DE1907071A1 - Foam - laminated fabrics - Google Patents

Foam - laminated fabrics

Info

Publication number
DE1907071A1
DE1907071A1 DE19691907071 DE1907071A DE1907071A1 DE 1907071 A1 DE1907071 A1 DE 1907071A1 DE 19691907071 DE19691907071 DE 19691907071 DE 1907071 A DE1907071 A DE 1907071A DE 1907071 A1 DE1907071 A1 DE 1907071A1
Authority
DE
Germany
Prior art keywords
paste
plasticizer
thermoplastic
textile
textile goods
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19691907071
Other languages
German (de)
Inventor
Schabel Dr Joachim
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Actega DS GmbH
Original Assignee
DS Chemie GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DS Chemie GmbH filed Critical DS Chemie GmbH
Priority to DE19691923406 priority Critical patent/DE1923406A1/en
Priority to DE19691907071 priority patent/DE1907071A1/en
Publication of DE1907071A1 publication Critical patent/DE1907071A1/en
Pending legal-status Critical Current

Abstract

Thermoplastics paste containing a plasticizer is applied to one side of the fabric and gelled by heating to a permanent porous structure. The paste is a PVC paste-containing a monomeric polymerisable plasticizer which polymerises at the gelling temp. of the PVC and becomes hard. Pref. the paste also contains a blowing agent which is decomposed below this polymerisation temp. The fabric can be a fibre web and the foam layer >5 mm thick.

Description

Verfahren zum Herstellen von schaumstoffbeschichteten Textilwaren und danach hergestellte Belagplatte.procedure for the manufacture of foam-coated textile goods and subsequently manufactured covering panels.

Die Erfindung bezieht sich auf ein Verfahren zum Herstellen von schaumstoffbeschichteten Textilwaren, wobei auf die Textilware einseitig eine weichmacherhaltige Thermoplastpaste aufgebracht und unter Erhitzung giliert wird, die eine bleibende Porenstruktur aufweist..The invention relates to a method for producing foam-coated Textile goods, with a thermoplastic paste containing plasticizer on one side of the textile goods is applied and gelled under heating, which has a permanent pore structure ..

Derartige Verfahren sind zur Herstellung von Kunstleder und flexiblen Bodenbelägen bekannt. Die danach hergestellten Erzeugnisse sind stets verhältnismässig flexibel sowie auch elastisch. Sie lassen sich mithin nur in dem Umfang verwenden, indem die Formstabilität keine nennenswerte Bedeutung hat.Such methods are for making synthetic leather and are flexible Flooring known. The products manufactured according to this are always proportionate flexible as well as elastic. They can therefore only be used to the extent that in that the dimensional stability has no significant significance.

Auf diese Weise beschichtete Teppiche finden daher inabeP sondere als Auslegeware Verwendung, die mit dem Boden in geeigneter Form verbunden wird. Durch die Verwendung derartiger Bodenbeläge wird unter anderem auch eine hervorra gende Schalldämmung sowie Wärmeisolierung erzielt.Carpets coated in this way are therefore particularly popular Use as carpeting, which is connected to the floor in a suitable manner. By using such floor coverings, among other things, an excellent low soundproofing and thermal insulation achieved.

Der Erfindung liegt die ELuEgabe zu Grunde, ein Verfahren der einleitend beschriebenen Art, eine zu dessen Durchführung geeignete Thermoplastpaste sowie danach bzw. damit beschich te Textilwaren zu schaffen, die sich in erheblich erweitertem Ausmasse verwenden lassen, um insbesondere ihre gute Schall-und Wärmeisolierung zu nutzen. Zugleich sollen dabei die hochwertigen Eigenschaften der textilen Seite der Ware, die aus einem Gewebe, einem Gewebe mit darin eingebundenen Florfäden oder auch aus einem Faservlies bestehen kann, besser als bislang zur Geltung kommen. Erfindungsgemäss wird dies dadurch ermöglicht, dass als Thermoplastpaste eine einen monomeren, polymerisierbaren sowie im Bereich der Geliertemperatur des Thermoplasten polymerisierend erhärtenden Weichmacher enthaltende Polyvinylchloridpaste verwendet wird.The invention is based on the ELuEgabe, a method of introductory type described, a suitable thermoplastic paste for its implementation and thereafter or so beschich te to create textile goods that are significantly expanded Let dimensions use especially their good sound and heat insulation to use. At the same time, the high-quality properties of the textile side are intended the goods, which are made of a fabric, a fabric with integrated pile threads or can also consist of a fiber fleece, come into their own better than before. According to the invention this is made possible by the fact that the thermoplastic paste is a monomeric, polymerizable and in the range of the gelling temperature of the thermoplastic Polyvinyl chloride paste containing polymerizing hardening plasticizers is used will.

