DE3801851A1 - SURFACE COVERING AND METHOD FOR THE PRODUCTION THEREOF - Google Patents
SURFACE COVERING AND METHOD FOR THE PRODUCTION THEREOFInfo
- Publication number
- DE3801851A1 DE3801851A1 DE3801851A DE3801851A DE3801851A1 DE 3801851 A1 DE3801851 A1 DE 3801851A1 DE 3801851 A DE3801851 A DE 3801851A DE 3801851 A DE3801851 A DE 3801851A DE 3801851 A1 DE3801851 A1 DE 3801851A1
- Authority
- DE
- Germany
- Prior art keywords
- surface covering
- covering according
- substrate
- coating
- solid particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die Erfindung betrifft einen Oberflächenbelag, bestehend aus einem Substrat mit einer darauf aufgebrachten undurchlässigen Beschichtung sowie ein Verfahren zu seiner Herstellung.The invention relates to a surface covering, consisting of from a substrate with an impermeable applied thereon Coating and a process for its production.
Bekannt sind Oberflächenbeläge, auf denen erhabene Elemente angeordnet sind, die Feststoffteilchen enthalten. So zum Beispiel sind aus der US-PS 43 48 447 rutschfeste Kunststoffbodenbeläge bekannt, bei denen anorganische Teilchen in eine gehärtete Kunststoffgrundmasse eingebettet sind, wobei sie im wesentlichen aneinander angrenzen. Da das Haftmittel in einem selektiven Muster aufgedruckt werden kann, bewirken die erhabenen Elemente das Aussehen eines in Deckung geprägten Bodenbelags. Da die Teilchen auf die haftvermittelnde Oberfläche der Grundmasse aufgebracht werden, durchdringen sie gewöhnlich die Kunststoffgrundmasse nicht gleichmäßig. Außerdem ist die Zahl der Teilchen stark begrenzt, und die Teilchen müssen zur vollständigen Verbindung mit dem Material mit einer dünnen Beschichtung aus einem transparenten Kunststoff abgedeckt werden. Bei der Beschichtung der Teilchen mit diesem dünnen Film wird auch die darunter liegende, zwischen den erhabenen Elementen angeordnete Beschichtung überzogen.Surface coverings on which raised elements are known are arranged, which contain solid particles. So for Example are from US-PS 43 48 447 non-slip plastic floor coverings known in which inorganic particles in a hardened plastic matrix are embedded, whereby they essentially adjoin each other. Because the adhesive can be printed in a selective pattern the raised elements have the appearance of a coined one Flooring. Because the particles adhere to the adhesive Surface of the base material are applied, penetrate they usually do not spread the plastic base evenly. In addition, the number of particles is very limited, and the Particles need to be fully bonded to the material with a thin coating of a transparent plastic be covered. When coating the particles with this thin film is also the one underneath, between the coating arranged arranged coating coated.
Bei den bekannten Lösungen können die erhabenen Elemente zwar eine gewisse dekorative Bedeutung haben, würden jedoch ein darunter liegendes Dekor, sofern vorhanden, beeinträchtigen und abdunkeln. Außerdem sind erhabene Elemente zwar günstig für die Steigerung der Verschleiß- und Rutschfestigkeit, bewirken jedoch zusätzliche Schwierigkeiten bei der Pflege von Oberflächen und Fußböden mit derartigen Belägen.In the known solutions, the raised elements can would have a certain decorative meaning, however an underlying decor, if any, impair and darken. In addition, there are sublime elements favorable for increasing wear and slip resistance, cause additional difficulties, however the care of surfaces and floors with such coverings.
