunque de un diámetro de 20 mm y provisto de un paso de tornillo. Se recorta luego una pieza de ensayo del conjunto soporte/depósito con un sacabocados de un diámetro de 18 mm. Se atornilla entonces el yunque sobre una prensa (STATIF MANUEL IMADA SV-2, de la sociedad SOMECO) equipada con un dinamómetro (IMADA DPS-20, de la sociedad SOMECO). The support is then glued on its adhesive face (adhesive side of the foam layer) on an anvil with a diameter of 20 mm and provided with a screw passage. A test piece of the support / reservoir assembly is then trimmed with a punch with a diameter of 18 mm. The anvil is then screwed onto a press (STATIF MANUEL IMADA SV-2, from SOMECO) equipped with a dynamometer (IMADA DPS-20, from SOMECO).

Sobre un papel blanco para fotocopiadora de 80 g/m2 de gramaje, se dibuja una tira de 33 mm de anchura y 29,7 cm de longitud, se hace un primer trazo a 2 cm del borde de la hoja y luego un segundo trazo a 5 cm del borde de la On a white paper for photocopier of 80 g / m2 of grammage, a strip 33 mm wide and 29.7 cm long is drawn, a first line is made 2 cm from the edge of the sheet and then a second line 5 cm from the edge of the

55 hoja, delimitando así el primer y segundo trazos una casilla sobre la tira; se dispone después una primera marca y una segunda marca situadas en la tira respectivamente en las señales de 8 cm y 16 cm del segundo trazo. Se ponen sobre la primera marca 20 l de agua y sobre la segunda marca 10 l de aceite de girasol refinado (vendido por la sociedad LESIEUR). 55 sheet, thus delimiting the first and second strokes a square on the strip; A first mark and a second mark are then placed on the strip respectively in the 8 cm and 16 cm signals of the second line. They are placed on the first brand 20 µl of water and on the second brand 10 µl of refined sunflower oil (sold by the company LESIEUR).

Se coloca el papel blanco sobre el zócalo de la prensa y se prensa luego la pieza de ensayo colocada sobre la casilla de la tira de papel a una presión de aproximadamente 300 g/cm2 ejercida durante 30 segundos. Se retira después la prensa y se coloca de nuevo la pieza de ensayo justo después del segundo trazo (por lo tanto al lado de la casilla), se efectúa de nuevo una presión de aproximadamente 300 g/cm2 y se desplaza, de manera rectilínea desde el contacto efectuado, el papel con una velocidad de 1 cm/s sobre toda la longitud de la tira, de tal forma que la pieza de ensayo atraviesa los depósitos de agua y de aceite. Tras retirar la pieza de ensayo, una parte del depósito se ha transferido al papel. Se mide entonces el color L*’,a*’,b*’ del depósito que permanece sobre la pieza de ensayo. The white paper is placed on the press base and then the test piece placed on the paper strip box is pressed at a pressure of approximately 300 g / cm2 exerted for 30 seconds. The press is then removed and the test piece is placed again just after the second stroke (therefore next to the box), a pressure of approximately 300 g / cm2 is carried out again and it is moved, rectilinearly from the contact made, the paper with a speed of 1 cm / s over the entire length of the strip, so that the test piece crosses the water and oil tanks. After removing the test piece, a part of the tank has been transferred to the paper. The color L * ’, a *’, b * ’of the deposit remaining on the test piece is then measured.

Se determina entonces la diferencia de color E2 entre el color del depósito que permanece sobre la pieza de ensayo y el color del soporte desnudo por la relación siguiente. The color difference E2 is then determined between the color of the reservoir that remains on the test piece and the color of the bare support by the following ratio.

imagen1image 1

El índice de permanencia de la composición, expresado en porcentaje, es igual a la razón: The permanence index of the composition, expressed as a percentage, is equal to the ratio:

imagen1image 1

Se efectúa la medición sobre 6 soportes sucesivamente y el valor de transferencia corresponde a la media de las 6 medidas obtenidas con los 6 soportes. The measurement is carried out on 6 supports successively and the transfer value corresponds to the average of the 6 measurements obtained with the 6 supports.

Por líquido orgánico, se entiende todo producto no acuoso líquido a temperatura ambiente (25°C). By organic liquid, any liquid non-aqueous product is understood at room temperature (25 ° C).

Por medio líquido orgánico cosméticamente aceptable, se entiende un medio que incluye al menos un compuesto orgánico líquido a temperatura ambiente (25°C) y presión atmosférica (105 Pa) compatible con las materias queratínicas, especialmente la piel y los labios, tal como los aceites o los solventes orgánicos habitualmente By "cosmetically acceptable organic liquid medium" means means that includes at least one liquid organic compound at room temperature (25 ° C) and atmospheric pressure (105 Pa) compatible with keratinous materials, especially the skin and lips, such as oils or organic solvents usually

25 empleados en las composiciones cosméticas. 25 employees in cosmetic compositions.

La composición según la invención puede incluir un polímero secuenciado etilénico lineal filmógeno libre de estireno. The composition according to the invention may include a stylogen-free film-forming linear ethylenic sequenced polymer.

Por "polímero libre de estireno", se entiende un polímero que contiene menos de un 10%, preferentemente menos de un 5%, preferentemente menos de un 2%, preferentemente aún menos de un 1% en peso, incluso que no contiene, de monómero estirénico, tal como el estireno o los derivados del estireno, como por ejemplo el metilestireno, el cloroestireno o el clorometilestireno. By "styrene-free polymer" is meant a polymer containing less than 10%, preferably less than 5%, preferably less than 2%, preferably even less than 1% by weight, even not containing, of styrenic monomer, such as styrene or styrene derivatives, such as methylstyrene, chlorostyrene or chloromethylstyrene.

Según un modo de realización, el polímero secuenciado de la composición según la invención procede de According to one embodiment, the sequenced polymer of the composition according to the invention comes from

35 monómeros etilénicos alifáticos. Por monómero alifático, se entiende un monómero que no tiene ningún grupo aromático. 35 aliphatic ethylenic monomers. By aliphatic monomer, is meant a monomer that has no aromatic group.

Por polímero "etilénico", se entiende un polímero obtenido por polimerización de monómeros que tienen una insaturación etilénica. By "ethylenic" polymer is meant a polymer obtained by polymerization of monomers having an ethylenic unsaturation.

Por polímero "secuenciado", se entiende un polímero que comprende al menos 2 secuencias distintas, preferentemente al menos 3 secuencias distintas. By "sequenced" polymer, a polymer is understood as comprising at least 2 different sequences, preferably at least 3 different sequences.

El polímero es un polímero de estructura lineal. En contraposición, un polímero de estructura no lineal es, por 45 ejemplo, un polímero de estructura ramificada, en estrella, injertada u otra. The polymer is a linear structure polymer. In contrast, a polymer of non-linear structure is, for example, a polymer of branched, star, grafted or other structure.

Por polímero "filmógeno", se entiende un polímero apto para formar, por sí solo o en presencia de un agente auxiliar de formación de película, una película continua y adherente sobre un soporte, especialmente sobre las materias queratínicas. By "film-forming" polymer, is meant a polymer capable of forming, on its own or in the presence of an auxiliary film-forming agent, a continuous and adherent film on a support, especially on keratin materials.

Preferiblemente, el polímero utilizado en la composición según la invención no contiene átomos de silicio en su esqueleto. Por "esqueleto", se entiende la cadena principal del polímero, en contraposición a las cadenas laterales pendientes. Preferably, the polymer used in the composition according to the invention does not contain silicon atoms in its skeleton. By "skeleton", the main polymer chain is understood, as opposed to the pending side chains.

55 Ventajosamente, el polímero secuenciado comprende al menos una primera secuencia y al menos una segunda secuencia tales como las descritas anteriormente. Advantageously, the sequenced polymer comprises at least a first sequence and at least a second sequence such as those described above.

Por "al menos" una secuencia, se entiende una o más secuencias. By "at least" one sequence, one or more sequences are understood.

Se precisa que, en lo que antecede y lo que viene a continuación, los términos "primera" y "segunda" secuencias no condicionan en modo alguno el orden de dichas secuencias (o bloques) en la estructura del polímero. It is specified that, in the foregoing and in what follows, the terms "first" and "second" sequences do not in any way condition the order of said sequences (or blocks) in the polymer structure.

Preferentemente, la primera y segunda secuencias de dicho polímero secuenciado son incompatibles entre sí. Preferably, the first and second sequences of said sequenced polymer are incompatible with each other.

Por "secuencias incompatibles entre sí ", se entiende que la mezcla formada por el polímero correspondiente a la primera secuencia y por el polímero correspondiente a la segunda secuencia no es miscible en el líquido orgánico mayoritario en peso del medio líquido orgánico de la composición, a temperatura ambiente (25°C) y presión atmosférica (105 Pa), para un contenido de la mezcla de polímeros superior o igual al 5% en peso con respecto al peso total de la mezcla (polímeros y solvente), entendiéndose que: By "sequences incompatible with each other", it is understood that the mixture formed by the polymer corresponding to the first sequence and by the polymer corresponding to the second sequence is not miscible in the organic liquid majority by weight of the organic liquid medium of the composition, a ambient temperature (25 ° C) and atmospheric pressure (105 Pa), for a content of the polymer mixture greater than or equal to 5% by weight with respect to the total weight of the mixture (polymers and solvent), it being understood that:

i) dichos polímeros están presentes en la mezcla en un contenido tal que la razón ponderal respectiva va de 10/90 a 90/10, y que ii) cada uno de los polímeros correspondientes a la primera y segunda secuencias tiene una masa molecular media (en peso o en número) igual a la del polímero secuenciado +/- 15%. i) said polymers are present in the mixture in a content such that the respective weight ratio ranges from 10/90 to 90/10, and that ii) each of the polymers corresponding to the first and second sequences has a mean molecular mass ( by weight or number) equal to that of the sequenced polymer +/- 15%.

En caso de que el medio líquido orgánico comprenda una mezcla de líquidos orgánicos, y en la hipótesis de dos o más líquidos orgánicos presentes en proporciones másicas idénticas, dicha mezcla de polímeros no es miscible en al menos uno de ellos. If the organic liquid medium comprises a mixture of organic liquids, and in the hypothesis of two or more organic liquids present in identical mass proportions, said polymer mixture is not miscible in at least one of them.

Por supuesto, en caso de que el medio líquido orgánico comprenda un único líquido orgánico, este último es el líquido orgánico mayoritario. Of course, in case the organic liquid medium comprises a single organic liquid, the latter is the majority organic liquid.

Ventajosamente, el líquido orgánico mayoritario de la composición es el solvente orgánico de polimerización del polímero secuenciado o el solvente orgánico mayoritario de la mezcla de solventes orgánicos de polimerización del polímero secuenciado. Advantageously, the majority organic liquid of the composition is the organic polymerization solvent of the sequenced polymer or the majority organic solvent of the mixture of organic solvents for polymerization of the sequenced polymer.

Preferentemente, el polímero secuenciado utilizado en la composición según la invención no es hidrosoluble, es decir, que el polímero no es soluble en agua o en una mezcla de agua y de monoalcoholes inferiores lineales o ramificados de 2 a 5 átomos de carbono, como el etanol, el isopropanol o el n-propanol, sin modificación de pH, a un contenido en materia activa de al menos un 1% en peso y a temperatura ambiente (25°C). Preferably, the sequenced polymer used in the composition according to the invention is not water soluble, that is, that the polymer is not soluble in water or in a mixture of water and linear or branched lower monoalcohols of 2 to 5 carbon atoms, such as ethanol, isopropanol or n-propanol, without pH modification, at an active matter content of at least 1% by weight and at room temperature (25 ° C).

Preferentemente, el polímero secuenciado utilizado en la composición según la invención no es un elastómero. Preferably, the sequenced polymer used in the composition according to the invention is not an elastomer.

Por "polímero no elastomérico", se entiende un polímero que, cuando se le somete a una tensión destinada a estirarlo (por ejemplo en un 30% en relación a su longitud inicial), no recupera una longitud sensiblemente idéntica a su longitud inicial cuando cesa la tensión. By "non-elastomeric polymer", a polymer is understood which, when subjected to a tension intended to stretch it (for example by 30% in relation to its initial length), does not recover a length substantially identical to its initial length when it ceases the tension.

De manera más específica, por "polímero no elastomérico" se designa un polímero que tiene una recuperación instantánea Ri < 50% y una recuperación retardada R2h < 70% después de haber sufrido un alargamiento del 30%. Preferentemente, Ri es < 30% y R2h < 50%. More specifically, by "non-elastomeric polymer" is meant a polymer that has an instantaneous recovery Ri <50% and a delayed recovery R2h <70% after having suffered an elongation of 30%. Preferably, Ri is <30% and R2h <50%.

Con más precisión, el carácter no elastomérico del polímero es determinado según el protocolo siguiente: More precisely, the non-elastomeric character of the polymer is determined according to the following protocol:

Se prepara una película de polímero por vertido de una solución del polímero en una matriz teflonada y secado después durante 7 días en un ambiente controlado a 23  5°C y 50  10% de humedad relativa. Se obtiene entonces una película de aproximadamente 100 m de espesor en la que se recortan piezas de ensayo rectangulares (por ejemplo con el sacabocados) de una anchura de 15 mm y de una longitud de 80 mm. A polymer film is prepared by pouring a solution of the polymer into a Teflon matrix and then drying for 7 days in a controlled environment at 23  5 ° C and 50  10% relative humidity. A film of approximately 100 µm thick is then obtained in which rectangular test pieces (for example with the punch) of a width of 15 mm and a length of 80 mm are cut.

Se impone a esta muestra una solicitación de tracción con un aparato comercializado bajo la referencia Zwick, en las mismas condiciones de temperatura y de humedad que para el secado. A tensile stress is imposed on this sample with an apparatus marketed under the Zwick reference, under the same temperature and humidity conditions as for drying.

Se estiran las piezas de ensayo a una velocidad de de 50 mm/min y la distancia entre las mordazas es de 50 mm, lo que corresponde a la longitud inicial (I0) de la pieza de ensayo. The test pieces are stretched at a speed of 50 mm / min and the distance between the jaws is 50 mm, which corresponds to the initial length (I0) of the test piece.

Se determina la recuperación instantánea Ri de la manera siguiente: Instant recovery Ri is determined as follows:

--
se estira la pieza de ensayo en un 30% (máx), es decir, en aproximadamente 0,3 veces su longitud inicial (I0);  the test piece is stretched by 30% (max), that is, approximately 0.3 times its initial length (I0);

--
se relaja la tensión imponiendo una velocidad de retorno igual a la velocidad de tracción, o sea, 50 mm/min, y se mide el alargamiento residual de la pieza de ensayo en porcentaje después de volver a tensión nula (i).  the tension is relaxed by imposing a return speed equal to the traction speed, that is, 50 mm / min, and the residual elongation of the test piece is measured in percentage after returning to zero voltage (i).

La recuperación instantánea en % (Ri) viene dada por la fórmula siguiente: The instantaneous recovery in% (Ri) is given by the following formula:

Ri = ((máx – i)/máx) x 100 Ri = ((max - i) / max) x 100

Para determinar la recuperación retardada, se mide el alargamiento residual de la pieza de ensayo en porcentaje (2h). To determine the delayed recovery, the residual elongation of the test piece is measured in percentage (2h).

La recuperación retardada en % (R2h) viene dada por la fórmula siguiente: Delayed recovery in% (R2h) is given by the following formula:

R2h = ((máx – 2h)/máx) x 100 R2h = ((max - 2h) / max) x 100

A título puramente indicativo, un polímero utilizado según un modo de realización de la invención posee una recuperación instantánea Ri del 10% y una recuperación retardada R2h del 30%. For purely indicative purposes, a polymer used according to an embodiment of the invention has an instantaneous recovery of 10% Ri and a delayed recovery R2h of 30%.

El índice de polidispersidad I del polímero es igual a la razón de la masa media ponderal Mw con respecto a la masa media numérica Mn. The polydispersity index I of the polymer is equal to the ratio of the weight average mass Mw with respect to the number average mass Mn.

Se determinan las masas molares medias ponderales (Mw) y numéricas (Mn) por cromatografía líquida por permeación de gel (solvente THF, curva de calibración establecida con patrones de poliestireno lineal, detector refractométrico). The weight average (Mw) and numerical (Mn) molar masses are determined by liquid chromatography by gel permeation (THF solvent, calibration curve established with linear polystyrene standards, refractometric detector).

La masa media ponderal (Mw) del polímero utilizado en las composiciones según la invención es preferentemente inferior o igual a 300.000; va, por ejemplo, de 35.000 a 200.000, y mejor de 45.000 a 150.000. The weight average mass (Mw) of the polymer used in the compositions according to the invention is preferably less than or equal to 300,000; it goes, for example, from 35,000 to 200,000, and better from 45,000 to 150,000.

La masa media numérica (Mn) del polímero utilizado en las composiciones según la invención es preferentemente inferior o igual a 70.000; va, por ejemplo, de 10.000 a 60.000, y mejor de 12.000 a 50.000. The number average mass (Mn) of the polymer used in the compositions according to the invention is preferably less than or equal to 70,000; it goes, for example, from 10,000 to 60,000, and better from 12,000 to 50,000.

El índice de polidispersidad del polímero secuenciado utilizado en las composiciones según la invención va especialmente de 2,8 a 6. The polydispersity index of the sequenced polymer used in the compositions according to the invention is especially from 2.8 to 6.

Cada secuencia o bloque del polímero utilizado en las composiciones según la invención procede de un tipo de monómero o de varios tipos de monómeros diferentes. Each sequence or block of the polymer used in the compositions according to the invention is derived from one type of monomer or from several different types of monomers.

Ello significa que cada secuencia puede estar constituida por un homopolímero o por un copolímero, pudiendo ser este copolímero constitutivo de la secuencia a su vez estadístico o alterno. This means that each sequence can be constituted by a homopolymer or by a copolymer, this copolymer can be constitutive of the sequence in turn statistical or alternate.