Auf diese Weise kommt man zu einem plattenähnlichen Erzeugnis, dessen Beschichtung eine ausgehärtete und sehr feste Schaumstruktur aufweist. Man kann derartige Platten als Tafeln aufteilen und sehr unterschiedlichen Verwendungszwecken zuführen. So ist z.B. die Aufteilung in kleinere Tafeln möglich, die durch blosses Aneinanderlegen einen hervorragenden maß-und formbeständigen Bodenbelag ergeben, ohne dass es besonderer Befestigungsmittel bedarf. Weiterhin lassen sich derartige Platten, hinreichende Beschichtungsstärke vorausgesetzt, für die Verkleidung von Türflügeln verwenden, so dass die von derartigen Türen abgeschlossenen Räume schalldicht werden. Besondere Vorteile ergeben sich bei der Verwendung der erfindungsgemäss erhaltenen Platten als Wandvertäfelung. Zu diesem Zwecke kann man sie einerseits mit einer normalen Wand durch z.B.In this way one arrives at a plate-like product, its Coating has a cured and very solid foam structure. One can Divide such panels as panels and very different uses respectively. For example, it is possible to divide them into smaller panels, which can be separated by simple Laying them next to one another results in an excellent dimensionally and dimensionally stable floor covering, without the need for special fasteners. Furthermore, such Plates, provided that the coating is sufficiently thick, for cladding Use door leaves so that the rooms enclosed by such doors are soundproof will. Particular advantages result from the use of the invention obtained panels as wall paneling. For this purpose you can use them on the one hand with a normal wall through e.g.

Kleben, Nageln oder Schrauben verbinden und verbessert somit deren Warme und Schallisolierung, wobei.gleichzeitig eine besonders hochwertige Wandverkleidung entsteht. Andererseits kann man aber auch auf die herkömmliche ausfahrung der tragenden oder nicht tragenden Wände mit Mauerwerk verzichten und diese lediglich als eine Rahmenkonstruktion ausführen, die z.B. einen oberen durchlaufenden Träger, gegebenenfalls Pfosten und in dem Falle, in dem auch horizontal angreifende Kräfte abzufangen sindv Diagonalstäbe aufweist. Eine derartige Konstruktion lAst sich dann sehr leicht beidseitig mit den erfindungsgemässen Platten, die auf entsprechende, gegebenenfalls geschosshohe Tafellänge zugeschnitten sind, verkleiden.Gluing, nailing or screwing together and thus improves their Warm and sound insulation, at the same time a particularly high-quality wall cladding arises. On the other hand, you can also rely on the conventional experience of the load-bearing or dispense with non-load-bearing walls with masonry and use these merely as one Execute frame construction, e.g. an upper continuous beam, if necessary Posts and in the case in which horizontally acting forces are to be intercepted v Has diagonal bars. Such a one Construction can then be done very lightly on both sides with the plates according to the invention, which are if necessary, floor-to-ceiling panels are cut to size.

Der sonst erforderliche Aufwand für das Ziegélmauerwerk, dess en Verputz und die Tapezierung entfallen damit.The otherwise required effort for the brickwork and plastering and there is no need for wallpapering.

Für die Zwecke der Wärmeisolation kennt man zwar schon Styropor-oder Polyurethan-Schäume, doch haben diese gegenüber den erfindungsgemäss hergestellten Platten den Nachteil, dass sie zu weich sein würden, um stabile Wände damit zu gestalten.For the purpose of thermal insulation, one already knows Styrofoam or Polyurethane foams, however, have compared to those produced according to the invention Panels have the disadvantage that they would be too soft to be used to create stable walls.

Eine weitere Anwendungsmöglichkeit, bei der gleichfalls die guten Wärme- und Schallisolationseigenschaften genutzt werden und auch die Textilseite der Platten zur Wirkung gelangt, besteht in der Innenauskleidung von Decken. Dadurch kann ebenfalls auf den Verputz und dergleichen verzichtet werden, da sich die entsprechend zugeschnittenen Tafeln unmittelbar mit den Deckenträgern verbinden lassen.Another application, which also has the good ones Heat and sound insulation properties are used and also the textile side of the panels comes into effect, consists in the inner lining of ceilings. Through this can also be dispensed with plastering and the like, since the accordingly Have the cut-to-size panels connected directly to the ceiling beams.

