EP0000157A1 - Process for the manufacture of highly concentrated aqueous solutions of salts of dicarboxylic acids with diamines and/of polyamide precondensates and their use - Google Patents
Process for the manufacture of highly concentrated aqueous solutions of salts of dicarboxylic acids with diamines and/of polyamide precondensates and their use Download PDFInfo
- Publication number
- EP0000157A1 EP0000157A1 EP78100175A EP78100175A EP0000157A1 EP 0000157 A1 EP0000157 A1 EP 0000157A1 EP 78100175 A EP78100175 A EP 78100175A EP 78100175 A EP78100175 A EP 78100175A EP 0000157 A1 EP0000157 A1 EP 0000157A1
- Authority
- EP
- European Patent Office
- Prior art keywords
- diamines
- dicarboxylic acid
- solutions
- dicarboxylic acids
- carbon atoms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Herstellung von hochkonzentrierten wäßrigen Lösungen von Salzen aus Dicarbonsäuren und Diaminen sowie Polyamidpräkondensaten durch Umsetzen von Alkandicarbonsäuren mit 6 bis 12 Kohlenstoffatomen und Diaminen der Formel NH2RNH2, in der R einen Alkylenrest mit 6 bis 12 Kohlenstoffatomen oder die Reste <IMAGE> bezeichnet, wobei man wäßrige Salzlösungen aus Dicarbonsäuren und Diaminen geringerer Konzentration, die eine entsprechende Menge der jeweiligen Dicarbonsäure im Überschuß gelöst enthalten, mit dem jeweiligen geschmolzenen Diamin in äquivalenten Mengen; bezogen auf die gelöste Dicarbonsäure, umsetzt, mit der Maßgabe, daß die Umsetzung unter erhöhtem Druck durchgeführt wird und eine Endtemperatur von 140 bis 210°C bei der Umsetzung eingehalten wird. Die hergestellten Lösungen werden zur Erzeugung von Polyamiden verwendet.Preparation of highly concentrated aqueous solutions of salts from dicarboxylic acids and diamines and polyamide precondensates by reacting alkanedicarboxylic acids with 6 to 12 carbon atoms and diamines of the formula NH2RNH2, in which R denotes an alkylene residue with 6 to 12 carbon atoms or the residues <IMAGE>, whereby aqueous salt solutions from dicarboxylic acids and diamines of lower concentration, which contain a corresponding amount of the respective dicarboxylic acid dissolved in excess, with the respective molten diamine in equivalent amounts; based on the dissolved dicarboxylic acid, with the proviso that the reaction is carried out under increased pressure and a final temperature of 140 to 210 ° C is maintained during the reaction. The solutions produced are used to produce polyamides.
Description
Gegenstand der Erfindung ist ein Verfahren zur Herstellung von hochkonzentrierten wäßrigen Lösungen von Salzen aus Dicarbonsäuren und Diaminen sowie Polyamidpräkondensaten durch Umsetzen von Alkandicarbonsäuren mit 6 bis 12 Kohlenstoffatomen und Diaminen mit der Formel NH2R NH2, in der R einen Alkylenrest mit 6 bis 12 Kohlenstoffatomen bezeichnet oder die Reste
Bei der in der Technik wohl bekannten Herstellung von Polyamiden aus Dicarbonsäuren und Diaminen geht man in der Regel von wäßrigen Salzlösungen aus Dicarbonsäuren und Diaminen aus. Wie aus der GB-PS 674 954, der DT-PS 1 060 139 und der DT-AS 11 58 257 bekannt ist, geht man hierbei im allgemeinen von 45 bis 70 gewichtsprozentigen Salzlösungen aus. Vor der eigentlichen Polykondensation ist es jedoch erforderlich, aus den Salzlösungen das überschüssige Wasser zum großen Teil zu entfernen. Dies hat den Nachteil, daß man große Flüssigkeitsmengen bewegen muß und darüber hinaus er-' hebliche Mengen an Energie verbraucht, um das Wasser zu entfernen.In the production of polyamides from dicarboxylic acids and diamines, which is well known in the art, aqueous salt solutions of dicarboxylic acids and diamines are generally used. As is known from GB-PS 674 954, DT-PS 1 060 139 and DT-AS 11 58 257, it is generally assumed that 45 to 70 percent by weight salt solutions are used. Before the actual polycondensation, however, it is necessary to remove a large part of the excess water from the salt solutions. This has the disadvantage that one must move large amounts of liquid and, moreover, consume considerable amounts of energy to remove the water.