Preferentemente, la secuencia intermedia procede esencialmente de monómeros constitutivos de la primera secuencia y de la segunda secuencia. Por "esencialmente", se entiende en al menos un 85%, preferentemente en al menos un 90%, mejor en un 95% y aún mejor en un 100%. Preferably, the intermediate sequence is essentially derived from monomers constituting the first sequence and the second sequence. By "essentially" is meant at least 85%, preferably at least 90%, better at 95% and even better at 100%.

Ventajosamente, la secuencia intermedia tiene una temperatura de transición vítrea Tg comprendida entre las temperaturas de transición vítrea de la primera y segunda secuencias. Advantageously, the intermediate sequence has a glass transition temperature Tg comprised between the glass transition temperatures of the first and second sequences.

Las temperaturas de transición vítrea indicadas de la primera y segunda secuencias pueden ser Tg teóricas determinadas a partir de las Tg teóricas de los monómeros constitutivos de cada una de las secuencias, que se pueden encontrar en un manual de referencia, tal como el Polymer Handbook, 3ª ed., 1989, John Wiley, según la relación siguiente, llamada Ley de Fox: The indicated glass transition temperatures of the first and second sequences may be theoretical Tg determined from the theoretical Tg of the constituent monomers of each of the sequences, which can be found in a reference manual, such as the Polymer Handbook, 3rd ed., 1989, John Wiley, according to the following relationship, called Fox's Law:

imagen1image 1

siendo i la fracción másica del monómero i en la secuencia considerada y siendo Tgi la temperatura de transición vítrea del homopolímero del monómero i. i being the mass fraction of monomer i in the sequence considered and Tgi being the glass transition temperature of homopolymer of monomer i.

Salvo indicación en contrario, las Tg indicadas para la primera y segunda secuencias en la presente solicitud son Tg teóricas. Unless otherwise indicated, the Tg indicated for the first and second sequences in the present application are theoretical Tg.

Ventajosamente, la primera y segunda secuencias del polímero son tales que la diferencia entre las temperaturas de transición vítrea de la primera y segunda secuencias es generalmente superior a 10°C, preferentemente superior a 20°C y mejor superior a 30°C. Advantageously, the first and second polymer sequences are such that the difference between the glass transition temperatures of the first and second sequences is generally greater than 10 ° C, preferably greater than 20 ° C and better greater than 30 ° C.

Se quiere designar en la presente invención mediante la expresión: «comprendido entre... y...», un intervalo de valores donde los límites mencionados quedan excluidos, y «de... a...» y «que va de... a...», un intervalo de valores donde los límites quedan incluidos. It is intended in the present invention by the expression: "comprised between ... and ...", a range of values where the mentioned limits are excluded, and "from ... to ..." and "ranging from ... to ... », a range of values where limits are included.

a) Secuencia que tiene una Tg superior o igual a 40°C a) Sequence that has a Tg greater than or equal to 40 ° C

5 La secuencia que tiene una Tg superior o igual a 40°C tiene, por ejemplo, una Tg de 40 a 150°C, preferentemente superior o igual a 50°C, por ejemplo de 50°C a 120°C, y mejor superior o igual a 60°C, por ejemplo de 60°C a 120°C. 5 The sequence having a Tg greater than or equal to 40 ° C has, for example, a Tg of 40 to 150 ° C, preferably greater than or equal to 50 ° C, for example 50 ° C to 120 ° C, and better greater than or equal to 60 ° C, for example from 60 ° C to 120 ° C.

La secuencia que tiene una Tg superior o igual a 40°C puede ser un homopolímero o un copolímero. The sequence having a Tg greater than or equal to 40 ° C may be a homopolymer or a copolymer.

10 En caso de que esta secuencia sea un homopolímero, procede de monómeros cuyo homopolímero tiene una temperatura de transición vítrea superior o igual a 40°C. 10 If this sequence is a homopolymer, it comes from monomers whose homopolymer has a glass transition temperature greater than or equal to 40 ° C.

En caso de que la primera secuencia sea un copolímero, puede proceder en todo o en parte de uno o de más 15 monómeros cuya naturaleza y concentración son seleccionadas de forma que la Tg del copolímero resultante sea superior o igual a 40°C. El copolímero puede, por ejemplo, incluir: If the first sequence is a copolymer, it can proceed in whole or in part from one or more of 15 monomers whose nature and concentration are selected such that the Tg of the resulting copolymer is greater than or equal to 40 ° C. The copolymer may, for example, include:

- monómeros cuyo homopolímero tiene una Tg superior o igual a 40°C, por ejemplo una Tg de 40 a - monomers whose homopolymer has a Tg greater than or equal to 40 ° C, for example a Tg of 40 to

150°C, preferentemente superior o igual a 50°C, por ejemplo de 50°C a 120°C, y mejor superior o igual a 20 60°C, por ejemplo de 60°C a 120°C, y 150 ° C, preferably greater than or equal to 50 ° C, for example from 50 ° C to 120 ° C, and better than or equal to 20 60 ° C, for example from 60 ° C to 120 ° C, and

- monómeros cuyo homopolímero tiene una Tg inferior a 40°C, seleccionados entre los monómeros cuyo homopolímero tiene una Tg comprendida entre 20 y 40°C y/o los monómeros cuyo homopolímero tiene una Tg inferior o igual a 20°C, por ejemplo una Tg de -100 a 20°C, preferentemente inferior a 15°C, especialmente de -80°C a 15°C y mejor inferior a 10°C, por ejemplo de -50°C a 0°C, tales como los que - monomers whose homopolymer has a Tg of less than 40 ° C, selected from the monomers whose homopolymer has a Tg between 20 and 40 ° C and / or the monomers whose homopolymer has a Tg of less than or equal to 20 ° C, for example a Tg from -100 to 20 ° C, preferably below 15 ° C, especially from -80 ° C to 15 ° C and better below 10 ° C, for example from -50 ° C to 0 ° C, such as those

25 se describen más adelante. 25 are described below.

Los monómeros cuyo homopolímero tiene una temperatura de transición vítrea superior o igual a 40°C son preferentemente seleccionados entre los monómeros siguientes, también llamados monómeros principales: Monomers whose homopolymer has a glass transition temperature greater than or equal to 40 ° C are preferably selected from the following monomers, also called principal monomers:

30 - los metacrilatos de fórmula CH2=C(CH3)-COOR1, donde R1 representa un grupo alquilo no substituido, lineal o ramificado, de 1 a 4 átomos de carbono, tal como un grupo metilo, etilo, propilo o isobutilo, o R1 representa un grupo cicloalquilo C4 a C12; 30 - methacrylates of formula CH2 = C (CH3) -COOR1, where R1 represents an unsubstituted, linear or branched alkyl group of 1 to 4 carbon atoms, such as a methyl, ethyl, propyl or isobutyl group, or R1 represents a C4 to C12 cycloalkyl group;

- los acrilatos de fórmula CH2=CH-COOR2, - acrylates of formula CH2 = CH-COOR2,

donde R2 representa un grupo cicloalquilo C4 a C12, tal como un grupo isobornilo o un grupo terc-butilo; 35 - las (met)acrilamidas de fórmula: wherein R2 represents a C4 to C12 cycloalkyl group, such as an isobornyl group or a tert-butyl group; 35 - the (meth) acrylamides of the formula:

imagen2image2

40 R7 representa H y R8 representa un grupo 1,1-dimetil-3-oxobutilo, y R’ designa H o metilo. Como ejemplo de monómeros, se pueden citar la N-butilacrilamida, la N-tbutilacrilamida, la N-isopropilacrilamida, la N,N-dimetilacrilamida y la N,N-dibutilacrilamida, R 7 represents H and R 8 represents a 1,1-dimethyl-3-oxobutyl group, and R 'designates H or methyl. As an example of monomers, there can be mentioned N-butylacrylamide, N-tbutylacrylamide, N-isopropylacrylamide, N, N-dimethylacrylamide and N, N-dibutyl acrylamide,

-y sus mezclas. -and their mixtures.

45 Son monómeros principales particularmente preferidos el metacrilato de metilo, el (met)acrilato de isobutilo, el (met)acrilato de isobornilo y sus mezclas. Particularly preferred major monomers are methyl methacrylate, isobutyl (meth) acrylate, isobornyl (meth) acrylate and mixtures thereof.

b) Secuencia que tiene una Tg inferior o igual a 20°C b) Sequence that has a Tg less than or equal to 20 ° C

50 La secuencia que tiene una Tg inferior o igual a 20°C tiene, por ejemplo, una Tg de -100 a 20°C, preferentemente inferior o igual a 15°C, especialmente de -80°C a 15°C y mejor inferior o igual a 10°C, por ejemplo de -50°C a 0°C. The sequence having a Tg of less than or equal to 20 ° C has, for example, a Tg of -100 to 20 ° C, preferably less than or equal to 15 ° C, especially of -80 ° C to 15 ° C and better less than or equal to 10 ° C, for example from -50 ° C to 0 ° C.

La secuencia que tiene una Tg inferior o igual a 20°C puede ser un homopolímero o un copolímero. The sequence having a Tg less than or equal to 20 ° C may be a homopolymer or a copolymer.

55 En caso de que esta secuencia sea un homopolímero, procede de monómeros tales que los homopolímeros preparados a partir de estos monómeros tienen temperaturas de transición vítrea inferiores o iguales a 20°C. Esta segunda secuencia puede ser un homopolímero, constituido por un solo tipo de monómero (donde la Tg del homopolímero correspondiente es inferior o igual a 20°C). 55 If this sequence is a homopolymer, it is derived from monomers such that the homopolymers prepared from these monomers have glass transition temperatures of less than or equal to 20 ° C. This second sequence may be a homopolymer, consisting of a single type of monomer (where the Tg of the corresponding homopolymer is less than or equal to 20 ° C).

En caso de que la secuencia que tiene una Tg inferior o igual a 20°C sea un copolímero, puede proceder en todo o en parte de uno o de más monómeros, cuya naturaleza y concentración son seleccionadas de forma que la Tg del copolímero resultante sea inferior o igual a 20°C. In the event that the sequence having a Tg less than or equal to 20 ° C is a copolymer, it may proceed in whole or in part from one or more monomers, the nature and concentration of which are selected so that the Tg of the resulting copolymer is less than or equal to 20 ° C.

Puede, por ejemplo, incluir: It can, for example, include:

--
uno o más monómeros cuyo correspondiente homopolímero tiene una Tg inferior o igual a 20°C, por ejemplo una Tg de -100°C a 20°C, preferentemente inferior a 15°C, especialmente de -80°C a 15°C y mejor inferior a 10°C, por ejemplo de -50°C a 0°C, y  one or more monomers whose corresponding homopolymer has a Tg less than or equal to 20 ° C, for example a Tg of -100 ° C to 20 ° C, preferably less than 15 ° C, especially from -80 ° C to 15 ° C and better below 10 ° C, for example from -50 ° C to 0 ° C, and

--
uno o más monómeros cuyo correspondiente homopolímero tiene una Tg superior a 20°C, tales como los monómeros que tienen una Tg superior o igual a 40°C, por ejemplo una Tg de 40 a 150°C, preferentemente superior o igual a 50°C, por ejemplo de 50°C a 120°C, y mejor superior o igual a 60°C, por ejemplo de 60°C a 120°C, y/o los monómeros que tienen una Tg comprendida entre 20 y 40°C, tales como los descritos anteriormente.  one or more monomers whose corresponding homopolymer has a Tg greater than 20 ° C, such as monomers having a Tg greater than or equal to 40 ° C, for example a Tg of 40 to 150 ° C, preferably greater than or equal to 50 ° C, for example from 50 ° C to 120 ° C, and better than or equal to 60 ° C, for example from 60 ° C to 120 ° C, and / or monomers having a Tg between 20 and 40 ° C , such as those described above.

Preferentemente, la secuencia que tiene una Tg inferior o igual a 20°C es un homopolímero. Preferably, the sequence having a Tg less than or equal to 20 ° C is a homopolymer.

Los monómeros cuyo homopolímero tiene una Tg inferior o igual a 20°C son preferentemente seleccionados entre los monómeros siguientes, o monómeros principales: Monomers whose homopolymer has a Tg less than or equal to 20 ° C are preferably selected from the following monomers, or major monomers:

--
los acrilatos de fórmula CH2=CHCOOR3, representando R3 un grupo alquilo no substituido C1 a C12, lineal o ramificado, a excepción del grupo tercbutilo, donde se encuentran eventualmente intercalados uno o más heteroátomos seleccionados entre O, N yS;  acrylates of formula CH2 = CHCOOR3, R3 representing a C1 to C12 unsubstituted alkyl group, linear or branched, with the exception of the tert-butyl group, where one or more heteroatoms selected from O are eventually intercalated, N yS;

--
los metacrilatos de fórmula CH2=C(CH3)-COOR4, representando R4 un grupo alquilo no substituido C6 a C12 lineal o ramificado, donde se encuentran eventualmente intercalados uno o más heteroátomos seleccionados entre 0, N y S;  methacrylates of formula CH2 = C (CH3) -COOR4, R4 representing a linear or branched C6 to C12 unsubstituted alkyl group, where they are located possibly interleaved one or more heteroatoms selected from 0, N and S;

--
los ésteres de vinilo de fórmula R5-CO-O-CH=CH2, donde R5 representa un grupo alquilo C4 a C12 lineal o ramificado;  vinyl esters of formula R5-CO-O-CH = CH2, where R5 represents a linear or branched C4 to C12 alkyl group;

--
los éteres de alcohol vinílico y de alcohol C4 a C12;  ethers of vinyl alcohol and C4 to C12 alcohol;

--
las N-alquil(C4 a C12)acrilamidas, tales como la N-octilacrilamida,  N-C4 to C12 alkyl acrylamides, such as N-octylacrylamide,

-y sus mezclas. -and their mixtures.

Los monómeros principales particularmente preferidos para la secuencia que tiene una Tg inferior o igual a 20°C son los acrilatos de alquilos cuya cadena de alquilo tiene de 1 a 10 átomos de carbono, a excepción del grupo terc-butilo, tales como el acrilato de metilo, el acrilato de isobutilo, el acrilato de 2-etilhexilo y sus mezclas. Particularly preferred major monomers for the sequence having a Tg less than or equal to 20 ° C are alkyl acrylates whose alkyl chain has 1 to 10 carbon atoms, with the exception of the tert-butyl group, such as the acrylate of methyl, isobutyl acrylate, 2-ethylhexyl acrylate and mixtures thereof.

c) Secuencia que tiene una Tg comprendida entre 20 y 40°C c) Sequence that has a Tg between 20 and 40 ° C

La secuencia que tiene una Tg comprendida entre 20 y 40°C puede ser un homopolímero o un copolímero. The sequence having a Tg between 20 and 40 ° C can be a homopolymer or a copolymer.

En caso de que esta secuencia sea un homopolímero, procede de un monómero (o monómero principal) cuyo homopolímero tiene una temperatura de transición vítrea comprendida entre 20 y 40°C. If this sequence is a homopolymer, it comes from a monomer (or main monomer) whose homopolymer has a glass transition temperature between 20 and 40 ° C.

Los monómeros cuyo homopolímero tiene una temperatura de transición vítrea comprendida entre 20 y 40°C son preferentemente seleccionados entre el metacrilato de n-butilo, el acrilato de ciclodecilo, el acrilato de neopentilo, la isodecilacrilamida y sus mezclas. Monomers whose homopolymer has a glass transition temperature between 20 and 40 ° C are preferably selected from n-butyl methacrylate, cyclodecyl acrylate, neopentyl acrylate, isodecyl acrylamide and mixtures thereof.

En caso de que la secuencia que tiene una Tg comprendida entre 20 y 40°C sea un copolímero, procede en todo o en parte de uno o de más monómeros (o monómeros principales) cuya naturaleza y concentración son seleccionadas de tal forma que la Tg del copolímero resultante esté comprendida entre 20 y 40°C. In the event that the sequence having a Tg between 20 and 40 ° C is a copolymer, it comes in whole or in part from one or more monomers (or main monomers) whose nature and concentration are selected such that the Tg of the resulting copolymer is between 20 and 40 ° C.

Ventajosamente, la secuencia que tiene una Tg comprendida entre 20 y 40°C es un copolímero procedente en todo Advantageously, the sequence having a Tg between 20 and 40 ° C is a copolymer from all

o en parte: or in part:

--
de monómeros principales cuyo correspondiente homopolímero tiene una Tg superior o igual a 40°C, por ejemplo una Tg de 40°C a 150°C, preferentemente superior o igual a 50°C, por ejemplo de 50 a 120°C, y mejor superior o igual a 60°C, por ejemplo de 60°C a 120°C, tales como los descritos anteriormente, y  of main monomers whose corresponding homopolymer has a Tg greater than or equal to 40 ° C, for example a Tg of 40 ° C to 150 ° C, preferably greater than or equal to 50 ° C, for example 50 to 120 ° C, and better greater than or equal to 60 ° C, for example from 60 ° C to 120 ° C, such as those described above, and

--
de monómeros principales cuyo correspondiente homopolímero tiene una Tg inferior o igual a 20°C, por  of main monomers whose corresponding homopolymer has a Tg less than or equal to 20 ° C, for

ejemplo una Tg de -100 a 20°C, preferentemente inferior o igual a 15°C, especialmente de -80°C a 15°C y mejor inferior o igual a 10°C, por ejemplo de -50°C a 0°C, tales como los descritos anteriormente, siendo seleccionados dichos monómeros de tal forma que la Tg del copolímero que forma la primera secuencia esté comprendida entre 20 y 40°C. for example a Tg of -100 to 20 ° C, preferably less than or equal to 15 ° C, especially -80 ° C to 15 ° C and better than or equal to 10 ° C, for example from -50 ° C to 0 ° C, such as those described above, said monomers being selected such that the Tg of the copolymer forming the first sequence is between 20 and 40 ° C.

Tales monómeros principales son, por ejemplo, seleccionados entre el metacrilato de metilo, el acrilato y el metacrilato de isobornilo, el acrilato de butilo, el acrilato de 2-etilhexilo y sus mezclas. Such major monomers are, for example, selected from methyl methacrylate, acrylate and isobornyl methacrylate, butyl acrylate, 2-ethylhexyl acrylate and mixtures thereof.