Die Aufgabe der Erfindung ist die Steigerung der Zahl der Feststoffteilchen, die in den erhabenen Elementen auf einem Oberflächenbelag angeordnet werden können, die Bereitstellung eines Oberflächenbelags, bei dem die auf der Oberfläche der erhabenen Elemente vorhandenen Feststoffteilchen gleichmäßiger über die erhabenen Elemente verteilt sind und bei dem zur Schaffung von in Deckung geprägten Merkmalen ohne chemische oder mechanische Prägung die erhabenen Elemente selektiv angeordnet sind, und die Bereitstellung eines Oberflächenbelags, bei welchem die erhabenen Elemente keinen Überzug aus transparentem Kunststoff benötigen.The object of the invention is to increase the number of Solid particles that are in the raised elements on a Surface covering can be arranged, providing of a surface covering in which the on the surface of the raised elements existing solid particles are distributed more evenly over the raised elements and in the creation of features characterized by coverage the raised ones without chemical or mechanical imprinting Items are selectively arranged and deployed a surface covering in which the raised elements do not need a transparent plastic cover.
Diese Aufgabe wird mit den in Patentanspruch 1 angegebenen Merkmalen gelöst, die in den Unteransprüchen vorteilhaft weitergebildet sind.This object is achieved with those specified in claim 1 Features solved, which are advantageous in the dependent claims are trained.
Eine Ausführungsform der Erfindung betrifft einen Oberflächenbelag, der ein Substrat, eine darauf angeordnete undurchlässige Beschichtung und erhabene Elemente umfaßt, die auf der Beschichtung selektiv angeordnet sind und einen thixotropen Kunststoff darstellen, der Feststoffteilchen enthält.One embodiment of the invention relates to a surface covering, which is a substrate, an impermeable one arranged thereon Coating and raised elements includes the are selectively arranged on the coating and one represent thixotropic plastic, the solid particles contains.
Eine weitere Ausführungsform der Erfindung betrifft ein Verfahren zur Herstellung eines Oberflächenbelags, welches die Bereitstellung einer undurchlässigen Beschichtung auf einem Substrat, die selektive Anordnung erhabener Elemente eines thixotropen Kunststoffes, der Feststoffteilchen enthält, und das Verschmelzen der erhabenen Elemente mit dem Substrat umfaßt, um einen Belag von einstückigem Aufbau zu erhalten.Another embodiment of the invention relates to a Process for producing a surface covering, which the provision of an impermeable coating a substrate, the selective arrangement of raised elements of a thixotropic plastic, the solid particles contains, and the fusion of the sublime elements with the Substrate encompassed to form a one-piece construction covering receive.
Anhand der Zeichnung wird die Erfindung näher erläutert. Es zeigt The invention is explained in more detail with reference to the drawing. It shows
Fig. 1 einen Querschnitt durch den erfindungsgemäßen Belag, Fig. 1 shows a cross section through the inventive coating,
Fig. 2 einen Querschnitt durch den Belag nach US-PS 43 48 447 und Fig. 2 shows a cross section through the covering according to US-PS 43 48 447 and
Fig. 3 in einem Diagramm die pseudoplastischen Eigenschaften eines Polyvinylchloridplastisols. Fig. 3 in a diagram the pseudoplastic properties of a polyvinyl chloride plastisol.
Elemente mit erhabener Oberfläche und insbesondere solche, die Feststoffteilchen enthalten, werden schon lange zur Steigerung der Rutsch- und Abriebfestigkeit von Oberflächenbelägen verwendet. Erfindungsgemäß kann ein Erzeugnis mit derartigen erhabenen Oberflächenelementen von größerer Dicke nach einem Verfahren hergestellt werden, das keine Beschichtung der Elemente und der umgebenden Bereiche erforderlich macht.Elements with a raised surface and especially those containing solid particles have long been Increasing the slip and abrasion resistance of surface coverings used. According to the invention, a product with such raised surface elements of larger size Thickness can be made by a process that does not Coating of the elements and the surrounding areas required makes.