Um überflüssige Mengen an Wasser zu vermeiden, wurde auch schon versucht, direkt von den flüssigen Ausgangsstoffen z.B. geschmolzener Adipinsäure und geschmolzenem Hexamethylendiamin bei der Polyamidherstellung auszugehen. Solche Verfahren sind beispielsweise aus der GB-PS 1 018 653 und BE-PS 640 369 bekannt. Abgesehen davon, daß sich geschmolzene Adipinsäure verändert, z.B. durch Decarboxylierung und Anhydridbildung, treten erhebliche Probleme bei der genauen Dosierung der Ausgangsstoffe auf. Dies gilt umso mehr als eine genaue Dosierung erforderlich ist, um äquivalente Verhältnisse einzuhalten.In order to avoid unnecessary amounts of water, attempts have already been made to directly extract the liquid starting materials, e.g. melted adipic acid and melted hexamethylenediamine in the production of polyamides. Such methods are known for example from GB-PS 1 018 653 and BE-PS 640 369. Apart from the fact that molten adipic acid changes, e.g. Due to decarboxylation and anhydride formation, there are considerable problems with the exact dosage of the starting materials. This is all the more true since an exact dosage is required in order to maintain equivalent ratios.
Aus der DT-OS 24 03 178 ist auch schon bekannt, kristalline Salze aus Dicarbonsäuren und Diaminen herzustellen, indem man Dicarbonsäure enthaltende Salzlösungen mit dem jeweiligen Diamin neutralisiert. Hierbei sollten jedoch Temperaturen von 80°C nicht überschritten werden.It is also known from DT-OS 24 03 178 to produce crystalline salts from dicarboxylic acids and diamines by neutralizing salt solutions containing dicarboxylic acid with the respective diamine. However, temperatures of 80 ° C should not be exceeded.
Es war die technische Aufgabe gestellt, Ausgangslösungen für die Herstellung von Polyamiden aus Dicarbonsäuren und Diaminen zur Verfügung zu stellen, die leicht handhabbar sind und möglichst wenig Wasser enthalten und die in den Ausgangslösungen enthaltene'Wärmeenergie nutzbar zu machen.The technical task was to provide starting solutions for the production of polyamides from dicarboxylic acids and diamines which are easy to handle and contain as little water as possible and which make it possible to utilize the thermal energy contained in the starting solutions.
Diese Aufgabe wird gelöst in einem Verfahren zur Herstellung von hochkonzentrierten wäßrigen Lösungen von Salzen aus Dicarbonsäuren und Diaminen sowie Polyamidpräkondensaten durch Umsetzen von Alkandicarbonsäuren mit 6 bis 12 Kohlenstoffatomen und Diaminen der Formel NH2RNH2, in der R einen Alkylenrest mit 6 bis 12 Kohlenstoffatomen oder die Reste
Das neue Verfahren hat den Vorteil, daß man unmittelbar zu hochkonzentrierten wäßrigen Ausgangslösungen für die Polyamidherstellung gelangt, die nicht mehr weiter konzentriert werden müssen. Weiter hat das neue Verfahren den Vorteil, daß man Ausgangslösungen erhält, in denen die enthaltene Neutralisationswärme für die Polykondensation genutzt wird. Schließlich hat das neue Verfahren den Vorteil, daß die Dosierung der Ausgangsstoffe und deren Vermischung einfach zu bewerkstelligen ist.The new process has the advantage that it immediately leads to highly concentrated aqueous starting solutions for polyamide production, which no longer need to be concentrated. The new process also has the advantage that starting solutions are obtained in which the heat of neutralization contained is used for the polycondensation. Finally, the new process has the advantage that the starting materials can be metered and mixed easily.
Im Hinblick auf die DT-OS 2 403 178 war es nicht angezeigt, bei der Neutralisation von Dicarbonsäuren mit Diaminen Temperaturen von 80°C zu überschreiten, da bei höheren Temperaturen für die Polykondensation unbrauchbare Produkte zu erwarten waren.With regard to DT-OS 2 403 178, it was not appropriate to exceed temperatures of 80 ° C. in the neutralization of dicarboxylic acids with diamines, since products which were unusable for polycondensation were to be expected at higher temperatures.