Preferentemente, la proporción de la segunda secuencia que tiene una Tg inferior o igual a 20°C va del 10 al 85% en peso del polímero, mejor del 20 al 70% y aún mejor del 20 al 50%. Preferably, the proportion of the second sequence having a Tg of less than or equal to 20 ° C ranges from 10 to 85% by weight of the polymer, better from 20 to 70% and even better from 20 to 50%.

Preferentemente, el polímero utilizado en las composiciones según la invención está libre de estireno. Preferably, the polymer used in the compositions according to the invention is free of styrene.

Cada una de las secuencias puede, no obstante, contener en proporción minoritaria al menos un monómero constitutivo de la otra secuencia. Each of the sequences can, however, contain in a minor proportion at least one constituent monomer of the other sequence.

Así, la primera secuencia puede contener al menos un monómero constitutivo de la segunda secuencia y a la inversa. Thus, the first sequence may contain at least one constituent monomer of the second sequence and vice versa.

Cada una de la primera y/o segunda secuencias puede contener, aparte de los monómeros indicados anteriormente, uno o más de otros monómeros llamados monómeros adicionales, diferentes de los monómeros principales antes citados. Each of the first and / or second sequences may contain, apart from the monomers indicated above, one or more other monomers called additional monomers, different from the main monomers mentioned above.

La naturaleza y la cantidad de este o estos monómeros adicionales son seleccionadas de manera que la secuencia en la cual se encuentran tenga la temperatura de transición vítrea deseada. The nature and amount of this or these additional monomers are selected so that the sequence in which they are found has the desired glass transition temperature.

Este monómero adicional es, por ejemplo, seleccionado entre: This additional monomer is, for example, selected from:

a) los monómeros hidrofílicos, tales como: a) hydrophilic monomers, such as:

--
los monómeros con insaturación(es) etilénica(s) que tienen al menos una función ácido carboxílico o  monomers with ethylenic unsaturation (s) that have at least one carboxylic acid function or

sulfónico, como por ejemplo: el ácido acrílico, el ácido metacrílico, el ácido crotónico, el anhídrido maleico, el ácido itacónico, el ácido fumárico, el ácido maleico, el ácido acrilamidopropanosulfónico, el ácido vinilbenzoico, el ácido vinilfosfórico y las sales de éstos; sulfonic acid, such as: acrylic acid, methacrylic acid, crotonic acid, maleic anhydride, itaconic acid, fumaric acid, maleic acid, acrylamidopropanesulfonic acid, vinylbenzoic acid, vinyl phosphoric acid and salts thereof ;

--
los monómeros con insaturación(es) etilénica(s) que tienen al menos una función amina terciaria, como la 2-vinilpiridina, la 4-vinilpiridina, el metacrilato de dimetilaminoetilo, el metacrilato de dietilaminoetilo, la dimetilaminopropilmetacrilamida y las sales de éstos;  monomers with ethylenic unsaturation (s) that have at least one tertiary amine function, such as 2-vinylpyridine, 4-vinylpyridine, dimethylaminoethyl methacrylate, diethylaminoethyl methacrylate, dimethylaminopropyl methacrylamide and salts thereof;

--
los metacrilatos de fórmula CH2=C(CH3)-COOR6, donde R6 representa un grupo alquilo lineal o ramificado de 1 a 4 átomos de carbono, tal como un grupo metilo, etilo, propilo o isobutilo, estando dicho grupo alquilo substituido por uno o más substituyentes seleccionados entre los grupos hidroxilo (como el metacrilato de 2-hidroxipropilo y el metacrilato de 2-hidroxietilo) y los átomos de halógenos (Cl, Br, I y F), tales como el metacrilato de trifluoroetilo;  methacrylates of formula CH2 = C (CH3) -COOR6, where R6 represents a linear or branched alkyl group of 1 to 4 carbon atoms, such as a methyl, ethyl, propyl or isobutyl group, said alkyl group being substituted by one or more substituents selected from the hydroxyl groups (such as 2-hydroxypropyl methacrylate and 2-hydroxyethyl methacrylate) and halogen atoms (Cl, Br, I and F), such as trifluoroethyl methacrylate;

--
los metacrilatos de fórmula CH2=C(CH3)-COOR9, representando R9 un grupo alquilo C6 a C12 lineal o ramificado, en el cual se encuentran eventualmente intercalados uno o más heteroátomos seleccionados entre 0, N y S, estando dicho grupo alquilo substituido por uno o más substituyentes seleccionados entre los grupos hidroxilo y los átomos de halógenos (Cl, Br, I y F);  methacrylates of formula CH2 = C (CH3) -COOR9, R9 representing a linear or branched C6 to C12 alkyl group, in which one or more heteroatoms selected from 0, N and S are intercalated, said alkyl group being substituted by one or more substituents selected from the hydroxyl groups and the halogen atoms (Cl, Br, I and F);

--
los acrilatos de fórmula CH2=CHCOOR10, representando R10 un grupo alquilo C1 a C12 lineal o ramificado substituido por uno o más substituyentes seleccionados entre los grupos hidroxilo y los átomos de halógeno (Cl, Br, I y F), tales como el acrilato de 2-hidroxipropilo y el acrilato de 2-hidroxietilo, o R10 representa un alquil(C1-C12)-OPOE (polioxietileno) con repetición de la unidad de oxietileno de 5 a 30 veces, por ejemplo metoxi-POE, o R10 representa un grupo polioxietilenado con 5 a 30 unidades de óxido de etileno;  acrylates of formula CH2 = CHCOOR10, R10 representing a linear or branched C1 to C12 alkyl group substituted by one or more substituents selected from hydroxyl groups and halogen atoms (Cl, Br, I and F), such as acrylate of 2-hydroxypropyl and 2-hydroxyethyl acrylate, or R10 represents a (C1-C12) -OPOE (polyoxyethylene) alkyl with repeat of the oxyethylene unit 5 to 30 times, for example methoxy-POE, or R10 represents a group polyoxyethylene with 5 to 30 units of ethylene oxide;

b) los monómeros con insaturación etilénica que tienen uno o más átomos de silicio, tales como el metacriloxipropiltrimetoxisilano y el metacriloxipropiltris(trimetilsiloxi)silano; b) ethylenically unsaturated monomers having one or more silicon atoms, such as methacryloxypropyltrimethoxysilane and methacryloxypropyltris (trimethylsiloxy) silane;

-y sus mezclas. -and their mixtures.

Son monómeros adicionales particularmente preferidos el ácido acrílico, el ácido metacrílico, el metacrilato de trifluoroetilo y sus mezclas. Particularly preferred additional monomers are acrylic acid, methacrylic acid, trifluoroethyl methacrylate and mixtures thereof.

Según un modo preferido de realización, el polímero utilizado en las composiciones según la invención es un polímero no siliconado, es decir, un polímero libre de átomo de silicio. According to a preferred embodiment, the polymer used in the compositions according to the invention is a non-siliconized polymer, that is, a silicon atom free polymer.

Este o estos monómeros adicionales representan generalmente una cantidad inferior o igual al 30% en peso, por ejemplo del 1 al 30% en peso, preferentemente del 5 al 20% en peso y preferentemente aún del 7 al 15% en peso del peso total de la primera y/o segunda secuencias. This or these additional monomers generally represent an amount less than or equal to 30% by weight, for example from 1 to 30% by weight, preferably from 5 to 20% by weight and preferably still from 7 to 15% by weight of the total weight of the first and / or second sequences.

Preferentemente, cada una de la primera y segunda secuencias incluye al menos un monómero seleccionado entre los ésteres de ácido (met)acrílico tales como los definidos anteriormente y eventualmente un monómero seleccionado entre el ácido (met)acrílico, y sus mezclas. Preferably, each of the first and second sequences includes at least one monomer selected from the esters of (meth) acrylic acid such as those defined above and possibly a monomer selected from (meth) acrylic acid, and mixtures thereof.

Ventajosamente, cada una de la primera y segunda secuencias procede en su totalidad de al menos un monómero seleccionado entre los ésteres de ácido (met)acrílico tales como los definidos anteriormente y eventualmente un monómero seleccionado entre el ácido (met)acrílico, y sus mezclas. Advantageously, each of the first and second sequences comes entirely from at least one monomer selected from the esters of (meth) acrylic acid such as those defined above and, optionally, a monomer selected from the (meth) acrylic acid, and mixtures thereof. .

El polímero utilizado en las composiciones según la invención puede ser obtenido por polimerización por radicales en solución según el procedimiento de preparación siguiente: The polymer used in the compositions according to the invention can be obtained by radical polymerization in solution according to the following preparation procedure:

- se introduce una parte del solvente de polimerización en un reactor adaptado y se calienta hasta alcanzar la temperatura adecuada para la polimerización (típicamente entre 60 y 120°C); - a part of the polymerization solvent is introduced into an adapted reactor and heated to the appropriate temperature for polymerization (typically between 60 and 120 ° C);

-una vez alcanzada esta temperatura, se introducen los monómeros constitutivos de la primera secuencia en presencia de una parte del iniciador de polimerización; - once this temperature has been reached, the constituent monomers of the first sequence are introduced in the presence of a part of the polymerization initiator;

--
al cabo de un tiempo T correspondiente a una razón de conversión máxima del 90%, se introducen los monómeros constitutivos de la segunda secuencia y la otra parte del iniciador;  after a time T corresponding to a maximum conversion ratio of 90%, the constituent monomers of the second sequence and the other part of the initiator are introduced;

--
se deja reaccionar a la mezcla durante un tiempo T’ (que va de 3 a 6 h), al cabo del cual se vuelve a llevar la mezcla a temperatura ambiente;  the mixture is allowed to react for a time T ’(ranging from 3 to 6 h), after which the mixture is brought back to room temperature;

--
se obtiene el polímero en solución en el solvente de polimerización.  The polymer in solution is obtained in the polymerization solvent.

Por solvente de polimerización, se entiende un solvente o una mezcla de solventes. El solvente de polimerización puede ser seleccionado especialmente entre el acetato de etilo, el acetato de butilo, los alcoholes tales como el isopropanol y el etanol, los alcanos alifáticos tales como el isododecano y sus mezclas. Preferentemente, el solvente de polimerización es una mezcla de acetato de butilo e isopropanol o el isododecano. By polymerization solvent, is meant a solvent or a mixture of solvents. The polymerization solvent can be selected especially from ethyl acetate, butyl acetate, alcohols such as isopropanol and ethanol, aliphatic alkanes such as isododecane and mixtures thereof. Preferably, the polymerization solvent is a mixture of butyl acetate and isopropanol or isododecane.

Según un primer modo de realización, el polímero utilizado en las composiciones según la invención comprende al menos una (especialmente una) primera secuencia que tiene una Tg superior o igual a 40°C, tal como se ha descrito anteriormente en a), y al menos una (especialmente una) segunda secuencia que tiene una Tg inferior o igual a 20°C, tal como se ha descrito anteriormente en b). According to a first embodiment, the polymer used in the compositions according to the invention comprises at least one (especially one) first sequence having a Tg greater than or equal to 40 ° C, as described above in a), and at minus one (especially a) second sequence having a Tg less than or equal to 20 ° C, as described above in b).

Preferentemente, la primera secuencia que tiene una Tg superior o igual a 40°C es un copolímero procedente de monómeros cuyo homopolímero tiene una temperatura de transición vítrea superior o igual a 40°C, tales como los monómeros antes descritos. Ventajosamente, la segunda secuencia que tiene una Tg inferior o igual a 20°C es un homopolímero, especialmente procedente de monómeros tales como los antes descritos. Preferably, the first sequence having a Tg greater than or equal to 40 ° C is a copolymer from monomers whose homopolymer has a glass transition temperature greater than or equal to 40 ° C, such as the monomers described above. Advantageously, the second sequence having a Tg of less than or equal to 20 ° C is a homopolymer, especially from monomers such as those described above.

Preferentemente, la proporción de la secuencia que tiene una Tg superior o igual a 40°C va del 20 al 90% en peso del polímero, mejor del 30 al 80% y aún mejor del 50 al 70%. Preferably, the proportion of the sequence having a Tg greater than or equal to 40 ° C ranges from 20 to 90% by weight of the polymer, better from 30 to 80% and even better from 50 to 70%.

Preferentemente, la proporción de la secuencia que tiene una Tg inferior o igual a 20°C va del 5 al 75% en peso del polímero, preferentemente del 15 al 50% y mejor del 25 al 45%. Preferably, the proportion of the sequence having a Tg of less than or equal to 20 ° C ranges from 5 to 75% by weight of the polymer, preferably from 15 to 50% and better from 25 to 45%.

Así, según una primera variante, el polímero utilizado en las composiciones según la invención puede comprender: Thus, according to a first variant, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo con una Tg de 70 a 110°C, que es un copolímero de metacrilato de metilo/ácido acrílico,  a first sequence of Tg greater than or equal to 40 ° C, for example with a Tg of 70 to 110 ° C, which is a methyl methacrylate / acrylic acid copolymer,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de 0 a 20°C, que es un homopolímero de acrilato de metilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from 0 to 20 ° C, which is a homopolymer of methyl acrylate, and

--
una secuencia intermedia, que es un copolímero de metacrilato de metilo/ácido acrílico/acrilato de metilo.  an intermediate sequence, which is a copolymer of methyl methacrylate / acrylic acid / methyl acrylate.

Según una segunda variante, el polímero utilizado en las composiciones según la invención puede comprender: According to a second variant, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo de 70 a 100°C, que es un copolímero de metacrilato de metilo/ácido acrílico/metacrilato de trifluoroetilo,  a first sequence of Tg greater than or equal to 40 ° C, for example from 70 to 100 ° C, which is a copolymer of methyl methacrylate / acrylic acid / trifluoroethyl methacrylate,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de 0 a 20°C, que es un homopolímero de acrilato de metilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from 0 to 20 ° C, which is a homopolymer of methyl acrylate, and

--
una secuencia intermedia, que es un copolímero estadístico de metacrilato de metilo/ácido acrílico/acrilato de metilo/metacrilato de trifluoroetilo.  an intermediate sequence, which is a statistical copolymer of methyl methacrylate / acrylic acid / methyl acrylate / trifluoroethyl methacrylate.

Según una tercera variante, el polímero utilizado en las composiciones según la invención puede comprender: According to a third variant, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo de 85 a 115°C, que es un copolímero de acrilato de isobornilo/metacrilato de isobutilo,  a first sequence of Tg greater than or equal to 40 ° C, for example from 85 to 115 ° C, which is an isobornyl acrylate / isobutyl methacrylate copolymer,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de -85 a -55°C, que es un homopolímero de acrilato de 2-etilhexilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from -85 to -55 ° C, which is a homopolymer of 2-ethylhexyl acrylate, and

--
una secuencia intermedia, que es un copolímero estadístico de acrilato de isobornilo/metacrilato de isobutilo/acrilato de 2-etilhexilo.  an intermediate sequence, which is a statistical copolymer of isobornyl acrylate / isobutyl methacrylate / 2-ethylhexyl acrylate.

Según una cuarta variante, el polímero utilizado en las composiciones según la invención puede comprender: According to a fourth variant, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo de 85 a 115°C, que es un copolímero de acrilato de isobornilo/metacrilato de metilo,  a first sequence of Tg greater than or equal to 40 ° C, for example from 85 to 115 ° C, which is an isobornyl acrylate / methyl methacrylate copolymer,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de -85 a -55°C, que es un homopolímero de acrilato de 2-etilhexilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from -85 to -55 ° C, which is a homopolymer of 2-ethylhexyl acrylate, and

--
una secuencia intermedia, que es un copolímero estadístico de acrilato de isobornilo/metacrilato de metilo/acrilato de 2-etilhexilo.  an intermediate sequence, which is a statistical copolymer of isobornyl acrylate / methyl methacrylate / 2-ethylhexyl acrylate.

Según una quinta variante, el polímero utilizado en las composiciones según la invención puede comprender: According to a fifth variant, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo de 95 a 125°C, que es un copolímero de acrilato de isobornilo/metacrilato de isobornilo,  a first sequence of Tg greater than or equal to 40 ° C, for example from 95 to 125 ° C, which is an isobornyl acrylate / isobornyl methacrylate copolymer,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de -85 a -55°C, que es un homopolímero de acrilato de 2-etilhexilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from -85 to -55 ° C, which is a homopolymer of 2-ethylhexyl acrylate, and

--
una secuencia intermedia, que es un copolímero estadístico de acrilato de isobornilo/metacrilato de isobornilo/acrilato de 2-etilhexilo.  an intermediate sequence, which is a statistical copolymer of isobornyl acrylate / isobornyl methacrylate / 2-ethylhexyl acrylate.

Según una sexta variante, el polímero utilizado en las composiciones según la invención puede comprender: According to a sixth variant, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo de 85 a 115°C, que es un copolímero de metacrilato de isobornilo/metacrilato de isobutilo,  a first sequence of Tg greater than or equal to 40 ° C, for example from 85 to 115 ° C, which is an isobornyl methacrylate / isobutyl methacrylate copolymer,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de -35 a -5°C, que es un homopolímero de acrilato de isobutilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from -35 to -5 ° C, which is an isobutyl acrylate homopolymer, and

--
una secuencia intermedia, que es un copolímero estadístico de metacrilato de isobornilo/metacrilato de isobutilo/acrilato de isobutilo.  an intermediate sequence, which is a statistical copolymer of isobornyl methacrylate / isobutyl methacrylate / isobutyl acrylate.

Según una séptima variante, el polímero utilizado en las composiciones según la invención puede comprender: According to a seventh variant, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo de 95 a 125°C, que es un copolímero de acrilato de isobornilo/metacrilato de isobornilo,  a first sequence of Tg greater than or equal to 40 ° C, for example from 95 to 125 ° C, which is an isobornyl acrylate / isobornyl methacrylate copolymer,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de -35 a -5°C, que es un homopolímero de acrilato de isobutilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from -35 to -5 ° C, which is an isobutyl acrylate homopolymer, and

--
una secuencia intermedia, que es un copolímero estadístico de metacrilato de isobornilo/metacrilato de isobornilo/acrilato de isobutilo.  an intermediate sequence, which is a statistical copolymer of isobornyl methacrylate / isobornyl methacrylate / isobutyl acrylate.