Bisher wurde ein Schichtaufbau, wie der in Fig. 2 gezeigte, dadurch erzeugt, daß ein Substrat 7 mit einer geeigneten Beschichtung 8 unter selektiver Aufbringung eines Haftmittels 15 wie eines nicht gelierten Plastisols hergestellt wurde. Die Feststoffteilchen, wie etwa die Elemente 10 und 11, wurden dann gleichmäßig aufgebracht, hafteten jedoch nur auf den Haftmittelbereichen, wobei der Rest entfernt wurde. Um die Teilchen in ihrer Position zu halten, wurde das Material dann mit einer gleichmäßigen Schicht eines transparenten Trittschichtmaterials 13 überzogen.So far, a layer structure, such as that shown in FIG. 2, has been produced by producing a substrate 7 with a suitable coating 8 with the selective application of an adhesive 15 such as a non-gelled plastisol. The solid particles, such as elements 10 and 11 , were then applied evenly, but adhered only to the adhesive areas, with the rest removed. The material was then coated with a uniform layer of a transparent wear layer material 13 to hold the particles in position.
Erfindungsgemäß wird, wie Fig. 1 zeigt, ein Substrat 20 mit einer geeigneten undurchlässigen Beschichtung 22 hergestellt und danach selektiv mit einen thixotropen Kunststoff 26, der Feststoffteilchen 28 enthält, darstellenden erhabenen Elementen 24 versehen. Da eine transparente verschleiß- widerstandsfähige Schicht nicht erforderlich ist, um die Teilchen dauerhaft miteinander zu verbinden, wie dies beim bekannten Verfahren der Fall ist, können die mit 30 bezeichneten Abschnitte der darunter liegenden Beschichtung 22 im Endprodukt unbeschichtet belassen werden.According to the invention, as shown in FIG. 1, a substrate 20 is produced with a suitable impermeable coating 22 and then selectively provided with raised elements 24 representing thixotropic plastic 26 , which contains solid particles 28 . Since a transparent wear-resistant layer is not required in order to permanently bond the particles to one another, as is the case with the known method, the sections of the coating 22 underneath, designated 30 , can be left uncoated in the end product.
Die Erfindung hängt nicht vom verwendeten Substrat ab. Für die Durchführung der Erfindung kann jedes der üblicherweise auf dem vorliegenden Gebiet verwendeten Substrate zum Einsatz gelangen. Ein geeignetes Substrat kann die unten im Beispiel beschriebene mit Plastisol gesättigte Glasmatte sein. Mit derselben vorteilhaften Wirkung könnte auch eine im feuchten Zustand aufgelegte Filzbahn sein, wie sie ebenfalls allgemein in der Oberflächenbeschichtungstechnik verwendet wird. Außerdem kann jedes Substrat zur Bildung einer Zwischenschicht auf der Rückseite in Form einer geschäumten oder kompakten Beschichtung überzogen werden.The invention does not depend on the substrate used. For the practice of the invention can be any of the usual substrates used in the present field reach. A suitable substrate can be found below in Example described glass mat saturated with plastisol be. With the same beneficial effect, one could in the wet state, felt sheet like her also generally in surface coating technology is used. In addition, any substrate can be used for formation an intermediate layer on the back in the form of a foamed or compact coating.
Es ist davon auszugehen, daß die Erfindung durch die Wahl des Substrats keineswegs eingeschränkt wird. Die Auswahl unter den zugänglichen Substraten erfolgt unter der Forderung nach günstiger Herstellung bzw. der physikalischen Eigenschaften des Endproduktes.It is believed that the invention is by choice the substrate is in no way restricted. The selection among the accessible substrates is under the requirement after cheap manufacture or the physical Properties of the end product.
Das gewählte Substrat sollte mit einem geeigneten undurchlässigen Stoff beschichtet werden. Es ist zwar möglich, die erhabenen Kunststoffelemente unmittelbar auf den im feuchten Zustand aufgelegten Filz aufzubringen, ohne daß eine undurchlässige Schicht zum Schutze des dazwischenliegenden Filzes aufgebracht wird, doch würde ein derartiges Produkt nur beschränkten kommerziellen Wert haben. Allermindestens wird gewöhnlich eine Dekorbeschichtung aufgebracht, selbst wenn das Endprodukt zu Schutzzwecken mit einer verschleiß- widerstandsfähigen Schicht zu versehen ist.The chosen substrate should be covered with a suitable impermeable Fabric to be coated. It is possible that raised plastic elements directly on the wet Applied felt condition without a impermeable layer to protect the intermediate Felt is applied, but would be such a product have limited commercial value. At least a decorative coating is usually applied, even if the end product is protected with a wear- resistant layer is to be provided.
