DE3439745C2 - - Google Patents
Info
- Publication number
- DE3439745C2 DE3439745C2 DE3439745A DE3439745A DE3439745C2 DE 3439745 C2 DE3439745 C2 DE 3439745C2 DE 3439745 A DE3439745 A DE 3439745A DE 3439745 A DE3439745 A DE 3439745A DE 3439745 C2 DE3439745 C2 DE 3439745C2
- Authority
- DE
- Germany
- Prior art keywords
- silicate
- mass
- filler
- component
- treated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Links
- 239000000945 filler Substances 0.000 claims description 19
- 239000000565 sealant Substances 0.000 claims description 9
- BPQQTUXANYXVAA-UHFFFAOYSA-N Orthosilicate Chemical compound [O-][Si]([O-])([O-])[O-] BPQQTUXANYXVAA-UHFFFAOYSA-N 0.000 claims description 8
- 239000000203 mixture Substances 0.000 claims description 7
- 229920001296 polysiloxane Polymers 0.000 claims description 6
- 239000003431 cross linking reagent Substances 0.000 claims description 4
- UQMGAWUIVYDWBP-UHFFFAOYSA-N silyl acetate Chemical class CC(=O)O[SiH3] UQMGAWUIVYDWBP-UHFFFAOYSA-N 0.000 claims description 4
- NKSJNEHGWDZZQF-UHFFFAOYSA-N ethenyl(trimethoxy)silane Chemical compound CO[Si](OC)(OC)C=C NKSJNEHGWDZZQF-UHFFFAOYSA-N 0.000 claims description 3
- 235000021355 Stearic acid Nutrition 0.000 claims description 2
- 239000003513 alkali Substances 0.000 claims description 2
- 235000012241 calcium silicate Nutrition 0.000 claims description 2
- CJZGTCYPCWQAJB-UHFFFAOYSA-L calcium stearate Chemical class [Ca+2].CCCCCCCCCCCCCCCCCC([O-])=O.CCCCCCCCCCCCCCCCCC([O-])=O CJZGTCYPCWQAJB-UHFFFAOYSA-L 0.000 claims description 2
- 239000000391 magnesium silicate Substances 0.000 claims description 2
- QIQXTHQIDYTFRH-UHFFFAOYSA-N octadecanoic acid Chemical compound CCCCCCCCCCCCCCCCCC(O)=O QIQXTHQIDYTFRH-UHFFFAOYSA-N 0.000 claims description 2
- OQCDKBAXFALNLD-UHFFFAOYSA-N octadecanoic acid Natural products CCCCCCCC(C)CCCCCCCCC(O)=O OQCDKBAXFALNLD-UHFFFAOYSA-N 0.000 claims description 2
- 150000004756 silanes Chemical class 0.000 claims description 2
- 239000008117 stearic acid Substances 0.000 claims description 2
- UKRDPEFKFJNXQM-UHFFFAOYSA-N vinylsilane Chemical compound [SiH3]C=C UKRDPEFKFJNXQM-UHFFFAOYSA-N 0.000 claims description 2
- YKTSYUJCYHOUJP-UHFFFAOYSA-N [O--].[Al+3].[Al+3].[O-][Si]([O-])([O-])[O-] Chemical compound [O--].[Al+3].[Al+3].[O-][Si]([O-])([O-])[O-] YKTSYUJCYHOUJP-UHFFFAOYSA-N 0.000 claims 2
- 229910052918 calcium silicate Inorganic materials 0.000 claims 1
- OYACROKNLOSFPA-UHFFFAOYSA-N calcium;dioxido(oxo)silane Chemical compound [Ca+2].[O-][Si]([O-])=O OYACROKNLOSFPA-UHFFFAOYSA-N 0.000 claims 1
- HCWCAKKEBCNQJP-UHFFFAOYSA-N magnesium orthosilicate Chemical compound [Mg+2].[Mg+2].[O-][Si]([O-])([O-])[O-] HCWCAKKEBCNQJP-UHFFFAOYSA-N 0.000 claims 1
- 229910052919 magnesium silicate Inorganic materials 0.000 claims 1
- 235000019792 magnesium silicate Nutrition 0.000 claims 1
- QTBSBXVTEAMEQO-UHFFFAOYSA-N Acetic acid Chemical compound CC(O)=O QTBSBXVTEAMEQO-UHFFFAOYSA-N 0.000 description 12
- -1 B. feldspar or Talc Chemical class 0.000 description 5
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 4
- 239000000463 material Substances 0.000 description 4
- 150000004760 silicates Chemical class 0.000 description 4