Gegenüber Holztafeln, an deren Stelle die erfindungsgemäss hergestellten Platten mithin in erheblichem Ausmass treten können, besteht neben der guten Wärme-und Schallisolierung sowie der hochwertigeren Textilseite noch der Vorteil, dass es nicht zu einem Verziehen kommen kann, dass die Festigkeit unabhängig von der Richtung ist und dass keine Feuchtigkeit aufgenommen werden kann,was wiederum vor allem für die Innenauskleidung von Äussenwänden oder bei gelegentlichen Wasserschäden erhebliche Bedeutung hat.Compared to wooden panels, in their place the one produced according to the invention Plates can therefore occur to a considerable extent, in addition to the good warmth and Soundproofing as well as the higher quality textile side still has the advantage that it No warping can occur, that the strength regardless of the direction is and that no moisture can be absorbed, which in turn is mainly for the inner lining of outer walls or, in the case of occasional water damage, considerable Has meaning.

Zweckmässig wird der PVC-Paste in an sich bekannter Weise ein bei Erhitzung Treibgas abspaltendes Treibmitte zugesetzt, dessen Zersetzungstemperatur in diesem Falle kleiner als die Poiymerisierungstemperatur des monomeren Weichmachers ist.The PVC paste is expediently incorporated in a manner known per se Heating Propellant-releasing propellant added, its decomposition temperature in this case lower than the polymerization temperature of the monomeric plasticizer is.

Überraschenderweise kommt es bei dem erfindungsgemässen Verfahren praktisch nicht mehr zu der sonst bei PVC-SchAumen bestehenden Gefahr, dass sich die Unebenheiten der Textilware, auf die die PVC-Paste aufgebracht wurde, nach der Gelierung in vielfacher Yergrösserung auf der Aussenfläche der Beschichtungsseite abzeichnen. Vielmehr behält die Aussenfläche der Beschichtung nahezu unverändert das Aussehen bei, das sie durch das Aufrakeln der Paste angenommen hat. Diese Erscheinung ist möglicherweise darauf zurückzuführen, dass bei der wie üblich angewendeten Art der Hitze zuführung die Aussenfläche der Beschichtungsseite bereits erhärtet bevor es zur Auswirkung der Unebenheiten der Textilstruktur kommen kann. Aus Gründen der besseren Verankerung der Paste mit den Fäden bzw. Fasern der Textilware ist es jedoch angebracht, die Thermoplastpaste zweistuflg aufzubringen, wobei sie zunächst in einer dUnnen9Sicht unter Druck auf die Textilware glättend aufgetragen. unmittelbar danach in einer stärkeren Schicht glättend aufgetragen und dann unter Erhitzung geliert wird.Surprisingly, it occurs with the method according to the invention practically no longer compared to what is otherwise used with PVC foams existing danger, that the unevenness of the textile goods to which the PVC paste was applied, after gelation in multiple enlargements on the outer surface of the coating side sign off. Rather, the outer surface of the coating remains almost unchanged the look it took on when the paste was applied. This appearance is possibly due to the fact that, as usual, Art the outside surface of the coating side has already hardened before the heat is supplied the unevenness of the textile structure can have an effect. Because of However, it is better anchoring of the paste with the threads or fibers of the textile goods appropriate to apply the thermoplastic paste in two stages, initially in Applying a thin layer of pressure to the textile goods under pressure. right away then applied in a thicker layer to smooth it out and then with heating is gelled.

Da in der Regel die Beschichtung erheblich stärker als bei dem bekannten Verfahren gewählt werden muss, ist es weiterhin angebracht, der Thermoplastpaste in an sich bekannter Weise anorganische Stoffe, die sonst als Füllstoffe dienen, mit der Maßgabe zuzusetzen, dass hierdurch die Thermoplastpaste -tiixotrope Eigenschaften annimmt. Somit wird verhindert, dass ein z.B. 10 bis 20 mm starker Auftrag seitlich von der Textilware heruntertropft.As a rule, the coating is considerably stronger than with the known Method must be chosen, it is still appropriate to use the thermoplastic paste In a known manner, inorganic substances that otherwise serve as fillers, with the proviso that this results in the thermoplastic paste -tiixotropic properties accepts. This prevents, for example, a 10 to 20 mm thick application from being applied laterally dripping down from the textile.