Gewöhnlich ist eine Glasmatte mit einer undurchlässigen Beschichtung, gewöhnlich einem Plastisol, herzustellen, das gegebenenfalls schäumbar sein kann, um die Matte zu imprägnieren und die Glasfasern abzudichten.Usually a glass mat is impervious To produce a coating, usually a plastisol, which can optionally be foamable to impregnate the mat and seal the glass fibers.
Die Beschichtung, die verwendet werden muß, kann somit einfach sein, wie z. B. ein Abdichtungsmittel für einen im feuchten Zustand aufgelegten Filz oder komplex, wie z. B. ein aus mehreren Schichten bzw. Elementen aufgebauter Körper. In allen Fällen muß die undurchlässige Beschichtung die Qualität einer verschleißwiderstandsfähigen Schicht aufweisen, das heißt sie muß der Abnützung, der ein Bodenbelag normalerweise ausgesetzt ist, standhalten. Die Durchführung der Erfindung ist nicht an eine konkrete undurchlässige Beschichtung gebunden. Dem Fachmann sind viele Beschichtungen und Beschichtungsmethoden bekannt, die auch zur Durchführung der Erfindung verwendet werden können. Dazu zählen schäumbare und nicht schäumbare Plastisole, Harztrockenmischungen, das Aufbringen von Auflagen mit Hilfe von Schablonen usw.The coating that must be used can thus be simple, such as B. a sealant for a damp felt or complex, e.g. B. one made up of several layers or elements Body. In all cases, the impermeable coating the quality of a wear-resistant layer have, that is, it must be the wear of a flooring normally exposed to withstand. The implementation the invention is not limited to a specific impermeable Coating bound. Many coatings are known to the person skilled in the art and coating methods known, too can be used to carry out the invention. These include foamable and non-foamable plastisols, Resin dry mixtures, the application of pads with Help of stencils etc.
Die Beschichtung sollte jedoch für das darauf aufgebrachte Material undurchlässig sein, so daß das aufgebrachte thixotrope Material auf der Oberfläche bleibt, damit die erhabenen Elemente gebildet werden können.However, the coating should be for the applied on it Material impermeable, so that the applied thixotropic material remains on the surface so the raised elements can be formed.
Auf der undurchlässigen Beschichtung werden die erhabenen Elemente dadurch erzeugt, daß man Kügelchen einer Feststoffteilchen enthaltenden pseudoplastischen thixotropen Flüssigkeit aufbringt. Die Beschichtung kann nach verschiedenen bekannten Methoden erfolgen. Mit gutem Erfolg ist jedoch der im nachfolgenden Beispiel beschriebene Siebdruck angewandt worden, obwohl dieser normalerweise zum Aufbringen von Druckfarben auf poröse Oberflächen dient.The raised ones are on the impermeable coating Elements produced by making beads of a solid particle containing pseudoplastic thixotropic Applying liquid. The coating can be different known methods. However, with good success the screen printing described in the following example has been used, although this is usually for application of printing inks on porous surfaces.
Die erhabenen Elemente können in beliebiger Form bzw. mit beliebigem Muster angeordnet werden, wobei jedoch geometrische Formen wie sich wiederholende Muster von erhabenen Kreisen, Quadraten, Rhomben und dergleichen sich als optisch wirksam erwiesen haben. Wie auch bei anderen Erzeugnissen auf diesem Gebiet, sollte die Zahl der Elemente pro Einheit für die wirksame Ausbildung einer verschleiß- widerstandsfähigen Oberfläche für den Belag vollkommen ausreichen. Die vertieften Bereiche zwischen den erhabenen haben sowohl dekorative als auch strukturelle Funktion wie zum Beispiel als Kanäle zur Ableitung von verschütteten Flßüssigkeiten usw.The raised elements can be in any shape or with any pattern, but geometric Shapes like repeating patterns of sublime Circles, squares, rhombuses and the like appear as have proven optically effective. As with other products in this area, the number of elements should per unit for the effective formation of a wear- resistant surface for the covering completely suffice. The recessed areas between the raised ones have both decorative and structural function like for example as channels to drain spilled material Liquids etc.