Según una octava variante, el polímero según la invención puede comprender: According to an eighth variant, the polymer according to the invention may comprise:

--
una primera secuencia de Tg superior o igual a 40°C, por ejemplo de 60 a 90°C, que es un copolímero de acrilato de isobornilo/metacrilato de isobutilo,  a first sequence of Tg greater than or equal to 40 ° C, for example from 60 to 90 ° C, which is an isobornyl acrylate / isobutyl methacrylate copolymer,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de -35 a -5°C, que es un homopolímero de acrilato de isobutilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from -35 to -5 ° C, which is an isobutyl acrylate homopolymer, and

--
una secuencia intermedia, que es un copolímero estadístico de acrilato de isobornilo/metacrilato de isobutilo/acrilato de isobutilo.  an intermediate sequence, which is a statistical copolymer of isobornyl acrylate / isobutyl methacrylate / isobutyl acrylate.

Según un segundo modo de realización, el polímero utilizado en las composiciones según la invención comprende al menos una (especialmente una) primera secuencia que tiene una temperatura de transición vítrea (Tg) comprendida entre 20 y 40°C, conforme a las secuencias descritas en c), y al menos una (especialmente una) segunda secuencia que tiene una temperatura de transición vítrea inferior o igual a 20°C, tal como se ha descrito anteriormente en b), o una temperatura de transición vítrea superior o igual a 40°C, tal como se ha descrito anteriormente en a). According to a second embodiment, the polymer used in the compositions according to the invention comprises at least one (especially one) first sequence having a glass transition temperature (Tg) between 20 and 40 ° C, according to the sequences described in c), and at least one (especially a) second sequence having a glass transition temperature less than or equal to 20 ° C, as described above in b), or a glass transition temperature greater than or equal to 40 ° C, as described above in a).

Preferentemente, la proporción de la primera secuencia que tiene una Tg comprendida entre 20 y 40°C va del 10 al 85% en peso del polímero, mejor del 30 al 80% y aún mejor del 50 al 70%. Preferably, the proportion of the first sequence having a Tg between 20 and 40 ° C ranges from 10 to 85% by weight of the polymer, better from 30 to 80% and even better from 50 to 70%.

Cuando la segunda secuencia es una secuencia que tiene una Tg superior o igual a 40°C, está preferentemente presente en una proporción del 10 al 85% en peso del polímero, mejor del 20 al 70% y aún mejor del 30 al 70%. When the second sequence is a sequence that has a Tg greater than or equal to 40 ° C, it is preferably present in a proportion of 10 to 85% by weight of the polymer, better than 20 to 70% and even better 30 to 70%.

Cuando la segunda secuencia es una secuencia que tiene una Tg inferior o igual a 20°C, está preferentemente presente en una proporción del 10 al 85% en peso del polímero, mejor del 20 al 70% y aún mejor del 20 al 50%. When the second sequence is a sequence having a Tg of less than or equal to 20 ° C, it is preferably present in a proportion of 10 to 85% by weight of the polymer, better than 20 to 70% and even better of 20 to 50%.

Preferentemente, la primera secuencia que tiene una Tg comprendida entre 20 y 40°C es un copolímero procedente de monómeros tales que el correspondiente homopolímero tiene una Tg superior o igual a 40°C y de monómeros tales que el correspondiente homopolímero tiene una Tg inferior o igual a 20°C..Ventajosamente, la segunda secuencia que tiene una Tg inferior o igual a 20°C o que tiene una Tg superior o igual a 40°C es un homopolímero. Preferably, the first sequence having a Tg between 20 and 40 ° C is a copolymer from monomers such that the corresponding homopolymer has a Tg greater than or equal to 40 ° C and of monomers such that the corresponding homopolymer has a Tg less than or equal to 20 ° C. Advantageously, the second sequence that has a Tg less than or equal to 20 ° C or that has a Tg greater than or equal to 40 ° C is a homopolymer.

Así, según una primera variante de este segundo modo de realización, el polímero utilizado en las composiciones según la invención puede comprender: Thus, according to a first variant of this second embodiment, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg comprendida entre 20 y 40°C, por ejemplo con una Tg de 25 a 39°C, que es un copolímero que incluye al menos un monómero de acrilato de metilo, al menos un monómero de metacrilato de metilo y al menos un monómero de ácido acrílico,  a first sequence of Tg comprised between 20 and 40 ° C, for example with a Tg of 25 to 39 ° C, which is a copolymer that includes at least one methyl acrylate monomer, at least one methyl methacrylate monomer and at minus an acrylic acid monomer,

--
una segunda secuencia de Tg superior o igual a 40°C, por ejemplo de 85 a 125°C, que es un homopolímero compuesto por monómeros de metacrilato de metilo, y  a second sequence of Tg greater than or equal to 40 ° C, for example from 85 to 125 ° C, which is a homopolymer composed of methyl methacrylate monomers, and

--
una secuencia intermedia que incluye al menos un monómero de acrilato de metilo, metacrilato de metilo, y  an intermediate sequence that includes at least one methyl acrylate monomer, methyl methacrylate, and

--
una secuencia intermedia que incluye metacrilato de metilo, al menos un monómero de ácido acrílico y al menos un monómero de acrilato de metilo.  an intermediate sequence that includes methyl methacrylate, at least one acrylic acid monomer and at least one methyl acrylate monomer.

Según una segunda variante de este segundo modo de realización, el polímero utilizado en las composiciones según la invención puede comprender: According to a second variant of this second embodiment, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg comprendida entre 20 y 40°C, por ejemplo con una Tg de 21 a 39°C, que es un copolímero que incluye acrilato de isobornilo/metacrilato de isobutilo/acrilato de 2-etilhexilo,  a first sequence of Tg comprised between 20 and 40 ° C, for example with a Tg of 21 to 39 ° C, which is a copolymer that includes isobutyl acrylate / isobutyl methacrylate / 2-ethylhexyl acrylate,

--
una segunda secuencia de Tg inferior o igual a 20°C, por ejemplo de -65 a -35°C, que es un homopolímero de metacrilato de metilo, y  a second sequence of Tg less than or equal to 20 ° C, for example from -65 to -35 ° C, which is a homopolymer of methyl methacrylate, and

--
una secuencia intermedia, que es un copolímero estadístico de acrilato de isobornilo/metacrilato de isobutilo/acrilato de 2-etilhexilo.  an intermediate sequence, which is a statistical copolymer of isobornyl acrylate / isobutyl methacrylate / 2-ethylhexyl acrylate.

Según una tercera variante de este segundo modo de realización, el polímero utilizado en las composiciones según la invención puede comprender: According to a third variant of this second embodiment, the polymer used in the compositions according to the invention may comprise:

--
una primera secuencia de Tg comprendida entre 20 y 40°C, por ejemplo con una Tg de 21 a 39°C, que es un copolímero de acrilato de isobornilo/acrilato de metilo/ácido acrílico,  a first sequence of Tg comprised between 20 and 40 ° C, for example with a Tg of 21 to 39 ° C, which is a copolymer of isobornyl acrylate / methyl acrylate / acrylic acid,

--
una segunda secuencia de Tg superior o igual a 40°C, por ejemplo de 85 a 115°C, que es un homopolímero de acrilato de isobornilo, y  a second sequence of Tg greater than or equal to 40 ° C, for example 85 to 115 ° C, which is an homopolymer of isobornyl acrylate, and

--
una secuencia intermedia, que es un copolímero estadístico de acrilato de isobornilo/acrilato de metilo/ácido acrílico.  an intermediate sequence, which is a statistical copolymer of isobornyl acrylate / methyl acrylate / acrylic acid.

El polímero secuenciado puede estar presente en la composición según la invención en un contenido del 0,1% al 60% en peso con respecto al peso total de la composición, preferentemente del 0,5% al 50% en peso y preferentemente aún del 1% al 40% en peso. The sequenced polymer may be present in the composition according to the invention in a content of 0.1% to 60% by weight with respect to the total weight of the composition, preferably 0.5% to 50% by weight and preferably even 1 % to 40% by weight.

Según un modo de realización particularmente preferido, el medio líquido orgánico de la composición contiene al menos un líquido orgánico, que es el solvente, o uno de los solventes, orgánico(s) de polimerización del polímero secuenciado tal como se ha descrito anteriormente. Ventajosamente, dicho solvente orgánico de polimerización es el líquido orgánico mayoritario en peso presente en el medio líquido orgánico de la composición cosmética. According to a particularly preferred embodiment, the organic liquid medium of the composition contains at least one organic liquid, which is the solvent, or one of the solvents, organic polymerization polymer (s) of the sequenced polymer as described above. Advantageously, said organic polymerization solvent is the majority organic liquid by weight present in the organic liquid medium of the cosmetic composition.

La composición cosmética según la invención incluye un medio cosméticamente aceptable, es decir, un medio compatible con las materias queratínicas, como la piel, los labios, el cabello, las pestañas, las cejas y las uñas. The cosmetic composition according to the invention includes a cosmetically acceptable medium, that is, a medium compatible with keratinous materials, such as skin, lips, hair, eyelashes, eyebrows and nails.

La composición según la invención puede incluir al menos un aceite volátil. The composition according to the invention may include at least one volatile oil.

Por "aceite", se entiende todo medio no acuoso líquido a temperatura ambiente (25°C) y presión atmosférica (760 mm de Hg), compatible con una aplicación sobre la piel, las mucosas (labios) y/o las faneras (uñas, pestañas, cejas, cabello). The term "oil" means any non-aqueous liquid medium at room temperature (25 ° C) and atmospheric pressure (760 mm Hg), compatible with an application on the skin, mucous membranes (lips) and / or pimples (nails , eyelashes, eyebrows, hair).

Por aceite volátil, se entiende todo medio no acuoso susceptible de evaporarse de la piel o de los labios en menos de una hora, que tiene especialmente una presión de vapor, a temperatura ambiente y presión atmosférica, de 10-3 a 300 mm de Hg (de 0,13 Pa a 40.000 Pa). By volatile oil, means any non-aqueous medium capable of evaporating from the skin or lips in less than an hour, which especially has a vapor pressure, at room temperature and atmospheric pressure, of 10-3 to 300 mm Hg (from 0.13 Pa to 40,000 Pa).

Según la invención, se pueden utilizar uno o más aceites volátiles. According to the invention, one or more volatile oils can be used.

Estos aceites pueden ser aceites hidrocarbonados o aceites siliconados que lleven eventualmente grupos alquilo o alcoxi pendientes o en el extremo de la cadena siliconada. These oils can be hydrocarbon oils or siliconized oils that eventually carry pendant alkyl or alkoxy groups or at the end of the siliconized chain.

Por aceite hidrocarbonado, se entiende un aceite formado esencialmente, incluso constituido, por átomos de carbono y de hidrógeno y eventualmente por átomos de oxígeno o de nitrógeno y que no contiene átomos de silicio By hydrocarbon oil, is meant an oil formed essentially, even constituted, by carbon and hydrogen atoms and eventually by oxygen or nitrogen atoms and which does not contain silicon atoms

o de flúor. Puede contener grupos alcohol, éster, éter, ácido carboxílico, amina y/o amida. or fluorine It may contain alcohol, ester, ether, carboxylic acid, amine and / or amide groups.

Como aceite de silicona volátil utilizable en la invención, se pueden citar las siliconas lineales o cíclicas que tienen de 2 a 7 átomos de silicio, llevando estas siliconas eventualmente grupos alquilo o alcoxi de 1 a 10 átomos de carbono. Como aceite de silicona volátil utilizable en la invención, se pueden citar especialmente el octametilciclotetrasiloxano, el decametilciclopentasiloxano, el dodecametilciclohexasiloxano, el heptametilhexiltrisiloxano, el heptametiloctiltrisiloxano, el octametiltrisiloxano, el decametiltetrasiloxano y sus mezclas. As volatile silicone oil usable in the invention, there may be mentioned linear or cyclic silicones having 2 to 7 silicon atoms, these silicones eventually carrying alkyl or alkoxy groups having 1 to 10 carbon atoms. As the volatile silicone oil usable in the invention, there may be mentioned especially octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, dodecamethylcyclohexasiloxane, heptamethylhexyltrisiloxane, heptamethyloctyltrisiloxane, octamethyltrisiloxane, decamethyltetraxyl, decamethyltetraxyl, decamethyltetraxyl, decamethyltriaxyl, decamethyltriaxyl, decamethyltriane, decamethylxyl

Como otro aceite volátil utilizable en la invención, se prefieren especialmente las isoparafinas C8-C16, como el isododecano, el isodecano y el isohexadecano, y por ejemplo los aceites vendidos bajo las denominaciones comerciales de ISOPAR o de PERMETHYL, y especialmente el isododecano (PERMETHYL 99 A). As another volatile oil usable in the invention, C8-C16 isoparaffins, such as isododecane, isodecane and isohexadecane, and for example oils sold under the trade names of ISOPAR or PERMETHYL, and especially isododecane (PERMETHYL) are especially preferred. 99 A).

El aceite volátil puede estar presente en la composición según la invención en un contenido del 1% al 70% en peso con respecto al peso total de la composición, preferentemente del 5% al 50% en peso y preferiblemente del 10% al 35% en peso. The volatile oil may be present in the composition according to the invention in a content of 1% to 70% by weight with respect to the total weight of the composition, preferably from 5% to 50% by weight and preferably from 10% to 35% by weight. weight.

La composición según la invención puede incluir un aceite no volátil. The composition according to the invention may include a non-volatile oil.

Se entiende por aceite no volátil un aceite susceptible de permanecer sobre la piel a temperatura ambiente (25°C) y presión atmosférica al menos una hora y que tiene especialmente una presión de vapor a temperatura ambiente (25°C) y presión atmosférica, no nula, inferior a 0,01 mm de Hg (1,33 Pa). Non-volatile oil is understood as an oil that can remain on the skin at room temperature (25 ° C) and atmospheric pressure for at least one hour and that especially has a vapor pressure at room temperature (25 ° C) and atmospheric pressure, not zero, less than 0.01 mm Hg (1.33 Pa).

El aceite no volátil puede ser seleccionado entre los aceites no volátiles siliconados o hidrocarbonados. Nonvolatile oil can be selected from silicone or hydrocarbon nonvolatile oils.

El aceite no volátil puede ser seleccionado entre los aceites no volátiles polares o apolares, los aceites no volátiles polares y sus mezclas. Nonvolatile oil can be selected from polar or nonpolar nonvolatile oils, polar nonvolatile oils and mixtures thereof.

El aceite no volátil puede estar presente en la composición según la invención en un contenido del 1% al 80% en peso con respecto al peso total de la composición, preferentemente del 5% al 60% en peso y preferiblemente del 10% al 50% en peso, especialmente del 20% al 50% en peso. The non-volatile oil may be present in the composition according to the invention in a content of 1% to 80% by weight with respect to the total weight of the composition, preferably 5% to 60% by weight and preferably 10% to 50% by weight, especially from 20% to 50% by weight.

Como aceite no volátil utilizable en la invención, se pueden citar: As non-volatile oil usable in the invention, there may be mentioned:

--
los aceites no volátiles hidrocarbonados, tales como el aceite de parafina (o vaselina), el escualano, el poliisobutileno hidrogenado (aceite de Parleam), el perhidroescualeno, el aceite de visón, de tortuga o de soja, o el aceite de almendra dulce, de calofilo, de palma, de pepitas de uva, de sésamo, de maíz, de arará, de colza, de girasol, de algodón, de albaricoque, de ricino, de aguacate, de jojoba, de oliva o de gérmenes de cereales; ésteres de ácido lanólico, de ácido oleico, de ácido láurico o de ácido esteárico; los ésteres grasos, especialmente C12-C36, tales como el miristato de isopropilo, el palmitato de isopropilo, el estearato de butilo, el laurato de hexilo, el adipato de diisopropilo, el isononanoato de isononilo, el palmitato de 2-etilhexilo, el laurato de 2-hexildecilo, el palmitato de 2-octildecilo, el miristato o el lactato de 2-octildodecilo, el succinato de di(2-etilhexilo), el malato de diisoestearilo o el triisoestearato de glicerina o de diglicerina; los ácidos grasos superiores, especialmente C14-C22, tales como el ácido mirístico, el ácido palmítico, el ácido esteárico, el ácido behénico, el ácido oleico, el ácido linoleico, el ácido linolénico o el ácido isoesteárico; los alcoholes grasos superiores, especialmente C16-C22, tales como el cetanol, el alcohol oleico, el alcohol linoleico o linolénico, el alcohol isoesteárico o el octildodecanol; y sus mezclas.  non-volatile hydrocarbon oils, such as paraffin oil (or petroleum jelly), squalane, hydrogenated polyisobutylene (Parleam oil), perhydrosqualene, mink, turtle or soybean oil, or sweet almond oil, of calofilo, of palm, of seeds of grape, of sesame, of corn, of plow, of rapeseed, of sunflower, of cotton, of apricot, of castor, of avocado, of jojoba, of olive or of germs of cereals; esters of lanolic acid, oleic acid, lauric acid or stearic acid; fatty esters, especially C12-C36, such as isopropyl myristate, isopropyl palmitate, butyl stearate, hexyl laurate, diisopropyl adipate, isononyl isononanoate, 2-ethylhexyl palmitate, laurate 2-hexyldecyl, 2-octildecyl palmitate, myristate or 2-octyldodecyl lactate, di (2-ethylhexyl) succinate, diisoestearyl malate or glycerin or diglycerin triisoestearate; higher fatty acids, especially C14-C22, such as myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid, linoleic acid, linolenic acid or isostearic acid; higher fatty alcohols, especially C16-C22, such as cetanol, oleic alcohol, linoleic or linolenic alcohol, isostearic alcohol or octyldodecanol; and their mixtures.