Erfindungsgemäß geht man von Alkandicarbonsäuren mit 6 bis 12 Kohlenstoffatomen aus. Bevorzugt verwendet-man gerad- kettige α-ω-Dicarbonsäuren der genannten Kohlenstoffzahl. Geeignete Dicarbonsäuren sind beispielsweise Adipinsäure, Korksäure, Azelainsäure, Sebacinsäure, Dekandisäure und Dodecandisäure. Besondere technische Bedeutung haben Adipinsäure und Sebacinsäure erlangt.According to the invention, alkane dicarboxylic acids with 6 to 12 carbon atoms are used. Straight-chain α-ω-dicarboxylic acids of the stated carbon number are preferably used. Suitable dicarboxylic acids are, for example, adipic acid, Suberic acid, azelaic acid, sebacic acid, decanedioic acid and dodecanedioic acid. Adipic acid and sebacic acid have acquired particular technical importance.
Ferner geht man von Diaminen der Formel NH2RNH2 aus, in der R einen Alkylenrest mit 6 bis 12 Kohlenstoffatomen oder die Reste
Man geht zunächst von einer wäßrigen Salzlösung aus Dicarbonsäuren und Diaminen geringerer Konzentration aus, die eine entsprechende Menge der jeweiligen Dicarbonsäure im überschuß gelöst enthält. Vorteilhaft verwendet man Lösungen, die 40 bis 65 Gewichtsprozent, insbesondere 50 bis 65 Gewichtsprozent an den jeweiligen Salzen, bezogen auf die Summe von Salz und Wasser, enthalten. Die Menge an gelöster Dicarbonsäure richtet sich nach der gewünschten Endkonzentration der herzustellenden hochkonzentrierten wäßrigen Lösungen.The starting point is an aqueous salt solution of dicarboxylic acids and diamines of lower concentration, which contains a corresponding amount of the particular dicarboxylic acid dissolved in excess. Solutions which contain 40 to 65 percent by weight, in particular 50 to 65 percent by weight, of the respective salts, based on the sum of salt and water, are advantageously used. The amount of dissolved dicarboxylic acid depends on the desired final concentration of the highly concentrated aqueous solutions to be prepared.
Nach einer bevorzugten Ausführungsform löst man in einer Salzlösung geringerer Konzentration feste Dicarbonsäure auf. Hierbei hält man in der Regel Temperaturen von 60 bis 110°C ein. So erhaltene freie Dicarbonsäure enthaltende Salzlösung wird dann mit geschmolzenem Diamin in äquivalenten Mengen bezogen auf die gelöste Dicarbonsäure umgesetzt. Vorteilhaft achtet man darauf, daß man den pH--Wert für den Äquivalenzpunkt des jeweils herzustellenden Salzes einhält. Beispielsweise ist der Äquivalenzpunkt für Hexymethylendiammoniumadipat pH 7,62 und für Hexamethylendiammoniumsebatcat pH 7,5 gemessen in 10 prozentiger wäßriger Lösung bei 25°C. Vorteilhaft führt man die Umsetzung in einer Mischstrecke durch, wobei man zunächst einen geringen Unterschuß an geschmolzenem Diamin zugibt und dann die präzise Einstellung durch eine weitere Zugabe vom geschmolzenen Diamin durchführt. Um den bei der Polykondensation eintretenden Verlust an Diaminen auszugleichen, verwendet man Diamine in der Regel im Überschuß z.B. bis 1,5 Molprozent.According to a preferred embodiment, solid dicarboxylic acid is dissolved in a salt solution of lower concentration. Temperatures of 60 to 110 ° C are generally maintained. Salt solution thus obtained containing free dicarboxylic acid is then reacted with molten diamine in equivalent amounts based on the dissolved dicarboxylic acid. It is advantageous to ensure that the pH value for the equivalence point of the salt to be produced is observed. For example, the equivalence point for hexymethylene diammonium adipate is pH 7.62 and for hexamethylene diammonium sebatcat pH 7.5 measured in 10 percent aqueous solution at 25 ° C. The reaction is advantageously carried out in a mixing section, first adding a small deficit of molten diamine and then carrying out the precise adjustment by adding molten diamine again. In order to compensate for the loss of diamines which occurs during the polycondensation, diamines are generally used in excess, e.g. up to 1.5 mole percent.