- 238000004381 surface treatment Methods 0.000 description 4
- 229910052782 aluminium Inorganic materials 0.000 description 3
- 238000006243 chemical reaction Methods 0.000 description 3
- 150000001875 compounds Chemical class 0.000 description 3
- 239000004971 Cross linker Substances 0.000 description 2
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 2
- 238000005299 abrasion Methods 0.000 description 2
- TZCXTZWJZNENPQ-UHFFFAOYSA-L barium sulfate Chemical compound [Ba+2].[O-]S([O-])(=O)=O TZCXTZWJZNENPQ-UHFFFAOYSA-L 0.000 description 2
- 239000003054 catalyst Substances 0.000 description 2
- 230000000694 effects Effects 0.000 description 2
- 239000010433 feldspar Substances 0.000 description 2
- 239000011159 matrix material Substances 0.000 description 2
- 239000000049 pigment Substances 0.000 description 2
- 239000004014 plasticizer Substances 0.000 description 2
- 238000007789 sealing Methods 0.000 description 2
- RMAQACBXLXPBSY-UHFFFAOYSA-N silicic acid Chemical compound O[Si](O)(O)O RMAQACBXLXPBSY-UHFFFAOYSA-N 0.000 description 2
- 235000012239 silicon dioxide Nutrition 0.000 description 2
- 239000000377 silicon dioxide Substances 0.000 description 2
- 230000006641 stabilisation Effects 0.000 description 2
- 238000011105 stabilization Methods 0.000 description 2
- 239000000758 substrate Substances 0.000 description 2
- 239000000454 talc Substances 0.000 description 2
- 229910052623 talc Inorganic materials 0.000 description 2
- 238000004073 vulcanization Methods 0.000 description 2
- 239000010456 wollastonite Substances 0.000 description 2
- 229910052882 wollastonite Inorganic materials 0.000 description 2
- 230000006750 UV protection Effects 0.000 description 1
- ISKQADXMHQSTHK-UHFFFAOYSA-N [4-(aminomethyl)phenyl]methanamine Chemical compound NCC1=CC=C(CN)C=C1 ISKQADXMHQSTHK-UHFFFAOYSA-N 0.000 description 1
- 239000002250 absorbent Substances 0.000 description 1
- 230000002745 absorbent Effects 0.000 description 1
- 230000001133 acceleration Effects 0.000 description 1
- 239000000853 adhesive Substances 0.000 description 1
- 230000001070 adhesive effect Effects 0.000 description 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 1
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 1
- 239000011230 binding agent Substances 0.000 description 1
- IHNSDAKWUWSLDU-UHFFFAOYSA-N bis(acetyloxymethyl)silylmethyl acetate Chemical compound C(C)(=O)OC[SiH](COC(C)=O)COC(C)=O IHNSDAKWUWSLDU-UHFFFAOYSA-N 0.000 description 1
- 229910052791 calcium Inorganic materials 0.000 description 1
- 239000011575 calcium Substances 0.000 description 1
- 239000000919 ceramic Substances 0.000 description 1
- 229910010293 ceramic material Inorganic materials 0.000 description 1
- 230000000052 comparative effect Effects 0.000 description 1
- 238000010276 construction Methods 0.000 description 1
- 238000004132 cross linking Methods 0.000 description 1
- 239000004205 dimethyl polysiloxane Substances 0.000 description 1
- 125000000524 functional group Chemical group 0.000 description 1
- 239000011521 glass Substances 0.000 description 1
- 125000002887 hydroxy group Chemical group [H]O* 0.000 description 1
- 230000003993 interaction Effects 0.000 description 1