--
los aceites siliconados no volátiles, tales como los polidimetilsiloxanos (PDMS) no volátiles; los polidimetilsiloxanos que llevan grupos alquilo, alcoxi o fenilo pendientes o en el extremo de la cadena siliconada, grupos de 2 a 24 átomos de carbono; las siliconas feniladas, como las feniltrimeticonas, las fenildimeticonas, los feniltrimetilsiloxidifenilsiloxanos, las difenildimeticonas o los difenilmetildifeniltrisiloxanos; los polisiloxanos modificados por ácidos grasos (especialmente C8-C20), alcoholes grasos (especialmente C8-C20) o polioxialquilenos (especialmente polioxietileno y/o polioxipropileno); las  nonvolatile silicone oils, such as nonvolatile polydimethylsiloxanes (PDMS); polydimethylsiloxanes bearing alkyl, alkoxy or phenyl groups pending or at the end of the siliconized chain, groups of 2 to 24 carbon atoms; phenylated silicones, such as phenyltrimethicones, phenyldimethicones, phenyltrimethylsiloxydiphenylsiloxanes, diphenyldimethicones or diphenylmethyldiphenyltrisiloxanes; polysiloxanes modified by fatty acids (especially C8-C20), fatty alcohols (especially C8-C20) or polyoxyalkylenes (especially polyoxyethylene and / or polyoxypropylene); the

siliconas aminadas; las siliconas con grupos hidroxilo; las siliconas fluoradas que llevan un grupo fluorado pendiente o en el extremo de la cadena siliconada de 1 a 12 átomos de carbono, donde todos o parte de los hidrógenos están substituidos por átomos de flúor; y sus mezclas aminated silicones; silicones with hydroxyl groups; fluorinated silicones bearing a pendant fluorinated group or at the end of the siliconized chain of 1 to 12 carbon atoms, where all or part of the hydrogens are substituted by fluorine atoms; and its mixtures

La composición según la invención puede incluir igualmente al menos un cuerpo graso sólido a temperatura ambiente, especialmente seleccionado entre las ceras, los cuerpos grasos pastosos, las gomas y sus mezclas. Estos cuerpos grasos pueden ser de origen animal, vegetal, mineral o sintético. The composition according to the invention may also include at least one solid fatty body at room temperature, especially selected from waxes, pasty fatty bodies, gums and mixtures thereof. These fatty bodies can be of animal, plant, mineral or synthetic origin.

Por cera en el sentido de la presente invención, se entiende un compuesto lipofílico, sólido a temperatura ambiente (25°C), con cambio de estado sólido/líquido reversible, que tiene un punto de fusión superior o igual a 30°C y que puede ir hasta 120°C. El punto de fusión de la cera puede ser medido con un calorímetro de barrido diferencial (D.S.C.), por ejemplo el calorímetro vendido bajo la denominación DSC 30 por la sociedad METLER. Wax within the meaning of the present invention means a lipophilic compound, solid at room temperature (25 ° C), with reversible solid / liquid state change, which has a melting point greater than or equal to 30 ° C and which It can go up to 120 ° C. The melting point of the wax can be measured with a differential scanning calorimeter (D.S.C.), for example the calorimeter sold under the designation DSC 30 by METLER.

Las ceras pueden ser hidrocarbonadas, fluoradas y/o siliconadas y ser de origen vegetal, mineral, animal y/o sintético. En particular, las ceras presentan una temperatura de fusión superior a 25°C y mejor superior a 45°C. Como cera utilizable en la composición de la invención, se pueden citar la cera de abejas, la cera de Carnauba o de Candelilla, la parafina, las ceras microcristalinas, la ceresina o la ozocerita, y las ceras sintéticas, como las ceras de polietileno o de Fischer Tropsch y las ceras de siliconas, como las alquil- o alcoxi-dimeticonas de 16 a 45 átomos de carbono. The waxes can be hydrocarbon, fluorinated and / or silicone and be of vegetable, mineral, animal and / or synthetic origin. In particular, the waxes have a melting temperature of greater than 25 ° C and better than 45 ° C. As wax usable in the composition of the invention, there may be mentioned beeswax, Carnauba or Candelilla wax, paraffin, microcrystalline waxes, ceresin or ozocerite, and synthetic waxes, such as polyethylene waxes or from Fischer Tropsch and silicone waxes, such as alkyl- or alkoxy-dimethicones of 16 to 45 carbon atoms.

Las gomas son generalmente polidimetilsiloxanos (PDMS) de alto peso molecular o gomas de celulosa o polisacáridos, y los cuerpos pastosos son generalmente compuestos hidrocarbonados, como las lanolinas y sus derivados, o también PDMS. The gums are generally high molecular weight polydimethylsiloxanes (PDMS) or cellulose gums or polysaccharides, and the pasty bodies are generally hydrocarbon compounds, such as lanolines and their derivatives, or also PDMS.

La naturaleza y la cantidad de los cuerpos sólidos son función de las propiedades mecánicas y de las texturas buscadas. A título indicativo, la composición puede contener de un 0,1 a un 50% en peso de ceras con respecto al peso total de la composición, y mejor de un 1 a un 30% en peso. The nature and quantity of solid bodies are a function of the mechanical properties and the desired textures. By way of indication, the composition may contain from 0.1 to 50% by weight of waxes with respect to the total weight of the composition, and better from 1 to 30% by weight.

La composición puede así incluir agua o una mezcla de agua y de solvente(s) orgánico(s) hidrofílico(s), como los alcoholes y especialmente los monoalcoholes inferiores lineales o ramificados de 2 a 5 átomos de carbono, como el etanol, el isopropanol o el n-propanol, y los polioles, como la glicerina, la diglicerina, el propilenglicol, el sorbitol, el pentilenglicol y los polietilenglicoles, o también éteres C2 y aldehídos C2-C4 hidrofílicos. The composition may thus include water or a mixture of water and hydrophilic organic solvent (s), such as alcohols and especially linear or branched lower monoalcohols of 2 to 5 carbon atoms, such as ethanol, isopropanol or n-propanol, and polyols, such as glycerin, diglycerin, propylene glycol, sorbitol, pentylene glycol and polyethylene glycols, or also C2 ethers and hydrophilic C2-C4 aldehydes.

El agua o la mezcla de agua y de solventes orgánicos hidrofílicos pueden estar presentes en la composición según la invención en un contenido del 0,1% al 99% en peso con respecto al peso total de la composición, y preferentemente del 10% al 80% en peso. The water or the mixture of water and hydrophilic organic solvents may be present in the composition according to the invention in a content of 0.1% to 99% by weight with respect to the total weight of the composition, and preferably 10% to 80 % in weigh.

La composición puede incluir, aparte del polímero secuenciado antes descrito según la invención, un polímero adicional, tal como un polímero filmógeno. Según la presente invención, se entiende por "polímero filmógeno" un polímero apto para formar, por sí solo o en presencia de un agente auxiliar de formación de película, una película continua y adherente sobre un soporte, especialmente sobre las materias queratínicas. The composition may include, apart from the sequenced polymer described above according to the invention, an additional polymer, such as a film forming polymer. According to the present invention, "film-forming polymer" is understood as a polymer capable of forming, on its own or in the presence of an auxiliary film-forming agent, a continuous and adherent film on a support, especially on keratin materials.

Entre los polímeros filmógenos utilizables en la composición de la presente invención, se pueden citar los polímeros sintéticos, de tipo radicales o de tipo policondensado, los polímeros de origen natural y sus mezclas. Como polímero filmógeno, se pueden citar, en particular, los polímeros acrílicos, los poliuretanos, los poliésteres, las poliamidas, las poliureas y los polímeros celulósicos, como la nitrocelulosa. Among the film-forming polymers usable in the composition of the present invention, there may be mentioned synthetic polymers, of the radical or polycondensate type, naturally occurring polymers and mixtures thereof. As the film-forming polymer, there may be mentioned, in particular, acrylic polymers, polyurethanes, polyesters, polyamides, polyureas and cellulosic polymers, such as nitrocellulose.

La composición según la invención puede además incluir una o más materias colorantes seleccionadas entre los colorantes hidrosolubles y las materias colorantes pulverulentas, como los pigmentos, los nácares y las lentejuelas bien conocidas por el experto en la técnica. Las materias colorantes pueden estar presentes en la composición en un contenido del 0,01% al 50% en peso con respecto al peso de la composición, preferentemente del 0,01% al 30% en peso. The composition according to the invention may also include one or more dye materials selected from water-soluble dyes and powdery dyes, such as pigments, mother of pearl and sequins well known to those skilled in the art. The coloring materials may be present in the composition in a content of 0.01% to 50% by weight with respect to the weight of the composition, preferably 0.01% to 30% by weight.

Por pigmentos, hay que entender partículas de cualquier forma, blancas o de color, minerales u orgánicas, insolubles en el medio fisiológico, destinadas a dar color a la composición. By pigments, we must understand particles of any shape, white or colored, mineral or organic, insoluble in the physiological environment, intended to give color to the composition.

Por nácares, hay que entender partículas de cualquier forma irisadas, especialmente producidas por ciertos moluscos en su concha o bien sintetizadas. By mother of pearl, we must understand iridescent particles of any form, especially produced by certain mollusks in their shell or synthesized.

Los pigmentos pueden ser blancos o de color, minerales y/u orgánicos. Se pueden citar, entre los pigmentos minerales, el dióxido de titanio, eventualmente tratado en superficie, los óxidos de zirconio o de cerio, así como los óxidos de zinc, de hierro (negro, amarillo o rojo) o de cromo, el violeta de manganeso, el azul ultramar, el hidrato cromo y el azul férrico, y los polvos metálicos como el polvo de aluminio o el polvo de cobre. The pigments can be white or colored, mineral and / or organic. It is possible to mention, among the mineral pigments, titanium dioxide, possibly surface treated, zirconium or cerium oxides, as well as zinc, iron (black, yellow or red) or chromium oxides, the violet of manganese, ultramarine blue, chromium hydrate and ferric blue, and metal powders such as aluminum powder or copper powder.

Entre los pigmentos orgánicos, se pueden citar el negro de carbón, los pigmentos de tipo D & C y las lacas a base de carmín de cochinilla o de bario, estroncio, calcio o aluminio. Among the organic pigments, carbon black, D&C type pigments and cochineal or barium carmine, strontium, calcium or aluminum lacquers can be mentioned.

Se pueden citar también los pigmentos con efecto, tales como las partículas que llevan un substrato orgánico o mineral, natural o sintético, por ejemplo el vidrio, las resinas acrílicas, el poliéster, el poliuretano, el tereftalato de polietileno, las cerámicas o las alúminas, estando dicho substrato recubierto o no de substancias metálicas, como el aluminio, el oro, la plata, el platino, el cobre o el bronce, o de óxidos metálicos, como el dióxido de titanio, el óxido de hierro o el óxido de cromo, y sus mezclas. It is also possible to mention the pigments with effect, such as particles that carry an organic or mineral substrate, natural or synthetic, for example glass, acrylic resins, polyester, polyurethane, polyethylene terephthalate, ceramics or aluminas said substrate being covered or not with metal substances, such as aluminum, gold, silver, platinum, copper or bronze, or metal oxides, such as titanium dioxide, iron oxide or chromium oxide , and their mixtures.

Los pigmentos nacarados pueden ser seleccionados entre los pigmentos nacarados blancos, tales como la mica recubierta de titanio o de oxicloruro de bismuto, y los pigmentos nacarados de color, tales como la mica titanio recubierta con óxidos de hierro, la mica titanio recubierta especialmente con azul férrico u óxido de cromo y la mica titanio recubierta con un pigmento orgánico del tipo antes citado, así como los pigmentos nacarados a base de oxicloruro de bismuto.. Se pueden utilizar igualmente los pigmentos interferenciales, especialmente de cristales líquidos o multicapas. Pearlescent pigments can be selected from white pearly pigments, such as titanium coated mica or bismuth oxychloride, and pearly colored pigments, such as titanium mica coated with iron oxides, titanium mica specially coated with blue ferric or chromium oxide and titanium mica coated with an organic pigment of the aforementioned type, as well as pearly pigments based on bismuth oxychloride. Interferential pigments, especially liquid or multilayer crystals, can also be used.

Los colorante hidrosolubles son, por ejemplo, el jugo de remolacha o el azul de metileno. Water-soluble dyes are, for example, beet juice or methylene blue.

La composición según la invención puede incluir al menos una carga, especialmente en un contenido del 0,01% al 50% en peso con respecto al peso total de la composición, preferentemente del 0,01% al 30% en peso. Por cargas, hay que entender partículas de cualquier forma, incoloras o blancas, minerales o de síntesis, insolubles en el medio de la composición sea cual sea la temperatura a la que se fabrica la composición. Estas cargas sirven especialmente para modificar la reología o la textura de la composición. The composition according to the invention can include at least one load, especially in a content of 0.01% to 50% by weight with respect to the total weight of the composition, preferably from 0.01% to 30% by weight. By charges, particles of any form, colorless or white, mineral or synthetic, insoluble in the medium of the composition must be understood regardless of the temperature at which the composition is manufactured. These charges are especially useful for modifying the rheology or texture of the composition.

Las cargas pueden ser minerales u orgánicas de cualquier forma, plaquetarias, esféricas u oblongas, sea cual sea la forma cristalográfica (por ejemplo, laminar, cúbica, hexagonal, ortorrómbica, etc.). Se pueden citar el talco, la mica, la sílice, el caolín, los polvos de poliamida (Nylon®) (Orgasol®, de la casa Atochem), de poli--alanina y de polietileno, los polvos de polímeros de tetrafluoroetileno (Teflón®), la lauroillisina, el almidón, el nitruro de boro, las microesferas huecas poliméricas, tales como las de cloruro de polivinilideno/acrilonitrilo, como el Expancel® (Nobel Industrie), o de copolímeros de ácido acrílico (Polytrap®, de la sociedad Dow Corning), y las microperlas de resina de silicona (Tospearls® de Toshiba, por ejemplo), las partículas de poliorganosiloxanos elastoméricos, el carbonato de calcio precipitado, el carbonato y el hidrocarbonato de magnesio, el hidroxiapatito, las microesferas de sílice huecas (Silica Beads®, de Maprecos), las microcápsulas de vidrio o de cerámica y los jabones metálicos derivados de ácidos orgánicos carboxílicos de 8 a 22 átomos de carbono, preferentemente de 12 a 18 átomos de carbono, por ejemplo el estearato de zinc, de magnesio o de litio, el laurato de zinc o el miristato de magnesio. Loads can be mineral or organic in any form, platelet, spherical or oblong, whatever the crystallographic form (for example, laminar, cubic, hexagonal, orthorhombic, etc.). Talc, mica, silica, kaolin, polyamide powders (Nylon®) (Orgasol®, from the Atochem house), poly--alanine and polyethylene, tetrafluoroethylene polymer powders ( Teflon®), lauroillisin, starch, boron nitride, hollow polymer microspheres, such as polyvinylidene chloride / acrylonitrile chloride, such as Expancel® (Nobel Industrie), or acrylic acid copolymers (Polytrap®, de Dow Corning), and silicone resin microbeads (Toshiba Tospearls®, for example), elastomeric polyorganosiloxane particles, precipitated calcium carbonate, magnesium carbonate and hydrocarbonate, hydroxyapatite, silica microspheres hollow (Silica Beads®, from Maprecos), glass or ceramic microcapsules and metallic soaps derived from carboxylic organic acids of 8 to 22 carbon atoms, preferably 12 to 18 carbon atoms, for example zinc, magnesium or lithium tearate, zinc laurate or magnesium myristate.

La composición según la invención puede igualmente contener ingredientes habitualmente utilizados en cosmética, tales como las vitaminas, los espesantes, los oligoelementos, los suavizantes, los secuestrantes, los perfumes, los agentes alcalinizantes o acidificantes, los conservantes, los filtros solares, los tensioactivos, los antioxidantes o sus mezclas. The composition according to the invention may also contain ingredients commonly used in cosmetics, such as vitamins, thickeners, trace elements, softeners, sequestrants, perfumes, alkalizing or acidifying agents, preservatives, sunscreens, surfactants, Antioxidants or mixtures

Por supuesto, el experto en la técnica velará por seleccionar este o estos eventuales compuestos complementarios, y/o su cantidad, de tal forma que las propiedades ventajosas de la composición correspondiente según la invención no resulten alteradas, o no lo sean substancialmente, por la adición contemplada. Of course, the person skilled in the art will take care to select this or these possible complementary compounds, and / or their quantity, in such a way that the advantageous properties of the corresponding composition according to the invention are not altered, or are not substantially altered, by the contemplated addition.

La composición según la invención puede presentarse especialmente en forma de suspensión, de dispersión, de solución, de gel o de emulsión, especialmente de emulsión de aceite-en-agua (Ac/Ag) o de agua-en-aceite (Ag/Ac), The composition according to the invention can be presented in particular in the form of a suspension, dispersion, solution, gel or emulsion, especially of oil-in-water (Ac / Ag) or water-in-oil (Ag / Ac) emulsion ),

o en forma de crema, de barra o de pasta, especialmente de pasta flexible (especialmente de pasta con una viscosidad dinámica a 25°C del orden de 0,1 a 40 Pa.s bajo una velocidad de cizallamiento de 200 s-1 después de 10 minutos de medición en geometría cónico/plana). La composición puede ser anhidra; por ejemplo, puede tratarse de una pasta o de una barra anhidra. La composición puede ser una composición sin aclarado. or in the form of cream, stick or paste, especially of flexible paste (especially of pasta with a dynamic viscosity at 25 ° C of the order of 0.1 to 40 Pa.s under a shear rate of 200 s-1 after 10 minutes of measurement in conical / flat geometry). The composition can be anhydrous; for example, it can be a paste or an anhydrous bar. The composition can be a composition without rinsing.

El experto en la técnica podrá seleccionar la forma galénica apropiada, así como su método de preparación, en base a sus conocimientos generales, teniendo en cuenta, por una parte, la naturaleza de los constituyentes utilizados, especialmente su solubilidad en el soporte, y por otra la aplicación contemplada para la composición. The person skilled in the art may select the appropriate galenic form, as well as its method of preparation, based on their general knowledge, taking into account, on the one hand, the nature of the constituents used, especially their solubility in the support, and by another the application contemplated for the composition.