Zu einembesonders hochwertigen Erzeugnis kommt man, wenn als Textilware ein Grundgewebe mit einer darin eingebundenen Florware verwendet wird, wobei die Beschichtung auf der Grundgewebeseite erfolgt. Die Florware ist dann dem Raum zugekehrt und gibt nicht nur dem Boden, sondern auch den Wänden, Türen und gegebenenfalls der Decke eine teppichähnliche Beschaffenheit. Für besondere Anwendungsfälle ist es uedoEh gleichfalls möglich, anstelle einer gewebten oder gewirkten Textilware ein Faservliess, z.B. eine Filzware, zu verwenden.You get a particularly high-quality product if it is a textile product a base fabric with a pile fabric bound therein is used, the Coating takes place on the base fabric side. The pile fabric is then facing the room and gives not only to the floor but also to the walls, doors and where appropriate the ceiling has a carpet-like texture. For special applications is it is also possible, instead of a woven or knitted textile product to use a fiber fleece, e.g. a felt fabric.

Im Anschluss an die Erhitzung wird die beschichtete Textilware bei geradflächiger Unterstützung abgekühlt und mittels luftgekühlter Schneidwerkzeuge auf ihre vorgesehenen Tafelmaße geschnitten. Die geradflächige Unterstüzung gewährleistet die Beibehaltung nahezu ebener Erzeugnisse. Zwar besitzen die Platten je nach ihrer Beschichtungsstärke eine sehr begrenzte Biegemöglichkeit, doch würde ein stärkeres Verziehen während der Abkühlung nur sehr schwer wieder auszugleichen sein. Luftgekühlte Schneidwerkzeuge, wie zum Beispiel luftgekühlte Sägen oder in Luft rotierende Trennmesser, haben gegenüber wassergekühlten den Vorteil, dass von der Textilware keine Nässe aufgenommen wird.Following the heating, the coated textile product is at straight support and cooled using air-cooled cutting tools cut to their intended board dimensions. The straight-surface support is guaranteed the retention of nearly flat products. Although the plates have depending on their Coating thickness a very limited bending possibility, but would be a stronger one Warping during cooling can be very difficult to compensate for. Air-cooled Cutting tools, such as air-cooled saws or cutting blades rotating in air, have the advantage over water-cooled that the textile goods do not get wet is recorded.

Die nach dem erfindungsgemässen Verfahren hergestellten Belagplatten haben vorteilhaft eine Dicke ihrer einseitigen Hartschaumschicht von mehr als 5 mm. Dadurch lassen sich die für Bauzwecke erforderlichen Schall- und W8rmeisolierungswerte erzielen. Das Verlegen der Belagplatten wird dadurch erleichtert, das-s wenigstens zwei ihrer Schmalseiten schräg verlaufen. Dadurch überdecken sich die Schaumschichten zweier aneinander angrenzender Belegplatten, während die Textilseiten etwa stumpf aneinander stossen. Die Schrägflächen bieten nicht nur für eine Verklebung eine bessere Angriffsmöglichkeit, sondern gewährleisten zugleich, dass sich keine Schall-Leitbrücken oder Wärmeleitbrücken bilden können. Zudem ist hierdurch auch die Verlegung in Ecken möglich. Wenn man rechtwinklige Tafeln herstellt, ist es überdies angebracht, dass bei jeder Tafel ihre aneinander angrenzenden Schmalseiten schräg verlaufen.The covering panels produced by the process according to the invention advantageously have a thickness of their one-sided rigid foam layer of more than 5 mm. This enables the sound and heat insulation values required for building purposes to be achieved achieve. The laying of the tiles is made easier, at least that two of its narrow sides run obliquely. This causes the foam layers to overlap two adjacent panels, while the textile pages are roughly blunt butt against each other. The inclined surfaces not only offer one for gluing better possibility of attack, but also ensure that there are no sound guide bridges or can form thermal bridges. In addition, this also makes it easier to lay in corners possible. In addition, when making rectangular panels, it is appropriate that on each board, their adjacent narrow sides run obliquely.

Die Thermoplastpaste zur DurchfüErung des erfindungsgemässen Verfahrens besteht erfindungegemäss aus Riyvinylchlorid, dem zwischen 5 und 30 Gewichtsprozente eines in Endstellung Doppelbindungen aufwesenden Weichmachers zugesetzt sind. Derartige, zur Polymerisierung neigende Weichmacher können zum Beispiel Diallylphtalat, Acrylsäureester und Methacrylsäureester sein.The thermoplastic paste for carrying out the method according to the invention consists of Riyvinylchlorid, which is between 5 and 30 percent by weight according to the invention a plasticizer present in the end position of double bonds are added. Such, Plasticizers that tend to polymerize are, for example, diallyl phthalate and acrylic acid esters and methacrylic acid esters.