Die erhabenen Elemente überragen das darunterliegende Substrat um ca. 0,75 mm (0,003 Inch) bis 20,3 mm (0,08 Inch), vorzugsweise um 3,8 mm (0,015 Inch) bis 11,4 mm (0,045 Inch) und insbesondere um 7,6 mm (0,03 Inch). Außerdem sollten die erhabenen Elemente ca. 30 bis 80% der Gesamtfläche des Endproduktes abdecken, um eine wirksame verschleiß- widerstandsfähige Oberfläche zu gewährleisten, wobei der genaue Prozentanteil eine Funktion der Geometrie der erhabenen Elemente ist.The raised elements protrude from the underlying substrate about 0.75 mm (0.003 inches) to 20.3 mm (0.08 inches), preferably by 3.8 mm (0.015 inches) to 11.4 mm (0.045 inches) and especially by 7.6 mm (0.03 inches). Besides, should the raised elements approx. 30 to 80% of the total area of the end product to ensure effective wear and tear to ensure resilient surface, the exact percentage a function of the geometry of the sublime Elements is.
Die Erfindung wurde durch die Kombination eines undurchlässig beschichteten Substrats mit den rheologischen Eigenschaften des aufgebrachten Kunststoffs ermöglicht. Bei einer Beschichtungstechnik, bei der zum Beispiel ein Drehsieb verwendet wird, kann ein pseudoplastisches thixotropes Material auf das beschichtete Substrat in einer Dicke aufgebracht werden, welche die Dicke übersteigt, mit der gewöhnliche Druckfarben aufgebracht werden. Aufgrund der Eigenschaften des Materials kann der seitliche Austrieb in Grenzen gehalten oder überhaupt vermieden werden.The invention was made impermeable by the combination of one coated substrate with the rheological properties of the applied plastic allows. At a coating technology in which, for example, a rotary screen used can be a pseudoplastic thixotropic Material applied to the coated substrate in a thickness which exceeds the thickness with the ordinary Printing inks are applied. Due to the Properties of the material can be driven out laterally Limits are kept or avoided at all.
Thixotrope Stoffe sind Stoffe, die ein doppeltes rheologisches Verhalten zeigen, das heißt hohe Viskosität bei geringer Scherbeanspruchung und geringe Viskosität bei hoher Scherbeanspruchung.Thixotropic substances are substances that have a double rheological Show behavior, that means high viscosity at low Shear stress and low viscosity at high Shear stress.
Pyrogenes und ausgefälltes SiO₂ sind wohl die am häufigsten verwendeten Thixotropiermittel, obwohl auch verschiedene andere anorganische und organische Stoffe als wirksam bekannt sind, wie z. B. solche anorganischen Stoffe, wie feinverteilte organophile Tone und organische Stoffe, wie hochsubstituierte Sorbatole oder Calcium-organische Komplexe. Im nachfolgenden Beispiel hat sich die Verwendung von pyrogener Kieselsäure (wie sie unter der Handelsbezeichnung Aerosil 200 der Firma Degussa Company im Handel erhältlich ist) als günstig erwiesen.Pyrogenic and precipitated SiO₂ are probably the most common Thixotropic agents used, although different other inorganic and organic substances as effective are known, such as B. such inorganic substances as finely divided organophilic clays and organic substances, such as highly substituted sorbatols or calcium-organic complexes. In the example below, the usage has been of fumed silica (as under the trade name Aerosil 200 from Degussa Company on the market is available) proved to be cheap.