- NLYAJNPCOHFWQQ-UHFFFAOYSA-N kaolin Chemical compound O.O.O=[Al]O[Si](=O)O[Si](=O)O[Al]=O NLYAJNPCOHFWQQ-UHFFFAOYSA-N 0.000 description 1
- 229910052622 kaolinite Inorganic materials 0.000 description 1
- 235000012243 magnesium silicates Nutrition 0.000 description 1
- 239000010445 mica Substances 0.000 description 1
- 229910052618 mica group Inorganic materials 0.000 description 1
- 239000012766 organic filler Substances 0.000 description 1
- 229920000435 poly(dimethylsiloxane) Polymers 0.000 description 1
- 229920002239 polyacrylonitrile Polymers 0.000 description 1
- 229920000642 polymer Polymers 0.000 description 1
- 238000006116 polymerization reaction Methods 0.000 description 1
- 239000000843 powder Substances 0.000 description 1
- 230000001681 protective effect Effects 0.000 description 1
- 230000001698 pyrogenic effect Effects 0.000 description 1
- 239000012763 reinforcing filler Substances 0.000 description 1
- 239000010935 stainless steel Substances 0.000 description 1
- 229910001220 stainless steel Inorganic materials 0.000 description 1
- 239000002562 thickening agent Substances 0.000 description 1
- 239000004408 titanium dioxide Substances 0.000 description 1
- 238000004383 yellowing Methods 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K9/00—Use of pretreated ingredients
- C08K9/04—Ingredients treated with organic substances
- C08K9/06—Ingredients treated with organic substances with silicon-containing compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/54—Silicon-containing compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K9/00—Use of pretreated ingredients
- C08K9/04—Ingredients treated with organic substances
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Sealing Material Composition (AREA)
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| DE19843439745 DE3439745A1 (de) | 1983-10-28 | 1984-10-26 | Kalthaertende dauerelastische einkomponenten-masse |
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| DE3339517 | 1983-10-28 | ||
| DE19843439745 DE3439745A1 (de) | 1983-10-28 | 1984-10-26 | Kalthaertende dauerelastische einkomponenten-masse |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| DE3439745A1 DE3439745A1 (de) | 1985-05-15 |
| DE3439745C2 true DE3439745C2 (enExample) | 1987-06-11 |
Family
ID=25815273
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| DE19843439745 Granted DE3439745A1 (de) | 1983-10-28 | 1984-10-26 | Kalthaertende dauerelastische einkomponenten-masse |
Country Status (1)
| Country | Link |
|---|---|
| DE (1) | DE3439745A1 (enExample) |
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN101903448B (zh) * | 2007-12-21 | 2012-12-26 | 陶氏康宁公司 | 可湿气固化的组合物 |
| CN106604969A (zh) * | 2015-01-28 | 2017-04-26 | 瓦克化学股份公司 | 通过缩合反应能够交联的有机聚硅氧烷组合物 |
Families Citing this family (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US6239378B1 (en) | 1999-02-02 | 2001-05-29 | Dow Corning Corporation | Flame resistant silicone rubber wire and cable coating composition |
| US6271299B1 (en) * | 1999-02-02 | 2001-08-07 | Dow Corning Corporation | Fire resistant sealant composition |