Als Treibmittel enthalten sie vorteilhaft an sich bekanntes Azodicarbonamid, auf dessen Zersetzungstemperatur die Polymerisierungstemperatur des Weichmachers durch Katalysatoren bzw. durch Inhibitoren eingestellt ist. Katalysatoren können allgemein organische Peroxyde sein, so zum Beispiel Tert.-butyl-peroxyd oder Benzoyl-Peroxyd. Als Inhibitor eignet sich zum Beispiel Di-tert.-Butyl-p-cresol. Die Zusätze des Treibmittels, des Katalysators bzw. Inhibitors bewegen sich in den üblichen Grenzen.As a propellant, they advantageously contain azodicarbonamide, which is known per se, its decomposition temperature is the polymerisation temperature of the plasticizer through catalysts or is set by inhibitors. Catalysts can generally be organic peroxides, for example tert-butyl peroxide or Benzoyl peroxide. Di-tert-butyl-p-cresol, for example, is suitable as an inhibitor. The additives of the propellant, the catalyst or inhibitor move in the usual limits.

Wciterhin enthält die erfindungsgemässe Thermoplastpaste noch vorteilhaft anorganische Zusätze, wie zum Beispiel Kaolin, Montmorillonit, Bentonite oder kollidoale Kieselsäure, um sie vor allem für stärkere Beschichtungen hinreichend thixotrop zu machen. Schliesslich können der Paste noch mit Vorteil Füllstoffe von kurzer Faserstruktur, wie Faserabfälle und trockenes Sägemehl zugesetzt werden.The thermoplastic paste according to the invention also advantageously contains wciterhin inorganic additives such as kaolin, montmorillonite, bentonite or collidoals Silica to make them sufficiently thixotropic, especially for thicker coatings close. Finally, the paste can still be used with fillers of short duration Fiber structure, such as fiber waste and dry sawdust are added.

Eine der erfindungsgemäss hergestellten Belegplatte ist in der Fig. 1 in Draufsicht und in der Fig. 2 im Schnitt wiedergegeben. One of the cover plates produced according to the invention is shown in FIG. 1 shown in plan view and in FIG. 2 in section.

In Fig. 1 erkennt man die dem Auge zugekehrte, schematisch dargestellte Gewebeseite 1 der Belegplatte. Die beiden, in der Eckante 2 aneinandergrenzenden Schmalseiten 3 und 4 sind schräg ausgeführt und besitzen eine der Neigung der gleichfalls schräg ausgeführten, in der Eckkante 5 aneinandergrenzenden Schmalseiten 6 und 7 komplementäre Neigung. Auf. diese Weise kann man beim Verlegen der Platte die beschriebene Fugendichte erzielen. In Fig. 1 you can see that facing the eye, shown schematically Fabric side 1 of the cover plate. The two adjoining each other in the corner edge 2 Narrow sides 3 and 4 are inclined and have the same inclination inclined narrow sides 6 and 7 adjoining one another in the corner edge 5 complementary inclination. On. this way you can do the one described when laying the plate Achieve joint density.

Der entsprechend der Schnittlinie II-II schematisch dargestellten Fig. 2 lässt sich entnehmen, wie die zu einem Hartschaum verfestigte Beschichtung 7'teilweise in das Gewebe 8 der Text ware eingedrungen ist und sich darin fest verankert hat Die Aussenfläche 9 der Beschichtung ist auch nach dem Gelieren und ScilMuman bemerkenswert glatt und zeigt nicht die llnæbenheiten sons-tiger Polyvinylchlorid-Beschichtungen, wenn diese ohne eine spezielle Grundierung des Grundgewebes 8 auf getragen wird. Man erkennt weiterhin die mit komplementärer Neigung ausgeführten Schmalseiten 4 und 6, dank welcher sich das beschriebene dichte Verlegen der Platten vornehmen lasst. The one shown schematically according to the section line II-II FIG. 2 shows how the coating solidified to form a hard foam 7 'the text has partially penetrated into the tissue 8 and is firmly anchored therein The outer surface 9 of the coating is also after gelling and ScilMuman remarkably smooth and does not show the smoothness other Polyvinyl chloride coatings, if they are used without a special primer Base fabric 8 is worn. You can still see those with a complementary tendency executed narrow sides 4 and 6, thanks to which the tight laying described of the plates.