Die Menge dieses der Harzpaste zugesetzten Materials bestimmt die thixotrope Natur des erhaltenen Systems und dessen Viskositäten bei den verschiedenen Schergeschwindigkeiten. Diese Eigenschaften bestimmen auch den seitlichen Austrieb des in Form von erhabenen Elementen auf das Substrat aufgebrachten Plastisols. Viskosität und Schergeschwindigkeit des thixotropen Plastisolmaterials stehen zueinander in Beziehung. Die Viskosität des thixotropen Materials wird daher gemessen, um den gewünschten seitlichen Austrieb des aufgebrachten Materials zu gewährleisten.The amount of this material added to the resin paste is determined the thixotropic nature of the system obtained and its viscosities at the different shear rates. These properties also determine the side Expulsion of the in the form of raised elements on the Plastisol applied to the substrate. Viscosity and shear rate of the thixotropic plastisol material in relation to each other. The viscosity of the thixotropic Material is therefore measured to the desired lateral To ensure expulsion of the applied material.
Die Viskosität, gemessen mit einem Brookfield-Viskosimeter unter Verwendung einer Spindel Nr. 6 bei 20 Umdrehungen pro Minute, liegt im Bereich von 8 bis 16 Pa · s (80 bis 160 Poise). Sie wird durch Variieren der zugegebenen Menge an Weichmacher oder eines anderen geeigneten, die Viskosität herabsetzenden Mittels eingestellt.The viscosity, measured with a Brookfield viscometer using a No. 6 spindle at 20 revolutions per Minute, is in the range of 8 to 16 Pa · s (80 to 160 Poise). It is made by varying the amount added Plasticizer or other suitable, the viscosity reducing agent set.
Als thixotrope Substanzen können erfindungsgemäß verschiedene Harzmaterialien verwendet werden und umfassen beliebige geeignete Harzplastisole. Bei dem nachfolgenden Beispiel erwies sich die Verwendung von Polyvinylchloridharzen als günstig.According to the invention, various thixotropic substances can be Resin materials are used and include any suitable resin plastisols. In the example below the use of polyvinyl chloride resins proved to be Cheap.
Um für die Ausführung der Erfindung brauchbar zu sein, muß der thixotrope Stoff in einer ausreichenden Menge vorliegen, damit das Harzsystem unter Scherbeanspruchung plastisch bleibt, die pseudoplastischen Eigenschaften aber sofort verliert, wenn die Scherkraft entfernt wird.In order to be useful for the practice of the invention the thixotropic substance is present in a sufficient amount, thus the resin system plastic under shear stress remains, but the pseudoplastic properties immediately loses if the shear force is removed.
Das Diagramm in Fig. 3, das mit Hilfe eines Haake RV-1 Viskosimeters erstellt wurde, zeigt die pseudoplastischen Eigenschaften des Materials.The diagram in Fig. 3, which was created using a Haake RV-1 viscometer, shows the pseudoplastic properties of the material.
Aus der Darstellung geht hervor, daß der thixotrope Stoff, ein aufgeschlämmtes PVC-Plastisol, bei geringer Scherbeanspruchung hohe Viskosität und bei hoher Scherbeanspruchung geringe Viskosität zeigt.The illustration shows that the thixotropic substance, a slurried PVC plastisol with low shear stress high viscosity and high shear stress shows low viscosity.
Obwohl der thixotrope Stoff selbst auf dem Endprodukt eine verschleißwiderstandsfähige Schicht bildet, werden die Abriebeigenschaften einer solchen verschleißwiderstandsfähigen Schicht durch Zugabe von Feststoffteilchen wesentlich verbessert. Solche Teilchen können ein organisches Material, wie Gummi, oder ein Kunststoff, wie Vinyl, oder ein anorganisches Material, wie Quarz oder dergleichen sein. Diese Teilchen können transparent oder beschichtet oder etwas gefärbt sein, wie beispielsweise bekannte harzbeschichtete Sande.Although the thixotropic substance itself is one on the end product wear-resistant layer forms the abrasion properties such a wear-resistant Layer by adding solid particles essential improved. Such particles can be organic Material, such as rubber, or a plastic, such as vinyl, or an inorganic material such as quartz or the like be. These particles can be transparent or coated or something colored, such as known resin-coated Sands.