Según otro aspecto, la invención se relaciona igualmente con un conjunto cosmético que comprende: According to another aspect, the invention also relates to a cosmetic assembly comprising:

i) un recipiente que delimita al menos un compartimento, estando cerrado dicho recipiente por un elemento de cierre, y ii) una composición dispuesta en el interior de dicho compartimento, guardando conformidad la composición con una cualquiera de las reivindicaciones que se dan más adelante. i) a container that delimits at least one compartment, said container being closed by a closure element, and ii) a composition disposed inside said compartment, keeping the composition in accordance with any one of the claims given below.

El recipiente puede ser de cualquier forma adecuada. Puede estar especialmente en forma de frasco, de tubo, de estuche, de caja o de maletín. The container can be of any suitable form. It can be especially in the form of a bottle, tube, case, box or case.

El elemento de cierre puede estar en forma de un tapón amovible, de una tapadera o de una cápsula, especialmente del tipo que lleva un cuerpo fijado al recipiente y una gorra articulada sobre el cuerpo. Puede estar igualmente en forma de un elemento que asegure el cierre selectivo del recipiente, especialmente una tapa abatible. The closure element may be in the form of a removable cap, a lid or a capsule, especially of the type that carries a body fixed to the container and a cap articulated on the body. It can also be in the form of an element that ensures selective closure of the container, especially a flip lid.

El recipiente puede estar asociado a un aplicador. El aplicador puede estar en forma de un pincel, tal como se describe, por ejemplo, en la patente FR 2.722.380. El aplicador puede estar en forma de un bloque de espuma o de elastómero, de un rotulador o de una espátula. El aplicador puede ser libre (borla o esponja) o solidario a un vástago llevado por el elemento de cierre, tal como se describe, por ejemplo, en la patente EE.UU. 5.492.426. El aplicador puede ser solidario al recipiente, tal como describe, por ejemplo, la patente FR 2.761.959. The container may be associated with an applicator. The applicator may be in the form of a brush, as described, for example, in FR 2,722,380. The applicator may be in the form of a foam or elastomer block, a marker or a spatula. The applicator can be free (tassel or sponge) or integral with a rod carried by the closure element, as described, for example, in US Pat. 5,492,426. The applicator may be integral with the container, as described, for example, in patent FR 2,761,959.

El producto puede estar contenido directamente en el recipiente o indirectamente. A modo de ejemplo, el producto puede estar dispuesto sobre un soporte impregnado, especialmente en forma de una toallita o de un tampón, y dispuesto (en forma unitaria o como una pluralidad) en una caja o en un sobre. Tal soporte que incorpora el producto está descrito, por ejemplo, en la solicitud WO 01/03538. The product can be contained directly in the container or indirectly. By way of example, the product may be arranged on an impregnated support, especially in the form of a wipe or a buffer, and arranged (in unit form or as a plurality) in a box or in an envelope. Such support incorporating the product is described, for example, in the application WO 01/03538.

El elemento de cierre puede acoplarse al recipiente por atornillamiento. Alternativamente, el acoplamiento entre el elemento de cierre y el recipiente se realiza de un modo distinto al atornillamiento, especialmente por un mecanismo de bayoneta, por trinquete o presión o por atracción magnética. Por "trinquete", se entiende en particular cualquier sistema que implique el paso de un burlete o de un cordón de materia por deformación elástica de una porción, especialmente del elemento de cierre, y luego por retorno a la posición de no tensión elásticamente de dicha porción tras el paso del burlete o del cordón. The closure element can be attached to the container by screwing. Alternatively, the coupling between the closure element and the container is carried out in a manner other than screwing, especially by a bayonet mechanism, by ratchet or pressure or by magnetic attraction. By "ratchet", it is understood in particular any system that involves the passage of a weatherstrip or a cord of matter by elastic deformation of a portion, especially of the closure element, and then by return to the position of elastically non-tension of said portion portion after the passage of the weatherstrip or cord.

El recipiente puede estar al menos en parte realizado en material termoplástico. A modo de ejemplos de materiales termoplásticos, se pueden citar el polipropileno o el polietileno. The container may be at least partly made of thermoplastic material. As examples of thermoplastic materials, polypropylene or polyethylene can be mentioned.

Alternativamente, el recipiente está realizado en material no termoplástico, especialmente en vidrio o en metal (o aleación). Alternatively, the container is made of non-thermoplastic material, especially glass or metal (or alloy).

El recipiente puede ser de paredes rígidas o de paredes deformables, especialmente en forma de tubo o de frasco tubo. The container can be made of rigid walls or deformable walls, especially in the form of a tube or a tube bottle.

El recipiente puede incluir medios destinados a provocar o facilitar la distribución de la composición. A modo de ejemplo, el recipiente puede ser de paredes deformables para provocar la salida de la composición en respuesta a una sobrepresión en el interior del recipiente, cuya sobrepresión es provocada por aplastamiento elástico (o no elástico) de las paredes del recipiente. Alternativamente, especialmente cuando el producto está en forma de barra, esta última puede ser arrastrada por un mecanismo a pistón. Siempre en el caso de una barra, especialmente de producto de maquillaje (barra de labios, base de maquillaje, etc.), el recipiente puede llevar un mecanismo, especialmente de cremallera, o con un vástago roscado, o con una rampa helicoidal, apto para desplazar una barra en la dirección de dicha abertura. Tal mecanismo está descrito, por ejemplo, en la patente FR 2.806.273 o en la patente FR 2.775.566. Tal mecanismo para un producto líquido está descrito en la patente FR 2.727.609. The container may include means intended to cause or facilitate the distribution of the composition. By way of example, the container can be of deformable walls to cause the composition to exit in response to an overpressure inside the container, whose overpressure is caused by elastic (or non-elastic) crushing of the walls of the container. Alternatively, especially when the product is in the form of a bar, the latter can be dragged by a piston mechanism. Always in the case of a bar, especially make-up product (lipstick, make-up base, etc.), the container can carry a mechanism, especially with a zipper, or with a threaded rod, or with a helical ramp, suitable to move a bar in the direction of said opening. Such a mechanism is described, for example, in FR 2,806,273 or in FR 2,775,566. Such a mechanism for a liquid product is described in FR 2,727,609.

El recipiente puede estar constituido por un maletín con un fondo que delimita al menos un alojamiento que contiene la composición y una tapadera, especialmente articulada sobre el fondo y apta para recubrir al menos en parte dicho fondo. Tal maletín está descrito, por ejemplo, en la solicitud WO 03/018423 o en la patente FR 2.791.042. The container may consist of a briefcase with a bottom that delimits at least one housing containing the composition and a lid, especially articulated on the bottom and suitable for covering at least part of said bottom. Such a briefcase is described, for example, in the application WO 03/018423 or in the patent FR 2,791,042.

El recipiente puede estar equipado con un escurridor dispuesto en proximidad a la abertura del recipiente. Tal escurridor permite escurrir el aplicador y eventualmente el vástago del que puede ser solidario. Tal escurridor está descrito, por ejemplo, en la patente FR 2.792.618. The container may be equipped with a drainer arranged in proximity to the opening of the container. Such a drainer allows the applicator to drain and eventually the rod from which it can be integral. Such a drainer is described, for example, in FR 2,792,618.

La composición puede estar a la presión atmosférica en el interior del recipiente (a temperatura ambiente). The composition may be at atmospheric pressure inside the vessel (at room temperature).

El contenido de las patentes o solicitudes de patentes citadas anteriormente es incorporado como referencia en la presente solicitud. The content of the patents or patent applications cited above is incorporated by reference in the present application.

La invención es ilustrada con más detalles mediante los ejemplos descritos a continuación. The invention is illustrated in more detail by the examples described below.

Ejemplo 1: Example 1:

Preparación de un polímero de poli(acrilato de isobornilo/metacrilato de isobutilo/acrilato de 2-etilhexilo) Preparation of a poly (isobornyl acrylate / isobutyl methacrylate / 2-ethylhexyl acrylate) polymer

Se introducen 100 g de isododecano en un reactor de 1 litro y se aumenta luego la temperatura para pasar de la temperatura ambiente (25°C) a 90°C en 1 hora. 100 g of isododecane are introduced into a 1 liter reactor and the temperature is then increased to go from room temperature (25 ° C) to 90 ° C in 1 hour.

Se añaden entonces, a 90°C y en 1 hora, 120 g de acrilato de isobornilo, 90 g de metacrilato de isobutilo, 110 g de isododecano y 1,8 g de 2,5-bis(2-etilhexanoilperoxi)-2,5-dimetilhexano (Trigonox® 141 de Akzo Nobel). Then, at 90 ° C and in 1 hour, 120 g of isobornyl acrylate, 90 g of isobutyl methacrylate, 110 g of isododecane and 1.8 g of 2,5-bis (2-ethylhexanoylperoxy) -2 are added, 5-dimethylhexane (Trigonox® 141 from Akzo Nobel).

Se mantiene la mezcla 1 h 30 a 90°C. The mixture is maintained for 1 h 30 at 90 ° C.

Se introducen entonces en la mezcla anterior, siempre a 90°C y en 30 minutos, 90 g de acrilato de 2-etilhexilo, 90 g de isododecano y 1,2 g de 2,5-bis(2-etilhexanoilperoxi)-2,5-dimetilhexano. Then, 90 g of 2-ethylhexyl acrylate, 90 g of isododecane and 1.2 g of 2,5-bis (2-ethylhexanoylperoxy) -2 are introduced into the above mixture, always at 90 ° C and in 30 minutes, 5-dimethylhexane.

Se mantiene la mezcla durante 3 horas a 90°C y se enfría después el conjunto. The mixture is maintained for 3 hours at 90 ° C and then the whole is cooled.

Se obtiene una solución al 50% en materia activa de polímero en isododecano. A 50% solution in active matter of polymer in isododecane is obtained.

Se obtiene un polímero que comprende una primera secuencia o bloque de poli(acrilato de isobornilo/metacrilato de isobutilo) que tiene una Tg de 80°C, una segunda secuencia de poliacrilato de 2-etilhexilo que tiene una Tg de -70°C y una secuencia intermedia que es un polímero estadístico de acrilato de isobornilo/metacrilato de isobutilo/acrilato de 2-etilhexilo. A polymer is obtained comprising a first sequence or block of poly (isobornyl acrylate / isobutyl methacrylate) having a Tg of 80 ° C, a second sequence of 2-ethylhexyl polyacrylate having a Tg of -70 ° C and an intermediate sequence that is a statistical polymer of isobornyl acrylate / isobutyl methacrylate / 2-ethylhexyl acrylate.

Este polímero presenta una masa media ponderal de 77.000 y una masa media numérica de 19.000, o sea, un índice de polidispersidad I de 4,05. This polymer has a weight average mass of 77,000 and a numerical average mass of 19,000, that is, a polydispersity index I of 4.05.

Ejemplo 2: Example 2:

Preparación de un polímero de poli(acrilato de isobornilo/metacrilato de isobornilo/acrilato de 2-etilhexilo) Preparation of a poly (isobornyl acrylate / isobornyl methacrylate / 2-ethylhexyl acrylate) polymer

Se introducen 100 g de isododecano en un reactor de 1 litro y se aumenta luego la temperatura para pasar de la temperatura ambiente (25°C) a 90°C en 1 hora. Se añaden entonces, a 90°C y en 1 hora, 105 g de acrilato de isobornilo, 105 g de metacrilato de isobornilo, 110 g 100 g of isododecane are introduced into a 1 liter reactor and the temperature is then increased to go from room temperature (25 ° C) to 90 ° C in 1 hour. Then, at 90 ° C and within 1 hour, 105 g of isobornyl acrylate, 105 g of isobornyl methacrylate, 110 g are added

de isododecano y 1,8 g de 2,5-bis(2-etilhexanoilperoxi)-2,5-dimetilhexano (Trigonox® 141 de Akzo Nobel). Se mantiene la mezcla 1 h 30 a 90°C. Se introducen entonces en la mezcla anterior, siempre a 90°C y en 30 minutos, 90 g de acrilato de 2-etilhexilo, 90 g of isododecane and 1.8 g of 2,5-bis (2-ethylhexanoylperoxy) -2,5-dimethylhexane (Trigonox® 141 from Akzo Nobel). The mixture is maintained for 1 h 30 at 90 ° C. Then 90 g of 2-ethylhexyl acrylate, 90 g are introduced into the previous mixture, always at 90 ° C and in 30 minutes

de isododecano y 1,2 g de 2,5-bis(2-etilhexanoilperoxi)-2,5-dimetilhexano. Se mantiene la mezcla durante 3 horas a 90°C y se enfría después el conjunto. Se obtiene una solución al 50% en materia activa de polímero en isododecano. Se obtiene un polímero que comprende una primera secuencia o bloque de poli(acrilato de isobornilo/metacrilato de of isododecane and 1.2 g of 2,5-bis (2-ethylhexanoylperoxy) -2,5-dimethylhexane. The mixture is maintained for 3 hours at 90 ° C and then the whole is cooled. A 50% solution in active matter of polymer in isododecane is obtained. A polymer is obtained which comprises a first sequence or block of poly (isobornyl acrylate / methacrylate of

isobornilo) que tiene una Tg de 110°C, una segunda secuencia de poliacrilato de 2-etilhexilo que tiene una Tg de -70°C y una secuencia intermedia que es un polímero estadístico de acrilato de isobornilo/metacrilato de isobornilo/acrilato de 2-etilhexilo. isobornyl) having a Tg of 110 ° C, a second sequence of 2-ethylhexyl polyacrylate having a Tg of -70 ° C and an intermediate sequence that is a statistical polymer of isobornyl acrylate / isobornyl methacrylate / 2 acrylate -ethylhexyl.

Este polímero presenta una masa media ponderal de 103.900 y una masa media numérica de 21.300, o sea, un índice de polidispersidad I de 4,89. This polymer has a weight average mass of 103,900 and a numerical average mass of 21,300, that is, a polydispersity index I of 4.89.

Ejemplos 3 y 4: Examples 3 and 4:

Se preparó una barra de carmín de labios que tenía la composición siguiente: A lipstick lipstick was prepared having the following composition:

Polímero del ejemplo 1 ó 2 al 50% en peso en isododecano 65 g Octildodecanol 11,34 g Cera de polietileno (Performalene 500 polyethylene de New Phase Technologies) 13 g Mezcla de alcoholes grasos C30-C50 y de hidrocarburo C30-C50 (80/20) (Performacol 550 de New Phase Technologies) 2 g Pigmentos 8,66 g Polymer of Example 1 or 2 at 50% by weight in isododecane 65 g Octyldodecanol 11.34 g Polyethylene wax (Performalene 500 polyethylene from New Phase Technologies) 13 g Mixture of C30-C50 fatty alcohols and C30-C50 hydrocarbon (80/20) (Performacol 550 from New Phase Technologies) 2 g Pigments 8.66 g

Se realiza un triturado pigmentario de los pigmentos en el octildodecanol efectuando tres pases de la mezcla por la trituradora de tres cilindros. A pigmentary crushing of the pigments in the octyldodecanol is carried out by making three passes of the mixture through the three-cylinder crusher.

Se derrite la mezcla de ceras y de triturado pigmentario a 100°C bajo agitación Rayneri y se mantiene la agitación durante 40 minutos. Se baja entonces la temperatura de la mezcla a 80°C y se añade el polímero mezclado con el isododecano. Se deja bajo agitación durante 15 minutos, se vierte luego la mezcla en un molde calentado a 42°C y se enfría después en un congelador a -18°C durante 30 minutos. The mixture of waxes and pigment crushing is melted at 100 ° C under Rayneri stirring and stirring is maintained for 40 minutes. The temperature of the mixture is then lowered to 80 ° C and the polymer mixed with the isododecane is added. It is left under stirring for 15 minutes, then the mixture is poured into a mold heated to 42 ° C and then cooled in a freezer at -18 ° C for 30 minutes.

Se acondicionan las barras obtenidas en un artículo de acondicionamiento. La barra de labios permite obtener un maquillaje que presenta buenas propiedades de ausencia de transferencia y de persistencia. The bars obtained in a conditioning article are conditioned. The lipstick allows to obtain a makeup that has good transfer-free properties and of persistence

Se mide el índice de persistencia de la barra de labios obtenida según el protocolo de medición antes descrito. Las barras de labios de los ejemplos 3 y 4 forman respectivamente una película que tiene un índice de persistencia The persistence index of the lipstick obtained is measured according to the measurement protocol described above. The lipsticks of examples 3 and 4 respectively form a film having a persistence index

del 100%. 100%

Ejemplo 5: Example 5:

Se preparó una barra de carmín de labios que tenía la composición siguiente: A lipstick lipstick was prepared having the following composition:

Polímero del ejemplo 1 al 50% en peso en isododecano OctildodecanolCera de polietileno (Performalene 500 polyethylene de New Phase Technologies)Mezcla de alcoholes grasos C30-C50 y de hidrocarburo C30-C50 (80/20) (Performacol 550 de New Phase Technologies)PigmentosIsododecanoPolymer of Example 1 at 50% by weight in isododecane Octyldodecanol Polyethylene wax (Performalene 500 polyethylene from New Phase Technologies) Mixture of C30-C50 fatty alcohols and C30-C50 hydrocarbon (80/20) (Performacol 550 from New Phase Technologies) Pigments
50 g 11,34 g 13 g 2 g 8,66 g 15 g 50 g 11.34 g 13 g 2 g 8.66 g 15 g

Esta barra de labios forma una película que tiene un índice de persistencia igual al 98,6%, medido según el protocolo antes descrito. This lipstick forms a film that has a persistence index equal to 98.6%, measured according to the protocol described above.