Nach einer anderen bevorzugten Ausführungsform löst man zunächst feste Dicarbonsäure in einer wäßrigen Lösung von Diamin im Unterschuß. Hierbei erhält man eine Salz- lösung aus Dicarbonsäure und Diamin, die eine überschüssige Menge an Dicarbonsäure gelöst enthält. Es versteht sich, daß man die Mengenverhältnisse so wählt, daß man eine Salzlösung der vorgenannten Konzentration erhält und die überschüssige Menge an Dicarbonsäure der gewünschten Endkonzentration der wäßrigen Lösung entspricht..Das Lösen der Dicarbonsäure erfolgt vorteilhaft bei Temperaturen von 60 bis 110°C, wobei man in der Regel atmosphärischen Druck einhält. Die so erhaltene freie Dicarbonsäure enthaltende Salzlösung wird dann mit geschmolzenem Diamin in äquivalenten Mengen bezogen auf gelöste Dicarbonsäure umgesetzt. Diese Umsetzung erfolgt vorteilhaft wie bei der vorgenannten Arbeitsweise beschrieben.According to another preferred embodiment, solid dicarboxylic acid is first dissolved in an aqueous solution of diamine in deficit. This gives a salt solution of dicarboxylic acid and diamine, which contains an excess amount of dicarboxylic acid in solution. It is understood that the proportions are chosen so that a salt solution of the aforementioned concentration is obtained and the excess amount of dicarboxylic acid corresponds to the desired final concentration of the aqueous solution. The dicarboxylic acid is advantageously dissolved at temperatures of 60 to 110 ° C., where you usually maintain atmospheric pressure. The salt solution thus obtained containing free dicarboxylic acid is then melted with diamine in equivalent amounts based on dissolved di implemented carboxylic acid. This implementation is advantageously carried out as described in the aforementioned procedure.
ist es, die erfindungsgemäßen wäßrigen Lösungen für die Kondensation zu verwenden, ohne vorher die Neutralisationswärme abzuführen. Unbeachtlich sind in diesem Zusammenhang apparativ bedingte Wärmeverluste.is to use the aqueous solutions according to the invention for the condensation without first removing the heat of neutralization. In this context, heat losses caused by the device are irrelevant.
Es ist auch möglich, einen Teil der Neutralisationswärme zum Lösen der Dicarbonsäuren in den Salzlö.sungen geringerer Konzentration zu verwenden.It is also possible to use part of the heat of neutralization to dissolve the dicarboxylic acids in the salt solutions of lower concentration.
Polyamide, die aus den erfindungsgemäßen Lösungen hergestellt werden, eignen sich zur Erzeugung von aus der Schmelze geformten Massen, wie Fäden, Fasern, Formteile, Platten oder Überzügen.Polyamides which are produced from the solutions according to the invention are suitable for the production of masses shaped from the melt, such as threads, fibers, moldings, plates or coatings.
Das Verfahren nach der Erfindung sei in folgenden Beispielen veranschaulicht.The method according to the invention is illustrated in the following examples.
5250 g AH-Salz (Hexamethylendiammoniumadipat) wurden in einem 40-1-Rührautoklaven in 3450 g Wasser unter Erwärmen auf 950C gelöst. Zu der so erhaltenen 60,3 prozentigen AH-Salz--Lösung wurden 8025 g feste Adipinsäure allmählich unter Rühren bei 90 bis 95°C zugegeben und gelöst. Der Autoklav wurde mit Stickstoff gespült und verschlossen. Der Inhalt wurde auf 100°C erhitzt, wobei sich ein Druck von 2 bar einstellte (alle Druckangaben sind Absolutwerte). 6375 g geschmolzenes Hexamethylendiamin von 100°C wurde aus einem Zulaufgefäß mit Stickstoffdruck innerhalb von 2 Minuten bei laufendem Rührer in den Autoklaven gedrückt. In der so erhaltenen 85 gewichtsprozentigen AH-Salz-Lösung stieg die Temperatur durch die freiwerdende Neutralisationswärme an und erreichte 2 Minuten nach Zugabe des Hexamethylendiamins 162°C. Während der Zugabe des Hexamethylendiamins'stieg der' Druck vorübergehend auf 4 bar und fiel bis zum Ende der Zugabe auf 3 bar.5250 g AH salt (hexamethylene diammonium adipate) were dissolved in a 40-1 stirred autoclave in 3450 g of water with heating to 95 0 C. To the 60.3 percent AH salt solution thus obtained, 8025 g of solid adipic acid were gradually added with stirring at 90 to 95 ° C. and dissolved. The autoclave was flushed with nitrogen and sealed. The contents were heated to 100 ° C, which resulted in a pressure of 2 bar (all pressure values are absolute values). 6375 g of molten hexamethylenediamine at 100 ° C. were pressed into the autoclave from a feed vessel with nitrogen pressure within 2 minutes with the stirrer running. In the 85% by weight AH salt solution thus obtained, the temperature rose due to the heat of neutralization released and reached 2 minutes after the addition of the hexamethylene diamine 162 ° C. During the addition of the hexamethylenediamine, the pressure rose temporarily to 4 bar and fell to 3 bar until the end of the addition.