Claims (9)

PatentansprücheClaims 1. Verfahren zum Herstellen von schaumstoffbeschichteter Textilware, wobei auf die Textilware einseitig eine weichmacherhaltige Thermoplastpaste aufgebracht und unter Erhitzung geliert wird, die eine bleibende Porenstruktur aufweist, dadurch gekennzeichnet, dass als Thermoplastpaste eine einen monomeren, polymerisierbaren sowie im Bereich der Geliertemperatur des Thermoplasten polymerisierend erhärtenden Weichmacher enthaltende Polyvinylchloridpaste verwendet wird.1. Process for the production of foam-coated textile goods, wherein a plasticizer-containing thermoplastic paste is applied to one side of the textile goods and is gelled under heating, which has a permanent pore structure, thereby characterized in that the thermoplastic paste is a monomeric, polymerizable as well as polymerizing hardening in the range of the gelling temperature of the thermoplastic Plasticizer-containing polyvinyl chloride paste is used. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die Polymnylchloridpaste in an sich bekannter Weise ein bei Erhitzung Treibgas abspaltendes Treibmittel zugesezt wird, deseen Zersetzungstemperatur kleiner als die Polymerisierungstemperatur des monomeren Weichmachers ist.2. The method according to claim 1, characterized in that the Polymnylchloridpaste a propellant which releases propellant gas when heated is added in a manner known per se the decomposition temperature is lower than the polymerization temperature of the monomeric plasticizer is. 3. Verfahren nach den Ansprüchen 1 und 2, dadurch gekennzeichnet, dass die Thermoplastpaste zweistufig aufgebracht wird, wobei sie zunächst in einer dünnen Schicht unter Druck auf die Textilware glättend aufgetragen, unmittelbar danach in einer stärkeren Schicht glättend aufgetragen und dann unter Erhitzung geliert wird.3. The method according to claims 1 and 2, characterized in that that the thermoplastic paste is applied in two stages, initially in one Apply a thin layer under pressure to the textile product, smoothing it, immediately then applied in a thicker layer to smooth it out and then with heating is gelled. 4T Verfahren nach den Ansprüchen 1 bis 3, dadurch gekennsaichnet, dass der Thermoplastpaste in an sich bekannter Weise anorganische Stoffe mit der MaRgabe zugesetzt werden, dass sie thixotrop wird.4T method according to claims 1 to 3, characterized in that that the thermoplastic paste in a known manner inorganic substances with the Must be added that it becomes thixotropic. 5. Verfahren nach den Ansprüchen 1 bis 4, dadurch gekennzerchne t, dass als Textilware ein Grundgewebe mit einer darin eingebundenen Florware verwendet wird, wobei die 5. The method according to claims 1 to 4, thereby gekennzerchne t, that a base fabric with a pile fabric integrated into it is used as a textile product will, with the 6. Verfahren nach den Ansprüchen 1 bis 4, dadurch gekennzeichnet, dass als Textilware ein Faserflies verwendet wird, 6. The method according to claims 1 to 4, characterized marked that a fiber fleece is used as textile goods, 7. Verfahren nach den Ansprüchen 1 bis 6, dadurch gekennzeichnet, dass die beschichtete Textilware im Anschluss an die Erhitzung unter geradflächiger Unterstützung abgekühlt und mittels luftgekühlter Schneidwerkzeuge auf vorgesehene Tafelmasse geschnitten wird.7. Procedure according to claims 1 to 6, characterized in that the coated textile goods After the heating it is cooled with straight support and by means of air-cooled cutting tools is cut to the intended table mass. 8. Nach dem Verfahren eines oder mehrerer der Voransprüche hergestellte Belagplatte, dadurch gekennzeichnet, dass ihre einseitige Haftschaumschicht eine Dicke von mehr als 5 mm besitzt.8. Manufactured according to the method of one or more of the preceding claims Covering plate, characterized in that its one-sided adhesive foam layer is a Thickness greater than 5mm. 9. Belagplatte nach Anspruch 8, dadurch gekenezeichnet, das@ w@@i@s@ens zwei ihrer Schmalseiten sc@@ä@ verlaufen.9. Covering plate according to claim 8, characterized in that the @ w @@ i @ s @ ens two of its narrow sides run sc @@ ä @. L e e r s e i t eL e r s e i t e
DE19691907071 1969-02-13 1969-02-13 Foam - laminated fabrics Pending DE1907071A1 (en)