Ejemplo 6: Example 6:

Se preparó una barra de carmín de labios que tenía la composición siguiente: A lipstick lipstick was prepared having the following composition:

Polímero del ejemplo 1 al 50% en peso en isododecano 30 g Octildodecanol 11,34 g Cera de polietileno (Performalene 500 polyethylene de New Phase Technologies) 15 g Mezcla de alcoholes grasos C30-C50 y de hidrocarburo C30-C50 (80/20) (Performacol 550 de New Phase Technologies) 2 g Pigmentos 8,66 g Isododecano 35 g Polymer of Example 1 at 50% by weight in isododecane 30 g Octyldodecanol 11.34 g Polyethylene wax (Performalene 500 polyethylene from New Phase Technologies) 15 g Mixture of C30-C50 fatty alcohols and C30-C50 hydrocarbon (80/20) (Performacol 550 from New Phase Technologies) 2 g Pigments 8.66 g Isododecane 35 g

Esta barra de labios forma una película que tiene un índice de persistencia igual al 98,6%, medido según el protocolo antes descrito. This lipstick forms a film that has a persistence index equal to 98.6%, measured according to the protocol described above.

Claims (62)

REIVINDICACIONES 1. Composición de maquillaje de los labios que incluye al menos un medio líquido orgánico cosméticamente aceptable y al menos un polímero etilénico secuenciado lineal filmógeno libre de estireno, cuyo polímero secuenciado contiene primera y segunda secuencias unidas entre sí por un segmento intermedio, que es un polímero estadístico que incluye al menos un monómero constitutivo de la primera secuencia y al menos un monómero constitutivo de la segunda secuencia, siendo seleccionada la primera secuencia del polímero entre: 1. Lip makeup composition that includes at least one cosmetic liquid organic medium acceptable and at least one styrene-free linear film-forming ethylene polymer, whose sequenced polymer contains first and second sequences linked together by an intermediate segment, which it is a statistical polymer that includes at least one constituent monomer of the first sequence and at least one constituent monomer of the second sequence, the first polymer sequence being selected from:
--
a) una secuencia que tiene una Tg superior o igual a 40°C,  a) a sequence that has a Tg greater than or equal to 40 ° C,
--
b) una secuencia que tiene una Tg inferior o igual a 20°C y  b) a sequence that has a Tg less than or equal to 20 ° C and
--
c) una secuencia que tiene una Tg comprendida entre 20 y 40°C, y  c) a sequence having a Tg between 20 and 40 ° C, and
siendo seleccionada la segunda secuencia en una categoría a), b) o c) diferente de la primera secuencia; y cuyo polímero secuenciado tiene un índice de polidispersidad I superior o igual a 2,8, siendo dicho polímero tal que, cuando está presente en cantidad suficiente en la composición, esta última es apta para formar un depósito que tiene un índice de persistencia superior o igual al 80%, determinado según el protocolo de medición descrito en la descripción. the second sequence being selected in a category a), b) or c) different from the first sequence; and whose sequenced polymer has a polydispersity index I greater than or equal to 2.8, said polymer being such that, when present in sufficient quantity in the composition, the latter is suitable to form a deposit that has a persistence index greater than or equal to 80%, determined according to the protocol of measurement described in the description.
2. Composición de maquillaje de los labios que incluye al menos un medio líquido orgánico cosméticamente aceptable y al menos un polímero etilénico secuenciado lineal filmógeno no elastomérico, cuyo polímero secuenciado contiene primera y segunda secuencias unidas entre sí por un segmento intermedio, que es un polímero estadístico que incluye al menos un monómero constitutivo de la primera secuencia y al menos un monómero constitutivo de la segunda secuencia, siendo seleccionada la primera secuencia del polímero entre: 2. Lip makeup composition that includes at least one cosmetic liquid organic medium acceptable and at least one non-elastomeric film-forming linear sequencing ethylene polymer, whose sequenced polymer contains first and second sequences linked together by an intermediate segment, which it is a statistical polymer that includes at least one constituent monomer of the first sequence and at least one constituent monomer of the second sequence, the first polymer sequence being selected from:
--
a) una secuencia que tiene una Tg superior o igual a 40°C,  a) a sequence that has a Tg greater than or equal to 40 ° C,
--
b) una secuencia que tiene una Tg inferior o igual a 20°C y  b) a sequence that has a Tg less than or equal to 20 ° C and
--
c) una secuencia que tiene una Tg comprendida entre 20 y 40°C, y  c) a sequence having a Tg between 20 and 40 ° C, and
siendo seleccionada la segunda secuencia en una categoría a), b) o c) diferente de la primera secuencia; y cuyo polímero secuenciado tiene un índice de polidispersidad I superior o igual a 2,8, siendo dicho polímero tal que, cuando está presente en cantidad suficiente en la composición, esta última es apta para formar un depósito que tiene un índice de permanencia superior o igual al 80%, determinado según el protocolo de medición descrito en la descripción. the second sequence being selected in a category a), b) or c) different from the first sequence; and whose sequenced polymer has a polydispersity index I greater than or equal to 2.8, said polymer being such that, when present in sufficient quantity in the composition, the latter is suitable to form a deposit that has a permanence index greater than or equal to 80%, determined according to the protocol of measurement described in the description.
3.3.
Composición según la reivindicación 1 ó 2, caracterizada por ser apta para formar un depósito con un índice de persistencia superior o igual al 85%, preferentemente inferior o igual al 90%, preferentemente superior o igual al 95%.  Composition according to claim 1 or 2, characterized in that it is capable of forming a deposit with a persistence index greater than or equal to 85%, preferably less than or equal to 90%, preferably greater than or equal to 95%.
4.Four.
Composición según una de las reivindicaciones precedentes, caracterizada por no ser soluble el polímero secuenciado a un contenido en materia activa de al menos el 1% en peso en agua o en una mezcla de agua y de monoalcoholes inferiores lineales o ramificados de 2 a 5 átomos de carbono, sin modificación de pH, a temperatura ambiente (25°C).  Composition according to one of the preceding claims, characterized in that the sequenced polymer is not soluble at an active matter content of at least 1% by weight in water or in a mixture of water and linear or branched lower monoalcohols of 2 to 5 atoms carbon, without pH modification, at room temperature (25 ° C).
5.5.
Composición según una de las reivindicaciones precedentes, caracterizada por tener la secuencia intermedia una temperatura de transición vítrea comprendida entre las temperaturas de transición vítrea de la primera y segunda secuencias.  Composition according to one of the preceding claims, characterized in that the intermediate sequence has a glass transition temperature comprised between the glass transition temperatures of the first and second sequences.
6.6.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por ser la primera y segunda secuencias de dicho polímero secuenciado incompatibles entre sí.  Composition according to any one of the preceding claims, characterized in that the first and second sequences of said sequenced polymer are incompatible with each other.
7.7.
Composición según una de las reivindicaciones precedentes, caracterizada por tener el polímero secuenciado un índice de polidispersidad comprendido entre 2,8 y 6.  Composition according to one of the preceding claims, characterized in that the sequenced polymer has a polydispersity index between 2.8 and 6.
8.8.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por comprender el polímero secuenciado al menos una primera secuencia con una temperatura de transición vítrea (Tg) superior o igual a 40°C y al menos una segunda secuencia con una temperatura de transición vítrea inferior o igual a 20°C.  Composition according to any one of the preceding claims, characterized by comprising the polymer sequenced at least a first sequence with a glass transition temperature (Tg) greater than or equal to 40 ° C and at least a second sequence with a glass transition temperature lower or equal to 20 ° C.
9.9.
Composición según la reivindicación precedente, caracterizada por ir la proporción de la primera secuencia del 20 al 90% en peso del polímero, mejor del 30 al 80% y aún mejor del 50 al 70%.  Composition according to the preceding claim, characterized in that the proportion of the first sequence ranges from 20 to 90% by weight of the polymer, better from 30 to 80% and even better from 50 to 70%.
10.10.
Composición según la reivindicación 8 ó 9, caracterizada por ir la proporción de la segunda secuencia que tiene una Tg inferior o igual a 20°C del 5 al 75% en peso del polímero, mejor del 15 al 50% y aún mejor del 25 al 45%.  Composition according to claim 8 or 9, characterized in that the proportion of the second sequence having a Tg of less than or equal to 20 ° C is from 5 to 75% by weight of the polymer, better from 15 to 50% and even better from 25 to Four. Five%.
11.eleven.
Composición según una de las reivindicaciones 1 a 7, caracterizada por comprender el polímero secuenciado al menos una primera secuencia con una temperatura de transición vítrea (Tg) comprendida entre 20 y 40°C y al menos una segunda secuencia con una temperatura de transición vítrea inferior o igual a 20°C o una temperatura de transición vítrea superior o igual a 40°C.  Composition according to one of claims 1 to 7, characterized in that the polymer comprises at least one first sequence with a glass transition temperature (Tg) between 20 and 40 ° C and at least a second sequence with a lower glass transition temperature or equal to 20 ° C or a glass transition temperature greater than or equal to 40 ° C.
5 5
12.12.
Composición según la reivindicación precedente, caracterizada por ir la proporción de la primera secuencia que tiene una Tg comprendida entre 20 y 40°C del 10 al 85% en peso del polímero, mejor del 30 al 80% y aún mejor del 50 al 70%.  Composition according to the preceding claim, characterized in that the proportion of the first sequence having a Tg between 20 and 40 ° C of 10 to 85% by weight of the polymer, better from 30 to 80% and even better from 50 to 70% .
13.13.
Composición según la reivindicación 11 ó 12, caracterizada por tener la segunda secuencia una Tg superior o igual a 40°C.  Composition according to claim 11 or 12, characterized in that the second sequence has a Tg greater than or equal to 40 ° C.
14. 14.
Composición según una cualquiera de las reivindicaciones 11 a 13, caracterizada por ir la proporción de la Composition according to any one of claims 11 to 13, characterized in that the proportion of the
segunda secuencia que tiene una Tg superior o igual a 40°C del 10 al 85%, preferentemente del 20 al 70% y mejor 15 del 30 al 70% en peso del polímero. second sequence having a Tg greater than or equal to 40 ° C from 10 to 85%, preferably from 20 to 70% and better from 30 to 70% by weight of the polymer.
15.fifteen.
Composición según la reivindicación 11 ó 12, caracterizada por tener la segunda secuencia una Tg inferior o igual a 20°C.  Composition according to claim 11 or 12, characterized in that the second sequence has a Tg less than or equal to 20 ° C.
16.16.
Composición según una de las reivindicaciones 7 a 9 y 14 ó 15, caracterizada por ir la proporción de la secuencia que tiene una temperatura de transición vítrea inferior o igual a 20°C del 20 al 90% en peso del polímero, mejor del 30 al 80% y aún mejor del 50 al 70%.  Composition according to one of claims 7 to 9 and 14 or 15, characterized in that the proportion of the sequence having a glass transition temperature of 20 to 90% by weight of the polymer is better, from 30 to 30 80% and even better from 50 to 70%.
17.17.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por proceder la  Composition according to any one of the preceding claims, characterized in that the
25 secuencia que tiene una Tg superior o igual a 40°C en todo o en parte de uno o más monómeros cuyo homopolímero tiene una temperatura de transición vítrea superior o igual a 40°C, especialmente una Tg de 40 a 150°C, preferentemente superior o igual a 50°C, especialmente de 50°C a 120°C y preferiblemente superior o igual a 60°C, especialmente de 60°C a 120°C. A sequence having a Tg greater than or equal to 40 ° C in all or part of one or more monomers whose homopolymer has a glass transition temperature greater than or equal to 40 ° C, especially a Tg of 40 to 150 ° C, preferably greater than or equal to 50 ° C, especially 50 ° C to 120 ° C and preferably greater than or equal to 60 ° C, especially 60 ° C to 120 ° C.
18. Composición según la reivindicación precedente, caracterizada por ser la secuencia que tiene una Tg superior 18. Composition according to the preceding claim, characterized in that it is the sequence having a higher Tg o igual a 40°C un copolímero procedente de monómeros cuyo homopolímero tiene una temperatura de transición vítrea superior o igual a 40°C. or equal to 40 ° C a copolymer from monomers whose homopolymer has a glass transition temperature greater than or equal to 40 ° C. 19. Composición según una de las reivindicaciones 17 ó 18, caracterizada por seleccionar los monómeros cuyo 35 homopolímero tiene una temperatura de transición vítrea superior o igual a 40°C entre los monómeros siguientes: 19. Composition according to one of claims 17 or 18, characterized by selecting the monomers whose homopolymer has a glass transition temperature greater than or equal to 40 ° C between the following monomers:
--
los metacrilatos de fórmula CH2=C(CH3)-COOR1, donde R1 representa un grupo alquilo no substituido, lineal o ramificado, de 1 a 4 átomos de carbono, tal como un grupo metilo, etilo, propilo o isobutilo, o R1 representa un grupo cicloalquilo C4 a C12;  methacrylates of formula CH2 = C (CH3) -COOR1, where R1 represents an unsubstituted, linear or branched alkyl group of 1 to 4 carbon atoms, such as a methyl, ethyl, propyl or isobutyl group, or R1 represents a C4 to C12 cycloalkyl group;
--
los acrilatos de fórmula CH2=CH-COOR2, donde R2 representa un grupo cicloalquilo C4 a C12, tales como el acrilato de isobornilo, o un grupo tercbutilo;  acrylates of formula CH2 = CH-COOR2, where R2 represents a C4 to C12 cycloalkyl group, such as isobornyl acrylate, or a tert-butyl group;
--
las (met)acrilamidas de fórmula:  the (meth) acrylamides of the formula:
imagen1image 1 45 donde R7 y R8, idénticos o diferentes, representan cada uno un átomo de hidrógeno o un grupo alquilo de 1 a 12 átomos de carbono lineal o ramificado, tal como un grupo n-butilo, t-butilo, isopropilo, isohexilo, isooctilo o isononilo; o R7 representa H y R8 representa un grupo 1,1-dimetil-3-oxobutilo, y R’ designa H o metilo. Where R7 and R8, identical or different, each represent a hydrogen atom or an alkyl group of 1 to 12 linear or branched carbon atoms, such as an n-butyl, t-butyl, isopropyl, isohexyl, isooctyl or isononyl; or R7 represents H and R8 represents a 1,1-dimethyl-3-oxobutyl group, and R ’designates H or methyl. -y sus mezclas. -and their mixtures.
20. Composición según una cualquiera de las reivindicaciones 17 a 19, caracterizada por seleccionar los monómeros cuyo homopolímero tiene una temperatura de transición vítrea superior o igual a 40°C entre el metacrilato de metilo, el metacrilato de isobutilo, el (met)acrilato de isobornilo y sus mezclas. 20. Composition according to any one of claims 17 to 19, characterized by selecting the monomers whose homopolymer has a glass transition temperature greater than or equal to 40 ° C between methyl methacrylate, isobutyl methacrylate, (meth) acrylate Isobornyl and its mixtures. 55 55
21.twenty-one.
Composición según una cualquiera de las reivindicaciones 1 a 17 y 19 ó 20, caracterizada por ser la secuencia que tiene una Tg superior o igual a 40°C un homopolímero.  Composition according to any one of claims 1 to 17 and 19 or 20, characterized in that the sequence having a Tg greater than or equal to 40 ° C is a homopolymer.
22.22
Composición según una cualquiera de las reivindicaciones 1 a 11 y 15 ó 16, caracterizada por proceder la secuencia que tiene una Tg inferior o igual a 20°C en todo o en parte de uno o más monómeros cuyo homopolímero tiene una temperatura de transición vítrea inferior o igual a 20°C, especialmente de -100 a 20°C, preferentemente inferior o igual a 15°C, especialmente de -80°C a 15°C y preferiblemente inferior o igual a 10°C, especialmente de -50°C a 0°C.  Composition according to any one of claims 1 to 11 and 15 or 16, characterized in that the sequence having a Tg less than or equal to 20 ° C proceeds in all or part of one or more monomers whose homopolymer has a lower glass transition temperature or equal to 20 ° C, especially from -100 to 20 ° C, preferably less than or equal to 15 ° C, especially from -80 ° C to 15 ° C and preferably less than or equal to 10 ° C, especially from -50 ° C at 0 ° C.
23.2. 3.
Composición según la reivindicación precedente, caracterizada por seleccionar los monómeros cuyo homopolímero tiene una temperatura de transición vítrea inferior o igual a 20°C entre los monómeros siguientes:  Composition according to the preceding claim, characterized by selecting the monomers whose homopolymer has a glass transition temperature of less than or equal to 20 ° C between the following monomers:
--
los acrilatos de fórmula CH2=CHCOOR3, representando R3 un grupo alquilo no substituido C1 a C12 lineal o ramificado, a excepción del grupo tercbutilo, donde se encuentran eventualmente intercalados uno o más heteroátomos seleccionados entre O, N yS;  acrylates of formula CH2 = CHCOOR3, R3 representing a linear or branched C1 to C12 unsubstituted alkyl group, with the exception of the tert-butyl group, where one or more heteroatoms selected from O are eventually intercalated, N yS;
--
los metacrilatos de fórmula CH2=C(CH3)-COOR4, representando R4 un grupo alquilo no substituido C6 a C12 lineal o ramificado, donde se encuentran eventualmente intercalados uno o más heteroátomos seleccionados entre 0, N y S;  methacrylates of formula CH2 = C (CH3) -COOR4, R4 representing a linear or branched C6 to C12 unsubstituted alkyl group, where they are located possibly interleaved one or more heteroatoms selected from 0, N and S;
--
los ésteres de vinilo de fórmula R5-CO-O-CH=CH2, donde R5 representa un grupo alquilo C4 a C12 lineal o ramificado;  vinyl esters of formula R5-CO-O-CH = CH2, where R5 represents a linear or branched C4 to C12 alkyl group;
-los éteres de vinilo y de alquilo C4 a C12, tales como el éter de vinilo y de metilo y el éter de vinilo y de etilo; - C4 to C12 vinyl and alkyl ethers, such as vinyl and methyl ether and vinyl and ethyl ether; - las N-alquil(C4 a C12)acrilamidas, tales como la N-octilacrilamida, y sus mezclas. - N-C4 to C12 alkyl acrylamides, such as N-octylacrylamide, and their mixtures.
24.24.