In analoger Weise erhält man Nylon 6,9 und Nylon 10,6 Salzlösungen.Analogously, nylon 6.9 and nylon 10.6 salt solutions are obtained.
Das Beispiel zeigt die Ausnutzung eines Teils der Neutralisationswärme zum Lösen der Dicarbonsäure.The example shows the use of part of the heat of neutralization to dissolve the dicarboxylic acid.
In einem Glaskolben mit Rührer, Rückflußkühler, Thermometer und Tropftrichter wurden 292 g feste Adipinsäure bei 20°C vorgelegt.292 g of solid adipic acid at 20 ° C. were placed in a glass flask equipped with a stirrer, reflux condenser, thermometer and dropping funnel.
Der Kolben wurde in ein als Schutzheizung wirkendes Wasserbad von 75°C eingetaucht; sofort danach wurde eine im Tropftrichter auf 90°C gehaltene Lösung von 75 g Hexamethylendiamin in 92 g Wasser innerhalb von 20 Sekunden unter Rühren zugegeben. Nach 2 Minuten war eine klare Lösung entstanden, deren Temperatur 69°C betrug. Die Zusammensetzung der Lösung war 37 % AH-Salz, 43 % Adipinsäure und 20 % Wasser. Die weitere Umsetzung erfolgte analog Beispiel 1.The flask was immersed in a water bath at 75 ° C acting as a protective heater; immediately thereafter, a solution of 75 g of hexamethylenediamine in 92 g of water, kept in the dropping funnel at 90 ° C., was added with stirring within 20 seconds. After 2 minutes a clear solution had formed, the temperature of which was 69 ° C. The composition of the solution was 37% AH salt, 43% adipic acid and 20% water. The further implementation was carried out analogously to Example 1.
Die im Beispiel 1 erhaltene AH-Salz-Lösung wurde ohne Abkühlen der Lösung polykondensiert. Sie wurde innerhalb von 3 1/2 Stunden auf 275°C erhitzt, wobei der Druck durch Abblasen von Wasserdampf auf 19 bar gehalten wurde. Nach Erreichen von 2750C wurde innerhalb von 1 Stunde auf Normaldruck entspannt und 1 Stunde bis 273°C nachkondensiert. Das Produkt wurde mit Stickstoffdruck aus dem Autoklaven herausgedruckt, wobei der Schmelzstrang in einem Wasser- bad abgekühlt und granuliert wurde. Das erhaltene Polyamid 66 hatte eine relative Viskosität von 2,54, gemessen in 1 prozentiger Lösung in 96 prozentiger Schwefelsäure, und einen Gehalt an sauren Gruppen von 54 mÄq/kg und an basischen Gruppen von 76 mÄq/kg.The AH salt solution obtained in Example 1 was polycondensed without cooling the solution. It was heated to 275 ° C. in the course of 3 1/2 hours, the pressure being kept at 19 bar by blowing off steam. After reaching 275 0 C was laid over 1 hour at normal pressure and postcondensed 1 hour to 273 ° C. The product was pressed out of the autoclave under nitrogen pressure, with the melt strand in a water Bad cooled and granulated. The polyamide 66 obtained had a relative viscosity of 2.54, measured in 1 percent solution in 96 percent sulfuric acid, and a content of acidic groups of 54 meq / kg and of basic groups of 76 meq / kg.
Claims (9)