Für die erfindungsgemäßen Zwecke sollten die Teilchen eine geeignete Größe aufweisen, um ein Sieb Nr. 10 nach der US-Standard-Siebreihe, das heißt ein Sieb mit einer Maschenweite von ca. 2,0 mm zu passieren, auf einem 200-Mesh-Sieb (nach US-Standard) mit einer Maschenweite von etwa 70 µm aber zurückzubleiben. Bevorzugte Ergebnisse wurden jedoch mit Teilchen erzielt, die ein 25-Mesh-Sieb (nach US-Standard) mit einer Maschenweite von etwa 600 µm passieren, auf einem 50-Mesh-Sieb (nach US-Standard) mit einer Maschenweite von etwa 250 µm aber zurückbleiben. Die Feststoffteilchen haben eine Mohs-Härte von 7 bis 9, vorzugsweise von ca. 7.For the purposes of the invention, the particles should be a are of a suitable size to fit a No. 10 sieve US standard sieve row, i.e. a sieve with a mesh size of about 2.0 mm to pass on a 200 mesh sieve (according to the US standard) with a mesh size of approximately 70 µm but to remain. Preferred results have been however achieved with particles that a 25 mesh sieve (after US standard) with a mesh size of about 600 µm happen on a 50 mesh sieve (according to US standard) a mesh size of about 250 microns remain. The Solid particles have a Mohs hardness of 7 to 9, preferably from approx. 7.
Eine 487,7 m (1600 Fuß) lange Rolle einer 4 m breiten Glasfasermatte der Fa. Schuller Company, wurde mit 500 g/m² eines Plastisols nachstehender Zusammensetzung gesättigt und in Kontakt mit einer ölgefüllten, auf 143 bis 146°C (290 bis 295°F) vorgewärmten Trommel geliert.A 487.7 m (1600 foot) roll of a 4 m wide Glass fiber mat from Schuller Company, was at 500 g / m² a plastisol of the following composition saturated and in contact with an oil-filled, at 143 to 146 ° C (290 up to 295 ° F) preheated drum.
Danach wurde die glatte Oberfläche der mit Plastisol gesättigten Matte mit 380 g/m² Plastisol der nachfolgenden Zusammensetzung beschichtet und geliert in Kontakt mit einer zweiten ölgefüllten und auf 141 bis 143°C (285 bis 290°F) vorgewärmten Trommel, um eine undurchlässige Beschichtung mit der Qualität einer verschleißwiderstandsfähigen Schicht zu erhalten.After that, the smooth surface became saturated with plastisol Mat with 380 g / m² plastisol of the following Composition coated and gelled in contact with a second oil-filled one and heated to 141 to 143 ° C (285 to 290 ° F) preheated drum to create an impermeable coating with the quality of a wear-resistant To get layer.
Ein Feststoffteilchen enthaltendes Plastisol der nachfolgenden Zusammensetzung wurde im Siebdruckverfahren in Form eines regelmäßigen geometrischen Musters auf die Oberfläche der gelierten undurchlässigen Beschichtung aufgebracht. A plastisol containing solid particles of the following Composition was shaped using the screen printing process a regular geometric pattern on the surface the gelled impermeable coating.
Die Viskosität des obigen mit Feststoffteilchen durchsetzten Plastisols muß im Bereich von 8 bis 16 Pa · s (80 bis 160 Poise) liegen, um das gewünschte Resultat zu erhalten. Die Viskosität wird durch Variieren der Menge des Weichmachers TXIB eingestellt.Mix the viscosity of the above with solid particles Plastisol must be in the range of 8 to 16 Pa · s (80 to 160 poise) to obtain the desired result. The viscosity is determined by varying the amount of plasticizer TXIB set.
Das bedruckte Plastisol wurde dann geliert und geschmolzen, indem man es 2 Minuten durch einen Heißluftofen, dessen Temperatur bei etwa 199°C (390°F) gehalten wurde, führte.The printed plastisol was then gelled and melted, by passing it through a convection oven for 2 minutes Temperature was maintained at about 199 ° C (390 ° F).