| DE19913810B4 (de) * | 1999-03-26 | 2005-02-03 | Quarzwerke Gmbh | Verfahren zur Reduzierung des Staubverhaltens von Silikaten, Silikate mit reduziertem Staubverhalten und deren Verwendung |
Family Cites Families (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE2911301C2 (de) * | 1979-03-22 | 1981-01-22 | Wacker-Chemie Gmbh, 8000 Muenchen | Bei Raumtemperatur zu Elastomeren vernetzbare Formmassen |
-
1984
- 1984-10-26 DE DE19843439745 patent/DE3439745A1/de active Granted
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN101903448B (zh) * | 2007-12-21 | 2012-12-26 | 陶氏康宁公司 | 可湿气固化的组合物 |
| CN106604969A (zh) * | 2015-01-28 | 2017-04-26 | 瓦克化学股份公司 | 通过缩合反应能够交联的有机聚硅氧烷组合物 |
| CN106604969B (zh) * | 2015-01-28 | 2019-10-22 | 瓦克化学股份公司 | 通过缩合反应能够交联的有机聚硅氧烷组合物 |
Also Published As
| Publication number | Publication date |
|---|---|
| DE3439745A1 (de) | 1985-05-15 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| DE2760050C1 (de) | Mit Silan ueberzogene Teilchen aus Calciumcarbonat oder Russ | |
| DE2528134A1 (de) | Silanhaltiges pulvergemisch und dessen verwendung | |
| DE2364856C3 (de) | Feuchtigkeitshärtende, lösungsmittelfreie Dichtungsmasse auf Basis von Organopolysiloxanen und Silikonöl | |
| EP0043501B1 (de) | Unter Wasserausschluss lagerfähige plastische Organopolysiloxan-Formmassen | |
| DE2244644C2 (enExample) | ||
| DE3439745C2 (enExample) | ||
| DE3836916A1 (de) | Unter ausschluss von feuchtigkeit lagerfaehige rtv-1k-massen, die ueberstreichbare elastomere bilden | |
| EP0018634B1 (de) | Zu Elastomeren vernetzbare Massen | |
| DE2240891C3 (de) | Dichtungs- und Überzugsmasse auf Polysulfidpolymerbasis und deren Verwendung | |
| DE1594281B2 (de) | Dichtungs- und isoliermasse auf der grundlage von fluessigen polysulfidpolymeren | |
| EP2641934A1 (de) | Siliconzusammensetzung mit verbesserten mechanischen Eigenschaften | |
| DE1282966B (de) | Verfahren zur Herstellung von Strahlenschutzkoerpern aus Organopolysiloxanen | |
| EP0107764B1 (de) | Giessharze auf Basis von Acrylsäureestern | |
| DE2524863C3 (de) | Mit einem Organosilan modifizierte mineralische Carbonate und/oder Sulfate | |
| DE2335082A1 (de) | Verstaerkte kautschukzusammensetzungen | |
| EP0005786B1 (de) | Zu Elastomeren vernetzbare Massen | |
| DE1669940B2 (de) | Unter formgebung durch vernetzung zu elastomeren haertbare massen auf organopolysiloxangrundlage | |
| EP0369291A2 (de) | Unter Feuchtigkeitsausschluss lagerfähige RTV-1K-Massen | |
| DD299187B5 (de) | Verfahren zur Herstellung von schwefelhaltigen Organosiliciumverbindungen | |
| EP0598339B1 (de) | Acrylfasern mit verbesserter Dispergierbarkeit in viskosen Matrizes, und Verfahren zur Herstellung von faserverstärkten Verbunden | |
| DE3447114C1 (de) | Giessharze auf Basis von Acrylsaeureestern | |
| AT345146B (de) | Bautenbeschichtungsmittel | |
| DE1794344C3 (de) | Polysulfidpolymermassen und deren Verwendung | |
| DE2145109C3 (de) | Härtbare Polysulfidpolymermasse | |
| DE1594281C3 (de) | Dichtungs- und Isoliermasse auf der Grundlage von flüssigen Polysulfidpoly- |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| OP8 | Request for examination as to paragraph 44 patent law | ||
| D2 | Grant after examination | ||
| 8363 | Opposition against the patent | ||
| 8331 | Complete revocation |