Composición según la reivindicación 22 ó 23, caracterizada por seleccionar los monómeros cuyo homopolímero tiene una temperatura de transición vítrea inferior o igual a 20°C entre los acrilatos de alquilo cuya cadena de alquilo tiene de 1 a 10 átomos de carbono, a excepción del grupo terc-butilo.  Composition according to claim 22 or 23, characterized by selecting the monomers whose homopolymer has a glass transition temperature of less than or equal to 20 ° C between the alkyl acrylates whose alkyl chain has 1 to 10 carbon atoms, with the exception of the group tert-butyl.
25.25.
Composición según una cualquiera de las reivindicaciones 1 a 12 y 16 a 24, caracterizada por ser la secuencia que tiene una temperatura de transición vítrea inferior o igual a 20°C un homopolímero.  Composition according to any one of claims 1 to 12 and 16 to 24, characterized in that the sequence having a glass transition temperature of less than or equal to 20 ° C is a homopolymer.
26.26.
Composición según una cualquiera de las reivindicaciones 1 a 6 y 11 a 25, caracterizada por proceder la secuencia que tiene una Tg comprendida entre 20 y 40°C en todo o en parte de uno o de más monómeros cuyo homopolímero tiene una temperatura de transición vítrea comprendida entre 20 y 40°C.  Composition according to any one of claims 1 to 6 and 11 to 25, characterized in that the sequence having a Tg comprised between 20 and 40 ° C proceeds in all or part of one or more monomers whose homopolymer has a glass transition temperature between 20 and 40 ° C.
27. 27.
Composición según una cualquiera de las reivindicaciones 1 a 6 y 11 a 26, caracterizada por ser la secuencia que tiene una Tg comprendida entre 20 y 40°C un homopolímero de un monómero seleccionado entre el metacrilato de n-butilo, el acrilato de ciclodecilo, el acrilato de neopentilo y la isodecilacrilamida. Composition according to any one of claims 1 to 6 and 11 to 26, characterized in that the sequence having a Tg between 20 and 40 ° C is a homopolymer of a monomer selected from n-butyl methacrylate, cyclodecyl acrylate, Neopentyl acrylate and isodecylacrylamide.
28. 28.
Composición según una cualquiera de las reivindicaciones 1 a 6 y 11 a 26, caracterizada por ser la secuencia que tiene una Tg comprendida entre 20 y 40°C un copolímero procedente en todo o en parte de: Composition according to any one of claims 1 to 6 and 11 to 26, characterized in that the sequence having a Tg comprised between 20 and 40 ° C is a copolymer from all or part of:
- monómeros cuyo homopolímero tiene una Tg superior o igual a 40°C, especialmente una Tg de 40°C a 150°C, preferentemente superior o igual a 50°C, especialmente de 50 a 120°C, y preferiblemente superior o igual a 60°C, especialmente de 60°C a 120°C, - monomers whose homopolymer has a Tg greater than or equal to 40 ° C, especially a Tg of 40 ° C to 150 ° C, preferably greater than or equal to 50 ° C, especially 50 to 120 ° C, and preferably greater than or equal to 60 ° C, especially from 60 ° C to 120 ° C, -y de monómeros cuyo homopolímero tiene una Tg inferior o igual a 20°C, especialmente de -100 a 20°C, preferentemente inferior o igual a 15°C, especialmente de -80°C a 15°C, y preferiblemente inferior -and of monomers whose homopolymer has a Tg less than or equal to 20 ° C, especially from -100 to 20 ° C, preferably less than or equal to 15 ° C, especially from -80 ° C to 15 ° C, and preferably lower o igual a 10°C, por ejemplo de -50°C a 0°C. or equal to 10 ° C, for example from -50 ° C to 0 ° C.
29. 29.
Composición según una cualquiera de las reivindicaciones 1 a 6 y 11 a 26 y 28, caracterizada por proceder la secuencia que tiene una Tg comprendida entre 20 y 40°C en todo o en parte de monómeros seleccionados entre el metacrilato de metilo, el (met)acrilato de isobornilo, el metacrilato de trifuoroetilo, el acrilato de butilo, el acrilato de 2etilhexilo y sus mezclas. Composition according to any one of claims 1 to 6 and 11 to 26 and 28, characterized in that the sequence having a Tg comprised between 20 and 40 ° C in all or part of monomers selected from methyl methacrylate, the (met ) isobornyl acrylate, trifuoroethyl methacrylate, butyl acrylate, 2-ethylhexyl acrylate and mixtures thereof.
30.30
Composición según una cualquiera de las reivindicaciones 1 a 20 y 22 a 24 y 26, 28 ó 29, caracterizada por comprender la primera secuencia y/o la segunda secuencia al menos un monómero adicional.  Composition according to any one of claims 1 to 20 and 22 to 24 and 26, 28 or 29, characterized in that the first sequence and / or the second sequence comprises at least one additional monomer.
31.31.
Composición según la reivindicación precedente, caracterizada por seleccionar el monómero adicional entre los monómeros hidrofílicos, los monómeros con insaturación etilénica que incluyen uno o más átomos de silicio y sus mezclas.  Composition according to the preceding claim, characterized by selecting the additional monomer among the hydrophilic monomers, the monomers with ethylenic unsaturation that include one or more silicon atoms and mixtures thereof.
32.32
Composición según la reivindicación 30 ó 31, caracterizada por seleccionar el monómero adicional entre:  Composition according to claim 30 or 31, characterized by selecting the additional monomer from:
--
los monómeros con insaturación(es) etilénica(s) que tienen al menos una función ácido carboxílico o sulfónico;  monomers with ethylenic unsaturation (s) that have at least one carboxylic or sulfonic acid function;
--
los metacrilatos de fórmula CH2=C(CH3)-COOR6, donde R6 representa un grupo alquilo lineal o ramificado de 1 a 4 átomos de carbono, estando dicho grupo alquilo substituido por uno o más substituyentes seleccionados entre el grupo hidroxilo y los átomos de halógenos;  methacrylates of formula CH2 = C (CH3) -COOR6, where R6 represents a linear or branched alkyl group of 1 to 4 carbon atoms, said alkyl group being substituted by one or more substituents selected from the hydroxyl group and the halogen atoms ;
--
los metacrilatos de fórmula CH2=C(CH3)-COOR9, representando R9 un grupo alquilo C6 a C12 lineal o ramificado, donde se encuentran eventualmente intercalados uno o más heteroátomos seleccionados entre 0, N y S, estando dicho grupo alquilo substituido por uno o más substituyentes seleccionados entre el grupo hidroxilo y los átomos de halógenos;  methacrylates of formula CH2 = C (CH3) -COOR9, R9 representing a linear or branched C6 to C12 alkyl group, where one or more heteroatoms selected from 0, N and S are intercalated, said alkyl group being substituted by one or more substituents selected from the hydroxyl group and halogen atoms;
--
los acrilatos de fórmula CH2=CHCOOR10, representando R10 un grupo alquilo C1 a C12 lineal o ramificado substituido por uno o más substituyentes seleccionados entre el grupo hidroxilo y los átomos de halógeno, o R10 representa un alquil(C1-C12)-OPOE (polioxietileno) con repetición de la unidad de oxietileno de 5 a 30 veces, o R10 representa un grupo polioxietilenado que tiene de 5 a 30 unidades de óxido de etileno;  acrylates of formula CH2 = CHCOOR10, R10 representing a linear or branched C1 to C12 alkyl group substituted by one or more substituents selected from the hydroxyl group and the halogen atoms, or R10 represents a (C1-C12) -OPOE (polyoxyethylene) alkyl ) with repetition of the oxyethylene unit 5 to 30 times, or R10 represents a polyoxyethylene group having 5 to 30 units of ethylene oxide;
--
los monómeros con insaturación(es) etilénica(s) que tienen al menos una función amina terciaria, y sus mezclas.  monomers with ethylenic unsaturation (s) that have at least one tertiary amine function, and mixtures thereof.
33.33.
Composición según una cualquiera de las reivindicaciones 30 a 32, caracterizada por seleccionar el o los monómeros adicionales entre el ácido acrílico, el ácido metacrílico, el metacrilato de trifluoroetilo y sus mezclas.  Composition according to any one of claims 30 to 32, characterized in that the additional monomer (s) are selected from acrylic acid, methacrylic acid, trifluoroethyl methacrylate and mixtures thereof.
34.3. 4.
Composición según una de las reivindicaciones 30 a 33, caracterizada por representar el o los monómeros adicionales de un 1 a un 30% en peso del peso total de la primera y/o segunda secuencias.  Composition according to one of claims 30 to 33, characterized in that it represents the additional monomer (s) from 1 to 30% by weight of the total weight of the first and / or second sequences.
35.35
Composición según una de las reivindicaciones 1 a 33, caracterizada por comprender cada una de la primera y segunda secuencias al menos un monómero seleccionado entre los ésteres de ácido (met)acrílico y eventualmente al menos un monómero seleccionado entre el ácido (met)acrílico, y sus mezclas.  Composition according to one of claims 1 to 33, characterized in that each of the first and second sequences comprises at least one monomer selected from the esters of (meth) acrylic acid and possibly at least one monomer selected from (meth) acrylic acid, and their mixtures.
36.36.
Composición según una de las reivindicaciones 1 a 35, caracterizada por proceder cada una de la primera y segunda secuencias en su totalidad de al menos un monómero seleccionado entre los ésteres de ácido (met)acrílico y eventualmente de al menos un monómero seleccionado entre el ácido (met)acrílico, y sus mezclas  Composition according to one of claims 1 to 35, characterized in that each of the first and second sequences comes in its entirety from at least one monomer selected from the esters of (meth) acrylic acid and possibly from at least one monomer selected from the acid (met) acrylic, and mixtures thereof
37.37.
Composición según una cualquiera de las reivindicaciones 2 a 38, caracterizada por estar el polímero secuenciado libre de estireno.  Composition according to any one of claims 2 to 38, characterized in that the styrene-free sequenced polymer is.
38. 38.
Composición según una de las reivindicaciones precedentes, caracterizada por tener el polímero secuenciado una masa media ponderal (Mw) inferior o igual a 300.000, preferentemente de 35.000 a 200.000 y mejor de 45.000 a Composition according to one of the preceding claims, characterized in that the sequenced polymer has a weight average mass (Mw) of less than or equal to 300,000, preferably 35,000 to 200,000 and better than 45,000 to
150.000. 150,000 39. Composición según una de las reivindicaciones precedentes, caracterizada por tener el polímero secuenciado una masa media numérica (Mn) inferior o igual a 70.000, preferentemente de 10.000 a 60.000 y mejor de 12.000 a Composition according to one of the preceding claims, characterized in that the sequenced polymer has a numerical average mass (Mn) of less than or equal to 70,000, preferably 10,000 to 60,000 and better than 12,000 to 50.000. 50,000
40.40
Composición según una de las reivindicaciones 1 y 3 a 39, caracterizada por no ser el polímero secuenciado un elastómero.  Composition according to one of claims 1 and 3 to 39, characterized in that the polymer is not an elastomer.
41.41.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por estar presente el polímero secuenciado en un contenido del 0,1% al 60% en peso con respecto al peso total de la composición, preferentemente del 0,5% al 50% en peso y preferentemente aún del 1% al 40% en peso.  Composition according to any one of the preceding claims, characterized in that the sequenced polymer is present in a content of 0.1% to 60% by weight with respect to the total weight of the composition, preferably 0.5% to 50% by weight and preferably still from 1% to 40% by weight.
42.42
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por incluir un aceite volátil.  Composition according to any one of the preceding claims, characterized by including a volatile oil.
43.43
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por incluir un aceite volátil seleccionado entre el octametilciclotetrasiloxano, el decametilciclopentasiloxano, el dodecametilciclohexasiloxano, el heptametilhexiltrisiloxano, el heptametiloctiltrisiloxano, el octametiltrisiloxano, el decametiltetrasiloxano, el isododecano, el isodecano y el isohexadecano.  Composition according to any one of the preceding claims, characterized by including a volatile oil chosen from octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, dodecamethylcyclohexasiloxane, heptamethylhexyltrisiloxane, heptamethyloctyltrisiloxane, octamethyltrisiloxane, decamethyltetrasiloxane, isododecane, isodecane and isohexadecane.
44.44.
Composición según la reivindicación 42 ó 43, caracterizada por estar presente el aceite volátil en un contenido del 1% al 70% en peso con respecto al peso total de la composición, preferentemente del 5% al 50% en peso y preferiblemente del 10% al 35% en peso.  Composition according to claim 42 or 43, characterized in that the volatile oil is present in a content of 1% to 70% by weight with respect to the total weight of the composition, preferably from 5% to 50% by weight and preferably from 10% to 35% by weight.
45.Four. Five.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por incluir un aceite no volátil.  Composition according to any one of the preceding claims, characterized by including a non-volatile oil.
46.46.
Composición según la reivindicación precedente, caracterizada por seleccionar el aceite no volátil entre los aceites no volátiles hidrocarbonados y los aceites no volátiles siliconados.  Composition according to the preceding claim, characterized in that the non-volatile oil is selected from hydrocarbon non-volatile oils and siliconized non-volatile oils.
47.47
Composición según la reivindicación 45 ó 46, caracterizada por estar presente el aceite no volátil en un contenido del 1% al 80% en peso con respecto al peso total de la composición, preferentemente del 5% al 60% en peso y preferiblemente del 10% al 50% en peso, especialmente del 20% al 50% en peso.  Composition according to claim 45 or 46, characterized in that the non-volatile oil is present in a content of 1% to 80% by weight with respect to the total weight of the composition, preferably 5% to 60% by weight and preferably 10% 50% by weight, especially 20% to 50% by weight.
48.48.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por incluir al menos un cuerpo graso sólido a temperatura ambiente seleccionado entre las ceras, los cuerpos grasos pastosos, las gomas y sus mezclas.  Composition according to any one of the preceding claims, characterized by including at least one solid fatty body at room temperature selected from among waxes, pasty fatty bodies, gums and mixtures thereof.
49.49.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por contener de un 0,1 a un 50% en peso de ceras con respecto al peso total de la composición, y preferentemente de un 1 a un 30% en peso.  Composition according to any one of the preceding claims, characterized in that it contains from 0.1 to 50% by weight of waxes with respect to the total weight of the composition, and preferably from 1 to 30% by weight.
50.fifty.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por incluir una materia colorante.  Composition according to any one of the preceding claims, characterized by including a coloring matter.
51.51.
Composición según una cualquiera de las reivindicaciones precedentes, caracterizada por incluir un ingrediente cosmético seleccionado entre los polímeros filmógenos adicionales, las vitaminas, los espesantes, los oligoelementos, los suavizantes, los secuestrantes, los perfumes, los agentes alcalinizantes o acidificantes, los conservantes, los filtros solares, los tensioactivos, los antioxidantes o sus mezclas.  Composition according to any one of the preceding claims, characterized in that it includes a cosmetic ingredient selected from the additional film-forming polymers, vitamins, thickeners, trace elements, softeners, sequestrants, perfumes, alkalizing or acidifying agents, preservatives, sunscreens, surfactants, antioxidants or mixtures thereof.
52.52
Composición cosmética según una cualquiera de las reivindicaciones precedentes, caracterizada por presentarse en forma de pasta o de barra.  Cosmetic composition according to any one of the preceding claims, characterized in that it is presented in the form of paste or bar.
53.53.
Composición cosmética según una cualquiera de las reivindicaciones precedentes, caracterizada por presentarse en forma anhidra.  Cosmetic composition according to any one of the preceding claims, characterized in that it is presented in an anhydrous form.
54.54
Conjunto cosmético que comprende:  Cosmetic set comprising:
a) un recipiente que delimita al menos un compartimento, estando cerrado dicho recipiente por un elemento de cierre, y b) una composición dispuesta en el interior de dicho compartimento, guardando conformidad la composición con una cualquiera de las reivindicaciones que anteceden. a) a container that delimits at least one compartment, said container being closed by a closure element, and b) a composition disposed within said compartment, the composition being in accordance with any one of the preceding claims.
55.55.
Conjunto cosmético según la reivindicación 54, caracterizado por estar formado el recipiente, al menos en parte, en al menos un material termoplástico.  Cosmetic assembly according to claim 54, characterized in that the container is formed, at least in part, in at least one thermoplastic material.
56.56.
Conjunto cosmético según la reivindicación 54, caracterizado por estar formado el recipiente, al menos en parte, en al menos un material no termoplástico, especialmente en vidrio o en metal.  Cosmetic assembly according to claim 54, characterized in that the container is formed, at least in part, in at least one non-thermoplastic material, especially in glass or metal.
57.57.
Conjunto según una cualquiera de las reivindicaciones 54 a 56, caracterizado por el hecho de que, en la posición cerrada del recipiente, el elemento de cierre está atornillado sobre el recipiente.  Assembly according to any one of claims 54 to 56, characterized in that, in the closed position of the container, the closure element is screwed onto the container.
58.58.
Conjunto según una cualquiera de las reivindicaciones 54 a 57, caracterizado por el hecho de que, en la posición cerrada del recipiente, el elemento de cierre se acopla al recipiente de otro modo que por atornillamiento, especialmente por trinquete, encoladura o soldadura.  Assembly according to any one of claims 54 to 57, characterized in that, in the closed position of the container, the closure element is coupled to the container other than by screwing, especially by ratchet, glueing or welding.
59.59.
Procedimiento cosmético de maquillaje de los labios, consistente en la aplicación sobre los labios de una composición según una cualquiera de las reivindicaciones 1 a 53.  Cosmetic lip makeup procedure, consisting of the application on the lips of a composition according to any one of claims 1 to 53.
60.60
Utilización de una composición según una cualquiera de las reivindicaciones 1 a 53 para obtener un depósito de maquillaje sobre los labios que tiene una buena persistencia, especialmente una buena persistencia tras contactar con agua o con un aceite alimentario.  Use of a composition according to any one of claims 1 to 53 to obtain a makeup deposit on the lips that has a good persistence, especially a good persistence after contact with water or a food oil.
ES03798229T 2002-09-26 2003-09-26 LIP BAR CONTAINING A SEQUENCED POLYMER. Expired - Lifetime ES2361010T3 (en)