Der erhaltene Verbundkörper hatte regelmäßig angeordnete erhabene Elemente, die ein in Deckung geprägtes Dekor simulieren und durchgehend eine praktisch homogene Dispersion von Feststoffteilchen enthalten. The composite body obtained had regularly arranged ones raised elements that simulate a cover embossed and a practically homogeneous dispersion throughout of solid particles included.
Es ist möglich, das vorliegende Produkt auch mit einer ebenen Oberfläche auszubilden.It is possible to use the present product with a to form a flat surface.
Das vorliegende Produkt wird auf dieselbe Weise wie das Produkt von Beispiel 1 mit dem Unterschied hergestellt, daß vor dem Schmelzen des Produkts noch eine zusätzliche Beschichtung aufgebracht wird. Nach dem Gelieren der erhabenen Elemente, wird auf die gesamte Oberfläche derselben eine Beschichtung aus dem obigen undurchlässigen Beschichtungsmaterial aufgebracht, um die vertieften Bereiche rund um die erhabenen Elemente auszufüllen. Wenn die graue Pigmentpaste von dfem undurchlässigen Beschichtungsmaterial entfernt wird, ist die die vertieften Bereiche ausfüllende Beschichtung transparent, und die Produkte von Beispiel 1 und Beispiel 2 sehen praktisch gleich aus, mit dem Unterschied, daß das Produkt von Beispiel 2 eine ebene Oberseite aufweist.This product is made in the same way as that Product of Example 1 with the difference that an additional coating before melting the product is applied. After gelling the sublime Elements, will cover the entire surface of the same a coating of the above impermeable coating material applied to the recessed areas to fill in around the sublime elements. If the gray pigment paste from impervious coating material is removed, which is the recessed areas filling coating transparent, and the products of Example 1 and Example 2 look practically the same, with the difference that the product of Example 2 is a flat one Has top.
Claims (12)
- a) ein Substrat
- b) eine undurchlässige Beschichtung, die mit wenigstens einer Oberfläche des Substrats verbunden ist, und
- c) auf der Beschichtung selektiv angeordnete, einen thixotropen Kunststoff mit Feststoffteilchen darstellende erhabene Elemente mit einer Dicke von ca. 0,75 mm (0,003 Inch) bis 20,3 mm (0,080 Inch) umfaßt, wobei der thixotrope Kunststoff wenigstens ein Thixotropiermittel, ausgewählt aus der Gruppe pyrogene Kieselsäuren, ausgefällte Kieselsäuren, feinpulverisierte organiphile Tone, in hohem Maße substituierte Sorbatole und Calcium-organische Komplexe, enthält.
- a) a substrate
- b) an impervious coating bonded to at least one surface of the substrate, and
- c) on the coating selectively arranged raised elements which represent a thixotropic plastic with solid particles and have a thickness of approximately 0.75 mm (0.003 inches) to 20.3 mm (0.080 inches), wherein the thixotropic plastic is selected at least one thixotropic agent from the group of pyrogenic silicas, precipitated silicas, finely powdered organiphilic clays, highly substituted sorbatols and calcium-organic complexes.
- a) auf wenigstens eine Oberfläche eines Substrats eine undurchlässige Beschichtung aufbringt,
- b) auf das beschichtete Substrat mit einer Siebdruckvorrichtung selektiv erhabene Elemente aufdruckt, die einen thixotropen Kunststoff darstellen, der Feststoffteilchen enthält, wobei die erhabenen Elemente in einem solchen Abstand voneinander angeordnet werden, daß dazwischen vertiefte Bereiche entstehen und die erhabenen Elemente vorzugsweise eine Höhe von 38 mm (0,15 Inch) bis 11,4 mm (0,045 Inch) haben und
- c) das auf diese Weise gebildete Material verschmilzt.
- a) applying an impermeable coating to at least one surface of a substrate,
- b) selectively printing raised elements on the coated substrate using a screen printing device, which represent a thixotropic plastic containing solid particles, the raised elements being arranged at such a distance from one another that recessed areas are formed between them and the raised elements are preferably 38 in height mm (0.15 inch) to 11.4 mm (0.045 inch) and
- c) the material thus formed melts.